Highlights
-
The acid etching Co-naphthalenedicarboxylic acid-based metal–organic frameworks (donated as AE-CoNDA) catalyst displayed an excellent oxygen evolution reaction (OER) activity for long-term stability.
-
Integration of the AE-CoNDA cocatalyst into BiVO4 achieved a remarkable PEC-OER activity.
-
The stretched Co-O bond length regulated the spin state transition at the Co active sites.
-
The optimized high spin state of Co sites adjusted the orbitals hybridization of Co 3d and O 2p.
Abstract
Metal–organic frameworks (MOFs) have been developed as an ideal platform for exploration of the relationship between intrinsic structure and catalytic activity, but the limited catalytic activity and stability has hampered their practical use in water splitting. Herein, we develop a bond length adjustment strategy for optimizing naphthalene-based MOFs that synthesized by acid etching Co-naphthalenedicarboxylic acid-based MOFs (donated as AE-CoNDA) to serve as efficient catalyst for water splitting. AE-CoNDA exhibits a low overpotential of 260 mV to reach 10 mA cm−2 and a small Tafel slope of 62 mV dec−1 with excellent stability over 100 h. After integrated AE-CoNDA onto BiVO4, photocurrent density of 4.3 mA cm−2 is achieved at 1.23 V. Experimental investigations demonstrate that the stretched Co–O bond length was found to optimize the orbitals hybridization of Co 3d and O 2p, which accounts for the fast kinetics and high activity. Theoretical calculations reveal that the stretched Co–O bond length strengthens the adsorption of oxygen-contained intermediates at the Co active sites for highly efficient water splitting.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Developing efficient and durable cocatalysts is regarded as one of the most significant efforts in promoting photoelectrochemical (PEC) water splitting [1,2,3,4,5]. Compared with the cathodic hydrogen evolution reaction (HER) [6], the sluggish reaction kinetics [7, 8] and complicated four-electron transfer pathway [9,10,11,12] for the anodic oxygen evolution reaction (OER) remain a major bottleneck to limit their commercial uses [13,14,15]. While various strategies have been developed to accelerate sluggish reaction kinetics for the OER, its performance and stability still need to be compromised [16,17,18].
Recently, various oxygen evolution cocatalysts (OECs) [19,20,21,22] have been exploited to obtain desired PEC-OER performance [23]. Traditional OECs often exhibited ill-defined structures undesirable for mechanistic studies. Fortunately, metal–organic frameworks (MOFs) with well-defined crystal structures [24, 25] and abundant exposed active sites [26,27,28] are ideal for investigating the intrinsic structure and catalytic activity relationship [29,30,31]. Up to date, several researchers developed MOF materials decorated photoelectrode, such as MOF-BiVO4, to improve PEC-OER activity; however, their conductivity and catalytic stability are invariably unsatisfied. MOFs materials as precursors often need to be converted into carbon-based OECs via high-temperature calcination, thus causing severe structure collapse and metal agglomeration [32, 33]. Therefore, it is highly desirable to develop uncarbonized MOFs materials as active and durable OECs through rational modification [34].
For the OER processes in alkaline, it typically involves a four-electron transfer pathway and complicated deprotonation process of oxygen-contained intermediates (e.g., OH*, O*, and OOH*) [35]. Conventional MOFs materials usually contain saturated coordinated metal nodes that are unfavorable for adsorption of oxygen-contained intermediates. In addition, the framework structure of traditional MOFs is vulnerable to severe collapse under harsh condition. Thereby, it is important to modify the crystal structure of MOFs for boosting the OER activity and enhancing photoelectrode’s stability. Like the natural enzyme structure [24], distorted structure of catalyst has an effect on electronic spin configuration of metal sites, which is closely associated with the binding energy for oxygen-contained intermediates on the metal sites. Compared to thermal-induced or photoinduced method, acid etching is simplicity of operation and easily control distorted degree.
In particular, a bond length adjustment strategy was represented to regulate the intrinsic electronic structure of Co-2,6-naphthalenedicarboxylic acid-based MOFs (AE-CoNDA) catalyst by acid etching treatment. The AE-CoNDA catalyst showed a superior OER performance and rapid kinetics in alkaline media, featured by a low overpotential of 260 mV to reach 10 mA cm−2 and a small Tafel slope of 62 mV dec−1. Integration of the AE-CoNDA cocatalyst into a BiVO4 for solar water splitting led to an AM 1.5G photocurrent density of 4.30 mA cm−2 at 1.23 V, which outperformed the PEC-OER performance for most reported Co-based BiVO4 photoanodes (Table S1). Experimental results verified that the electronic structure on the Co active center in the AE-CoNDA was reconfigured by the bond length adjustment. An optimized bond length corresponded to the spin state transition from an intermediate spin (eg1t2g6) to a high spin (eg2t2g5) at the Co active site, facilitating the oxygen-contained intermediates adsorption. Theoretical calculations uncovered the optimized adsorption energy between the metal sites with optimal bond length and oxygen-contained intermediates for enhancing the OER performance.
2 Experimental Procedures
2.1 Synthesis of AE-CoNDA
2,6-naphthalenedicarboxylic acid (2,6-NDA, 172.9 mg) and CoCl2·6H2O (190.2 mg) were dissolved in a mixed solution containing 32-mL dimethyl formamide (DMF), 2-mL ethanol, and 2-mL deionized water. Thereafter, 1.0-mL triethylamine (TEA) was injected into the above solution mixture under vigorous stirring to form a uniform colloidal suspension. The formed suspension was sealed and further ultrasonicated for 300 min at 70 kHz and room temperature. The obtained sample was further immersed in a 0.2-mM acetic acid solution for acid etching. The resultant precipitate was washed with DMF and ethanol for three times, and dried in vacuum oven at 60 °C.
2.2 Characterization
Morphologies of the as-prepared samples were obtained on a field emission scanning electron microscopy (FESEM) (Hitachi SU-8010), transmission electron microscopy (TEM) (HT7700), and high-resolution transmission electron microscopy (HR-TEM) (JEOL JEM-2001F). The crystal structures of the as-prepared samples were analyzed by X-ray powder diffraction (XRD) (Empyrean 200,895) using Cu Kα radiation. Chemical structures of the as-prepared samples were measured by X-ray photoelectron spectroscopy (XPS, Escalab250Xi) with Al Kα radiation. Raman spectra were obtained by a LabRAM HR Evolution unit. The metal content in samples was analyzed by inductively coupled plasma mass spectrometry (ICP-MS) (Vista Axial). The X-ray absorption spectroscopic (XAS) measurements of the as-prepared samples were conducted in Beijing Synchrotron Radiation Facility and Taiwan Synchrotron Radiation Facility. Quantum Design MPMS-7 superconducting quantum interference device (MPMS-VSM) magnetometer was utilized to obtain the magnetic properties of the as-prepared catalysts. The electron paramagnetic resonance (EPR) data of the as-prepared catalysts were acquired on a Bruker EMXmicro.
2.3 Electrochemical Measurements
All electrochemical measurements were carried out by an electrochemical analyzer (CHI 760E) in a typical three-electrode cell. A saturated calomel electrode (SCE, CH Instruments) was used as the reference electrode, and a graphite rod was used as the counter electrode. The potential was converted to reversible hydrogen electrode (RHE) via a Nernst equation (ERHE = ESCE × 0.244 V + 0.0591 × pH). To evaluate the OER activities, the scan rate of linear sweep voltammetry (LSV) was set as 1.0 mV s−1 with the potentials from 1 to 1.8 V vs. RHE in 1.0 M KOH. Electrochemical impedance spectroscopy (EIS) was measured at 1.5 V vs. RHE with a frequency range from 105 to 0.01 Hz. All polarization curves were calibrated with iR correction unless noted. Cyclic voltammetry cycles (CVs) at 0.96–1.06 V vs. RHE with the scan rates from 10 to 50 mV s−1 were applied.
2.4 PEC-OER Measurements
The PEC-OER measurements were conducted with a front-side illumination in all cases (light enters from the absorber side). A saturated calomel electrode (SCE, CH Instruments) and a Pt wire were used as reference electrode and counter electrode, respectively. The recorded potential vs. SCE (ESCE) was converted against RHE using the Nernst equation (ERHE = ESCE × 0.244 V + 0.0591 × pH). A 1.0 M potassium borate buffer, prepared by adjusting the pH of 1.0 M H3BO3 to 9.0 with KOH solution, was used as the electrolyte. The stability of photoanode was evaluated by measuring curves of the potential vs. time at 1.0, 2.0, and 2.5 mA cm−2.
2.5 Computational Methods
All spin-polarized density functional theory (DFT) calculations were performed with Vienna Ab initio Simulation Package (VASP). In this work, the generalized gradient approximation (GGA) within Perdew–Burke–Ernzerhof (PBE) method was used to describe the exchange–correlation interaction. The core electrons were replaced by the projector augmented wave (PAW) pseudopotential, and 450-eV plane-wave expansion was setup for energy cut-offs. The k-points sampling was set to 1 × 1 × 1 Monkhorst–Pack k-points grid for geometrical optimization and that of electronic property calculation was 1 × 1 × 2. The convergence threshold was set to 10–5 eV and 0.05 eV Å−1 for energy and force, respectively. Weak interaction was described by DFT-D3 method using empirical correction in Grimme’s scheme.
The (1 × 2) surface of bulk CoNDA (100) was chosen, which contains 16 Co atoms, 83 O atoms, 96 C atoms, and 64 H atoms. A vacuum slab of about 15 Å was maintained in the super-cell configuration that was large enough for the calculations. To simulate the tensile state of structure, tensile CoNDA structure was constructed by expanding the lattice parameters of the pristine CoNDA in three directions by 5%.
3 Results and Discussion
3.1 Solar-driven Water Oxidation Activity of AE-CoNDA@BiVO4
AE-CoNDA as cocatalyst was synthesized by ultrasonic exfoliation of a mixed solution of CoCl2·6H2O, 2,6-NDA, and DMF, followed by acid etching at a predetermined concentration of acetic acid. The AE-CoNDA@BiVO4 was assembled by spraying the AE-CoNDA ink on BiVO4, as illustrated in Fig. S1. Morphological images (Figs. S2–S5) exhibited that the AE-CoNDA and control samples uniformly coated on the nanoworm-like BiVO4 surface. Especially, the HR-TEM image of AE-CoNDA@BiVO4 (Fig. S2) exhibits a lattice fringe of 1.18 nm for the interlayer spacing distance of naphthalene-based MOF with transition metal nodes along the [100] direction, which assigned to AE-CoNDA. In addition, in XRD pattern (Fig. S6), the diffraction peak below 10° stands for crystalline MOF structure, indicating that the AE-CoNDA is highly crystallized. Raman spectra (Fig. S7) also show obvious characteristic peaks which assigned to naphthalene-based MOF. Above results confirmed that AE-CoNDA was highly crystallized and successfully deposited on BiVO4 photoelectrode.
To demonstrate the catalytic performance, we first investigated PEC water oxidation property of AE-CoNDA@BiVO4 in alkaline electrolyte under AM 1.5G irradiation, as illustrated in Fig. 1a. The optimized AE-CoNDA@BiVO4 delivered a high photocurrent density of 4.30 mA cm−2 at 1.23 V (Figs. 1b and S8), which was much greater than that for BiVO4 alone (1.30 mA cm−2 at 1.23 V) and CoNDA@BiVO4 (3.20 mA cm−2 at 1.23 V). In addition, the AE-CoNDA@BiVO4 possessed a maximum incident photon-to-current conversion efficiency (IPCE) of 54.0% at 400 nm at 1.23 V (Fig. 1c), which was about 1.6 and 1.3 times higher than that of bare BiVO4 (33.0%) and CoNDA@BiVO4 (43.0%), respectively. AE-CoNDA@BiVO4 showed the maximum photon-to-current efficiency (ABPE) of 1.61% at 0.6 V (Fig. 1d), which was superior to that of BiVO4 (0.82% at 0.78 V) and CoNDA@BiVO4 (1.12% at 0.6 V). The lower charge transfer resistance for the AE-CoNDA@BiVO4 than that of CoNDA@BiVO4 and BiVO4 alone under light irradiation demonstrated that more effective interfacial charge transfer occurred at the AE-CoNDA@BiVO4 interface (Fig. S9). Moreover, clearly, it was seen that after introduction of AE-CoNDA, both charge transfer efficiency (ηtransfer) and charge transport efficiency (ηtransport) of AE-CoNDA@BiVO4 (Figs. S10–S13) increased throughout the whole potential range. The product analyses revealed that the generated photocurrent was mainly from the O2 production on AE-CoNDA@BiVO4 rather self-corrosion of photoelectrode (Fig. 1e). Besides, the potential on AE-CoNDA@BiVO4 was not raised for at least 50 h to maintain photocurrent density at 2.5 mA cm−2 (Fig. 1e), which is much durable than CoNDA@BiVO4 under 1.5 mA cm−2 and BiVO4 under 1.0 mA cm−2 (Fig. S14). Notably, the observed PEC-OER activity for AE-CoNDA@BiVO4 was regarded as an extreme high record among all reported Co-based BiVO4 hybrid photoanodes (Fig. 1f and Table S1). To further support the enhancement of photo-generated charge carrier transfer efficiency of BiVO4 after integrating AE-CoNDA cocatalyst, operando-irradiated XPS measurements [35, 36] were conducted (Fig. S15). The results revealed that the holes transferred from BiVO4 to AE-CoNDA cocatalyst occurred.
3.2 Vital Role of AE-CoNDA as Cocatalyst
To probe the crucial role of AE-CoNDA as cocatalyst, the OER performance of AE-CoNDA was further evaluated in a three-electrode cell in 1.0 M KOH solution. The control samples with different reaction conditions were also synthesized to investigate the contribution of acetic acid etching. The optimal etching time was found to be 1.0 h, and optimal concentration of acetic acid was 0.2 mM (Figs. S16–S18). As shown in Fig. 2a, the as-prepared AE-CoNDA delivered only a low overpotential of 260 mV to reach a current density of 10 mA cm−2. Compared to the CoNDA without acid etching (360 mV), this result highlights the significant role of acid etching in enhancing the OER performance. Notably, the overpotential for the AE-CoNDA was even smaller than that of the benchmark Ir/C (330 mV) at the same current density, demonstrating the excellent OER activity for the former. The fast reaction kinetics of AE-CoNDA was further underscored by its smaller Tafel slope (62 mV dec−1) than that of CoNDA with 82 mV dec−1, and even commercial Ir/C with 97 mV dec−1, respectively (Fig. 2b). The AE-CoNDA further exhibited a much smaller electrochemical resistance (Rct) (Fig. S19 and Table S2) than that of the CoNDA, implying a fast charge transfer for AE-CoNDA. The ratio of inner charge to outer charge density for AE-CoNDA was calculated to be 94.5 (Figs. 2c and S20), which was much higher than that of CoNDA (52.7), as a result of the high electrochemical porosity. These results suggested that the acid etching not only increased the electrode roughness [37], but also produced abundant exposed active sites. The larger electrochemically active surface area (ECSA) of AE-CoNDA than that of CoNDA indicated the more electroactive surfaces for AE-CoNDA (Figs. S21 and S22). Moreover, the turnover frequency (TOF) of AE-CoNDA was calculated to be 18.66 h−1 at an overpotential of 0.3 V, which was approximately three times higher than the corresponding value for CoNDA (5.86 h−1) (Fig. 2d). Above results claimed that the increase in active surface area is not the main reason for the increase in the current density of the catalyst, but the intrinsic characteristics of the catalyst promote the catalytic activity of the catalyst, resulting in a higher current density.
To further validate the rapid charge transfer for AE-CoNDA, in situ EIS measurements were conducted (Table S2). The results showed that the Rct value of AE-CoNDA was much lower than that of CoNDA over a wide range of potential (Fig. 2e), indicating the fast charge transfer efficiency for AE-CoNDA. Besides, the Rct value of the AE-CoNDA became stable at low potential (1.4 V), demonstrated that the OER process was triggered at low potentials on the AE-CoNDA [38, 39]. Notably, the excellent alkaline OER performance in terms of the overpotential (260 mV at 10 mA cm−2) and Tafel slope (62 mV dec−1) for the AE-CoNDA was superior to those of almost all non-carbonized Co MOF-based OER electrocatalysts previously reported (Table S3). Moreover, the OER process on the AE-CoNDA was stable, no apparent change in the overpotential was observed over 100 h of continuous operation (Fig. 2f), which is much stable than CoNDA under same potential (Fig. S23). Especially, the XRD pattern (Fig. S24a) and Raman spectra (Fig. S24b) of AE-CoNDA after OER process remained similar curves with pristine AE-CoNDA, indicating structural stability of catalyst.
3.3 Analysis of Intrinsic Structure on AE-CoNDA
To gain the insights of superior OER activity on AE-CoNDA, we first performed XPS measurements. In the high-resolution Co 2p, O 1s, and C 1s XPS spectra (Figs. 3a, b and S25), the Co 2p XPS peaks in the AE-CoNDA displayed a higher binding energy, shifted approxiately 0.62 and 0.40 eV, while O 1s XPS peaks positively shifted 0.06 eV to higher binding energy, as the peaks of O-C = O and C–C/C = C negatively shifted to lower binding energies (Fig. S25). These results demonstrated the electrons from Co atoms within AE-CoNDA transferred to the O atoms adjacent to C atoms and ultimately located on the C atoms. To deeply investigate the fine structure of AE-CoNDA, we further conducted X-ray absorption spectroscopy (XAS). The obtained X-ray absorption near-edge structure (XANES) spectra (Fig. 3c) showed the absorption edge with an increased photon energy of Co species within the AE-CoNDA in comparison with CoNDA and Co foil, indicating a higher valence state for Co species in AE-CoNDA. Moreover, the Co L-edge XAS spectra of the AE-CoNDA (Fig. 3d) exhibited a Co absorption edge shifted to a higher photon energy relative to that of the Co foil and CoNDA, but close to that of reference CoO, suggesting the average Co valence state of + 2 for AE-CoNDA.
Figure 4a shows the corresponding Fourier transforms of extended X-ray absorption fine structure (EXAFS) of AE-CoNDA, which reveals the major peak located at 1.6 Å attributable to the nearest shell coordination of the Co–O bond. It is noteworthy that the Co–O peak of AE-CoNDA shifted toward a higher R direction by about 0.05 Å relative to that of CoNDA, indicating that the bond length of Co–O in the AE-CoNDA was stretched [35]. The stretched Co–O bond is ascribed to partial destruction of CoNDA structure and weakened interaction between Co cations and NDA ligand after acid etching. The EXAFS fitting was performed for the coordination shells in the R range of 1.0–3.0 Å. Amplitude reduction factor S02 as determined from fitting was 0.85. The EXAFS fitting results (Table S4) validated that the coordination number of Co–O bonds was determined to be smaller than 6. Additionally, as revealed by the EPR spectra (Fig. S26), an apparent signal at g-factor value of 1.86 was observed for AE-CoNDA, whose intensity was stronger than which of CoNDA, indicating more uncoupled Co centers as defects in the framework in AE-CoNDA [40]. EXAFS fitting result and EPR results proved distorted octahedral configurations and unsaturated coordinative Co species of CoO6 centers in AE-CoNDA.
To gain more insights into the electron configuration and spin state of AE-CoNDA with stretched Co–O bond length, the O K-edge XAS spectra were further analyzed. As shown in Fig. 4b, the O K-edge XAS spectra consisted of two characteristic peaks between 532.0 and 534.0 eV, arising from the hybridization between unoccupied O 2p and Co 3d orbitals. Clearly, the intensity of O K-edge from AE-CoNDA was enhanced after acid etching, indicating an increased unoccupied density of states and a strengthening orbital hybridization of O 2p and Co 3d orbitals. Such enhanced intensity in O K-edge spectra, accompanying with the Co L-edge peak for AE-CoNDA (Fig. 3d), suggests an electron reconfiguration occurred in both the O 2p and Co 3d orbitals.
It is important to notice that the electronic configuration of Co species primarily dominated the spin state of Co species. To deeply explore the spin state of Co species within AE-CoNDA, we further carried out the zero-field cooling (ZFC) temperature-dependent magnetic susceptibility tests with a magnetic property measurement system (MPMS-VSM) [41]. The total effective magnetic moment (μeff) of AE-CoNDA was obtained through χ−1-T liner fitting to calculate the eg occupancy. In Fig. 4c, the calculated μeff for AE-CoNDA and CoNDA was 3.667 and 1.935, respectively, and the number of d-orbital unpaired electrons can be further calculated by formula [42]. Thus, the eg occupancy of Co species raised from approximate 0.98 to 1.84 after Co–O bond length stretched. The calculated eg occupancy indicated more unpaired d electrons existed in the AE-CoNDA (Fig. 4d), which induced a spin state transition from an intermediate spin (eg1t2g6) to a high spin (eg2t2g5) of AE-CoNDA [43].
3.4 Theoretical Evaluation of the Enhancement Effect on OER Activity for AE-CoNDA
To give an in-depth understanding of the relationship between the spin state of Co active sites and adsorption ability of oxygen-contained intermediates, we performed DFT calculations. Firstly, a CoNDA model with short bond length and AE-CoNDA model with long bond length were established (Fig. S27). As shown in Fig. 5a, the Co active sites adsorbed oxygen-contained intermediates of OH*, O*, and OOH* through hybridization between the O 2p and Co 3d orbitals throughout the OER process. Considering that the high spin state of Co active sites was beneficial for Co 3d and O 2p orbital hybridization to facilitate the adsorption of oxygen-contained intermediates [44], we also calculated the spin-resolved density of spin (DOS). The 3d-orbital of Co sites was splitted as dx2-y2, dz2, dxy, dxz, and dyz orbitals in Fig. 5b and c. As for AE-CoNDA (Fig. 5b), the state density of dz2 (close to the Fermi level) was much stronger than that of CoNDA (Fig. 5c), demonstrating that more electrons transferred between different orbitals in AE-CoNDA. The overlapped area between the Co dz2 orbital and O 2p orbital for AE-CoNDA was larger than that for CoNDA, indicating an enhanced interaction between the Co active sites and oxygen-contained intermediates after the Co–O bond length stretching. These results demonstrated that the bond length stretching facilitated the electron transfer from the t2g orbitals to the eg orbitals, thus leading to a high spin state [40].
As displayed in Fig. 5d, the AE-CoNDA model showed an accumulated charge of O center in NDA linker from Co active sites with the stretched Co–O bond length compared to control CoNDA, indicating a rapid electron transfer for AE-CoNDA [45]. The specific free energy (ΔG) for each elementary step was calculated to estimate their OER activity at the center Co sites. In Fig. 5e, it can be clearly seen that the elementary steps for the formation of OH* and transition of OOH* to O2 desorption were down-hilled, while other reaction steps involved in the OER process for AE-CoNDA and CoNDA were up-hilled. Based on its ΔG diagram, the ΔG value for O* formation at the center Co sites decreased from 1.41 eV for CoNDA to 1.26 eV for AE-CoNDA, revealing that the spin state transition from intermediate spin to high spin led to a decrease in free energy. The application of a bias (U = 0.4 V) also caused a decrease in the ΔG of OH* to O* for AE-CoNDA compared with CoNDA (Fig. S28). Therefore, the formation of the stretched Co–O bond led to a high spin state for the Co active sites, ensuring a readily combination of the O* with the center Co sites. As a result, a reaction path from OH* to O*, which was evidenced as the rate-determined step, was significantly accelerated for AE-CoNDA (Fig. 5e).
4 Conclusion
We have developed a highly active AE-CoNDA catalyst with a stretched Co–O bond length and a high spin state. The AE-CoNDA required only a low OER overpotential of 260 mV to reach 10 mA cm−2 with a long-term stability. The AE-CoNDA and BiVO4 integrated photoanode achieved a photocurrent density of 4.30 mA cm−2 at 1.23 V under AM 1.5G irradiation, superior IPCE of 54.0%, ABPE of 1.61%, and prolonged durability in base. Extensive structural characterization verified that the spin state of the center Co sites within the AE-CoNDA was transferred from an intermediate spin state (eg1t2g6) to a high spin (eg2t2g5) by bond length stretching. The DFT calculations disclosed that the high spin state of AE-CoNDA enhanced the Co 3d and O 2p orbital hybridization, promoting the reaction kinetics for the RDS (OH* → O*). The in situ electrochemical spectroscopic results demonstrated the bond stretching in AE-CoNDA accelerated the OH* adsorption and facilitated the transfer of photoinduced electrons and holes within the AE-CoNDA@BiVO4. This work reports a creative idea for using the bond length adjustment strategy to accelerate the OER kinetics of MOFs-based catalysts, which could be applicable to various photoanodes for a variety of solar-driven applications and renewable energy conversions.
References
M. Crespo-Quesada, L.M. Pazos-Outón, J. Warnan, M.F. Kuehnel, R.H. Friend et al., Metal-encapsulated organolead halide perovskite photocathode for solar-driven hydrogen evolution in water. Nat. Commun. 7, 12555 (2016). https://doi.org/10.1038/ncomms12555
X. Yu, V.L. Zholobenko, S. Moldovan, D. Hu, D. Wu et al., Stoichiometric methane conversion to ethane using photochemical looping at ambient temperature. Nat. Energy 5, 511–519 (2020). https://doi.org/10.1038/s41560-020-0616-7
J.Z. Zhang, E. Reisner, Advancing photosystem II photoelectrochemistry for semi-artificial photosynthesis. Nat. Rev. Chem. 4, 6–21 (2020). https://doi.org/10.1038/s41570-019-0149-4
T. Bouwens, T.M.A. Bakker, K. Zhu, J. Hasenack, M. Dieperink et al., Using supramolecular machinery to engineer directional charge propagation in photoelectrochemical devices. Nat. Chem. 15, 213–221 (2023). https://doi.org/10.1038/s41557-022-01068-y
V. Andrei, G.M. Ucoski, C. Pornrungroj, C. Uswachoke, Q. Wang et al., Floating perovskite-BiVO4 devices for scalable solar fuel production. Nature 608, 518–522 (2022). https://doi.org/10.1038/s41586-022-04978-6
X. You, D. Zhang, X.-G. Zhang, X. Li, J.-H. Tian et al., Exploring the cation regulation mechanism for interfacial water involved in the hydrogen evolution reaction by in situ Raman spectroscopy. Nano-Micro Lett. 16, 53 (2023). https://doi.org/10.1007/s40820-023-01285-1
S. Lyu, C. Guo, J. Wang, Z. Li, B. Yang et al., Exceptional catalytic activity of oxygen evolution reaction via two-dimensional graphene multilayer confined metal-organic frameworks. Nat. Commun. 13, 6171 (2022). https://doi.org/10.1038/s41467-022-33847-z
K. Wang, Y. Wang, B. Yang, Z. Li, X. Qin et al., Highly active ruthenium sites stabilized by modulating electron-feeding for sustainable acidic oxygen-evolution electrocatalysis. Energy Environ. Sci. 15, 2356–2365 (2022). https://doi.org/10.1039/D1EE03610F
D.Y. Chung, P.P. Lopes, P. Farinazzo Bergamo Dias Martins, H. He, T. Kawaguchi et al., Dynamic stability of active sites in hydr(oxy)oxides for the oxygen evolution reaction. Nat. Energy 5, 222–230 (2020). https://doi.org/10.1038/s41560-020-0576-y
Z.-F. Huang, J. Song, Y. Du, S. Xi, S. Dou et al., Chemical and structural origin of lattice oxygen oxidation in Co–Zn oxyhydroxide oxygen evolution electrocatalysts. Nat. Energy 4, 329–338 (2019). https://doi.org/10.1038/s41560-019-0355-9
Y. Tong, Y. Guo, P. Chen, H. Liu, M. Zhang et al., Spin-state regulation of perovskite cobaltite to realize enhanced oxygen evolution activity. Chem 3, 812–821 (2017). https://doi.org/10.1016/j.chempr.2017.09.003
R.R. Rao, I.E.L. Stephens, J.R. Durrant, Understanding what controls the rate of electrochemical oxygen evolution. Joule 5, 16–18 (2021). https://doi.org/10.1016/j.joule.2020.12.017
H.-F. Wang, L. Chen, H. Pang, S. Kaskel, Q. Xu, MOF-derived electrocatalysts for oxygen reduction, oxygen evolution and hydrogen evolution reactions. Chem. Soc. Rev. 49, 1414–1448 (2020). https://doi.org/10.1039/c9cs00906j
X. Zhou, B. Fu, L. Li, Z. Tian, X. Xu et al., Hydrogen-substituted graphdiyne encapsulated cuprous oxide photocathode for efficient and stable photoelectrochemical water reduction. Nat. Commun. 13, 5770 (2022). https://doi.org/10.1038/s41467-022-33445-z
J. Xie, F. Wang, Y. Zhou, Y. Dong, Y. Chai et al., Internal polarization field induced hydroxyl spillover effect for industrial water splitting electrolyzers. Nano-Micro. Lett. 16, 39 (2023). https://doi.org/10.1007/s40820-023-01253-9
X. Ling, F. Du, Y. Zhang, Y. Shen, W. Gao et al., Bimetallic oxyhydroxide in situ derived from an Fe2Co-MOF for efficient electrocatalytic oxygen evolution. J. Mater. Chem. A 9, 13271–13278 (2021). https://doi.org/10.1039/D1TA02159A
V. Andrei, R.A. Jagt, M. Rahaman, L. Lari, V.K. Lazarov et al., Long-term solar water and CO2 splitting with photoelectrochemical BiOI–BiVO4 tandems. Nat. Mater. 21, 864–868 (2022). https://doi.org/10.1038/s41563-022-01262-w
H. Wu, L. Zhang, A. Du, R. Irani, R. van de Krol et al., Low-bias photoelectrochemical water splitting via mediating trap states and small polaron hopping. Nat. Commun. 13, 6231 (2022). https://doi.org/10.1038/s41467-022-33905-6
L.-W. Wu, C. Liu, Y. Han, Y. Yu, Z. Liu et al., In situ spectroscopic identification of the electron-transfer intermediates of photoelectrochemical proton-coupled electron transfer of water oxidation on Au. J. Am. Chem. Soc. 145, 2035–2039 (2023). https://doi.org/10.1021/jacs.2c11882
X. Zhang, P. Zhai, Y. Zhang, Y. Wu, C. Wang et al., Engineering single-atomic Ni-N4-O sites on semiconductor photoanodes for high-performance photoelectrochemical water splitting. J. Am. Chem. Soc. 143, 20657–20669 (2021). https://doi.org/10.1021/jacs.1c07391
Y. Qi, J. Zhang, Y. Kong, Y. Zhao, S. Chen et al., Unraveling of cocatalysts photodeposited selectively on facets of BiVO4 to boost solar water splitting. Nat. Commun. 13, 484 (2022). https://doi.org/10.1038/s41467-022-28146-6
D. Lee, W. Wang, C. Zhou, X. Tong, M. Liu et al., The impact of surface composition on the interfacial energetics and photoelectrochemical properties of BiVO4. Nat. Energy 6, 287–294 (2021). https://doi.org/10.1038/s41560-021-00777-x
T.W. Kim, K.S. Choi, Nanoporous BiVO4 photoanodes with dual-layer oxygen evolution catalysts for solar water splitting. Science 343, 990–994 (2014). https://doi.org/10.1126/science.1246913
Y. Gao, J. Wang, Y. Yang, J. Wang, C. Zhang et al., Engineering spin states of isolated copper species in a metal–organic framework improves urea electrosynthesis. Nano-Micro Lett. 15, 158 (2023). https://doi.org/10.1007/s40820-023-01127-0
S. Zhao, C. Tan, C.-T. He, P. An, F. Xie et al., Structural transformation of highly active metal–organic framework electrocatalysts during the oxygen evolution reaction. Nat. Energy 5, 881–890 (2020). https://doi.org/10.1038/s41560-020-00709-1
J. Yang, Y. Shen, Y. Sun, J. Xian, Y. Long et al., Ir nanoparticles anchored on metal-organic frameworks for efficient overall water splitting under pH-universal conditions. Angew. Chem. Int. Ed. 62, e202302220 (2023). https://doi.org/10.1002/anie.202302220
H. Hu, Z. Wang, L. Cao, L. Zeng, C. Zhang et al., Metal-organic frameworks embedded in a liposome facilitate overall photocatalytic water splitting. Nat. Chem. 13, 358–366 (2021). https://doi.org/10.1038/s41557-020-00635-5
J. Xian, S. Li, H. Su, P. Liao, S. Wang et al., Electrosynthesis of α-amino acids from NO and other NOx species over CoFe alloy-decorated self-standing carbon fiber membranes. Angew. Chem. Int. Ed. 62, e202306726 (2023). https://doi.org/10.1002/anie.202306726
Z. Jiang, X. Xu, Y. Ma, H.S. Cho, D. Ding et al., Filling metal-organic framework mesopores with TiO2 for CO2 photoreduction. Nature 586, 549–554 (2020). https://doi.org/10.1038/s41586-020-2738-2
Z. Xue, K. Liu, Q. Liu, Y. Li, M. Li et al., Missing-linker metal-organic frameworks for oxygen evolution reaction. Nat. Commun. 10, 5048 (2019). https://doi.org/10.1038/s41467-019-13051-2
W. Cheng, X. Zhao, H. Su, F. Tang, W. Che et al., Lattice-strained metal–organic-framework arrays for bifunctional oxygen electrocatalysis. Nat. Energy 4, 115–122 (2019). https://doi.org/10.1038/s41560-018-0308-8
Y. Sun, Z. Xue, Q. Liu, Y. Jia, Y. Li et al., Modulating electronic structure of metal-organic frameworks by introducing atomically dispersed Ru for efficient hydrogen evolution. Nat. Commun. 12, 1369 (2021). https://doi.org/10.1038/s41467-021-21595-5
K. Liu, J. Fu, Y. Lin, T. Luo, G. Ni et al., Insights into the activity of single-atom Fe-N-C catalysts for oxygen reduction reaction. Nat. Commun. 13, 2075 (2022). https://doi.org/10.1038/s41467-022-29797-1
F. Cheng, X. Peng, L. Hu, B. Yang, Z. Li et al., Accelerated water activation and stabilized metal-organic framework via constructing triangular active-regions for ampere-level current density hydrogen production. Nat. Commun. 13, 6486 (2022). https://doi.org/10.1038/s41467-022-34278-6
F. He, Q. Zheng, X. Yang, L. Wang, Z. Zhao et al., Spin-state modulation on metal-organic frameworks for electrocatalytic oxygen evolution. Adv. Mater. 35, e2304022 (2023). https://doi.org/10.1002/adma.202304022
L. Zhang, R. Long, Y. Zhang, D. Duan, Y. Xiong et al., Direct observation of dynamic bond evolution in single-atom Pt/C3 N4 catalysts. Angew. Chem. Int. Ed. Engl. 59, 6224–6229 (2020). https://doi.org/10.1002/anie.201915774
W.H. Lee, M.H. Han, Y.J. Ko, B.K. Min, K.H. Chae et al., Electrode reconstruction strategy for oxygen evolution reaction: maintaining Fe-CoOOH phase with intermediate-spin state during electrolysis. Nat. Commun. 13, 605 (2022). https://doi.org/10.1038/s41467-022-28260-5
H. Tao, Y. Xu, X. Huang, J. Chen, L. Pei et al., A general method to probe oxygen evolution intermediates at operating conditions. Joule 3, 1498–1509 (2019). https://doi.org/10.1016/j.joule.2019.03.012
S. Chibani, C. Michel, F. Delbecq, C. Pinel, M. Besson, On the key role of hydroxyl groups in platinum-catalysed alcohol oxidation in aqueous medium. Catal. Sci. Technol. 3, 339–350 (2013). https://doi.org/10.1039/C2CY20363D
X. Kang, K. Lyu, L. Li, J. Li, L. Kimberley et al., Integration of mesopores and crystal defects in metal-organic frameworks via templated electrosynthesis. Nat. Commun. 10, 4466 (2019). https://doi.org/10.1038/s41467-019-12268-5
F. He, Y. Zhao, X. Yang, S. Zheng, B. Yang et al., Metal-organic frameworks with assembled bifunctional microreactor for charge modulation and strain generation toward enhanced oxygen electrocatalysis. ACS Nano 16, 9523–9534 (2022). https://doi.org/10.1021/acsnano.2c02685
J.-Y. Zhang, Y. Yan, B. Mei, R. Qi, T. He et al., Local spin-state tuning of cobalt–iron selenide nanoframes for the boosted oxygen evolution. Energy Environ. Sci. 14, 365–373 (2021). https://doi.org/10.1039/D0EE03500A
B.E. Van Kuiken, M. Khalil, Simulating picosecond iron K-edge X-ray absorption spectra by ab initio methods to study photoinduced changes in the electronic structure of Fe(II) spin crossover complexes. J. Phys. Chem. A 115, 10749–10761 (2011). https://doi.org/10.1021/jp2056333
G. Zhou, P. Wang, H. Li, B. Hu, Y. Sun et al., Spin-sate reconfiguration induced by alternating magnetic field for efficient oxygen evolution reaction. Nat. Commun. 12, 4827 (2021). https://doi.org/10.1038/s41467-021-25095-4
J. Suntivich, K.J. May, H.A. Gasteiger, J.B. Goodenough, Y. Shao-Horn, A perovskite oxide optimized for oxygen evolution catalysis from molecular orbital principles. Science 334, 1383–1385 (2011). https://doi.org/10.1126/science.1212858
Acknowledgements
This work was supported by the National Key Research and Development Program of China (2022YFB4002100), the development project of Zhejiang Province's "Jianbing" and "Lingyan" (2023C01226), the National Natural Science Foundation of China (22278364, U22A20432, 22238008, 22211530045, and 22178308), the Fundamental Research Funds for the Central Universities (226-2022-00044 and 226-2022-00055), the Science Foundation of Donghai Laboratory (DH-2022ZY0009), the Startup Foundation for Hundred-Talent Program of Zhejiang University, and Scientific Research Fund of Zhejiang Provincial Education Department. XAS data were collected at BL14W1 beamline i Beijing Synchrotron Radiation Facility (BSRF), and Taiwan Synchrotron Radiation Facility (TSRF).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of Interest
The authors declare no conflict of interest. They have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
He, F., Liu, Y., Yang, X. et al. Accelerating Oxygen Electrocatalysis Kinetics on Metal–Organic Frameworks via Bond Length Optimization. Nano-Micro Lett. 16, 175 (2024). https://doi.org/10.1007/s40820-024-01382-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-024-01382-9