Abstract
In our article, we show the results for wires with in situ MgB2 core doped with 8 at % of nano-SiC and ex situ MgB2 barrier doped with 8 at % of nano-diamond. All wires were annealed under high isostatic pressure of 1 GPa for 15 min in a temperature range from 700 to 800 ℃. Measurements were made using the vibrating magnetometer. The critical current density was determined with the Bean model. The study of the structure and composition of the MgB2 material were performed by using a scanning electron microscope (SEM). Our results show that annealing at 700 ℃ under isostatic pressure of 1 GPa allows to significant reduction of Mg and nano-SiC migration from the in situ MgB2 core to the ex situ MgB2 barrier. Further studies indicate that annealing at 750 ℃, under the same pressure of 1 GPa, also inhibits the migration of Mg and nano-SiC from the in situ MgB2 core to the ex situ MgB2 barrier. However, annealing at 800 ℃, and under the pressure of 1 GPa, leads to the total penetration of the barrier by Mg and nano-SiC.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
In the Mg + 2B compound, the synthesis reaction depends mainly on Mg, due to its low melting point of 650 ℃ under normal pressure [1, 2], compared to boron, which has a very high melting point of 2075 ℃, and its influence of atomic diffusion is very little. Moreover, the research shows that the isostatic pressure increases the melting point of Mg, e.g. 1 GPa, from 650 to 725 ℃ [1, 2]. The results presented by Gajda et al. [3, 4] show that heat treatment for temperatures at which Mg is in the solid state allows to obtain small grains and a large number of connection between grains. This leads to a high magnetic and transport critical current density (Jmc and Jtc). Additionally, it was noticed that heat treatment temperature above the Mg melting point leads to the formation of large grains and reduces the number of connections between grains [3, 4]. This decreases the Jmc and Jtc in the MgB2 material. Recent studies pointed out that the density of the unreacted Mg + 2B compound has a great influence on the synthesis reactions at Mg solid state [4] e.g. annealing temperature of 630 ℃ for precursor powders of Mg and B with high density of unreacted compound Mg + 2B (1.5 g/cm3) allows for a more complete synthesis reaction compared to the lower density of the unreacted compound M + 2B (1.38 g/cm3) [4]. Moreover, the density of the unreacted compound Mg + 2B has a greater influence on the synthesis reaction with Mg in the solid state than the grain size of B [3].
The diffusion barriers in MgB2 wires have are very important. They inhibit Mg reactions with the wire sheath, e.g. copper (Cu) sheath. This allows to obtain a large amount of superconducting phase. Moreover, the metal diffusion barriers are essential in multi-filament MgB2 wires, in which have small amount of superconducting material. The lack of metal barrier causes Mg to react with the wire sheath e.g. Cu, and significantly reduces the amount of superconducting material. Currently, the diffusion barriers in MgB2 wires are made with Nb, Ta, Ti, and Fe [5,6,7]. The measurements show that MgB2 wires without diffusion barriers have significantly lower critical current density, especially in high magnetic fields, than MgB2 wires with metal diffusion barriers [8, 9]. Unfortunately, these barriers are expensive and their hardness increases after cold drawing. The higher hardness might lead to damage of the metal barrier, e.g. during the reduction of the wires diameter. The hardness of metal barriers is reduced by thermal treatment after cold drawing, which improves the ductility of the diffusion metal barriers. The costs of these technological processes (e.g. cold drawing and recrystallization) and the high price of the metal used for the barriers significantly increase the final cost of MgB2 wires. A search for a different solution led to the idea of using a cheap, easy-to-produce reacted MgB2 material [10, 11]. It turns out that the cold drawing process does not increase hardness of ex situ MgB2 diffusion barrier because it is made of ex situ MgB2 powder [10, 11]. This means that the ex situ MgB2 barrier does not require annealing process after cold treatment. Additionally, ex situ MgB2 barrier has significantly cheaper components than metal diffusion barriers. All this reasons decrease the final price of MgB2 wires with the ex situ MgB2 barrier compared to MgB2 wires with metal diffusion barriers.
The studies conducted so far showed that SiC and C doping of MgB2 materials lead to the significant increases in Birr, Bc2, and Jc [12,13,14]. Furthermore, thermal treatment under high pressure allows the increase of the phase density and homogeneity of the MgB2 material, promotes the formation of small grains, and increases the number of connections between the grains in MgB2 wires with Nb diffusion barrier [15].
Our research shows that the synthesis reactions in MgB2 wires with the ex situ MgB2 barrier should be carried out at the temperature which Mg is in the solid state or not higher than approx. 25 ℃ above the Mg melting point. This allows the formation of a large amount of superconducting phase in the in situ MgB2 material and limits the diffusion of the doping from the in situ MgB2 material to the ex situ MgB2 barrier. This allows to obtain high critical parameters (Tc, Birr, and Jc) in MgB2 wires with ex situ MgB2 barrier.
2 Materials and Methods
The ex situ MgB2 material was made with commercially available, high-purity powders from Alfa Aesar. Moreover, the barrier was doped with 8 at% of nano-diamond (nD). In situ MgB2 material was produced from Mg with 99.8% of purity and amorphous nanoboron precursors powders, as a wire core. Additionally, in situ MgB2 was doped with 8 at.% nano-SiC (Nanostructured & Amorphous Materials Inc.). Both materials were treated under cold isostatic pressing (CIP) of 0.3 GPa. The total fill factor of superconductors was about 40% (whole MgB2 material: in situ MgB2 core and ex situ MgB2 barrier). The in situ MgB2 wires with ex situ MgB2 barrier were made in a GlidCop sheath of 1.2 mm diameter. The thermal treatments were carried out in the isostatic process at a 5 N purity argon atmosphere, with a pressure of 1 GPa, at various temperatures ranging from 700 to 800 ℃ for 15 min of annealing time (Table 1) [16]. The magnetic measurements were performed using vibrating magnetometer (VSM) at a temperature of 4.2 K. These measurements allow us to determine the critical temperature (Tc), irreversible magnetic field (Birr), and the magnetic critical current density (Jmc). Jmc was calculated using the Bean model (Jmc = 15 π Δm/4r, where r, MgB2 grain radius and Δm, the thickness of the magnetic hysteresis loop) [17]. The structure and composition were examined with a Zeiss Ultra Plus scanning electron microscope and FEI Nova Nano SEM 230 SEM.
The samples for FEI Nova NanoSEM 230 SEM were performed for cut MgB2 wires. This greatly reduces contamination that is generated during sample preparation by polishing for SEM analysis. On the other hand, the samples for the Zeiss Ultra Plus scanning electron microscope studies were cut with a wire saw. Care was taken to limit the formation of impurities.
3 Results and Discussion
SEM studies in Fig. 1a–c show that the final structure of nano-SiC doping in situ MgB2 core with ex situ MgB2 barrier, during the synthesis reaction, does not depend on the Mg state of matter. This means that, based on the results of Fig. 1a–c, we are not able to accurately determine the effect of the Mg state (solid or liquid) on the admixture distribution, grain size, and critical parameters. Moreover, in Fig. 1a–c, the process of Mg penetration from the in situ MgB2 core to the ex situ MgB2 barrier is not visible. This significantly influences the critical parameters of MgB2 wires.
The results in Fig. 1d–f show distribution of Mg in nano-SiC-doped MgB2 wire with ex situ MgB2 barrier. Based on these results, we can notice that in samples A and B, the distribution of Mg in the in situ MgB2 core is slightly different than in the ex situ MgB2 barrier. A slightly difference in the distribution of Mg in the structure of MgB2 wires with the ex situ MgB2 barrier does not allow to fully confirm the diffusion of Mg from the in situ MgB2 core to the ex situ MgB2 barrier during the synthesis reaction in the solid state of Mg, and at the point of the Mg transition from solid to liquid [1, 2]. On the other hand, the distribution of Mg in sample C is very homogeneous both in the ex situ MgB2 barrier and in the in situ MgB2 core. This means that liquid Mg [1, 2] completely penetrates the ex situ MgB2 barrier. The transfer of Mg from ex situ MgB2 to in situ MgB2 is imperceptible and negligible due to the high melting point (decomposition temperature above 800 ℃) [18] of the ex situ material and the short heating time (15 min.).
The further results in Fig. 1g–i present the Si distribution in the structure of the MgB2 wires with the ex situ MgB2 barrier. These results indicate that the nano-SiC particles remain in the in situ MgB2 core during the synthesis reaction at 700 °C and 750 °C under the isostatic pressure of 1 GPa. On the other hand, thermal treatment at 800 ℃ and the isostatic pressure of 1 GPa lead to the homogeneous distribution of nano-SiC particles in the entire structure of the MgB2 wire. We performed additional tests for nano-SiC particles in MgB2 wire with ex situ MgB2 barrier (linear analysis of composition and EDS analysis). Figure 2a shows that nano-SiC particles remain in the in situ MgB2 core after annealing at temperature of 750 ℃ and isostatic pressures of 1 GPa. Similar result was obtained for sample A (700 ℃ and 1 GPa). Figure 2b shows that annealing at the temperature of 800 ℃ and the isostatic pressure of 1 GPa leads to amount reduction of nano-SiC particles in the in situ MgB2 core and allows to obtain the homogeneous nano-SiC particle distribution throughout the MgB2 wire with the ex situ MgB2 barrier. Energy dispersion X-ray spectroscopy (EDS) analysis for samples A and B (Fig. 3a) showed that the nano-SiC particles remain in the in situ MgB2 core during the synthesis reaction at temperatures of 700 ℃ and 750 ℃ under conditions of 1 GPa isostatic pressure. The situation was different for the temperature of 800 ℃, when a significant reduction of these particles in the core took place. We know that silicon carbide (SiC) has high melting point of about 2730 ℃. Hence, the SiC nanoparticles cannot penetrate to the ex situ MgB2 barrier from the in situ MgB2 core, and that in turn means that only liquid Mg from the in situ MgB2 core can transfer the SiC nanoparticles to the ex situ MgB2 barrier. On the basis of Figs. 1, 2, 3, it is seen that the SiC nanoparticles from the in situ MgB2 core do not diffuse into the ex situ MgB2 barrier during the synthesis reaction in Mg solid state and at temperature which the Mg transition point from the solid to the liquid state. On the other hand, the results in Figs. 1–3 show that the thermal treatment in the liquid state of Mg leads to penetration of ex situ MgB2 barrier by the SiC nanoparticles.
The results in Fig. 4 show that the solid-state reaction of Mg and the Mg transition point from solid to liquid allow to obtain small in situ MgB2 core grain size, while heat treatment in the liquid state of Mg leads to large MgB2 grains.
Shi et al. [19] point out that magnetic critical current density (Jcm) is dependent on superconducting current paths form different kinds of loops, such as large loops over the whole sample, medium loops among neighboring grains, or small loops within grains. This indicates that Jcm is limited by both transverse and longitudinal connectivity [19]. Moreover, it is known that Jcm is dependent on grain size, voids, impurities, admixtures, micro-cracks, amount of superconducting phase, and pinning centers [20,21,22,23]. The results in Fig. 5 show that the thermal treatment under an isostatic pressure of 1 GPa at the Mg melting point allows to significantly increase the magnetic critical current density (Jcm) than solid state annealing of Mg at the isostatic pressure of 1 GPa. Such a large increase in Jcm in sample B may be the result of several factors e.g. improving and increasing the number of transverse and longitudinal connections between the grains, small grain size, and voids, more superconducting phase in the in situ MgB2 core, increasing the density of pinning centers. Moreover, the thermal treatment in the liquid state of Mg under isostatic pressure of 1 GPa leads to a significant reduction of Jcm in low and medium magnetic fields compared to Jcm of sample B (Mg transition from solid to liquid state). This reduction in Jcm may be due to the increase in grain size in the in situ MgB2 core in sample C (Fig. 4c). Larger grain sizes lead to a reduction in the number of inter-grain connections. Another factor which caused the Jcm reduction in sample C was the migration of Mg and nano-SiC form the in situ MgB2 core to the ex situ MgB2 barrier. This also causes a reduction in the amount of interconnections between the grains in the ex situ MgB2 barrier, because at the grain boundaries might appear nano-SiC particles, Mg2Si material and C. Additionally, migration of Mg and nano-SiC into the ex situ MgB2 barrier reduces the amount of the superconducting phase in the in situ MgB2 core, which in turn reduces the Jcm. Research presented by Wang et al. and Ghorbani et al. also showed that Si cannot be incorporated into the crystal lattice [24, 25]. This indicates that Si is at the grain boundaries and can form low and middle field pinning centers [23]. Li et al. [26] showed that Si can generate thermal stress, which in turn can create high-field pinning centers [21]. This indicates that migration of nano-SiC particle into the ex situ MgB2 barrier leads to the reduction of the pinning centers density in the in situ MgB2 core. It also leads to the reduction of Jcm in MgB2 wires with ex situ MgB2 barrier.
4 Conclusions
Our results show that annealing in the solid state of Mg and at the Mg melting point under the isostatic pressure of 1 GPa significantly reduces SiC diffusion from the in situ MgB2 core to the ex situ MgB2 barrier. Furthermore, thermal treatment at the Mg transition point from solid to liquid under isostatic pressure of 1 GPa allows to obtain small grains (in situ MgB2 core), improves and increases the number of connections between the grains, and also increases the pinning center density and Jcm. This is in contrast to the heat treatment of Mg in the liquid state under the pressure of 1 GPa, where the diffusion of SiC from in situ MgB2 core to the ex situ MgB2 barrier creates larger grain sizes (in situ MgB2 core), decreases the number of connections between the grains, and also reduces the pinning center density and Jcm.
References
Pelissier, J.L.: Determination of the phase diagram of magnesium: a model-potential approach in the sub-megabar range. Phys. Scr. 34, 838–841 (1986)
Avedesian, M., Baker, H.: ASM specialty handbook-magnesium and magnesium alloys. ASM. Mat.Db 1681–1683 (1999)
Gajda, D., et al.: Influence of amorphous boron grain size, high isostatic pressure, annealing temperature, and filling density of unreacted material on structure, critical parameters, n-value, and engineering critical current density in MgB2 wires. Mater. (Basel). 14, 3600 (2021)
Gajda, D., et al.: The significant influence of packing density of unreacted Mg+2B mixture and heat treatment conditions on some of critical parameters for MgB2/Fe wires. J. Alloys Compd. 889, 161665 (2021)
Kim, J.H., et al.: Influence of hot-pressing on MgB2/Nb/Monel wires. Physica C: Superconductivity and its Applications (2010). https://doi.org/10.1016/j.physc.2010.05.129
Santra, S., et al.: Comparison of interfacial and critical current behaviour of Al+Al2O3 sheathed MgB2 wires with Ta and Ti diffusion barriers. J. Alloys Compd. 807, 151665 (2019)
Li, C., et al.: Significant improvement in superconducting properties of in situ powder-in-tube MgB2 wires through anthracene doping and heat treatment optimization. Supercond. Sci. Technol. 32, (2019)
Woźniak, M., Juda, K.L., Hopkins, S.C., Gajda, D., Glowacki, B.A.: Optimization of the copper addition to the core of in situ Cu-sheathed MgB2 wires. Supercond. Sci. Technol. 26, 105008 (2013)
Li, G.Z., Yang, Y., Susner, M.A., Sumption, M.D., Collings, E.W.: Critical current densities and n-values of MgB 2 strands over a wide range of temperatures and fields. Supercond. Sci. Technol. 25, 025001 (2012)
Kario, A., et al.: Superconducting and microstructural properties of (Mg+2B)+MgB2 /Cu wires obtained by high gas pressure technology. Acta Phys. Pol. A - Acta Phys. Pol A 111, (2007)
Gajda, D., et al.: The critical parameters in in-situ MgB2 wires and tapes with ex-situ MgB2 barrier after hot isostatic pressure, cold drawing, cold rolling and doping. J. Appl. Phys. (2015). https://doi.org/10.1063/1.4919364
Kazakov, S.M., et al.: Carbon substitution in MgB 2 single crystals: structural and superconducting properties. Phys. Rev. B - Condens. Matter Mater. Phys. (2005). https://doi.org/10.1103/PhysRevB.71.024533
Dou, S., et al. Publisher’s Note: Mechanism of enhancement in electromagnetic properties of MgB2 by nano SiC doping [Phys. Rev. Lett. 98, 097002 (2007)]. Phys. Rev. Lett. 98, (2007)
De Silva, K.S., et al.: A significant improvement in the superconducting properties of MgB2 by co-doping with graphene and nano-SiC. Scr. Mater. 67, 802–805 (2012)
Gajda, D., et al.: Significant enhancement of the critical current of MgB2 wires through a reduction of the diameter using HIP method. Scr. Mater. 143, 77–80 (2018)
Gajda, D., et al.: Formation of high-field pinning centers in superconducting MgB2 Wires by using high hot isostatic pressure process. J. Supercond. Nov. Magn. 30, 3397–3402 (2017)
Horvat, J., Yeoh, W.K., Kim, J.H., Dou, S.X.: Transport and magnetic critical current in superconducting MgB2 wires. Supercond. Sci. Technol. 21, 065003 (2008)
Glowacki, B.A., et al.: Superconductivity of powder-in-tube MgB2 wires. Supercond. Sci. Technol. 14, (2001)
Shi, Z.X., Susner, M.A., Sumption, M.D., Collings, E.W.: Doping effect and flux pinning mechanism of nano-SiC additions in MgB2 strands. (2011). https://doi.org/10.1088/0953-2048/24/6/065015
Horvat, J., Soltanian, S., Wang, X.L., Dou, S.X.: Effect of sample size on magnetic Jc for MgB2 superconductor. Appl. Phys. Lett. 84, 3109–3111 (2004)
Gajda, D., Zaleski, A., Morawski, A., Hossain, M.S.A.: New types of high field pinning centers and pinning centers for the peak effect. Supercond. Sci. Technol. (2017). https://doi.org/10.1088/1361-6668/aa769f
Liang, G., et al.: Effects of MgO impurities and micro-cracks on the critical current density of Ti-sheathed MgB2 wires. Phys. C Supercond. 457, 47–54 (2007)
Cimberle, M.R., Novak, M., Manfrinetti, P., Palenzona, A.: Magnetic characterization of sintered MgB2 samples: effect of the substitution or doping with Li. Al and Si. (2001). https://doi.org/10.1088/0953-2048/15/1/308
Wang, X.L., et al.: Enhancement of the in-field J c of MgB 2 via SiCl 4 dopig. Phys. Rev. B 81, 224514 (2010)
Ghorbani, S.R., Wang, X.L., Hossain, M.S.A., Dou, S.X., Lee, S.-I.: Coexistence of the δ l and δ T c flux pinning mechanisms in nano-Si-doped MgB 2. Supercond. Sci. Technol. 23, 025019 (2010)
Li, W.X., Zeng, R., Lu, L., Dou, S.X.: Effect of thermal strain on Jc and Tc in high density nano-SiC doped MgB2. J. Appl. Phys. 109, 07E108 (2011)
Funding
This research was supported by The National Centre for Research and Development [grant number POIR.04.01.02–00-0047/17, “Prosuprex”].
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Filar, K., Morawski, A., Zaleski, A. et al. Superconducting Properties and Microstructure Changes after Heat Treatment of In Situ MgB2 Wires with Ex Situ MgB2 Barriers. J Supercond Nov Magn 35, 1491–1497 (2022). https://doi.org/10.1007/s10948-022-06296-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-022-06296-4