Abstract
This work provides useful insights into the development of HfO2-based memristive systems with a p-type silicon bottom electrode that are compatible with the complementary metal–oxide–semiconductor technology. The results obtained reveal the importance of the top electrode selection to achieve unique device characteristics. The Ag/HfO2/Si devices have exhibited a larger memory window and self-compliance characteristics. On the other hand, the Au/HfO2/Si devices have displayed substantial cycle-to-cycle variation in the ON-state conductance. These device characteristics can be used as an indicator for the design of resistive-switching devices in various scenes such as, memory, security, and sensing. The current–voltage (I–V) characteristics of Ag/HfO2/Si and Au/HfO2/Si devices under positive and negative bias conditions have provided valuable information on the ON and OFF states of the devices and the underlying resistive switching mechanisms. Repeatable, low-power, and forming-free bipolar resistive switching is obtained with both device structures, with the Au/HfO2/Si devices displaying a poorer device-to-device reproducibility. Furthermore, the Au/HfO2/Si devices have exhibited N-type negative differential resistance (NDR), suggesting Joule-heating activated migration of oxygen vacancies to be responsible for the SET process in the unstable unipolar mode.
Similar content being viewed by others
Introduction
Nonvolatile memories based on resistive random access memories (ReRAMs) have attracted wide attention as an alternative to the conventional Si-based Flash memory devices1. However, the use of memristors and memristive systems2 is not limited to memories, and their potential for numerous applications such as reconfigurable computing3, neuromorphic computing4,5, sensing6,7,8,9, and security10,11,12 has been demonstrated previously. A review of some of the prospective applications of this promising technology can be found in13.
The use of p- and n-type doped silicon as bottom electrode (BE) in memristive systems remains an unfulfilled potential to both develop memory, computing, and sensor components using the traditional silicon-based microelectronic technology, and to integrate all these different functionalities monolithically on a single platform. It is also worth mentioning that 3D crossbar arrays employing silicon electrodes have been shown to effectively address the well-known sneak path problem14,15,16 by introducing nonlinearity or asymmetry to the I–V characteristic of the device through the self-rectifying effect17, offering thus an exciting opportunity for the realization of high density, parallel-processing memristor arrays. Moreover, memristive systems based on CMOS compatible functional layers such as silicon oxide17,18 and hafnium oxide8,19,20 deposited on highly-doped silicon electrodes are promising candidates for establishing future systems such as sensing-immersed-in-computation21. Hafnium oxide is highly regarded for being a binary system with only two thermodynamically stable phases in equilibrium: insulating and conducting phases22. This stability is anticipated to qualify HfO2 for the development of memristive systems exhibiting high reliability and endurance23.
The electrodes employed in memristor-based electronic devices may significantly affect the resistive switching (RS) behavior. For metal-oxide thin-film systems that make use of inert metals as electrodes, the switching mode is mostly bipolar24,25,26,27,28, although unipolar operation characteristics have also been demonstrated18. In some cases, the mode of operation could be changed between bipolar and unipolar by adjusting the operation conditions29 or by introducing and tuning the thickness of an oxygen scavenging metal layer30.
For a memristor architecture with a highly-doped Si bottom electrode, studies concerned with the impact of the top electrode (TE) material on the properties of the memristor are very rare18,19. To understand the switching mechanism and to design memristive systems with different functionalities, it is important to know how the SET/RESET operation depends on the choice of top electrode. We have previously reported on the RS behavior of the Ag/HfO2/p+-Si devices20. In this work, the device characteristics have been studied in TE (Ag or Au)/HfO2 based memristors on highly-doped p-type Si substrates (illustrated in Fig. 1) by employing electrical characterisation. We have investigated the RS phenomenon in these structures using different electrical biasing schemes, and identified the conditions that induced repeatable high-to-low and low-to-high resistance transitions. Accordingly, we report the important device characteristics such as VSET, VRESET, RON, ROFF, as well as the variation in these characteristics. The TE material has been found to play a key role on the SET/RESET voltage distributions as well as the characteristics of transition from the high resistance state (HRS) to low resistance state (LRS). The results reveal that the Au/HfO2/p+-Si devices exhibit high cycle-to-cycle and device-to-device variations. It is important and useful to report these unique properties considering the fact that memristive devices find applications in systems where the variability presents a natural opportunity, such as the security applications10,11,12,31,32.
Experimental results
Physical characterization
HfO2 layer thicknesses of around 15 and 20 nm have been obtained for the samples with the Ag and Au TEs, respectively, as seen from the transmission electron microscopy (TEM) images (Fig. 2a,b). The microstructure of the HfO2 films used in these samples are very similar as demonstrated in the topographic images of the oxide surface obtained by Atomic Force Microscopy (AFM) (Fig. 2c,d).
Electrical characterization
The polarity of the electrical bias applied to the memristive stacks may influence the RS characteristics. For instance, the electroforming process for the valence change memory (VCM) based bipolar devices may be polarity dependent due to the built-in asymmetry of the contacts at the top and bottom electrode interfaces as determined by the device design and fabrication procedure33. In the case of chemical metallization memory (ECM)34,35 based devices, the formation of a filament requires the electrochemical dissolution of an active electrode (usually Ag or Cu), followed by the drift of the injected metal cation clusters toward the counter electrode by a positive voltage applied to the active electrode26,36,37. Thus, the comparison of the response of these devices to different biasing schemes may provide valuable information for deciphering the nature of resistive switching in a material system. Observing the current–voltage (I–V) characteristics of pristine devices through initiating sweeps of opposite polarities on different devices forms the basis of our experimental methodology.
The samples employed in this work did not require an initial electroforming step38 to produce a repeatable resistive switching behavior. However, as shown in Fig. 3a, the device with the Ag TE exhibited a stable SET/RESET operation only following eight voltage sweep cycles, prior to which it exhibited self-rectifying characteristics17,20. Moreover, during the SET operation, the current increased sharply to a level below 10–4 A and then increased gradually till the externally applied compliance current (CC), exhibiting the property of self-compliance. The CC was applied to prevent the permanent dielectric breakdown of the metal-oxide and device deterioration39. On the other hand, as shown in Fig. 3b, the current flowing through the Au/HfO2/Si device reached the CC of 10–4 A during the abrupt HRS-to-LRS transition without any self-compliance imposed by the device. Both devices with Ag and Au TEs exhibited a bipolar RS behavior as shown in Fig. 3a,b, respectively, but with different characteristics which are analyzed next. It is worth mentioning that this behavior could not be confirmed with every Au/HfO2/Si device tested, presenting a challenge in terms of write/erase reproducibility within the reported electrical testing conditions.
For each of the Ag/HfO2/Si and Au/HfO2/Si devices, we extracted important device characteristics, such as the VSET, VRESET, RLRS, and RHRS using the data from 50 consecutive SET-RESET sweep cycles presented in Fig. 3a,b. The resistance values were extracted at a voltage of 0.2 V. Figure 3c,d show the statistical distribution of the VSET-VRESET and RHRS-RLRS for the TE/HfO2/Si devices, respectively. It is seen that: (i) the electrical switching in the Au/HfO2/Si stack gives a more scattered distribution of the VRESET and RLRS values than in the case of the Ag/HfO2/Si stack; (ii) the Au/HfO2/Si stack also displays larger VSET and lower VRESET average values. Furthermore, the HRS and LRS resistance values extracted at 0.2 V were used to estimate the off-to-on resistance ratio at each cycle. The Ag/HfO2/Si and Au/HfO2/Si devices have exhibited a mean ROFF/RON ratio of ~ 2 × 103 and ~ 900, respectively (see Supplementary Fig. S1 online). These results reveal the key role which the TE plays in determining the performance of TE/HfO2/Si memristive systems.
To further understand the nature of RS behavior of the TE/HfO2/Si devices with different TEs, we investigated the I–V characteristics of pristine devices by applying sweeps of negative polarity, as given in Fig. 4a,b for the Ag and Au top electrodes, respectively. This approach was chosen to eliminate the injection of Ag cations into the hafnium oxide layer though the following electrochemical dissolution half-reaction Ag → Agz+ + ze− that may take place within the voltage sweep window applied under the positive bias, where the cation valence z is either 1 or 240. It is seen from Fig. 4a,b that: (i) regardless of the type of TE used, the SET and RESET operations occur in the same voltage polarity; (ii) both devices exhibit instability of the SET/RESET operation and the LRS becomes volatile following a couple of sweeps after the first SET (sweep 1), as shown by sweep 7 and sweep 4, respectively, for the Ag/HfO2/Si and Au/HfO2/Si devices; (iii) for the same stack, the SET and RESET operations occur at around a similar voltage within a range from − 3 to − 4 V and − 4 to − 5 V, respectively, in Ag/HfO2/Si and Au/HfO2/Si stacks. Another interesting observation worth to be discussed is that the I–V slope of the first SET (sweep 1) of the Au/HfO2/Si stack, shown in Fig. 4b, is negative between ~ − 2.6 and − 4.2 V (VSET) corresponding to a voltage-controlled, or N-type, negative differential resistance (NDR)41 region followed by an abrupt transition to the LRS.
Discussion
It is suggested in the literature that, in principle, a voltage controlled NDR is possible through Joule heating and may occur when the resistance increases superlinearly with temperature42. Furthermore, it may render the active material electrically unstable. As a result, for reasons of electrical stability, as well as in consistency with the minimum entropy production principle, high field domains separating regions of low field form in initially isotropic materials41. Under conditions of negative conductivity which prevail in the case of NDR, normal random fluctuations in the carrier distribution can form large space charge regions leading to domains of high electric field. A permanent nucleation site such as a crystal defect, a doping inhomogeneity, or the cathode itself are considered as sources of the random noise fluctuation43. In this regard, the generation of oxygen vacancies in metal-oxide films at the metal-oxide/anode interface by the electrochemical redox reactions44,45,46 may lead to space charge fluctuations. In fact, the generation of oxygen vacancies may be facilitated in the case of N-type NDR in an attempt to reach stability. Bersuker et al.24 reported a straightforward positive correlation between the temperature increase and oxygen vacancy generation, as well as the importance of a nonuniform temperature profile in promoting the formation of a conductive filament. Similarly, a large internal temperature gradient caused by the Joule heating in the device has been suggested to facilitate the inward migration of oxygen vacancies by the thermophoresis, or Soret effect, to form a conductive filament between the electrodes47. It has also been reported that the coexistence of NDR and RS may strongly depend on the ambient relative humidity48. The authors suggested that the water molecules could be combined with the oxygen vacancies, thereby accelerating the rupture of oxygen vacancy filaments. The same mechanism could be playing a role in reducing the current as the magnitude of the voltage is increased beyond ~ 2.7 V up to the VSET (Fig. 4b, sweep 1). Therefore, the observation of a voltage-controlled NDR followed by an abrupt transition to the LRS looks very much like the indication of a filament forming process involving oxygen vacancies, although further studies are needed to verify this hypothesis. The proximity in values of the SET and RESET voltages, as seen in Fig. 4b, suggests that the transition from LRS to HRS requires reaching a critical local temperature in the filament.
The mean SET voltage for the bipolar RS of the Ag/HfO2/Si device is extracted to be \(\stackrel{-}{{V}_{SET}}=1.36 V.\) On the other hand, the SET operation of unipolar RS of the same device required a negative bias of 3 to 4 V in magnitude. The difference in the magnitudes of VSET observed between the bipolar and unipolar modes is significant, suggesting major differences in the mechanism that is responsible for the SET process under opposite bias polarities. From the similarity between the magnitudes of VSET for the Ag/HfO2/Si and Au/HfO2/Si devices in the unipolar mode, we infer the switching kinetics of the Ag/HfO2/Si devices to be also controlled by Joule heating as discussed for the Au/HfO2/Si devices above. On the other hand, a low SET voltage exhibited in the bipolar mode suggests a dominant ECM behavior25.
Under positive bias to the Ag electrode, Ag preferentially oxidizes to Ag+40 with the standard redox potential in aqueous solutions given as Ag+/Ag (E° = 0.80 V)49. This is followed by the migration of Ag+ cations through the oxide layer and the nucleation and growth of Ag by reduction at the counter electrode37. The standard redox potentials for Au are given as Au3+/Au (E° = 1.52 V), and Au+/Au (E° = 1.83 V)49. The Au-related redox reactions are governed by more positive standard reduction potentials compared to the Ag+/Ag system. This indicates that Ag would be more easily oxidized than Au in positive bias40. It is worth noting that oxygen is insoluble in gold and will not form a three-dimensional oxide50. Therefore, the ionization of Au at the anode interface is not possible through the oxidation of Au atoms at the Au/oxide interface due to the reduction of the oxide, while Ag ions can also be injected from the oxidized Ag.
The mean SET voltage for the bipolar RS of Au/HfO2/Si devices is extracted to be \(\stackrel{-}{{V}_{SET}}=2.04 V\), which is close to the \(\stackrel{-}{{V}_{SET}}\) (1.36 V) of Ag/HfO2/Si devices but significantly less than the range of SET voltages (from 4 to 5 V in magnitude) required for their unipolar operation. Considering the small difference between the \(\stackrel{-}{{V}_{SET}}\) of the Ag/HfO2/Si and Au/HfO2/Si devices, it is of interest to investigate the possibility of the metal ion injection and migration to play a role in the switching kinetics of the bipolar RS of the Au/HfO2/Si devices. The findings on the diffusion of Au ions in dielectrics reveal differences among various material systems. For example, a study that used Rutherford backscattering (RBS) analysis and capacitance–voltage measurements could not detect the diffusion of Au in SiO2 for temperatures up to 600 °C and fields as high as 106 V/cm51. Contrarily, the migration of Au cations from the electrode into the oxide was reported in Y/Y2O3/Au stacks52. It should be emphasized that in the aforementioned work, the value of voltage applied to the samples exceeded 10.6 V, which is significantly higher than the value of the maximum positive voltage applied to the Au electrode (i.e., 3 V) in our study. Diffusion of Au atoms in HfO2, Al2O3, and SiO2 thin-films has been reported in another study, but only above 500 °C53. Furthermore, it is suggested in the literature that the migration rate of metal ions in the oxide films may be strongly influenced by the structural properties of the films such as porosity and density40. On the basis of these findings, it is hard to conclude whether Au cations played a role in the bipolar resistive switching exhibited by our devices but it is also hard to rule out the possibility completely.
That said, there is evidence that a large ROFF/RON ratio is more likely to be obtained with the ECM-type devices54,55. In this regard, the smaller ratio demonstrated by the Au/HfO2/Si devices compared to the Ag/HfO2/Si devices suggests that migration of anions, typically oxygen vacancies, may be playing a role in controlling the bipolar switching in the Au/HfO2/Si devices.
The statistical distributions of important device characteristics provide critical insights for the design of memristive systems for different applications. In terms of the voltage demand in writing operations, both Ag/HfO2/Si (~ 1.36 V) and Au/HfO2/Si (~ 2.04 V) devices exhibit a superior performance compared to the silicon-based flash memory technology (16–20 V)2. A high on/off conductance ratio is desirable for the memory applications2. Therefore, the larger memory window (~ 2 × 103) of the Ag/HfO2/Si devices make them suitable candidates for memory applications. Similar results have been previously reported for TiN/HfOx/Ti/TiN (> 103)56 and Cu/HfO2/Pt (103–104)57 devices. On the other hand, the RLRS of the Au/HfO2/Si devices is observed to be much more dispersed than that of the Ag/HfO2/Si. This high cycle-to-cycle variation of the RLRS in the Au/HfO2/Si devices (see Supplementary Figs. S2–S4 online) may be exploited for some applications in which the variability presents a natural opportunity. Security applications, a key research area for continued increased performance of future integrated circuits, is one of the areas where variations in device characteristics could be utilized10,11,31,58. Furthermore, the self-compliance characteristic, as demonstrated by the Ag/HfO2/Si devices, is reported to provide a compelling advantage for practical high-density ReRAMs by reducing the complexity of peripheral circuit design59. Also, these devices come with a high endurance potential due to the lack of necessity for electroforming which can cause significant damage to a device38.
Conclusions
In summary, we have investigated the detailed resistive switching behavior of HfO2-based devices, fabricated with highly-doped p-type Si BEs and two different TEs of Ag or Au, by means of I–V measurements. We have demonstrated that the behavior is significantly influenced by the choice of the TE. For instance, the mean ON/OFF ratio decreases from ~ 2 × 103 to ~ 900 as the TE changes from Ag to Au. It was found that both Ag/HfO2/Si and Au/HfO2/Si devices can exhibit bipolar and unipolar resistive switching modes. Although the bipolar mode was reproducible for the Ag/HfO2/Si devices, this behavior could not be confirmed with every Au/HfO2/Si device tested within the reported electrical testing conditions. The unipolar mode, which was obtained under the negative bias polarity, was unstable for both device types. During the SET operation of this mode, the Au/HfO2/Si devices exhibited N-type NDR which is a phenomenon regarded as difficult to be observed in practice. The associated I-V suggests the Joule-heating activated migration of oxygen vacancies and filament formation to be responsible for the SET process in the unipolar mode. On the other hand, a SET voltage much smaller than that of the unipolar mode suggests an ECM-based SET process for the bipolar mode. Further investigations in the future would be necessary to assess the possibility that Au ions diffusing into the HfO2 film may be involved in the filament forming process.
Methods
Device fabrication
The Ag/HfO2/Si and Au/HfO2/Si devices investigated in this work were fabricated on two separate Si wafers with a resistivity of 0.004–0.007 Ω-cm (Wafer Works Corp.). For both types of devices, the highly-doped Si substrate served as the BE. The top electrodes (~ 60-nm-thick) were deposited by sputtering through a shadow mask with 2 mm × 2 mm openings. The hafnium oxide thin film in the Ag/HfO2/Si stack was deposited by radio frequency (RF) sputtering using an HfO2 target of 99.9% purity (AJA International), in Ar atmosphere at 10 mTorr pressure. Similarly, that of the Au/HfO2/Si stack was deposited at 4 mTorr pressure in Ar atmosphere by using an HfO2 target of 99.99% (Testbourne Ltd.). During the HfO2 depositions, the power was set to 100 W and 120 W, respectively, for the Ag/HfO2/Si and Au/HfO2/Si stacks.
Physical characterization
TEM imaging of the samples was performed with a FEI Titan S/TEM. The images were obtained in TEM mode at 300 kV. Topographic images of the hafnium oxide films were obtained by a MFP-3D Origin AFM (Asylum Research) using the AC mode imaging in air.
Electrical characterization
The current–voltage (I–V) measurements were performed using two parameter analyser systems (Keithley 4200-SCS and Keithley 2450). The Si electrode was electrically grounded in all of the measurements.
References
Waser, R., Dittmann, R., Staikov, G. & Szot, K. Redox-based resistive switching memories–nanoionic mechanisms, prospects, and challenges. Adv. Mater. 21, 2632–2663 (2009).
Tetzlaff, R. Memristors and Memristive Systems 3–403 (Springer, New York, 2013).
Zidan, M. A. et al. Field-programmable crossbar array (FPCA) for reconfigurable computing. IEEE Trans. Multi-Scale Comput. Syst. 4, 698–710 (2017).
Serb, A. et al. Unsupervised learning in probabilistic neural networks with multi-state metal-oxide memristive synapses. Nat. Commun. 7, 1–9 (2016).
Mehonic, A. & Kenyon, A. J. Emulating the electrical activity of the neuron using a silicon oxide RRAM cell. Front. Neurosci. 10, 57 (2016).
Carrara, S. et al. Memristive-biosensors: a new detection method by using nanofabricated memristors. Sens. Actuators B 171, 449–457 (2012).
Tzouvadaki, I. et al. 2015 11th Conference on Ph.D. Research in Microelectronics and Electronics (PRIME). 17–20 (IEEE).
Hadi, S. A. et al. Bipolar Cu/HfO2/p++ Si memristors by sol-gel spin coating method and their application to environmental sensing. Sci. Rep. 9, 9983 (2019).
Vidiš, M. et al. Gasistor: a memristor based gas-triggered switch and gas sensor with memory. Appl. Phys. Lett. 115, 093504 (2019).
Rajendran, J. et al. Nano meets security: Exploring nanoelectronic devices for security applications. Proc. IEEE 103, 829–849 (2015).
Pang, Y. et al. Optimization of RRAM-based physical unclonable function with a novel differential read-out method. IEEE Electron Device Lett. 38, 168–171 (2017).
Pang, Y. et al. 2017 IEEE International Electron Devices Meeting (IEDM). 12.12. 11–12.12. 14 (IEEE).
Pan, F., Gao, S., Chen, C., Song, C. & Zeng, F. Recent progress in resistive random access memories: materials, switching mechanisms, and performance. Mater. Sci. Eng. R 83, 1–59 (2014).
Joshua Yang, J. et al. Engineering nonlinearity into memristors for passive crossbar applications. Appl. Phys. Lett. 100, 113501 (2012).
Yang, J. J., Strukov, D. B. & Stewart, D. R. Memristive devices for computing. Nat. Nanotechnol. 8, 13 (2013).
Humood, K. et al. Proc. - Int. Conf. Microelectron., 31st. 244–248 (IEEE).
Li, C. et al. Three-dimensional crossbar arrays of self-rectifying Si/SiO2/Si memristors. Nat. Commun. 8, 15666. https://doi.org/10.1038/ncomms15666 (2017).
Li, C., Jiang, H. & Xia, Q. Low voltage resistive switching devices based on chemically produced silicon oxide. Appl. Phys. Lett. 103, 062104. https://doi.org/10.1063/1.4817970 (2013).
Munoz-Gorriz, J., Acero, M., Gonzalez, M. & Campabadal, F. Span. Conf. Electron Devices, Proc., 11th. 1–4 (IEEE).
Saylan, S. et al. Silver/(sub-10-nm) hafnium-oxide-based resistive switching devices on silicon: characteristics and switching mechanism. Nanotechnology 31, 165202 (2020).
Bishop, M. D., Wong, H.-S.P., Mitra, S. & Shulaker, M. M. Monolithic 3-D Integration. IEEE Micro 39, 16–27 (2019).
Miao, F. et al. Anatomy of a nanoscale conduction channel reveals the mechanism of a high-performance memristor. Adv. Mater. 23, 5633–5640 (2011).
Lee, H. et al. 2010 Int. Electron Devices Meet. 19.17. 11–19.17. 14 (IEEE).
Bersuker, G. et al. Metal oxide resistive memory switching mechanism based on conductive filament properties. J. Appl. Phys. 110, 124518. https://doi.org/10.1063/1.3671565 (2011).
Lin, K.-L. et al. Electrode dependence of filament formation in HfO2 resistive-switching memory. J. Appl. Phys. 99, 063507 (2011).
Saadi, M. et al. On the mechanisms of cation injection in conducting bridge memories: The case of HfO2 in contact with noble metal anodes (Au, Cu, Ag). J. Appl. Phys. 119, 114501. https://doi.org/10.1063/1.4943776 (2016).
Wouters, D. J., Menzel, S., Rupp, J. A., Hennen, T. & Waser, R. On the universality of the I-V switching characteristics in non-volatile and volatile resistive switching oxides. Faraday Discuss. 213, 183–196 (2019).
Pi, S. et al. Memristor crossbar arrays with 6-nm half-pitch and 2-nm critical dimension. Nat. Nanotechnol. 14, 35–39 (2019).
Wedig, A. et al. Nanoscale cation motion in TaOx, HfOx and TiOx memristive systems. Nat. Nanotechnol. 11, 67 (2016).
Schonhals, A. et al. 2015 IEEE International Memory Workshop (IMW). 1–4 (IEEE).
IEEE. International Roadmap for Devices and Systems: Beyond CMOS. (2020).
Abunahla, H. et al. 2016 IEEE 59th International Midwest Symposium on Circuits and Systems (MWSCAS). 1–4 (IEEE).
Yang, J. J., Inoue, I. H., Mikolajick, T. & Hwang, C. S. Metal oxide memories based on thermochemical and valence change mechanisms. MRS Bull. 37, 131–137 (2012).
Valov, I., Waser, R., Jameson, J. R. & Kozicki, M. N. Electrochemical metallization memories—fundamentals, applications, prospects. Nanotechnology 22, 254003 (2011).
Ambrosi, E. et al. Electrochemical metallization ReRAMs (ECM)-Experiments and modelling: general discussion. Faraday Discuss. 213, 115–150 (2019).
Lübben, M., Wiefels, S., Waser, R. & Valov, I. Processes and effects of oxygen and moisture in resistively switching TaOx and HfOx. Adv. Electron. Mater. 4, 1700458 (2018).
Tsuruoka, T. et al. Effects of moisture on the switching characteristics of oxide-based gapless-type atomic switches. Adv. Funct. Mater. 22, 70–77 (2012).
Williams, R. S. Summary of the Faraday Discussion on New memory paradigms: memristive phenomena and neuromorphic applications. Faraday Discuss. 213, 579–587 (2019).
Ielmini, D. Resistive switching memories based on metal oxides: mechanisms, reliability and scaling. Semicond. Sci. Technol. 31, 063002 (2016).
Tsuruoka, T. et al. Redox reactions at Cu, Ag/Ta2O5 interfaces and the effects of Ta2O5 film density on the forming process in atomic switch structures. Adv. Funct. Mater. 25, 6374–6381 (2015).
Ridley, B. Specific negative resistance in solids. Proc. Phys. Soc. 82, 954 (1963).
Gibson, G. A. Designing negative differential resistance devices based on self-heating. Adv. Funct. Mater. 28, 1704175 (2018).
Streetman, B. G. & Banerjee, S. Solid State Electronic Devices (Prentice Hall, Englewood Cliffs, NJ, 1995).
Kim, K. M., Jeong, D. S. & Hwang, C. S. Nanofilamentary resistive switching in binary oxide system; a review on the present status and outlook. Nanotechnology 22, 254002 (2011).
Jeong, D. S., Schroeder, H., Breuer, U. & Waser, R. Characteristic electroforming behavior in Pt/TiO2/Pt resistive switching cells depending on atmosphere. J. Appl. Phys. 104, 123716 (2008).
Yang, J. J. et al. The mechanism of electroforming of metal oxide memristive switches. Nanotechnology 20, 215201 (2009).
Pickett, M. D., Perner, F. A. & Williams, R. S. Stateful Negative Differential Resistance Devices (Wiley, Amsterdam, 2013).
Zhou, G. et al. Coexistence of negative differential resistance and resistive switching memory at room temperature in TiOx modulated by moisture. Advanced Electronic Materials 4, 1700567 (2018).
Bard, A., Parsons, R. & Jordan, J. Standard potentials in aqueous solution. New York 668, 294–320 (1985).
Jones, T. E., Piccinin, S. & Stampfl, C. Relativity and the nobility of gold. Mater. Chem. Phys. 141, 14–17 (2013).
McBrayer, J. D., Swanson, R. & Sigmon, T. Diffusion of metals in silicon dioxide. J. Electrochem. Soc. 133, 1242 (1986).
Noya, A., Kuriki, S., Matsumoto, G. & Hirano, M. A study of gold migration in Au-Y2O3-Y junctions by secondary ion mass spectrometry. Thin Solid Films 59, 143–146 (1979).
Čechal, J., Polčák, J. & Šikola, T. S. Detachment limited kinetics of gold diffusion through ultrathin oxide layers. J. Phys. Chem. C 118, 17549–17555 (2014).
Yang, Y. C., Fan, B., Zeng, F. & Pan, F. Bipolar resistance switching characteristics in TiN/ZnO: Mn/Pt junctions developed for nonvolatile resistive memory application. J. Nanosci. Nanotechnol. 10, 7370–7373 (2010).
Chen, C., Yang, Y., Zeng, F. & Pan, F. Bipolar resistive switching in Cu/AlN/Pt nonvolatile memory device. Appl. Phys. Lett. 97, 083502 (2010).
Lee, H.-Y. et al. Int. Electron Devices Meet. 297 (IEEE).
Haemori, M., Nagata, T. & Chikyow, T. Impact of Cu electrode on switching behavior in a Cu/HfO2/Pt structure and resultant Cu ion diffusion. Appl. Phys. Express 2, 061401 (2009).
Abunahla, H., Shehada, D., Yeun, C. Y., Mohammad, B. & Stouraitis, T. 2017 24th IEEE International Conference on Electronics, Circuits and Systems (ICECS). 58–61 (IEEE).
Hsu, C.-W., Hou, T.-H., Chen, M.-C., Wang, I.-T. & Lo, C.-L. Bipolar Ni/TiO2/HfO2/Ni RRAM with multilevel states and self-rectifying characteristics. IEEE Electron Device Lett. 34, 885–887 (2013).
Acknowledgements
We gratefully appreciate the support of Dr. Cyril Aubry for the TEM lamella preparation and TEM imaging for the Au/HfO2/Si device. The research reported in this publication was supported by funding from the United Arab Emirates Space Agency, Space Missions Science and Technology Directorate, under award no. K08 2016 001 and Khalifa University of Science and Technology (KU). The proposed project is in line with United Arab Emirates Space Agency’s Space Science, Technology and Innovation (ST&I) Roadmap aimed at developing enabling technologies for Space exploration, which is intended to accomplish the objectives of the UAE Space strategy. The authors also acknowledge the access to KU Micro & Nano Fabrication facilities, Microscopy Suite, and SoCC supported by KU under award no. RC2 2018-020, utilized for fabrication and electrical & material characterisation of the devices.
Author information
Authors and Affiliations
Contributions
S.S. and H.M.A. fabricated the devices. S.S. and K.H. performed the electrical measurements. S.S. conducted the AFM characterisation. F.R. carried out the TEM lamella preparation and TEM imaging for the Ag/HfO2/Si device. S.S., H.M.A., K.H., M.A.J., and B.M. analysed the results. B.M. directed the project and provided guidance throughout. S.S. drafted the article. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Saylan, S., Aldosari, H.M., Humood, K. et al. Effects of top electrode material in hafnium-oxide-based memristive systems on highly-doped Si. Sci Rep 10, 19541 (2020). https://doi.org/10.1038/s41598-020-76333-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-76333-6
- Springer Nature Limited
This article is cited by
-
Contact size-dependent switching instabilities in HfO2 RRAM
Journal of Materials Science: Materials in Electronics (2022)
-
Effect of the Compliance Current on the Retention Time of Cu/HfO2-Based Memristive Devices
Journal of Electronic Materials (2021)