Abstract
In tissue engineering, alginate has been an attractive material due to its biocompatibility and ability to form hydrogels, unless its uncontrollable degradation could be an undesirable feature. Here, we developed a simple and easy method to tune the degradation profile of the fibrous alginate scaffolds by the microfluidic wet spinning techniques, according with the use of isopropyl alcohol for dense packing of alginate chains in the microfiber production and the increase of crosslinking with Ca2+ ion. The degradation profiling was analyzed by mass losses, swelling ratios, and also observation of the morphologic changes. The results demonstrated that high packing density might be provided by self-aggregation of polymer chains through high dipole interactions between sheath and core fluids and that the increase of crosslinking rates could make degradation of alginate scaffold controllable. We suggest that the tunable degradation of the alginate fibrous scaffolds may expand its utilities for biomedical applications such as drug delivery, in vitro cell culture, wound healing, tissue engineering and regenerative medicine.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
Langer R, Vacanti JP. Tissue engineering. Science 1993;260:920–926.
Langer R, Tirrell DA. Designing materials for biology and medicine. Nature 2004;428:487–492.
Fisher MB, Mauck RL. Tissue engineering and regenerative medicine: recent innovations and the transition to translation. Tissue Eng Part B Rev 2013;19:1–13.
Kuo CK, Ma PX. Ionically crosslinked alginate hydrogels as scaffolds for tissue engineering: part 1. Structure, gelation rate and mechanical properties. Biomaterials 2001;22:511–521.
Lee KY, Rowley JA, Eiselt P, Moy EM, Bouhadir KH, Mooney DJ. Controlling mechanical and swelling properties of alginate hydrogels independently by cross-linker type and cross-linking density. Macromolecules 2000;33:4291–4294.
Paguirigan A, Beebe DJ. Gelatin based microfluidic devices for cell culture. Lab Chip 2006;6:407–413.
Khademhosseini A, Langer R. Microengineered hydrogels for tissue engineering. Biomaterials 2007;28:5087–5092.
Geckil H, Xu F, Zhang X, Moon S, Demirci U. Engineering hydrogels as extracellular matrix mimics. Nanomedicine (Lond) 2010;5:469–484.
Lee BR, Hwang JW, Choi YY, Wong SF, Hwang YH, Lee DY, et al. In situ formation and collagen-alginate composite encapsulation of pancreatic islet spheroids. Biomaterials 2012;33:837–845.
Lee BR, Lee KH, Kang E, Kim DS, Lee SH. Microfluidic wet spinning of chitosan-alginate microfibers and encapsulation of HepG2 cells in fibers. Biomicrofluidics 2011;5:22208.
Jun Y, Kang AR, Lee JS, Jeong GS, Ju J, Lee DY, et al. 3D co-culturing model of primary pancreatic islets and hepatocytes in hybrid spheroid to overcome pancreatic cell shortage. Biomaterials 2013;34:3784–3794.
Barnett SE, Varley SJ. The effects of calcium alginate on wound healing. Ann R Coll Surg Engl 1987;69:153–155.
Lee KH, Shin SJ, Kim CB, Kim JK, Cho YW, Chung BG, et al. Microfluidic synthesis of pure chitosan microfibers for bio-artificial liver chip. Lab Chip 2010;10:1328–1334.
Jeon O, Bouhadir KH, Mansour JM, Alsberg E. Photocrosslinked alginate hydrogels with tunable biodegradation rates and mechanical properties. Biomaterials 2009;30:2724–2734.
Ashton RS, Banerjee A, Punyani S, Schaffer DV, Kane RS. Scaffolds based on degradable alginate hydrogels and poly(lactide-co-glycolide) microspheres for stem cell culture. Biomaterials 2007;28:5518–5525.
Abdi SIH, Choi JY, Lau HC, Lim JO. Controlled release of oxygen from PLGA-alginate layered matrix and its in vitro characterization on the viability of muscle cells under hypoxic environment. Tissue Eng Regen Med 2013;10:131–138.
Lee KY, Mooney DJ. Alginate: properties and biomedical applications. Prog Polym Sci 2012;37:106–126.
Doyle JW, Roth TP, Smith RM, Li YQ, Dunn RM. Effects of calcium alginate on cellular wound healing processes modeled in vitro. J Biomed Mater Res 1996;32:561–568.
Bouhadir KH, Lee KY, Alsberg E, Damm KL, Anderson KW, Mooney DJ. Degradation of partially oxidized alginate and its potential application for tissue engineering. Biotechnol Prog 2001;17:945–950.
Shin Y, Han S, Jeon JS, Yamamoto K, Zervantonakis IK, Sudo R, et al. Microfluidic assay for simultaneous culture of multiple cell types on surfaces or within hydrogels. Nat Protoc 2012;7:1247–1259.
Andersson H, van den Berg A. Microfabrication and microfluidics for tissue engineering: state of the art and future opportunities. Lab Chip 2004;4:98–103.
El-Ali J, Sorger PK, Jensen KF. Cells on chips. Nature 2006;442:403–411.
Chae SK, Kang E, Khademhosseini A, Lee SH. Micro/nanometer-scale fiber with highly ordered structures by mimicking the spinning process of silkworm. Adv Mater 2013;25:3071–3078.
Ahn SY, Mun CH, Lee SH. Microfluidic spinning of fibrous alginate carrier having highly enhanced drug loading capability and delayed release profile. RSC Adv 2015;5:15172–15181.
Shin SJ, Park JY, Lee JY, Park H, Park YD, Lee KB, et al. “On the fly” continuous generation of alginate fibers using a microfluidic device. Langmuir 2007;23:9104–9108.
Hwang CM, Khademhosseini A, Park Y, Sun K, Lee SH. Microfluidic chip-based fabrication of PLGA microfiber scaffolds for tissue engineering. Langmuir 2008;24:6845–6851.
Oh SY, Yoo DI, Shin Y, Kim HC, Kim HY, Chung YS, et al. Crystalline structure analysis of cellulose treated with sodium hydroxide and carbon dioxide by means of X-ray diffraction and FTIR spectroscopy. Carbohydr Res 2005;340:2376–2391.
Yuno-Ohta N, Yamada M, Inomata M, Konagai H, Kataoka T. Gluten gel and film properties in the presence of cysteine and sodium alginate. J Food Sci 2009;74:E285–E290.
Hong JS, Shin SJ, Lee SH, Wong E, Cooper-White J. Spherical and cylindrical microencapsulation of living cells using microfluidic devices. Korea-Aust Rheol J 2007;19:157–164.
Zhang ZM, Wan MX, Wei Y. Highly crystalline polyaniline nanostructures doped with dicarhoxylic acids. Adv Funct Mater 2006;16:1100–1104.
Kim JH, Noh H, Kang JH, Lee BS, Choi J, Park K, et al. Characteristics of PLLA films blended with PEG block copolymers as additives for biodegradable polymer stents. Biomed Eng Lett 2011;1:42–48.
Dhandayuthapani B, Yoshida Y, Maekawa T, Kumar DS. Polymeric scaffolds in tissue engineering application: a review. Int J Polym Sci 2011 [Epub]. http://dx.doi.org/10.1155/2011/290602.
Ghim JH, Hussein KH, Park KM, Woo HM. Hepatic cell encapsulation using a decellularized liver scaffold. Biomed Eng Lett 2015;5:58–64.
Shasteen C, Choy YB. Controlling degradation rate of poly(lactic acid) for its biomedical applications. Biomed Eng Lett 2011;1:163–167.
Andersen T, Melvik JE, Gåserød O, Alsberg E, Christensen BE. Ionically gelled alginate foams: physical properties controlled by type, amount and source of gelling ions. Carbohydr Polym 2014;99:249–256.
Grant GT, Morris ER, Rees DA, Smith PJC, Thom D. Biological interactions between polysaccharides and divalent cations: the egg-box model. FEBS Lett 1973;32:195–198.
Morris ER, Powell DA, Gidley MJ, Rees DA. Conformations and interactions of pectins. I. Polymorphism between gel and solid states of calcium polygalacturonate. J Mol Biol 1982;155:507–516.
Blandino A, Macías M, Cantero D. Formation of calcium alginate gel capsules: influence of sodium alginate and CaCl2 concentration on gelation kinetics. J Biosci Bioeng 1999;88:686–689.
Bajpai SK, Sharma S. Investigation of swelling/degradation behaviour of alginate beads crosslinked with Ca2+ and Ba2+ ions. React Funct Polym 2004;59:129–140.
Pasparakis G, Bouropoulos N. Swelling studies and in vitro release of verapamil from calcium alginate and calcium alginate-chitosan beads. Int J Pharm 2006;323:34–42.
Mason MN, Metters AT, Bowman CN, Anseth KS. Predicting controlled-release behavior of degradable PLA-b-PEG-b-PLA hydrogels. Macromolecules 2001;34:4630–4635.
Lu L, Peter SJ, Lyman MD, Lai HL, Leite SM, Tamada JA, et al. In vitro and in vivo degradation of porous poly(DL-lactic-co-glycolic acid) foams. Biomaterials 2000;21:1837–1845.
Chae SK, Mun CH, Noh DY, Kang E, Lee SH. Simple fabrication method for a porous poly(vinyl alcohol) matrix by multisolvent mixtures for an air-exposed model of the lung epithelial system. Langmuir 2014; 30: 12107–12113.
Kang E, Jeong GS, Choi YY, Lee KH, Khademhosseini A, Lee SH. Digitally tunable physicochemical coding of material composition and topography in continuous microfibres. Nat Mater 2011;10:877–883.
Jeong GS, Lee SH. Microfluidic spinning of grooved microfiber for guided neuronal cell culture using surface tension mediated grooved round channel. Tissue Eng Regen Med 2014;11:291–296.
Jun Y, Kang E, Chae S, Lee SH. Microfluidic spinning of micro-and nano-scale fibers for tissue engineering. Lab Chip 2014;14:2145–2160.
Author information
Authors and Affiliations
Corresponding author
Additional information
These authors contributed equally to this work.
Rights and permissions
About this article
Cite this article
Mun, C.H., Hwang, JY. & Lee, SH. Microfluidic spinning of the fibrous alginate scaffolds for modulation of the degradation profile. Tissue Eng Regen Med 13, 140–148 (2016). https://doi.org/10.1007/s13770-016-9048-7
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13770-016-9048-7