Abstract
Nanostructured manganese oxide (Mn2O3) thin films were synthesized by spin coating method. The effect of preparation conditions, such as calcination temperature, rotation speed, as well as solution aging time on structural, morphological, and optical properties of the samples were investigated. The phase of the grown films changed from amorphous to orthorhombic by applying the calcination temperature beyond 400 °C. At low calcination temperature, agglomerations of the particles happened and no uniform structure formed. Furthermore, the results indicated that employing higher rotation speeds led to decrement of the samples crystallinity. Aging the solution did not change the absorption edge of the samples. However, the optical transmittance of the samples decreased by about 10 percent.
Highlights
-
Mn2O3 thin films have been prepared by sol-gel spin coating technique.
-
Structural, morphological, and optical properties of Mn2O3 thin films have been studied.
-
The effects of calcination temperature as well as rotation spin in spinning process have been investigated.
-
The effect of solution aging on physical properties of the Manganese oxide thin films has been studied.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Nanostructured transition metal oxide thin films have attracted the attention of researchers and industry due to their unique physical and chemical properties [1,2,3,4]. Their special properties are because of the finite size and high surface to volume ratio. Among these nanomaterials, manganese oxide is particularly interested due to its non-toxicity, low prices, and availability. Manganese oxide nanostructures have a wide areas of applications in optics, electronics, and chemistry [5]. These nanostructures are widely used in electrochromic devices [6, 7], lithium-ion batteries [8,9,10], sensors [11, 12], high-efficiency chemical electrodes [13], electrochemical capacitors [9, 14], and so on.
Different methods can be used to fabricate manganese oxide nanostructures such as hydrothermal [15] and sol–gel [16]. Sol–gel has some advantages such as low processing temperatures, high chemical homogeneity, and the ability to control the size and morphology of nanostructures. In addition, their thin films can be produced by several methods like pulsed laser deposition [17], vacuum evaporation [18], chemical vapor deposition [19], spray pyrolysis [20], chemical bath deposition [21], atomic layer deposition [22], spin-coating [23], and sol–gel method [24]. Among these coating methods, spin-coating is a promising method that attracted the attention of researches due to low cost, fast operating, easily controllable coating variables, homogeneity, and uniformity of the products [25].
Manganese has different oxidation states and it can be converted to Mn2 +, Mn3+, and Mn+4 ions to form MnO, Mn2O3, MnO2, Mn2O7, Mn3O4 [26]. Various crystallographic phases of α, β, δ, λ, and γ have been reported for manganese oxide nanostructures in the literature [27]. Morphology and crystallographic forms of manganese oxide nanostructures strongly depends on the preparation conditions. Recently, α-MnO2 nanowires prepared by the hydrothermal method are reported for electromagnetic shielding [28]. Augustin et al have studied the effect of calcination temperature and O2 and Ar flows on manganese oxide formed by chemical precipitation method [29]. According to their results, the calcination temperature and the presence of gas flow significantly affects crystalline phase, lattice parameters, and crystallite size of MnOx species. They have found the best electrochemical performance for α-Mn2O3 phase through the linear sweep voltammetry measurements. Very recently, Fang et al. have reported the effect of Tween surfactant on morphology and electrical conductivity of Mn2O3 nanostructures formed by the solvothermal method. Their results have revealed the formation of different morphologies and electrical conductivity improvement upon adding the surfactant [30].
Furthermore, the MnO2–ZnO thin films prepared by dip-coating method on glass substrates have been reported and the effect of different zinc concentration has been investigated [31]. In addition, tetrapropylammonium manganese oxide thin films have been formed onto nickel foils by dip-coating technique showing interesting capacitive behavior, good reversibility, and cycling stability [32]. Moreover, MnO2 films deposited by sputtering at different annealing temperature have been studied [33]. The results have shown the annealing temperature as an important parameter causing the appearance of β-MnO2 and well crystallized β-Mn2O3 phases at 450 °C and 600 °C, respectively. Also, the effect of calcination temperature on self-assembled MnO2 thin films prepared directly on Ni-coated PET substrates has been investigated by Pang et al. [34]. According to their results, calcination temperature had a significant effect on the surface morphology, and the charge capacities increased reasonably with increasing the calcination temperatures up to 200 °C. In another research, spin coating of different commercial powders with different manganese oxide phases has been studied [35]. The effects of calcination temperature on morphological, structural, and electrochemical properties, and oxygen/hydrogen evolutions have been investigated. The results have shown that the MnO2 sample with amorphous structure had turned to α-Mn2O3 crystalline phase after calcination at 500 °C for 2 h. Furthermore, the results indicated that spin-coated samples had better oxygen/hydrogen evolution performance compared to electrodeposited films.
To the best of our knowledge, the effect of calcination temperature on structural, morphological, and optical properties of manganese oxide thin films prepared by sol–gel spin coating method has not been considered until now. Therefore, the focus of the present research has been made on the effect of calcination temperature on the physical properties of manganese oxide thin films by using sol–gel spin coating method. For this purpose, three annealing temperatures of 400, 450, and 500 °C have been considered to find the optimum calcination temperature. In addition, rotation spin in spinning process, as well as the effect of solution aging on physical properties of the manganese oxide thin films, have been studied.
2 Experimental
Mn2O3 thin films were prepared by using sol–gel spin coating method. Typically, a certain amount of manganese acetate (C6H9MnO6·4H2O, Merck, 98%) was dissolved in 6 ml mono-ethanolamine (C2H7NO, Merck, 98%) with a molar ratio of 1:1. Then, 10 ml 2-methoxyethanol (CH3OCH2CH2OH, Merck, 98%) was added. The final concentration of manganese acetate was 0.5 M. Then the mixture was stirred for 3 h by a magnetic stirrer at 80 °C. pH of the resulting solution was 7. After aging the solution for 24 h, manganese oxide thin films were deposited on pre-cleaned soda-lime glass substrates by spin coating technique at different rotation speeds (2000–4000 rpm) for 30 s. The spin coating apparatus used in the present investigation can rotate up to 9000 rpm with the accuracy of 5 rpm. A rotary pump was used during layer deposition to avoid substrate separation while the deposition process was going on.
The wet films were dried in an oven at 100 °C for 30 min. This process was repeated several times to have thin films of different layer numbers with desirable physical properties. Finally, the films were calcined at different temperatures (400–450–500 °C) in the presence of oxygen flux (grade 6) by tube furnace. The resulting samples are labeled as listed in Table 1. In addition, the effect of solution aging period was investigated, and samples were labeled as non-aged, 15 d, 30 d, and 45 d, for fresh solution, 15 days, 30 days, and 45 days aged solutions, respectively.
The crystalline structure of the films was analyzed by X-ray diffraction (XRD) analysis (ADVANCE-D8 model) with Cuka radiation source (λ = 1.5406 Å). Morphology of the prepared thin films were characterized by field emission scanning electron microscopy (FE-SEM) by means of a MIRA3 TESCAN- LMU electron microscope instrument and elemental combination, as well as concentrations of the films were, analyzed by energy-dispersive X-ray spectroscopy (EDX) using attached to FESEM instrument. UV–Vis optical transmittance was performed by a Perkin Elmer Lambda 25 double beam spectrophotometer. The absorption coefficient and band gap of the samples were estimated by using Beer–Lambert law and Tauc plot, respectively. According to Tauc’s equation one can find the band gap of material from the following equation: [36]
where α is the absorption coefficient, A is a constant, h is Planck’s constant, υ is the frequency, and Eg is the band gap. The exponent n is 2 and 1/2 for indirect and direct allowed transitions, respectively. So for direct band gap material the plotying of (αhυ)2 versus hυ and calculating the intersection of the linear fit and the photon energy axis, gives the value to Eg.
The crystalline size of the samples (D) was calculated by the Debye–Scherrer equation: [37]
where k is a constant, λ is the wavelength of X-rays (1.5418 Å), β is the FWHM (full width at half maximum), k is the Scherrer constant which dependent on the crystallite shape (here k = 0.9), and θ is the Bragg angle.
3 Results and discussion
3.1 Effect of calcination temperature
XRD analysis has been carried out, to find out the structural properties of the samples. Figure 1a shows XRD patterns of samples with 5 deposited layers and (b) shows XRD of samples with 6 layers, which calcined at different temperatures. It is clear from Fig. 1a that for relatively low calcination temperature (i.e., 400 °C) no crystalline phase has been detected. By increasing the calcination temperature to 450 °C, Mn2O3 phase with orthorhombic structure and pbca space group matching with card number of 01-071-0635, is formed. Further increasing the calcination temperate for \(S_{500}^6\) sample leads to crystallinity improvement and other crystalline planes, such as (211) and (400) can be detected in XRD pattern of this sample (Fig. 1b). XRD patterns revealed the [222] direction as the preferred growth orientation of the samples. By using Scherrer’s equation, crystallite size of the samples was calculated as 19.3 nm, 25.2 nm, and 28.6 for \(S_{450}^5\), \(S_{450}^6\), and \(S_{500}^6\), respectively. The increase in grain size may be attributed to both the layer number increment and increase of the calcination temperature.
Further investigation on structural properties and quantitative analysis of XRD patterns has been performed using Rietveld method by MAUD software refinement program, version 2.8. Figure 2 exhibits Rietveld fitting output and experimental results for \(S_{500}^6\) sample. Peak positions of orthorhombic Mn2O3 are marked as bar sequences below XRD patterns and difference between observed (Io) and calculated (Ic) intensities is plotted at the bottom of the plot.
Generally, Relative agreement factorsRwp, which weights residual error, is used to ascertain the ability of the performed structural model to account for the experimental data [38]. The value of goodness of fit (GOF) difference between experimental data and the calculated curve is calculated using the following equation:[39]
where Rexp is the expected error. An appropriate fit observed with the GOF value of 0.61 for \(S_{500}^6\) sample, notably indicates the fitting is appropriate for this nanostructured thin film. The calculated cell parameters are a = 9.36, b = 9.32, and c = 9.39 angstrom.
Morphological analysis of \(S_{400}^5\), \(S_{450}^5\), \(S_{400}^6\), \(S_{450}^6\), \(S_{500}^6\), and \(S_{500}^7\) samples are presented in Fig. 3a–f. Insets 3e is the EDX analysis of that sample. At lower calcination temperatures, for both 5 and 6 layer samples, a non-uniform surface without any distinct nanostructure can be observed. In the case of the highest calcination temperature, Fig. 3f reveals that the growth mechanism changes significantly with increasing the number of layers from 5 to 6.
EDS analysis for \(S_{500}^6\) sample showed no impurity element in the layer. The obtained atomic ratio of oxygen and manganese was 69% and 31%, respectively, which is in good agreement with the predicted theoretical values for Mn2O3.
Fig. 4a and c exhibit transmittance spectra and Fig. 4b and d exhibit (αhυ)2 versus hυ plot of 5 layer and 6 layer thin films, respectively. Results showed that by increasing the calcination temperature, the transmittance of deposited films decreased. Furthermore, by increasing the calcination temperature, band gap of the samples shifted to lower values and a red shift could be observed which indicated formation of smaller crystallite size due to quantum confinement effect. Interestingly, considering the SEM images, one may conclude that increasing the calcination temperature has led to increase of some particles in size. In fact, it may not be the case necessarily. That is, what is observed in SEM image might be some domains which have enlarged due to aggregation of small crystallites. On the other hand, the crystallite size of the samples calculated using Scherrer’s equation shows no much difference which may be an evidence of aggregation happening.
3.2 Effect of rotation speed
In this part, the effect of spin speed on physical properties of the samples has been studied. Figure 5 shows XRD patterns of S2000, S2500, S3000, and S4000 samples. The calculated crystallite sizes are 19.8 nm, 19.8 nm, 28.6 nm, and 13.4 nm, respectively. This shows that for lower speeds the crystallite size did not change, while for the highest speed (i.e. 4000 rpm) the crystallite size decreased, which could be attributed to the effect of high rotation speed in preventing the uniform dispersion of the solution on the surface.
Figure 6 displays FESEM images of samples deposited at different rotation speeds. The morphology of S2000 sample (Fig. 6a) is not uniform. The surface is not covered by the nanoparticles as well as cracks can be seen all over the surface. The nanoparticles are more uniformly distributed for S2500 sample (Fig. 6b), and cracks are less than that in previous sample. S3000 sample showed a uniformly distributed nanoparticles without any pinhole or crack on the surface. In the case of S4000 sample (Fig. 6d), the spinning speed is so fast that the solution did not have the chance for uniform dispersion on the surface, so again cracks and non-uniformity in the morphology of the sample can be observed.
Optical transmittance and Tauc’s plot of the samples as functions of rotation speed (for S2000–S4000 samples) are displayed in Fig. 7a, b, respectively. High spin speed leads to more transparent thin film due to lowering the thickness of the sample. The calculated band gaps are ranging from 3.95 eV to 4.05 eV. S4000 shows the highest transparency and the largest optical band gap. As it is clearly seen, the transmittance decrement has led to band gap shift towards lower energies.
3.3 Effect of solution aging
At the next step, precursor solution has been aged for different periods. For this purpose, deposition conditions were selected identical to those of sample \(S_{500}^6\). The starting solution was aged for 15, 30, and 45 days (acronyms are explained in the “Experimental” section). Results are collected and compared with non-aged (fresh) solution results. Figure 8 demonstrates the XRD patterns of the samples. Calculated crystallite sizes were 28.6 nm, 17.4 nm, 16.9, and 16.5 nm for fresh, 15 d, 30 d, and 45 d samples. The results showed that crystallite size decreased significantly with solution aging. On the other hand, some other crystallographic planes such as (233), (431), and (440) appeared upon increasing the aging time of solution.
Figure 9 represents the surface morphology of Mn2O3 thin films with different aging periods. It can be seen that for non-aged (Fig. 9a) and 15 d (Fig. 9b) samples small nanoparticles have been grown up. But by further increasing the solution aging time, grain-growth mechanism has been changed and surface has been composed of bigger agglomeration of nanoparticles.
Figure 10 shows the optical transmittance spectra and absorption coefficient of Mn2O3 thin films with different aging times. From Fig. 10a, the optical transmittance of the samples decreased about 10 percent by increasing the aging time. However, aging the solution did not change the absorption edge of the samples and according to Fig. 10b the band gap of samples with different aging times was found to be 3.92 eV.
4 Conclusion
Mn2O3 thin films have been deposited on soda-lime glass substrates by spin coating method. The effect of calcination temperature, rotation speed, and solution aging time was studied by means of XRD, FESEM, and optical transmission spectroscopy techniques. The results showed that relatively low calcination temperature, i.e. 400°C led to amorphous thin films, while by increasing it orthorhombic phase formed. For higher rotation speeds, the crystallinity of the samples decreased since solution was not able to disperse uniformly on substrate surface. FESEM results indicated that for low calcination temperature a uniform structure was not formed and agglomerations of particles happened. It was also observed that the calcination temperature and rotation speed can significantly affect the transparency of the films and make shift in their band gap energy. Aging the solution did not change the absorption edge of the samples. However, the optical transmittance of the samples decreased about 10 percent.
References
Shaikh A, Waikar M, Sonkawade R (2019) Effect of different precursors on electrochemical properties of manganese oxide thin films prepared by SILAR method. Synth Met 247:1–9
Astinchap B, Moradian R, Namdari T, Jurečka S, Ţălu Ş (2019) Prepared σ-MnO2 thin films by chemical bath deposition methods and study of its optical and microstructure properties. Optical Quantum Electron 51(6):170
Ahmadian H, Tehrani FS, Aliannezhadi M (2019) Hydrothermal synthesis and characterization of WO3 nanostructures: effects of capping agent and pH. Mater Res Express 6(10):105024
Jamali M, Tehrani FS (2020) Effect of synthesis route on the structural and morphological properties of WO3 nanostructures. Mater Sci Semiconductor Process 107:104829
Sharma S, Chauhan P, Husain S (2016) Structural and optical properties of Mn2O3 nanoparticles and its gas sensing properties. Adv Mater Proc 1:220–225
Mansouri M (2018) Effects of vacancy-defected, dopant and the adsorption of water upon Mn2O3 and Mn3O4 (001) surfaces: a first-principles study. Acta Physica Polonica A 133(5):1178–1185
Yang S et al. (2019) The excellent electrochemical performances of ZnMn2O4/Mn2O3: The composite cathode material for potential aqueous zinc ion batteries. J Electroanalytical Chem 832:69–74
Parveen N et al. (2019) Feasibility of using hollow double walled Mn2O3 nanocubes for hybrid Na-air battery. Chem Eng J 360:415–422
Abrego-Martínez J et al. (2019) Nanostructured Mn2O3/Pt/CNTs selective electrode for oxygen reduction reaction and methanol tolerance in mixed-reactant membraneless micro-DMFC. Electrochim Acta 297:230–239
Lee JH, Kim KJ (2013) Superior electrochemical properties of porous Mn2O3-coated LiMn2O4 thin-film cathodes for Li-ion microbatteries. Electrochim Acta 102:196–201
Sasikumar R, Chen T-W, Chen S-M, Rwei S-P, Yu M-C(2018) Facile synthesis of Mn2O3 for highly active catalytic oxidation and reduction of organic substances and electrochemical determination of L-methionine Int J Electrochem Sci 13(5):4561–4574
Korotcenkov G, Brinzari V, Ham M (2018) Materials acceptable for gas sensor design: advantages and limitations. Key Eng Mater 780:80–89
Hou Y, Cheng Y, Hobson T, Liu J (2010) Design and synthesis of hierarchical MnO2 nanospheres/carbon nanotubes/conducting polymer ternary composite for high performance electrochemical electrodes. Nano Lett 10(7):2727–2733
Liu P-P, Zheng Y-Q, Zhu H-L, Li T-T (2019) Mn2O3 hollow nanotube arrays on Ni foam as efficient supercapacitors and electrocatalysts for oxygen evolution reaction. ACS Appl Nano Mater 2(2):744–749
Zhang X et al. (2019) Influence of hydrothermal synthesis temperature on the redox and oxygen mobility properties of manganese oxides in the catalytic oxidation of toluene. Trans Metal Chem 44:663–670
Bach S, Henry M, Baffier N, Livage J (1990) Sol-gel synthesis of manganese oxides. J Solid State Chem 88(2):325–333
Yang D (2012) Pulsed laser deposition of cobalt-doped manganese oxide thin films for supercapacitor applications. J Power Sources 198:416–422
Broughton J, Brett M (2004) Investigation of thin sputtered Mn films for electrochemical capacitors. Electrochim Acta 49(25):4439–4446
Maruyama T, Osaki Y (1995) Electrochromic properries of manganese oxide thin films prepared by chemical vapor deposition. J Electrochem Soc 142(9):3137–3141
Walter C, Menezes PW, Loos S, Dau H, Driess M (2018) Facile formation of nanostructured manganese oxide films as high‐performance catalysts for the oxygen evolution reaction. ChemSusChem 11(15):2554–2561
Sarkar A, Satpati AK, Kumar V, Kumar S (2015) Sol-gel synthesis of manganese oxide films and their predominant electrochemical properties. Electrochim Acta 167:126–131
Nilsen O, Fjellvåg H, Kjekshus A (2003) Growth of manganese oxide thin films by atomic layer deposition. Thin Solid Films 444(1–2):44–51
Komaraiah D, Radha E, Reddy MR, Kumar JS, Sayanna R (2019) Structural, optical properties and photocatalytic activity of nanocrystalline TiO2 thin films deposited by sol–gel spin coating. i-Manager’s J Mater Sci 7(1):28
Ziller S, von Bülow J, Dahl S, Lindén M (2017) A fast sol–gel synthesis leading to highly crystalline birnessites under non-hydrothermal conditions. Dalton Trans 46(14):4582–4588
Sahu N, Parija B, Panigrahi S (2009) Fundamental understanding and modeling of spin coating process: a review. Indian J Phys 83(4):493–502
Maezono R, Ishihara S, Nagaosa N (1998) Phase diagram of manganese oxides. Phys Rev B 58(17):11583
Devaraj S, Munichandraiah N (2008) Effect of crystallographic structure of MnO2 on its electrochemical capacitance properties. J Phys Chem C 112(11):4406–4417
Awad MA, Hadia NMA (2018) Towards understanding the morphological, magnetic, optical and electrical properties of MnO2 nanowires for magneto-and optoelectronic applications. J Mater Sci: Mater Electron 29(24):20695–20702
Augustin M et al. (2015) Manganese oxide phases and morphologies: a study on calcination temperature and atmospheric dependence. Beilstein J Nanotechnol 6(1):47–59
Fang Y, Wang Y, Wang F, Zhu J (2019) 3D structured Mn2O3 synthesized using tween surfactant: influence on the morphology and oxygen reduction catalytic performance. CrystEngComm 21(3):420–429
Falahatgar S, Ghodsi F (2016) Optical characterization of nanostructured MnO2ZnO thin films prepared from acetate-based sol−gel precursors. Opt-Int J Light Electron Opt 127(3):1059–1065
Chin S-F, Pang S-C, Anderson MA (2002) Material and electrochemical characterization of tetrapropylammonium manganese oxide thin films as novel electrode materials for electrochemical capacitors. J Electrochem Soc 149(4):A379–A384
Fau P, Bonino J, Rousset A (1994) Electrical properties of sputtered MnO2 thin films. Appl Surf Sci 78(2):203–210
Pang SC, Chin SF, Ling CY (2011) Preparation and characterization of self-assembled manganese dioxide thin films. J Nanotechnol 2011:789305
Hernández S et al. (2016) Spin-coated vs. electrodeposited Mn oxide films as water oxidation catalysts. Materials 9(4):296
Hassanien A, Akl AA (2016) Effect of Se addition on optical and electrical properties of chalcogenide CdSSe thin films. Superlattice Microst 89:153–169
Aawani E, Memarian N, Dizaji HR (2019) Synthesis and characterization of reduced graphene oxide–V2O5 nanocomposite for enhanced photocatalytic activity under different types of irradiation. J Phys Chem Solids 125:8–15
Venkatramu V et al. (2010) Nanocrystalline lanthanide-doped Lu3Ga5O12 garnets: interesting materials for light-emitting devices. Nanotechnology 21(17):175703
Sain S, Patra S, Pradhan S (2012) Quickest ever single-step mechanosynthesis of Cd0.5Zn0.5S quantum dots: nanostructure and optical characterizations. Mater Res Bull 47(4):1062–1072
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Bahadori, A., Dizaji, H.R., Memarian, N. et al. Effect of preparation conditions on physical properties of manganese oxide thin films. J Sol-Gel Sci Technol 95, 180–189 (2020). https://doi.org/10.1007/s10971-020-05296-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-020-05296-x