The oxidation behavior in air at 1000–1250°C of four Ni-Cr-W alloys containing sufficient chromium content (∼22 at. % Cr) for protective Cr2O3 formation in a binary Ni-Cr alloy is reported. Generally for alloys high in W (10 and 16 at.% W), the rejection of tungsten into the alloy beneath the scale introduced a steep Cr concentration gradient and slower Cr diffusion such that continuous precipitation of Cr2O3 internal oxides prevented the formation of a Cr2O3 protective scale. The alloy most dilute in W (1.6 at. % W) formed a protective scale at short times with little outer NiO scale, but scale fractures led to internal oxidation and rapid nonprotective kinetics. After an initially rapid oxidation increment to form NiO, the 3 at.% Walloy formed a protective Cr2O3 scale with about the same steady-state parabolic kinetics as a binary Ni-30Cr alloy. The effect of ternary Wadditions on the development of Cr2O3 scales on Ni-Cr-W alloys is considered as a ternary analog to Wagner's description of the oxidation of Cu-Pt or Cu-Pd alloys.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
G. B. Belton and R. L. McCarron,J. Phys. Chem. 68, 1852 (1964).
C. Wagner,Corros. Sci. 8, 889 (1968).
W. W. Smeltzer and D. P. Whittle,J. Electrochem. Soc. 125, 1116 (1978).
O. T. Ziebold and R. E. Ogilvie,Anal. Chem. 35, 621 (1963).
S. Mrowec, “Attack of High Temperature Alloys in Sulfiding Gases,” in Properties of High Temperature Alloys, Z. A. Foroulis and F. A. Pettit, eds. (Electrochem. Soc., Princeton, 1976).
G. C. Wood and T. Hodgkiess,J. Electrochem. Soc. 113, 319 (1966).
C. S. Giggins and F. S. Pettit,Trans. Met. Soc. A.I.M.E. 245, 2495 (1969).
G. C. Wood and T. Hodgkiess,Nature 211, 1358 (1966).
G. H. Meier and R. A. Rapp,Z. Phys. Chem. 54, 168 (1971).
C. E. Birchenall, “Diffusion in Oxides,” inMass Transport in Oxides, NBS Spec. Publ. 296, J. B. Wachtman and A. D. Franklin, eds. (1967), p. 119.
N. N. Khoi, W. W. Smeltzer, and J. D. Embury,J. Electrochem. Soc. 122, 1495 (1975).
C. Wagner,J. Electrochem. Soc. 103, 571 (1956).
S. Espevik, R. A. Rapp, P. L. Daniel, and J. P. Hirth,Oxid. Met. to be published.
L. C. Walters and R. E. Grace,J. Appl. Phys. 8, 2331 (1968).
W. C. Hagel and A. U. Seybolt,J. Electrochem. Soc. 108, 1146 (1961).
D. Caplan and G. I. Sproule,Oxid. Met. 9, 459 (1975).
C. E. Birchenall, unpublished research, private communication.
K. Momma, H. Suto, and H. Oikawa,Nippon Kinzoku Gakkaishi 28, 197 (1964).
Author information
Authors and Affiliations
Additional information
Former address: Scandinavian Institute of Dental Materials, Oslo, Norway (deceased).
Rights and permissions
About this article
Cite this article
Espevik, S., Rapp, R.A., Daniel, P.L. et al. Oxidation of Ni-Cr-W ternary alloys. Oxid Met 14, 85–108 (1980). https://doi.org/10.1007/BF00603987
Received:
Issue Date:
DOI: https://doi.org/10.1007/BF00603987