Abstract
Detailed phase relations have been determined within the systems Fe2O3-MgO-TiO2 and FeO-MgO-TiO2. Experiments were performed over the temperature interval 1173–1473 K by equilibrating pelletized, fine-grained oxide mixtures in either inert calcia-stabilized zirconia pots (Fe2O3-MgO-TiO2 system) or evacuated silica tubes (FeO-MgO-TiO2 system). Equilibrium phase assemblages were determined by combined optical microscope, X-ray diffraction and EMP examination. Phase relations in the Fe2O3-MgO-TiO2 ternary are dominated by the instability of the M2O3 solid solution relative to the phase assemblage M3O4 + M3O5. A miscibility gap along the M2O3 binary also gives rise to two, 3-phase fields (α-M2O3 + M3O5 + M3O4 and α′-M2O3 + M3O5 + M3O4) separated by the M3O4 + M3O5 phase field. Phase relations in the FeO-MgO-TiO2 ternary were divided into two sub-systems. For the FeTiO3-MgTiO3-TiO2 sub-ternary, there is complete solid solution along the M2O3 and M3O5 binary joins at high temperature. At low temperatures (T < 1373 K) the M3O5 pseudobrookite solid solution decomposes to M2O3 + TiO2. Increasing the concentration of MgO in M3O5 phase results in a decrease in the temperature at which M3O5 becomes unstable and compositional tie lines linking M2O3 and TiO2 fan out, before the appearance of a three-phase region where M2O3, M3O5, and TiO2 coexist. Within the expanded FeO-MgO-TiO2 system, at temperatures above ∼1273 K there is a continuous solid solution along the M3O4 binary. At low temperatures (T < 1273 K) the Mg2TiO4 end-member breaks down to MgO and MgTiO3. The M3O4 phase shows significant non-stoichiometry, down to at least 1173 K. Fe2+-Mg partitioning data were obtained for coexisting M2O3-M3O5 and M2O3-M3O4 pairs in the FeO-MgO-TiO2 ternary. Assuming a regular solution mixing model for all phases, the M2O3 and M3O4 solid solutions were both found to exhibit moderate positive deviations from ideality (∼2600 J/mol), whereas the data for the M3O5 binary suggest close to ideal behaviour.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Author information
Authors and Affiliations
Additional information
Received: 22 May 1998 / Accepted: 3 November 1998
Rights and permissions
About this article
Cite this article
Pownceby, M., Fisher-White, M. Phase equilibria in the systems Fe2O3-MgO-TiO2 and FeO-MgO-TiO2 between 1173 and 1473 K, and Fe2+-Mg mixing properties of ilmenite, ferrous-pseudobrookite and ulvöspinel solid solutions. Contrib Mineral Petrol 135, 198–211 (1999). https://doi.org/10.1007/s004100050506
Issue Date:
DOI: https://doi.org/10.1007/s004100050506