Abstract
Two-dimensional (2D) semiconductors, especially transition metal dichalcogenides (TMDs), have been envisioned as promising candidates in extending Moore’s law. To achieve this, the controllable growth of wafer-scale TMDs single crystals or periodic single-crystal patterns are fundamental issues. Herein, we present a universal route for synthesizing arrays of unidirectionally orientated monolayer TMDs ribbons (e.g., MoS2, WS2, MoSe2, WSe2, MoSxSe2-x), by using the step edges of high-miller-index Au facets as templates. Density functional theory calculations regarding the growth kinetics of specific edges have been performed to reveal the morphological transition from triangular domains to patterned ribbons. More intriguingly, we find that, the uniformly aligned TMDs ribbons can merge into single-crystal films through a one-dimensional edge epitaxial growth mode. This work hereby puts forward an alternative pathway for the direct synthesis of inch-scale uniform monolayer TMDs single-crystals or patterned ribbons, which should promote their applications as channel materials in high-performance electronics or other fields.
Similar content being viewed by others
Introduction
Two-dimensional (2D) semiconducting transition metal dichalcogenides (TMDs) have attracted tremendous interest for their broad-range applications in electronics, optoelectronics, catalysis, etc.1,2,3. The morphology or dimensionality of TMDs is a critical factor to determine their physical properties. For instance, one-dimension (1D) monolayer MoS2 ribbon is predicted to possess novel properties such as metallic edge states4, 1D confined plasmons5, ferromagnetic behaviors6, etc. Besides, it can present improved catalytic property in hydrogen evolution reaction (HER) due to the abundant active edge sites7, and more importantly, maintained high carrier mobility8. So far, the fabrication of monolayer TMDs ribbons has largely depended on micro-nanofabrication approaches, by using electron beam or optical lithography patterning techniques9. However, these top-down methods are evidently tedious and usually need to start with large-area uniform continuous films or crystals.
Recently, several strategies have been developed for the direct synthesis of monolayer TMDs ribbons10, such as Na-Mo-O droplets driven growth on NaCl single crystals11, substrate-directed synthesis on phosphine pre-treated Si(001) substrates12, as well as ledge-directed epitaxy on β-Ga2O3 (100)13. These strategies have individually achieved the control of their thickness, orientation and dimensionality, nevertheless, the synthesis of TMDs ribbons possessing all the above advantages has not been realized.
Wafer-scale monolayer TMDs single crystals, characterized by intrinsically high crystallinity and extremely uniform property, have long been pursued. However, due to the non-centrosymmetric structures of TMDs, antiparallel domains and twin boundaries usually evolved on most growth substrates14,15,16, similar to those encountered in the preparation of h-BN. Lately, wafer-scale growth of monolayer h-BN single crystal was achieved by using liquid Au as substrate via the self-collimation of circular h-BN grains17. Wafer-scale monolayer h-BN single crystals were also realized on Cu(110)18 and Cu(111)19 substrates, where the nucleation and growth of h-BN domains were dominantly guided by the substrate-step edges. Very recently, our group realized the epitaxial growth of inch-scale monolayer MoS2 single crystals on Au(111) films20, demonstrating the potential for the unidirectionally oriented growth of TMDs grains. Despite these achievements, the successful attempts regarding the growth of wafer-scale monolayer TMDs single crystals on Au substrates remain very limited21,22. Meanwhile, the step-edge-guided growth of single-crystal TMDs has also been explored on insulating sapphire substrates23,24,25,26. Particularly, inch-scale single-crystal MoS2 and WS2 monolayers have been achieved on C-A and A plane sapphire substrates, in which the nucleation of MoS2 and WS2 are along the <10\(\bar{1}\)0> step edges of sapphire, further proving the effect of step edges on the alignment of TMDs domains. However, the direction of the step edge on sapphire is highly dependent on the miscut direction, and it is rather difficult to maintain a fixed cutting angle with such a high accuracy (e.g.,1°) over an inch scale.
Herein, we design a substrate-step templated growth strategy for synthesizing large-area uniform, unidirectionally aligned, monolayer single-crystal TMDs ribbons, by using the step edges of vicinal Au(111) single crystals as growth fronts. The superiorities of this route are summarized as follows: (1) the uniformly oriented step edges on high-index Au facets can trigger the anisotropic growth of TMDs, and direct the alignment of the resulted monolayer ribbons; (2) the chemical inertness of Au substrate to chalcogen precursor makes it a universal template for synthesizing various monolayer TMDs ribbons (e.g., MoS2, WS2, MoSe2, WSe2); (3) different from the growth on insulating substrates, the monolayer TMDs grown on Au metals are featured with relatively strong interface coupling, which can be another parameter for mediating the van der Waals epitaxial growth of 2D layered materials toward wafer-scale single crystals; (4) the synergistic effect of substrate-step-edge guided 1D epitaxy, combined with substrate-lattice-match directed 2D epitaxy modes are expected to direct the epitaxial growth of single-crystal TMDs monolayers. This work is expected to offer an alternative strategy for the synthesis of monolayer patterned TMDs ribbons or wafer-scale single-crystal films. The practical applications of the dimension controllable monolayer materials (ribbons or films) will also be demonstrated in more versatile fields, e.g., as channel materials in high-performance electronic devices and as catalysts in HER.
Results
Theoretical calculations for the evolution of monolayer TMDs ribbons
To initialize the growth of monolayer MoS2 ribbons, it is a general route to introduce anisotropic template with broken symmetry, e.g., by introducing substrate steps27. Such a substrate-template-directed synthesis strategy has previously been used for the growth of 1D GaN28, graphene29, and MoS2 nanowires30. In our experiment, a series of high-miller-index Au facets vicinal to (111) with bunched atomic steps were selected as growth templates, as obtained by melting and resolidifying Au foils on W templates (see Methods for more details). As reported previously, the types of the MoS2 terminated edges were quite different for 1D stripes and 2D triangles, i.e., Mo-zigzag (Mo-zz)/S-zigzag (S-zz) edges and Mo-zz edges, respectively, as characterized by transmission electron microscope (TEM) in previous literatures27,28. Moreover, the edge type of monolayer MoS2 achieved by the CVD growth process highly depended on the S/Mo ratio of precursors31,32,33,34. In this regard, the effect of S/Mo ratio should have a significant effect on the morphology of monolayer MoS2.
To confirm this, CVD growth was executed on a representative Au(223) facet with MoO3 and S as precursors (growth conditions: 750 °C for 3 min, Supplementary Fig. 1). When the mass ratio of S/Mo was set at 3:1, monolayer MoS2 triangular domains were obtained (Fig. 1b). As the S/Mo ratio decreased to 2:1, monolayer MoS2 ribbons evolved under similar growth conditions (Fig. 1c). X-ray photoemission spectroscopy (XPS) spectra confirmed the formation of MoS2 compounds (Supplementary Fig. 2). Atomic force microscope (AFM) images of as-grown monolayer MoS2 triangular domains and ribbons on Au substrates (Supplementary Fig. 3) clearly show that the edges of MoS2 are usually aligned along the steps of Au substrates, providing straightforward evidence for the step-edge-guided growth mechanism. Nevertheless, further decreasing the S/Mo ratio to 1:1 led to the formation of irregularly shaped MoOxS2−x crystals (Supplementary Fig. 4), probably due to the insufficient feeding of the S feedstock30.
To further understand the role of S/Mo ratio in the morphological evolution of monolayer MoS2, density functional theory (DFT) calculations were then performed to simulate the MoS2 growth on Au(111). The kinetic growth of MoS2 can be analyzed by exploring the nucleation barriers of two dominating edges on Au(111) around <110> step during the atomic accretion process, i.e., S-zz and reconstructed Mo-terminated zigzag (Mo’-zz) edges due to their higher nucleation barriers than those of armchair, and Mo-zz (see details in Supplementary Figs. 5‒7). Using Mo atoms and S2 dimers as the feeding units, the relative nucleation barriers (ΔE) for these two edges under different chemical potentials of Mo and S (labeled as μMo and μS, respectively) were calculated. For the case of high μS and low μMo (bottom right in Fig. 1d), the nucleation barriers of S-zz are smaller than that of Mo’-zz edges (ΔE < 0). Hereby, Mo-oriented edges should be prevalent in parallel with the evolution of triangular-shaped domains. As μS decreases (ΔE > 0, bottom left in Fig. 1d), the growth velocity of S-zz edge declines significantly, and S-zz edge becomes the dominating one. Following our previous results20, the minimum energy configuration corresponds to Mo-zz edges docking to Au <110> steps on the (111) surface. Thereby, the ribbons terminated with Mo-zz edges along the Au <110> steps (on one side) and terminated with free S-zz edges on the terraces (on the other side) should be more preferentially evolved. The schematic diagram in Fig. 1e depicts the shape evolutions of MoS2 from triangles to isosceles trapezoid or quasi stripes with the change of S/Mo ratios.
Controllable growth of uniformly aligned monolayer TMDs ribbons
According to our theoretical calculations, the following mechanism is proposed for the formation of unidirectionally oriented monolayer MoS2 ribbons. As schematically illustrated in Fig. 2a, MoS2 species tend to first nucleate at the step edges on the high-miller-index Au facets, considering of the high binding energy between them. Under a relatively small S/Mo ratio, the growth rate of S-zz edge was slower than that of Mo-zz edge, inducing the formation of MoS2 ribbons terminated by Mo-zz and S-zz edges on either side.
As evidenced by scanning electron microscopy (SEM) images (Fig. 2c), the derived MoS2 ribbons are uniformly distributed on the Au(223) facet with unidirectional alignment. These monolayer MoS2 ribbons present straight edges, totally distinct from the sawtooth-like edged nanoribbons stringed by triangular domains (grown on β-Ga2O3 (100))13. Moreover, the widths and lengths of the obtained MoS2 ribbons are tunable within 20‒120 nm and 3‒30 um, respectively (Supplementary Fig. 8). Their aspect ratios (102‒103) are much larger than most of the TMDs ribbons reported previously (10‒102)11,12,13,30,31,35,36 (Supplementary Table 1). AFM characterization of a typical MoS2 ribbon shows a thickness of ~0.7 nm, again confirming its monolayer nature (Supplementary Fig. 9).
Raman and photoluminescence (PL) spectra were then collected from the monolayer MoS2 ribbons transferred on SiO2/Si substrates. The Raman characteristic peaks are fixed at ~386 cm−1 (E12g) and 406 cm−1 (A1g) (Fig. 2d), with a frequency difference (Δ) ~20 cm−1, justifying the monolayer nature of the MoS2 ribbons37. However, the Raman intensity of the ribbon edge is slightly lower than that of the center region (Fig. 2e), probably due to the reduced electron density at the ribbon edge. Meanwhile, the PL spectrum from the ribbon edge exhibits a blue-shifted peak (at ~677 nm) and lower intensity (Fig. 2g) relative to the center region (at ~684 nm), which may arise from the strain at the ribbon edge38,39.
More intriguingly, such step-edge-guided growth of monolayer MoS2 ribbons was also realized on monolayer graphene or h-BN-covered vicinal Au(111) facets. As shown in Fig. 2i, well-aligned monolayer MoS2 ribbons occurred on a monolayer graphene-coated Au(213) facet, as confirmed by the coexistence of characteristic Raman signals for monolayer MoS2, i.e., E 12g (~386 cm−1) and A1g (~406 cm−1) peaks, and graphene on the same region (Supplementary Fig. 10). Besides, patterned monolayer MoS2 ribbons were also achieved on the monolayer h-BN/Au(111) template (Supplementary Fig. 11). The compatibility of Au substrate with the growth of TMDs, graphene, and h-BN makes it possible to construct van der Waals heterostructures based on these 2D layered materials.
Apart from monolayer MoS2, monolayer TMDs alloys ribbons, such as MoSxSe2–x, were also achieved on an Au(235) facet by using mixed S and Se as chalcogen precursor (Fig. 2k). Raman spectrum (inset of Fig. 6g) shows two groups of characteristic peaks, in line with that of MoS2 (at ~386 and 405 cm−1) and MoSe2 (at ~270 cm−1), justifying the formation of MoSxSe2–x compounds40. Given these facts, the substrate-step-edge guided growth route can be utilized as a universal pathway for the growth of TMDs ribbons and their alloys.
Preparation of inch-scale high-miller-index Au single-crystal films
The key point of this synthetic route relies on the preparation of anisotropic substrate of vicinal Au(111) single-crystal facets. To achieve this, Au foils on W templates were melted and resolidified at ~1100 °C and maintained for ~20 min. The schematic and photograph of a representative Au film (with a size of 3 cm × 3 cm) featured with Au(223) facet are presented in Fig. 3a, b, respectively. The facet surface was characterized by uniformly distributed, parallel bunched steps, as evidenced by the AFM image in Fig. 3c. X-ray diffraction (XRD) pattern of the as-prepared Au/W film shows the (111) peaks of Au film, and the (200) and (211) peaks of W foil (Fig. 3c).
However, due to the limited resolution of XRD, it is difficult to distinguish the exact miller-index of the Au facet. Further electron backscatter diffraction (EBSD) characterization reveals the evolution of such a single-crystal Au(223) facet (Fig. 3d). Large-area EBSD maps collected on the whole sample surface show uniform color contrast and nearly undetectable angular variation (Supplementary Fig. 12), confirming the single crystallinity of the Au(223) facet. Notably, a series of single-crystal Au(111) vicinal facets were also achieved through the current annealing process, including (235), (213), (346), (456), etc. (Fig. 3d and Supplementary Fig. 13), as defined by the homogeneous color contrasts in the inverse pole figure maps.
The derived high-miller-index Au facets belong to a category of facets vicinal to Au(111), which are composed of a regular succession of (111) terraces separated by monatomic steps. Notably, the appearance of a specific high-index facet is relatively random, as similarly proposed in the preparation of atomic sawtooth high-miller-index Au facets through different annealing processes21. Herein, the formation of the high-index facet is probably due to the close contact between Au liquid and W template at high temperature, in which the strain energy should be the driving force, rather than the surface energy for the formation of Au(111). This phenomenon was also reported in the preparation of high-miller-index single-crystal Cu foils, in which the stress on Cu foil was introduced by using graphite susceptor41. Notably, a variety of vicinal Au(111) facets, independent of the specific index (e.g., Au(456), Au(346)), were all proved to be capable of inducing the formation of monolayer MoS2 ribbon arrays (Fig. 3e, f). Besides, the as-grown monolayer MoS2 ribbon presents a relatively high density on the high-miller-index Au facet with a high density of step (Supplementary Fig. 14). This provides an effective route for ribbon density regulation.
Monolayer TMDs single-crystal films merged by 1D ribbons
The lateral growth and merging behavior of monolayer TMDs ribbons were then investigated by deliberately increasing the coverage. As shown in Fig. 4b‒d, upon extending the growth time from 2, 4 to 6 min, monolayer MoS2 ribbons with average widths of ~130 and ~190 nm, and continuous full-coverage MoS2 film were achieved on the Au(223) facet steadily. In this regard, the growth should obey a step-flow growth mode, inducing the formation of single-crystal film through the merging of unidirectionally aligned grains. The single crystallinity of the monolayer film was first verified by low-energy electron diffraction (LEED) measurements. The obtained diffraction spots indicate the existence of MoS2 on the high-index Au(223) stepped surface (indicated by red circles in Fig. 4e) and Au(111) terraced substrate (yellow circles). The uniform diffraction pattern that appeared on the inch-scale sample should indicate the epitaxial growth of monolayer MoS2 single crystal on the Au(223) facet (Fig. 4f and Supplementary Fig. 15).
TEM and scanning transmission electron microscopy (STEM) characterizations were then conducted to identify the lattice orientation and edge structure. A representative atomically resolved STEM image presents well-ordered honeycomb lattices (Fig. 4h). On large scales, the crystal lattice of MoS2 maintains the same orientation, showing almost no obvious grain boundary. Selected-area electron diffraction (SAED) patterns collected on the film (Supplementary Fig. 16) reveal nearly identical lattice orientation (deviation smaller than ±0.1°), highly indicative of the single-crystal nature of the MoS2 film. Moreover, the edge types on both sides of the monolayer MoS2 ribbon are identified as Mo-zz and S-zz edges from both SAED pattern (Supplementary Fig. 17) and atomic-resolution STEM image (Fig. 4i), and this result is consistent with our previous calculations. Dark-field TEM images of the monolayer MoS2 film show uniform intensity over the entire area, again confirming its single crystallinity (Supplementary Fig. 18).
On-site scanning tunneling microscopy (STM) measurements were then performed to determine the crystalline quality. A large-area STM image reveals the covering of a continuous monolayer MoS2 film on the Au(111) terraces (Fig. 5a). Further magnified image (from the region marked by the green square in Fig. 5a) presents the evolution of a large-area hexagonally shaped moiré pattern with a period of ∼3.21 ± 0.10 nm (Fig. 5b). Moreover, the orientation of the MoS2 atomic row aligns well with the moiré row direction (as denoted by green and yellow arrows, respectively). This alignment was also confirmed by the corresponding 2D fast Fourier transform image (inset of Fig. 5b), indicating an epitaxial relationship between them. As calculated, the moiré supercell (highlighted by a white rhombus) is in line with a (10 × 10) supercell of MoS2 (a1 = 0.320 nm) on an (11 × 11) supercell of Au(111) (a2 = 0.288 nm). Furthermore, atomic-resolution STM images collected from the entire film show the same lattice orientation (Fig. 5b‒d and Supplementary Fig. 19), highly indicating the single-crystal nature of the monolayer MoS2 film.
Further photograph and optical microscopy (OM) images reveal homogenous color contrasts for the 1-inch single-crystal MoS2 film transferred on SiO2/Si (Fig. 5e). Additional Raman and PL intensity mappings also suggest the homogeneous optical properties (Fig. 5f, g). Moreover, almost no obvious contrast difference can be noticed in the second-harmonic generation intensity mapping (Fig. 5h), which unambiguously confirms the single crystallinity of the monolayer MoS2 film.
Syntheses of other monolayer TMDs ribbon arrays
To further display the universality of our synthetic strategy, other TMDs ribbons and alloys, such as WS2, MoSe2, WSe2, and MoSxSe2-x were also synthesized on the high-miller-index facets vicinal to Au(111) (Fig. 6a‒h), by using MO3 (M = Mo, W) and S, Se as precursors. Corresponding Raman data and STEM image confirm the desired chemical composition and monolayer nature of the ribbons.
The ready access to monolayer TMDs ribbons provides us an opportunity for exploring their exotic electronic and catalytic performances. In order to characterize their electronic properties, back-gated FETs were constructed for MoS2 ribbons on SiO2/Si substrates (Fig. 6i). The transfer (Supplementary Fig. 20) and output curves (Fig. 6j) of a representative device show typical n-type transfer characteristics. Statistical data measured on these FETs (Supplementary Fig. 21) show a narrow electron mobility distribution 7‒11 cm2 V−1 s−1 and an on/off ratio of 105‒106, comparable to the performance of 2D MoS2 monolayers achieved on Au substrates20. Notably, the performance of the FETs based on monolayer MoS2 grown on Au are not as good as those of monolayer MoS2 films grown on sapphire16,28,42. This may originate from the different sample transfer processes used for them (e.g., electrochemical bubbling transfer), wherein contamination and structural defects were usually introduced. Hereby, a more efficient and clean sample transfer process should be developed in the future.
Besides the potential application as channel material, monolayer MoS2 ribbon was also predicted to possess higher catalytic performance in HER than its 2D counterpart, owing to the exposure of more abundant active edge sites. The applications of 1D monolayer MoS2 ribbons and 2D monolayer MoS2 flakes grown on Au/W substrates are also addressed as electrocatalysts in HER (Fig. 6k). The overpotential (at a current density of 10 mA cm−2) and Tafel slope of monolayer MoS2 ribbons were measured to be ~194 mV and 56 mV dec−1, respectively, obviously lower than the values for 2D MoS2 flakes (~220 mV and 71 mV dec−1) (Fig. 6l and Supplementary Fig. 22). Moreover, the catalytic current density exhibited negligible loss (<5%) after 1000 cycles, indicating the relatively high catalytic stability. The loading of the catalysts can be further increased toward low-cost, high-efficiency, and large-scale application explorations.
Discussion
In conclusion, we have realized the direct synthesis of periodic monolayer TMDs ribbon arrays, and wafer-scale TMDs single crystals on high-miller-index Au facets vicinal to (111) via a designed step-edge-directed synthetic strategy. Monolayer TMDs ribbons characterized by strictly monolayer thickness, high aspect ratio, relatively straight edge, and uniform alignment have been achieved. Based on this, an alternative epitaxial growth approach for wafer-scale TMDs single crystals is proposed by merging these uniformly aligned monolayer ribbons through a unique 1D edge-epitaxy mode. This work hereby opens a pathway for the single-crystal growth of 2D semiconductors on a wafer scale, as well as deepens our understanding of the epitaxial growth mechanism for the wafer-scale synthesis of 2D layered materials on insulating or conducting templates. This work should also propel the application explorations of monolayer TMDs ribbons or single crystals as channel materials in nanoelectronics and efficient catalysts in energy-related fields.
Methods
Preparation of vicinal Au(111) single crystals
The commercial polycrystalline gold foils (99.99%, ~50 µm thickness) were first ultrasonic cleaned in HCl solution (20% wt) for 10 min, and then in an acetone solution for 10 min. To prepare the high-miller-index facets vicinal to Au(111), a piece of cleansed gold foil was placed on an etched tungsten foil on a graphite boat, annealing at ~1100 °C for 20 min with a mixture of Ar/H2 (300/50 sccm) as the carrier gas. The gold will firstly melt into liquid at ~1100 °C, and resolidified to induce the formation of Au(111) vicinal facets after cooling down processes.
Synthesis of monolayer TMDs ribbons
For the growth of MoS2 ribbons, the MoO3 and S powders were placed in the upstream of Au(111)/W substrate at a distance of 4 and 20 cm in a three-zone tube furnace, respectively. The growth was performed in a low-pressure environment with the protection of Ar (50 sccm) gas. The typical temperatures of S, MoO3 (2‒3 mg), and Au(111) substrates were ~100, ~530, and ~750 °C, respectively. The S/Mo ratio was defined by the quantity of S and MoO3 precursors. Notably, this growth temperature was relatively higher than that used for the growth of triangular monolayer MoS2 domains (~720 °C) in our previous work20.
For the growth of monolayer WS2 ribbons, the typical temperatures of S, WO3, and Au substrates were set at ~100, 820, and 820 °C, respectively. For the growth of 1D monolayer MoSe2 and WSe2 ribbons, a mixture of Ar (50 sccm) and H2 (5 sccm) was used as the carrier gas. The Se powder was placed in the upstream of a substrate at a distance of 16 cm. The typical temperatures for Se, MoO3 (WO3), and Au substrates were set at ~200, 530 (820), 820 °C, respectively. For the synthesis of monolayer MoSxSe2–x ribbons, the MoO3 precursor and a mixed S and Se precursor were placed in the upstream of Au/W substrate at a distance of 1 and 20 cm, respectively. The typical temperatures for the Au substrates, MoO3, and S/Se mixture were set at 850, 800, and 200 °C, respectively. The growth process was performed under a mixture flow of Ar (50 sccm) and H2 (5 sccm) gases. The synthetic recipes for MoS2 ribbons grown on graphene and h-BN monolayers are provided in the Supplementary information.
Calculation methods
The theoretical calculations based on DFT were performed by the Vienna ab initio simulation package43. Details of calculations are provided in the Supplementary information.
Characterization of MoS2 ribbons
The MoS2 ribbons and single crystals were systematically characterized by SEM (Hitachi S-4800, 2 kV), OM (Nikon ECLIPSE, LV100ND), Raman and PL spectroscopy (Horiba Jobin-Yvon, LabRAM HR800, with an excitation wavelength of 532 nm), spectral imaging (WITec, Alpha 300R), AFM (Bruker, Dimension Icon), XPS (Kratos Analytical Ltd. AXIS-Ultra with monochromatic Al Ka X-ray), TEM (FEI Tecnai F20, acceleration voltage of 200 kV), STEM (JEOL ARM200F, acceleration voltage 80 kV), and STM (Omicron, the base pressure: 10−10 mbar). The LEED measurements were carried out in an ultra-high vacuum (3 × 10−10 Torr) and the electron energy was fixed at 96 eV. The electron beam spot size is about 500 μm. The single-crystal Au(111) vicinal facets were characterized by XRD (Bruker D8-Discover, with a Cu Kα radiation source) and EBSD (Oxford instruments).
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Cai, Z., Liu, B., Zou, X. & Cheng, H. M. Chemical vapor deposition growth and applications of two-dimensional materials and their heterostructures. Chem. Rev. 118, 6091–6133 (2018).
Liu, Y. et al. Promises and prospects of two-dimensional transistors. Nature 591, 43–53 (2021).
Acerce, M., Akdoan, E. K. & Chhowalla, M. Metallic molybdenum disulfide nanosheet-based electrochemical actuators. Nature 549, 370–373 (2017).
Lin, J. et al. Flexible metallic nanowires with self-adaptive contacts to semiconducting transition-metal dichalcogenide monolayers. Nat. Nanotechnol. 9, 436–442 (2014).
Li, Y. et al. Plasmonics of 2D nanomaterials: properties and applications. Adv. Sci. 4, 1600430 (2017).
Li, Y., Zhou, Z., Zhang, S. & Chen, Z. MoS2 nanoribbons: high stability and unusual electronic and magnetic properties. J. Am. Chem. Soc. 130, 16739–16744 (2008).
Padmajan Sasikala, S. et al. Longitudinal unzipping of 2D transition metal dichalcogenides. Nat. Commun. 11, 5032 (2020).
Cai, Y., Zhang, G. & Zhang, Y. W. Polarity-reversed robust carrier mobility in monolayer MoS2 nanoribbons. J. Am. Chem. Soc. 136, 6269–6275 (2014).
Liu, X. et al. Top-down fabrication of sub-nanometre semiconducting nanoribbons derived from molybdenum disulfide sheets. Nat. Commun. 4, 1776 (2013).
Li, X. et al. Realizing the intrinsic anisotropic growth of 1T′ReS2 on selected Au(101) substrate toward large-scale single crystal fabrication. Adv. Funct. Mater. 31, 2102138 (2021).
Li, S. et al. Vapour-liquid-solid growth of monolayer MoS2 nanoribbons. Nat. Mater. 17, 535–542 (2018).
Chowdhury, T. et al. Substrate-directed synthesis of MoS2 nanocrystals with tunable dimensionality and optical properties. Nat. Nanotechnol. 15, 29–34 (2020).
Aljarb, A. et al. Ledge-directed epitaxy of continuously self-aligned single-crystalline nanoribbons of transition metal dichalcogenides. Nat. Mater. 19, 1300–1306 (2020).
Yu, H. et al. Wafer-scale growth and transfer of highly-oriented monolayer MoS2 continuous films. ACS Nano 11, 12001–12007 (2017).
Ji, Q. et al. Epitaxial monolayer MoS2 on mica with novel photoluminescence. Nano Lett. 13, 3870–3877 (2013).
Wang, Q. et al. Wafer-scale highly oriented monolayer MoS2 with large domain sizes. Nano Lett. 20, 7193–7199 (2020).
Lee, J. S. et al. Wafer-scale single-crystal hexagonal boron nitride film via self-collimated grain formation. Science 362, 817–821 (2018).
Wang, L. et al. Epitaxial growth of a 100-square-centimetre single-crystal hexagonal boron nitride monolayer on copper. Nature 570, 91–95 (2019).
Chen, T. A. et al. Wafer-scale single-crystal hexagonal boron nitride monolayers on Cu (111). Nature 579, 219–223 (2020).
Yang, P. et al. Epitaxial growth of centimeter-scale single-crystal MoS2 monolayer on Au(111). ACS Nano 14, 5036–5045 (2020).
Choi, S. H. et al. Epitaxial single-crystal growth of transition metal dichalcogenide monolayers via the atomic sawtooth Au surface. Adv. Mater. 33, 2006601 (2021).
Li, J. et al. Single-crystal MoS2 monolayer wafer grown on Au (111) film substrates. Small 17, 2100743 (2021).
Chen, L. et al. Step-edge-guided nucleation and growth of aligned WSe2 on sapphire via a layer-over-layer growth mode. ACS Nano 9, 8368–8375 (2015).
Chubarov, M. et al. Wafer-scale epitaxial growth of unidirectional WS2 monolayers on sapphire. ACS Nano 15, 2532–2541 (2021).
Li, T. et al. Epitaxial growth of wafer-scale molybdenum disulfide semiconductor single crystals on sapphire. Nat. Nanotechnol. 16, 1201–1207 (2021).
Wang, J. et al. Dual-coupling-guided epitaxial growth of wafer-scale single-crystal WS2 monolayer on vicinal a-plane sapphire. Nat. Nanotechnol. 17, 33–38 (2021).
Xu, H. et al. Controllable synthesis of 2D and 1D MoS2 nanostructures on Au surface. Adv. Funct. Mater. 27, 1603887 (2017).
Xia, B. Y. et al. One-dimensional nanostructures: synthesis, characterization, and applications. Adv. Funct. Mater. 15, 353–389 (2003).
Pan, Z., Liu, N., Fu, L. & Liu, Z. Wrinkle engineering: a new approach to massive graphene nanoribbon arrays. J. Am. Chem. Soc. 133, 17578–17581 (2011).
Xu, H. et al. Oscillating edge states in one-dimensional MoS2 nanowires. Nat. Commun. 7, 12904 (2016).
Chen, Y. et al. Fabrication of MoSe2 nanoribbons via an unusual morphological phase transition. Nat. Commun. 8, 1–9 (2017).
Zhao, X. et al. Mo-terminated edge reconstructions in nanoporous molybdenum disulfide film. Nano Lett. 18, 482–490 (2018).
Van Der Zande, A. M. et al. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 12, 554–561 (2013).
Cong, C. et al. Synthesis and optical properties of large-area single-crystalline 2D semiconductor WS2 monolayer from chemical vapor deposition. Adv. Opt. Mater. 2, 131–136 (2014).
Han, Y. et al. Sub-nanometre channels embedded in two-dimensional materials. Nat. Mater. 17, 129–133 (2018).
Zhu, C. et al. Strain-driven growth of ultra-long two-dimensional nano-channels. Nat. Commun. 11, 772 (2020).
Shi, J. et al. Controllable growth and transfer of monolayer MoS2 on Au foils and its potential application in hydrogen evolution reaction. ACS Nano 8, 10196–10204 (2014).
Liu, Z. et al. Strain and structure heterogeneity in MoS2 atomic layers grown by chemical vapour deposition. Nat. Commun. 5, 5246 (2014).
Ago, H. et al. Visualization of grain structure and boundaries of polycrystalline graphene and two-dimensional materials by epitaxial growth of transition metal dichalcogenides. ACS Nano 10, 3233–3240 (2016).
Li, H. et al. Lateral growth of composition graded atomic layer MoS2(1– x) Se2x nanosheets. J. Am. Chem. Soc. 137, 5284–5287 (2015).
Li, Y. et al. Large single-crystal Cu foils with high-index facets by strain-engineered anomalous grain growth. Adv. Mater. 32, 2002034 (2020).
Sebastian, A. et al. Benchmarking monolayer MoS2 and WS2 field-effect transistors. Nat. Commun. 12, 693 (2021).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Acknowledgements
The work was supported by the National Key Research and Development Program of China (Nos. 2021YFA1202901, P.Y., W.Q., J.H., L.Z., S.P., Y.S., Y.H., F.C., Y.F., 2018YFA0703700, P.Y., Y. F.), the National Natural Science Foundation of China (Nos. 51991344, P.Y., Y.F., 51991340, P.Y., Y.F., 51925201, P.Y., Y.F., 52021006, P.Y., Y.F., 61775006, X.L., B.T., Q.C., U1632266, Q.J., S.Q., 11927807, Q.J., S.Q.), the Beijing Natural Science Foundation (No.2192021, P.Y., Y.F.), Guangdong Innovative and Entrepreneurial Research Team Program (No. 2017ZT07C341, D.W., Xiaolong Zou) and the Bureau of Industry and Information Technology of Shenzhen for the 2017 Graphene Manufacturing Innovation Center Project (No. 201901171523, D.W., Xiaolong Zou). Xiaoxu Zhao thanks the support from the Presidential Postdoctoral Fellowship, Nanyang Technological University, Singapore via grant 03INS000973C150. Z.L. thanks the support from the Ministry of Education, Singapore, under its AcRF Tier 3 Programme “Geometrical Quantum Materials” (MOE2018-T3-1-002). The authors would like to acknowledge the Facility for Analysis, Characterization, Testing, and Simulation, Nanyang Technological University, Singapore, for use of their electron microscopy.
Author information
Authors and Affiliations
Contributions
P.Y. and Y.Z. conceived the idea and wrote the paper. D.W. and Xiaolong Zou performed the theoretical calculations and participated in the paper writing. Xiao Zhao and Z.L. performed the scanning transmission electron microscopy (STEM) experiments. W.Q. and S.P. did the scanning tunnel microscope (STM) characterizations. Q.J. and S.Q. carried out the low-energy electron diffraction (LEED) analysis. X.L., B.T., and Q.C. fabricated the devices and performed the electrical measurements. J.H., L.Z., Y.S., Y.H., and F.C. reviewed and edited the manuscript. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Ang-Yu Lu and the other anonymous reviewers for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, P., Wang, D., Zhao, X. et al. Epitaxial growth of inch-scale single-crystal transition metal dichalcogenides through the patching of unidirectionally orientated ribbons. Nat Commun 13, 3238 (2022). https://doi.org/10.1038/s41467-022-30900-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-30900-9
- Springer Nature Limited
This article is cited by
-
Quasi-equilibrium growth of inch-scale single-crystal monolayer α-In2Se3 on fluor-phlogopite
Nature Communications (2024)
-
Phase-engineered synthesis of atomically thin te single crystals with high on-state currents
Nature Communications (2024)
-
Radiationless optical modes in metasurfaces: recent progress and applications
Light: Science & Applications (2024)
-
Towards the scalable synthesis of two-dimensional heterostructures and superlattices beyond exfoliation and restacking
Nature Materials (2024)
-
1T′-transition metal dichalcogenide monolayers stabilized on 4H-Au nanowires for ultrasensitive SERS detection
Nature Materials (2024)