Abstract
The reliability of Pb-free solder joints is controlled by their microstructural constituents. Therefore, knowledge of the solder microconstituents’ mechanical properties as a function of temperature is required. Sn-Ag-Cu lead-free solder alloy contains three phases: a Sn-rich phase, and the intermetallic compounds (IMCs) Cu6Sn5 and Ag3Sn. Typically, the Sn-rich phase is surrounded by a eutectic mixture of β-Sn, Cu6Sn5, and Ag3Sn. In this paper, we report on the Young’s modulus and hardness of the Cu6Sn5 and Cu3Sn IMCs, the β-Sn phase, and the eutectic compound, as measured by nanoindentation at elevated temperatures. For both the β-Sn phase and the eutectic compound, the hardness and Young’s modulus exhibited strong temperature dependence. In the case of the intermetallics, this temperature dependence is observed for Cu6Sn5, but the mechanical properties of Cu3Sn are more stable up to 200°C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
X. Deng, N. Chawla, K.K. Chawla, and M. Koopman, Acta Mater. 52, 4291 (2004).
X. Deng, M. Koopman, N. Chawla, and K.K. Chawla, Mater. Sci. Eng. A 364, 240 (2004).
F. Gao and T. Takemoto, Mater. Lett. 60, 2315 (2006).
J. Glazer, Int. Mater. Rev. 40, 65 (1995).
J. Glazer, J. Electron. Mater. 23, 693 (1994).
M. McCormack and S. Jin, JOM 45(7), 36 (1993).
W.J. Plumbridge, J. Mater. Sci. 31, 2501 (1996).
P. Vianco and D. Frear, JOM 45(7), 14 (1993).
N. Chawla, Int. Mater. Rev. 54, 368 (2009).
H. Zhiheng, L. Changqing, P. Conway, and R. Thomson, HDP ’04. Proceeding of the Sixth IEEE CPMT Conference, vol. 52 (2004).
F. Gao, H. Nishikawa, T. Takemoto, and J. Qu, Microelectron. Reliab. 49, 296 (2009).
R.R. Chromik, R.P. Vinci, S.L. Allen, and M.R. Notis, J. Mater. Res. 18, 2251 (2003).
Y. Sun, J. Liang, Z.-H. Xu, G. Wang, and X. Li, J. Mater. Sci. Mater. Electron. 19, 514 (2007).
P.-F. Yang, Y.-S. Lai, S.-R. Jian, J. Chen, and R.-S. Chen, Mater. Sci. Eng. A 485, 305 (2008).
X. Deng, G. Piotrowski, J.J. Williams, and N. Chawla, J. Electron. Mater. 32, 1403 (2003).
W.C. Oliver and G.M. Pharr, J. Mater. Res. 7, 1564 (1992).
J.C. Trenkle, C.E. Packard, and C.A. Schuh, Rev. Sci. Instrum. 81, 073901 (2010).
F. Guo, S. Choi, J.P. Lucas, and K.N. Subramanian, J. Electron. Mater. 29, 1241 (2000).
G. Zeng, S. Xue, L. Zhang, L. Gao, W. Dai, and J. Luo, J. Mater. Sci. Mater. Electron. 21, 421 (2010).
L. Jiang and N. Chawla, Scripta Mater. 63, 480 (2010).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lotfian, S., Molina-Aldareguia, J., Yazzie, K. et al. Mechanical Characterization of Lead-Free Sn-Ag-Cu Solder Joints by High-Temperature Nanoindentation. J. Electron. Mater. 42, 1085–1091 (2013). https://doi.org/10.1007/s11664-013-2517-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-013-2517-z