Abstract
In order to examine the effect of extrusion ratio on the microstructure and mechanical behavior in Al-Cu-Mg-Ag alloy, the Al-6.3Cu-0.48Mg-0.4Ag alloy was subjected to extruding with different extrusion ratios of 17, 30 and 67. The results indicate that the grains are refined and the strength is improved effectively with increasing extrusion ratio. However, further investigation shows that the extrusion ratio of 30 is more effective than the lower extrusion ratio (17) and the higher extrusion ratio (67) to refine the grains in the T6-temper alloy. Moreover, the sample with an extrusion ratio of 30 obtains more precipitates and superior mechanical properties after T6 treatment. This study supports the idea that there exists a critical extrusion ratio for grain refinement and improvement of mechanical properties for the T6-temper alloy. Recrystallization and precipitation during T6 treatment were introduced to explain the effects of extrusion ratio on the microstructure and mechanical properties of the Al-Cu-Mg-Ag alloys.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Hou Y H, Gu YX, Liu Z Y, et al. Modeling of Whole Process of Ageing Precipitation and Strengthening in Al-Cu-Mg-Ag Alloys with High Cu-to-Mg Mass Ratio[J]. Trans. Nonferrous Met. Soc. China, 2010, 20 (5): 863–869
Lumley R N, Morton A J, Polmear I J. Enhanced Creep Performance in An Al-Cu-Mg-Ag Alloy through Underageing[J]. Acta Mater., 2002, 50 (14): 3597–3608
Hutchinson C R, Fan X, Pennycook S J, et al. On the Origin of the High Coarsening Resistance of Omega Plates in Al-Cu-Mg-Ag Alloys[J]. Acta Mater., 2001, 49 (14): 2827–2841
Skrotzki B, Shiflet G, Starke E. On The Effect of Stress on Nucleation and Growth of Precipitates in an Al-Cu-Mg-Ag Alloy[J]. Metall. Mater. Trans. A, 1996, 27 (11): 3431–3444
Polmear I J, Pons G, Barbaux Y, et al. After Concorde: Evaluation of Creep Resistant Al-Cu-Mg-Ag Alloys[J]. Mater. Sci. Technol., 1999, 15 (8): 861–868
Estrin Y, Vinogradov A. Extreme Grain Refinement by Severe Plastic Deformation: A Wealth of Challenging Science[J]. Acta Mater., 2013, 61 (3): 782–817
Orlov D, Raab G, Lamark T T, et al. Improvement of Mechanical Properties of Magnesium Alloy ZK60 by Integrated Extrusion and Equal Channel Angular Pressing[J]. Acta Mater., 2011, 59 (1): 375–385
Cheng S, Zhao Y H, Zhu Y T, et al. Optimizing the Strength and Ductility of Fine Structured 2024 Al Alloy by Nano-precipitation[J]. Acta Mater., 2007, 55 (17): 5822–5832
Zhao Y L, Yang Z Q, Zhang Z, et al. Double-peak Age Strengthening of Cold-worked 2024 Aluminum Alloy[J]. Acta Mater., 2013, 61 (5): 1624–1638
Kim J K, Jeong H G, Hong S I, et al. Effect of Aging Treatment on Heavily Deformed Microstructure of A 6061 Aluminum Alloy after Equal Channel Angular Pressing[J]. Scripta Mater., 2001, 45 (8): 901–907
Wang Z C, Prangnell P B. Microstructure Refinement and Mechanical Properties of Severely Deformed Al-Mg-Li Alloys[J]. Mater. Sci. Eng. A, 2002, 328 (1): 87–97
Shaeri M H, Salehi M T, Seyyedein S H, et al. Microstructure and Mechanical Properties of Al-7075 Alloy Processed by Equal Channel Angular Pressing Combined with Aging Treatment[J]. Mater. Des., 2014, 57: 250–257
Liu X Y, Pan Q L, Zhang X L, et al. Effects of Stress-aging on The Microstructure and Properties of An Aging Forming Al-Cu-Mg-Ag Alloy[J]. Mater. Des., 2014, 58: 247–251
Sha G, Wang Y B, Liao X Z, et al. Influence of Equal-channel Angular Pressing on Precipitation in an Al-Zn-Mg-Cu Alloy[J]. Acta Mater., 2009, 57 (10): 3123–3132
Barnett M R. A Rationale for the Strong Dependence of Mechanical Twinning on Grain Size[J]. Scripta Mater., 2008, 59 (7): 696–698
Rofman O V, Bate P S. Dynamic Grain Growth and Particle Coarsening in Al-3.5Cu[J]. Acta Mater., 2010, 58 (7): 2527–2534
Zhang G J, Liu G, Ding X D, et al. Experiment and Modeling Study of Aged Aluminium Alloys Strengthening Response[J]. Acta Metall. Sinica, 2003, 39 (8): 803–808
Liddicoat P V, Liao X Z, Zhao Y, et al. Nanostructural Hierarchy Increases the Strength of Aluminium Alloys[J]. Nat. Commun., 2010, 63 (1): 1–6
Hu T, Ma K, Topping T D, et al. Precipitation Phenomena in An Ultrafine-grained Al Alloy[J]. Acta Mater., 2013, 61: 2163–2178
Ma K, Wen H, Hu T, et al. Mechanical Behavior and Strengthening Mechanisms in Ultrafine Grain Precipitation-strengthened Aluminum Alloy[J]. Acta Mater., 2014, 62: 141–155
Author information
Authors and Affiliations
Corresponding author
Additional information
Funded by the National Natural Science Foundation of China (No.51071075) and the Deep Continental Scientific Drilling Equipment Development (SinoProbe-09-05), as well as by the 985 Project-Automotive Engineering of Jilin University
Rights and permissions
About this article
Cite this article
Xu, X., Zhao, Y., Zhang, M. et al. Effect of Extrusion Ratio on the Microstructure and Mechanical Properties in an Al-Cu-Mg-Ag Alloy. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 33, 710–714 (2018). https://doi.org/10.1007/s11595-018-1882-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-018-1882-0