Preparation of Nd3+: Gd3 Ga5 O12 polycrystalline material by sol-gel method was preparated in this paper. The structure and the pattern of the sample were analyzed by thermogravimetric analysis and differential thermal analysis (TG-DTA), Infrared spectrum, XRD, TEM and electron spectrum, which indicated that the powder with good characteristics of 70–100 nm can be obtained by sintering at 1 000°C. It was shown that the chemical composition of the sample was agreed with experimental requirements by electron spectrum analysis.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
B. Keszei and J. Paitz,Journal of crystal Growth,226 (2001), 95.
Jiang Ben-xue and Zhao zhi-wei,Journal of synthetic crystals,33(2004), 581.
T. Yanagitani, H. Yagi, and I chikawa M,Manufacture method of fine powder of YAG, Japan Patent, 1998, 10-101333.
T. Yanagitani, H. Yagi, and I chikawa M,Manufacture method of fine powder of YAG, Japan Patent, 1998, 10-101411.
J. Lu, J. Song, and M. Prabhu,J. Appl. Phys.,39(2002), 1048.
J. Kong, D. Y. Tang, and D. Y. Shen,Proc. SPIE,4914 (2002), 69.
J. Lu, J. F. Bission, and K. Takaichi,Appl. Phys. Lett.,83 (2003), 1101.
J. Lu, K. Takaichi, and T. Uematsu,Appl. Phys. Lett.,81 (2002), 4324.