Abstract
Twinning is commonly activated in plastic deformation of low stacking-fault face-centered cubic (Fcc) metals but rarely found in body-centered cubic (Bcc) metals under room temperature and slow strain rates. Here, by conducting in situ transmission electron microscopy (TEM) at atomic scale, we discover that, in stark contrast to those in most Fcc metals, a majority of deformation twins in Bcc metals are unstable and undergo spontaneously detwinning upon unloading. Such unexpected instability of Bcc twins is found to be closely related to the prevalence of the inclined twin boundaries—a peculiar structure where twin boundaries are not parallel to the twinning plane, and the degree of instability is in direct proportion to the fraction of the inclined twin boundary. This work provides significant insights into the structure and stability of deformation twins in Bcc metals.
Similar content being viewed by others
Introduction
Twinning as a common deformation mode plays a significant role in the mechanical properties of materials1. Twin boundaries can not only act as an effective barrier to hinder dislocation motion and accumulate dislocations but also provide the motion path and nucleation sites for dislocations, contributing to the excellent mechanical properties without the traditional trade-off between strength and ductility2,3,4. An ideal coherent twin boundary (CTB) with a coincidence interface is considered as a low-energy boundary with excellent thermal stability3,5, which provides massive space for property adjustments. Understanding the twinning ability and the stability of the twin structure is critical for engineering nanotwins toward advanced materials design.
Body-centered cubic (Bcc) metals, such as ferritic steels, are widely used as structural materials and magnetic functional materials. Different from metals with closed-packed structures such as face-centered cubic (Fcc), Bcc metals show poor twinning ability due to their high stacking faults energy6,7. As a result, dislocation plasticity normally dominates the plastic deformation of Bcc metals, whereas deformation twinning is only activated under extreme conditions, e.g., high stress, high strain rate, and low temperatures8. Recently, twinning-dominated plasticity in nanoscale Bcc metals was discovered by in-situ transmission electron microscope (TEM) experiment9,10, offering a good opportunity to directly study the twinning process and the thermodynamic stability of the twin that associate with the structures and energies of twin boundaries, which remains largely unclear in Bcc metals.
Here, by performing atomistic in-situ TEM study, we reveal that the twin stability and the detwinning process in Bcc tungsten (W) are strongly dependent on the type of twin boundary. Specifically, the stability of deformation twins in bcc metals is found to be controlled by a unique interface structure of the inclined twin boundary. Quantitative analysis demonstrates that the high energy of the inclined twin boundary contributes significantly to the driving force for detwinning and twins containing a high proportion of inclined twin boundaries show higher self-detwinning rates. Our work reveals the underlying mechanism of unstable deformation twins in Bcc metals and provides deep understanding of the (de)twinning behaviors, which is significant for the design and processing of twin structures in Bcc metals. Moreover, the spontaneous detwinning associated with the unstable twin brings possibilities to develop advanced materials with prominent pseudoelasticity and self-healing effect.
Results
Spontaneous detwinning
High-energy twin boundaries are generally deemed to reduce the stability of deformation twins. When a W single crystal was loaded as shown in Fig. 1a, a deformation twin was formed near the edge of the pillar. It is worth noting a large portion of the twinned region was filled with Moiré fringes (MF) (Fig. 1b, c). The MF is formed by overlapping of the twinned and matrix lattices11 as is proved by the diffraction analysis of the MF pattern shown in Supplementary Fig. 1A, indicating that the twin has not fully propagated along the crystal thickness direction. Therefore, there should exist an inclined twin boundary, which is nonparallel to the twinning plane between the twin and matrix in the overlapped region. This inclined twin boundary is fundamentally different from the traditional twin boundary–CTB and the MF region should coincide with the projection of this inclined twin boundary in the current viewing direction. Finally, a deformation twin with ~70% MF region was formed after the fracture of the pillar, whereas no contact existed between two fractured crystals after 496 s (Fig. 1d), excluding any loading effect on the following structural changes. Subsequently, a peculiar phenomenon, spontaneous detwinning of this twin occurred and proceeded steadily, as shown in Fig. 1e–l. The reduction of the MF region indicates the gradual retraction of the inclined twin boundary and the transformation from bulgy to flat-shaped twin boundaries is supposed to lower the interface energy12 (Fig. 1e–g). The length of the twin decreased quickly from 13.7 nm to 10.9 nm before 121 s (Fig. 1g) and then changed slowly when the size of inclined twin boundary has decreased significantly (Fig. 1h–j). The twin tip as the vertical front of the twin spontaneously retracted towards the bottom surface and the twin vanished quickly when the twin became very small and close to the surface (Fig. 1k, l). Detailed detwinning process could be found in Supplementary Movie 1.
Steps (marked in Fig. 1e) were often found on the inclined twin boundaries, which were regarded as the trace of the gliding of twinning partials on the CTB13. These steps disappeared during the detwinning (Fig. 1f), indicating that the reverse motion of twinning partials along CTB contributed partly to the self-detwinning process. Some parts of the inclined twin boundary moved relatively faster than others, as marked by the yellow arrow in Fig. 1e, which may result from the structural inhomogeneity along the inclined twin boundary. The detwinning process eliminated the twinned structure and strain, recovering the perfect lattice (Fig. 1l).
Electron beam irradiation is suspected to affect the twin boundary structures and migration of the twin boundaries14,15. To exclude this effect, beam-blanked experiments were carried out (see Supplementary Fig. 2). The retraction of the MF region still occurred and the twin disappeared after 40 min without the continuous electron beam exposure, implying that the observed detwinning process is intrinsic. Abundant of molecular dynamics (MD) simulations show that the driving force for detwinning during unloading in Bcc nanowires is attributed to the large surface energy difference between the {110} and {100} facets16,17. Here, our experiments show that spontaneous detwinning we discovered was very likely driven by the high energy of the inclined twin boundary rather than external effects.
Profound differences in the structure of twin boundaries in Bcc tungsten and Fcc silver
Interestingly, the existence of inclined twin boundaries in deformation twins is a common phenomenon in tungsten. Figure 2 shows representative deformation twins in Bcc (tungsten-W) and Fcc metals (silver, Ag) when both of them were viewed along the <110> direction parallel to the twin plane (i.e., CTB). Compared with the sharp twin boundaries in Ag (Fig. 2c), there exist a lot of inclined twin boundaries (see the MF patterns) near the CTB and the twin tip in W (Fig. 2a, b, respectively). The diffraction analyses of the Moiré fringe patterns in Fig. 2a, b are shown in Supplementary Fig. 1B, C. The MF patterns usually formed during twinning process under loading. Examples of MF forming under compression and tension can be found in Supplementary Fig. 3 and Supplementary Movies 2 and 3. The profile of the MF region is usually flexuous and irregular, implying that the slope of the inclined twin boundary is diversified. As a result, the detailed structure of this inclined interface cannot be determined directly by the projection view provided by the TEM image. The detailed three-dimensional (3D) structure of the inclined twin boundary needs to be studied by future advanced experiments and simulations. However, as a non-CTB, strong lattice distortion is deemed to exist near the inclined twin boundary, giving rise to higher strain energy compared with the CTB18. In addition, the shear strain within the matrix right in front of the twin tip provides an additional driving force for the detwinning.
Statistical analysis shows that >90% of the twins found in Bcc W possess the inclined twin boundaries (Fig. 1d). Moreover, the area fractions of MF region in deformation twins are also calculated (see Supplementary Fig. 4 for details). Most of the twins with over 90% MF counted here were captured during loading. By contrast, no MF formed in Ag crystal and the CTB is very sharp. The twin tip is usually bounded by an incoherent twin boundary parallel to the {112} plane, where the periodic stacking of twinning partials could lead to zero macro-strain19,20 (e.g., Supplementary Fig. 5A in Pt), and thus remarkably reduce the extra energy cost over the CTB energy21. Representative deformation twins in platinum and gold can be found in Supplementary Fig. 5. Admittedly, some distorted twin boundaries with MF were occasionally found in Fcc metals with low stacking-fault energies, which especially underwent severe plastic deformation, which might be induced by the operation of the pole mechanism that is hardly activated in Bcc metals 1.
The proportion of the inclined twin boundary on detwinning
The proportion of the inclined twin boundary plays an important role in the instability of deformation twins and detwinning in W, and most captured spontaneous detwinning happened in twins with over 70% MF region. As shown in Fig. 3a–d, detwinning proceeded quickly in the twin enriched in MFs, especially in the first 28 s, and completed after 62 s. This trend was also observed in Fig. 1, where the detwinning rate (i.e., the rate of reduction in the twin area) kept decreasing with the shrinking area of the MF (Fig. 3e), implying that the instability of the twin in Bcc metals is closely associated with the proportion of inclined twin boundaries. It is noteworthy that the abnormal increase in the detwinning rate after 1681.5 s in Fig. 3e can be attributed to the increasing imaging force22 acting on the twinning dislocations as they approached the surface (Fig. 1g, h). Similarly, detwinning could be facilitated when the twin was very small and near the surface, such as the self-detwinning processes observed in tiny twins as shown in Supplementary Fig. 6.
To further quantify the effect of inclined twin boundary on the stability of twins, the dependence of the average detwinning rate on the inclined twin boundary in twins with similar sizes (2–10 nm) was investigated, as shown in Fig. 3. Here, the detwinning rate is defined as the average changing rate of the twin area. Clearly, the detwinning rate increases with the MF area fraction. When the percentage of MF region is lower than ~60%, the deformation twins kept stable without obvious spontaneous detwinning after 30 min (Supplementary Fig. 7). This indicated the instability of the twin structure increases with the proportion of inclined twin boundaries and the interface energy of the inclined twin boundary provides the main driving force for detwinning.
Discussion
The thermodynamic instability of deformed structures is largely decided by the excess energy compared with the perfect structure. For deformation twins, the excess energy is mainly from the interface energy of twin boundaries and the shear strain induced by twinning. The shear strain also induces the reorientation of the single crystal leading to the surface energy difference between the pristine crystal and deformed counterpart16. These excess energies provide the driving force for detwinning. MD simulation indicated that high-energy interfaces rather than coherent twin boundaries could induce the detwinning in Bcc nanowires during unloading17, consistent with our experimental observation.
As shown in Supplementary Fig. 3, the formation of the inclined twin boundary in Bcc metals is associated with the twinning process. One possible reason is the proposed double-cross-slip-assisted twinning process23. In the current study, we note that the propagation of twinning partials is very slow, which could be another factor contributing to the formation of inclined twin boundaries. Compared with the high glide velocity of twinning partials in Fcc metals24, the lattice friction is very high for dislocation slip in Bcc metals, especially for screw dislocations25,26,27. Besides, the twinning partials are deemed to be formed by the dissociation of full screw dislocations28, which move slowly through a kink-pair mechanism in Bcc metals29. In addition, kinks like small steps in screw parts of the twinning partial may increase the lattice distortion near the inclined twin boundary and its complexity further. Moreover, twinning partials nucleated from the surface are subjected to higher resistance when propagating to the thicker region and thus demonstrated lower mobility30, which increases the probability to form the inclined twin boundary. In addition, previous simulation results31,32 indicated that the Peierls stress of the screw partial is much higher than that of the edge partial. Furthermore, the prominent mobility difference between screw and edge partials is supposed to contribute to the formation of the curvy dislocation lines on the inclined twin boundary.
The instability of deformation twins and the high interface energy of the inclined twin boundary likely originate from the curved twinning partials in Bcc crystals. As shown in Fig. 4a, a group of curved twinning partials pile on parallel twinning planes (marked with (112)) in the nanocrystal due to the partial penetration of the partial dislocation, forming a 3D inclined twin boundary (the gray hook surface) and thus the corresponding MF region (cyan region in Fig. 4b) when viewed along the electron beam direction of [1-10]. To understand the detwinning mechanism, we further analyzed the dynamic behavior of twinning partials quantitatively. Due to the complex morphology and the core structure of the curved twinning partial, one simplified model was developed, as schematically shown in Supplementary Figs. 8C and 9A. Each 1/6[11-1] twinning partial was treated as a half-circle dislocation loop subject to four types of forces when external forces are absent, i.e., the restoring force \(F_{{\mathrm{{restore}}}}\) due to the curvature of the dislocation line, \(F_{{\mathrm{{SF}}}}\) due to the stacking-fault formation in crystals33, the positive and negative image forces, \(F_{{\mathrm{{image}}}}^ +\) and \(F_{{\mathrm{{image}}}}^ -\), respectively, originating from the opposite surfaces, and the friction force \(F_{{\mathrm{{friction}}}}\) due to the lattice resistance, as shown in Fig. 4c and Supplementary Fig. 9A. \(F_{{\mathrm{{restore}}}}\) reflects the strain induced by the curvature of the dislocation line and thus the elevated energy of the inclined twin boundary, whereas \(F_{{\mathrm{{SF}}}}\) for one individual twinning dislocation results from the existence of the stacking fault in the interior of the nanocrystal. Considering the formation of MF via the stacking of multiple twinning dislocation on different twinning planes, the drag force due to the existence of the twin with two twin boundaries is \(2F_{{\mathrm{{twin}}}\,{\mathrm{{fault}}}}\) (the twin fault force)33. It is noteworthy that F is defined as the force applied per unit length of the dislocation line in our analysis. The detailed calculation can be found in the Supplementary Discussion. Based on the analytical model, there exists a critical area fraction of MF fc above which the average net force \(\bar F_{{\mathrm{{total}}}}\) on the twin is positive (Supplementary Fig. 10), providing the driving force for spontaneous detwinning. We found that except in cases where twinning partials are located extremely close to the surface (e.g., <5 nm distance to the surface, as shown in Supplementary Fig. 11), the image force is trivial compared with the twin fault force or stacking-fault force—the property that is intrinsic to materials, indicating that the detwinning phenomenon and mechanism observed in W nanocrystals could be inherent to Bcc metals regardless of specimen size. Although the assumed geometry of the dislocation line is related to the sample size in the analytical model, the curvature of the dislocation line, which determines the restoring force and influences the structure of the inclined twin boundary in the actual materials is closely associated with the mobility of dislocations, especially for Bcc materials. Given that in bulk materials, the driving force for detwinning is mainly determined by (2\(F_{{\mathrm{{twin}}}\,{\mathrm{{fault}}}}\) + Frestore − Ffriction), the detwinning behavior in Bcc metals should be material dependent, and those with relatively high stacking-fault and twin-boundary energies are more likely to demonstrate low stability in deformation twins.
The unstable twin structure can significantly influence the mechanical properties of Bcc metals, especially in small-sized Bcc metals where deformation twinning becomes a competing deformation mode against dislocation plasticity due to their comparable activation stresses9,34,35. Massive inclined twin boundaries with high interface energy formed during deformation make it difficult to induce continuous and steady twinning networks in Bcc metals. This also gives little chances to induce secondary twinning. Moreover, the inclined twin boundary as the high-energy interface provides opportunities to accumulate the mechanical energy during plastic deformation and twinning, which, followed by subsequent self-detwinning, makes small-sized Bcc metals potentially applicable for microdevices with the ability of storage and release of mechanical energy36 with considerable conversion efficiency. Besides, the excellent pseudoelasticity enabled by unstable twin is different from that by phase transformation37,38 or surface diffusion39,40, which makes materials recoverable to the initial structure even when they are deformed over the elastic limit41. In addition, self-detwinning in Bcc metals helps remove the plastic strain and may heal the “wound” induced by twinning. Consecutive twinning and detwinning during cyclic loadings might provide the pathway to bear the fatigue deformation and improve the fatigue life of Bcc metals42. These findings provide assistance for making Bcc nanomaterials with magnificent properties applicable in micro-electro-mechanical systems.
In conclusion, unstable twin in Bcc nanocrystals was revealed by capturing atomic-scale self-detwinning process through in-situ TEM experiments. In addition, the intrinsic instability of twin in Bcc metals is related to the inclined twin boundary with high interfacial energy that provides the driving force for spontaneous detwinning. The formation of inclined twin boundaries might be contributed to the low mobility of twinning partials in Bcc metals and the geometry of the twinning grain. The high proportion of inclined twin boundaries would facilitate complete detwinning. These findings offer new insights for understanding deformation twinning in Bcc metals, as well as guidelines for processing new structural and functional materials. For unstable twin structures, adding appropriate alloy elements may lower the interface energy and stabilize the twin and dislocation structure43, which provides possibilities to improve properties of Bcc metals by implanting high-density nanotwins.
Methods
Materials and in-situ experiment
Tungsten polycrystalline rods with diameter 0.013 inch (bought from ESPI Metal) used in the experiment and the metal purity is 99.98 wt.%. In-situ deformation tests were operated on a Nanofactory scanning tunneling microscopy inside a FEI Titian 80-300Kv TEM. The nanocrystal preparation method is referred in ref. 9, through welding two nano-tips together to form a nanocrystal bridge. When fracture occurred on the boundary between the nanocrystal and the substrate, as well as of the connection site, there is only physical contact and no chemical bonding between the indenter and the nanocrystal in the later compression loading, making the indenter touch the nanocrystal again. The strain rate is controlled by adjusting the displacement rate of the probe side with a piezo-manipulator and a common rate is about 10−3 s−1.
Data availability
All data needed to evaluate the conclusions in the paper are present in the paper and/or the Supplementary Information.
References
Christian, J. W. & Mahajan, S. Deformation twinning. Prog. Mater. Sci. 39, 1–157 (1995).
Lei, L., Yongfeng, S., Xianhua, C., Lihua, Q. & Lu, K. Ultrahigh strength and high electrical conductivity in copper. Science 304, 422–426 (2004).
Lu, K., Lu, L. & Suresh, S. Strengthening materials by engineering coherent internal boundaries at the nanoscale. Science 324, 349–352 (2009).
Lu, L., Chen, X., Huang, X. & Lu, K. Revealing the maximum strength in nanotwinned copper. Science 323, 607–610 (2009).
Zhang, X. & Misra, A. Superior thermal stability of coherent twin boundaries in nanotwinned metals. Scr. Mater. 66, 860–865 (2012).
Vítek, V. Intrinsic stacking faults in body-centred cubic crystals. Philos. Mag. 18, 773–786 (1968).
Ogata, S., Li, J. & Yip, S. Energy landscape of deformation twinning in bcc and fcc metals. Phys. Rev. B 71, 224102 (2005).
Hsiung, L. & Lassila, D. Shock-induced deformation twinning and omega transformation in tantalum and tantalum–tungsten alloys. Acta Mater. 48, 4851–4865 (2000).
Wang, J. et al. In situ atomic-scale observation of twinning-dominated deformation in nanoscale body-centred cubic tungsten. Nat. Mater. 14, 594 (2015).
Wei, S., Wang, Q., Wei, H. & Wang, J. Bending-induced deformation twinning in body-centered cubic tungsten nanowires. Mater. Res. Lett. 7, 210–216 (2019).
Meadows, D., Johnson, W. & Allen, J. Generation of surface contours by moiré patterns. Appl. Opt. 9, 942–947 (1970).
Gutierrez-Urrutia, I. et al. Twinning and detwinning mechanisms in a BCC Ti Mo-Fe multilayered alloy. In IOP Conference Series: Materials Science and Engineering 219, 012042 (IOP Publishing, 2017).
Zhu, Y. et al. Dislocation–twin interactions in nanocrystalline fcc metals. Acta Mater. 59, 812–821 (2011).
Song, D., Li, X., Xue, J., Duan, H. & Jin, Z. Irradiation-enhanced twin boundary migration in BCC Fe. Philos. Mag. Lett. 94, 361–369 (2014).
Li, N. et al. Incoherent twin boundary migration induced by ion irradiation in Cu. J. Appl. Phys. 113, 023508 (2013).
Cao, A. Shape memory effects and pseudoelasticity in bcc metallic nanowires. J. Appl. Phys. 108, 113531 (2010).
Yang, Y., Li, S., Ding, X., Sun, J. & Salje, E. K. Interface driven pseudo‐elasticity in a‐Fe nanowires. Adv. Funct. Mater. 26, 760–767 (2016).
Yamaguchi, M. & Vitek, V. Twin boundaries and incoherent steps on twin boundaries in body-centered-cubic metals. Philos. Mag. 34, 1–11 (1976).
Wang, J. et al. Detwinning mechanisms for growth twins in face-centered cubic metals. Acta Mater. 58, 2262–2270 (2010).
Wang, J., Anderoglu, O., Hirth, J. P., Misra, A. & Zhang X. Dislocation structures of Σ3 {112} twin boundaries in face centered cubic metals. Appl. Phys. Lett. 95, 021908 (2009).
Schmidt, C., Finnis, M., Ernst, F. & Vitek, V. Theoretical and experimental investigations of structures and energies of Σ= 3,[112] tilt grain boundaries in copper. Philos. Mag. A 77, 1161–1184 (1998).
Weinberger, C. R. & Cai, W. Surface-controlled dislocation multiplication in metal micropillars. Proc. Natl Acad. Sci. USA 105, 14304–14307 (2008).
Chen, C., Florando, J., Kumar, M., Ramesh, K. & Hemker, K. Incipient deformation twinning in dynamically sheared bcc tantalum. Acta Mater. 69, 114–125 (2014).
Kibey, S., Liu, J., Johnson, D. & Sehitoglu, H. Predicting twinning stress in fcc metals: Linking twin-energy pathways to twin nucleation. Acta Mater. 55, 6843–6851 (2007).
Weinberger, C. R., Battaile, C. C., Buchheit, T. E. & Holm, E. A. Incorporating atomistic data of lattice friction into BCC crystal plasticity models. Int. J. Plasticity 37, 16–30 (2012).
Weinberger, C. R., Tucker, G. J. & Foiles, S. M. Peierls potential of screw dislocations in bcc transition metals: predictions from density functional theory. Phys. Rev. B 87, 054114 (2013).
Greer, J. R., Weinberger, C. R. & Cai, W. Comparing the strength of fcc and bcc sub-micrometer pillars: compression experiments and dislocation dynamics simulations. Mater. Sci. Eng. A 493, 21–25 (2008).
Sleeswyk, A. ½<111> screw dislocations and the nucleation of {112}<111> twins in the bcc lattice. Philos. Mag. 8, 1467–1486 (1963).
Marian, J., Cai, W. & Bulatov, V. V. Dynamic transitions from smooth to rough to twinning in dislocation motion. Nat. Mater. 3, 158–163 (2004).
Dutta, A. et al. Lattice resistance to dislocation motion at the nanoscale. Phys. Rev. Lett. 101, 115506 (2008).
Ogata, S., Li, J. & Yip, S. Twinning pathway in BCC molybdenum. Europhys. Lett. 68, 405 (2004).
Ostapovets, A. & Paidar, V. Evaluation of the Peierls stress for boundary dislocations. The. Phys. Met. Metallogr. 111, 229–235 (2011).
Li, B. Q., Sui, M. L., Li, B., Ma, E. & Mao, S. X. Reversible twinning in pure aluminum. Phys. Rev. Lett. 102, 205504 (2009).
Chen, M. et al. Deformation twinning in nanocrystalline aluminum. Science 300, 1275–1277 (2003).
Zhu, Y. T. et al. Nucleation and growth of deformation twins in nanocrystalline aluminum. Appl. Phys. Lett. 85, 5049–5051 (2004).
Li, S. et al. High-efficiency mechanical energy storage and retrieval using interfaces in nanowires. Nano Lett. 10, 1774–1779 (2010).
Otsuka, K., Sakamoto, H. & Shimizu, K. Successive stress-induced martensitic transformations and associated transformation pseudoelasticity in Cu-Al-Ni alloys. Acta Metall. 27, 585–601 (1979).
Miyazaki, S., Ohmi, Y., Otsuka, K. & Suzuki, Y. Characteristics of deformation and transformation pseudoelasticity in Ti-Ni alloys. Le. J. de. Phys. Colloq. 43, C4–255 (1982).
Sun, J. et al. Liquid-like pseudoelasticity of sub-10-nm crystalline silver particles. Nat. Mater. 13, 1007–1012 (2014).
Gu, X. W., Hanson, L. A., Eisler, C. N., Koc, M. A. & Alivisatos, A. P. Pseudoelasticity at large strains in Au nanocrystals. Phys. Rev. Lett. 121, 056102 (2018).
Delaey, L., Krishnan, R., Tas, H. & Warlimont, H. Thermoelasticity, pseudoelasticity and the memory effects associated with martensitic transformations. J. Mater. Sci. 9, 1521–1535 (1974).
Pan, Q., Zhou, H., Lu, Q., Gao, H. & Lu, L. History-independent cyclic response of nanotwinned metals. Nature 551, 214 (2017).
Nie, J., Zhu, Y., Liu, J. & Fang, X. Periodic segregation of solute atoms in fully coherent twin boundaries. Science 340, 957–960 (2013).
Acknowledgements
S.X.M. acknowledges support from the National Science Foundation CMMI 1760916 through University of Pittsburgh. This work was performed, in part, at the William R. Wiley Environmental Molecular Sciences Laboratory, a national scientific user facility sponsored by U.S. Department of Energy, Office of Biological and Environmental Research, and located at PNNL. PNNL is operated by Battelle for the U.S. Department of Energy under contract DE-AC05-76RLO1830.
Author information
Authors and Affiliations
Contributions
S.X.M. conceived the project. X.W. carried out the TEM experiments under the direction of S.X.M. and C.M.W. X.W and L.Z. analyzed the data. X.W., L.Z., and S.X.M. wrote the manuscript. J.W and Y.H. contributed to the discussion and revision of the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Changqiang Chen, Kelvin Xie and the other anonymous reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, X., Wang, J., He, Y. et al. Unstable twin in body-centered cubic tungsten nanocrystals. Nat Commun 11, 2497 (2020). https://doi.org/10.1038/s41467-020-16349-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-16349-8
- Springer Nature Limited
This article is cited by
-
Atomic-scale observation of nucleation- and growth-controlled deformation twinning in body-centered cubic nanocrystals
Nature Communications (2024)
-
Atomistic study on the microscopic mechanism of grain boundary embrittlement induced by small dense helium bubbles in iron
Nuclear Science and Techniques (2024)
-
Twinning dominated microstructural evolution in tungsten under impact loading
Journal of Materials Science (2024)
-
Ultra-strong tungsten refractory high-entropy alloy via stepwise controllable coherent nanoprecipitations
Nature Communications (2023)
-
{112} 〈111〉 Twins or Twinned Variants Induced by Martensitic Transformation?
Acta Metallurgica Sinica (English Letters) (2023)