Abstract
The negative effect of high concentration of heavy metals in the environment on living species prompted this research. A study of adsorption of zinc on synthesized magnetite (MG), baobab fruit shell (BB) and magnetite–baobab composite (MB) was carried out. The adsorption of Zn(II) ions was examined using batch equilibrium technique. The effects of initial metal ions concentrations (15–150 mg/L for zinc), adsorbent dose (0.05–0.3 g), contact time (5–150 min), pH (2–8) and temperature (303–343 K) on the sorption capacity of these adsorbents were investigated. The Zn(II) ions at a solution concentration of 150 mg/g gave maximum adsorption capacity of 38.25, 33.95 and 29.20 mg/g for MB, MG and BB, respectively. The adsorption of Zn(II) metal ions was modelled using Langmuir, Freundlich and Temkin isotherms. The highest correlation coefficient (R2) value was obtained from Freundlich model for Zn(II) adsorption on MG and MB as 0.986 and 0.973, respectively, while that of Zn(II) on BB was obtained from Langmuir model as 0.993. The kinetic and thermodynamic studies revealed that the adsorption processes followed pseudo-second-order kinetics and were endothermic in nature. Desorption experiments were conducted on the spent adsorbent using 0.1, 0.2, 0.5, 1.0 and 2.0 M HCl to determine the reusability potentials of the adsorbents. There was an decrease in the amount of Zn(II) ions adsorbed after each stage of desorption process varied between the different acid concentrations. The 0.1 M HCl gave the highest degree of adsorption for Zn(II) on BB, while 0.2 M HCl was the best for MG and MB.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Increase in industrial and mining activities has led to various deteriorations of the ecosystem and therefore poses dangers to human health and environment (Foo and Hammed 2010). Heavy metals are natural components of the earth’s crust. They cannot be degraded or destroyed. To a small extent, they enter our bodies via food, drinking water and air. As trace elements, some heavy metals (e.g. copper, selenium, zinc) are essential to maintain the metabolism of the human body. However, at a high concentration, they can lead to poisoning. Heavy metal poisoning could result, for instance, from drinking water contamination (e.g. lead pipes), high ambient air concentrations near emission sources or intake via the food chain. Heavy metals are dangerous because they tend to bioaccumulate in the body tissues for no known usefulness (Tangjuank et al. 2009). A high concentration of zinc has been observed in wastewaters from pharmaceutical, galvanizing, paint, pigment, insecticide and cosmetic industries. It has also been reported that zinc ions occur in the leachate of landfills at high concentrations. Low concentration of zinc is necessary for the growth of living systems, but it can easily bioaccumulate, which may become harmful to health once beyond the permissible limits.
With the increase in technological development and industrialization in our society, this consequently leads to an increase in the contamination of the environment through various means. Industrial waste, exhausts from factory engines and turbines, products of nuclear weapons among others lead to the release of some toxic heavy metals to our waters and air which also invariably have some complicated effects on the environment and human beings. Heavy metal contamination of water, air and soil regimes continued un-abated despite several decontamination processes that have been developed. This makes research in process development with the synthesis of new adsorbent materials or modification of existing ones a necessity of recent time. Heavy metals are often discharged by a number of industrial processes, and this can lead to the contamination of freshwater and marine environment. Adsorption is one of the most effective and economic techniques for removing heavy metal ions from aqueous solutions. The efficiency of adsorption relies on the capability of the adsorbent to concentrate or adsorb metal ions from dilute solution onto its surfaces and the rate of removing such ions from the solutions. Different adsorbents such as activated carbon, zeolites, resins, biosorbents, hydrogel and magnetic hydrogel have been used for the removal of heavy metal ions by adsorption. Despite the availability of a number of adsorbents for the removal of low concentrations of heavy metal ions from the aqueous solution, there is still a need for the development of new adsorbent with superior adsorption capacity, facile adsorption–desorption kinetics, high stability and easiness of operation. Composite preparation is a growing area, particularly when low-cost materials of comparable adsorption capacities are involved. Magnetite is known for its good adsorption capacity for heavy metals but its synthesis is expensive for wastewater treatment; on the other hand, adsorption capacity of biomass adsorbents is relatively low. Preparation of composite from these two precursors will produce a new structural material with novel adsorption property. This informs the choice of our contribution to this area of adsorption process which focus on the use of magnetite, baobab and magnetite–baobab composite for Zn(II) removal from aqueous solutions.
Materials and methods
Sample collection and preparation
The baobab fruit shells (BFS) were obtained from University of Ilorin, Ilorin, Kwara State, and were rinsed with distilled water to remove dust and impurities deposited on the surface. The BFS were then air-dried and then oven-dried at 80 °C to constant mass. The dried shells were pulverized and sieved to obtain particle sizes ≤ 300 µm. The baobab shell powder was soaked in 0.1 M HNO3 for 24 h. Acid treatment was done to expose more ion binding sites. The mixture was filtered and the powder residue washed with distilled water several times until wash solution is neutral after which the filtered biomass was air-dried at ambient temperature. It was then pulverized and sieved below 90 µm (Chigondo et al., 2013). All reagents that were used in this study were of analytical grade. Working standard solutions were prepared from analytical-grade reagents and by serial dilution method from the stock solutions. All synthetic procedures and characterizations for magnetite and magnetite–baobab composite were discussed in an article under review.
Preparation of magnetite–baobab composite mixture
A 80 g of FeSO4 was dissolved in 560 mL deionized water which has been previously flushed with N2. The 1-L glass reaction vessel (1 L) was closed with an airtight plastic lid having holes for insertion of N2 gas inlets and a thermometer. The reaction vessel was placed in a thermostat water bath at a temperature of 90 °C, a thermometer was inserted for temperature control, and a gas inlet for nitrogen purging. The whole reaction was carried out under nitrogen. Once the reaction temperature was reached, 240 mL of an oxygen-free solution containing 6.46 g KNO3 and 44.9 g KOH was added dropwise within approximately 5 min through a drop funnel. After the addition of this solution, it was heated for another 40 min (Cornell and Schwertmann 1996). Then, 11 g of baobab powder was added to the mixture, stirred and heated for another 10 min to produce magnetite–baobab ratio 2:1 composite mixture.
Batch adsorption experiment
Batch adsorption studies were performed by mixing 0.1 g each of the adsorbents (magnetite, baobab and magnetite–baobab composite) with a 25 mL of varying initial concentrations, 15–150 mg/L Zn(II) ion solutions in a 100-mL conical flask. The conical flasks were tightly covered during the equilibration period and placed on a temperature-controlled motorized orbital mechanical shaker (SHA-B Water Bath Temperature Oscillator) for a period of 5 h at 30 °C. After reaching adsorption equilibrium, the supernatant liquids were filtered and the un-adsorbed Zn ions in the filtrates were analysed by atomic spectrophotometry (AAS) (Salami and Adekola 2002). The quantities of Zn(II) adsorbed were calculated from Eq. (1) (Vibhawari and Pandey 2012; Adekola et al. 2011). The amount of Zn(II) ions adsorbed by magnetite, baobab and magnetite–baobab composite mixture was calculated separately based on the difference between the initial and final concentration of metal ion solution in every flask after specified period of shaking using Eq. 1:
To express the per cent of each metal ion removed from the aqueous solutions by the adsorbents (%Rem), the equation below was used (Abia and Asuquo 2006):
where qe is the quantity of metal adsorbed (mg/g), C0 and Cf are the initial and final concentration of metal ion in solution at any time in (mg/L), V is the total volume of the metal standard solution in the flask (L), and M is the mass of adsorbent used in (g).
Equilibrium adsorption studies: effect of initial metal ion concentration
A 25 mL of 15, 25, 50, 75, 100, 150 mg/L Zn(II) solutions were prepared by serial dilution of the stock solution and were contacted separately with 0.1 g of magnetite, baobab and magnetite–baobab composite mixture at 30 °C for 5 h. At the end of 5 h, the mixtures were filtered. The un-adsorbed Zn(II) ions in the filtrate were analysed by AAS (Jimoh et al. 2012). The quantity adsorbed, qe, was calculated from Eq. 1.
Effect of contact time
A 0.1 g of magnetite, baobab and magnetite–baobab composite mixture was weighed separately in 100-mL conical flasks. A 25 mL of the optimum concentration (150 mg/L zinc) solution was added separately to each of the magnetite, baobab and magnetite–baobab mixture in the beaker. Each solution was agitated for different time interval of 5, 10, 15, 30, 45, 60, 90, 120 and 150 min to investigate the effect of contact time. After the completion of the reaction, the mixtures were filtered and followed by the determination of the residual metal ion concentrations using AAS. The quantity adsorbed was calculated using Eq. (1) (Abdus-Salam and Itiola 2012).
Effect of adsorbent dose
The Zn(II) concentration that gave optimal adsorption per 0.1 g magnetite, baobab, magnetite–baobab composite mixture was used. A 25 mL of the Zn(II) solution was contacted with varying amounts of magnetite for 5 min, baobab for 120 min and magnetite–baobab composite for 60 min (0.1, 0.5, 1.0, 1.5, and 2.0 g) at laboratory temperature, 30 °C, and at the optimal concentration [150 mg/L Zn (II)]. The mixtures were agitated with an orbital mechanical shaker model SHA-B Water Bath Constant Temperature Oscillator. At the completion of the contact, the solutions were filtered and the filtrate was analysed for Zn(II) using AAS (Abdus-Salam and Itiola 2012). The quantity adsorbed, qe, was calculated from Eq. 1.
Effect of temperature
The temperature of the working solution was varied between 30 and 70 °C (30, 40, 50, 60 and 70 °C). A 25 mL of the optimum concentration, 150 mg/L Zn(II), was contacted with 0.05 g of magnetite for 5 min, 0.1 g of baobab for 120 min and 0.05 g of magnetite–baobab composite mixture for 90 min in 100-mL conical flasks. The mixtures were equilibrated at contact time at aforementioned temperatures. The mixtures were filtered, and the filtrates were analysed for Zn(II) using AAS spectrophotometer, and the quantities adsorbed were calculated by using Eq. (1) (Abdus-Salam and Itiola 2012).
Effect of pH
The effect of pH on Zn(II) adsorption was carried out over a pH range of 2–8. A 25 mL of the optimum concentration 150 mg/L Zn(II) was contacted with 0.05 g each of magnetite for 5 min and magnetite–baobab composite mixture for 90 min and 0.1 g of baobab for 120 min in 100-mL conical flasks. The mixtures were equilibrated at contact time at 70 °C. The mixtures were filtered, and the filtrates were analysed for Zn(II) using AAS. The quantity adsorbed was calculated from equation (Abdus-Salam and Itiola 2012).
Results and discussion
Equilibrium studies: effect of initial metal ion concentration
It was observed from Fig. 1 that the total amount of Zn(II) ions adsorbed per gram of the adsorbents (magnetite, baobab and magnetite–baobab composite) increased with increasing concentration while the percentage removal of the adsorbates reduced. Magnetite–baobab composite exhibited a higher adsorption capacity (mg/g) for Zn(II) compared to magnetite and baobab. Also, magnetite showed a higher adsorption capacity for both Zn(II) than baobab. At low concentration, the available driving force for transfer of metal ions onto the adsorbent particles is low, while at high concentration, there is a corresponding increase in the driving force, thereby enhancing the interaction between the metal ions in the aqueous phase and the active sites of the adsorbents. As a result of this, there was an increase in the uptake of Zn(II) ions. Similar results were obtained on the monosorption of Cu, Pb, Fe, Cr and Cd ions from aqueous solutions using coconut husk (Agbozu and Emoruwa 2014). A high metal concentration saturates the adsorbent sites more quickly, thereby decreasing the overall percentage metal removal (Yeddou and Bensmaili 2007). Therefore, there was an increase in the quantity of metal ions adsorbed (qe) with an increase in the initial concentration, while the % removal was decreased which is the trend in a similar research (Andal and Sakthi 2010). Hence, the increasing value qe is not directly proportional to the increasing initial concentration.
From Fig. 1, magnetite–baobab composite showed a higher adsorption capacity for Zn(II) with 31.97 mg/g in comparison with magnetite (24.97 mg/g) and baobab (22.16 mg/g). Therefore, it can be deduced from these plots that the adsorption capacity for the three adsorbents is in the order of magnetite–baobab (MB) > magnetite (MG) > baobab (BB) for both Pb(II) and Zn(II).
The influence of using varying amounts of adsorbents (0.05–0.30 g) while adsorbate initial concentration was fixed (Fig. 2) showed that as the adsorbent dosage was increased, the amount adsorbed also increased but the amount adsorbed per unit mass of the adsorbent decreased considerably for magnetite (MG), baobab (BB) and magnetite–baobab composite (MB). When the agitation speed and reactor size are kept constant after optimization of these parameters, increasing the adsorbent dose will reduce accessibility of adsorbate to the active sites on the adsorbent. The decrease in adsorption per unit mass with increasing dose of adsorbent is attributed to possible overlapping of adsorption sites as adsorbent dose increases or clogging of adsorbent which will equally reduce the effective adsorption sites. Concentration factor involving low metal-to-adsorbent ratio at low metal concentrations can be considered in explaining the dependence of adsorption on adsorbent dose. The percentage of metal ion adsorbed is dependent upon the initial concentration, and at higher concentrations, the available sites of adsorption become fewer (Sekar et al. 2004: Gueu et al. 2006).
From Fig. 2, it was observed that as the adsorbents dose increased from 0.05 to 0.3 g, the quantity adsorbed (mg/g) decreased from 26.35 to 9.59 mg/g for Zn(II) on MG, 22.17–10.02 mg/g for Zn(II) on BB and 26.54–10.80 mg/g for Zn(II) on MB composite. This showed the high adsorption capacity of the magnetite and magnetite–baobab composite particles at low dosage. The biosorption of Pb(II) and Zn(II) from aqueous solution using Nordmann fir cones as the adsorbents (Yusuf et al. 2009) followed similar trend. Also, the influence of adsorbent concentration on adsorption of Pb and Zn on natural goethite (Abdus-Salam and Adekola 2005) followed this trend.
It is evident from Fig. 3 that MG showed rapid metal adsorption within 5 min of contact time due to the easy accessibility of the adsorption sites on the adsorbent and was followed by decrease/desorption of metals at longer contact times. The rate of adsorption indicated that the removal of 66.75% for Zn(II) was observed in the first 5 min of contact time. Some earlier reports had it that equilibrium time can be attained in a very short period for the removal of heavy metals on iron oxides reported (Jiang et al. 2013: Liliana and Juan 2013; Khodabakhshi et al. 2011). Furthermore, the rapid adsorption of Zn(II) by magnetite can be attributed to the external surface adsorption which is different from the microporous adsorption process which makes it easier for Zn(II) to access the active sites of magnetite readily resulting in rapid approach of equilibrium (Saidur 2013).
The effect of contact time on the biosorption of Zn(II) on BB showed that the amount of the adsorbed metal ions increases with increasing time till 120 min for Zn(II) with adsorption capacity of 22.48 mg/g. Also, the equilibrium time for adsorption of Zn(II) on MB was 60 min with 26.86 mg/g adsorbed. A constant adsorption is indicative of equilibration due to saturation of adsorption sites. Rapid adsorption of metal ions during the initial stage was due to the large initial concentration gradient between the adsorbate in solution and the number of available vacant sites on the adsorbent surface (Chigondo et al. 2013).
Effect of temperature
It is observed from Fig. 4 that as the experimental temperature increases from 30 to 70 °C, the Zn(II) adsorption also increased. For magnetite (MG), it increased from 28.60% at 30 °C to 50.27% at 70 °C for Zn(II). There were three stages of adsorption process as depicted by the curves: an initial slow (30–50 °C), a fast (50–60 °C) and a slow (60–70 °C) increase in the adsorption given rise to an S-like curve. Also, for baobab (BB), there was a slight increase in adsorption uptake from 60.03% (30 °C) to 69.75% (70 °C) for Zn(II). For Zn(II) adsorption on magnetite–baobab (MB) composite, the quantity adsorbed and the experimental temperature were directly proportional. The adsorption increased from 33.23% (30 °C) to 51.65% (70 °C) for Zn(II) with the S-like adsorption curve pattern similar to that of magnetite.
Generally, the increase suggests that the adsorption process is endothermic in nature. It also suggests that there were chemical interactions between the adsorbents and the metal ions in solutions. For ions to be adsorbed on the adsorbents, hydrated ions have to lose their hydrated shell, and this dehydration process needs energy which is compensated for by increase in temperature (Alvarez-Ayuso et al. 2003; Omar and Al-Itaw 2007; Babarinde and Babalola 2010; Castaldi et al. 2008). The removal of water molecules from hydrated ions is essentially an endothermic process. This increase is probably due to increase in the energy of the solution with increasing temperature which stimulated the diffusion of Zn(II) ions unto the adsorbent particles surface.
Effect of pH
From Fig. 5, it was observed that the percentage removal of Zn(II) ions in the aqueous solution was low at lower pH values and increased with increasing initial pH of the solution for MG, BB and MB adsorbents. The removal of Zn(II) by MG was about 90.98% at pH 8.0 and 63.53% at a pH 2.0. Adsorption of Zn(II) onto MB followed a similar trend of which quantity adsorbed increased with an increase in the pH of the solution as observed from Fig. 5. At pH of 8.0, 38.25 mg/g of Zn(II) was adsorbed as compared to 14.07 mg/g adsorbed at 2.0. It was observed that the maximum adsorption of Zn(II) on MG, BB and MB adsorbents occurred within the pH range 6–8. Increase in adsorption with pH increase may be due to the variation of surface charge of adsorbents as a function of pH of the solution. The dependence of metal sorption on pH is related to both the surface functional groups of the adsorbent and the metal ion chemistry in solution (Wang and Xing 2002) which gave rise to a S-like curves. The uptake and equilibrium adsorption capacity of metal removal from aqueous solution are strongly affected by the pH (Zvinowanda et al. 2009). The maximum adsorption of Zn(II) ions was achieved at pH 6. At pH higher than 6, both metal ions were precipitated. Therefore, the removal of metal ions at higher pH values greater than 6 was due to the formation of precipitates rather than adsorption (Bayat 2002). The adsorption capacity increased with an increase in pH up to pH 6 for Zn(II). The increase in metal adsorption with an increase in pH is due to a decrease in competition between hydrogen ions and metal ions for the surface sites and also due to a decrease in positive surface charge. As the pH increases, more negatively charged surface becomes available and thus facilitates greater metal adsorption. At low pH, the higher concentration and mobility of H+ ions favour its adsorption compared to metal ions. Metal ions are more soluble at lower pH values, and this reduces their adsorption (Onundi et al. 2010). Furthermore, at lower pH, the surface of the adsorbent is surrounded by hydrogen ions (H+) thereby blocking metal ions from binding sites on baobab. A similar trend was observed in the studies of sorption of Pb(II) and Cu(II) onto magnetite eggshells–Fe3O4 powder (Ren et al. 2012) and removal of Pt2+ and Au3+ ions from aqueous solutions by magnetite nanoparticles (Liliana and Juan 2013).
Adsorption isotherm of Zn(II) ions on MG, BB and MB
The adsorption isotherm describes graphically how adsorbates interact with adsorbents, and this is important in the optimization of the use of adsorbents (Bulut and Aydin 2005). The equilibrium data were analysed using the Langmuir, Freundlich and Temkin isotherm models. High correlation value, R2 (close or equal to 1), indicates the conformity among experimental data with model isotherm.
Langmuir adsorption isotherm
Figure 6 shows a plot of Ce/qe versus Ce from Eq. 3. Figure 9 represents the Langmuir isotherm behaviour for the adsorption of Zn(II) ion on magnetite, baobab and magnetite–baobab composite sample.
where Ce is the equilibrium concentration of the adsorbate (mg/L), qe is the amount of adsorbate adsorbed per unit mass of adsorbate (mg/g), KL is the Langmuir constant related to the energy of adsorption, and qmax is the maximum adsorption capacity (mg/g).
It can be deduced from the graphs using the correlation coefficient (R2) values that the experimental data for the BB fitted most into the model with 0.9932 followed by that of MG with 0.9506 and MB with 0.9145 for Zn(II) ion. The applicability of the Langmuir isotherm indicates good monolayer coverage of Pb(II) and Zn(II) ions on the surface of MG, BB and MB which suggest the formation of a monolayer on the adsorbent surface in the given concentrations range (Alli and Muhammad 2008). The fact that the Langmuir isotherm fits the experimental data very well may be due to the homogenous distribution of active sites on the adsorbent since the Langmuir equation assumes that the surface is homogenous. The separation factor RL for the isotherm can be used to predict the shape and the favourability condition of the adsorption process
where RL is the separation factor, C0 is the initial concentration of Zn(II) ions (mg/L), and KL is the Langmuir adsorption constant (L/mg). The result of the separation factor (RL) presented in Table 1 from this research work showed that the values are within the range (0 < RL < 1) which indicates that the adsorption of Zn(II) onto the three adsorbents is favourable.
Freundlich adsorption isotherm
The equilibrium concentrations of Zn(II) earlier obtained were subjected to Freundlich equation as shown in Eq. 5
where qe is the amount of metal up take at equilibrium in (mg/g), Ce is the equilibrium adsorbate concentration in the bulk solution (mg/L), kf and n are Freundlich constants, Kf value is a measure of overall adsorption capacity of the adsorbent (mg/g), and n is a measure of adsorption intensity. The plot of log qe versus log Ce is shown in Fig. 7.
Comparing the correlation coefficient values for the adsorption of Zn(II) on the adsorbents (Fig. 7), the best fittings of data are in the descending order: MG > BB = MB with R2 of magnetite being 0.986, while both baobab and magnetite–baobab composites have the same R2 value of 0.973. The isotherm yielded a good linear plots having Freundlich adsorption intensity, n, constant for Zn(II) on MG, BB and MB adsorbents as 1.253, 2.320 and 2.170, respectively. The n values predict whether the adsorption of a given ion is favourable or not. Since n > 1 for adsorption of Pb(II) and Zn(II), the adsorption intensity is favourable at higher concentration (Adekola et al. 2011)].
Temkin adsorption isotherm
Figure 8 represents the Temkin isotherm behaviour for the adsorption of Zn(II) on magnetite, baobab and magnetite–baobab composite. The quantity adsorbed was calculated from Eq. 6. The plot of qe versus In Ce gave the values of constants A and B as the intercept and slope of the curve, respectively.
where A = Temkin isotherm equilibrium binding constant (L/g), b0 = Temkin isotherm constant related to heat of adsorption (J/mol), Ce is the equilibrium solute concentration in the bulk solution (mg/L), R = universal gas constant (8.314 J/molK) and T = temperature, and B is a constant defined as \(\frac{RT}{{b_{0} }} = B\).
The adsorption data obtained for Zn(II) on BB fitted best with correlation coefficient (R2) value of 0.967, followed by 0.955 for MG and 0.862 for MB. The Temkin adsorption equilibrium binding energy constant, A, for MG, BB and MB composite is 0.3397 L/mg, 2.380 L/mg and 4.047 L/mg for Zn(II) ions adsorption. This indicates that MB composite has higher adsorbent metal ion potential for Zn(II) followed by that of BB while MG has the least potential. The low values of BB suggest that there is an indirect interaction among the particles of adsorbents and adsorbates which corresponds to the linear decrease in the heat of adsorption of all the molecules in the layer. Table 1 shows the isotherm model parameters for Zn(II) on the three adsorbents.
Adsorption kinetics
The kinetics of Zn(II) sorption onto MG, BB, and MB were investigated using pseudo-first-order and pseudo-second-order kinetic models. The rate of Zn(II) adsorption on these adsorbents was described by these adsorption kinetics as a function of time. It helps to determine equilibrium time which gives useful information relating to the design of adsorption process and pollution flux (Abdus-Salam and Itiola 2012). The closeness of the experimental data and the model-predicted values were expressed by the correlation coefficient. A relatively high R2 value implies that the model successfully illustrates the kinetics of Zn(II) adsorption.
Pseudo-first-order kinetic model (Abdus-Salam and Itiola 2012)
The rate constant values and amount of metal ions adsorbed are evaluated from the slope and intercept of Fig. 9 as described by linearized pseudo-first-order kinetic equation:
where qe and qt are the quantity of Zn(II) ions adsorbed (mg/g) at equilibrium and at any time t, respectively, and k1 (min−1) is the rate constant of the pseudo-first-order adsorption operation. Negative slopes were obtained in respect of plots of Zn(II) adsorption data for BB and MB, while the R2 value for MG was low for practical application of the model. The qe and k1 obtained are summarized in Table 2.
Pseudo-second-order kinetic model
Figure 10 shows the linear plot of pseudo-second-order model which describes the relative fitness of the model to experimental data for the adsorption of Zn(II) on the three adsorbents as described by simplified form of the pseudo-second-order equation (Abdus-Salam and Itiola 2012).
where qe and qt are the quantity of metal ions adsorbed (mg/g) at equilibrium and any time t, respectively, k2 (g/mg/min) is the rate constant of the pseudo-second-order adsorption operation. The plot of \(\frac{t}{{q_{t} }}\) versus t gives linear curve with \(\frac{1}{{q_{\text{e}} }}\) and \(\frac{1}{{k_{2} q_{\text{e}}^{2} }}\) as slope and intercept, respectively. This plot yielded good results with high correlation coefficient R2 for Zn(II) (0.998) on MG, (0.994) on BB and (0.999) on MB indicating the best fittings of experimental data to pseudo-second-order model and described the adsorption process the best. The qe and k2 obtained are reported in Table 2.
The pseudo-second-order adsorption kinetics equation is a better kinetics model than the pseudo-first-order kinetics equation, since it gave a better fit of experimental data with higher correlation coefficients compared to pseudo-first order. Similar behaviour was also reported on the synthetic magnetite nanoparticles applied to the removal of Pt2+ and Au2+ ions from aqueous solution (Liliana and Juan 2013) and removal of Zinc from aqueous solutions by magnetite silica core–shell nanoparticles (Emadi et al. 2013). Hence, on the basis of the excellent fitting of experimental data in the pseudo-second-order kinetic model and the correlation coefficient value (R2 close to 1), the main adsorption mechanism is probably a chemisorption reaction which may be the rate-limiting step. In chemisorptions, the heavy metals stick to the adsorbent surface forming a chemical (usually covalent) bond and tend to find sites that maximize their coordination with the surface (Atkins 1995).
Adsorption thermodynamics
Thermodynamic analysis was applied to the data obtained on the effect of temperature on adsorption. The thermodynamic parameters such as changes in Gibbs free energy (ΔG), enthalpy (ΔH) and entropy (ΔS) were determined from Eqs. (9, 10 and 11).
where Kc is the equilibrium constant, Ce is the equilibrium concentration of adsorbate in solution (mg/L), and CAe is the solid-phase concentration at equilibrium (mg/L). \(\Delta G^\circ\), \(\Delta H^\circ\) and \(\Delta S^\circ\) are changes in Gibbs free energy (KJ/mol), enthalpy (KJ/mol) and entropy (J/mol/K), respectively; R is the gas constant (8.314 J/mol/K); and T is the temperature (K). The values of ΔH and ΔS were, respectively, evaluated from the slope and intercept of the van’t Hoff plot of InKc versus 1/T (Eq. 11) as presented in Fig. 11. The thermodynamic parameters are summarized in Table 3.
From Table 3, the positive values of ΔH that range from 9.26 to 21.17 kJ/mol for Zn(II) onto the three adsorbents indicate that the reactions were physisorptions and endothermic in nature which implies an increase in adsorption capacity with temperature increase. Adsorption is generally regarded to be physiosorption when the ΔH value ranges between 2.1 and 20.9 kJ/mol but chemisorption when ΔH value ranges between 80 and 200 kJ/mol (Liu and Liu 2008; Abdus-Salam and Buhari 2016). The positive values of ΔS which range from 33.73 to 61.33 J/K/mol for Zn(II) on the adsorbents suggest an increased randomness at the adsorbent–adsorbate interface during the fixation of the adsorbate ions on the active site of the adsorbent (Jain and Sharma 2002). The negative values of ΔG for the adsorption of Zn(II) on Mg, BB and MB imply that the adsorption processes were feasible and spontaneous. Furthermore, the decrease in ΔG value with increasing adsorption temperature reveals that adsorption of Zn(II) onto the three adsorbents becomes better at higher temperatures.
Desorption
The data obtained from desorption experiment are plotted in Fig. 12a–c) to determine suitable leachant for regeneration and the reusability potential of the adsorbents (Abdus-Salam and Itiola 2012).
The initial conditions of the adsorbents (quantities of adsorbent and adsorbate to be desorbed) were the same before they were subjected to desorption experiment. It is observed from Fig. 12a–c that the quantities adsorbed after each step of desorption decreased with more steps of adsorption–desorption process. This might be due to the incomplete desorption of adsorbates which makes some adsorption sites not available during the subsequent adsorption. However, the results showed that the adsorbent has high potential of reusability. The 01 M HCl leachant provided the best regeneration conditions for adsorption–desorption process for adsorption of Zn(II) on MB and BB. The stepwise adsorption of Zn(II) on MB is 87.86, 71.87 and 67.05%, while on BB is 93.19, 79.34 and 70.86%. The percentage Zn(II) adsorbed onto MG in the respective three steps of adsorption–desorption processes was the highest for 0.2 M HCl stripping agent with 81.85, 63.65 and 59.60%.
Conclusion
This study has demonstrated that the synthesized magnetite particles (MG), baobab fruit shells (BB) and magnetite–baobab composite (MB) have favourable properties for the adsorption of zinc(II) ions from aqueous solutions. The adsorbents were investigated on the effect of initial metal ion concentration, adsorbent dose, contact time, temperature and pH which are highly dependent on the efficiency of adsorption. The Langmuir, Freundlich and Temkin isotherm models were employed to describe the Pb(II) and Zn(II) adsorption onto the adsorbents of which Freundlich isotherm fitted the experimental data best with. The pseudo-second-order kinetic model best-described the adsorption of Zn(II) on the adsorbents with R2 value close to unity suggesting covalently bonded chemical process. Thermodynamic studies showed that the adsorption processes were endothermic and mostly spontaneous for Zn(II) on MG, BB and MB. The three adsorbents have also been found to have high efficiency for reuse at low concentrations of HCl leachant which suggests a good regenerative potential for the adsorbents usage.
References
Abdus-Salam N, Adekola FA (2005) The influence of pH and adsorbent concentration on adsorption of lead and zinc on a natural goethite. Afr J Sci Technol 6(2):55–66
Abdus-Salam N, Buhari M (2016) Adsorption of alizarin and fluorescein dyes onto palm seeds activated carbon: kinetic and thermodynamic studies. J Chem Soc Pak 38(4):604–614
Abdus-Salam N, Itiola AD (2012) Potential application of termite mound for adsorption and removal of Pb(II) from aqueous solutions. J Chem Soc Niger 9:373–382
Abia AA, Asuquo ED (2006) Lead (II) and Nickel (I) adsorption kinetics from aqueous metal solutions using chemically modified and unmodified agricultural adsorbents. Afr J Biotechnol 5(16):1475–1482
Adekola FA, Abdus-Salam N, Abdul-Rauf LB (2011) Removal of arsenic from aqueous solution by synthetic hematite. J Chem Soc Niger 36(2):52–58
Agbozu IE, Emoruwa FO (2014) Batch adsorption of heavy metals (Cu, Pb, Fe, Cr and Cd) from aqueous solutions using coconut husk. J Environ Sci 8(4):239–246
Alli H, Muhammad SK (2008) Biosorption of crystal violet from water on leaf biomass of Calotropis procera. J Environ Sci Technol 1(3):143–150
Alvarez-Ayuso E, Garcia-Sanchez A, Querol X (2003) Purification of metal electroplating waste waters using zeolites. Water Res 37(20):4855–4862
Andal NM, Sakthi V (2010) A comparative study on the sorption characteristics of Pb(II) and Hg(II) onto activated carbon. J Chem 7(3):967–974
Atkins PW (1995) Physical chemistry, 5th edn. Oxford University Press, New York, pp 122–124
Babarinde NA, Babalola JO (2010) The biosorption of Pb(II) from solution by elephant grass: kinetic equilibrium and thermodynamic studies. Pac J Sci Technol 11(1):622–630
Bayat B (2002) Comparative study of adsorption properties of Turkish fly ashes 1. The case of nickel(II), copper(II) and zinc(II). J Hazard Mater 144:251–273
Bulut Y, Aydin H (2005) A kinetic and thermodynamic study of methylene blue adsorption on wheat shells. Desalination 194:259–267
Castaldi P, Santona L, Enzo S, Melis P (2008) Sorption process and XRD analysis of a zeolite. J Hazard Mater 156:428–434
Chigondo F, Nyamunda BC, Sithole SC, Gwatidzo L (2013) Removal of lead (II) and copper (II) ions from aqueous solution by baobab (Adononsia digitata) fruit shells biomass. IOSR J Appl Chem: IOSR-JAC 5(1):43–50
Cornell RM, Schwertmann U (1996) The iron oxides: structure, properties, reaction, occurrences and uses, 2nd edn. Wiley, New York, p 665
Emadi M, Shams E, Amini MK (2013) Removal of zinc from aqueous solutions by magnetite silica core-shell nanoparticles. J Environ Chem 5:1–10
Foo KY, Hammed BH (2010) Review: insight into the modelling of adsorption isotherm systems. Chem Eng J 156:2–10
Gueu S, Yao B, Adouby K, Ado G (2006) Heavy metals removal in aqueous solution by activated carbons prepared from coconut shell and seed shell of the palm tree. J Appl Sci 6(13):2789–2793
Jain CK, Sharma MK (2002) Adsorption of cadmium on bed sediments in river hindon: adsorption models and kinetics. Water Air Soil Pollut 137(1–4):1–19
Jiang W, Miguel P, Dionysios D, Mohammad HE, Dimitra T, Kevin O (2013) Chromium (VI) removal by maghemite nanoparticles. Chem Eng J 222:527–533
Jimoh TO, Buoro AT, Muriana M (2012) Utilization of Blighiasapida (Akee apple) pods in the removal of lead, cadmium and cobalt ions from aqueous solution. J Environ Chem Ecotoxicol 4(10):178–187
Khodabakhshi A, Amin MM, Mozaffari M (2011) Synthesis of magnetite nanoparticles and evaluation of its efficiency for arsenic removal from simulated industrial wastewater. Iran J Environ Health Sci Eng 8(3):189–200
Liliana G, Juan CM (2013) Synthesis of Magnetite nanoparticles and exploring their application in their application in the removal of Pt2+ and Au3+ ions from aqueous solutions. Eur Chem Bull 2(7):445–452
Liu Y, Liu YJ (2008) Biosorption isotherms, kinetics and thermodynamics. Sep Purif Technol 61:229
Omar W, Al-Itaw H (2007) Removal of Pb2+ ions from aqueous solution by adsorption on kaolinite clay. Am J Appl Sci 4(7):502–507
Onundi YB, Mamun AA, Al Khatib MF, Ahmed YM (2010) Adsorption of copper, nickel and lead ions from synthetic semiconductor industrial wastewater by palm shell activated carbon. Int J Environ Sci Technol 7(4):751–758
Ren J, Bopape MF, Setshedi K, Kitinya JO, Onyango MS (2012) Sorption of Pb(II) and Cu(II) by low-cost magnetic eggshell-Fe3O4 powder. Chem Ind Chem Eng Q 18(2):221–231
Saidur C (2013) Application of mixed iron oxides in subsurface remediation technologies. A thesis submitted in partial fulfilment of the requirements for the degree of Doctor of philosophy, Department of Civil and Environmental Engineering, Western University London, Ontario, Canada, pp 78–309
Salami N, Adekola FA (2002) A study of Sorption of cadmium by geothite in aqueous solution. Bull Chem Soc Ethopia 16(1):1–7
Sekar M, Sakthi V, Rengaraj S (2004) Kinetics and equilibrium adsorption study of Lead(II) onto activated carbon prepared from coconut shell. J Colloid Interface Sci 279(2):307–313
Tangjuank S, Insuk N, Tontrakoon J, Udeye V (2009) Adsorption of lead(II) and cadmium(II) ions from aqueous solutions by adsorption on activated carbon prepared from cashew nut shells. World Acad Sci Eng Technol 6(2):298–306
Vibhawari, Pandey ND (2012) Single and competitive sorption of heavy metal ions of (Cd2+ & Cu2+) on a clayey soil. E-J Chem 7(SI):S27–S34. https://doi.org/10.1155/2010/710546
Wang K, Xing B (2002) Adsorption and desorption of cadmium by goethite pretreated with phosphate. Chemosphere 48(7):665–670
Yeddou N, Bensmaili A (2007) Equilibrium and kinetic modelling of iron adsorption in eggshells in a batch system: effect of temperature. Desalination 206(1–3):127–134
Yusuf K, Ozkan A, Handan U (2009) Biosorption of Lead(II) and Zn(II) from aqueous solution by Nordmann fir Abies nordmanniana (Spach. Subsp. Nordmanniana) cones. Acta Chim Slov 56:451–456
Zvinowanda CM, Okonkwo OJ, Sekhula MM, Agyei NM, Sadiku R (2009) Application of maize tassel for the removal of Pb, Se, sr, U and V from borehole water contaminated with mine wastewater in the presence of alkaline metals. J Hazard Mater 164:884–891
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations’.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Abdus-Salam, N., Adekola, S.K. Adsorption studies of zinc(II) on magnetite, baobab (Adansonia digitata) and magnetite–baobab composite. Appl Water Sci 8, 222 (2018). https://doi.org/10.1007/s13201-018-0867-7