Abstract
In recent years, the exploitation of natural resources and industrial development have led to the production of harmful pollutants. Much of these contaminants end up in water resources, reducing the availability of drinking water. Therefore, it is necessary to find remedies to this situation. Solutions could be the adsorption or the degradation through photocatalysis of these compounds. A good candidate for this task is titanium dioxide (TiO2), due to its non-toxicity, stability and low cost. In this work, we propose a novel synthesis of TiO2 nanoparticles (NPs), with high adsorption capacity, produced at low temperature in alkaline environment. Adsorption tests were conducted using methylene blue and diclofenac as model pollutants. Moreover, the obtained NPs have been characterized through Raman spectroscopy, Scanning and Transmission electron microscopies and with thermogravimetric analysis. The results showed a porous structure with a high surface area, able to efficiently adsorb large amounts of dye from the aqueous solution. These properties make the obtained TiO2 powders suitable for applications devoted to the adsorption and recovery of harmful compounds.
Graphic abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
Water is an essential element for life. The availability of drinking water is threatened mainly by over-exploitation of water sources and excessive pollution. According to the 2019 World Health Organization report, in 2017, 29% of the global population lacked “safely managed drinking water” meaning water at home, available, and safe [1]. Presence of harmful compounds in water is mainly due to industrial, agricultural, and domestic activities [2] and creates problems directly or indirectly to the flora and fauna and consequently also to mankind. Moreover, this type of pollution has negative effects not only on health, but also from a socio-economic perspective [3, 4]. Two viable solutions against pollutants are their recovery through porous, high-surface, adsorbent materials that can be easily separated from the reaction environment (e.g., by centrifugation or by fixing it onto a substrate) [5, 6] or their neutralization and dissociation via chemical reactions of photocatalysis. Activated carbon, clay minerals, zeolites and polymers are some of the most utilized porous and adsorbent materials [7,8,9] whereas TiO2, ZnO, CeO2 ZrO2 and WO3 are chosen for their photocatalytic activity [10,11,12], or more in general, in the catalysis of chemical reactions [13,14,15].
Among the latter, TiO2 has attracted a great interest in the scientific community. This material is chemically stable, non-toxic and low cost [16] and it is used in the degradation of harmful and organic compounds [17,18,19,20] through its photoactivity triggered by ultraviolet light (UV), which generates electron-gap pairs responsible for the production of free radicals. Moreover, titanium dioxide is well known also for its mechanical and optical properties [21,22,23] which are applied in several fields, such as energetic, environmental, antibacterial and material science [24].
It has a compact crystalline structure and exists in three phases: anatase, rutile and brookite. It can be synthesized by several chemical [25,26,27,28] and physical [29, 30] techniques in the form of nanoparticles (NPs) [31, 32] and thin films [33,34,35]. At low calcination temperatures (TC < 400 °C), it is amorphous and exhibits a porous structure but, to our best knowledge, there are no many studies that take into consideration this property for environment applications. TiO2-based materials with adsorption capacity are generally made of composite materials [36,37,38,39]. This is also confirmed by a 2018 review analysing titania materials fixed on adsorbent substrates for the production of composite structures [40].
In this work, novel porous TiO2 nanopowders with a high and direct adsorption capacity, prepared by sol–gel method at low temperature (TC = 100 °C) and in an alkaline environment, were produced. We present a fast and simple synthesis of these NPs with an eco-friendly procedure, as it does not use toxic reagents. The chemical structure of the obtained materials has been characterised by Raman spectroscopy, scanning (SEM) and transmission electron (TEM) microscopies and thermogravimetric analysis (TGA) measurements. Methylene blue (MB) and diclofenac have been also used to study the adsorption behaviour of the TiO2 nanoparticles. The results have shown a very high and unusual seizing capacity of MB by the nanoparticles, a photocatalysis-independent phenomenon, due to the porous structure and high surface area of the nanoparticles. This adsorption is shown to be extremely fast and more advantageous than a photocatalysis process.
2 Materials and synthesis procedure
The titania (TiO2) nanopowders were synthesized by the sol–gel method. All the chemicals used were of reagent-grade purity and were purchased from Sigma-Aldrich. The production of titanium dioxide nanopowders was carried out in alkaline medium, using NH4OH, and in a neutral water medium as a comparison. In particular, for the alkaline solution preparation, 13.5 ml of NH4OH at 28–30% was added to 10 ml of ultrapure water milliQ. Subsequently, 1.5 ml of Titanium tetraisopropoxide (TTIP) was added to the solution and left in agitation for 60 min and then kept in dark for 24 h. The obtained precipitate was washed and collected two times with 2-propanol and other two times with ultrapure water, in an orbital shaker. After washing, the products were dried in an oven for 2 h at 50 °C. Such powders were then thermally treated for 3 h in a muffle at three different calcination temperatures TC = 100, 450 and 800 °C. Then, the powder samples were packed into glass holders without any other preparations.
2.1 Characterization techniques
Raman spectra were recorded with an InVia spectrometer, manufactured by Renishaw PLC (Gloucestershire, UK), equipped with optical microscope manufactured by Leica (Wetzlar, Germany). The excitation source was the 514.5 nm output of an Ar+ ions laser working at a maximum output power of 25 MW. All spectra were recorded using a resolution of 1.5 cm−1 over the spectral range of 150–3000 cm−1 at room temperature. X-Ray diffraction analyses were performed on titania powders, using a Rigaku Miniflex diffractometer, operating in step‐scan mode and employing Cu Kα radiation at 30 kV and 100 mA. The measurements were collected from 10° to 80°, with a 0.010° step size and a scan speed of 0.25° min−1.
SEM images were acquired by the scanning electron microscope JEOL JSM-5410LV with a Si(Li) windowless detector for the energy-dispersive X-ray microanalysis, an emission source of tungsten filament (W), a resolution of 3.5 nm, a magnification of 100–200,000× and an acceleration voltage of 0.5–30 kV. The samples were observed at low-vacuum mode, avoiding any kind of polishing and without covering by a conductive layer. Analysis was processed using Link Isis software by Oxford Instruments and Image Pro-Plus by Media Cybernetics.
TEM images of TiO2 materials were taken using Hitachi 7700 transmission electron microscope operated at 100 kV. This acceleration voltage was settled to obtain a sufficient resolution and minimal radiation damage of the material. Specimens for TEM observations were prepared by drop-casting of freshly solutions containing TiO2 nanoparticles onto standard carbon supported 600-mesh copper grid and drying slowly in air naturally.
Thermogravimetric analysis was used to monitor the mass variation of the titania powder samples. The system checks weight loss in function of time or temperature. The apparatus consisted of a Simultaneous Thermal Analyzer STA 409 by NETZSCH. Tests required a temperature ramp from 10 to 1100 °C, with a heating rate of 10 °C/min. Each sample was measured three times. The analysis was conducted in air atmosphere. The degradation rate can be known if the tangent at the curve is traced.
2.2 Adsorption tests
Adsorption tests were carried out on samples of TiO2 powders prepared in neutral and alkaline pH condition. The adsorption properties of the samples were evaluated by studying the variation in the methylene blue concentration in aqueous medium spectrophotometrically (using a PerkinElmer Lambda 45 UV–Vis spectrophotometer) via the solution absorbance in the Lambert–Beer regime. A quantity of 2.5 mg of TiO2 nanopowder was dispersed in 2 ml of the MB solution with a starting concentration of 1.5 × 10–5 M. Another test was conducted with diclofenac. Also in this case, 2.5 mg of TiO2 nanopowder was dispersed in 2 ml of diclofenac solution at a concentration of 1 × 10–4 M. The absorbance (A) of the solutions was measured at regular intervals (30 min), until the adsorption equilibrium was reached, recovering a fraction of the solution after centrifuging. Adsorption was studied monitoring the peak absorption of the MB at 665 nm and the peak absorption of diclofenac at 276 nm. Results are reported as A/A0, where A0 is the absorbance value of the solution a t = 0 min.
3 Results and discussion
3.1 Raman characterization
Raman spectra are reported in Fig. 1. The analysis revealed the typical active modes of anatase for the samples prepared in a neutral medium and calcinated at 100 °C and 400 °C. The peaks were observed at 151, 403, 518 and 639 cm−1 for the powder treated at 100 °C and at 144, 397, 516 and 636 cm−1 for that at 400 °C, and are attributed [41] to the vibration symmetries Eg, B1g, A1g/B1g and Eg, respectively. The active mode shift at 151 cm−1 observed in the sample treated at 100 °C in neutral medium could be related to low crystallinity and to the presence of oxygen vacancies in the TiO2 structure, as reported in literature [42, 43]. The samples treated at the highest temperature (TC = 800 °C) showed three optical phonon peaks of the rutile phase: a very low-intensity mode centred at 143 cm−1 and two high-intensity modes at 446 and 609 cm−1, related to the B1g, Eg and A1g symmetries, respectively. The band observed around 235 cm−1 is generally attributed to the two-photon scattering [44].
Both TiO2 nanoparticles synthesized in neutral and alkaline environments showed similar structures at the Raman analysis. Only the powder treated at 100 °C and prepared in alkaline solution showed a strong amorphous structure, probably induced by the sol (nitrogen was introduced during the sol–gel preparation as ammonium) and by the low temperature, inadequate to induce the crystallization of the titanium dioxide. On the other hand, temperatures of 400 °C and 800 °C were sufficient to induce the crystallization (anatase and rutile, respectively) in the same basic environment.
3.2 TEM and SEM analyses
To study the morphology of nanoparticles, TEM and SEM observations of the nanopowders prepared in neutral and alkaline conditions and thermally treated at 100 °C and 400 °C were carried out. Under the transmission microscope, the alkaline low-temperature sample appeared as very thin sheets folded and/or rolled up along the edges (Fig. 2a). On the contrary, the sample prepared in neutral environment at low temperature (Fig. 2b) showed a granular structure typical of sol–gel synthesis.
In addition, the increase in temperature (TC = 400 °C) induced a drastic change in the nanoparticles morphology. The powders synthesized in neutral or alkaline environments developed, instead, a granular structure (Fig. 3a, b). We founded the same result at the highest temperature (TC = 800 °C) (images are not reported here).
The structure of the alkaline sample treated at 100 °C, observed at TEM, was studied in detail at SEM. Under the scanning microscope, nanoparticles revealed a highly porous nano-tubular structure (Fig. 4a–c).
SEM and TEM analyses confirmed the extremely porous nature of the TiO2 NPs with a large surface area.
3.3 Thermogravimetic analysis
Thermogravimetric analysis tests were carried out to study the mass variation as a function of the temperature and to indirectly acquire information regarding the surface area of the nanoparticles. Generally, a mass variation, observed in an incompatible temperature range with the phase transition temperature, may be related to desorption of molecules from the surface of the material, so the greater the change in mass, the greater the surface area of the material. The measurements were conducted on TiO2 powders prepared in neutral and alkaline environments at different temperatures (TC = 100, 400 and 800 °C). The samples were heated up to 1100 °C and the mass variation vs temperature was measured. The resulting graphs are displayed in Fig. 5. Samples calcined at 800 °C did not highlight a change in mass, while those calcined at 400 °C showed only a slight decrease in mass (< 5%). Only the powders dried during preparation at 100 °C, revealed a greater decrease in mass: in particular, we found a mass loss of about 10% for those prepared in neutral environment and a more consistent decrease of 22.5% for the samples synthetized in alkaline medium. The mass variation occurred at temperatures in range between 20 and 200 °C, in which the molecules, such as water adsorbed to the surface [45], pass into the gas phase reducing the mass of the sample. Therefore, the change in mass is due to desorption of molecules from the surface and not to a phase change of titanium dioxide, which occurs at higher temperatures [46]. These results were in accordance with the high surface area observed by electron microscopy analyses.
3.4 Adsorption tests
Figure 6 shows the MB absorption kinetics of TiO2 nanopowders prepared in neutral and alkaline media, calcinated at different temperatures (TC = 100, 400, 800 °C). The graph shows the absorbance values normalized with respect to the initial value (A/A0), as a function of time. All samples reached the adsorption equilibrium after about 30 min. Only one sample revealed a different behaviour from the others. Differently from the others, the nanopowder prepared in alkaline environment and calcinated at 100 °C showed a rapid drop in the absorbance value of the solution, “decolorizing” it in a few minutes.
It was, therefore, studied in detail the kinetics of adsorption of this sample. To achieve the sample saturation, the solution was centrifuged, and the liquid phase was recovered. Subsequently, the nanopowder was dispersed in a fresh MB solution. Once again, the powder showed a rapid adsorption of the dye, completely absorbing the MB within 30 min. This effect was then studied for several times and, only after 12 cycles, the phenomenon demonstrated a slowdown, as shown in Fig. 7.
The strong adsorption of the dye may be due to an effect of opposite surface charge, which guarantees the attraction between organic molecule and TiO2, to a high surface area of titania NPs or to a synergistic effect of these two factors. To understand the charge influence on the adsorption, a test with diclofenac (a molecule with an opposite charge to MB) was carried out.
Figure 8 shows the absorption kinetics of this molecule on TiO2 powder prepared at 100 °C in basic pH environment. In this case, the adsorption resulted much more limited and the system reached the equilibrium after 230 min. Therefore, the charge of the target molecule seems to play a role in this phenomenon.
The obtained results are very interesting and have been compared with literature. Table 1 shows the adsorption performance comparison between our material and two found in recent papers. The comparison takes into account the different starting conditions in terms of concentration, amount of TiO2 used and exposure time. The TiO2 described in our work is capable of absorbing a good amount of dye in 30 min. This quantity is even greater taking into account that, after 30 min, the sample has not reached the saturation and, therefore, several cycles are needed to reach it, bringing the absorbed amount to rather high values.
4 Conclusion
In this work, TiO2 NPs with high adsorption capacity were synthetized with a simple and eco-friendly procedure. The powder prepared in basic environment and at low temperature (TC = 100 °C) revealed a more complex and porous structure than other nanoparticles synthesized in neutral environment. TEM and SEM analyses highlighted also a high surface area. In addition, these nanoparticles showed a good affinity for methylene blue rather than diclofenac, indicating that the extreme adsorbing capacity founded is due to the synergistic effect of surface charge and surface area. According to these considerations, these titania-based materials can be effectively applied in the context of adsorption and recovery of pollutants from wastewaters.
References
Unicef, World Health Organization. Progress on household drinking water, sanitation and hygiene 2000–2017: Special focus on inequalities. 2019
P.A.G.M. Scheren, H.A. Zanting, A.M.C. Lemmens, Estimation of water pollution sources in Lake Victoria, East Africa: application and elaboration of the rapid assessment methodology. J. Environ. Manage. 58(4), 235–248 (2000)
A. Ebenstein, The consequences of industrialization: evidence from water pollution and digestive cancers in China. Rev. Econ. Stat. 94(1), 186–201 (2012)
Z. Garba, Domestic water pollution among local communities in Nigeria—causes and consequences. Eur. J. Sci. Res. 52(4), 592–603 (2011)
L. Li, B. Li, L. Wu, X. Zhao, J. Zhang, Magnetic, superhydrophobic and durable silicone sponges and their applications in removal of organic pollutants from water. Chem. Commun. 50, 7831–7833 (2014)
P. Samanta, A.V. Desai, S. Let, S.K. Ghosh, Advanced porous materials for sensing, capture and detoxification of organic pollutants toward water remediation. ACS Sustain. Chem. Eng. 7(8), 7456–7478 (2019)
Q.U. Jiuhui, Research progress of novel adsorption processes in water purification: a review. J. Environ. Sci. 20, 1–13 (2008)
J. Wang, Y. Xu, B. Ding, Z. Chang, X. Zhang, Y. Yamauchi, K.C.-W. Wu, Confined self-assembly in two-dimensional interlayer space: monolayered mesoporous carbon nanosheets with in-plane orderly arranged mesopores and a highly graphitized framework. Angew. Chem. Int. Ed. 57(11), 2894–2898 (2018)
E. Doustkhah, J. Lin, S. Rostamnia, C. Len, R. Luque, X. Luo, Y. Bando, K.C.-W. Wu, J. Kim, Y. Yamauchi, Y. Ide, Development of sulfonic-acid-functionalized mesoporous materials: synthesis and catalytic applications. Chem. Eur. J. 25(7), 1614–2163 (2019)
H. Ren, P. Koshy, W. Chen, S. Qi, C.C. Sorrell, Photocatalytic materials and technologies for air purification. J. Hazard. Mater. 325, 340–366 (2017)
C.C. Lee, C.L. Chen, Y.T. Liao, K.C.W. Wu, C.C. Chueh, Enhancing efficiency and stability of photovoltaic cells by using perovskite/Zr-MOF heterojunction including bilayer and hybrid structures. Adv. Sci 6(5), 1801715 (2019)
C.-C. Chueh, C. Chen, Y. Su, H. Konnerth, Y. Gu, C. Kung, K.C.-W. Wu, Harnessing MOF materials in photovoltaic devices: recent advances, challenges, and perspectives. J Mat. Chem. A. 7, 17079–17095 (2019)
Y. Liao, B.M. Matsagar, K.C.-W. Wu, Metal-organic framework (MOF)-derived effective solid catalysts for valorization of lignocellulosic biomass. ACS Sustain. Chem. Eng. 6(11), 13628–13643 (2018)
H. Konnerth, B.M. Matsagar, S.S. Chen, M.H.G. Prechtl, F.-K. Shieh, K.C.-W. Wu, Metal-organic framework (MOF)-derived catalysts for fine chemical production. Coord. Chem. Rev 416, 213319 (2020)
Y. Liao, V.C. Nguyen, N. Ishiguro, A.P. Young, C. Tsung, K.C.-W. Wu, Engineering a homogeneous alloy-oxide interface derived from metal-organic frameworks for selective oxidation of 5-hydroxymethylfurfural to 2,5-furandicarboxylic acid. Appl. Catal. B 270, 118805 (2020)
F. Madjene, L. Aoudjit, S. Igoud, H. Lebik, B. Boutra, A review: titanium dioxide photocatalysis for water treatment. Trans. J. Sci. Technol. 3(10), 1857–8047 (2013)
K. Xiaolan, L. Sihang, D. Zideng, H. Yunping, S. Xuezhi, T. Zhenquan, Titanium dioxide: from engineering to applications. Catalysts 9(2), 191 (2019)
A. Fujishima, X. Zhang, D.A. Tryk, TiO2 photocatalysis and related surface phenomena. Surf. Sci. Rep. 63, 515–582 (2008)
Y. Lee, S. Lee, H.S. Kim, J.T. Moon, J.B. Joo, I. Choi, Multifunctional and recyclable TiO2 hybrid sponges for efficient sorption, detection, and photocatalytic decomposition of organic pollutants. J. Ind. Eng. Chem. 73, 328–335 (2019)
A. Fujishima, K. Honda, Electrochemical photolysis of water at a semiconductor electrode. Nature 238, 37 (1972)
V.C. Gudla, F. Jensen, A. Simar, R. Shabadi, R. Ambat, Friction stir processed Al–TiO2 surface composites: anodising behaviour and optical appearance. Appl. Surf. Sci. 324, 554–562 (2015)
V.C. Gudla, V.E. Johansen, S. Canulescu, J. Schou, R. Ambat, Simulation of reflectance from white-anodised aluminium surfaces using polyurethane–TiO2 composite coatings. J. Mater. Sci. 50, 4565–4575 (2015)
R.U. Din, V.C. Gudla, M.S. Jellesen, R. Ambat, Microstructure and corrosion performance of steam-based conversion coatings produced in the presence of TiO2 particles on aluminium alloys. Surf. Coat. Technol. 296, 1–12 (2016)
X. Chen, S.S. Mao, Titanium dioxide nanomaterials: synthesis, properties, modifications, and applications. Chem. Rev. 107(7), 2891–2959 (2007)
B.K. Mutuma, G.N. Shao, W.D. Kim, H.T. Kim, Sol–gel synthesis of mesoporous anatase–brookite and anatase–brookite–rutile TiO2 nanoparticles and their photocatalytic properties. J. Colloid Interface Sci. 442, 1–7 (2015)
T. Kalaivani, P. Anilkumar, Role of temperature on the phase modification of TiO2 nanoparticles synthesized by the precipitation method. Silicon 10(4), 1679–1686 (2018)
C.C. Wang, J.Y. Ying, Sol–gel synthesis and hydrothermal processing of anatase and rutile titania nanocrystals. Chem. Mater. 11, 3113 (1999)
S. Seifried, M. Winterer, H. Hahn, Nanocrystalline titania films and particles by chemical vapor synthesis. Chem. Vap. Depos. 6, 239 (2000)
H.M. Smith, A.F. Turner, Vacuum deposited thin films using a ruby laser. Appl. Opt. 4(1), 147 (1965)
L. Velardi, L. Scrimieri, G. Vasco, A. Serra, D. Manno, V. Nassisi, L. Calcagnile, G. Quarta, Nickel doped TiO2 films by a modified laser plasma source for photocatalytic applications. J. Inst. 15, C03039 (2020)
A. Nath, S.S. Laha, A. Khare, Synthesis of TiO2 nanoparticles via laser ablation at titanium–water interface. Integr. Ferroelectr. 121(1), 58 (2010)
L. Velardi, L. Scrimieri, A. Serra, D. Manno, L. Calcagnile, The synergistic role of pH and calcination temperature in sol–gel titanium dioxide powders. Appl. Phys. A 125, 735 (2019)
A. Jilani, M. Shaaban, A.H. Hammad, Advance deposition techniques for thin film and coating, in Modern technologies for creating the thin-film systems and coatings (Chapter 8). ed. by N.N. Nikitenkov (IntechOpen, London, 2017)
W.B. Wang, A. Yanguas-Gil, Y. Yang, Chemical vapor deposition of TiO2 thin films from a new halogen-free precursor. J. Vac. Sci. Technol. A. 32, 061502 (2014)
L. Scrimieri, A. Serra, D. Manno, P. Alifano, S.M. Tredici, M. Calcagnile, L. Calcagnile, TiO2 films by sol–gel spin coating deposition with microbial anti-adhesion properties. Surf. Interface Anal. 51, 1351–1358 (2019)
D. Kim, M. Jung, K. Sangjin, H. Kim, H.J. Lee, K. Oh, M. Moon, UV-responsive nano-sponge for oil absorption and desorption. Sci. Rep. 5, 12908 (2015)
L. Zhao, F. Xue, B. Yu, J. Xie, X. Zhang, R. Wu, R. Wang, Z. Hu, S. Yang, J. Luo, TiO2–graphene sponge for the removal of tetracycline. J. Nanopart. Res. 17, 16 (2015)
M.I. Arabatzis, P. Falaras, Synthesis of porous nanocrystalline TiO2 foam. Nano Lett. 3(2), 249–251 (2003)
R. Hickman, E. Walker, S. Chowdhury, TiO2-PDMS composite sponge for adsorption and solar mediated photodegradation of dye pollutants. J. Water Process Eng. 24, 74–82 (2018)
S. MiarAlipour, D. Friedmann, J. Scott, R. Amal, TiO2/porous adsorbents: recent advances and novel applications. J. Hazard. Mater. 341, 404–423 (2018)
W. Ma, Z. Lu, M. Zhang, Investigation of structural transformations in nanophase titanium dioxide by Raman spectroscopy. Appl. Phys. A 66, 621 (1998)
T. Aguilar, I. Carrillo-Berdugo, R. GómezVillarejo, J. Gallardo, P. Merino, J. Piñero, R. Alcántara, C. Fernández-Lorenzo, J. Navas, A solvothermal synthesis of TiO2 nanoparticles in a non-polar medium to prepare highly stable nanofluids with improved thermal properties. Nanomaterials 8(10), 816 (2018)
R. Alcántara, J. Navas, C. Fernández-Lorenzo, J. Martín, E. Guillén, J.A. Anta, Synthesis and Raman spectroscopy study of TiO2 nanoparticles. Phys. Status Solidi (C). 8(6), 1970–1973 (2011)
S. Challagulla, K. Tarafder, R. Ganesan, S. Roy, Structure sensitive photocatalytic reduction of nitroarenes over TiO2. Sci. Rep. 7, 8783 (2017)
N. Agoudjil, T. Benkacem, Synthesis of porous titanium dioxide membranes. Desalination 206(1–3), 531–537 (2007)
L. Velardi, L. Scrimieri, A. Serra, D. Manno, L. Calcagnile, Effect of temperature on the physical, optical and photocatalytic properties of TiO2 nanoparticle. SN Appl. Sci (2020)
Y. Geng, J. Zhang, J. Zhou, J. Lei, Study on adsorption of methylene blue by a novel composite material of TiO2 and alum sludge. RSC Adv. 8, 32799–32807 (2018)
A. Mohammadi, A. Karimi, Methylene blue removal using surface-modified TiO2 nanoparticles: a comparative study on adsorption and photocatalytic degradation. J. Water Environ. Nanotechnol. 2(2), 118–128 (2017)
Funding
Open access funding provided by Università del Salento within the CRUI-CARE Agreement.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Scrimieri, L., Velardi, L., Serra, A. et al. Enhanced adsorption capacity of porous titanium dioxide nanoparticles synthetized in alkaline sol. Appl. Phys. A 126, 926 (2020). https://doi.org/10.1007/s00339-020-04103-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00339-020-04103-2