Abstract
MgCo2O4 nanowires are synthesized for the first time through two-step synthesis method, followed by annealing of the MgCo2O4 precursors. The microstructure and morphology of MgCo2O4 nanowires are examined by powder X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, and X-ray photoelectron spectroscopy. MgCo2O4 nanowires give rise to a BET surface area of 45.1 m2 g−1 and the adsorption average pore size of 11.5 nm. When tested as an anode for lithium-ion batteries, the MgCo2O4 nanowires electrode exhibit exceptional properties in terms of specific capacity, cycling performance, and rate capacity compared with previously reported Co-based binary metal oxides. For instance, when the current densities increase from 5, 10, 15, and 20 A g−1, the discharge capacities of the MgCo2O4 nanowires electrode are about 649, 348, 188, and 121 mAh g−1, respectively. The enhanced electrochemical performance of the MgCo2O4 nanowires can be mainly attributed to the nanostructures which lead to decreased lithium-ion diffusion distances and increased active sites for Li insertion/extraction reactions.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
The depletable traditional energy resources and the increasing urgent attentions to environmental pollution are main driving forces for the development of renewable and clean energy sources (Mondal et al. 2014; Tian et al. 2007). As one of the most promising type of energy storage device, lithium-ion batteries (LIBs) have attracted more and more attention in recent years due to its high-power capability, long cycle lifetime, and fast charge and discharge rates, such as mobile communication devices, portable electronics stationary, and energy storage. (Lou et al. 2014; Zhao et al. 2012; Cherian et al. 2013). It is well known that the capacity of anode material for lithium storage relates to their morphology and microstructure. The precise design of materials with controlled nanosized shapes provides one of the most effective ways of developing high-performance energy devices, because the high surface area of nanostructures leads to decreased lithium-ion diffusion distances and increased active sites for Li insertion/extraction reactions (Bai et al. 2014; Wang et al. 2011; Fu et al. 2013).
Recently, various nanostructured transition-metal oxides (TMO) have been exploited as one of the most promising candidates for potential application in energy-related devices, owing to their higher theoretical reversible capacities. (e.g., 782 mAh g−1 of SnO2 (Li et al. 2010); 717 mAh g−1 of NiO (Aravindan et al. 2013); and 890 mAh g−1 of Co3O4 (Xiao et al. 2013). Among the TMO, cobalt-based nanomaterials have shown the highest capacity and the best electrochemical performances, compared to nickel oxide and iron oxides. (Du et al. 2011). However, cobalt is toxic and expensive, numerous efforts are made toward replacing Co3O4 partially with other inexpensive and environmentally friendly metal oxides to lower the toxicity and reduce the cost (Sharma et al. 2007a; Mondal et al. 2014). To date, many binary metal oxides, such as CuCo2O4 (Sharma et al. 2007b), ZnCo2O4 (Luo et al. 2012), FeCo2O4, MgCo2O4 (Sharma et al. 2008), MnCo2O4 (Li et al. 2014a), and NiCo2O4 (Shen et al. 2014), have also been reported as preliminary anode materials for LIBs. Among them, although NiCo2O4 and FeCo2O4 exhibit higher theoretical reversible capacities (890 and 900 mAh g−1, respectively), the simple structures, poor electric conductivity, and severe volume variations during the electrochemical reaction led to structural instabilities and fast capacity decrease, especially. They show poor rate capability which is the most important for practical applications of LIBs. Mohamed et al. reported FeCo2O4 nanoflakes, the reversible capacity is ~1570 mAh g−1 at a current density of 0.2 A g−1, then ~1433 mAh g−1 at 0.4 A g−1, and ~1222 mAh g−1 at 0.8 A g−1 (Mohamed et al. 2014). Li et al. synthesized NiCo2O4 microspheres, the discharge capacities of which are 753, 556, and 393 mA h g−1, as the current density increased stepwise to 0.4, 0.8, and 1.6 A g−1, respectively (Li et al. 2013). One strategy can be proposed to buffer the volume variations and improve the rate capability. It could use Co-based binary metal oxides like ACo2O4 during the first discharge, cobalt metal atoms are extruded from the pristine material, and a metal atoms form inactive metal oxides particles, which can inhibit the volume change (Chamas et al. 2013; Liu et al. 2014). Although MgCo2O4 shows the lower theoretical capacity (~780 mAh g−1) compared with FeCo2O4 and NiCo2O4, during the first discharge, Mg atoms form inactive MgO. The inactive MgO can remit volume variations effectively during the electrochemical reaction. There are only a few reports on the application of MgCo2O4 as an anode material. Chowdari et al. first reported the preparation of needle-shape MgCo2O4 as an anode material for LIBs, the obtained MgCo2O4 showed electrochemical performances with an initial reversible capacity of 900 mAh g−1 and 17 % of the capacity (160 mAh g−1) was retained over 50 cycles at a current of 60 mA g−1(Sharma et al. 2008). However, the needle-shape MgCo2O4 showed low reversible capacity and poor cycling performance in practical application. Therefore, it is necessary to further improve the capacity, cyclic stability, and rate performance of MgCo2O4.
In this study, we report a simple and mild route at relatively low temperature (100 °C) to fabricate MgCo2O4 nanowires by two-step synthesis method. What’s more, there is still no report in the literature to fabricate MgCo2O4 nanowires on Ni foam as binder-free electrodes. MgCo2O4 nanowires connected directly with Ni foam can provide numerous efficient transport pathways for ions and electrons and avoid the use of polymer binders and conducting additives. When applied as anode materials for LIBs, the MgCo2O4 nanowires exhibit remarkable rate performance and excellent cycling stability even at a high charge/discharge current density.
Experimental
Synthesis of MgCo2O4 nanowires on Ni foam
In a typical synthesis, 1 mmol Mg(NO3)2·6H2O, 2 mmol Co(NO3)2·6H2O, 12 mmol CO(NH2)2, and 6 mmol of hexamethylene-tetramine were dissolved in 30 ml distilled water and stirred for several minutes. After putting a Ni foam wafer (16 mm in diameter and 1 mm in thickness) treated with 3 M HCl solution for 30 min, the solution was then transferred into a 50 ml Teflon-lined stainless autoclave and maintained at 100 °C for 8 h. During the hydrothermal process, hydrolysis–precipitation took place, which produced the precipitated precursor of Mg, Co-hydroxide-carbonate on the Ni foam wafer (Kang et al. 2013). After hydrothermal growth, the resulting Mg, Co-hydroxide-carbonate was taken out and washed with distilled water and absolute ethanol for 10 times, and then dried at 60 °C for 12 h. Finally, the precursor was annealed at a low temperature of 350 °C for 3 h to obtain MgCo2O4 nanowires. The representative synthetic process of the sample is illustrated in Fig. 1. For comparison, the powder product of MgCo2O4 was also produced by following the same procedure except that no Ni foam wafer was introduced.
Material characterization
Powder X-ray diffraction (XRD) patterns of samples were recorded by a Bruker D8 ADVANCE X-ray powder diffractometer using Cu Kα radiation (λ = 0.15418 nm) at a scanning rate of 0.02° s−1 in the 2θ range from 30 to 70°. Scanning electron microscopy (SEM) images of samples were carried out by a FEI Quanta 400 ESEM-FEG (environmental scanning electron microscope-field emission gun) equipped with an X-ray energy dispersive spectrometer (EDS). The microstructures of these nanowires were observed by transmission electron microscopy (TEM, FEI, Tecnai-20) and high-resolution transmission electron microscopy (HRTEM, J JEOL JEM-3010). The specific surface area and pore size distribution of the samples were recorded using nitrogen adsorption via Brunauer–Emmett–Teller (BET, TriStar 3020 analyzer) and Barrett–Joyner–Halenda (BJH) method at 77 K.
Electrochemical measurements
Electrochemical measurements were performed at 25 °C using coin cells (CR2025) with pure lithium foil as the counter and reference electrode. The MgCo2O4 microspheres electrode consisted of 80 % active material, 10 % of acetylene black, and 10 % of PVDF using N-methyl pyrrolidone (NMP) as solvent, and then the mixed suspension was pasted on Ni foam wafer (16 mm in diameter and 1 mm in thickness). After drying in a vacuum oven for 12 h at 80 °C, the nickel foam was pressed at 20 MPa so as to obtain good contact between nickel foam and the active material, the MgCo2O4 microsphere electrode was thus obtained. The MgCo2O4 nanowires grown on Ni foam wafer (MgCo2O4 loading: ~2 mg cm−2) sample were directly used as working electrode without any binders or conductive additives. Cells were constructed in a glove box in argon atmosphere under a dew point below −65°. The electrolyte was 1 M LiPF6 dissolved in a mixture of dimethyl carbonate, diethyl carbonate, and ethylene carbonate (1:1:1 by volume), and the separator was microporous polypropylene film. The electrochemical experiments were carried out on a LAND battery program-control test system in cut-off voltages of 0.005 and 3.0 V. Cyclic voltammetry (CV) was carried out on a CHI 660D electrochemical workstation at a scan rate of 0.1 mV s−1 in the potential range of 0–3.0 V vs. Li/Li+. Electrochemical impedance spectroscopy (EIS) was performed by using the same electrochemical workstation with the frequency range from 0.01 to 100 kHz.
Results and discussion
In order to study the crystal structure and phase purity of the obtained products, MgCo2O4 nanowires grown on Ni foam were sonicated for 1 h to peel the nanowires off from the substrate. As shown in Fig. 2, seven distinct diffraction peaks are observed at 2θ values of 31.03, 36.81, 38.27, 44.60, 55.19, 58.89, and 64.98°, respectively. All of these diffraction peaks can be indexed to (220), (311), (222), (400), (422), (511), and (440) crystal planes and assigned to MgCo2O4 with a spinel crystalline structure (JCPDS No. 02-1073). No additional diffraction peaks from other than MgCo2O4 are detectable, indicating the high purity of the synthesized product.
The typical survey XPS spectrum of the product is depicted by using a Gaussian fitting method, the Co 2p emission spectrum (Fig. 3a) is best fitted with two spin-orbit doublets, characteristic of Co2+ and Co3+ (Xie et al. 2013). The peaks located at 51 eV in Fig. 3b reveal the high-resolution Mg 2p spectrum, and the results are in good agreement with the literature (Casey et al. 2008; Corneille et al. 1994). Figure 3c reveals the high-resolution O1 s spectrum; it comprises two oxygen contributions, the component O1 at 529.6 eV is typical of metal–oxygen bonds, another peak at 532.5 eV corresponds to a higher number of defect sites with low oxygen coordination usually observed in materials with small particles(Yuan et al. 2012).
The morphology of the as-synthesized MgCo2O4 nanowires is characterized by SEM, as shown in Fig. 4a–f. It can be clearly observed from Fig. 4a that the Ni foam is constructed by plenty of Ni belts with smooth surface. Figure 4b–d shows the gradually high-magnification SEM images of MgCo2O4 nanowires. It is observed that these MgCo2O4 nanowires are directly grown from and closely contacted with the Ni substrate. These nanowires have an edge length of 1–3 μm and a uniform thickness of ~60 nm. In comparison, without the Ni foam as the substrate, the formed MgCo2O4 nanowires are assembled in spherical shapes without uniform direction (Fig. 4e, f); this is because the nanowires unites often possess high surface free energy, and they tend to stack together and form sphere structure to minimize the total energy of the system when no template is used to confine their growth direction (Wang et al. 2013; Cao et al. 2009).
The SEM micrograph, EDS microanalysis, and the corresponding mapping images of the cross-section of MgCo2O4 nanowires are shown in Fig. 5a–f. The EDS microanalysis of Fig. 5b clearly indicates that the MgCo2O4 nanowires constitute only Mg, Co, and O elements with atomic ratio of almost of 1:2:4, demonstrating the formation of pure MgCo2O4 nanowires. The elemental maps shown in Fig. 5c–f provide clearer information about the element spatial distribution within the cross-section of MgCo2O4 nanowires, which further confirm the formation of pure MgCo2O4 nanowires products.
To further investigate the detailed morphology and structure of MgCo2O4 nanowires, TEM, HRTEM, and SAED analysis are employed (Fig. 6a–e). TEM image in Fig. 6a clearly shows that the sample has an edge length of 1–3 μm and a uniform thickness of ~60 nm, which is in good agreement with the SEM observation. HRTEM image in Fig. 6b observation reveals that the porous nanowire consists of quasi-continuous nanoparticles of 10–20 nm in diameter. To analyze the crystal accurately, a HRTEM image is derived from the red rectangle in (Fig. 6c–d). The lattice spacing is measured to be 0.288 nm, in a good agreement with the theoretical interplane spacing of MgCo2O4 (220) planes. SAED pattern in Fig. 6e implies that these particles are single crystalline in nature. Figure 6f shows a typical TEM image of the MgCo2O4 microspheres, and it can be clearly seen that each microsphere is composed of many aggregated nanowires. Such a phenomenon is consistent with the SEM image (Fig. 4f).
Figure 7 shows the N2 adsorption–desorption isotherms and the corresponding BJH pore size distribution plot of MgCo2O4 nanowires and microspheres. All of the isotherms in Fig. 7a, b can be classified as type IV isotherm with a type-H4 hysteresis loop, implying the existence of mesoporous structure in the material (Vinu et al. 2005). According to the investigative results, the BET surface areas of MgCo2O4 nanowires and microspheres are 45.1 and 30.6 m2 g−1, respectively. According to the corresponding BJH pore size distribution (the inset of Fig. 7) recorded from nitrogen isotherms, the adsorption average pore size is 11.5 nm for MgCo2O4 nanowires and 9.2 nm for MgCo2O4 microspheres, which further confirmed the mesoporous feature of these materials. The relatively large specific surface area and identified porosity are beneficial for the Li+ diffusion and electrode–electrolyte contacts during the electrochemical process.
The electrochemical properties of MgCo2O4 nanowires as a conductivity-agent-free and binder-free anode for LIBs are examined by CV and discharging and charging test. The initial three CV curves of the electrode between 0 and 3 V (vs. Li/Li+) at a scan rate of 0.1 mV s−1 are shown in Fig. 8a. It can be seen from the CV results in Fig. 8a that there is a substantial difference between the first and subsequent cycles. The peak at 0.33 V observed in the first discharge CVs is ascribed to the formation of the SEI layer (Eq. (1)) and the reduction of Co3+ to metallic Co, Mg2+ is not reduced to Mg0 due to the high bond energy of MgO (Eq. (2)) (Connor and Irvine 2001). At the second scan, the reduction peak shifts to about 0.8 V and becomes broader compared to the first cycle, while the anodic scans almost without changes. Two oxidation peaks are found at 1.6 and 2.3 V. The weak peak at 1.6 V should correspond to the dissolution of the SEI layer, and the strong peak at 2.3 V can be assigned to the reaction (Eqs. (3), (4)). Moreover, it is obvious that the peak intensity drops significantly in the second cycle, indicating the occurrence of some irreversible reactions associated with the SEI formation.
Figure 8b shows the discharge and charge curves of MgCo2O4 nanowires electrode for the 1st and 2nd at a current density of 2.5 A g−1. The first discharge and charge capacity are 1357 and 1029 mAh g−1, respectively. Accordingly, the coulombic efficiency of MgCo2O4 in the first cycle can be calculated to be 76 %. These values are higher than the theoretical capacity of MgCo2O4. The extra capacity can be ascribed to solid-electrolyte interphase (SEI) formation and the decomposition of electrolytes. Upon the second discharge–charge process, the discharge and charge capacities are 998 and 949 mAh g−1, respectively; and the coulombic efficiency increases significantly up to about 95 %. Figure 8c gives a comparison of reversible capacity versus cycle number for MgCo2O4 nanowires and microspheres electrode. As can be seen in Fig. 8c, from the second cycle onwards, the MgCo2O4 nanowires electrode exhibits slightly capacity decay and around 53 % of the initial reversible capacity can be retained over 60 cycles at a current density of 2.5 A g−1. For MgCo2O4 microspheres electrode, after 60 cycles, the reversible capacity is only 83 mAh g−1, and the initial reversible capacity is only 22 %. MgCo2O4 nanowires electrode also shows remarkable rate performance compared to the MgCo2O4 microspheres electrode. As shown in Fig. 8d, at the current densities increase from 5, 10, 15, and 20 A g−1, and the discharge capacities of the MgCo2O4 nanowires electrode are about 649, 348, 188, and 121 mAh g−1, respectively. More importantly, when the rate is switched abruptly from 20 to 2.5 A g−1, the specific capacity is exceptionally high at 690 mAh g−1. These results indicate that the MgCo2O4 nanowires structure has very significant potential for high-rate anode materials in LIBs. While the capacities of MgCo2O4 microspheres electrode are 155, 88, 75, and 31 mAh g−1 at the current densities increase from 5, 10, 15, and 20 A g−1. Apparently, the above results that the improvement in lithium storage properties should attribute to the nanostructured morphology, providing a high-specific surface area to add the contact area between active electrode materials and electrolyte. The high contact area can also provide more active sites for lithium-ion insertion/extraction. In addition, during the first discharge, Mg metal atoms form inactive MgO, which can inhibit volume variations effectively during the electrochemical reaction. Based on the above discussed electrochemical performance of MgCo2O4 nanowires electrode, it is found that our produced MgCo2O4 nanowires exhibited higher rate capability than those of previously reported Co-based binary metal oxides (Table 1).
To explore the cause for the large capacity degradation, EIS of the MgCo2O4 microsphere and MgCo2O4 nanowires material after the first cycle and the 60th cycle are shown in Fig. 9. The semicircle stands for the charge-transfer impedance on electrode/electrolyte interface (Cao et al. 2013). It can be seen clearly that the diameter of the semicircle of the MgCo2O4 nanowire electrode after the first cycle is much smaller than that of the MgCo2O4 microsphere electrode, demonstrating that the Ni substrate existed in the system increased the charge-transfer process compared to pure powder materials. The results indicate that Ni substrate enhances the conductivity of pure binary metal oxide materials. After the 60th cycles, it is worth noting that the charge-transfer resistance is enlarged for two samples. The increase in charge-transfer resistance can give rise to capacity decay during the cycling process.
Conclusion
In summary, we demonstrated a simple hydrothermal reaction for the synthesis of MgCo2O4 nanowires at a low temperature as 100 °C. MgCo2O4 nanowires, assembled by plenty of quasi-continuous nanoparticles, give rise to a BET surface area of 45.1 m2 g−1 and the adsorption average pore size of 11.5 nm. When tested as an anode for LIBs, the MgCo2O4 nanowires electrodes exhibit exceptional properties in terms of specific capacity, cycling performance, and rate capacity compared with previously reported Co-based binary metal oxides. The discharge capacities of the MgCo2O4 nanowires electrode are about 649, 348, 188, and 121 mAh g−1, when the current densities increase from 5, 10, 15, and 20 A g−1, respectively. EIS measurements have confirmed that Ni substrate enhances the conductivity of pure binary metal oxide materials. In addition, MgCo2O4 nanowires with nanostructure can provide numerous efficient transport pathways for ions and electrons and relieve the pulverization of active anode material during charging/discharging processes.
References
Aravindan V, Kumar PS, Sundaramurthy J, Ling WC, Ramakrishna S, Madhavi S (2013) Electrospun NiO nanofibers as high performance anode material for Li-ion batteries. J Power Sources 227:284–290
Bai J, Li XG, Liu GZ, Qian YT, Xiong SL (2014) Unusual formation of ZnCo2O4 3D hierarchical twin microspheres as a high-rate and ultralong-life lithium-ion battery anode material. Adv Funct Mater 24:3012–3020
Cao F, Hu W, Zhou L, Shi W, Song S, Lei Y, Wang S, Zhang H (2009) 3D Fe3S4 flower-like microspheres: high-yield synthesis via a biomolecule-assisted solution approach, their electrical, magnetic and electrochemical hydrogen storage properties. Dalton Trans 42:9246–9252
Cao F, Pan GX, Tang PS, Chen HF (2013) NiO nanowall array prepared by a hydrothermal synthesis method and its enhanced electrochemical performance for lithium ion batteries. Mater Res Bull 48:1178–1183
Casey P, Hughes G, O’Connor E, Long RD, Hurley PK (2008) Growth and characterisation of thin MgO layers on Si(100) surfaces. J Phys: Conf Ser 100:42–46
Chamas M, Sougrati MT, Reibel C, Lippens PE (2013) Quantitative analysis of the initial restructuring step of nanostructured FeSn2-based anodes for Li-ion batteries. Chem Mater 25:2410–2420
Chen HW, Liu AF, Zhang XL, Mu JB, Bai YM, Hou JX (2015) Three-dimensional hierarchical ZnCo2O4 flower-like microspheres assembled from porous nanosheets: hydrothermal synthesis and electrochemical properties. Ceram Int 41:7556–7564
Cherian CT, Sundaramurthy J, Reddy MV, Kumar PS, Mani K, Pliszka D, Sow CH, Ramakrishna S, Chowdari BVR (2013) Morphologically robust NiFe2O4 nanofibers as high capacity Li-ion battery anode material. ACS Appl Mater Interfaces 5:9957–9963
Connor PA, Irvine JTS (2001) Novel tin oxide spinel-based anodes for Li-ion batteries. J Power Sources 223:97–98
Corneille JS, He JW, Goodman DW (1994) XPS characterization of ultra-thin MgO films on a Mo (100) surface. Surf Sci 306:269–278
Du N, Xu YF, Zhang H, Yu JX, Zhai CX, Yang D (2011) Porous ZnCo2O4 nanowires synthesis via sacrificial templates: high-performance anode materials of Li-ion batteries. Inorg Chem 50:3320–3324
Fu YJ, Yang ZB, Li XW, Wang XH, Liu DQ, Hu DK, Qiao L, He DY (2013) Template-free synthesized Ni nanofoams as nanostructured current collectors for high-performance electrodes in lithium ion batteries. J Mater Chem A 1:10002–10007
Fu CC, Li GS, Luo D, Huang XS, Zheng J, Li LP (2014) One-step calcination-free synthesis of multicomponent spinel assembled microspheres for high-performance anodes of Li-ion batteries: a case study of MnCo2O4. ACS Appl Mater Interfaces 6:2439–2449
Hao SJ, Zhang B, Ball S, Copley M, Xu ZC, Srinivasan M, Zhou K, Mhaisalkar S, Huang YZ (2015) Synthesis of multimodal porous ZnCo2O4 and its electrochemical properties as an anode material for lithium ion batteries. J Power Sources 294:112–119
Hu LL, Qu BH, Li CC, Chen YJ, Mei L, Lei DN, Chen LB, Li QH, Wang TH (2013) Facile synthesis of uniform mesoporous ZnCo2O4 microspheres as a high-performance anode material for Li-ion batteries. J Mater Chem A 1:5596–5602
Huang GY, Xu SM, Xu ZH, Sun HY, Li LY (2014) Core-shell ellipsoidal MnCo2O4 anode with micro-/nano-structure and concentration gradient for lithium-ion batteries. ACS Appl Mater Interfaces 6:21325–21334
Kang WP, Feng F, Zhang MM, Liu SJ, Shen Q (2013) Structural features and electrochemical properties of nanostructured ZnCo2O4 synthesized by an oxalate precursor method. J Nanopart Res 15:1891–1897
Li LM, Yin XM, Liu S, Wang YG, Chen LB, Wang TH (2010) Electrospun porous SnO2 nanotubes as high capacity anode materials for lithium ion batteries. Electrochem Commun 12:1383–1386
Li JF, Xiong SL, Liu YR, Ju ZC, Qian YT (2013) High electrochemical performance of monodisperse NiCo2O4 mesoporous microspheres as an anode material for Li-ion batteries. ACS Appl Mater Interfaces 5:981–988
Li JF, Wang JZ, Liang X, Zhang ZJ, Liu HK, Qian YT, Xiong SL (2014a) Hollow MnCo2O4 submicrospheres with multilevel interiors: from mesoporous spheres to yolk-in-double-shell structures. ACS Appl Mater Interfaces 6:24–30
Li L, Zhang YQ, Liu XY, Shi SJ, Zhao XY, Zhang H, Ge X, Cai GF, Gu CD, Wang XL, Tu JP (2014b) One-dimension MnCo2O4 nanowire arrays for electrochemical energy storage. Electrochim Acta 116:467–474
Liu CJ, Xue FH, Huang H, Yu XH, Xie CJ, Shi MS, Cao GZ, Jung YG, Dong XL (2014) Preparation and electrochemical properties of Fe–Sn (C) nanocomposites as anode for lithium-ion batteries. Electrochim Acta 129:93–99
Lou FL, Zhou HT, Tran Buan MEM, Bruer FV, Rønning M, Walmsley JC, Chen D (2014) Coaxial carbon/metal oxide/aligned carbon nanotube arrays as high-performance anodes for lithium ion batteries. ChemSusChem 7:1335–1346
Luo W, Hu XL, Sun YM, Huang YH (2012) Electrospun porous ZnCo2O4 nanotubes as a high-performance anode material for lithium-ion batteries. J Mater Chem 22:8916–8921
Mohamed SG, Hung TF, Chen CJ, Chen CK, Hu SF, Liu RS, Wang KC, Xing XK, Liu HM, Liu AS, Hsieh MH, Lee BJ (2013) Flower-like ZnCo2O4 nanowires: toward a high performance anode material for Li-ion batteries. RSC Adv 3:20143–20149
Mohamed SG, Chen CJ, Chen CK, Hu SF, Liu RS (2014) High-performance lithium-ion battery and symmetric supercapacitors based on FeCo2O4 nanoflakes electrodes. ACS Appl Mater Interfaces 6:22701–22708
Mondal AK, Su D, Chen SQ, Xie XQ, Wang GX (2014) Highly porous NiCo2O4 nanoflakes and nanobelts as anode materials for lithium-ion batteries with excellent rate capability. ACS Appl Mater Interfaces 6:14827–14835
Sharma BY, Sharma N, Rao GVS, Chowdari BVR (2007a) Nanophase ZnCo2O4 as a high performance anode material for Li-ion batteries. Adv Funct Mater 17:2855–2861
Sharma Y, Sharma N, Rao GVS, Chowdari BVR (2007b) Lithium recycling behaviour of nano-phase-CuCo2O4 as anode for lithium-ion batteries. J Power Sources 173:495–501
Sharma Y, Sharma N, Rao GVS, Chowdari BVR (2008) Studies on spinel cobaltites, FeCo2O4 and MgCo2O4 as anodes for Li-ion batteries. Solid State Ionics 179:587–597
Shen LF, Che Q, Li HS, Zhang XG (2014) Mesoporous NiCo2O4 nanowire arrays grown on carbon textiles as binder-free flexible electrodes for energy storage. Adv Funct Mater 24:2630–2637
Song X, Ru Q, Mo YD, Hu SJ, An B (2014) A novel fiber bundle structure ZnCo2O4 as a high capacity anode material for lithium-ion battery. J Alloy Compd 60:6219–6225
Tian B, Zheng XT, Kempa J, Fang Y, Yu N, Yu G, Huang J, Lieber CM (2007) Coaxial silicon nanowires as solar cells and nanoelectronic power sources. Nature 449:885–889
Vinu A, Sawant DP, Ariga K, Hartmann M, Halligudi SB (2005) Benzylation of benzene and other aromatics by benzyl chloride over mesoporous AlSBA-15 catalysts. Microporous Mesoporous Mater 80:195–203
Wang XH, Li XW, Sun XL, Li F, Liu QM, Wang Q, He DY (2011) Nanostructured NiO electrode for high rate Li-ion batteries. J Mater Chem 21:3571–3573
Wang G, Wang H, Bai J, Ren Z (2013) PVP-assisted assembly of lanthanum carbonate hydroxide with hierarchical architectures and their luminescence properties. Chem Eng J 214:386–393
Wu XH, Wu WW, Wang KT, Chen W, He D (2015) Synthesis and electrochemical performance of Wu-like MnCo2O4 as an anode material for sodium ion batteries. Mater Lett 147:85–87
Xiao YL, Zai JT, Tao LQ, Li B, Han QY, Yu C, Qian XF (2013) MnFe2O4–graphene nanocomposites with enhanced performances as anode materials for Li-ion batteries. Phys Chem Chem Phys 15:3939–3945
Xie QS, Li F, Guo HZ, Wang LS, Chen YZ, Yue GH, Peng DL (2013) Template-free synthesis of amorphous double-shelled zinc-cobalt citrate hollow microspheres and their transformation to crystalline ZnCo2O4 microspheres. ACS Appl Mater Interfaces 5:5508–5517
Yuan CZ, Li JY, Hou LR, Zhang XG, Shen LF, Lou XW (2012) Ultrathin mesoporous NiCo2O4 nanosheets supported on Ni foam as advanced electrodes for supercapacitors. Adv Funct Mater 22:4592–4597
Zhao XY, Cao MH, Hu CW (2012) Binder strategy towards improving the rate performance of nanosheet assembled SnO2 hollow microspheres. RSC Adv 2:11737–11742
Zheng QY, Zhang XY, Shen YM (2015) Fabrication of free-standing NiCo2O4 nanoarrays via a facile modified hydrothermal synthesis method and their applications for lithium ion batteries and high-rate alkaline batteries. Mater Res Bull 63:211–215
Acknowledgments
This work was supported by the financial supports of the National Natural Science Foundation of China (Nos. 21301140 and 21061130551), and the Natural Science Foundation of Shaanxi Province (No. 2013JQ2004).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Wang, X., Zhai, G. & Wang, H. Facile synthesis of MgCo2O4 nanowires as binder-free flexible anode materials for high-performance Li-ion batteries. J Nanopart Res 17, 339 (2015). https://doi.org/10.1007/s11051-015-3131-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11051-015-3131-1