Abstract
Conventional colored latex particles have poor solvent resistance due to the absence of chemical bonds between the dye and polymer component, resulting in staining and greatly restricting its application. In this research, the disperse dye was chemically bonded to the polymer to prepare covalent and solvent-resistance colored latex particles. Firstly, C.I. Disperse Red 60, as a common disperse dye in industry, was modified by acryloyl chloride (amidation reaction) for the purpose of introducing the C=C bonds. The structure of modified C.I. Disperse Red 60 was confirmed by 1HNMR, FTIR and elemental analysis and its spectral property was also evaluated. Then the covalent colored latex particles were synthesized via miniemulsion copolymerization of styrene (St) and ethyl acrylate (EA) in presence of modified C.I. Disperse Red 60 monomer. Results of FTIR, TG, DSC and TEM indicated that the covalent colored latex particles were successfully prepared. By using UV-spectroscopy, the solvent resistance of the colored latex membranes in petroleum ether, hexane, cyclohexane, and ethanol was monitored, respectively. Slight change of the absorption was detected for 10 days, which verified the excellent solvent resistance of covalent colored latex membranes. Finally, the prepared colored latex particles were applied on cotton printing in the absence of binder. The results showed that the colored latex particles printed fabric had superior rubbing fastness and soft hand feel.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
J. Zhang, X. Li, X. Shi, H. Mei, X. Zhou, and X. Wang, Prog. Nat. Sci.: Mater. Int., 22, 71 (2012).
B. Li, S. Jie, Y. Jiang, J. Wang, and C. Kan, J. Appl. Polym. Sci., 129, 1484 (2013).
D. Gao, C. Rui, B. Lyu, J. Ma, and X. Duan, Appl. Surface Sci., 435, 195 (2018).
S. Xin, P. G. Jessop, and M. F. Cunningham, Green Chemistry, 19, 1889 (2017).
S. Fu, J. Lu, X. Luo, and F. Bai, Colloid Surf. A-Physicochem. Eng. Asp., 423, 131 (2013).
K. Fang, H. Gao, F. Sun, W. Chen, R. Xie, and Y. Cai, Fiber. Polym., 18, 2255 (2017).
X. Fei, L. Cao, and Y. Liu, Dyes Pigment., 125, 192 (2016).
K. Fang and B. Ren, Dyes Pigment., 100, 50 (2014).
K. Fang, Z. Li, Y. Cai, L. Hao, and X. Liu, Dyes Pigment., 136, 191 (2017).
A. Amin, M. Ali Reza, and S. M. Hamid, Langmuir the Acs J. Surfaces Colloids, 31, 10672 (2015).
M. Li, C. Zhang, L. Fang, L. Shi, Z. Tang, H. Y. Lu, and C. F. Chen, Acs Appl. Mater. Interfaces, 10, 8225 (2018).
S. Y. Lee, J. Choi, J. R. Jeong, J. H. Shin, and S. H. Kim, Adv. Mater., 29, 1605450 (2017).
F. H. Mostegel, M. Roth, M. Gassner, A. Oesterreicher, R. Piock, M. Edler, and T. Griesser, Prog. Org. Coat., 94, 116 (2016).
M. M. Irani, F. Nourmohammadian, S. Bastani, F. Najafi, and N. M. Mahmoodi, J. Luminescence, 199, 499 (2018).
O. A. Hakeim, A. A. Arafa, M. K. Zahran, and L. A. W. Abdou, Colloid Surf. A-Physicochem. Eng. Asp., 447, 172 (2014).
W. Y. Ji, F. Cardinaux, C. Lapointe, Z. Chi, T. G. Mason, K. H. Ahn, and F. Scheffold, Colloid Surf. A-Physicochem. Eng. Asp., 546, 360 (2018).
K. Fang, T. Song, K. Zhang, W. Chen, Y. Cai, and L. Hao, J. Appl. Polym. Sci., 134, 44987 (2017).
B. Li, J. Shen, R. Liang, W. Ji, and C. Kan, Colloid Polym. Sci., 290, 1893 (2012).
J. Wang, B. Li, Q. Jin, X. Huang, S. Jie, and C. Kan, Des. Monomers Polym., 18, 611 (2015).
L. Min, L. Zhang, H. Peng, S. Fu, L. Min, L. Zhang, H. Peng, S. Fu, L. Min, and L. Zhang, J. Appl. Polym. Sci., 135, 45826 (2018).
L. Wang, L. Zhang, Z. Yi, L. Min, and S. Fu, Colloid Surf. A-Physicochem. Eng. Asp., 533, 33 (2017).
S. Chisca, P. Duong, A.-H. Emwas, R. Sougrat, and S. P. Nunes, Polym. Chem., 6, 543 (2015).
L. Min, W. Ma, L. Zhang, C. Agbo, and S. Fu, Acs Sustain. Chem. Eng., 5, 758 (2016).
M. Li, K. Zhang, and K. Xie, Carbohydr. Polym., 113, 77 (2014).
S. Fu, M. Zhang, and C. Xu, J. Imaging Sci. Technol., 54, 10505 (2010).
Acknowledgements
This research was supported by and the Natural Science Foundation of Jiangsu Province [Grant numbers BK20191334], the Postgraduate Research & Practice Innovation Program of Jiangsu Province [Grant numbers KYCX18_1830], the Fundamental Research Funds for the Central Universities [Grant numbers JUSRP51514], the China Postdoctoral Science Foundation Funded Project [Grant numbers 2018M630520].
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Yang, Y., Li, M., Tang, A. et al. Preparation of Covalent and Solvent-resistance Colored Latex Particles and Its Application on Cotton Fabric. Fibers Polym 21, 1685–1693 (2020). https://doi.org/10.1007/s12221-020-9990-9
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-020-9990-9