Abstract
The formation of HfB2–SiC (10–65 vol % SiC) ultra-high-temperature ceramics by hot pressing of HfB2–(SiO2–C) composite powder synthesized by the sol–gel method was studied. By the example of HfB2–30 vol % SiC ceramic, it was shown that the synthesis of nanocrystalline silicon carbide is completed at temperatures of as low as ≥1700°C (crystallite size 35–39 nm). The production of the composite materials with various contents of fine silicon carbide at 1800°C demonstrated that the samples of the composition HfB2–SiC (20–30 vol % SiC) are characterized by the formation of SiC crystallites of the minimum sizes (36–38 nm), by the highest density (89%), and by higher oxidation resistance during heating in an air flow to 1400°C.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
E. P. Simonenko, D. V. Sevast’yanov, N. P. Simonenko, et al., Russ. J. Inorg. Chem. 58, 1669 (2013). doi 10.1134/S0036023613140039
L. Silvestroni, H.-J. Kleebe, W. G. Fahrenholtz, and J. Watts, Sci. Rep. 7, Art. no. 40730 (2017). doi 10.1038/srep40730
E. P. Simonenko, A. N. Gordeev, N. P. Simonenko, et al., Russ. J. Inorg. Chem. 61, 1203 (2016). doi 10.1134/S003602361610017X
M. Mallik, A. J. Kailath, K. K. Ray, et al., J. Eur. Ceram. Soc. 37, 559 (2017). doi 10.1016/j.jeurceramsoc.2016.09.024
A. Nisar, S. Ariharan, T. Venkateswaran, et al., Carbon 111, 269 (2017). doi 10.1016/j.carbon.2016.10.002
V. G. Sevast’yanov, E. P. Simonenko, A. N. Gordeev, et al., Russ. J. Inorg. Chem. 58, 1269 (2013). doi 10.1134/S003602361311017X
M. Asl Shahedi, F. Golmohammadi, M. Ghassemi Kakroudi, and M. Shokouhimehr, Ceram. Int. 42, 4498 (2016). doi 10.1016/j.ceramint.2015.11.139
M. Asl Shahedi, M. Ghassemi Kakroudi, I. Farahbakhsh, et al., Ceram. Int. 42, 18612 (2016). doi 10.1016/j.ceramint.2016.08.20
V. G. Sevastyanov, E. P. Simonenko, A. N. Gordeev, et al., Russ. J. Inorg. Chem. 59, 1298 (2014). doi 10.1134/S0036023614110217
V. G. Sevastyanov, E. P. Simonenko, A. N. Gordeev, et al., Russ. J. Inorg. Chem. 59, 1361 (2014). doi 10.1134/S0036023614120250
L. Wang, D. Kong, G. Fang, and J. Liang, Int. J. Appl. Ceram. Technol. 14, 31 (2017). doi 10.1111/ijac.12613
V. G. Sevastyanov, E. P. Simonenko, A. N. Gordeev, et al., Russ. J. Inorg. Chem. 60, 1360 (2015). doi 10.1134/S0036023615110133
M. Patel, V. Singh, and V. V. B. Prasad, Oxid. Met. 86, 339 (2016).
D. V. Grashchenkov, O. Yu. Sorokin, Yu. E. Lebedeva, and M. L. Vaganova, Russ. J. Appl. Chem. 88, 386 (2015).
Yu. B. Lyamin, V. Z. Poilov, E. N. Pryamilova, et al., Russ. J. Inorg. Chem. 61, 149 (2016). doi 10.1134/S0036023616020133
W. Tan, M. Adducci, C. Petorak, et al., J. Eur. Ceram. Soc. 36, 3833 (2016). doi 10.1016/j.jeurceramsoc.2016.04.013
D. L. Poerschke, M. D. Novak, N. Abdul-Jabbar, et al., J. Eur. Ceram. Soc. 36, 3697 (2016). doi 10.1016/j.jeurceramsoc.2016.05.048
D. V. Kolovertnov and I. B. Ban’kovskaya, Glass Phys. Chem. 41, 324 (2015).
B. Du, N. Li, B. Ke, et al., Ceram. Int. 42, 14292 (2016). doi 10.1016/j.ceramint.2016.06.041
Y. An, X. Xu, and K. Gui, Ceram. Int. 42, 14066 (2016). doi 10.1016/j.ceramint.2016.06.014
X. Jin, L. Dong, Q. Li, et al., Ceram. Int. 42, 13309 (2016). doi 10.1016/j.ceramint.2016.05.040
B. Zhang, X. Zhang, C. Hong, et al., ACS Appl. Mater. Interfaces 8, 11675 (2016). doi 10.1021/acsami.6b00822
H. Jin, S. Meng, X. Zhang, et al., J. Am. Ceram. Soc. 99, 2474 (2016). doi 10.1111/jace.14232
L. A. Chevykalova, I. Yu. Kelina, I. L. Mikhal’chik, et al., Refract. Ind. Ceram. 54, 455 (2014).
X. Jin, L. Dong, H. Xu, et al., Ceram. Int. 42, 9051 (2016). doi 10.1016/j.ceramint.2016.02.164
H. Jin, S. Meng, X. Zhang, et al., J. Eur. Ceram. Soc. 36, 1855 (2016). doi 10.1016/j.jeurceramsoc.2016.02.040
Yoon D.-H. Muksin and K. Raju, Ceram. Int. 42, 7300 (2016). doi 10.1016/j.ceramint.2016.01.126
Y. Yuan, J.-X. Liu, and G.-J. Zhang, Ceram. Int. 42, 7861 (2016). doi 10.1016/j.ceramint.2016.01.067
Z. Kovacova, L. Baca, E. Neubauer, and M. Kitzmantel, J. Eur. Ceram. Soc. 36, 3041 (2016). doi 10.1016/j.jeurceramsoc.2015.12.028
H. Jin, S. Meng, X. Zhang, et al., Ceram. Int. 42, 6480 (2016). doi 10.1016/j.ceramint.2015.12.132
M. Asl Shahedi, A. Sabahi Namini, and M. Ghassemi Kakroudi, Ceram. Int. 42, 5375 (2016). doi 10.1016/j.ceramint.2015.12.072
X. Zhang, Z. Chen, X. Xiong, et al., Ceram. Int. 42, 2798 (2016). doi 10.1016/j.ceramint.2015.11.012
Y. Yan, Z. Huang, S. Dong, and D. Jiang, J. Am. Ceram. Soc. 89, 3589 (2006). doi 10.1111/j.1551-2916.2006.01270.x
S. Guo, J. Yang, H. Tanaka, and Y. Kagawa, Compos. Sci. Technol. 68, 3033 (2008).
H. Zhang, Y. Yan, Z. Huang, et al., Key Eng. Mater. 434–435, 193 (2010). doi 10.4028/www.scientific.net/KEM.434-435.193
M. Ikegami, S. Guo, and Y. Kagawa, Ceram. Int. 38, 769 (2012).
V. Zamora, A. L. Ortiz, F. Guiberteau, and M. Nygren, J. Eur. Ceram. Soc. 32, 2529 (2012).
W. Han, S. Zhou, and J. Zhang, Ceram. Int. 40, 16665 (2014).
M. Mashhadi, H. Khaksari, and S. Safi, J. Mater. Res. Technol. 4, 416 (2015).
M. Jaberi Zamharir, M. Shahedi Asl, M. Ghassemi Kakroudi, et al., Ceram. Int. 41, 9628 (2015).
E. P. Simonenko, N. P. Simonenko, G. P. Kopitsa, et al., Russ. J. Inorg. Chem. 61, 1347 (2016). doi 10.1134/S0036023616110206
V. G. Sevastyanov, E. P. Simonenko, N. P. Simonenko, et al., Kompoz. Nanostrukt. 6 (4), 198 (2014).
E. P. Simonenko, N. P. Simonenko, A. V. Derbenev, et al., Russ. J. Inorg. Chem. 58, 1143 (2013). doi 10.1134/S0036023613100215
E. P. Simonenko, N. P. Simonenko, V. G. Sevastyanov, and N. T. Kuznetsov, Russ. J. Inorg. Chem. 61, 1483 (2016). doi 10.1134/S0036023616120172
E. P. Simonenko, N. P. Simonenko, D. V. Sevastyanov, et al., Russ. J. Inorg. Chem. 61, 1649 (2016). doi 10.1134/S0036023616130039
H. Zhang, F. Fu, Y. Cao, et al., Interceram. 62, 282 (2013).
T. Wang, Y. Zhang, J. Li, et al., J. Nanosci. Nanotechnol. 15, 7402 (2015). doi 10.1166/jnn.2015.10583
Y. Cao, H. Zhang, F. Li, et al., Ceram. Int. 41, 7823 (2015). doi 10.1016/j.ceramint.2015.02.117
Y. Zhang, Y. Zhang, R.-X. Li, et al., J. Taiwan Inst. Chem. Eng. 46, 200 (2015). doi 10.1016/j.jtice.2014.09.022
B. Zhao, Y. Zhang, J. Li, et al., J. Solid State Chem. 207, 1 (2013). doi 10.1016/j.jssc.2013.08.028
Y. Yan, H. Zhang, Z. Huang, et al., J. Am. Ceram. Soc. 91, 1372 (2008). doi 10.1111/j.1551-2916.2008.02296.x
N. Patra, D. D. Jayaseelan, and W. E. Lee, Adv. Appl. Ceram. 115, 36 (2016).
X. P. Che, S. Z. Zhu, L. J. Yang, and Q. Xu, Adv. Mater. Res. 105–106, 213 (2010).
X. Deng, S. Du, H. Zhang, et al., Ceram. Int. 41, 14419 (2015).
S. Chakraborty, D. Debnath, A. R. Mallick, et al., Int. J. Refract. Met. Hard Mater. 52, 176 (2015).
D. Debnath, S. Chakraborty, A. R. Mallick, et al., Adv. Appl. Ceram. 114, 45 (2015).
M. Jalaly, M. Tamizifar, M. S. Bafghi, and F. J. Gotor, J. Alloys Compd. 581, 782 (2013).
M. Jalaly, M. S.-S. Bafghi, M. Tamizifar, and F. J. Gotor, Int. J. Appl. Ceram. Technol. 12, 551 (2015).
W.-W. Wu, G.-J. Zhang, Y.-M. Kan, and P.-L. Wang, Mater. Lett. 63, 1422 (2009).
H.-C. Oh, S.-H. Lee, and S.-C. Choi, Int. J. Refract. Met. Hard Mater. 42, 132 (2014).
X. Deng, S. Du, H. Zhang, et al., Ceram. Int. 41, 14419 (2015).
N. T. Kuznetsov, V. G. Sevast’janov, E.P. Simonenko, et al., Patent RU no. 2556599, July 10, 2015.
E. P. Simonenko, A. V. Derbenev, N. P. Simonenko, et al., Russ. J. Inorg. Chem. 62, 863 (2017). doi 10.1134/S0036023617070221
V. G. Sevastyanov, Y. S. Ezhov, E. P. Simonenko, and N. T. Kuznetsov, Mater. Sci. Forum 457–460, 59 (2004). doi 10.4028/www.scientific.net/MSF.457-460.59
R. G. Pavelko, V. G. Sevast’yanov, Yu. S. Ezhov, and N. T. Kuznetsov, Inorg. Mater. 43, 700 (2007). doi 10.1134/S0020168507070059
W. Wong-Ng, H. F. McMurdie, B. Paretzkin, et al., Powder Diffr. 2, 257 (1987).
T. Kawamura, Mineral. J. 4, 333 (1965).
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © E.P. Simonenko, N.P. Simonenko, E.K. Papynov, E.A. Gridasova, V.G. Sevastyanov, N.T. Kuznetsov, 2018, published in Zhurnal Neorganicheskoi Khimii, 2018, Vol. 63, No. 1, pp. 3–18.
Rights and permissions
About this article
Cite this article
Simonenko, E.P., Simonenko, N.P., Papynov, E.K. et al. Production of HfB2–SiC (10–65 vol % SiC) Ultra-High-Temperature Ceramics by Hot Pressing of HfB2–(SiO2–C) Composite Powder Synthesized by the Sol–Gel Method. Russ. J. Inorg. Chem. 63, 1–15 (2018). https://doi.org/10.1134/S0036023618010187
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S0036023618010187