Nano-sized silicon carbide (SiC) powder was prepared by thermal plasma process using silicon tetrachloride (SiCl4) and methane (CH4). The synthesized powder was characterized by X-ray diffraction pattern, scanning electron microscopy, transmission electron microscopy, FT-IR spectroscopy and particle size analyzer. The powder was dominated by β-SiC including some of α-SiC and free carbon species. The quality of the powder was varied with process conditions such as the molar ratio of H/Si and C/Si, and collecting positions. It was known that the conversion to SiC was mainly affected by the addition of hydrogen gas because it promoted the decomposition and reduction of SiCL. CH4 was easily decomposed to carbon species for the formation of SiC as well as removal of impure oxygen, but excessive carbon suppressed the formation of crystalline SiC and resulted in the solid carbon contamination. The optimum ratio of H/Si was approx. 26 and that of C/Si was 1.1. For collecting positions, the powder collected at the vessel and filter was preferable to that at the reaction tube. The average size of the powder synthesized was estimated to be below 100 nm and uniform in distribution.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Bolous, M. I., Fauchais, P. and Pfender E., “Thermal Plasmas-Fundamental and Applications”, Plenum Press, New York (1994).
Chemsage program, Version 3.2, GTT-Technologies, Germany (1996).
Chen, L., Goto, T. and Hirai, T., “Preparation of Silicon Carbide Powders by Chemical Vapor Deposition of the SiH4-CH4-H2 System”,J. Mater. Sci.,24, 3824 (1989).
Chen, C. Y., Lin, C. I. and Chen, S. H., “Kinetics of Synthesis of Silicon Carbide by Carbothermic Reduction of Silicon Dioxide”,British Ceramic Transactions,99(2), 57 (2000).
Guo, J. Y., Gitzhofer, F. and Boulous, M. I., “Effects of Process Parameters on Ultrafrne SiC Synthesis Using Induction Plasmas”,Plasma Chemistry and Plasma Processing,17(2), 219 (1997).
Hollabaugh, C. M., Hull, D. E., Newkirk, L. R. and Petrovic, J. I., “R.F.Plasma System for the Production of Ultrafine, Ultrapure Silicon Carbide Powder”,J. Mater. Sci.,18, 3190 (1983).
Kameyama, T., Sakanaka, K., Motoe, A., Tsunoda, T., Nakanaga, T., Wakayama, N. I., Takeo, H. and Fukuda, K., “Highly Efficient and Stable Radio-frequency Thermal Plasma System for the Production of Ultrafine and Ultrapure β-SiC Powder”,J. Mater. Sci.,25, 1058 (1990).
Koc, R., Glatzmaier, G. and Sibold, J., “β-SiC Production by Reacting Silica Gel with Hydrocarbon Gas”,J. Mater. Sci.,36, 995 (2001).
Oh, S.-M. and Park, D.-W., “Preparation of Ultrafine Alumina Powders by D.C. Plasma Jet”,Korean J. Chem. Eng.,17, 299 (2000).
Oh., S.-M. and Park, D.-W., “Production of Ultrafrne Titanium Dioxide by DC Plasma Jet”,Thin Solid Films,386, 233 (2001).
Park, H.-S. and Rhee, S.-W., “Thermal Plasma Synthesis of Silicon Carbide Powders”,HWAHAKKONGHAK,28, 451 (1990).
Park, H.-S., Seon, H.-S., Rhee, S.-W., Lee, K.-H. and Baik, S.-G., “Thermal Plasma Chemical Vapor Deposition for SiC Powders from SiCH3Cl3-H2”,J. Mater. Sci.,26, 5957 (1991).
Pfender, E., “Thermal Plasma Technology; Where do we Stand and Where are we going?”,Plasma Chemistry and Plasma Processing,19(1), 1 (1999).
Pickles, C. A., Toguri, J. M. and Simpson, C. J., “Plasma Arc Production of Silicon Carbide Crystals”,British Ceramic Transactions,94(3), 89 (1995).
Zhu, C. W., Zhao, G. Y., Revankar, V. and Hlavacek, V., “Synthesis of Ultrafrne SiC Powders in a d.c. Plasma Reaction”,J. Mater. Sci.,28, 659 (1993).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Oh, SM., Cappelli, M. & Park, DW. Preparation of nano-sized silicon carbide powder using thermal plasma. Korean J. Chem. Eng. 19, 903–907 (2002). https://doi.org/10.1007/BF02706987
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF02706987