Abstract
Here, two ionic liquids 1-methyl-3-propane sulfonic-imidazolium (PSMIM) and 1-methyl-3-propane sulfonic-imidazolium hydrosulfate (PSMIMHSO4) are synthesized, and these ionic liquids mixed with different of heteropolyacid Cs2.5H0.5PW12O40 have been used as catalysts for esterification of cooking oil for preparation of biodiesel. Then those catalysts are characterized by Infrared spectrometer, X-ray diffractometer, nuclear magnetic resonance, elemental analyses and high-performance liquid chromatography. PSMIM and PSMIMHSO4 mixed with Cs2.5H0.5PW12O40 at the mass ratio of 1:1 are able to effectively catalyze esterification, using cooking oil as starting material at ratio of 1:20 (catalyst/cooking oil) and cooking oil to methanol at mass ratio of 1:6 for preparation of biodiesel with 3.5 h at 343 K. The result showed that 97.1 % yield of biodiesel could be obtained at optimized operation using PSMIMHSO4 mixed with Cs2.5H0.5PW12O40 at the mass ratio of 1:1 as catalyst.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
In the past decades, the global energy shortage and environment deterioration continue to grow rapidly. The quality of life today is dependent upon access to a bountiful supply of affordable and low-cost energy. For a sustainable development, the energy should be derived from non-fossil sources, which are ideally reliable and safe, affordable, and limitless. Therefore, development of clean alternative fuels and renewable energy has become an important subject for world-wide researchers. Because of its environmentally friendliness, renewability and other advantages, biodiesel is expected to replace traditional diesel fuel to meet the needs of sustainable development of society [1, 2]. At present, biodiesel production mainly uses a variety of oils and lower alcohol as raw materials, and acid and alkalinity can be used as catalyst [3] such as homogeneous acid or base, lipase, or heterogeneous acid or base catalysts. Conventionally, this reaction is carried out using homogeneous acid or base catalysts, such as sulfonic acid, potassium hydroxide, sodium hydroxide, or their alkoxides [4–8]. However, these catalysts are corrosive and are not easily recovered, leading to the release of environmentally unfriendly effluents, which inevitably leads to a series of environmental problems. Because of the detrimental effects of these catalysts, great efforts directed toward the development of environmentally friendly catalysts have been made. The use of lipases as biocatalysts for biodiesel production has been of great interest due to its environmental friendliness [9–12]. However, some alcohols such as methanol deactivate the lipase to some extent and the enzyme stability was poor. Moreover, glycerol, which is a byproduct, easily adsorbs on the surface of the lipase and inhibits the enzyme activity. Although heterogeneous acid or base catalysts are environmentally friendly, they also have drawbacks, such as low catalytic activity and deactivation [3, 13–15]. Due to the disadvantages of equipment corrosion and separation difficulty, concentrated sulfuric acid is much maligned in the esterification stage [16–20].
Keggin heteropoly acids (HPAs) have been reported to have the potential for biodiesel synthesis [14, 21–27]. Solid super acid Cs2.5H0.5PW12O40 is not only BrÖnsted acid, but also Lewis acid, which has good catalytic activity, selectivity, and corrosion resistance [28, 29]. The activity of Cs2.5H0.5PW12O40 relative to the other catalysts became higher than conventional acids such as H2SO4, Al2O3–SiO2, zeolites and acidic resins [15, 30–32]. Cs2.5H0.5PW12O40 is a widely applicable water-tolerant solid acid. As an important green solvent, acidic ionic liquids (ILs) can dissolve a variety of solute and favor the dispersion of catalyst in catalytic phase transfer reaction. Ionic liquids have attracted much interest as relatively clean and promising catalysts and alternative solvents that possess important attributes, such as wide liquid range, negligible vapor pressure, high catalytic activity, excellent chemical and thermal stability, potential recoverability, design possibilities, and ease of separation of the products from reactants [33–37]. Meanwhile acidic ionic liquid could also improve the acid catalytic performance [38]. Due to the booming demand of biodiesel and the limitations of traditional method, a novel method for the synthesis of biodiesel has been highly desirable. The method of mixing phosphotungstic salt with ionic liquid presents the remarkable advantage over the high yield of esterification.
In this study, 1-methyl-3-propane sulfonic-imidazolium (PSMIM), 1-methyl-3-propane sulfonic-imidazolium hydrosulfate (PSMIMHSO4) and Cs2.5H0.5PW12O40 were prepared. Performances of two ionic liquids mixed with Cs2.5H0.5PW12O40 were, respectively, evaluated as catalysts in the esterification. Catalysts were characterized by nuclear magnetic resonance (NMR), infrared (IR) spectroscopy, elemental analyses, X-ray diffractometer (XRD) and high-performance liquid chromatography (HPLC). The effects of varying reaction conditions on the production of biodiesel were extensively studied and compared to different catalysts.
Experimental
Preparation of PSMIM
1,3-propyl sulfonic acid (40.0 g) was completely dissolved in 300 mL toluene. N-methyl imidazole (27.0 g) was slowly added while being stirred under an ice bath. Then the temperature was slowly raised to 298 K and maintained for 2 h. The product was then filtered from the mixture liquid and washed with diethyl ether and ether acetate for three times, respectively. The solid was obtained after heating at 343 K for 5 h [38].
Preparation of PSMIMHSO4
PSMIM (23.3 g) was dissolved in 100 mL deionized water. Then sulfuric acid (10.9 g) was slowly added while being stirred at room temperature. After that, the temperature was raised to 363 K and then maintained for 2 h. The deionized water was removed from the product using a rotary evaporator [38].
Preparation of Cs2.5H0.5PW12O40
An aqueous solution of Cs2CO3 (0.3528 g) was added drop-wise to an H3PW12O40·19H2O (2.8000 g) solution under vigorous stirring. The fine suspension was held at room temperature overnight and subsequently to dryness at 323 K. The ratio polyacid–cesium carbonate was regulated in such a way that the final stoichiometry corresponded to Cs2.5H0.5PW12O40 [39].
Preparation of mixture catalysts
PSMIM was mixed with Cs2.5H0.5PW12O40 with deionized water as catalyst at room temperature and dried at 353 K, while mixing at the mass ratio of 1:1 named PSC. Meanwhile, PSMIMHSO4 was mixed with Cs2.5H0.5PW12O40 with the same method, while mixing at the mass ratio of 1:1 named PSSC.
Preparation of biodiesel
Cooking oil (10 g), methanol and the catalyst [40, 41] were taken into a flask with stirring and refluxing. Then the catalyst was separated from flask by centrifuge. Subsequently, methanol (5.0 g) and potassium hydroxide (0.25 g) were also added into the flask with stirring and reflux for 0.5 h. The methanol was removed from the product using a rotary evaporator at 313 K, followed by cooling to room temperature. After that, the supernatant was separated from product by centrifuge and quickly subjected for HPLC analysis,
Characterization and evaluation of the catalyst
Infrared spectrometer (AVATAR 370 from Thermo Nicolet) was used to analyze the ionic liquid and heteropoly acid and its salt at 500–4,000 cm−1.
X-ray Diffractometer (Deutschland RUKER D2 PHASER) was scanned with CuKα in the range of 10°–80° at a rate of 0.02°s−1.
Nuclear magnetic resonance (NMR) was used to characterize the ionic liquid.
PSMIM1HNMR (400 MHz, D2O): δ2.138 (m, 2H, J = 7.2 Hz), 2.822 (t, 2H, J = 7.2 Hz), 3.806 (s, 3H), 4.270 (t, 2H, J = 7.2 Hz), 7.365 (s, 1H), 7.437(s, 1H), 8.655 (s, 1H). 13CNMR (400 MHz, D2O): δ25.11, 35.73, 47.24, 47.72, 122.16, 123.76, 136.17.
PSMIMHSO 14 HNMR (400 MHz, D2O): δ2.135(t, 2H, J = 7.2 Hz), 2.745 (s, 2H), 3.717 (s, 3H), 4.181 (t, 2H, J = 7.2 Hz), 7.271 (s, 1H), 7.339 (s, 1H), 8.560 (s, 1H). 13CNMR(400 MHz, D2O): δ24.99, 35.65, 47.15, 47.65, 122.10, 123.71, 136.06.
Elemental analyses (EA) were performed on a Perkin-Elmer 2,400 elemental analyzer for C, H, N and S. Anal. calc. for PSMIM: C, 41.18 %; H, 5.88 %; N, 13.73 %; S, 15.69 %; found: 41.24 %; H, 5.83 %; N, 13.74 %, S, 15.65 %. Anal. calc. for PSMIMHSO4: C, 27.81 %; H, 4.64 %; N, 9.27 %; S, 21.19 %. found: C,27.83 %; H, 4.60 %; N, 9.33 %; S, 21.14 %.
The purity of the ionic liquid was analyzed by HPLC (Agilent1100). The conditions of HPLC: separation column is the ODS C18. Water and methanol were used as a mobile phase, the ratio of water and methanol was 1:9 and the speed was 1.0 mL/min. The detectable wavelength of UV was 215 nm at room temperature.
Analysis
The yield was analyzed by HPLC (Agilent1100). The conditions of HPLC: separation column is the ODS C18. Acetonitrile was used as a mobile phase at a flow rate of 1.0 mL/min. The volume of each sample was 15 µL. The detectable wavelength of UV was 205 nm at room temperature.
The calculation formula is:
Yield of biodiesel = (Conversion of cooking oil) × (Selectivity of cooking oil to biodiesel formation)
Result and discussion
FT-IR of ionic liquids
Figure 1 shows FT-IR of sulfonic acid ionic liquids. The peaks at 3156, 3116 and 1575 cm−1 represent –N–H, –C–H and –C=N– stretching vibration of the imidazole ring, respectively. The peaks from 2,965 to 2,992 cm−1 are ascribed to the C–H stretching vibration of –CH2 and N–CH2, and the peaks at 1,487 and 1,398 cm−1 are formation vibration of CH2 and CH3. The peak at 749 cm−1 is the bending vibration of the imidazole ring. Meanwhile, a strong peak appears at 1,171 cm−1, which is the S=O stretching vibration of HSO4- and -SO3 [38].
FT-IR of phosphotungstic acid and its salt
Figure 2 shows FT-IR of phosphotungstic acid and its salt. The peaks at 1,075, 976, 904 and 787 cm−1 represent H3PW12O40·19H2O. The peaks at 1078, 983, 889 and 785 cm−1 represent Cs2.5H0.5PW12O40. It can be seen that H3PW12O40·19H2O and Cs2.5H0.5PW12O40 keep the Keggin structure of phosphotungstic acid from FT-IR. The peak at 1,078 cm−1 belongs to P-Oa (Oa-oxygen atoms bound to three W atoms and to P) stretching vibration of the center of tetrahedron. The peak at 983 cm−1 is W-Ob (Ob-terminal oxygen atom) vibration. The peak at 889 cm−1 is W-Oc-W (Oc-corner sharing bridging oxygen atom) vibration. The peak at 785 cm−1 is W-Oe-W (Oe-edge sharing bridging oxygen atom) vibration [39, 42]. When Cs2.5H0.5PW12O40 mixed with ionic liquids, compounds also keep the Keggin structure of phosphotungstic acid and the structure of ionic liquids.
XRD of phosphotungstic acid and its salt
XRD patterns of t phosphotungstic acid and its salt are shown in Fig. 3. XRD patterns of H3PW12O40·19H2O at 8.5°, 10.6°, 20.4° and 27.9° are the characteristic peaks. XRD patterns of Cs2.5H0.5PW12O40 at 10.4°, 18.3°, 26.0°, 30.1° and 35.4° are the characteristic peaks [39, 42]. As H3PW12O40·19H2O and Cs2.5H0.5PW12O40 remain the same, characteristic peaks of XRD patterns, it is concluded that Cs2.5H0.5PW12O40 keep the Keggin structure.
Effect of mass ratio of mixed catalytic system
Cs2.5H0.5PW12O40 was mixed with PSMIMHSO4 at different mass ratio to catalyze the reaction at 343 K for 3.5 h.
Figure 4 shows that the yield of biodiesel rises, as the ratio of PSMIMHSO4 is increasing. After the mass ratio of 1:1, the yield of biodiesel rises slowly. Thus, the optimized mass ratio is 1:1 in the reaction.
Effect of reaction temperature
The experiment of esterification was tested while using PSSC (0.5 g) as catalyst from 313 to 363 K for 3.5 h, cooking oil was 10 g and methanol was 60 g. By adjusting the temperature of water bath kettle to what it is needed.
Figure 5 shows that the yield of biodiesel significantly increases with the rising of the temperature. From Fig. 5, it is observed that the higher activity is favored at high temperature, which is likely related to that the more H+ released from the ionic liquid at higher temperature, thus leading to the stronger acidity, and the higher yield [38]. Meanwhile, the acidic activity of Cs2.5H0.5PW12O40 also is increasing while rising the temperature. After 343 K, the yield of biodiesel is nearly full and yield incremental very slow. Thus, 343 K is the temperature to obtain the satisfactory esterification yield.
Effect of reaction time
The experiment of esterification was tested while using PSSC (0.5 g) as catalyst at 343 K by adjusting the time.
The effect of reaction time on the yield is presented (Fig. 6). It can be seen from Fig. 6 that the PSSC is very efficient for biodiesel. The high yield 97.1 % is achieved after 3.5 h, which is very high for biodiesel synthesis from cooking oil [43, 44]. It is generally known that the biodiesel reaction is carried out through three steps. The triglycerides are transformed to diglycerides, monoglycerides and glycerol. The byproduct content would cause the hydrolysis of the ester compounds. The diglycerides and monoglycerides have both the hydrophobic long carbon chain and the hydrophilic hydroxyl, which can bring the water to the acid sites. The yield varies little after 3.5 h, which remained nearly constant, indicating a nearly equilibrium yield. Therefore, the appropriate reaction time is 3.5 h.
Effect of the mass of catalyst
The experiment of esterification was tested while using PSSC as catalyst at different mass at 343 K for 3.5 h.
In Fig. 7, the influence of the mass of catalyst is presented. The optimum mass of catalyst was found to be 0.5 g in this reaction. The excessive of the catalyst did not lead to an obvious further increase in yield, indicating a nearly equilibrium yield was achieved.
Effect of the methanol amount
The experiment of esterification was tested while using PSSC as catalyst at different mass at 343 K for 3.5 h.
The mass ratio of the cooking oil and methanol is investigated (Fig. 8). The methanol amount is vital for the reaction. Since the reaction involved in biodiesel is reversible, one would expect that increasing the amount of methanol would shift the reaction equilibrium toward the products [45]. The biodiesel would produce water and the byproduct water would cause the hydrolysis of the ester, which reduced the yield. More methanol promotes the reaction equilibrium forward to obtain the high yield. On the other hand, too much methanol may cause the dilute effect and decrease yield [38]. When 60 g methanol is added, the maximum yield is reached. Therefore, the mass of methanol is optimized as 60 g.
Compared with traditional acid catalysts
By comparing the yield of PSMIM and its functionalized PSMIMHSO4 from Table 1, it is found that the yield of PSMIMHSO4 improves more than PSMIM. It is explained that the presence of the anionic group HSO4− enhanced the acidity of BrÖnsted acid, which improve the activity of ionic liquid and have the positive of acid catalyst in the process of esterification. But the acidity of two ionic liquid is lower than H2SO4, so their yields are lower than H2SO4 [38]. However, the high byproduct content causes the serious hydrolysis of ester products to decrease the yield of reaction. The traditional homogeneous catalyst H2SO4 has relatively low activities for the production of biodiesel. Although H2SO4 has a strong acidity, materials and products are carbonized partly during the process, which reduced the biodiesel quality.
Per equal catalyst weight, H3PW12O40·19H2O is almost as effective as H2SO4 [46] and the yield of H3PW12O40·19H2O is almost the same as H2SO4. H3PW12O40·19H2O is more active than H2SO4 in the reaction and exhibits the great advantage of these H3PW12O40·19H2O as catalyst compared to the traditional catalyst in view of corrosivity. However, H3PW12O40·19H2O is soluble in methanol and difficult to separate from water or methanol. Therefore, salts of alkaline cation Cs+ for H3PW12O40·19H2O are introduced in the study. The salts with large monovalent ions exhibited an impressive performance that they revealed similar activities compared to the parent acid in acid-catalyzed reactions [47]. On the other hand, Cs2.5H0.5PW12O40, which are both BrÖnsted acid and Lewis acid, exhibits larger surface area and higher activity than H3PW12O40·19H2O [46], and the acid activity of Cs2.5H0.5PW12O40 is about 15 times higher than H2SO4 [28]. That is, the yield of Cs2.5H0.5PW12O40 is higher than H3PW12O40·19H2O and H2SO4.
Cs2.5H0.5PW12O40 and ionic liquid are mixed to form new catalytic system to improve the yield. As a result, the yield has been obviously improved. Because ionic liquid has a high viscosity, it could disperse Cs2.5H0.5PW12O40 uniformly so as to increase the contact area of Cs2.5H0.5PW12O40. In addition, the ionic liquid could dissolve the carbon deposition, which could probably cover the acid site of Cs2.5H0.5PW12O40. So it could be used as a phase transfer catalyst. Thus, the yield of mixed catalytic system is improved.
Catalyst reusability
Catalytic stability of Cs2.5H0.5PW12O40/PSMIMHSO4, which is presented in Fig. 9, is evaluated by performing consecutive batch runs with the same catalyst sample, at same conditions. It is found that the yield of biodiesel kept unchanged, even slightly decreased with runs at the first five runs. This may be because the more acids of catalyst are formed under mechanical agitation, which increases the surface area of catalyst to enhance the catalytic property. However, the yield of biodiesel obviously decreased after the sixth run mainly due to the loss of acids in the process of taking sample or separating product. Nevertheless, about 70.1 % yield can still be obtained even when esterification reaction of the 10th run is finished. Therefore, the advantage of esterification using Cs2.5H0.5PW12O40/PSMIMHSO4 as phase transfer catalyst is obvious.
Conclusions
In the present investigation, PSMIM, PSMIMHSO4 and Cs2.5H0.5PW12O40 were successfully prepared. Then two ionic liquids mixed with Cs2.5H0.5PW12O40 were used as the phase transfer catalysts for biodiesel production. And those were characterization by NMR, IR, EA, XRD and HPLC. PSSC was used as a catalyst to test the optimum conditions, which was the mass ratio of 1:1(PSMIMHSO4/Cs2.5H0.5PW12O40). The best reaction temperature was determined at 343 K, the best reaction time was 3.5 h, the optimum mass of catalyst was 0.5 g and the optimum amount of methanol was 60 g. Meanwhile, through the comparison for the catalytic activity of PSMIM, PSMIMHSO4, H2SO4, H3PW12O40·19H2O and Cs2.5H0.5PW12O40, the acid activity of Cs2.5H0.5PW12O40 was higher than others under the same conditions. After mixing, the yield was improved, so the acid activity of the mixed catalytic system was higher than any others. In addition, because of the presence of anionic group HSO4−, the acid activity of Cs2.5H0.5PW12O40 mixed with PSMIMHSO4 was higher than the acid activity of Cs2.5H0.5PW12O40 mixed with PSMIM.
References
Ma F, Hanna MA (1999) Biodiesel production: a review. Bioresour Technol 70:1–15
Gerpen JV (2005) Biodiesel processing and production. Fuel Process Technol 86:1097–1107
Lopez DE, Goodwin JG Jr, Bruce DA, Lotero E (2005) Transesterification of triacetin with methanol on solid acid and base catalysts. Appl Catal A 295:97–105
Crabbe E, Nolasco-Hipolito C, Kobayashi G, Sonomoto K, Ishizaki A (2001) Biodiesel production from crude palm oil and evaluation of butanol extraction and fuel properties. Process Biochem 37:65–71
Al-Widyan MI, Al-Shyoukh AO (2002) Experimental evaluation of the transesterification of waste palm oil into biodiesel. Bioresour Technol 85:253–256
Felizardo P, Neiva Correia MJ, Raposo I, Mendes JF, Berkemeier R, Bordado JM (2006) Production of biodiesel from waste frying oils. Waste Manag 26:487–494
Tapasvi D, Wiesenborn D, Gustafson C (2005) Process model for biodiesel production from various feedstocks. Transact ASAE 48:2215–2221
Vicente G, Martínez M, Aracil J (2005) Optimization of Brassica carinata oil methanolysis for biodiesel production. J Am Oil Chem Soc 82:899–904
Shimada Y, Watanabe Y, Sugihara A, Tominaga Y (2002) Enzymatic alcoholysis for biodiesel fuel production and application of the reaction to oil processing. J Mol Catal B Enzym 17:133–142
Wu H, Zong M, Lou W (2003) Transesterification of fste oil to biodiesel in solvent free system catalyzed by immobilized lipase. Chin J Catal 11:903–908
Xu Y, Du W, Liu D, Zeng J (2003) A novel enzymatic route for biodiesel production from renewable oils in a solvent-free medium. Biotechnol Lett 25:1239–1241
Du W, Xu Y, Liu D, Zeng J (2004) Comparative study on lipase-catalyzed transformation of soybean oil for biodiesel production with different acyl acceptors. J Mol Catal B Enzym 30:125–129
Gryglewicz S (1999) Rapeseed oil methyl esters preparation using héterogeneous catalysts. Bioresour Technol 70:249–253
Suppes GJ, Dasari MA, Doskocil EJ, Mankidy PJ, Goff MJ (2004) Transesterification of soybean oil with zeolite and metal catalysts. Appl Catal A 257:213–223
Jitputti J, Kitiyanan B, Rangsunvigit P, Bunyakiat K, Attanatho L, Jenvanitpanjakul P (2006) Transesterification of crude palm kernel oil and crude coconut oil by different solid catalysts. Chem Eng J 116:61–66
Harmer MA, Sun Q (2001) Solid acid catalysis using ion-exchange resins. Appl Catal A 221:45–62
Sharma M (1995) Some novel aspects of cationic ion-exchange resins as catalysts. React Funct Polym 26:3–23
Chakrabarti A, Sharma M (1993) Cationic ion exchange resins as catalyst. React Polym 20:1–45
Tejero J, Cunill F, Iborra M, Izquierdo J, Fité C (2002) Dehydration of 1-pentanol to di- < i > n </i > -pentyl ether over ion-exchange resin catalysts. J Mol Catal A Chem 182:541–554
Siril P, Cross HE, Brown D (2008) New polystyrene sulfonic acid resin catalysts with enhanced acidic and catalytic properties. J Mol Catal A Chem 279:63–68
Schuchardt U, Vargas RM, Gelbard G (1995) Alkylguanidines as catalysts for the transesterification of rapeseed oil. J Mol Catal A Chem 99:65–70
Furuta S, Matsuhashi H, Arata K (2004) Biodiesel fuel production with solid superacid catalysis in fixed bed reactor under atmospheric pressure. Catal Commun 5:721–723
Guerreiro L, Castanheiro J, Fonseca I, Martin-Aranda R, Ramos A, Vital J (2006) Transesterification of soybean oil over sulfonic acid functionalised polymeric membranes. Catal Today 118:166–171
Aranda DA, Santos RT, Tapanes NC, Ramos ALD, Antunes OAC (2008) Acid-catalyzed homogeneous esterification reaction for biodiesel production from palm fatty acids. Catal Lett 122:20–25
Shu Q, Yang B, Yuan H, Qing S, Zhu G (2007) Synthesis of biodiesel from soybean oil and methanol catalyzed by zeolite beta modified with La3+. Catal Commun 8:2159–2165
Mbaraka IK, Radu DR, Lin VS-Y, Shanks BH (2003) Organosulfonic acid-functionalized mesoporous silicas for the esterification of fatty acid. J Catal 219:329–336
Takagaki A, Toda M, Okamura M, Kondo JN, Hayashi S, Domen K, Hara M (2006) Esterification of higher fatty acids by a novel strong solid acid. Catal Today 116:157–161
Okuhara T, Mizuno N, Misono M (2001) Catalysis by heteropoly compounds—recent developments. Appl Catal A 222:63–77
Kozhevnikov IV (1998) Catalysis by heteropoly acids and multicomponent polyoxometalates in liquid-phase reactions. Chem Rev 98:171–198
Lotero E, Liu Y, Lopez DE, Suwannakarn K, Bruce DA, Goodwin JG (2005) Synthesis of biodiesel via acid catalysis. Ind Eng Chem Res 44:5353–5363
Arzamendi G, Campo I, Arguiñarena E, Sánchez M, Montes M, Gandía LM (2008) Synthesis of biodiesel from sunflower oil with silica-supported NaOH catalysts. J Chem Technol Biotechnol 83:862–870
Narasimharao K, Brown D, Lee AF, Newman A, Siril P, Tavener S, Wilson K (2007) Structure–activity relations in Cs-doped heteropolyacid catalysts for biodiesel production. J Catal 248:226–234
Seddon KR (1997) Ionic liquids for clean technology. J Chem Technol Biotechnol 68:351–356
Welton T (1999) Room-temperature ionic liquids. Solvents for synthesis and catalysis. Chem Rev 99:2071–2084
Wasserscheid P, Keim W (2000) Ionic liquids-new solutions for transition metal catalysis. Angew Chem 39:3772–3789
Wilkes JS (2002) A short history of ionic liquids—from molten salts to neoteric solvents. Green Chem 4:73–80
Dupont J, de Souza RF, Suarez PA (2002) Ionic liquid (molten salt) phase organometallic catalysis. Chem Rev 102:3667–3692
Wu Q, Chen H, Han M, Wang D, Wang J (2007) Transesterification of cottonseed oil catalyzed by Brønsted acidic ionic liquids. Ind Eng Chem Res 46:7955–7960
Kimura M, Nakato T, Okuhara T (1997) Water-tolerant solid acid catalysis of Cs2.5H0.5PW12O40 for hydrolysis of esters in the presence of excess water. Appl Catal A 165:227–240
Sharma Y, Singh B (2008) Development of biodiesel from karanja, a tree found in rural India. Fuel 87:1740–1742
Fang L, Xing R, Wu H, Li X, Liu Y, Wu P (2010) Clean synthesis of biodiesel over solid acid catalysts of sulfonated mesopolymers. Sci China Chem 53:1481–1486
Zhu Z, Yang W (2009) Preparation, characterization and shape-selective catalysis of supported heteropolyacid salts K2. 5H0. 5PW12O40,(NH4) 2.5 H0. 5PW12O40, and Ce0. 83H0. 5PW12O40 on MCM-41 mesoporous silica. J Phys Chem C 113:17025–17031
Jacobson K, Gopinath R, Meher LC, Dalai AK (2008) Solid acid catalyzed biodiesel production from waste cooking oil. Appl Catal B 85:86–91
Guo F, Fang Z, Tian X-F, Long Y-D, Jiang L-Q (2011) One-step production of biodiesel from Jatropha oil with high-acid value in ionic liquids. Bioresour Technol 102:6469–6472
Liang X, Gong G, Wu H, Yang J (2009) Highly efficient procedure for the synthesis of biodiesel from soybean oil using chloroaluminate ionic liquid as catalyst. Fuel 88:613–616
Timofeeva M, Maksimovskaya R, Paukshtis E, Kozhevnikov I (1995) Esterification of 2, 6-pyridinedicarboxylic acid with n-butanol catalyzed by heteropoly acid H3PW12O40 or its Ce(III) salt. J Mol Catal A Chem 102:73–77
Zhang S, Zu Y-G, Fu Y-J, Luo M, Zhang D-Y, Efferth T (2010) Rapid microwave-assisted transesterification of yellow horn oil to biodiesel using a heteropolyacid solid catalyst. Bioresour Technol 101:931–936
Acknowledgments
Research was sponsored by The Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning and the Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution License which permits any use, distribution, and reproduction in any medium, provided the original author(s) and the source are credited.
About this article
Cite this article
Wu, J., Gao, Y., Zhang, W. et al. Esterification of cooking oil for biodiesel production using composites Cs2.5H0.5PW12O40/ionic liquids catalysts. Appl Petrochem Res 4, 305–312 (2014). https://doi.org/10.1007/s13203-014-0066-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13203-014-0066-x