Abstract
Collagen integrity should be considered on using a sterilizing agent for fish skin grafts. This study defined the optimal concentration of silver nanoparticles (Ag NPs) for sterilization of fish skin grafts without disrupting collagen content based on microbiological and histological evaluation. Strips of tilapia skin (n = 5) were randomly allocated to be immersed in Ag NPs solution at different concentrations of 25, 50, 100, and 250 µg/mL, respectively, for 5 min. The treated skin strips underwent bacteriological and histological evaluation. Yeast and fungi were more sensitive to Ag NPs than bacteria. On increasing the nanoparticles concentration, the total counts of aerobic bacteria decrease giving 933.3 ± 28.67, 601 ± 27.66, 288 ± 16.8, 15 ± 4.08 (CFU/cm2 ± S.D) at 25, 50, 100, and 250 µg/mL, respectively, comparing with untreated sample (1453.3 ± 57.92). Yeasts and filamentous fungi also exhibited a similar response, achieving a complete inhibition at 100 and 250 µg/mL. Bacillus cereus and Escherichia coli were the dominant aerobic bacteria, Candida albicans and Rhodotorula glutinis were the dominant aerobic yeasts, whereas Aspergillus niger, Aspergillus fumigatus, and Rhizopus stolonifer were the dominant aerobic fungi. The collagen fibers were loose with a wavey pattern at 25 µg/mL, wavey and slightly disorganized at 50 µg/mL, highly disorganized at 100 µg/mL, and compactly arranged and slightly loose at 250 µg/mL. Ag NPs at a concentration of 250 µg/mL could be considered a reliable and feasible method for the sterilization of fish skin grafts before application on human skin with an effective antimicrobial effect and less disrupting impact on collagen content.
Similar content being viewed by others
Introduction
Tilapia skin is a well-known biological material used as an occlusive dressing for burn healing. It is also a cheap and important source of type I collagen. Additionally, it was confirmed that it contains non-infectious microbiota1, and has a morphological structure homologous to the human skin2. Tilapia skin is also a highly available product, safe, innovative, and easy to apply materials. Thus, it could be suggested as a potential xenograft for treating burns and regenerative medicine3.
Due to their numerous applications, silver nanoparticles (Ag NPs) are one of the largest and most commonly synthesized nanomaterials, they are unique antimicrobial agents and are used in various commercial medications4. Ag NPs have got a lot of attention as a specialized tool for managing a variety of bacterial, fungal, and viral illnesses, especially with the rise of antibiotic-resistant microorganisms5. The nanoparticles' tiny size allows for improved contact with the bacterial cell as well as easier penetration causing the cell to generate a high amount of reactive oxygen species (ROS) for defense6,7. ROS is a molecule that causes cell death and can kill cells in one of two ways: apoptosis or necrosis8,9,10. Nano-silver can interact with cell components such as proteins, lipids, enzymes, and DNA once it has been pierced by bacteria. This interaction causes significant damage to bacterial cells, including malfunction and eventual death, especially with bacterial cell ribosomes that produce ribosome denaturation, and inhibits protein synthesis11. Silver nanoparticles have antibacterial effects against common fish and animal pathogenic bacteria like Aeromonas hydrophila, Aeromonas salmonoid, Aeromonas bestiarum, Klebsiella pneumoniae, Pseudomonas flourescens, Vibrio harveyi, Micrococcus luteus, Proteus spp., Staphylococcus aureus, and Flavobacterium spp.12,13,14,15,16,17,18.
It is urgent to sterilize fish skin grafts before their application to human skin. However, collagen integrity should be considered in the sterilization of fish skin grafts along with the efficient antimicrobial effect of the sterilizing agent. In a previous study, Ibrahim et al.3, investigated that the silver nanoparticles (Ag NPs) explored advantage over both; chlorhexidine gluconate 4% and povidone iodine 10% in sterilizing of fish skin based on the microbial count and the collagen fiber integrity. However, this study had a limited use of one concentration of Ag NPs (25 µg/mL).
Therefore, this study represents a continuation of the previous work, aimed to evaluate different concentrations of the Ag NPs to determine the idealistic concentration for sterilizing fish skin grafts without disrupting their collagen content based on microbiological and histological evaluations.
Results
Microbiological analysis
The inhibiting effect of different concentrations of Ag NPs (25, 50, 100, and 250 µg/mL) on the microbial growth of aerobic bacteria, yeasts, and filamentous fungi are shown in Fig. 1A–C. It was clear that yeast and fungi were more sensitive to Ag NPs than bacteria. For bacteria, on increasing the nanoparticles concentration, the total counts of aerobic bacteria decrease giving 933.3 ± 28.67, 601 ± 27.66, 288 ± 16.8, 15 ± 4.08 (CFU/cm2 ± S.D) at 25, 50, 100, and 250 µg/mL, respectively, comparing with the untreated sample (1453.3 ± 57.92) (Fig. 1A). Yeasts and filamentous fungi also exhibited a similar response, achieving a complete inhibition at 100 and 250 µg/mL, while giving 434.3 ± 24.3 and 218 ± 17.9 for aerobic yeasts and 142.7 ± 7.13 and 61.3 ± 8.6 for aerobic fungi at 25 and 50 µg/mL, respectively, comparing with the untreated sample (816 ± 47.3 and 194 ± 4.3) for yeasts and fungi, respectively (Fig. 1B, C). On examining the microbial species isolated from the fish skin; Bacillus cereus and Escherichia coli were the dominant aerobic bacteria, Candida albicans and Rhodotorula glutinis were the dominant aerobic yeasts, while Aspergillus niger, Aspergillus fumigatus, and Rhizopus stolonifer were the dominant aerobic fungi as shown in Table 1.
Histological analysis
The histological analysis of the untreated fish skin in the control group revealed that the dermis contained compactly arranged collagen fibers in a parallel pattern, covered with epidermis with a characteristic distribution of melanocytes (Fig. 2A). The collagen fibers were loose with a wavey pattern at 25 µg/mL (Fig. 2B), wavey and slightly disorganized at 50 µg/mL (Fig. 2C), highly disorganized at 100 µg/mL (P < 0.0001) (Fig. 2D), and compactly arranged with slight looseness at 250 µg/mL (Fig. 2E).
Histochemical analysis
This study also examined the collagen fiber organization in the Ag NPs-treated and untreated groups by staining the skin samples with Crossmon’s trichrome. Collagen intensity was measured in the fish skin using ImageJ (version 1.48v). There was a moderate change in collagen intensity and organization at 25 µg/mL (Fig. 2G and L) compared with the control group (Fig. 2F and K). A mild change in the disposition pattern of collagen fibers and collagen intensity was recorded at 50 µg/mL (Fig. 2H and M). However, there was a significant (p < 0.0001) reduction in the intensity of the collagen fibers at 100 µg/mL (Figs. 2I and N and 3). The fish skin showed well-organized collagen fibers and a high percentage of collagen intensity at 250 µg/mL, compared to the control group (Figs. 2J and O and 4).
Discussion
Tilapia skin has been used as an occlusive dressing for burn and wound healing because of its high content of collagen and homogeneity to human skin1,2,3. Tilapia skin grafts cannot be applied to the skin before being sterilized. The sterilization process of the Tilapia skin grafts should be a dual action of an efficient antimicrobial effect and a preserving effect on collagen content. Here, this study explored that immersion for 5 min in 250 µg/mL Ag NPs solution could be an optimal method for the sterilization of Tilapia skin grafts achieving efficient antimicrobial, as well as collagen preserving impacts. Moreover, this method is time-saving and economical, which makes it reliable, feasible, and reproducible in clinical applications.
Infections caused by bacteria, fungi, and viruses are serious issues in the aquaculture sector19. Antibiotics are the commercially accessible approach for treating infections; nevertheless, overuse over time leads to the evolution of resistant strains, rendering antibiotic treatments ineffective and failed the treatment20,21.
Many researchers have utilized silver nanoparticles for controlling microbial pathogens such as controlling various strains of the pathogenic bacteria Escherichia coli22,23 and, inhibiting the pathogenic bacteria; Bacillus cereus, Staphylococcus aureus, Escherichia coli, and Salmonella typhimurium effectively using silver nanoparticles24. Also, it was effective against pathogenic Candida albicans, C. glabrata, C. geochares, and C. saitoana. Soliman et al.25, recorded the high antimicrobial activity of silver nanoparticles against Candida sp., Streptococcus sp., Bacillus sp., Staphylococcus sp., Shigella sp., and E. coli. Mathivanan et al.26, utilized silver nanoparticles to control P. fluorescens, Proteus mirabilis, E. coli, B. cereus and S. aureus. Similar findings were found in this study, especially at the higher concentration (250 µg/mL) of Ag NPs exhibiting efficient antimicrobial impact.
Silver nanoparticles disrupt the respiratory chain of the targeted bacterium. During this suppression of the respiratory chain via respiratory enzymes, silver ions may interact with the thiol enzyme group, resulting in ROS27,28. ROS, as a significant factor impacting oxidative stress, can damage bacterial cell macromolecules such as protein synthesis and alteration, enzyme inhibition, lipid synthesis, and bacterial cell DNA and RNA oxidation and damage. ROS can induce cell death at high levels, but it can also cause serious damage or mutation to the DNA of bacterial cells at low levels29.
Palmer et al.30, indicated that all sterilization techniques can significantly affect both the physical properties and biological activity of collagen. Therefore, the selection of a safe sterilization method is a challenge.
Ethylene oxide (EtO) has been used to sterilize collagen-based wound dressings. However, EtO has some limitations; it may produce toxic residues, acts as a carcinogenic agent and is not suitable for materials stored in fluidic medium31. Moreover, EtO irreversibly alkylates amino acid residues, possibly affecting many properties of collagen such as the number of free amine groups and the degradation rate32. Huang et al.33, reported that skin sterilization with peracetic acid causes looseness in the pattern of collagen fibrils. Alves et al.2, recorded changes in collagen composition and organization in skin samples treated with chlorhexidine and sequential glycerol concentrations.
In this study, silver nanoparticles represent identical preservative of collagen integrity, especially at 250 µg/mL concentration. Concerning the collagen deposition, it was noted that it was higher at 250 µg/mL, compared to other concentrations. Cameron et al.34, and Gong et al.35, found that increasing the concentration of the Ag NPs as a percentage was associated with a higher deposition of collagen and promoted macrophage migration for discriminatory remodeling.
Many previous investigations indicated that the usage of silver as widespread bandages can reduce inflammation and scarring, potentially stop bacterial outgrowth and enhance the healthy process, inducing remodeling in the wound area36. This process occurs through the direct expression of certain growth factors, which leads to vasculogenesis, re-epithelialization, and deposition of collagen fibers. Moreover, silver nanoparticles can elucidate the transformation of the fibroblast to myofibroblast, which is responsible for the contraction of the wound and speed up the course of healing, and similarly can stimulate keratinocytes to proliferate in the injured area37,38.
Conclusions
Ag NPs solution at the concentration of 250 µg/mL could be considered a reliable and feasible method for the sterilization of fish skin grafts by immersion for 5 min before application on human skin with an effective antimicrobial effect and a less disrupting impact on collagen content.
Materials and methods
Ethical approval
The National Ethical Committee of The Faculty of Veterinary Medicine, Assiut University, Assiut, Egypt, has approved all the procedures in this study under the Egyptian bylaws and OIE animal welfare standards for animal care and use in research and education.
Synthesis of silver nanoparticles (Ag NPs)
In a typical synthesis process, a solution (A): dissolve 1 wt% of starch (Purity 98%, algomhoria, Egypt) in distilled water with the assistance of heat until obtaining a clear solution. A solution (B): dissolve 8 wt% of silver nitrate (Purity 99%, Sigma-Aldrich, USA) in distilled water in a dark container. The solution (A) was then mixed with the solution (B) in a ratio of 10:1. The mixture was transferred to a sterilized autoclave at 80 °C for 5 min. After cooling down to room temperature, the resultant solution was stored in the refrigerator for further usage.
Different silver nanoparticles concentrations specifically 25, 50, 100, and 250 µg/mL were prepared, where the concentration was adjusted using the equation:
where C1, C2, V2, and V2 refer to the initial and final concentrations and volumes, respectively.
Tilapia skin collection
Tilapia skins were collected from fresh Nile tilapia (Oreochromis niloticus) (weigh: 520 ± 40 gm; standard length: 17 ± 3 cm), obtained from tanks of The Aquatic Medicine Unit, Faculty of Veterinary Medicine, Assiut University, Assiut, Egypt. Fish were euthanized physically by decapitation. Fish skins were dissected from the underlying tissues after the removal of fish scales and divided into 5 × 3- cm strips in sterile normal saline.
Sterilization procedure
Strips of fish skin (n = 5) were randomly allocated to be immersed in silver nanoparticles (Ag NPs) solution at different concentrations of 25, 50, 100, and 250 µg/mL for 5 minutes (min) each. The Ag NPs-treated skin strips underwent bacteriological and histological evaluation following each treatment.
Microbiological evaluation of Ag NPs-treated fish skin
The dilution plate method was used for counting the microbial cells attached to the fish skin following Downes et al.39, Using a sterilized swab needle, fish skin (3 × 3 cm2) was swabbed before (control) and after each treatment and suspended in 10 mL sterilized saline solution and mixed using a vortex (VELP Scientifica, UK) for 2 min. Different types of media were used for microbial counting and identification. Nutrient agar and MacConkey agar media were used for counting the total aerobic bacteria40, yeast malt extract medium used for yeast counting41, and potato dextrose agar medium for filamentous fungi42. One milliliter of the solution was transferred into sterilized Petri dishes (three replicates for each) and a sterilized isolation medium of 45 °C was poured into the dish. The plates were left for solidification in sterile laminar flow. Plates were incubated for 24 h at 35 ± 1 °C for bacteria, 3 days at 28 ± 1 °C for yeasts, and 7 days at 28 ± 1 °C for filamentous fungi. The number of developed colonies was calculated as CFU/Cm2. Developed colonies with morphological character differences, such as colony color, size, pigmentation, and edge, were sub-cultured and purified using the same media. Bacterial isolates were identified using the biochemical tests as described by Bergey’s Manual of Systematic Bacteriology43. Yeast isolates were identified according to the phenotypic characteristics including shape, color, surface, margin, budding, the formation of pseudohyphae, mycelium, arthroconidia, ballistoconidia, chlamydospore, endospore, germ tube, glucose fermentation, and carbon source utilization41.
Histological evaluation of Ag NPs-treated fish skin
Specimens (0.5 × 0.5 cm) were collected from the Ag NPs-treated and untreated (control) fish skins and fixed in Bouin’s solution for 22 h. After proper fixation, specimens were processed through dehydration in ethanol, clearance in methyl benzoate, and embedded in paraffin wax. Paraffin sections of 5 µm were obtained and were stained with Harris hematoxylin and Eosin (HX) for general histological evaluation and with Crossmon’s trichrome for evaluation of collagen content.
Negative image study
The negative image study was conducted using CMEIAS color segmentation. Improved computing technology was used to process color images by segmenting foreground object pixels from the background with this technique is especially useful because of the complex color micrographs that existed in this study.
Morphometrical analysis
The histological evaluation was conducted blindly on coded samples, and a comparison was performed with the sections from the untreated- and treated groups. Histological evaluation to assess the integrity and organization of collagen fibers was based on 0–3 scale44,45. Collagen integrity scores: 0 = continue, long fiber, 1 = slightly fragmented, 2 = moderately fragmented, 3 = severely fragmented. Collagen organization scores: 0 = compact and parallel, 1 = slightly loose and wave, 2 = moderately loose, wavy, and cross to each other, 3 = no identifiable pattern. Using threshold area fraction determination, the percentage of the collagen-positive area was calculated using ImageJ (ImageJ Software Version 1.48v)2. The amount of collagen was reported as a percentage of the total number of pixels in the optical view as a percentage and expressed as mean ± SEM.
Statistical analysis
Statistical analyses were performed by one-way ANOVA using GraphPad Prism software version 5.03 (GraphPad Software Inc., La Jolla, CA, USA). p-values of < 0.05 were considered statistically significant. Figures were generated using Adobe Photoshop CS6 and Prism 5 version 5.03.
Ethical approval
All the procedures in this study have been approved by The National Ethical Committee of The Faculty of Veterinary Medicine, Assiut University, Assiut, Egypt, under the Egyptian bylaws and OIE animal welfare standards for animal care and use in research and education. We did not use any human skin. This study was conducted in compliance with the ARRIVE guidelines. All methods were performed in accordance with relevant guideline and regulations.
Data availability
All data generated or analyzed during this study are included in this published article.
References
Junior, E. M. L. et al. Characterization of the microbiota of the skin and oral cavity of Oreochromis niloticus Caracterização da microbiota da pele e cavidade oral de Oreochromis niloticus. J. Health Biol. Sci. 4, 193–197 (2016).
Alves, A. P. N. N. et al. Study of tensiometric properties, microbiological and collagen content in nile tilapia skin submitted to different sterilization methods. Cell Tissue Bank. 19, 373–382 (2018).
Ibrahim, A., Hassan, D., Kelany, N., Kotb, S. & Soliman, M. Validation of three different sterilization methods of tilapia skin dressing: Impact on microbiological enumeration and collagen content. Front. Vet. Sci. 7, 597751–597751. https://doi.org/10.3389/fvets.2020.597751 (2020).
Mabrouk, M. M. et al. Impact of aqueous exposure to silver nanoparticles on growth performance, redox status, non-specific immunity, and histopathological changes of Nile Tilapia, Oreochromis niloticus, challenged with Aeromonas hydrophila. Aquacult. Rep. 21, 100816 (2021).
Shaalan, M., Saleh, M., El-Mahdy, M. & El-Matbouli, M. Recent progress in applications of nanoparticles in fish medicine: A review. Nanomed. Nanotechnol. Biol. Med. 12, 701–710. https://doi.org/10.1016/j.nano.2015.11.005 (2016).
Rai, M., Yadav, A. & Gade, A. Silver nanoparticles as a new generation of antimicrobials. Biotechnol. Adv. 27, 76–83 (2009).
Abdelhamid, H. N., Mahmoud, G.A.-E. & Sharmouk, W. A cerium-based MOFzyme with multi-enzyme-like activity for the disruption and inhibition of fungal recolonization. J. Mater. Chem. B 8, 7548–7556 (2020).
Cohen, G. M. Caspases: The executioners of apoptosis. Biochem. J. 326, 1–16 (1997).
Fadeel, B., Åhlin, A., Henter, J.-I., Orrenius, S. & Hampton, M. B. Involvement of caspases in neutrophil apoptosis: Regulation by reactive oxygen species. Blood J. Am. Soc. Hematol. 92, 4808–4818 (1998).
De Silva, C. et al. The mechanistic action of biosynthesised silver nanoparticles and its application in aquaculture and livestock industries. Animals 11, 2097 (2021).
Jung, W. K. et al. Antibacterial activity and mechanism of action of the silver ion in Staphylococcus aureus and Escherichia coli. Appl. Environ. Microbiol. 74, 2171–2178 (2008).
Soltani, M. et al. The inhibitory effect of silver nanoparticles on the bacterial fish pathogens, Streptococcus iniae Lactococcus garvieae, yersinia ruckeri Aeromonas hydrophila. Iran. J. Vet. Med. 3, 137–142 (2009).
Vaseeharan, B., Ramasamy, P. & Chen, J. C. Antibacterial activity of silver nanoparticles (Ag NPs) synthesized by tea leaf extracts against pathogenic Vibrio harveyi and its protective efficacy on juvenile Feneropenaeus indicus. Lett. Appl. Microbiol. 50, 352–356. https://doi.org/10.1111/j.1472-765X.2010.02799.x (2010).
Antony, J. J. et al. Antimicrobial activity of Leucas aspera engineered silver nanoparticles against Aeromonas hydrophila in infected Catla catla. Colloids Surf. B 109, 20–24 (2013).
Prakash, P., Gnanaprakasam, P., Emmanuel, R., Arokiyaraj, S. & Saravanan, M. Green synthesis of silver nanoparticles from leaf extract of Mimusops elengi, Linn. for enhanced antibacterial activity against multi drug resistant clinical isolates. Colloids Surf. B Biointerfaces 108, 255–259 (2013).
Mahanty, A. et al. Phytoextracts-synthesized silver nanoparticles inhibit bacterial fish pathogen Aeromonas hydrophila. Indian J. Microbiol. 53, 438–446 (2013).
Swain, P. et al. Antimicrobial activity of metal based nanoparticles against microbes associated with diseases in aquaculture. World J. Microbiol. Biotechnol. 30, 2491–2502. https://doi.org/10.1007/s11274-014-1674-4 (2014).
Shaalan, M. et al. Silver nanoparticles: Their role as antibacterial agent against Aeromonas salmonicida subsp. salmonicida in rainbow trout (Oncorhynchus mykiss). Res. Vet. Sci. 119, 196–204. https://doi.org/10.1016/j.rvsc.2018.06.019 (2018).
Mahmoud, G.A.-E., Osman, Y. A. & Abdel-Hakeem, S. S. Hydrolytic bacteria associated with natural helminth infection in the midgut of Red Sea marbled spinefoot rabbit fish Siganus rivulatus. Microb. Pathog. 147, 104404 (2020).
Pelgrift, R. Y. & Friedman, A. J. Nanotechnology as a therapeutic tool to combat microbial resistance. Adv. Drug Deliv. Rev. 65, 1803–1815 (2013).
Ibrahim, A. B., Mahmoud, G. A. E., Meurer, F. & Bodensteiner, M. Preparation and crystallographic studies of a new mercuric salicylaldimine complex for fabrication of microscaled and nanoscaled mercuric sulfide as antimicrobial agents against human pathogenic yeasts and filamentous fungi. Appl. Organomet. Chem. 35, e6134 (2021).
Lu, Z., Rong, K., Li, J., Yang, H. & Chen, R. Size-dependent antibacterial activities of silver nanoparticles against oral anaerobic pathogenic bacteria. J. Mater. Sci. Mater. Med. 24, 1465–1471 (2013).
Hong, X., Wen, J., Xiong, X. & Hu, Y. Shape effect on the antibacterial activity of silver nanoparticles synthesized via a microwave-assisted method. Environ. Sci. Pollut. Res. 23, 4489–4497 (2016).
Patra, J. K. & Baek, K.-H. Antibacterial activity and synergistic antibacterial potential of biosynthesized silver nanoparticles against foodborne pathogenic bacteria along with its anticandidal and antioxidant effects. Front. Microbiol. 8, 167 (2017).
Soliman, H., Elsayed, A. & Dyaa, A. Antimicrobial activity of silver nanoparticles biosynthesised by Rhodotorula sp. strain ATL72. Egypt. J. Basic Appl. Sci. 5, 228–233. https://doi.org/10.1016/j.ejbas.2018.05.005 (2018).
Mathivanan, K. et al. Biologically synthesized silver nanoparticles against pathogenic bacteria: Synthesis, calcination and characterization. Biocatal. Agric. Biotechnol. 22, 101373 (2019).
Matsumura, Y., Yoshikata, K., Kunisaki, S.-I. & Tsuchido, T. Mode of bactericidal action of silver zeolite and its comparison with that of silver nitrate. Appl. Environ. Microbiol. 69, 4278–4281 (2003).
Nathan, C. & Cunningham-Bussel, A. Beyond oxidative stress: An immunologist’s guide to reactive oxygen species. Nat. Rev. Immunol. 13, 349–361 (2013).
Ebrahiminezhad, A., Raee, M. J., Manafi, Z., Sotoodeh-Jahromi, A. & Ghasemi, Y. Ancient and novel forms of silver in medicine and biomedicine. J. Adv. Med. Sci. Appl. Technol. 2, 122–128 (2016).
Palmer, I. et al. Identification of a suitable sterilisation method for collagen derived from a marine Demosponge. Int. J. Nano Biomater. 4, 148 (2012).
Cheung, D. T., Perelman, N., Tong, D. & Nimni, M. E. The effect of γ-irradiation on collagen molecules, isolated α-chains, and crosslinked native fibers. J. Biomed. Mater. Res. 24, 581–589 (1990).
LH, O. D. et al. Influence of ethylene oxide gas treatment on the in vitro degradation behavior of dermal sheep collagen. J. Biomed. Mater. Res. 29, 149–155 (1995).
Huang, N. F. et al. The modulation of endothelial cell morphology, function, and survival using anisotropic nanofibrillar collagen scaffolds. Biomaterials 34, 4038–4047 (2013).
Cameron, S. J., Hosseinian, F. & Willmore, W. G. A current overview of the biological and cellular effects of nanosilver. Int. J. Mol. Sci. 19, 2030 (2018).
Gong, C.-P., Li, S.-C. & Wang, R.-Y. Development of biosynthesized silver nanoparticles based formulation for treating wounds during nursing care in hospitals. J. Photochem. Photobiol. B 183, 137–141 (2018).
Toczek, J., Sadłocha, M., Major, K. & Stojko, R. Benefit of silver and gold nanoparticles in wound healing process after endometrial cancer protocol. Biomedicines 10, 679 (2022).
Liu, X. et al. Silver nanoparticles mediate differential responses in keratinocytes and fibroblasts during skin wound healing. Chem. Med. Chem. 5, 468–475 (2010).
Nam, G., Rangasamy, S., Purushothaman, B. & Song, J. M. The application of bactericidal silver nanoparticles in wound treatment. Nanomater. Nanotechnol. 5, 5–23 (2015).
Downes, F. P., Ito, K., Itō, K. & Association, A. P. H. Compendium of Methods for the Microbiological Examination of Foods. (American Public Health Association, 2001).
Atlas, R. M. Handbook of Microbiological Media. (CRC Press, Boca Raton, FL, 1993).
Barnett, R. W. P. & Yarrow, D. Yeasts: Characteristics and identification. Pediatr. Dermatol. 18, 547–547. https://doi.org/10.1046/j.1525-1470.2001.1862020a.x (2001).
Leslie, B. A. S. The Fusarium Laboratory Manual (Blackwell Publishing, 2006).
Bergey, D. H. & Holt, J. G. Bergey’s Manual of Determinative Bacteriology (Williams & Wilkins, 1994).
Chen, J. et al. Autologous tenocyte therapy for experimental Achilles tendinopathy in a rabbit model. Tissue Eng. Part A 17, 2037–2048 (2011).
Farfaras, S. et al. More histologic and ultrastructural degenerative signs in the subscapularis tendon and the joint capsule in male patients with shoulder impingement. Knee Surg. Sports Traumatol. Arthrosc. 26, 79–87 (2018).
Acknowledgements
The authors are thankful to The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB) for providing open access funding.
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
A.I. and A.E.: designed the study and collected fish skin samples, A.E.: prepared the AgNPs concentrations, G.M.: conducted the microbiological examination, D.M.: performed the histological examination. All the authors wrote, revised, and approved the paper for publication, all authors reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Elshahawy, A.M., Mahmoud, G.AE., Mokhtar, D.M. et al. The optimal concentration of silver nanoparticles in sterilizing fish skin grafts. Sci Rep 12, 19483 (2022). https://doi.org/10.1038/s41598-022-23853-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-23853-y
- Springer Nature Limited