Abstract
Interface damage and delamination is usually accompanied by frictional slip at contacting interfaces under compressive normal stress. Under tensile stress the separation and opening mode develops. The present study provides a simplified analysis of progressive interface failure under applied in plane tractions and normal compressive traction. The cohesive crack model is used to simulate damage frictional traction present at contact. Both monotonic and cyclic loadings are considered for an elastic plate bonded to a rigid substrate by means of cohesive interface. The analysis of progressive delamination process revealed three solution types, namely short, medium and long plate solutions. For cyclic loading the states of frictional slip accompanied by shake down or incremental failure are distinguished. The finite element solutions confirm the validity of simplified analysis. The thermal loading case is studied separately under monotonic and cyclic temperature loading history. The cracking of plate is now accompanied by frictional slip and progressive delamination of the interface layer. The analysis predicts the cracking pattern and the size of delaminated zones.
Access provided by Autonomous University of Puebla. Download to read the full chapter text
Chapter PDF
Similar content being viewed by others
Keywords
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.
Bibliography
D. C. Agrawal and R. Raj. Measurement of the ultimate shear strength of a metal-ceramic interface. Acta metall, 37(4): 1265–1270, 1989.
D. C. Agrawal and R. Raj. Ultimate shear strengths of copper-silica and nickel-silica interfaces. Materials Science and Engineering, A126:125–131, 1990.
S. P. Baker, X. Wang, and C.-Y. Hui. Effect of nonlinear elastic behavior on bilayer decohesion of thin metal films from nonmetal substrate. Journal of Applied Mechanics, 69:407–414, July 2002.
G. I. Barenblatt. The mathematical theory of equilibrium cracks in brittle fracture. In Advances in Applied Mechanics, volume 7, pages 55–129. Academic Press, New York, 1962.
S. J. Bennison and B. R. Lawn. Role of interfacial crack bridging sliding friction in the crack resistance and strength properties of non-transforming ceramics. Acta Metallurgica, 37(10):2659–2671, 1989.
M. Białas and Z. Mróz. Modelling of progressive interface failure under combined normal compression and shear stress. Submitted to International Journal of Solids and Structures, 2004.
B. F. Chen, J. Hwang, I. F. Chen, G. P. Yu, and J-H. Huang. A tensile-film-cracking model for evaluating interfacial shear strength of elastic film on ductile substrate. Surface and Coatings Technology, 126:91–95, 2000.
S. Chi and Y.-L. Chung. Cracking in coating-substrate composite with multi-layered and fgm coatings. Engineering Fracture Mechanics, 70:1227–1243, 2003.
Y.-L. Chung and C.-F. Pon. Boundary element analysis of cracked film-substrate media. International Journal of Solids and Structures, 38:75–90, 2001.
D. S. Dugdale. Yielding of steel sheets containing slits. Journal of Mechanics and Physics of Solids, 8:100–104, 1960.
B. Erdem Alaca, M. T. A. Saif, and Huseyin Sehitoglu. On the interface debond at the edge of a thin film on a thick substrate. Acta Materialia, 50:1197–1209, 2002.
A. G. Evans and J. W. Hutchinson. Effect of non-planarity on the mixed mode fracture resistance. Ada Metallurgica, 37(3):909–916, 1989.
T. S. Gross and D. A. Mendelsohn. Model I stress intensity factors induced by fracture surface roughness under pure mode III loading: application to the effect of loading models on stress corrosion crack growth. Metallurgical and Material Transactions A, 20(10), 1989.
U. A. Handge, Y. Leterrier, G. Rochat, I. M. Sokolov, and A. Blumen. Two scaling domains in multiple cracking phenomena. Physical Review E, 62(6):7807–7810, 2000.
U. A. Handge, I. M. Sokolov, and A. Blumen. Disorder and plasticity in the fragmentation of coatings. Physical Review E, 64:106–109, 2001.
A. Hillerborg, M. Modeer, and P. E. Peterson. Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements. Cement and Concrete Research, 6:773–782, 1976.
D. R. Hiltunen and R. Roque. A mechanics-based prediction model for thermal cracking of asphaltic concrete pavements. Association of Asphalt Paving Technologists, 63: 81–117, 1994.
J. W. Hutchinson and Z. Suo. Mixed mode cracking of layered materials. In J. W. Hutchinson and T. Y. Wu, editors, Advances in Applied Mechanics, volume 29, pages 63–191. Academic Press, 1991.
S.-R. Kim and J. A. Nairn. Fracture mechanics analysis of coating/substrate systems. part i: Analysis of tensile and bending experiments. Engineering Fracture Mechanics, 65:573–593, 2000a.
S.-R. Kim and J. A. Nairn. Fracture mechanics analysis of coating/substrate systems. part ii: Experiments in bending. Engineering Fracture Mechanics, 65:595–607, 2000b.
K. Kokini and Y. R. Takeuchi. Multiple surface thermal fracture of graded ceramic coatings. Journal of Thermal Stresses, 27:715–725, 1998.
Z. Mróz and M. Białas. A simplified analysis of interface failure under compressive normal stress and monotonic or cyclic shear loading. International Journal of Numerical and Analytical Methods in Geomechanics. In press, 2004.
Z. Mróz and A. Seweryn. Non local failure and damage evolution rule: application to a dilatant crack model. Journal de Physique IV, 8(Pr 8):257–268, 1998.
Z. Mróz and S. Stupkiewicz. Hysteretic effects and progressive delamination at composite interfaces. In R. Pyrz, editor, IUTAM Symposium on Micro structure-Property Interactions in Composite Materials, pages 247–264. Kluwer Academic Publishers, 1995.
J. A. Nairn and S.-R. Kim. A fracture mechanics analysis of multiple cracking in coatings. Engineering Fracture Mechanics, 42:195–208, 1992.
M. Ortiz. Computational micro-mechanics. Computational Mechanics, 18(5):324–338, 1996.
H. L. Schreyer and A. Peffer. Fiber pullout based on a one-dimensinal model of decohesion. Mechanics of Materials, 32:821–836, 2000.
G. W. Schulze and F. Erdogan. Periodic cracking of elastic coating. International Journal of Solids and Structures, 35(28–29):3615–3634, 1998.
F.-S. Shieu, R. Raj, and S. L. Sass. Control of mechanical properties of metal-ceramic interfaces through interfacial reactions. Acta metall mater., 38(11):2215–2224, 1990.
D. H. Timm, B. B. Guzina, and V. R. Voller. Prediction of thermal crack spacing. International Journal of Solids and Structures, 40:125–142, 2003.
S. Wolfram. The Mathematica Book (4th ed.). Wolfram Media/Cambridge University Press, 1999.
Z. C. Xia and J. W. Hutchinson. Crack patterns in thin films. Journal of Mechanics and Physics of Solids, 48:1107–1131, 2000.
B. Yang and K. Ravi-Chandar. Antiplane shear crack growth under quasistatic loading in a damaging material. International Journal of Solids and Structures, 35(28,29): 3695–3715, 1997.
T.-Y. Zhang and M.-H. Zhao. Equilibrium depth and spacing of cracks in a tensile residual stressed thin film deposited on a brittle substrate. Engineering Fracture Mechanics, 69:589–596, 2002.
Author information
Authors and Affiliations
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2005 CISM, Udine
About this chapter
Cite this chapter
Białas, M., Mróz, Z. (2005). Damage Modelling at Material Interfaces. In: Sadowski, T. (eds) Multiscale Modelling of Damage and Fracture Processes in Composite Materials. CISM International Centre for Mechanical Sciences, vol 474. Springer, Vienna. https://doi.org/10.1007/3-211-38102-3_6
Download citation
DOI: https://doi.org/10.1007/3-211-38102-3_6
Publisher Name: Springer, Vienna
Print ISBN: 978-3-211-29558-8
Online ISBN: 978-3-211-38102-1
eBook Packages: EngineeringEngineering (R0)