Abstract
The present investigations on generative manufacturing using metallic materials pursue the idea of transferring the microscopic structural morphology of a dual-phase steel in modified form to the macroscopic level. The aim is to be able to join materials of different lattice modifications and to combine their positive properties. This applies in particular to the combination of high tensile strength and good formability. For this investigation, a specimen was created from a high-strength ferritic/martensitic (25%) and an austenitic (75%) material with a defined welding sequence. The specimen was deliberately manufactured anisotropically using welding layers in order to quantify its properties. Tensile tests were performed on specimens with different weld seam orientations to determine the direction-dependent properties. As can be proven by the results, the application of welding processes with different materials results in an anisotropic behaviour in generative manufacturing. With regard to tensile strength and elongation, there is an integral value of the mechanical-technological properties of both base materials. The existing anisotropy can be utilized with regard to the design by adapting the alignment of the weld layers to the load.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The increasing importance of resource-efficient handling of raw materials is driving development to design components more efficiently. As a result, manufacturing processes are being reorganized and the trend is that components are no longer milled from the “solid”, but generated using 3D printing processes. Generative manufacturing processes, such as wire arc additive manufacturing (WAAM), can increase the degree of material utilization [1,2,3,4]. The CMT arc welding technology is feasible for manufacturing bead structures [5,6,7]. Furthermore, this process offers the possibility of a multi-material design. For this purpose, different materials are specifically combined with each other in order to adjust local mechanical properties to the strains. For the targeted adjustment of the mechanical properties, the basic idea is to transfer the microscopic structure of the dual-phase steel or duplex steel in modified form to the macroscopic level [7]. The combination of morphologies is intended to utilize advantages of the microstructures, thereby increasing the effectiveness and variety of possible part designs. In addition, the arc-based generative manufacturing offers the possibility to locally adjust the material properties depending on the load, due to the process immanent conditions. This kind of multi-material design is exclusive to additive manufacturing processes.
Furthermore, an anisotropic behaviour can be achieved by using welding layers. The mechanical properties are specifically enhanced by the alignment of the layers. The result of this targeted integration of materials and layer alignment is an exact adjustment of the mechanical properties to the existing strains [8].
2 Basics
The primary goal of the investigations is the validation of the welding feasibility of a multi-material design. The microscopic structure of duplex and dual-phase steels, as shown schematically in Fig. 1, serves as a template for the layer structure. Duplex steels consist of equal parts of ferrite and austenite, as shown in Fig. 1a. They combine the advantages of both microstructures. Ferritic steels have a high strength. Austenitic steels, on the other hand, are characterized by high toughness. This combination produces very good mechanical and technological properties [10].
Figure 1b shows the schematic representation of a dual-phase steel, which are characterized by a low carbon content and consist of a ferritic matrix in which about 20% martensite is embedded [11].
These two microstructures result in a fusion of the positive properties of the individual parts. This principle can, in a figurative sense, be applied to the macroscopic level. Above all, the combination of the different advantages of the different materials should lead to an adaptation of the mechanical properties [12, 13].
A soft metal matrix reinforced with hard areas improves the mechanical-technological properties with regard to strength and toughness.
The specimen will be welded by stringer bead welding. The soft matrix is represented by the austenitic FeNi36 with the standard designation EN Ni36 (Table 1). The high-strength part is a filler metal Mn4Ni1,5CrMo with the standard designation DIN EN ISO 16834-A G 69 [15] (Table 2).
Both the pure welding wires and the weld metal of the Mn4Ni1,5CrMo are classified in the Schaeffler diagram in form of the nickel and chromium equivalent, with FeNi36 being outside the evaluable range.
Formula for calculating the nickel equivalent [17]:
Formula for calculating the chrome equivalent [17]:
3 Experimental investigation
To produce the specimen, the layers of the FeNi36 were welded first. The Mn4Ni1,5CrMo welding beads were inserted into the gaps between the weld seams. This procedure creates a soft matrix with high-strength components. Due to the simple layer structure for welding, the soft matrix represents in this first investigation a percentage of 75% of the test specimen with an insular distribution of the high-strength steel. This can be seen schematically in Fig. 2.
3.1 Welding parameters
Due to the different welding filler materials, different welding parameters are required to produce the specimen with alternating line beads. The parameters listed in Table 3 have shown a particularly good surface quality between the individual bead layers.
To produce the specimen, three stringer beads of FeNi36 were alternately welded to one stringer bead of Mn4Ni1,5CrMo. As seen in Fig. 2, the white parts are the FeNi36 and were welded first from left to right and let gaps on the black parts. These parts were filled after a change of the welding wire with stringer beads of Mn4Ni1,5CrMo. In this layer structure, test piece was built up a height of ten layers. The welded specimen is shown in Fig. 3.
3.2 Sample preparation
To investigate the mechanical-technological properties and a possible anisotropy of the multi-material design, tensile samples were taken. These were manufactured in different orientations to the weld layers and then subjected to destructive tensile tests.
The alignments are transverse upright to the welding direction, transverse flat to the welding direction and longitudinal upright to the welding direction. These are shown schematically in Fig. 4. The different alignments are used to investigate whether anisotropic behaviour occurs and whether multi-material construction is feasible.
In addition, a microsection and a specimen for hardness measurement were created from the welded specimen. The transition areas between FeNi36 and Mn4Ni1,5CrMo were examined metallographically. The joining of the two materials and the absence of cracks, pores and inclusions were carefully examined. Furthermore, the microstructures are analysed.
4 Results
4.1 Structural morphology
The morphology of the microstructures is examined and their susceptibility to hot and cold cracking is classified with reference to the Schaeffler diagram. Only the weld metal of the Mn4Ni1,5CrMo is classified by the diagram, since the FeNi36 is outside the nickel equivalent and therefore cannot be determined. The weld metal of the Mn4Ni1,5CrMo is calculated with a process-related mixing of 20%. According to formula (1), this results in a nickel equivalent NiEqu,weld metal,Mn4Ni1,5CrMo = 12.331%, and according to formula (2), a chromium equivalent of CrEqu,weld metal,Mn4Ni1,5CrMo = 1.676%. In comparison, the pure filler metal equals to NiÄqu,Mn4Ni1,5CrMo = 5.135% and CrÄqu,Mn4Ni1,5CrMo = 1.715%. If these values are classified in the Schaeffler diagram, the points shown in Fig. 5 result. The pure filler metal Mn4Ni1,5CrMo is in the purely martensitic range and is susceptible to cold cracking. Through the combination with FeNi36, the Mn4Ni1,5CrMo weld metal is shifted in the direction of the martensitic-austenitic range. This shift increases the susceptibility to hot cracking because of 20% mixing with FeNi36, while the susceptibility to cold cracking below 400 °C remains unchanged.
Figure 6 shows that layer 1 has a martensitic structure. The needle-like structure of the martensitic is homogeneously distributed over the entire section. Compared with the other layers, it is finer-grained, since no further welding process takes place over these layers and thus no additional heat influence on the microstructure occurs. The black spots in the microstructure are the smallest carbides formed from the melt.
Layer 2 also has a martensitic structure with austenitic and ferritic islands, depends on the mixing in the stinger bead. Since this was reheated due to the layer welded above it, part of the carbon, dissolved in the body-centred tetragonal martensite lattice, could diffuse and thus fold down into austenite and a body-centred cubic ferritic lattice.
Figure 7 shows that layer 3 has larger areas of ferrite and austenite than layer 1 or 2. This is due to the heat input by the welding process. It is noticeable that the ferrite is acicular, as it has no time to grow due to the cooling speed. This also applies to layer 4. In contrast to layer 3, this microstructure is finer and more homogeneous. Due to the influence of temperature, cementite is precipitated at the ferrite grain boundaries by diffusion processes. In addition, no carbides are visible in the lower layers.
The microstructure of the cross section was examined to determine the microstructure morphologies of the individual phases. The high-strength weld seams made of Mn4Ni1,5CrMo have an austenitic-ferritic/martensitic structure. The soft matrix of FeNi36, on the other hand, consists entirely of austenite.
Figure 8 shows the transition of the high-strength beads to the soft matrix. This shows two microstructures, which are separate from each other, as it corresponds to the idea. Furthermore, neither pores, cracks nor inclusions are visible. This shows that ferritic/martensitic and austenitic microstructures can exist side by side without a clear transition zone. The mixing between the two layers is marginal due to the low heat input. In order to avoid undesired effects such as brittle phase formation in the mixing zone, the two types of microstructure must be clearly separated from each other.
4.2 Material characteristics
The hardness distribution diagram in Fig. 9 shows the homogeneously distributed hardness of the FeNi36.The high-strength inclusions are clearly visible in the hardness measurement. This macrostructure resembles the microscopic appearance of a dual-phase steel and represents the basic idea of hard phases in a soft matrix.
To evaluate the mechanical properties, the tensile strength of the welded test piece is determined. A possible anisotropy can be detected by comparing the yield strength and ductility.
The mechanical properties of the base materials are listed in Table 4 for comparison.
Based on the mechanical properties of the base materials, the objective is to achieve an improvement in yield strength and tensile strength compared with FeNi36 and to approximate the yield strength and tensile strength of Mn4Ni1,5CrMo, while increasing ductility. However, welding defects cannot be excluded. These reduce the elongation at break under certain circumstances. The reason for this may be the selected layer structure, which will be modified and optimized in further investigations.
The mechanical properties of the welding specimens in Table 5 show that the yield strength as well as the tensile strength of the specimens is higher compared with FeNi36. The alignment with the respective tensile strengths and yield strengths is illustrated in Fig. 10. A supporting effect is achieved in the soft matrix with the high-strength incorporation. If the yield strengths are calculated according to the mixing rule using the phase fractions of FeNi36 and Mn4Ni1,5CrMo from base metal values, this is calculated as Rp0.2 = 412 N/mm2. This value is below the experimentally determined values of the multi-material design. The phase fraction of the Mn4Ni1,5CrMo is higher, especially in the case of the sample with its longitudinal edge, due to the alignment. This is where the yield strength reaches the maximum value. The calculated determination of the tensile strength also results in a lower value than the experimental determination. The tensile strength calculated according to the mixing rule is Rm = 565 N/mm2 from base metal values. The behaviour of the tensile strength is analogous to that of the yield strength and withstands the highest loads when stress is parallel to the welding direction.
If the tensile strength and ductility values are compared on the basis of the different layer orientation, it can be seen that an anisotropic behaviour in the workpiece can be achieved by using GMAW layers. In fact of welding defects, the ductility of the test specimen shows a loss.
The tensile strength and ductility show the anisotropic properties of the specimen based on the welding direction. This can therefore be used in the wire arc additive manufacturing of load-adjusted workpieces.
5 Conclusion
The presented investigations show that a multi-material component design is achievable in arc-based generative manufacturing. Furthermore, it was shown that through the multi-material design, the material properties can be adapted locally to the load, since the two materials can be processed with each other without a clear transition zone. The tensile tests have shown that the soft matrix is supported by the high-strength inclusions and thus has a higher yield strength and tensile strength. Welding defects of the test specimen effect in a loss of ductility. In addition, a greater increase in yield strength and tensile strength can be achieved through the use of the multi-material design than would be expected through the mathematical determination. After comparing the mechanical properties for the different orientations, an anisotropy of the material can be determined by using GMAW processes. This is of great advantage with regard to resource-efficient, load-oriented design adapted to local properties.
6 Outlook
The main focus is on investigating the ductility of the samples. This should be improved by a different layer arrangement. As further investigations, the influences on the fatigue strength are to be examined more closely. The aim is to examine the crack growth in a targeted manner. Furthermore, follow-up tests with different metal combinations will follow.
References
Ding J, Martina F, Lockett H, Williams S et al (2015) Manufacture of complex titanium parts using wire+arc additive manufacture adrian addison. Titanium Europe
Artaza T, Alberdi A, Murua M et al (2017) Design and integration of WAAM technology and in situ monitoring system in a gantry machine. Manufacturing Engineering Society International Conference 2017
Bekker ACM, Verlinden JC , Galimberti G (2016) Callenges in assessing the sustainability of wire + arc additive. In: Solid Freeform Fabrication, Austin TX
Chabot A, Rauch M, Hascoët J-Y (2019) Towards a multi-sensor monitoring methodology for AM metallic processes. Welding in the World 63:759–769
Rodriguez N, Vázquez L, Huarte I, Arruti E, Tabernero I, Alvarez P (2018) Wire and arc additive manufacturing: a comparison between CMTand TopTIG processes applied to stainless steel. Welding in the World 62:1083–1096
Posch G, Chladil K, Chladil H (2017) Material properties of CMT—metal additive manufacturedduplex stainless steel blade-like geometries. Weld World 61:873–882
Hosseini VA, Högström M, Hurtig K, Bermejo MAV, Stridh L-E, Karlsson L (2019) Wire-arc additive manufacturing of a duplex stainless steel: thermalcycle analysis and microstructure characterization. Welding in the World
Leicher M, Treutler K, Kamper S, Wesling V (2019) Multimaterial design in der additiven Fertigung - Validierung der Machbarkeit. Tagungsband 3. Niedersächsisches Symposium Materialtechnik, pp 37–48
Hornbogen E (1983) Werkstoffe. Springer-Verlag Verlin Heidelberg
Schulze G (2010) Die Metallurgie des Schweißens. Springer-Verlag Berlin Heidelberg, Heidelberg
Weißbach W (2010) Werkstoffkunde, 17. Auflage ed., Vieweg+Teubner, Ed. Wiesbaden: GWV Fachverlage GmbH
Li X (2018) Additive manufacturing of advanced multi-component alloys: bulk metallic glasses and high entropy alloys. Adv Eng Mater 20
Zhang D, Sun S, Qiu D, Gibson MA, Dargusch MS, Brandt M, Qian M, Easton M (2018) Metal alloys for fusion-based additive manufacturing. Adv Eng Mater 20
METALCOR, “www.metalcor.de,” 16. Januar 2019. [Online]. Available: www.metalcor.de/datenblatt/79/
DIN Deutsches Institut für Normung e.V., “Schweißzusätze –Drahtelektroden, Drähte, Stäbe und Schweißgut zumSchutzgasschweißen von hochfesten Stählen –Einteilung (ISO 16834:2012);Deutsche Fassung EN ISO 16834:2012,” Beuth Verlag GmbH, Berlin, 2012
Hermann Fliess & Co. GmbH, “Fliess,” 16. Januar 2019. [Online]. Available: www.fliess.com
Matthes K-J, Schneider W (2012) Schweißtechnik. Schweißen von metallischen Konstruktionswerkstoffen. München, Fachbuchverlag Leipzig im Carl Hanser Verlag
Acknowledgements
The authors thank the company Fliess for providing the welding filler metals.
Funding
Open Access funding provided by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Recommended for publication by Commission I - Additive Manufacturing, Surfacing, and Thermal Cutting
This article is part of the collection Additive Manufacturing – Processes, Simulation and Inspection
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Leicher, M., Kamper, S., Treutler, K. et al. Multi-material design in additive manufacturing—feasibility validation. Weld World 64, 1341–1347 (2020). https://doi.org/10.1007/s40194-020-00887-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40194-020-00887-2