Abstract
Water electrolysis is considered one of the major sources of green hydrogen as the fuel of the future. However, due to limited freshwater resources, more interest has been geared toward seawater electrolysis for hydrogen production. The development of effective and selective electrocatalysts from earth-abundant elements for oxygen evolution reaction (OER) as the bottleneck for seawater electrolysis is highly desirable. This work introduces novel Pd-doped Co nanoparticles encapsulated in graphite carbon shell electrode (Pd-doped CoNPs@C shell) as a highly active OER electrocatalyst towards alkaline seawater oxidation, which outperforms the state-of-the-art catalyst, RuO2. Significantly, Pd-doped CoNPs@C shell electrode exhibiting low OER overpotential of ≈213, ≈372, and ≈ 429 mV at 10, 50, and 100 mA/cm2, respectively together with a small Tafel slope of ≈ 120 mV/dec than pure Co@C and Pd@C electrode in alkaline seawater media. The high catalytic activity at the aforementioned current density reveals decent selectivity, thus obviating the evolution of chloride reaction (CER), i.e., ∼490 mV, as competitive to the OER. Results indicated that Pd-doped Co nanoparticles encapsulated in graphite carbon shell (Pd-doped CoNPs@C electrode) could be a very promising candidate for seawater electrolysis.
Similar content being viewed by others
Introduction
The growing need for energy and concerns about fossil fuel consumption necessitates using green and sustainable energy sources1,2. Hydrogen, as a clean fuel, has gotten huge attention and has been thoroughly investigated as a viable alternative to fossil fuels3,4. Despite its tremendous application potential, current commercial hydrogen production relies on fossil fuels with huge carbon emissions5,6. As a result, it is critical to investigate a cleaner, more sustainable, and more efficient strategy for hydrogen production. Water splitting with high energy conversion efficiency has recently been exploited as an efficient and environmentally friendly option7,8. Therefore, electrochemical water splitting, i.e., water electrolysis, is currently being explored for the futuristic expansion of hydrogen production9. As water electrolysis has shown promising results, however, freshwater resources are scarce in many regions worldwide. Although seawater is an abundant resource, accounting for almost 97% of the planet's water, seawater electrolysis is still in its infancy10,11. Therefore, seawater electrolysis has become a hot research topic, which is mainly based on anodic oxygen evolution and cathodic hydrogen evolution reactions, i.e., OER and HER, respectively. Unfortunately, the presence of electrochemically active chloride anions, which may severely deteriorate the electrocatalysts and compete with the OER is considered the main obstacle to seawater electrolysis10,11. Furthermore, the complex chemistry of seawater might cause insoluble precipitates to develop on the active site of the catalyst surface, lowering its performance12,13,14,15.
Significant activation barriers in the HER and OER pathways lead to large overpotentials, resulting in slow water electrolysis kinetics16,17. To reduce the activation energy barrier, lower the overpotential, and eventually higher energy conversion efficiency, electrocatalysts should poses high activity18. Therefore, it has great importance to develop active and selective electrocatalysts to drive the OER activity in seawater environment19. Water electrolysis preferably take place in acidic or alkaline media. Unfortunately, the lack of efficient and low-cost catalysts makes acid electrolyzers technologically and commercially unviable3,20. As a result, huge efforts have been made to produce catalysts with high activity and stability in alkaline media based on existing alkaline oxygen evolution electrocatalysts, to speed the commercialization of alkaline electrolyzers for hydrogen production.
In general, noble metal-based catalysts are thought to be the best electrocatalysts for stimulating electrochemical reactions such as HER, OER, and oxygen reduction reaction (ORR)21,22 but they are costly and scarce, making them unsuitable for large-scale commercial production23,24. As a result, finding low-cost, high efficiency electrocatalysts for is paramount. This motivates a worldwide search for non-noble metal-based alternatives, such as Co-25, Ni-26, and Mo-based catalysts 27. Co-based catalysts, in particular, are excellent low-cost electrocatalysts for OER4. Various Co-based catalysts, such as CoO28, CoSe229, CoP30, CoPS31, Co2B32, CuCo33, and FeCo34, have sprung due to their simple preparation, low cost, and excellent activity as well as durability when compared to other Co-based complexes35. Bimetallic catalysts that combine platinum group elements with Co usually provide higher catalytic performance through cooperative effect that is not visible in their monometallic counterparts4,36.
Theoretical and experimental data show that alloying platinum group elements with Co alter the average surface energy as well as the width of the d-band due to cumulative strain and ligand effect. This can lead to changes in surface chemical characteristics and a significant increase the activity37,38. Palladium, has been explored as a potential alloying element because of its stronger affinity for OER and lower cost than Pt39. In addition, integrating alloy with carbon substrates, especially encapsulating them in heteroatom-doped carbon, can enhance OER performance8,37. Furthermore, Bao et al. reported that combining a carbon shell with a metal core could boost activity and stability at the same time. Recently, N-doped graphene-encased metal or alloy has emerged as a novel and exciting electrocatalysts40. Furthermore, electrons would flow from the metal core to the outside carbon layer due to the distinct working functions of metal and nonmetal, increasing the density of carbon states near the Fermi level and optimizing their kinetic processes for various fundamental steps41. As a result, the overall activity of metal-doped carbon structures can be tailored using either the carbon shell or the metal core. Accordingly, electrical structures of carbon can be modified to boost their activities by altering doping types, doping concentrations, element types, metal proportions, and structures in the alloy core42. In this study, Pd-doped Co nanoparticles encapsulated in graphitic carbon shell (Pd-doped CoNPs@C electrode) are developed with simple and cost-effective route. The developed catalyst is then assessed as a selective anode towards cost-efficient OER under alkaline pH conditions from seawater splitting.
Experimental section
Chemicals and materials
Palladium (II) acetate PdAc (Pd (CH3CO2)2.), Cobalt (II) acetate CoAc (Co (CH3CO2)2), and Poly (Vinyl Alcohol) PVA (Mw 85,000–124,00) were purchased from Sigma-Aldrich. All the chemicals were used as received without any further purification. Milli-Q ultrapure water (≈18.2 MΩ) was used for all the syntheses.
Synthesis of Pd-doped Co nanoparticles encapsulated in graphite carbon shell
A typical synthesis of Pd-doped CoNPs@C electrode was conducted as follows: 5.0 g of 10 wt% PVA, 0.8 gm of CoAc, and 0.2 gm of PdAc were mixed very well with continuous stirring at 60 °C for 10 h. The obtained so-gel was dried first at 80 °C for 48 h and then under vacuum at 80 °C for 12 h. Finally, the obtained solid mixture was crushed, ground, and sintered under an Ar atmosphere at 1 atm and 700 °C for 5 h. Figure 1 shows the schematic of the synthesis procedure for Pd-doped CoNPs@C electrode.
Characterizations
Field-emission scanning electron FESEM-FEI microscopy (ThermoFisher Scientific, MA, USA), transmission electron (TEM) microscope (JEM-2100F, JEOL, Japan), and high-resolution TEM (HRTEM) techniques were utilized for morphological characterizations while, the X-ray diffractometer XRD (XRD- D/max 2500 Rigaku, TX, USA) and X-ray photoelectron spectroscopy XPS (AXIS Ultra DLD, Kratus, UK) techniques were used to analyze the phase structure/crystallinity and the surface chemistries of the prepared Pd-doped CoNPs@C electrode, respectively. The element loading amount was estimated by Inductively coupled plasma mass spectrometry ICP-MS (Perkin Elmer NexION 300D).
Electrochemical measurements
Electrochemical tests were performed using Reference 3000 electrochemical workstation (Gamry, PA, USA). The catalytic performance was evaluated in 1.0 M KOH and 1.0 M KOH + 0.6 M NaCl aqueous solution with a conventional three-electrode system. The Ag/AgCl electrode and Pt wire were used as reference and counter electrodes, respectively. The glassy carbon as a working electrode was prepared with 15 µL of the catalyst ink composed of 2.0 mg of catalyst nanoparticles, 200 µL n-propanol, 200 µl of Nafion 117 solution and 200 µL DI water. The linear sweep voltammetry (LSV) polarization curves were obtained at a scan rate of 10 mV/s. The uncompensated resistance (Rs) and charge transfer resistance (Rct) were measured using the electrochemical impedance spectroscopic (EIS) techniques with a frequency range from 1 MHz to 1 Hz under the open-circuit potential, the Tafel slope was obtained by linear fitting, the plot of “log(i) versus η”. The electrochemical active surface area (ECSA) was evaluated through the double-layer capacitance (Cdl) values measured from the CV curve within a non-faradic potential window at various scan rates of 10, 25, 50, and 100 mV/s.
Results and discussions
Morphology and structural characterizations
The X-ray diffraction measurements were carried out to determine the underlying crystal structure of the synthesized Pd-doped CoNPs@C electrode. As observed, the XRD pattern Fig. 2A shows three diffraction peaks located at 43.6°, 50.5° and 74.7° which are correspond well to the (111), (200) and (220) lattice planes of the face-centered cubic crystalline cobalt-palladium nanoparticles (JCPDS no. 65–6174), respectively. Meanwhile, compared with the standard patterns of Co (JCPDS: no. 88–2325) and Pd (JCPDS: no. 65–6174), the peak positions shifted to the large angles, which can be attributed to the insertion of Pd in the Co cubic structure (Fig. 2B)8,43. The X-ray photoelectron spectroscopy (XPS) was further employed to explore the surface chemistry of the synthesized Pd-doped CoNPs@C electrode. As observed, the full XPS spectrum Fig. 3A shows the major binding energies of Pd3d, Co2p, C1s and O1s at 320, 780, 286 and 531 eV, respectively which clarify the existence of Pd, Co, C and O in the synthesized Pd-doped CoNPs@C electrode. As can be observed in Fig. 3B, the high-resolution C1s spectrum can be deconvoluted into two obvious individual peaks of Sp2 carbon at 284.7 eV and C−OH at 286 eV44. On the other hand, the high-resolution O1s spectrum (Fig. 3C) can be deconvoluted into two peaks at 531.2 eV and 533 eV belong to metal oxide and C−OH, respectively45. However, the high resolution XPS spectra for Co2p (Fig. 3D) can be deconvoluted into 2p1/2 and 2p3/2 components, which confirm the presence of metallic and oxidic state of Co. As observed in Fig. 3D, a pair of peaks at 781.69 eV and 797.55 eV belong to metallic state Co, while a pair of peaks at 786.09 eV and 802.62 eV belong to the oxidic sate of Co. Similarly, as observed in high-resolution Pd3d spectra of synthesized Pd-doped CoNPs@C electrode presented in Fig. 3E can be deconvoluted into two components. A pair of peaks at 334.5 eV and 339.8 eV cab be assigned to the Pd 3d5/2 and 3d3/2 peaks of metallic Pd, while other pair of peaks at 335.2 eV and 340.4 eV are assigned to Pd 3d5/2 and 3d3/2 peaks of oxidic state of Pd. The existence of oxidic state of Pd/Co was probably attributed to the surface oxidation of metallic Co/Pd46. It is worth noting that both Pd3d and Co2p binding energies of the synthesized Pd-doped CoNPs@C electrode shift to the higher binding energies compared to their standard values, indicating the incorporation of Pd and Co in the synthesized Pd-doped CoNPs@C electrode. The binding energy shift in Pd3d and Co2p to the higher binding energies can be attributed to the existence of oxidic Co/Pd in PdCo, which is consistent with the literature46. However, inductively coupled plasma mass spectrometry (ICP-MS) result reveals that the Pd/Co molar ratio in the synthesized Pd-doped CoNPs@C electrode was 8:2. The morphology and structure of the synthesized Pd-doped CoNPs@C electrode were investigated by SEM and TEM techniques. As observed in the SAM image (Fig. 4A) the synthesized Pd-doped CoNPs@C electrode maintains quite spherical structure with cluster of uniformly distributed particles. Moreover, the average particles size was in the range of 50–100 nm (Fig. 4B). On the other hand, as shown in the TEM image (Fig. 5A) the metallic nanoparticles enveloped by the graphite shell. However, the high magnification TEM image (Fig. 5B) stated that the synthesized Pd-doped CoNPs@C electrode comprises of both crystalline and amorphous parts (marked by solid line). Further, close observation shows more than one lattice spacing of 0.221 and 0.191 nm can be attributed to the (111) and (200) planes of the Pd-Co alloying, respectively. This observation simultaneously supports the XRD results (Fig. 2A. What’s more the elemental mapping on the randomly selected area shows that Pd and Co are uniformly distributed over the whole nanoparticles (Fig. 5C). However, Co is dominant (94.1%) followed by C (4.61%) and Pd (1.29%).
Electrocatalytic performance
Electrocatalytic OER performance in 1.0 M KOH aqueous solution
To assess the efficiency of the developed electrocatalyst, the OER electrocatalytic performance for prepared Pd-doped CoNPs@C, Pd@C, Co@C, and pristine C electrodes, along with RuO2 electrode was investigated by LSV using the conventional three-electrode setup in 1.0 M KOH aqueous solution at a scan rate of 10 mV/s. As seen in Fig. 6A, the Pd-doped CoNPs@C electrode exhibit a small onset potential with a high current response when compared with the Pd@C, Co@C, and pristine C electrode. Importantly, as seen, the Pd-doped CoNPs@C electrode had a very low overpotential of 198.7 mV to deliver the current density of 10 mA/cm2, which is comparable to that of commercial RuO2 electrode under the same conditions47. Figure 6B also shows that the Pd-doped CoNPs@C electrode achieved the current density of 50 and 100 mA/cm2 at the overpotential of 339.5 and 399.5 mV, respectively, while the required overpotential values to afford ƞ10, and ƞ50, current density for Pd@C (ƞ10 = 375.7 mV, ƞ50 = 543.4 mV), and Co@C (ƞ10 = 312.6 mV, ƞ50 = 420.5 mV) was much higher than Pd-doped CoNPs@C electrode.
To further validate our findings, we deliberately study the kinetic behavior of Pd-doped CoNPs@C, Pd@C, and Co@C electrodes towards the OER reaction at the electrode–electrolyte interface using the Tafel plot. As seen in Fig. 7A, the corresponding Tafel slope for the Pd-doped CoNPs@C electrode was the smallest (65.32 mv/dec.) when compared with Pd@C (120.5 mv/dec.), and Co@C electrode (101.6 mV/dec.). The results indicate that the Pd-doped CoNPs@C electrode have faster reaction kinetics and superior OER activity when compared to the Pd@C and Co@C electrode.
Electrocatalytic OER performance in alkaline seawater medium
After demonstrating such a good electrocatalytic performance of Pd-doped CoNPs @C electrode in an alkaline medium, it is worth performing the same electrochemical analyses in an alkaline seawater medium. Therefore, the electrocatalytic OER performance of the Pd-doped CoNPs@C electrode was evaluated in 1 M KOH + 0.6 M NaCl. As shown in Fig. 6C Pd-doped CoNPs@C electrode exhibit slight activity decay in 1 M KOH + 0.6 M NaCl, but as expected, Pd-doped CoNPs@C electrode demonstrate reasonably good OER activity among other formulations with a low overpotential of ≈213 mV to deliver a current density of 10 mA/cm2, followed by Co@C (≈ 348 mV) and Pd@C (≈ 657 mV). Nevertheless, it is worthwhile to mention that to deliver a current density of 100 mA/cm2, the overpotential (≈ 429.5 mV) required for Pd-doped CoNPs@C electrode is lower than that to initiate hypochlorite formation (≥ 490 mV) as shown in Fig. 6D. The corresponding Tafel slope (Fig. 7B) for all the formulations shows significant increases compared to the values obtained under the alkaline conditions. The existence of Cl− may contribute to its OER reaction kinetics degradation, as it is easily adsorbed and block the active sites of the metal-based electrocatalysts system48.
To figure out the enhanced OER activity of Pd-doped CoNPs@C electrode over the Co@C and Pd@C electrode, ECSA and EIS techniques have been used. First, ESCA of Pd-doped CoNPs@C, Co@C, and Pd@C electrode was explored using the CV test as the ESCA is equal to the Cdl that could be obtained from the CV curves. These CV curves were measured in the non-faradaic region at various scan rates of 10, 25, 50, 75 and 100 mV/s vs RHE (Supporting information, Figure S1). As seen in Fig. 8A, the Pd-doped CoNPs@C electrode deliver the highest Cdl value (55.1 mF/cm2) compared to Pd@C electrode (17.9 mF/cm2) and Co@C electrode (21.9 mF/cm2). The higher Cdl value delivered by Pd-doped CoNPs@C electrode shows the more accessible active sites for OER. Further, EIS was recorded to examine the inherent conductivity of Pd-doped CoNPs @C electrode and all other reference electrodes. As seen in Fig. 8B, Pd-doped CoNPs@C electrode showed smaller semicircles loop diameter compared to the Pd@C electrode and Co@C electrodes. A Randle circuit model can be used to deduce the EIS data. Based on the equivalent circuit (inset Fig. 8B) Pd-doped CoNPs@C electrode showed much lower Rct (12.34 Ω cm2), suggesting that electron transfer between electrode and electrolyte is very fast. To understand the factual contribution, the OER current densities of Pd-doped CoNPs@C electrode, Pd@C and Co@C electrode have been normalized to the corresponding Cdl, as shown in Fig. 9. It is worth observing that Pd-doped CoNPs@C electrode exhibit the highest Cdl normalized OER performance especially compared to all other references as can be seen in Fig. 9A,B. The cyclic stability of OER electrocatalysts is also a critical challenge for practical applications. Therefore, the LSV check was executed at 100 mV/s for 10,000 consecutive cycles. As can be seen, Pd-doped CoNPs@C electrode is quite stable but gradual shift in the potential after 3000 LSV cycles is attributed to the bubbles accumulation at the active area of the electrode (Fig. 10). However, only 6% overpotential was increased to maintain the same current density after 10,000 cycles (inset Fig. 10).
However, based on the above studies, the mechanism is established to underline the improved catalytic activity of Pd-doped CoNPs @C electrode toward OER can be attributed to the following unique features.
-
1)
The structural change due to doping of Pd nanoparticles can improve intrinsic catalytic activity, reduce activation energy and enhance the adsorption of OH− and OOH− intermediates toward OER, which can be realistically considered through the synergistic effect of individual elements and the rich interfaces (i.e. Pd–Co–C)49. In addition, integrating the inherent conductive characteristic of graphitic carbon around PdCo nanoparticles can also promote potent charge transfer between Pd-doped CoNPs@C electrode and electrolyte, which is proven by the low charge transfer resistance50.
-
2)
In accordance with ECSA results, Pd nanoparticle doping has significantly enhanced the Co/C active sites, which can reasonably be considered toward the OER responses. What’s more, from the XPS measurements (Fig. 3D,E), it can be claimed that the weak oxophilicity of Pd-doped CoNPs@C electrode is also responsible for the improved OER activity51.
-
3)
Besides the above, EIS results further confirm that the doping of Pd nanoparticles gives rise to low internal resistance and fast charge transfer for a low onset potential and high OER kinetics. In addition, numerous Pd-doped Co nanoparticles are assembled on the graphitic carbonaceous nanostructure, which can offer a pathway for fast electron transport from the electrode and electrolyte52.
-
4)
Finally, the distinctive morphology makes Pd-doped CoNPs@C electrode possesses excellent OER activity and durability.
Conclusion
We propose Pd-doped Co nanoparticles encapsulated in graphitic shell (Pd-doped CoNPs@C electrode), as an effective and cost efficient electrocatalyst for OER in water electrolysis, more specifically for alkaline seawater electrolysis. The Pd-doped CoNPs@C electrode shows reasonably high activity and selectivity over chlorine evolution reaction (CER) under alkaline pH conditions for seawater oxidation. The synergistic effect of individual elements and the rich interfaces (i.e., Pd–Co–C) significantly contributed to the increased electrochemical active surface area and reasonable improved electrode performance (i.e., low internal resistance, low onset potential, fast charge transfer and high OER kinetics) were clearly observed. In conclusion, this study provides quite sufficient experimental details for research and development of efficient and cost-effective electrocatalysts for seawater oxidation.
Data availability
All data generated or analyzed during this study are included in this published article.
References
Chen, A. & Ostrom, C. Palladium-based nanomaterials: Synthesis and electrochemical applications. Chem. Rev. 115(21), 11999–12044 (2015).
Tang, Y.-J. et al. Porous molybdenum-based hybrid catalysts for highly efficient hydrogen evolution. Angew. Chem. Int. Ed. 54(44), 12928–12932 (2015).
Wang, T. et al. A highly efficient and stable biphasic nanocrystalline Ni–Mo–N catalyst for hydrogen evolution in both acidic and alkaline electrolytes. Nano Energy 22, 111–119 (2016).
Su, J. et al. Ruthenium-cobalt nanoalloys encapsulated in nitrogen-doped graphene as active electrocatalysts for producing hydrogen in alkaline media. Nat. Commun. 8(1), 14969–14969 (2017).
Zheng, Y., Jiao, Y. & Qiao, S. Z. Engineering of carbon-based electrocatalysts for emerging energy conversion: From fundamentality to functionality. Adv. Mater. 27(36), 5372–5378 (2015).
Xie, X. et al. Electrocatalytic hydrogen evolution in neutral pH solutions: Dual-phase synergy. ACS Catal. 9(9), 8712–8718 (2019).
Walter, M. G. et al. Solar water splitting cells. Chem. Rev. 110(11), 6446–6473 (2010).
Zhong, M. et al. PdCo alloys@N-doped porous carbon supported on reduced graphene oxide as a highly efficient electrocatalyst for hydrogen evolution reaction. J. Mater. Sci. 56(25), 14222–14233 (2021).
Su, J. et al. Co3ZnC/Co nano heterojunctions encapsulated in N-doped graphene layers derived from PBAs as highly efficient bi-functional OER and ORR electrocatalysts. J. Mater. Chem. A 4(23), 9204–9212 (2016).
Dresp, S. et al. Direct electrolytic splitting of seawater: Opportunities and challenges. ACS Energy Lett. 4(4), 933–942 (2019).
Tong, W. et al. Electrolysis of low-grade and saline surface water. Nature Energy 5(5), 367–377 (2020).
Ge, R. et al. Phase-selective synthesis of self-supported RuP films for efficient hydrogen evolution electrocatalysis in alkaline media. Nanoscale 10(29), 13930–13935 (2018).
Gao, S. et al. Electrocatalytic H2 production from seawater over Co N-codoped nanocarbons. Nanoscale 7(6), 2306–2316 (2015).
Zhao, Q. et al. Approaching a high-rate and sustainable production of hydrogen peroxide: oxygen reduction on Co–N–C single-atom electrocatalysts in simulated seawater. Energy Environ. Sci. 14(10), 5444–5456 (2021).
Yun, K. et al. Solar-driven, highly sustained splitting of seawater into hydrogen and oxygen fuels. Proc. Natl. Acad. Sci. 116(14), 6624–6629 (2019).
Xu, S. et al. Iron-based phosphides as electrocatalysts for the hydrogen evolution reaction: Recent advances and future prospects. J. Mater. Chem. A 8(38), 19729–19745 (2020).
Jiang, S. et al. Recent advances in seawater electrolysis. Catalysts 12(2), 123 (2022).
Dincer, I. & Acar, C. Review and evaluation of hydrogen production methods for better sustainability. Int. J. Hydrog. Energy 40(34), 11094–11111 (2015).
Yang, Y. et al. Non-precious alloy encapsulated in nitrogen-doped graphene layers derived from MOFs as an active and durable hydrogen evolution reaction catalyst. Energy Environ. Sci. 8(12), 3563–3571 (2015).
Gong, M. et al. A mini review on nickel-based electrocatalysts for alkaline hydrogen evolution reaction. Nano Res. 9(1), 28–46 (2016).
Sheng, W. et al. Correlating the hydrogen evolution reaction activity in alkaline electrolytes with the hydrogen binding energy on monometallic surfaces. Energy Environ. Sci. 6(5), 1509–1512 (2013).
Zhu, L. et al. A rhodium/silicon co-electrocatalyst design concept to surpass platinum hydrogen evolution activity at high overpotentials. Nat. Commun. 7(1), 12272–12272 (2016).
Wang, Y.-J., Wilkinson, D. P. & Zhang, J. Noncarbon support materials for polymer electrolyte membrane fuel cell electrocatalysts. Chem. Rev. 111(12), 7625–7651 (2011).
McCrory, C. C. L. et al. Benchmarking hydrogen evolving reaction and oxygen evolving reaction electrocatalysts for solar water splitting devices. J. Am. Chem. Soc. 137(13), 4347–4357 (2015).
Hu, X. et al. 2D Fe-containing cobalt phosphide/cobalt oxide lateral heterostructure with enhanced activity for oxygen evolution reaction. Nano Energy 56, 109–117 (2019).
Jiao, Y. et al. Metal-organic framework derived Ni/NiO micro-particles with subtle lattice distortions for high-performance electrocatalyst and supercapacitor. Appl. Catal. B Environ. 244, 732–739 (2019).
Li, J.-S. et al. Reduced graphene oxide-supported MoP@P-Doped porous carbon nano-octahedrons as high-performance electrocatalysts for hydrogen evolution. ACS Sustain. Chem. Eng. 6(8), 10252–10259 (2018).
Zhang, K. et al. N-doped CoO nanowire arrays as efficient electrocatalysts for oxygen evolution reaction. J. Energy Chem. 37, 13–17 (2019).
Xue, N. et al. Sulfur-doped CoSe2 porous nanosheets as efficient electrocatalysts for the hydrogen evolution reaction. ACS Appl. Mater. Interfaces 12(25), 28288–28297 (2020).
Zhu, D. et al. A free-standing and flexible phosphorus/nitrogen dual-doped three-dimensional reticular porous carbon frameworks encapsulated cobalt phosphide with superior performance for nitrite detection in drinking water and sausage samples. Sens. Actuators B Chem. 321, 128541–128541 (2020).
Cabán-Acevedo, M. et al. Efficient hydrogen evolution catalysis using ternary pyrite-type cobalt phosphosulphide. Nat. Mater. 14(12), 1245–1251 (2015).
Guo, Y. et al. Multifunctional Co–B–O@CoxB catalysts for efficient hydrogen generation. Int. J. Hydrog. Energy 45(1), 380–390 (2020).
Kuang, M. et al. Cu, Co-embedded N-enriched mesoporous carbon for efficient oxygen reduction and hydrogen evolution reactions. Adv. Energy Mater. 7(17), 1700193–1700193 (2017).
Zhou, J. et al. Ultrafast fabrication of porous transition metal foams for efficient electrocatalytic water splitting. Appl. Catal. B Environ. 288, 120002–120002 (2021).
Anantharaj, S. et al. Recent trends and perspectives in electrochemical water splitting with an emphasis on sulfide, selenide, and phosphide catalysts of Fe Co, and Ni: A review. ACS Catal. 6(12), 8069–8097 (2016).
Li, J.-S. et al. Synergistically enhanced hydrogen evolution reaction by ruthenium nanoparticles dispersed on N-doped carbon hollow nanospheres. Chem. Commun. 56(50), 6802–6805 (2020).
Chen, J. et al. Active and durable hydrogen evolution reaction catalyst derived from Pd-doped metal-organic frameworks. ACS Appl. Mater. Interfaces 8(21), 13378–13383 (2016).
Zheng, Y. et al. Advancing the electrochemistry of the hydrogen-evolution reaction through combining experiment and theory. Angew. Chem. Int. Ed. 54(1), 52–65 (2015).
Ao, Y. et al. Palladium cobalt alloy encapsulated in carbon nanofibers as bifunctional electrocatalyst for high-efficiency overall hydrazine splitting. J. Colloid Interface Sci. 601, 495–504 (2021).
Cui, X. et al. Single layer graphene encapsulating non-precious metals as high-performance electrocatalysts for water oxidation. Energy Environ. Sci. 9(1), 123–129 (2016).
Deng, D. et al. Toward N-doped graphene via solvothermal synthesis. Chem. Mater. 23(5), 1188–1193 (2011).
Yang, Y. et al. MOFs-derived N-doped carbon-encapsulated metal/alloy electrocatalysts to tune the electronic structure and reactivity of carbon active sites†. Chin. J. Chem. 39(9), 2626–2637 (2021).
Xue, H. et al. Fabrication of PdCo bimetallic nanoparticles anchored on three-dimensional ordered N-doped porous carbon as an efficient catalyst for oxygen reduction reaction. ACS Appl. Mater. Interfaces 8(32), 20766–20771 (2016).
Deming, C. P. et al. Oxygen electroreduction catalyzed by palladium nanoparticles supported on nitrogen-doped graphene quantum dots: Impacts of nitrogen dopants. ACS Sustain. Chem. Eng. 4(12), 6580–6589 (2016).
Guan, S. et al. Influence of anneal temperature in air on surface morphology and photoluminescence of ZnO thin films. IOP Conf. Ser. Mater. Sci. Eng. 522, 12004–12004 (2019).
Li, T. et al. Tuning the surface segregation composition of a PdCo alloy by the atmosphere for increasing electrocatalytic activity. Sustain. Energy Fuels 4(1), 380–386 (2020).
Ghouri, Z. K. et al. Theoretical and experimental investigations of Co-Cu bimetallic alloys-incorporated carbon nanowires as an efficient bi-functional electrocatalyst for water splitting. J. Ind. Eng. Chem. 96, 243–253 (2021).
Zhang, F. et al. Rational design of oxygen evolution reaction catalysts for seawater electrolysis. Trends Chem. 3(6), 485–498 (2021).
He, H. et al. Modulating the electrocatalytic performance of palladium with the electronic metal–support interaction: a case study on oxygen evolution reaction. ACS Catal. 8(7), 6617–6626 (2018).
Zeng, M. et al. Metallic cobalt nanoparticles encapsulated in nitrogen-enriched graphene shells: its bifunctional electrocatalysis and application in zinc–air batteries. Adv. Funct. Mater. 26(24), 4397–4404 (2016).
Sheng, G. et al. Hollow PdCo alloy nanospheres with mesoporous shells as high-performance catalysts for methanol oxidation. J. Colloid Interface Sci. 522, 264–271 (2018).
Liu, Z. et al. Promotion of overall water splitting activity over a wide pH range by interfacial electrical effects of metallic NiCo-nitrides nanoparticle/NiCo2O4 nanoflake/graphite fibers. Adv. Sci. 6(5), 1801829 (2019).
Acknowledgements
This study is supported by a grant from the Qatar National Research Fund under the National Priorities Research Program–Award Number–NPRP12S-0131-190024 and co-funding support from Qatar Shell Research and Technology Center (QSRTC). The paper’s contents are solely the responsibility of the authors and do not necessarily represent the official views of the Qatar National Research Fund. Further, M.M.N and Z.K.G wish to acknowledge a Research Fellow Grant from the Ministry of Higher Education through Universiti Teknologi Malaysia with Q.K130000.21A6.00P33.
Author information
Authors and Affiliations
Contributions
K.A. helped in the analysis, experimental work and co-wrote the manuscript; K.E. helped in the data analysis and revised the manuscript; M.N. helped in the data analysis; A.B. contributed to the characterization and analyzed data; A.A.W. helped in the analysis and experimental work; D.J.H. helped in the analysis, experimental work and revised the manuscript to improve the language; Z.K.G. conceived the idea, designs the experiments, and followed up the experimental work. All authors reviewed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ghouri, Z.K., Hughes, D.J., Ahmed, K. et al. Nanoengineered, Pd-doped Co@C nanoparticles as an effective electrocatalyst for OER in alkaline seawater electrolysis. Sci Rep 13, 20866 (2023). https://doi.org/10.1038/s41598-023-46292-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-46292-9
- Springer Nature Limited