Abstract
Molecular dynamic, Monte-Carlo simulation approach and electrochemical methods were used to study the temperature effects on mild steel (MS) corrosion in 1.0 M of HCl in the absence and presence of triazepine carboxylate compounds. The inhibition action of all triazepine carboxylates compound studied was performed via adsorption on MS surface. Comparison between several adsorption isotherms reveals that the adsorption was spontaneous and followed Langmuir isotherm in HCl for all inhibitors and at all studied temperatures. Furthermore, selection is founded on the correlation coefficient is known nearly linear and value close to one. Kinetic and thermodynamic parameters for all inhibitors led to suggest the occurrence of chemical mechanism and also the spontaneity of the adsorption process on mild steel surface. The corrosion inhibition mechanism was discussed with the light of some triazepine carboxylate compounds constituents. The effect of molecular structure on the inhibition efficiency has been explored by quantum chemical computations and obvious correlations were observed. The binding energies of tested triazepine carboxylate compounds on Fe (110) surfaces were calculated using molecular dynamics simulation. Very good agreement was obtained with the experimental data. In addition, Atomic force microscopy (AFM) indicated that Cl–Me–CN molecules contributed to a protective layer formation by their adsorption on the steel surface. AFM parameters, such as root mean square roughness (Rq), average roughness (Ra), and ten-point height (Sz), revealed that a smoother surface of inhibited mild steel was obtained, compared to uninhibited steel surface.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
It has been observed that the adsorption of corrosion inhibitors depends mainly on certain physico-chemical properties of the molecule such as functional groups, steric factors, aromaticity, electron density at the donor atoms and π orbital character of donating electrons, and also on the electronic structure of the molecules [1,2,3,4,5,6,7]. Inhibition performance dependence of the pickling acid process parameters such as (temperature) and the comparison of the obtained thermodynamic data of the corrosion process had been recently the object of large amount of investigation [8,9,10,11,12]. Accordingly, acid pickling inhibitors are expected to be chemically stable to provide high protective efficiency.
Our previous studies have shown three triazepine carboxylate compounds, which was found to exhibit good corrosion inhibition efficiencies. It is found that these compounds namely, ethyl 4,9-bis(4-chlorophenyl)-8-cyano-3-hydroxy-2,7-dioxo-1,2,5,7-tetrahydropyrido[1,2-b]triazepine-10-carboxylate (2Cl–Et), methyl 4,9-bis(4-chlorophenyl)-8-cyano-3-hydroxy-2,7-dioxo-1,2,5,7-tetrahydropyrido[1,2-b]triazepine-10-carboxylate (2Cl–Me), and ethyl 9-(4-chlorophenyl)-8-cyano-3-hydroxy-2,7-dioxo-4-(p-tolyl)-1,2,5,7-tetrahydropyrido[1,2-b]triazepine-10-carboxylate (Cl–Me–Et) act as excellent inhibitors and their inhibition efficiencies follow the order: 2Cl–Me > 2Cl–Et > Cl–Me–Et, and they depend on the type of the substituent. In addition, it is found also that the Density Function Theory (DFT) parameters confirmed those obtained by experimental studies [7]. In continuation of our research for the development of new efficient corrosion inhibitors and to understand their inhibitive mechanism, the influence of temperature as critical parameter of industrial acid pickling process on triazepine carboxylate compounds, adsorption process has been investigated by using electrochemical, molecular dynamic, Monte-Carlo simulation methods. Besides, various thermodynamic parameters for triazepine carboxylate compounds inhibitors adsorption on mild steel surface were estimated and discussed. Also, the kinetic and thermodynamic parameters were calculated and discussed. On the light of triazepine carboxylate compounds, the inhibition mechanism for mild steel in molar hydrochloric acid was elucidated.
2 Experimental Part
2.1 Materials, Sample Preparation and Aggressive Medium
The experiments were performed with mild steel rods as shown in Table 1. The used mild steel specimens have a rectangular form 2.5 cm × 2.0 cm × 0.05 cm. The specimen’s surface was polished with emery paper at different grit sizes (from 180 to 1200), rinsed with distilled water, degreased with ethanol, and dried at hot air. The examined inhibitors are ethyl 4-(4-chlorophenyl)-8-cyano-3-hydroxy-2,7-dioxo-9-(p-tolyl)-1,2,5,7-tetrahydropyrido[1,2-b] [1, 2, 4] triazepine-10-carboxylate (Cl–Me–CO2Et), 4-(4-chlorophenyl)-3-hydroxy-2,7-dioxo-9-(p-tolyl)-1,2,5,7-tetrahydropyrido[1,2-b] [1, 2, 4] triazepine-8,10-dicarbonitrile (Cl–Me–CN) and 3-hydroxy-2,7-dioxo-9-phenyl-4-(p-tolyl)-1,2,5,7-tetrahydropyrido[1,2-b] [1, 2, 4] triazepine-8,10-dicarbonitrile (Me–CN) where their molecules were synthesized according to the Serrar et al. procedure [13] and their formulas are indicated in Fig. 1.
The aggressive medium of 1.0 M HCl was prepared by dilution of analytical grade 37% HCl with distilled water. The employed concentration range of tested triazepine carboxylate compounds was from 10−6 to 10−3 M of studied inhibitors in various temperatures ranging 298–328 ± 2 K.
2.2 Electrochemical Methods
For electrochemical measurements, the electrolysis cell closed by a cap with five apertures. The working electrode was pressure-fitted into a polytetrafluoroethylene holder (PTFE) exposing only 1 cm2 of area to the aggressive solution. Pt and saturated calomel were used as counter and reference electrode (SCE), respectively. All potentials were measured against the last electrode.
The potentiodynamic polarization curves were recorded by changing the electrode potential automatically from negative values to positive values versus (Ecorr) using a Potentiostat/Galvanostat type PGZ 100, with a scan rate of 1 mV/s after 1 h of immersion time until reaching steady state. The test solution was thermostatically controlled at 298 ± 2 K in air atmosphere without bubbling. To evaluate corrosion kinetic parameters, a fitting by Stern–Geary equation was used [14]. The corrosion inhibition efficiency was evaluated from the corrosion current densities values using the relationship (1):
where \(i_{{{\text{corr}}}}^{0}\) and \({i_{{\text{corr}}}}\) are the corrosion current densities values without and with inhibitor, respectively.
Finally, the electrochemical impedance spectroscopy measurements were carried out at Open Circuit Potential (OCP) in the frequency range of 100 KHz–10 mHz, with 10 points per decade, at the rest potential, after 30 min of acid immersion, by applying 10 mV peak to peak voltage excitation. Nyquist plots were made from these experiments. Fitting curves of the experiments was done using ZView 2 software. The inhibition efficiencies ηEIS% were calculated from Nyquist plots by Eq. (2):
where \(R_{{{\text{ct}}}}^{^\circ }\) and \({R_{{\text{ct}}}}\) are the charge transfer resistance of steel electrode in the absence and in presence of inhibitor.
In order to ensure reproducibility, all experiments were repeated three times where the evaluated inaccuracy did not exceed 10%.
2.3 Adsorption Studies
Inhibitive ability of a triazepine carboxylate compounds to a greater extent depends on its adsorption on metal surface. Various adsorption isotherm models considered were described below and tested.
where Kads is the equilibrium constant of the adsorption process; Cinh is the inhibitor concentration; f is the factor of energetic inhomogeneity, and the parameter ‘a’ in Eq. (6) is the water molecules number replaced by inhibitor molecules on metallic surface.
2.4 Molecular Dynamic Modelling
Recently, molecular dynamics simulation constituted an advancement part in corrosion inhibition studies as it is employed at the atomistic level to explore the interaction of inhibitor molecules on metal surfaces [15]. The simulation of adsorption process of inhibitor molecules on Iron surfaces was investigated by molecular dynamics simulation using (Material Studio 2017) software from Accelrys Inc, USA. The most stable planes of crystalline metals are the one with densely packed; it is commonly used in molecular dynamics simulations to represent the corroding substrate metal [16, 17]. The simulations were performed in a simulation box of dimensions (3.44 nm × 4.05 nm × 5.34 nm). The molecular dynamics simulations were carried out with periodic boundary conditions to model a representative part of the interface devoid of any arbitrary boundary effects. Firstly, the surface of (pure Fe crystal) was cleaved, and relaxed by minimizing its energy by means of molecular mechanics. Next, the surface of cleaved plane Fe (110) was enlarged to a super cell of an appropriate size, and then a vacuum slab with zero Thickness was built above these surfaces. Since corrosion inhibition in aqueous solution is an electrochemistry process, the use of water molecules and different ions is essential. The effect of chemical species involved in the adsorption system was taken into consideration; thus, the system in the molecular dynamics simulations incorporated 250 H2O, 5 H+, 5 Cl− and one inhibitor molecule in each case [18]. Finally, the most stable orientation of inhibitor molecules on metal surface was searched by Monte-Carlo search simulations. The molecular dynamics simulations were performed at 298 K (controlled by the Andersen thermostat) using a canonical ensemble (NVT) with a time step of 1.0 fs and a simulation time of 500 ps. For the whole simulation procedure, the COMPASS (Condensed-phase Optimized Molecular Potentials for Atomistic Simulation Studies) force field [19] was used, because it allows the accurate and simultaneous prediction of structural, conformational, vibrational, and thermo-physical properties for a broad range of chemical species, including organic molecules, metals, metal oxides, and metal halides [20].
2.5 Morphology Analysis Using (AFM) Technique
Atomic force microscopy (AFM) analysis is one of the major analysis methods to study a surface and was used here for the further investigation of the formation of a protective film on the surface of the mild steel. AFM was used to investigate the topography image of the uninhibited and inhibited mild steel surface using 10−3 M of ethyl 9-(4-chlorophenyl)-8-cyano-3-hydroxy-2,7-dioxo-4-(p-tolyl)-1,2,5,7-tetrahydropyrido[1,2-b] [1, 2, 4] triazepine-10-carboxylate (Cl–Me–CN).
3 Results and Discussion
3.1 Corrosion Inhibition Efficiency Studies
In our first part of this work, we have introduced that all the tested triazepine carboxylate derivatives act as good corrosion inhibitors for mild steel electrode in 1.0 M HCl solution.
The intensity-potential curves indicated that these compounds operate as mixed type inhibitors and their inhibition efficiencies increase with their concentrations to attain a maximum at 10−3 M.
It is established also that the mechanism of the anodic and cathodic reactions change by the addition of triazepine carboxylate compounds. It is found that these compounds act by an adsorption mechanism on the metallic surface and their inhibition efficiency depends on the nature of the alkyl substituents, where the Cl–Me–CN compounds are the best. The electrochemical impedance spectroscopy (EIS) was utilized to decide and provide us the kinetic information and important mechanistic for the examined electrochemical system. Figure 2 presents respectively its Potentiodynamic polarization curves and Nyquist plots. Table 2 resumes the effect of triazepines carboxylate derivatives on mild steel corrosion in 1.0 M HCl using different electrochemical techniques such as Potentiodynamic polarization curves and electrochemical impedance spectroscopy.
Furthermore, in order to gain more information about the adsorption type of triazepine carboxylates compounds and its effectiveness at higher temperatures:
-
Corrosion Kinetic Study;
-
Temperature effect on the corrosion inhibition of mild steel;
-
Corrosion inhibition stability studies versus temperature;
-
Thermodynamic parameters of the adsorption process;
-
Adsorption isotherm analysis and thermodynamic parameters;
-
Surface morphology was also investigated using (Atomic force microscopy);
-
Monte-Carlo simulation & Pair correlation function;
-
Finally, corrosion protection mechanism was proposed for all triazepine carboxylate compounds studied.
3.2 Temperature Effect on the Inhibition Efficiency
In order to get others information about the type of adsorption and the effectiveness of the triazepine carboxylate compounds at higher temperature (simulation of industrial process condition), polarization experiment was conducted in the range of 298–328 ± 2 K without and with triazepine carboxylate compounds. Figure 3 presents the obtained potentiodynamic polarization curves and their corresponding data are presented in Table 3.
It is clear that according to the substitution of each triazepine carboxylate compounds studied, it can be noted that the inhibition efficiency of inhibitors depends on the temperature and decreases with the rise of temperature from 298 to 328 ± 2 K. This can be explained by the decrease of the strength of the adsorption process at elevated temperature [21]. It is seen also that the presence of carboxylate compounds will provide a film barrier protecting steel surface from being exposed to acidic media. Surface coverage θ was calculated from the following equation [22]:
where \({i}_{\text{c}\text{o}\text{r}\text{r}}\), \({i}_{\text{c}\text{o}\text{r}\text{r}}^{\text{i}}\), and \({i}_{\text{s}\text{a}\text{t}}\) are the corrosion current density values in the absence and the presence of triazepine carboxylate compounds.
As isat << icorr, thus
Analysis of the results in Table 7 indicates that the Electrochemical kinetic parameters,
-
Corrosion potential (Ecorr)
-
Corrosion current density (icorr)
-
And cathodic Tafel slope (bc), depend of substitution of triazepine carboxylate compounds.
This is more clearly illustrated in Table 3 by the variations of surface coverage with temperature:
-
Whimpers from 0.941 for Me–CN compound at 298 ± 2 K to 0.865 at 328 ± 2 K;
-
Also surface coverage of Cl–Me–CO2Et compound decreases from 0.926 to 0.855 respectively at 298 K and 328 ± 2 K;
-
Moreover for Cl–Me–CN compounds reduce from 0.946 to 0.840 respectively at 298–328 ± 2 K.
Increasing of inhibition efficiency (η%) will reduce the rate of corrosion process due to higher surface coverage (θ) from carboxylate compounds studied. This is due to the highest concentration of inhibitor and can protect the mild steel surface from the aggressive hydrochloric acid environment. At this condition, the surface coverage is the highest with 0.946 for Cl–Me–CN compared to the protection using 0.941 for Me–CN and 0.926 for Cl–Me–CO2Et. It is noted that the Large surface areas of mild steel are covered by all triazepine carboxylate compounds film and this reduces the reaction sites available.
3.3 Corrosion Inhibition Stability Studies Versus Temperature
Furthermore, calculating standard deviation (σinh) is very important to determine the stability of triazepine carboxylate compounds in acid medium against variation of temperatures. Statistical data such as absolute deviation (Ad), standard deviation (ση), mean \(\stackrel{-}{(x})\)are listed in Table 3. The range of a set of data is the difference between the highest and lowest measurements. Algebraically, the range (Rη) can be expressed as
where (\({\eta }_{better}\)) and (\({\eta }_{less})\) are the great and less value of inhibition efficiency obtained for each inhibitor, respectively.
The mean \(\stackrel{-}{x}\) is part of calculating the range (Rη) and it is the primary calculation for reporting the measured value. The mean is found by adding up the sum of inhibition efficiency obtained for temperature range studied and then dividing by the number of tests.
However, the average deviation of inhibition efficiency measurements is calculated using Eq. (12):
Absolute deviations are represented algebraically as
The obtained results are listed in Table 3. Standard deviation is a reliable statistic for reporting precision, and the following formula below can be used:
The standard deviation of the inhibition efficiency reveals very good stability of all triazepine carboxylate inhibitors studied at temperature range of 298–328 ± 2 K. Value of standard deviation (ση) is 4.75%, 3.06% and 3.33% for Me–CN, Cl–Me–CO2Et and Cl–Me–CN, respectively. These results confirmed that there were no significant changes, or variation between all temperatures. All plots follow the same pattern.
3.4 Adsorption Isotherm Analysis and Thermodynamic Parameters
The efficiency of an organic species as a successful corrosion inhibitor is mainly dependent on its ability to get adsorbed on the surface of the metal. Adsorption isotherm models can provide important clues to the nature of metal/inhibitor interaction. Attempts were made to find a good fit for triazepine carboxylate compounds adsorption on mild steel surface with various isotherms. So, the coverage surface values (θ) can be easily determined from AC impedance, Tafel polarization or the linear polarization by the ratio η %/100. In the present study, the coverage surface values were evaluated from Tafel polarization (Table 3).
Adsorption isotherm models considered were fitted and presented in (Fig. 4). Their corresponding fitting curve results are shown in Table 4. It is demonstrated that the triazepine carboxylate compounds were adsorbed on mild steel surface according to Langmuir isotherm model (Fig. 4a). The correlation coefficient is known nearly linear (R2 close to 1), i.e., 0.99999 for both Cl–Me–CN and Cl–Me–CO2Et compounds and 0.99995 for Me–CN inhibitor. The values of regression coefficients (R2) given in Table 4 confirmed the validity of the approach. Besides, isothermal adsorption Langmuir describes molecules adsorbed triazepine carboxylate compounds just stick to outer layers of the surface of the mild steel or just form a monolayer without bond strong.
This kind of isotherm involves the assumption of no interaction between the adsorbed species on the electrode surface [23]. So, the adsorption constant, (Kads), is related to the free energy of adsorption, (ΔG*ads), by Eq. (15):
where the value 55.55 represents the water concentration in solution by mol L−1; R is the universal gas constant, and T is the absolute temperature.
The values of (Kads), (R2), (ΔG*ads) and other parameters are calculated and are given in Table 5. The high obtained value of (Kads) reflects the high adsorption ability of this inhibitor on the mild steel surface.
In addition, if the value of (∆G*ads) is − 40 kJ/mol or more negative, it indicates the transfer of the electrons from the inhibitor to the metal surface forming a coordinate bond between them. (ΔG*ads) are lower than above, for example, − 20 kJ/mol, leading to a weak electrostatic attraction between the charged inhibitor and the charged metal surface in the corrosion medium [24, 25].
Moreover, the negative value of (ΔG*ads) indicates the
-
stability of the adsorption layer on the steel surface;
-
spontaneity of the adsorption process;
-
strong interaction between triazepine carboxylate inhibitor molecules and the mild steel surface [26, 27].
The perusal of (ΔG*ads) value ranging from − 39.3 to − 44.8 kJ/mol suggests that the adsorption of pyoverdine follows chemisorptions which is spontaneous in nature [28].
3.5 Thermodynamic Parameters of Activation Corrosion Process
In order to gain more information about the adsorption type of triazepine carboxylates compounds and its effectiveness at higher temperatures, potentiodynamic polarization curves for mild steel in 1.0 M HCl without and with various concentrations of triazepine carboxylates compounds were used in the temperatures range from 298 to 328 ± 2 K. The activation parameters for the corrosion reaction can be regarded as an Arrhenius-type process, according to the following equation:
where (Ea) is the apparent activation corrosion energy; (R) is the universal gas constant, and (A) is the Arrhenius pre-exponential factor. The apparent activation energies (Ea) in the absence and in the presence of triazepine carboxylates compounds for mild steel are calculated by linear regression between ln(icorr) and 1/T (Fig. 5), and the results are given in Table 3. All the linear regression coefficients are close to 1, indicating that the steel corrosion in hydrochloric acid can be elucidated using the kinetic model.
A corresponding increase in the corrosion rate occurs because of the greater area of metal that is consequently exposed to the acid environment [29]. The enthalpy and entropy of activation respectively (ΔHa) and (ΔSa) for the intermediate complex in the transition state for the corrosion of mild steel in 1.0 M HCl in the absence and in the presence of triazepine carboxylates compounds were obtained by applying the alternative formulation of Arrhenius equation [30]:
where (h) is the Plank’s constant and (N) is the Avogadro’s number. Figure 6 shows a plot of ln(icorr/T) versus 1/T. A straight line is obtained with a slope of (−ΔHa/R) and an intercept of (ln R/Nh + ΔSa/R) from which the values of (ΔHa) and (ΔSa) were calculated and reported in Table 3. The positive values of (ΔHa) in the absence and the presence of triazepine carboxylates compounds reflect the endothermic nature of the mild steel dissolution process. One can also notice that (Ea) and (ΔHa) values vary in the same way as shown in Table 3, indicating that the corrosion process is a unimolecular reaction. This result permits to verify the known thermodynamic equation between the (Ea) and (ΔHa).
Therefore, when all the details are worked out one ends up with an expression that again takes the form of an Arrhenius exponential multiplied by a slowly varying function of (T). The precise form of the temperature dependence depends upon the reaction, and can be calculated using formulas from statistical mechanics involving the partition functions of the reactants and of the activated complex. Nevertheless, in order to carry simple calculations, Eq. (19) was rearranged to become
A plot of ln (icorr/T) against 1000/T should give a straight line with a slope of (− ∆Ha/R) and intercept of [ln (R/Nh) + (∆Sa/R)], as shown in Fig. 6. (ΔHa) and (ΔSa) were calculated and tabulated in Table 3. The activation energy (Ea) increases in the presence of the inhibitor; the same patterns were observed for all triazepine carboxylate compounds studied. Increases in (Ea) with the presence of triazepine carboxylate compounds indicate that a physical (electrostatic) adsorption occurred in the first stage. The increase in (Ea) may be resulted either due to physical adsorption that occurs in first stage [31] or due to decrease in the adsorption of inhibitor molecules on the steel surface with increasing temperature [29]. The (Ea) value was (Ea−(Me–CN) = 43.7 kJ mol−1), (Ea−(Cl–Me–CO2Et) = 39,1 kJ mol−1) and (Ea−(Cl–Me–CN) = 51.4 kJ mol−1), respectively, for Me–CN, Cl–Me–CO2Et and Cl–Me–CN. The (Ea) value for all inhibitors studied was greater than 20 kJ mol−1 in both the presence and absence of the triazepine carboxylates compounds, which reveals that the entire process is controlled by the surface reaction.
The values of (\({\varDelta H}_{\text{a}\text{d}\text{s}}^{\text{*}})\) are nearly the same and are higher in the presence of the inhibitor. This indicates that the energy barrier of the corrosion reaction increased in the presence of the inhibitor without changing the mechanism of dissolution.
The positive values of (\({\varDelta H}_{\text{a}\text{d}\text{s}}^{\text{*}})\) for both corrosion processes with and without the inhibitor reveal the endothermic nature of the steel dissolution process and indicate that the dissolution of steel is difficult [32].
According to the recorded values of enthalpy of activation (Table 3), exothermic adsorption behaviour was detected depending on applied temperatures. The value of enthalpy of activation \(\left({\varDelta H}_{\text{a}\text{d}\text{s}}^{\text{*}}\right)\) is respectively (41.1 KJ × mol−1), (36.5 KJ × mol−1) and (48.8 KJ × mol−1) for the Me–CN, Cl–Me-CO2Et and Cl–Me–CN.
The large negative value of \(\left({\varDelta S}_{\text{a}}^{\text{*}}\right)\) for mild steel in 1.0 M HCl implies that the activated complex is the rate-determining step, rather than the dissociation step. In the presence of the triazepine carboxylate inhibitors, the value of (\({\varDelta S}_{\text{a}}^{\text{*}})\) increases and is generally interpreted as an increase in disorder as the reactants are converted to the activated complexes [33]. The values of activation entropy (\({\varDelta S}_{\text{a}}^{\text{*}}\)) are higher for inhibited solutions than that for the uninhibited solution (Table 3). The positive increment of (\({\varDelta S}_{\text{a}}^{\text{*}}\)) suggesting that an increase in randomness occurred on going from reactants to the activated complex. This observation is in agreement with the findings of other workers [34].
3.6 Surface Morphology (AFM)
Atomic force microscopy (AFM) is a very high-resolution type of scanning probe microscopy, with demonstrated resolution in the order of fractions of a nanometer, more than 1000 times better than the optical diffraction limit. The morphology of the surface of mild steel after immersion for 6 h in 1.0 M HCl solution without and with 10−3 M of Cl–Me–CN was examined in the light of an atomic force microscope.
The three-dimensional (3D) AFM morphology and the AFM cross-sectional profile for polished mild steel surface (reference sample), mild steel surface immersed in 1.0 M HCl (blank sample), and the mild steel surface immersed in 1.0 M HCl containing 10−3 M of Cl–Me–CO2Et are shown in (Fig. 7a, b). Also, in Table 6, summary of the root mean square (Sq), average roughness (Sa), peak-to-peak (Sy), ten-point height (Sz), surface skewness (Ssk) and coefficient of kurtosis (Ska) values for the mild steel surface immersed in protected and non-protected aggressive medium are listed.
Whereas (Sq) is root-mean-square roughness (the average of the measured height deviations taken within the evaluation length and measured from the mean line) and (Sa) is the average roughness (the average deviation of all points’ roughness profile from a mean line over the evaluation length). Figure 7a displays corroded metal surface in the absence of the Cl–Me–CN inhibitor immersed in 1.0 M HCl. The values of Root Mean Square (Sq), Average Roughness (Sa) and the Ten-point height (Sz) height for the polished carbon steel surface (inhibited sample) are 496.13, 521.46 and 1612.17 nm, respectively. The slight roughness observed on the polished carbon steel surface was due to atmospheric corrosion.
These data suggest that the carbon steel surface immersed in 1.0 M HCl has a greater surface roughness. Figure 7b displays the mild steel surface after immersion in 1.0 M HCl containing 10−3 M of Cl–Me–CN. The (Sq), (Sa) and (Sz) values for the mild steel surface are 54.064, 40.748 and 305.693 nm, respectively. The Root Mean Square (Sq), Average Roughness (Sa), and the Ten-point height (Sz) are considerably less in the inhibited environment compared to the uninhibited environment. These parameters confirm that the surface is smoother. The smoothness of the surface is due to the formation of a compact protective film of Fe2+/Cl–Me–CN complex on the metal surface, thereby, inhibiting the corrosion of mild steel.
3.7 Molecular Dynamic Simulation
The adsorption mode of investigated derivatives on Fe (1 1 0) surface was studied by the molecular dynamics simulation method. At the molecular level, the most stable configuration of the molecules on the metal surface and the values of the adsorption (EAdsorption) between organic inhibitor and the metal surface are the results of the simulations process [35]. The most stable (lowest energy) configurations of the tested compounds on Fe (110) surfaces are depicted in Fig. 8.
It was observed that the heteroatoms of the compounds adsorbed on the iron at first. Then, the remaining centres of the compounds have moved gradually close to the metal surface. Therefore, as shown in Fig. 8, the studied molecules Cl–Me–CN and Me–CN adsorbed on the Fe surfaces with an almost flat orientation, where compound Cl–Me–CO2Et is not fully oriented in flat position on metal surface. The parallel configuration as in compound Cl–Me–CN and Me–CN supports the maximum surface coverage and the higher binding interaction.
The values of (Eads) are large and negative implies that the binding between the investigated inhibitors and the metal surface is spontaneous, and the more negative values of the adsorption energy can be attributed to the stable and strong interaction of the inhibitor on the metal surface [36]. It is observed in Table 7 that the binding energy of Cl–Me–CN on the iron surface is higher than the energy determined for H3O+ and Cl−. This supports that the inhibitors are stable on the iron surface than other competing species. It has been reported that the organic inhibitors with unoccupied orbitals promote the formation of a chelate on the metal surface by accepting electrons from a d-orbital of the metal during such strong adsorption process [34]. Therefore, the compound Cl–Me–CO2Et and Me–CN can form a stable chelate with the iron after strong adsorption, and this leads to a good corrosion inhibition efficiency.
The radial distribution function (RDF) g (r) is a modern tool used to measure the bond length which provides an indication on the type of interaction of inhibitor molecules on metal surface. In literature, when the first peak occurs at 1–3.5 Å, this implies the chemisorption whereas the physisorption is associated with the peaks longer than 3.5 Å. The radial distribution function of heteroatoms of inhibitors graphically as shown in Fig. 9 shows that all the bond length values of are less than 3.5 Å, so chemical interactions might occur between these atoms and the metallic surface.
3.8 Mechanism of Corrosion Inhibition
The experimental results suggested that the corrosion inhibition mechanism is appertained to the adsorption of the investigated compounds on the metal surface. The unshared electron pairs on (O, N) heteroatoms along with π-electrons of aromatic systems and multiple bonds contribute virtually in the adsorption process.
The studied triazepine carboxylate compounds are favourably chemisorbed on the metal surface. In the first stage of the chemisorption, the protonated form of interested compounds competes with aqueous H+.
The evolution of H2 gas occurs followed by a transformation of triazepine carboxylate compounds inhibitors to their neutral state and this step is accompanied by electron transfer unshared on heteroatoms (O, N) to the vacant d-orbital of iron surface atoms. As a consequence, the metal surfaces are accumulated with excess negative charge where back donation is more probable from metal surface to the anti-bonding orbital of inhibitors compounds. Both donation and back donation synergize and substantiate the adsorption of the inhibitor molecules on mild steel surface. In this report, the (Cl–Me–CN) exhibits the highest corrosion inhibition performance. This pertains to the difference in molecular structure of compounds studied due to the electronic effect and basic nature of substitution in (Cl–Me–CN) compound that enhance the inhibitive power.
4 Conclusion
Triazepine carboxylate compounds studied (Cl–Me–CN, Me–CN and Cl–Me–CO2Et) are acting as good corrosion inhibitors in 1.0 M HCl, and their inhibition efficiency increases with increasing concentration, and best performance is for (Cl–Me–CN). The inhibition efficiency trend of inhibitors obtained from electrochemical and molecular dynamic simulation is in good agreement. The experimental data give very good curves fitting for the applied adsorption isotherms as correlation coefficients (R2) were in the range of 0.99995 ≤ R2 ≤ 0.99999. All the inhibitors follow the Langmuir adsorption isotherm with slopes of almost unity, monolayer interaction between the adsorbed species. The high negative value of (∆G*ads) indicates that triazepine carboxylate compounds can be adsorbed on mild steel surface by chemical mechanism and also the spontaneity of the adsorption process. Surface examination via means of Atomic force microscopy (AFM) shows a remarkable mitigation of mild steel corrosion by the formation of protective layer on steel surface. Molecular dynamic simulations supported the experimental results that showed Cl–Me–CN, Me–CN and Cl–Me–CO2Et as efficient corrosion inhibitors. On the other hand, it could be interesting also to study the effect of these compounds on the corrosion of another metal in another acidic medium such as H2SO4 and 1.0 M H3PO4. This study confirmed the performance and the other application of the triazepine carboxylate compounds.
References
Jiang Z, Wang J, Hu Q et al (1995) The influence of 1-(2-pyridylazo)-2-naphthol (PAN) on the corrosion of titanium in 10 N sulfuric acid solution. Corros Sci 37:1245
El-Rehim SSA, Refaey SAM et al (2001) Corrosion inhibition of mild steel in acidic medium using 2-amino thiophenoland 2-cyanomethyl benzothiazole. J Appl Electrochem 31:429
Popova A, Sokolova E, Raicheva S et al (2003) AC and DC study of the temperature effect on mild steel corrosion in acid media in the presence of benzimidazole derivatives. Corros Sci 45:33
Wang HL, Fan HB, Zheng JS (2003) Corrosion inhibition of mild steel in hydrochloric acid solution by a mercapto-triazole compound. Mater Chem Phys 77:655
Bouklah M, Benchat N, Hammouti B et al (2006) Thermodynamic characterisation of steel corrosion and inhibitor adsorption of pyridazine compounds in 0.5 M H2SO4. Mater Lett 60:1901
Popova A, Christov M, Vasilev A (2007) Inhibitive properties of quaternary ammonium bromides of N-containing heterocycles on acid mild steel corrosion. Part II: EIS results. Corros Sci 49:3290
Alaoui K, Touir R, Galai M et al (2018) Electrochemical and computational studies of some triazepine carboxylate compounds as acid corrosion inhibitors for mild steel. J Bio- Tribo Corros 4:37
El Kacimi Y, Galai M, Alaoui K et al (2018) Surface morphology studies and kinetic-thermodynamic characterization of steels treated in 5.0 M HCl medium: hot-dip galvanizing application. Anti Corros Methods Mater 65(2):176–189
Durnie W, Marco RD, Jefferson A et al (1999) Development of a structure—activity relationship for oil field corrosion inhibitors. J Electrochem Soc 146:1751–1756
Oguzie EE, Okolue BN, Ebenso EE el al (2004) Evaluation of the inhibitory effect of methylene blue dye on the corrosion of aluminum in hydrochloric acid. Mater Chem Phys 87:394–401
Tang L, Lia X, Lia L, Qua Q, Mua G, Liua G (2005) The effect of 1-(2-pyridylazo)-2-naphthol on the corrosion of cold rolled steel in acid media: Part 2: inhibitive action in 0.5 M sulfuric acid. Mater Chem Phys 94:353–359
Tang L, Mu G, Liu G (2003) The effect of neutral red on the corrosion inhibition of cold rolled steel in 1.0 M hydrochloric acid. Corros Sci 45:2251–2262
Serrar H, Marmouzi I, Benzekri Z et al (2017) Synthesis and evaluation of novel pyrido[1,2-b][1,2,4]triazine-2,6-dione and pyrido[1,2-b][1,2,4]triazepine-2,7-dione derivatives as antioxidant agents. Lett Org Chem 14:267–277
Stern M, Geary AL (1957) Electrochemical polarization I. A theoretical analysis of the shape of polarization curves. J Electrochem Soc 104:56–63
Tang Y, Yang X, Yang W, Wan R, Chen Y, Yin X (2010) A preliminary investigation of corrosion inhibition of mild steel in 0.5 M H2SO4 by 2-amino-5-(n-pyridyl)-1, 3, 4-thiadiazole: polarization, EIS and molecular dynamics simulations. Corros Sci 52:1801–1808
Salarvand Z, Amirnasr M, Talebian M, Raeissi K, Meghdadi S (2017) Enhanced corrosion resistance of mild steel in 1 M HCl solution by trace amount of 2-phenyl-benzothiazole derivatives: experimental, quantum chemical calculations and molecular dynamics simulation studies. Corros Sci 114:133–145
Obot IB, Obi-Egbedi NO, Ebenso EE, Afolabi AS, Oguzie EE (2013) Experimental, quantum chemical calculations, and molecular dynamic simulations insight into the corrosion inhibition properties of 2-(6-methylpyridin-2-yl) oxazolo [5, 4-f][1, 10] phenanthroline on mild steel. Res Chem Intermed 39:1927–1948
Fouda AS, Ismail MA, Elewady GY, Abousalem AS (2017) Evaluation of 4-amidinophenyl-2,2′-bithiophene and its aza-analogue as novel corrosion inhibitors for CS in acidic media: experimental and theoretical study. J Mol Liq 240:372–388. https://doi.org/10.1016/j.molliq.2017.05.089
Fouda AS, Ismail MA, Abousalem AS, Elewady GY (2017) Experimental and theoretical studies on corrosion inhibition of 4-amidinophenyl-2,2′-bifuran and its analogues in acidic media. RSC Adv 7:46414–46430. https://doi.org/10.1039/c7ra08092a
Sun H, Ren P, Fried JR (1998) The COMPASS force field: parameterization and validation for phosphazenes. Comput Theor Polym Sci 8:229–246
El Faydy M, Galai M, Rbaa M, Ouakki M, Lakhrissi B, Touhami ME, Y. El Kacimi (2018) Synthesis and application of new quinoline as hydrochloric acid corrosion inhibitor of carbon steel. Anal Bioanal Electrochem 10(7) 815–839
Khamis E (1990) The effect of temperature on the acidic dissolution of steel in the presence of inhibitors. Corrosion 46:476–484
Elayyachy M, El Idrissi A, Hammouti B (2006) New thio-compounds as corrosion inhibitor for steel in 1 M HCl. Corros Sci 48:2470–2479
El Nemr A, Moneer AA, Khaled A, El Sikaily A, El-Sai GF (2014) Modeling of synergistic halide additives’ effect on the corrosion of aluminum in basic solution containing dye. Mater Chem Phys 144:139–154
Dhar HP, Conway BE, Joshi KM (1973) On the form of adsorption isotherms for substitutional adsorption of molecules of different sizes. Electrochim Acta 18:789–798
Avci G (2008) Inhibitor effect of N,N’-methylenediacrylamide on corrosion behavior of mild steel in 0.5 M HCl. Mater Chem Phys 112:234–238
Bayol E, Gurten AA, Dursun M, Kayakırılmaz K (2008) Adsorption behavior and ınhibition corrosion effect of sodium carboxymethyl cellulose on mild steel in acidic medium. Acta Phys Chim Sin 24:2236–2242
El-Sayed M, Sherif (2006) Effects of 2-amino-5-(ethylthio)-1,3,4-thiadiazole on copper corrosion as a corrosion inhibitor in 3%NaCl solutions. Appl Surf Sci 252:8615–8619
Szauer T, Brandt A (1981) On the role of fatty acid in adsorption and corrosion inhibition of iron by amine fatty acid salts in acidic solution. Electrochim Acta 26:1257–1260
Abd E, Rehim SS, Ibrahim MAM, Khalid KF (2001) The inhibition of 4-(2′-amino-5′-methylphenylazo) antipyrine on corrosion of mild steel in HCl solution. Mater Chem Phys 70:268–273
Noor EA, Al-Moubaraki AH (2008) Thermodynamic study of metal corrosion and inhibitor adsorption processes in mild steel/1-methyl-4-styryl pyridinium iodides/hydrochloric acid systems. Mater Chem Phys 110:145–154
Behpour M, Ghoreishi SM, Soltani N, Salavati NM, Hamadanian M, Gandomi A (2008) Electrochemical and theoretical investigation on the corrosion inhibition of mild steel by thiosalicylaldehyde derivatives in hydrochloric acid solution. Corros Sci 50:2172–2181
El Ouali I, Hammouti B, Aouniti A, Ramli Y, Azougagh M, Essassi EM, Bouachrine M (2010) Thermodynamic characterisation of steel corrosion in HCl in the presence of 2-phenylthieno (3, 2-b) quinoxaline. J Mater Environ Sci 1:1–8
Singh AK, Quraishi MA (2010) The effect of some bis-thiadiazole derivatives on the corrosion of mild steel in hydrochloric acid. Corros Sci 52:1373–1385
El Belghiti M, Karzazi Y, Dafali A, Hammouti B, Bentiss F, Obot IB, Bahadur I, Ebenso EE (2016) Experimental, quantum chemical and Monte Carlo simulation studies of 3, 5-disubstituted-4-amino-1, 2, 4-triazoles as corrosion inhibitors on mild steel in acidic medium. J Mol Liq 218:281–293
Saha SK, Hens A, Murmu NC, Banerjee P (2016) A comparative density functional theory and molecular dynamics simulation studies of the corrosion inhibitory action of two novel N-heterocyclic organic compounds along with a few others over steel surface. J Mol Liq 215:486–495
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Alaoui, K., Ouakki, M., Abousalem, A.S. et al. Molecular Dynamics, Monte-Carlo Simulations and Atomic Force Microscopy to Study the Interfacial Adsorption Behaviour of Some Triazepine Carboxylate Compounds as Corrosion Inhibitors in Acid Medium. J Bio Tribo Corros 5, 1 (2019). https://doi.org/10.1007/s40735-018-0196-2
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40735-018-0196-2