Abstract
A356 Al alloy melt solidified partially while flowing down a bottom cooled tilted plate. Columnar dendrites were formed on the plate wall. Because of forced convection, the dendrites were sheared off into equiaxed/fragmented grains and washed away by producing semisolid slurry at plate exit. Plate vibration enabled necessary shear for generating slurry which got solidified in metal mold to produce semisolid-cast billets of desired microstructure. Semisolid-cast billets were also heat treated to improve surface quality. The present investigation illustrates effect of plate vibration on solidification and microstructural and mechanical properties of semisolid-cast and heat-treated billets produced using tilted plate. This study involves five different plate vibrations (0, 15, 30, 40, and 50 Hz). Plate vibration of 30 Hz gave the finest and globular microstructure with superior mechanical properties. Because, little lower plate vibration slowed down dendrite fragmentation and grain refinement owing to inadequate shearing causing increase in grain size and decrease in shape factor, primary α-phase fraction, and grain density. Whereas, little higher plate vibration caused coarsening (which opposes grain refinement) due to coalescence/agglomeration and Ostwald ripening also resulting the same. Such variation in grain size with plate vibration caused variations in mechanical properties because of Hall–Petch effect. The results obtained are along the expected lines and in very good agreement with the results available in the literature.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Form GW, Wallace JF (1960) Typical microstructure of cast metals. Trans AFS 68:145–156
Campbell J (1981) Solidification technology in the foundry and casthouse. Metals Soc 61–64
Motegi T, Ohno A (1987) Solidification processing. Institute of Metals 176–179
Flemings MC (1991) Behaviour of metal alloys in the semi-solid state. Metall Trans A 22:957–981
Kirkwood DH (1994) Semi-solid metal processing. Int Mater Rev 39:173–189
Fan Z (2002) Semisolid metal processing. Int Mater Rev 47:49–85
Fisher TP (1973) Effects of vibrational energy on the solidification of aluminium alloy. British Foundryman 66:71–84
Abd-El-Azim AN (1981) Effect of low frequency mechanical vibration on the structure of Al-Si eutectic alloys. Mater Sci Forum 7:118–120
Campbell J (1981) Effects of vibration during solidification. Int Mater Rev 2:71–106
Abramov VO, Abramov OV, Straumal BB, Gust W (1997) Hypereutectic Al–Si based alloys with a thixotropic microstructure produced by ultrasonic treatment. Mater Design 18:323–326
Eskin GI (2001) Broad prospects for commercial application of the ultrasonic (cavitation) melt treatment of light alloys. Ultrason Chem 8:319–325
Jian X, Xu H, Meek T, Han Q (2005) Effect of power ultrasound on solidification of aluminium A356 alloy. Mater Lett 59:190–193
Kocatepe K, Burdett CF (2000) Effect of low frequency vibration on macro and micro structures of LM6 alloys. J Mater Sci 35:3327–3335
Abu-Dheir N, Khraisheh M, Saito K, Male A (2005) Silicon morphology modification in the eutectic Al-Si alloy using mechanical mold vibration. Mater Sci Eng A 393:109–117
Kocatepe K (2007) Effect of low frequency vibration on porosity of LM25 and LM6 alloys. Mater Design 28:1767–1775
Gencalp S, Saklakoglu N (2010) Semisolid microstructure evolution during cooling slope casting under vibration of A380 aluminium alloy. Mater Manuf Process 25:943–947
Gencalp S, Saklakoglu N (2012) Effects of low-frequency mechanical vibration and casting temperatures on microstructure of semisolid AlSi8Cu3Fe alloy. Arab J Sci Eng 37:2255–2267
Jiang W, Fan Z, Liu D, Wu H (2013) Influence of gas flowrate on filling ability and internal quality of A356 aluminum alloy castings fabricated using the expendable pattern shell casting with vacuum and low pressure. Int J Adv Manuf Technol 67:2459–2468
Jiang W, Fan Z, Chen X, Wang B, Hebao W (2014) Combined effects of mechanical vibration and wall thickness on microstructure and mechanical properties of A356 aluminum alloy produced produced by expendable pattern shell casting. Mater Sci Eng A 619:228–237
Kund NK, Dutta P (2010) Numerical simulation of solidification of liquid aluminium alloy flowing on cooling slope. Trans Nonferrous Met Soc China 20:s898–s905
Kund NK, Dutta P (2012) Scaling analysis of solidification of liquid aluminium alloy flowing on cooling slope. Trans Indian Institute of Metals 65:587–594
Kund NK (2014) Influence of melt pouring temperature and plate inclination on solidification and microstructure of A356 aluminum alloy produced using oblique plate. Trans Nonferrous Met Soc China 24:3465–3476
Kund NK (2015) Influence of plate length and plate cooling rate on solidification and microstructure of A356 alloy produced by oblique plate. Trans Nonferrous Met Soc China 25:61–71
Kund NK, Dutta P (2015) Numerical study of solidification of A356 aluminum alloy flowing on an oblique plate with experimental validation. J Taiwan Inst Chem Ers 51:159–170
Kund NK, Dutta P (2016) Numerical study of influence of oblique plate length and cooling rate on solidification and macrosegregation of A356 aluminum alloy melt with experimental comparison. J Alloys Compd 678:343–354
Doherty RD (2003) Comments on mechanical deformation of dendrites by fluid flow during the solidification of undercooled melts. Scripta Mater 49:1219–1222
Genda G, Yuyon C, Geing A (1987) Mechanism of coarsening of dendrite during solidification. Proceedings Inglaterra 416–419
Wan G, Sahm PR (1990) Ostwald ripening in the isothermal rheocasting process. Acta Metall Mater 38:967–972
Abdul-Karem W, Green N, Al-Raheem KF (2012) Vibration-assisted filling capability in thin wall investment casting. Int J Adv Manuf Technol 61:873–887
Abdul-Karem W, Green N, Al-Raheem KF, Hasan AHA (2013) Effect of vibration after filling on mechanical reliability in the thin wall investment casting with fillability filling regime-part 1. Int J Adv Manuf Technol 67:2075–2082
Guo HM, Zhang AS, Yang XJ, Yan MM, Ding Y (2014) Microstructure formation and mechanical properties of AZ31 magnesium alloy solidified with a novel mechanical vibration technique. Metall Mater Trans A 45:438–446
Zhang X, Kang J, Wang S, Ma J, Huang T (2015) The effect of ultrasonic processing on solidification microstructure and heat transfer in stainless steel melt. Ultrason Sonochem 27:307–315
Ruirun C, Deshuang Z, Jingjie G, Tengfei M, Hongsheng D, Yanqing S, Hengzhi F (2016) A novel method for grain refinement and microstructure modification in TiAl alloy by ultrasonic vibration. Mater Sci Eng A 653:23–26
Jiang W, Chen X, Wang B, Fan Z, Wu H (2016) Effects of vibration frequency on microstructure, mechanical properties, and fracture behaviour of A356 aluminum alloy obtained by expendable pattern shell casting. Int J Adv Manuf Technol 83:167–175
Funding
The financial support received from Ministry of Mines, TIFAC, and DST is gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kund, N.K. Effect of tilted plate vibration on solidification and microstructural and mechanical properties of semisolid cast and heat-treated A356 Al alloy. Int J Adv Manuf Technol 97, 1617–1626 (2018). https://doi.org/10.1007/s00170-018-2063-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-018-2063-1