Abstract
Experiments have shown that graphene-supported Ni-single atom catalysts (Ni-SACs) provide a promising strategy for the electrochemical reduction of CO2 to CO, but the nature of the Ni sites (Ni-N2C2, Ni-N3C1, Ni-N4) in Ni-SACs has not been determined experimentally. Here, we apply the recently developed grand canonical potential kinetics (GCP-K) formulation of quantum mechanics to predict the kinetics as a function of applied potential (U) to determine faradic efficiency, turn over frequency, and Tafel slope for CO and H2 production for all three sites. We predict an onset potential (at 10 mA cm−2) Uonset = −0.84 V (vs. RHE) for Ni-N2C2 site and Uonset = −0.92 V for Ni-N3C1 site in agreement with experiments, and Uonset = −1.03 V for Ni-N4. We predict that the highest current is for Ni-N4, leading to 700 mA cm−2 at U = −1.12 V. To help determine the actual sites in the experiments, we predict the XPS binding energy shift and CO vibrational frequency for each site.
Similar content being viewed by others
Introduction
Fossil fuels have been the primary source to produce energy for industrial applications and human activities for decades1,2, leading to high concentration of atmospheric CO2 that create serious environmental, ecological, and climate problems. It is now essential to find improved catalysts to convert CO2 to useful chemicals3. Indeed progress is being made in electrochemical transformation of CO2 into chemical fuels4,5, however, the extreme stability of CO2 makes it inert for chemical reactions in aqueous solution, demanding a large overpotential to overcome the high activation barrier. Moreover, the hydrogen evolution reaction (HER) side reaction can easily dominate under the same conditions, diminishing efficiency6,7,8. Thus we want CO2 reduction catalysts with high faradic efficiency for CO but negligible HER faradic efficiency. The column 11 elements (IB group) (Cu, Ag, Au) and their alloys provide the best catalysts to date9,10,11,12,13,14, however, poor selectivity and stability limit their use in practical applications that which require high activity, excellent selectivity, and long-term stability. In recent years, single atom catalysts (SACs) have emerged as an effective strategy to create new electrocatalysts with maximal atomic efficiency and high selectivity for specific catalytic reactions15,16,17,18. Atomically dispersed metals on suitable substrates have demonstrated unique electronic properties with great potential for electrocatalytic CO2 reduction19,20,21. In particular, graphene, a single atomic layer of carbon, has proved to be an effective support. It has large surface area, high conductivity, high stability, and the capability to tune electronic properties by forming strong chemical bonds to guest atoms22,23,24. Several experimental studies have been published recently on the CO2 reduction reaction (CO2RR) for the nickel single atom catalysts (Ni–SACs) on graphene20,21,25,26,27,28,29, but the performance varies markedly perhaps because of differences in the number of carbon or nitrogen bonds to Ni.
Recent developments in quantum mechanics (QM) based methods provide new tools determine the reaction mechanisms for heterogeneous electrochemical reactions. Recently we extended the standard fixed electron QM to allow constant potential Grand Canonical QM (GC-QM) to describe the kinetics at fixed potential (U) for direct comparison to experiment30. In particular, we recently developed the grand canonical potential kinetics (GCP-K) method to combine fixed charge and fixed potential QM to allow the reaction barriers to change continuously as the applied potential is changed, leading directly to current versus potential relation (Tafel slope)31.
Here we report the application of GCP-K to predict the reaction mechanism and rates for CO2RR over Ni–SACs for the Ni–N2C2, Ni–N3C1, and Ni–N4 sites in graphene. We find that Ni–N2C2 leads to the lowest onset potential of −0.84 V (vs RHE) to achieve 10 mA cm−2 current density, leading to a Tafel slope of 52 mV dec−1 and a turn-over frequency (TOF) of 3903 h−1 per Ni site at neutral (pH 7) electrolyte conditions, showing best agreement with various experimental observations at lower overpotentials. We predict the onset potential for 10 mA cm−2 current density of −0.92 V for Ni–N3C1 and −1.03 V for Ni–N4 (which exhibits the highest saturation current for high applied potentials). We use quantum mechanics to predict the binding energy (BE) shift for the N and C 1s X-ray photoelectron spectroscopy (XPS) and the CO vibrational frequencies to help interpret the experimental nitrogen coordinations in Ni–SACs. We predict that the N 1s BE shift ranges from +1.18 to +0.96 eV for Ni–N4 and Ni–N2C2 respectively. The adsorbed CO intermediate vibrations range from 1985 cm−1 (perpendicular) at −1.0 V on Ni–N2C2 site to 1942 cm−1 in the xz plane at −1.25 V applied potential on the Ni–N4 site.
Results
Grand canonical potential kinetics formulation
Recently, we developed the GCP-K methodology to determine the kinetics for heterogenous electrochemistry as a function of applied potential while allowing the transition states to evolve continuously31. GCP-K uses a Legendre transformation to convert from fixed charge free energy, F (n), to grand canonical, G (n; U), allowing the thermodynamic free energy for heterogeneous electrochemical reactions to depend on the applied potential (U). The derivation starts with the general definition of the grand canonical potential32,33,34
where G is the grand canonical free energy, which depends on the number of electron (n), applied potential (U vs SHE), total free energy (F) as a function of n, and electronic energy (\(U_{{\mathrm{SHE}}} = \mu _{e,{\mathrm{SHE}}}\)/e) at the standard hydrogen electrode (SHE) condition. The sign of U is defined as the potential used in experiments, i.e., U = −0.5 V corresponds to −0.5 V vs SHE. We calculate how the number of electrons depends on the applied potential to obtain G (n;U) as a thermodynamic potential. To do this, we shift the Fermi level to correspond to the applied potential by changing the electronic band occupation, varying the number of electrons in the systems (Eq. 2)35,36. Finally, we obtain GCP (U) through minimizing G (n;U) according to (3)37,38
Approximating F(n) locally as quadratic and minimizing G (n;U) leads to a quadratic form in GCP (U). This quadratic dependence is consistent with the relevant empirical forms from other studies39,40,41. To obtain GCP (U) we fit a quadratic expansion of F(n):
where a, b, and c are determined from QM. Minimization of (4) (Supplementary Table 1–5) leads to Eq. (5).
These parameters can be related to the physical quantities as follows,
First, the differential capacitance, \(C_{{\mathrm{diff}}} = \frac{{\partial n}}{{\partial U}} = - \frac{1}{{2a}}{\mathrm{which}}\,{\mathrm{leads}}\,{\mathrm{to,}}\,{\mathrm{a}} = - \frac{1}{{2C_{{\mathrm{diff}}}}}\)
Second, at the potential of zero charge, \(n\left( {U_{{\mathrm{PZC}}}} \right) = n_0\), so we obtain
Thus, we can write, \(b = {\mathrm{\mu }}_{e,{\mathrm{SHE}}} - eU_{{\mathrm{PZC}}}\)
Finally, \(F\left( {n = n_0} \right) = c\), when the system is neutral, the potential of zero charge (UPZC).
Putting these physical quantities into Eqs. (4) and (5), we write the grand canonical potential and free energy expressions (Supplementary Notes 1) as in Eqs. (6) and (7)
where, \(n_0\) is the number of electrons at zero net charge (total number of valence electron), \(\mu _{e,{\mathrm{SHE}}}\) is the chemical potential of an electron vs standard hydrogen electrode (SHE), and e is the energy in eV. This quadratic form of free energy F(n) and grand canonical potential GCP (U) accounts for the change in capacitance as the potential changes.
Our procedure is first to carry out QM for a range of fixed charges using VASPsol solvation. Then we use the CANDLE solvation model implemented in jDFTx to obtain the free energies at the same constant charge. Then we recalculate the constant potential free energies using the Legendre transform. For stable intermediates the optimized geometry from VASPsol is used. For transition states we use the above procedure for each point along the climbing image nudged elastic band (CI-NEB) surface so that the transition state adjusts properly as the potential is changed.
Structural model of Ni–SACs for CO2 reduction reaction
Experimental studies show that adding a Ni2+ containing metal solution to N-doped graphene oxide solution and then annealing at high temperature leads to electrocatalysts with Ni-nitrogen/carbon moieties embedded within the graphene matrix. The central Ni atom is coordinated to nitrogen/carbon(s) through strong covalent bonding, making this a single atom catalyst embedded within the graphene matrix. Each Ni may be bonded to 2 to 4 N’s atom along with 2–0 C’s, which we denote as Ni–N2C2, Ni–N3C1, or Ni–N4 (refs. 16,27,42). Our calculated formation energies show that Ni–N4 is energetically most favorable (−1.13 eV) while Ni–N2C2 structure (1.04 eV) is the least favorable. We examine here CO2RR considering all three possible structures and compare their catalytic performance.
The reduction process of CO2 into CO involves two major steps, each involving a net transfer of one electron as the reactant is transformed to product (Fig. 1). We consider all three cases of Ni–N4−xCx (x = 0–2) as possible configurations of Ni–SAC, embedded in a 4 × 4 periodic super cell of graphene, as shown in Fig. 1a, b. We examined the Eley-Rideal (ER) mechanism43 for CO2 reduction, where water from solution reacts with an adsorbed CO2 molecule to form *COOH and OH− in solution. We start with one CO2 physisorbed on the single Ni sites including three explicit water molecules plus implicit solvation of this entire surface (Fig. 1c). As we apply a negative potential, the system builds up negative charge at the surface that induces linear CO2 to bend slightly on Ni–SAC. This bent CO2 facilitates a proton transfer from water to form the COOH intermediate, which binds strongly to the central Ni atom with Ni–C = 1.98–1.94 Å for various surface charges of 0–1.5 (a positive value represents excess electron compared to neutral, n − n0). This proton comes from a neighboring explicit water to form either cis-COOH (with the H pointing up) or trans-COOH (with the H pointing down). Simultaneously, product OH− forms, stabilized by two other explicit water molecules (optimized) plus the implicit solvation, as shown in Fig. 1d, e respectively.
Figure 1f–i shows the second step of dehydroxylating the adsorbed COOH species by an explicit water to produce CO product plus H2O and OH− (stabilized by water molecules and implicit solvent). The CO affinity on these Ni–SAC sites depends on the number of N’s bonded to the Ni, but none have a strong affinity for CO species (unlike Ni metal catalysts)44,45. Our calculations show that Ni-N4 has the least affinity for CO (Ni–CO bond distance ~2.53–2.27 Å), leading to tilted adsorbed CO (\({\mathrm{\angle OCNi}} = 116^\circ\)) (Fig. 1h) while Ni–N2C2 sites (Fig. 1i) show relatively stronger affinity toward CO (Ni–CO distance from 1.80 to 1.92 Å) and CO adsorbed almost linearly. This adsorbed CO desorbs from the Ni site along a straight pathway (\({\mathrm{\angle OCNi}} = 176.5^\circ\)) to slightly tilted (\({\mathrm{\angle OCNi}} = 152^\circ\)) depending on the applied potentials. The Ni–N3C1 site shows adsorption intermediate between Ni–N2C2 and Ni–N4 sites (Supplementary Data 1).
The quadratic behavior of the grand canonical potential was examined thoroughly for the whole process. The dependence for the trans-COOH reaction on applied potential is shown in Fig. 2. Figure 2a shows that the free energy, F(n) obtained from the CANDLE implicit solvation method, correlates linearly with system charge. However, subtracting the free energy contribution of each electron at SHE leads to the quadratic dependence shown in Fig. 2b, according to Eq. (6) leading to Eq. (8),
Figure 2b shows that the optimum charge is slightly negative. Thus, at zero potential, the intermediate has a little more extra charge than the neutral. In electrochemical conditions, applying a negative potential, U, shifts the free energy minimum of G (n, U) by neU in Eq. (8). Figure 2c shows that this shifts the minimum of G (n, U) toward higher charge (the case of U = −0.8 V is shown Fig. 2c), which drives the reaction toward the product containing more charge.
Transition states change as a function of applied potential
We first carried out constant charge DFT and then transformed the free energies to obtain GCP (U), leading to transition states (TS) exactly equivalent with the results from constant potential calculations (as shown in our earlier work using the minimax theorem)31,46. The free energy of the transition state, FTS(n) obtained from the fixed charge (n) calculation is transformed into the grand canonical potential GCPTS,n (U) via a Legendre transformation. Since the transition state is the highest barrier along the minimum energy path (MEP), the TS geometry changes with applied potential, U.
Figure 3 shows how the CO2 to OCOH reaction barrier depends on the applied potential for the three types of Ni sites along the minimum energy path and transition states at U = −0.8 V vs RHE. The conversion of linear CO2 through bent CO2 to COOH is endothermic. The slightly bent state (image 02) is followed by the transfer of a H from HOH to form OCOH plus an OH− stabilized by the two H2O (images 03–04). The transition state (image 04) has a geometry similar to the *COOH intermediate but with a slightly higher energy (1.65 kcal mol−1) arising from reorientation of the bottom water molecule (Fig. 3a). This protonation step has an energy barrier shown in Fig. 3b. For Ni–N2C2, the linear CO2 (initial state) (\({\mathrm{\angle}} {\mathrm{OCO}} = 178.34^\circ\)), first becomes slightly bent (\({\mathrm{\angle}} {\mathrm{OCO}} = 167^\circ\)) at the 02 image leading to a low energy barrier (1.55 kcal mol−1 at U = −0.8 V), indicating fast decoupled electron transfer followed by proton transfer with higher energy barrier (9.24 kcal mol−1) at image 04. For Ni–N3C1, we find a 1.97 kcal mol−1 energy barrier to form slightly bent CO2 and a barrier of 17.72 kcal mol−1 to form OCOH. Finally, for Ni–N4 we find a 2.31 kcal mol−1 energy barrier to form slightly bent CO2 and a barrier of 26.97 kcal mol−1 to form OCOH at −0.8 V potential. The reaction pathways and energies for the conversion of linear CO2 to trans-COOH are shown in Supplementary Fig. 3. In contrast to step 1, the reaction pathway for conversion of cis-COOH to CO clearly involves a sharp TS and lower energy barrier at constant applied potential as shown in Fig. 4a, b. The reaction pathway shows the bond breaking between OC–OH step (image 3) has the highest energy barrier. Among all studied sites, Ni–N3C1 shows the highest barrier of 10.01 kcal mol−1 while Ni–N4 shows the lowest barrier of 7.02 kcal mol−1 at U = −0.53 V applied potential (Fig. 4b). The pathways with free energy for the formation of CO from trans-OCOH is shown in Supplementary Fig. 4.
Figure 4c–e illustrates the geometric change of the TS as a function of applied potential along the reaction path. Along the reaction path (Fig. 4a), we show two spatial coordinates: (1) distance between OC–OH in the COOH TS, which changes from 1.46 Å to 2.77 Å as U = −0.8 changes to 0 V (Fig. 4d) and (2) the distance between the new OH bond to the OH of COOH and the old OH bond of the H2O molecule donating the proton changes from 1.71 Å to 1.04 Å as U = −0.8 V changes to 0 V (Fig. 4e).
Our results show that the TS at zero applied potential is very similar to the product but as U becomes more negative, the TS moves toward the reactant, becoming similar to the reactant at U = −0.8 V (Fig. 4c). As the potential becomes more negative, the reaction barrier decreases making the path more favorable to convert reactants into products. Thus, we find the OC–OH distance decrease uniformly with U (Fig. 4d) and the COOH–H2O distance increases uniformly (Fig. 4e). The charges associated with the adsorbed species change linearly with U, leading to a smooth reaction pathway along the reaction coordinate. At zero potential, the transformation begins with a charge of 0.4 on the Ni–SACs, which increases to 1.0 as the applied potential is increased to −0.8 V. To show the linear relationship between applied potential and charges on the species more quantitatively, we compare this reaction path for the GCP-K model with the conventional Butler–Volmer PCET kinetics in Fig. 5. This shows that at potential U0, the transition state, TS0 (Fig. 5a) corresponds to the spatial geometry R0 but as the applied potential changes to U1 the transition state (TS1) moves leftward toward reactant reaching to R1 (refs. 47,48). In this grand canonical potential kinetics (GCP-K) description, the fractional charges change continuously along the reaction coordinates as the applied potential is changed, as shown in Fig. 5b, c. Initially, at zero voltage the reaction barrier is 16.89 kcal mol−1, the TS has a slightly negative charge (0.4 e) and the OC–OH distance is about 2.77 Å, very similar to the product (Fig. 4c). But as the applied potential is changed to −0.8 V, the barrier decreases continuously to 2.98 kcal mol−1 while the TS shifts continuously toward the reactant with a short (1.46 Å) OC–OH distance at a more negative charge of 1.0 e. The charge difference between the transition states at 0 V (TS0V) and −0.8 V (TS−0.8) is 0.6 e as shown in Fig. 5d, e. Thus, we describe the charge transfer as a potential dependent continuous process during the electrochemical reaction as the intermediates adsorb on the electrode surface and react along the reaction path leading to a smooth path for the reaction. Similarly, we observe a continuous change of the transition state (TS) with applied potential for the trans-COOH to CO conversion reaction for the Ni–N4 site (Supplementary Fig. 5). We also observe similar behavior for the reaction at the Ni–N2C2 and Ni–N3C1 sites. As shown above, the conversion of CO2 to COOH leads to a lower energy barrier for Ni–N2C2 and Ni–N3C1 sites than for Ni–N4. This makes the 2nd step reaction slightly less favorable for Ni–N2C2 and Ni–N3C1 sites. The conversion of cis-COOH and trans-COOH into CO on Ni–N3C1 and Ni–N2C2 involve higher energy barriers than on Ni–N4 (Supplementary Figs. 6–8).
The hydrogen evolution reaction on Ni–SACs
The hydrogen evolution reaction (HER) competes with the CO2RR, decreasing the faradic efficiency (FE) for CO evolution. HER can take place either by reducing protons (\(2{\mathrm{H}}^ + + 2{\mathrm{e}}^ - \to {\mathrm{H}}_2\)) or by reduction of water \((2{\mathrm{H}}_2{\mathrm{O}} + 2{\mathrm{e}}^ - \to {\mathrm{H}}_2 + 2{\mathrm{OH}}^ - )\) from aqueous solution via the Volmer-Tafel/Heyrovsky reaction. Thus, we must examine the comparative activity of HER and CO2RR on the same catalysts and electrolyte conditions. Since our electrolytic environment is neutral (pH 7), we considered the HER via water reduction. Therefore, there are two steps: In step 1 shows hydrogen from solvent water gradually moves toward Ni surface and finally absorbs onto the Ni site via the Volmer reaction, producing OH− solvated by the explicit H2O molecules (Fig. 6a) and step 2 involves the adsorbed hydrogen slowly combining with a second hydrogen from solution H2O to finally evolves as H2 gas via the Heyrovsky reaction (Fig. 6c). Figure 6b, d show that HER depends strongly on the number of N bonded to the Ni. Thus, at pH 7 and U = −0.8 V applied potential we find that the hydrogen adsorption on Ni–N2C2 site from solvent water involves a transition state (TS) with an energy barrier of 11.43 kcal mol−1(Fig. 6b), while it requires relatively higher energy of 15.46 kcal mol−1 to combine with a second hydrogen from water in solution to evolves as H2 gas via Heyrovsky step (Fig. 6d). On the other hand, the calculated reaction barrier for the Volmer step to put H* on the surface is 15.04 kcal mol−1 and the Heyrovsky step of forming H2, it is 9.36 kcal mol−1 on Ni–N3C1 sites. Here the H* is adsorbed on the bridge sites of the Ni–C bond (Supplementary Figs. 9–10). The bond distances of C–H and Ni–H in the bridge site position are about 1.14 and 1.80 Å, respectively. The Ni–N4 sites are least favorable for HER. The calculated reaction barrier for the Volmer step is 30.26 kcal mol−1, while the Heyrovsky step has a barrier of 6.69 kcal mol−1 at pH 7 and applied potential −0.8 V conditions (Supplementary Figs. 9–12). The Ni–N4 sites are preferred to minimize HER.
Reaction mechanism for CO2 reduction
We calculated the CO2 reduction reaction at neutral pH condition on Ni–SACs with three different Ni sites configurations: Ni–N2C2, Ni–N3C1, and Ni–N4 embedded in graphene. The reference fermi energy of the electron is shifted by pH × 0.059 eV to put the applied potential in terms of RHE. We summarize the free energy activation barriers and reaction free energies in Fig. 7a obtained using grand canonical potential GCP (U) kinetics for all possible intermediates, transition states, and products during CO2 reduction at pH 7 and −0.8 V vs RHE applied potential.
Overall, CO2 reduction on Ni–N2C2 site via the cis pathway is most favorable at U = −0.84 V, the onset potential for 10 mA cm−2 current density. But in the last step of forming CO, the bond to Ni is too strong, limiting the maximum current at more negative potentials. The CO2 conversion to cis-COOH reaction is energetically most favorable on Ni–N2C2 sites. In the first step the applied potential adds negative charge to CO2, causing it to bend. Next it reacts with a proton from a solution H2O to form cis-COOH via TS01 with a barrier of 9.24 kcal mol−1. This cis-COOH can convert back into CO2 with a small barrier (TS10) of 0.16 kcal mol−1 or it can abstract a second hydrogen from solution to form CO plus H2O and OH− with a barrier (TS13) of 6.29 kcal mol−1. This CO is strongly adsorbed on the central Ni surface; to evolve as CO gas requires a barrier (TS30) of 16.57 kcal mol−1. This desorption frees up the binding site for further reaction or it can form cis-COOH again by the back reaction with a barrier (TS31) of 7.58 kcal mol−1. On the other hand, linear CO2 is converted into trans-COOH on Ni–N2C2 sites with a barrier (TS02) of 9.96 kcal mol−1, slightly higher than cis although the reverse process has a same barrier (TS20) of 0.16 kcal mol−1 or it can react with another hydrogen from solution to form adsorbed CO with slightly lower barrier (TS23) of 5.82 kcal mol−1. This adsorbed CO is finally evolved into solution as CO gas with the same barrier (TS30) as cis, 16.57 kcal mol−1, leaving an empty catalyst surface or it can convert into trans-COOH by back reaction with high barrier (TS32) of 7.58 kcal mol−1.
Although Ni–N2C2 sites initiate the CO production at the lowest U, Ni–N3C1 dominates in the potential range of U = −0.92 V to −1.12 V, where the maximum current is limited due to strong bonding of CO to the Ni site. The conversion of CO2 to cis-COOH on the Ni–N3C1 site leads to a barrier (TS01) of 17.72 kcal mol−1, which is more uphill than Ni–N2C2 site. This reaction can be reversed with a very small barrier (TS10) of 0.90 kcal mol−1 or it can abstract a second hydrogen from solution and convert into CO with a forward barrier (TS13) of 6.65 kcal mol−1. This adsorbed CO has intermediate affinity on Ni and can evolve as CO gas with a barrier (TS30) of 10.18 kcal mol−1, leaving the Ni site vacant for further reactions or it can form cis-COOH again by the reverse reaction with a barrier (TS31) of 13.46 kcal mol−1. The conversion involving the trans-COOH intermediate on N–N3C1 sites is slightly easier than for the cis form. Here, the CO2 is converted into trans-COOH with a barrier (TS02) of 14.62 kcal mol−1, the reverse reaction to produce CO2 has a small barrier (TS20) of 1.49 kcal mol−1 or it can react with another hydrogen from solution to form adsorbed CO plus H2O and OH− with a relatively higher barrier (TS23) of 7.88 kcal mol−1 than for cis case. The adsorbed CO can evolve as CO gas with a barrier (TS30) of 10.18 kcal mol−1, leaving the active site available for next reaction or it can convert into the trans-COOH by the reverse reaction with a high barrier (TS32) of 14.67 kcal mol−1.
Ni–N4 sites produce the maximum current for CO production with higher faradic efficiency, but at higher potentials. The trans pathway provides a lower energy barrier than cis for both steps of CO production. The CO2 conversion to cis-COOH (Supplementary Note 2) is energetically uphill by 26.97 kcal mol−1 via the TS01 step on Ni–N4 site, much higher than the other Ni sites. The cis-COOH can convert back into CO2 with a barrier (TS10) of 1.65 kcal mol−1 or it can abstract a second hydrogen from solution to form adsorbed CO at a barrier (TS13) of 2.98 kcal mol−1. This CO is very weakly adsorbed on the Ni site and evolves as CO gas with a barrier (TS30) of 6.39 kcal mol−1, leaving free the binding site for further reaction or it can form cis-COOH again by back reaction with a barrier (TS31) of 17.43 kcal mol−1. The CO2 to CO conversion along the trans path has a lower energy barrier because the trans-COOH intermediate is more stable than cis-COOH. The CO2 is converted into trans-COOH with a lower barrier (TS02) of 23.30 kcal mol−1. The reverse process has low barrier (TS20) of 1.11 kcal mol−1 or it can react with another hydrogen from solution to form adsorbed CO with no barrier (TS23). This weakly adsorbed CO is finally evolved from solution as CO gas with the same barrier (TS30), leaving an empty catalysts surface or it can convert into trans-COOH by back reaction with high barrier (TS32) of 14.45 kcal mol−1.
Overall kinetics and comparison with experiments
The Free energies of all reaction intermediates and transition states were calculated as a function of applied potential using our quadratic transformation of the grand canonical potential. Since, the reaction rates depend directly on the applied potential, we obtain the rates from the free energy change to the TS using the Eyring rate equation. Finally, the overall reaction rate and species concentration are calculated using a microkinetic model. The rate equations for each species are as follows below:
and, the Eyring rate equation for rate constant:
where, \(x_i\) is the concentration of each species, \(k_{ij}(U)\) is the potential dependent rate constant, \(k_B\) is the Boltzmann’s constant, and h is the Planck’s constant. Here we apply the constraint \({\mathrm{\Sigma }}_ix_i = 1\). Solving for the rate at the onset potential for each case, we obtain the concentration of each species as summarized in Table 1.
Solving these equations to obtain the kinetics as a function of applied potential leads to the current density as a function of applied potential shown in Fig. 7b–e for the CO2 reduction reaction. Depending on each reaction rate, the concentrations change as a function of the applied potential. Figure 7b, c shows the CO partial current densities as a function of applied potential for the Ni–N2C2, Ni–N3C1 and Ni–N4 catalysts. The I–V curves show that CO2RR starts first from Ni–N2C2 sites at −0.7 V with Uonset (10 mA cm−2) = −0.84 V. At U = −0.84 V, we calculate the CO faradic efficiency (FE) to be 98% with a turn-over-frequency (TOF) of 3903 h−1 per site. We calculate the Tafel slope for Ni–N2C2 to be 52 mV dec−1 (Fig. 7d), which is dominated by fast electron transfer followed by a slow protonation step converting CO2 to COOH as the rate limiting step (RDS). We find that for U < −0.9 V the current tends to saturate with a very large Tafel slope due to the strong CO bond to the Ni site. For U < −0.93 V, Ni–N3C1 becomes more active than Ni–N2C2 site, which are blocked by strong CO binding (Fig. 7c). For the Ni–N3C1 site, we obtain Uonset = −0.92 V, FE = 78% and TOF = 2940 h−1 with a maximum Tafel slope of 62 mV dec−1. The Tafel slope drastically increases for U < −1.06 V due to strong CO bonding to Ni site. Then as U < −1.05 V, Ni–N4 dominates CO production. For Ni–N4, we find Uonset = −1.03 V with a high FE = 99%, and TOF = 3944 h−1 with a Tafel slope of 55 mV dec−1. Here the binding of CO to the Ni is weaker, so that very high currents are predicted (this may be limited by transport and other issues). Overall, the Ni–N2C2 site dominates CO production for U ~ −0.85 V, with Ni–N3C1 dominating by −0.95 V, and Ni–N4 dominating by −1.12 V. For comparison, Fig. 7b shows the experimental data for CO2RR from three papers, normalized (Supplementary Note 3) to have the same active sites concentrations21,25,27. The recent experimental papers lead to an onset potential at 10 mA cm−2 of −0.7, −0.84, and −0.93 V in reasonable agreement with our predictions for the Ni–N2C2 site (Uonset = −0.84 V) and Ni–N3C1 site (Uonset = −0.92 V)20,25,27,28,49. Thus, we conclude that experimental Ni–SACs may have all three sites in different proportions contributing to the overall CO2 reduction performance.
The I–V curves for HER are shown in Fig. 7e. Most notable is that HER for Ni–N3C1 site starts at U = − 0.72 V, reaches 5 mA cm−2 at −0.96 V, and 10 mA cm−2 at −1.09 V. In contrast HER for Ni–N2C2 and Ni–N4 do not start until U < −0.98 V. This suggests that to reduce HER the synthesis should attempt to minimize Ni–N3C1 sites and use applied potentials less negative than U = −1.0 V where CO performance is reasonably high. The Tafel slopes obtained for HER on Ni–N2C2 sites is 100 mV dec−1 and for Ni–N3C1 it is 153 mV dec−1 (Supplementary Fig. 13). This can be compared to the experimental value of 140 mV dec−125. For Ni–N4 site, HER is very slow, leading to Uonset = −1.31 V for 10 mA cm−2, with a Tafel slope 84 mV dec−1. Thus Ni–N4 is the best overall performer with a current of 40 mA cm−2 at U = −1.05 V with CO FE ~ 100%.
Comparison of QM based descriptors with experiments
In order to find the synthesis conditions that maximize production of the desired sites, say Ni–N4 it would be useful to have descriptors indicating which sites dominate prior to experimentally inserting into a cell. The CO stretching vibration is prominent in the FT-IR, occurring experimentally at 1900–2060 cm−1 on Ni single sites50. We calculated the vibration wavenumbers for adsorbed CO on different Ni-sites at applied potentials corresponding to high adsorbed CO concentrations (Supplementary Fig. 14). We found that U = −1.0 V leads to the highest amount of CO adsorbed on Ni–N2C2 moiety, leading to 1985 cm−1 with vertical polarization. For Ni–N3C1, the highest CO concentration is for U = −1.1 V, leading to 1959 cm−1 while for Ni–N4, the highest CO concentration is for U = −1.25 V leading to 1942 cm−1. Both latter cases lead to CO polarization off from vertical. Our calculated values are in the range of experiment and the dependence on site is sufficiently large to identify which Ni sites are present. Additionally, we used QM calculation to predict XPS BE shifts for N 1s to identify how many nitrogens are bonded to Ni in Ni–SACs. The experimentally deconvoluted N 1s peaks indicate several nitrogen moieties, but only pyridinic nitrogen bonded to Ni shows a shift from normal pyridinic N BE value. The experimental BE difference between pyridinic N and M-Nx varies from 0.9 to 1.3 eV.
So, we took pyridinic N 1s as reference BE for comparing the BE shifts. The BE shift, ΔBE for N 1s is 0.96 eV (lowest) for Ni–N2C2 site and 1.18 eV (highest) for Ni–N4 site, which are in the range of experiment (Table 2). We found that the C 1s BE decreases to 0.62 eV and 1.21 eV for Ni–N3C1 and Ni–N2C2. Finally, we also observed that the Ni 2p BE shift is 0.28 eV for Ni–N2C2 (lowest) and 0.90 eV for Ni–N4 site (highest). These differences might be too small to be resolved experimentally.
Discussion
The CO2 reduction to CO involves four steps. Firstly, linear CO2 binds to the catalysts surface (*) by forming bent *CO2− via electron transfer
then hydrogen transfer from water converts bent CO2 into adsorbed *COOH intermediate plus solvated OH−
then a second hydrogen transfer from water converts adsorbed *COOH intermediate into bound CO plus H2O plus solvated OH−
Finally, the bound *CO desorbs from the catalyst surface as CO gas, and making the surface empty (*) for further reaction
The Tafel slope provides an indication of the rate determining step for this reaction. According to Butler–Volmer equation, Tafel slopes should be around 120, 60, 40 mV dec−1, and ∞ if the rate determining steps are (9), (10), (11), and (12), respectively. We calculated Tafel slopes of 52, 62, and 55 mV dec−1 for Ni–N2C2, Ni–N3C1 and Ni–N4, respectively, obtained near to their onset potential, Uonset.
Our calculations show that CO2 activation is easier due to presence of Ni+ instead of Ni2+, where the highest occupied molecular orbital (HOMO) of Ni+ in Ni–SACs (Ni \(3d_{x^{2} - y^{2}}\) rather than \(3d_{z^{2}}\) for Ni2+) has tendency to overlap with the C 2p* orbital in CO2. Thus, protonation of *\({\mathrm{CO}}_2^ -\) to become *COOH leads to the highest energy barrier (Figs. 3 and 7), which is the RDS for all active sites we studied. This should lead to Tafel slope ~60 mV dec−1. Recently, Gu et al.52 observed that the initial electron for reduction of CO2 is decoupled from a proton transfer on Fe3+–N–C and found that CO2 adsorption is fast, and the rate limiting step is protonation of the adsorbed CO2– to form an adsorbed COOH intermediate, with an experimental Tafel slope of 64 mV dec−1. Moreover, experiments by Liu et al.29 for CO2RR on a Ni-single atom catalyst confirmed the presence of Ni+ by operando spectroscopic characterization. They observed that the proton transfer to the adsorbed *CO2 is the rate determining step with a Tafel slope of 72 mV dec−1. Thus the experiments lead to Tafel slope very close to the 62 mV dec−1 we calculate for Ni–N3C1.
It has been shown experimentally49 that Ni-single atom catalysts can deliver a large current density of 220 mA cm−2 at −1.0 V RHE with 88.5% FE. We predict that our most active site at −1.0 V, Ni–N3C1, leads to a CO current of 259 mA cm−2, slightly higher than experiment (192 mA cm−2). This may be due to mass transport issues that we ignore. According to Singh et al.53,54 at higher negative potential (−1.0 V vs RHE), the transport of CO2 to the catalyst and the transport of OH− anions away from the catalyst become rate limiting due to cathodic polarization. Moreover, as a consequence of the latter effect, the pH near the catalyst surface rises well above 7, and the concentration of CO2 decreases dramatically because of the reaction of CO2 with OH− anions to form HCO3− and CO3− anions. The net effect is to alter the current-voltage profile significantly.
The double layer capacitance is an important parameter that can affect the current-voltage relations for CO2 reduction. The double layer capacitance arises from charge transfer in contact between the conductive electrode and the electrolytic solution. Experimentally, the double layer capacitance, Cdiff, is between 20 and 25 μF cm−2 for most metal surfaces. Ringe et al.55 assumed a value of 25 μF cm−2 in their model to address double layer effects for CO2 reduction reaction on Ag (111) single crystal electrode. As described earlier, the GCP-K leads directly to a differential capacitance, Cdiff, that can be compared to experiment. The values for various intermediates are shown in Table 3. We found that the capacity differences, Cdiff are 12–29 μF cm−2 for Ni–N2C2, 12–20 μF cm−2 for Ni–N3C1, and 13–22 μF cm−2 for Ni–N4 system, close to the observed values (20–25 μF cm−2) reported experimentally56,57. This further validates our methodology for catalyst-electrolyte interface. We also calculated the PZC and F0 value for each of reaction intermediates for the various active sites (Supplementary Tables 3–5)
.
In conclusion, we examined the reaction mechanism and kinetics for the reduction of CO2 over graphene-supported Ni-single atom catalysts (Ni–SACs) using the new grand canonical potential kinetics (GCP-K) formulation. This allows the geometry of the transition states and the charge transfer from electrode to adsorbed species to change continuously along the reaction coordinates as the potential is changed. GCP-K describes the electron transfer accompanying proton or hydrogen transfer as a continuous process, rather than as a discrete electron jump as in the PCET formulation of traditional Butler–Volmer kinetics.
We applied the GCP-K method to determine the reaction mechanism and kinetics for CO2RR on all three Ni sites: Ni–N2C2, Ni–N3C1, and Ni–N4 likely to be present in Ni–SACs. We find each site leads to unique kinetics with Ni–N2C2 dominant for −0.93 < U < −0.75 V, producing 10 mA cm−2 current density at Uonset = −0.84 V, with a Tafel slope of 52 mV dec−1, a faradic efficiency (FE) of 98%, and TOF = 3903 h−1 per Ni site. On the other hand, Ni–N3C1 dominant for −1.05 < U < −0.93 V producing 10 mA cm−2 current density at Uonset = −0.92 V, with a Tafel slope of 62 mV dec−1, a FE = 78% and TOF = 2940 h−1 per Ni site while Ni-N4 dominant for U < −1.05 V producing 10 mA cm−2 current density at Uonset = −1.03 V with a Tafel slope of 55 mV dec−1, a FE = 99% faradic efficiency, and TOF = 3944 h−1 per Ni site. These predicted overall kinetics show reasonable agreement with experimental studies. Thus ref. 25,27 leads to CO dependence on U similar to what we find for Ni–N2C2. We find that HER activity on Ni–SAC depends very much on the site, with HER on Ni–N3C1 starting at U = −0.8 V. The Ni–N4 leads to the best overall performance for CO2 reduction: At U = −1.05 V we find 40 mA cm−2 with CO FE ~ 100%.
In order to help guide identification of the sites in experimental synthesized Ni–SACs, we predicted the XPS N and C 1s and Ni 2p BE shift and the CO vibrational frequencies for various sites. We find that the pyridinic N 1s XPS binding shifts is highest (+1.18 eV) for Ni–N4 and lowest (+0.96 eV) for Ni–N2C2. While the C 1s shift is −0.62 for Ni–N3C1 and −1.21 eV for Ni–N2C2. Finally, The Ni 2p BE shift is +0.90 eV (maximum) for Ni–N4 and +0.28 eV (minimum) for Ni–N2C2 site. The CO stretch for CO bound to Ni is 1985 cm−1 at −1.0 V on Ni–N2C2 site and 1942 cm−1 at −1.25 V on Ni–N4 site. These predicted results for Ni–N2C2 site agree best with experiment, but we expect that most synthesized catalysts have mixtures of all three Ni sites so that the total CO current for arises from each of them.
Methods
Computational details
The geometry optimization was performed as a function of constant charge using the PBE-D3 functional58,59,60 with VASPsol61,62 implemented in VASP63,64,65 and including spin polarization (Supplementary Note 2). Then we used the Legendre transformation to transform the VASP results to constant potential followed by using the CANDLE solvation model35 (as implemented in jDFTx v.1.2.1)66 for the final constant potential results. Here we included a few waters to describe explicitly the polarization involved in proton transfer. The positions of these waters were optimized with VASPsol. For the reaction barriers we did free energy calculation for each point along the NEB reaction path using VASPsol, so that the geometry of the transition state could change adiabatically as a function of applied potential. The VTST package67 with climbing image nudged elastic band (CI-NEB)68 was used to obtain the reaction pathway and transition states including solvation.
We used a plane wave basis set with 500 eV cutoff energy. The geometry optimization criteria were set to 10−6 eV for energy and 0.01 eV Å−1 for forces on each atom while for CI-NEB we used 0.02 eV Å−1. A Gaussian smearing of 0.05 eV was applied throughout the whole calculation. The K-points were selected to be 5 × 5 × 1 for structure relaxation and energy calculations. The graphene unit cell dimensions were optimized to be 2.46 Å × 2.46 Å with 20 Å distance between layers perpendicular to the surface. Finally, 4 × 4 super cells of graphene were used with 26 carbon atoms and 1 metal atom placed on the carbon divacancy.
The single point jDFTx calculations were used to obtain the combined DFT and solvation free energy using the geometry optimized with VASPsol. The jDFTx calculation was chosen because of the accuracy in describing continuum solvation and for including constant potentials for electrochemical reaction. But we found that a single point calculation is sufficient for the stable species since the structures observed are similar in both VASPsol and jDFTx (Supplementary Table 6). The CANDLE solvation model was used in jDFTx to describe solvation implicitly. Using this scheme, \(\mu _{e,{\mathrm{SHE}}}\) = 4.66 eV, which was used for all structures. A plane wave basis set with energy cutoff of 20 Hartree was used with a k-point mesh of 5 × 5 × 1. The free energy convergence criteria were set to 10−8 Hartree.
XPS BE shift calculations were performed using the core level energies implemented in VASP63. There are two methods for such calculations; we used simpler option (ICORELEVEL = 1) to calculate the core levels in the initial state approximation. This is based on the observation in recent publications that this method leads relative BE shifts in good agreement with experimental XPS69,70. This method involves recalculating the KS eigenvalues of the core states after a self-consistent calculation of the valence charge density. The phonon density of states were calculated using VASP by setting IBRION = 5 in the INCAR file. The Hessian matrix and the vibrational frequencies of a system were calculated using atom displacements in all three cartesian directions with a step size of 0.015 Å (POTIM). We allowed only the adsorbed molecule to vibrate and the vibrational frequencies were taken from the normal mode analysis. To calculate entropy, we used the phonon density of states, as found in OUTCAR as “f” on the real axis. Then we extracted total vibrational ZPE, enthalpy, and entropy.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Turner, J. A. A realizable renewable energy future. Science 285, 687 (1999).
Chu, S. & Majumdar, A. Opportunities and challenges for a sustainable energy future. Nature 488, 294–303 (2012).
Wang, Y. et al. Paleo-CO2 variation trends and the Cretaceous greenhouse climate. Earth Sci. Rev. 129, 136–147 (2014).
Sun, Z., Ma, T., Tao, H., Fan, Q. & Han, B. Fundamentals and challenges of electrochemical CO2 reduction using two-dimensional materials. Chem 3, 560–587 (2017).
Gao, S. et al. Partially oxidized atomic cobalt layers for carbon dioxide electroreduction to liquid fuel. Nature 529, 68–71 (2016).
Voiry, D., Shin, H. S., Loh, K. P. & Chhowalla, M. Low-dimensional catalysts for hydrogen evolution and CO2 reduction. Nat. Rev. Chem. 2, 0105 (2018).
Ooka, H., Figueiredo, M. C. & Koper, M. T. M. Competition between hydrogen evolution and carbon dioxide reduction on copper electrodes in mildly acidic media. Langmuir 33, 9307–9313 (2017).
Whipple, D. T. & Kenis, P. J. A. Prospects of CO2 utilization via direct heterogeneous electrochemical reduction. J. Phys. Chem. Lett. 1, 3451–3458 (2010).
Zhu, W. et al. Monodisperse Au nanoparticles for selective electrocatalytic reduction of CO2 to CO. J. Am. Chem. Soc. 135, 16833–16836 (2013).
Li, C. W. & Kanan, M. W. CO2 reduction at low overpotential on Cu electrodes resulting from the reduction of thick Cu2O films. J. Am. Chem. Soc. 134, 7231–7234 (2012).
Cheng, T., Xiao, H. & Goddard, W. A. Reaction mechanisms for the electrochemical reduction of CO2 to CO and formate on the Cu(100) surface at 298 K from quantum mechanics free energy calculations with explicit water. J. Am. Chem. Soc. 138, 13802–13805 (2016).
Sarfraz, S., Garcia-Esparza, A. T., Jedidi, A., Cavallo, L. & Takanabe, K. Cu–Sn bimetallic catalyst for selective aqueous electroreduction of CO2 to CO. ACS Catal. 6, 2842–2851 (2016).
Kim, D., Resasco, J., Yu, Y., Asiri, A. M. & Yang, P. Synergistic geometric and electronic effects for electrochemical reduction of carbon dioxide using gold–copper bimetallic nanoparticles. Nat. Commun. 5, 4948 (2014).
Cheng, T., Huang, Y., Xiao, H. & Goddard, W. A. Predicted structures of the active sites responsible for the improved reduction of carbon dioxide by gold nanoparticles. J. Phys. Chem. Lett. 8, 3317–3320 (2017).
Fei, H. et al. Atomic cobalt on nitrogen-doped graphene for hydrogen generation. Nat. Commun. 6, 8668 (2015).
Hossain, M. D. et al. Rational design of graphene-supported single atom catalysts for hydrogen evolution reaction. Adv. Energy Mater. 9, 1803689 (2019).
Yang, L. et al. Unveiling the high-activity origin of single-atom iron catalysts for oxygen reduction reaction. Proc. Natl Acad. Sci. USA 115, 6626–6631 (2018).
Chen, Y. et al. Enhanced oxygen reduction with single-atomic-site iron catalysts for a zinc-air battery and hydrogen-air fuel cell. Nat. Commun. 9, 5422 (2018).
Back, S., Lim, J., Kim, N.-Y., Kim, Y.-H. & Jung, Y. Single-atom catalysts for CO2 electroreduction with significant activity and selectivity improvements. Chem. Sci. 8, 1090–1096 (2017).
Ju, W. et al. Understanding activity and selectivity of metal-nitrogen-doped carbon catalysts for electrochemical reduction of CO2. Nat. Commun. 8, 944 (2017).
Yang, H. B. et al. Atomically dispersed Ni(i) as the active site for electrochemical CO2 reduction. Nat. Energy 3, 140–147 (2018).
Liu, M., Zhang, R. & Chen, W. Graphene-supported nanoelectrocatalysts for fuel cells: synthesis, properties, and applications. Chem. Rev. 114, 5117–5160 (2014).
Li, Y. et al. MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. J. Am. Chem. Soc. 133, 7296–7299 (2011).
Chen, Y. et al. Single-atom catalysts: synthetic strategies and electrochemical applications. Joule 2, 1242–1264 (2018).
Jiang, K. et al. Isolated Ni single atoms in graphene nanosheets for high-performance CO2 reduction. Energy Environ. Sci. 11, 893–903 (2018).
Yan, C. et al. Coordinatively unsaturated nickel–nitrogen sites towards selective and high-rate CO2 electroreduction. Energy Environ. Sci. 11, 1204–1210 (2018).
Zhao, C. et al. Ionic exchange of metal–organic frameworks to access single nickel sites for efficient electroreduction of CO2. J. Am. Chem. Soc. 139, 8078–8081 (2017).
Su, P., Iwase, K., Nakanishi, S., Hashimoto, K. & Kamiya, K. Nickel-nitrogen-modified graphene: an efficient electrocatalyst for the reduction of carbon dioxide to carbon monoxide. Small 12, 6083–6089 (2016).
Liu, S. et al. Elucidating the electrocatalytic CO2 reduction reaction over a model single-atom nickel catalyst. Angew. Chem. Int. Ed. Engl. 59, 798–803 (2020).
Sundararaman, R., GoddardIII, W. A. & Arias, T. A. Grand canonical electronic density-functional theory: Algorithms and applications to electrochemistry. J. Chem. Phys. 146, 114104 (2017).
Huang, Y., Nielsen, R. J. & Goddard, W. A. Reaction mechanism for the hydrogen evolution reaction on the basal plane sulfur vacancy site of MoS2 using grand canonical potential kinetics. J. Am. Chem. Soc. 140, 16773–16782 (2018).
Sha, Y., Yu, T. H., Merinov, B. V. & Goddard, W. A. Prediction of the dependence of the fuel cell oxygen reduction reactions on operating voltage from DFT calculations. J. Phys. Chem. C. 116, 6166–6173 (2012).
Jinnouchi, R. & Anderson, A. B. Electronic structure calculations of liquid-solid interfaces: combination of density functional theory and modified Poisson-Boltzmann theory. Phys. Rev. B 77, 245417 (2008).
Gunceler, D., Letchworth-Weaver, K., Sundararaman, R., Schwarz, K. A. & Arias, T. A. The importance of nonlinear fluid response in joint density-functional theory studies of battery systems. Model. Simul. Mater. Sci. Eng. 21, 074005 (2013).
Sundararaman, R. & Goddard, W. A. The charge-asymmetric nonlocally determined local-electric (CANDLE) solvation model. J. Chem. Phys. 142, 064107 (2015).
Goodpaster, J. D., Bell, A. T. & Head-Gordon, M. Identification of possible pathways for C–C bond formation during electrochemical reduction of CO2: new theoretical insights from an improved electrochemical model. J. Phys. Chem. Lett. 7, 1471–1477 (2016).
Xiao, H., Cheng, T., Goddard, W. A. & Sundararaman, R. Mechanistic explanation of the pH dependence and onset potentials for hydrocarbon products from electrochemical reduction of CO on Cu (111). J. Am. Chem. Soc. 138, 483–486 (2016).
Chan, K. & Nørskov, J. K. Potential dependence of electrochemical barriers from ab initio calculations. J. Phys. Chem. Lett. 7, 1686–1690 (2016).
Taylor, C. D., Wasileski, S. A., Filhol, J.-S. & Neurock, M. First principles reaction modeling of the electrochemical interface: consideration and calculation of a tunable surface potential from atomic and electronic structure. Phys. Rev. B 73, 165402 (2006).
Taylor, C. D. & Neurock, M. Theoretical insights into the structure and reactivity of the aqueous/metal interface. Curr. Opin. Solid State Mater. Sci. 9, 49–65 (2005).
Mamatkulov, M. & Filhol, J. S. An abinitio study of electrochemical vs. electromechanical properties: the case of CO adsorbed on a Pt(111) surface. Phys. Chem. Chem. Phys. 13, 7675–7684 (2011).
Fei, H. et al. General synthesis and definitive structural identification of MN4C4 single-atom catalysts with tunable electrocatalytic activities. Nat. Catal. 1, 63–72 (2018).
Lin, W., Stocker, K. M. & Schatz, G. C. Mechanisms of hydrogen-assisted CO2 reduction on nickel. J. Am. Chem. Soc. 139, 4663–4666 (2017).
Zhao, Z., Chen, Z. & Lu, G. Computational discovery of nickel-based catalysts for CO2 reduction to formic acid. J. Phys. Chem. C. 121, 20865–20870 (2017).
Akhade, S. A. et al. Poisoning effect of adsorbed CO during CO2 electroreduction on late transition metals. Phys. Chem. Chem. Phys. 16, 20429–20435 (2014).
v. Neumann, J. Zur Theorie der Gesellschaftsspiele. Mathematische Annalen. 100, 295–320 (1928).
Sato, N. in Electrochemistry at metal and semiconductor electrodes (ed. Sato, N.) 213–233 (Elsevier Science, 1998).
Bard, A. J. & Faulkner L. R. Electrochemical Methods: Fundamentals and Applications (Wiley, 2000).
Möller, T. et al. Efficient CO2 to CO electrolysis on solid Ni–N–C catalysts at industrial current densities. Energy Environ. Sci. 12, 640–647 (2019).
Vogt, C. et al. Unravelling structure sensitivity in CO2 hydrogenation over nickel. Nat. Catal. 1, 127–134 (2018).
Artyushkova, K. et al. Density functional theory calculations of XPS binding energy shift for nitrogen-containing graphene-like structures. Chem. Commun. 49, 2539–2541 (2013).
Gu, J., Hsu, C.-S., Bai, L., Chen, H. M. & Hu, X. Atomically dispersed Fe3+ sites catalyze efficient CO2 electroreduction to CO. Science 364, 1091 (2019).
Singh, M. R., Clark, E. L. & Bell, A. T. Effects of electrolyte, catalyst, and membrane composition and operating conditions on the performance of solar-driven electrochemical reduction of carbon dioxide. Phys. Chem. Chem. Phys. 17, 18924–18936 (2015).
Singh, M. R., Goodpaster, J. D., Weber, A. Z., Head-Gordon, M. & Bell, A. T. Mechanistic insights into electrochemical reduction of CO2 over Ag using density functional theory and transport models. Proc. Natl Acad. Sci. USA 114, E8812 (2017).
Ringe, S. et al. Understanding cation effects in electrochemical CO2 reduction. Energy Environ. Sci. 12, 3001–3014 (2019).
Hamelin, A., Vitanov, T., Sevastyanov, E. & Popov, A. The electrochemical double layer on sp metal single crystals: the current status of data. J. Electroanal. Chem. Interfacial Electrochem. 145, 225–264 (1983).
Valette, G. Double layer on silver single crystal electrodes in contact with electrolytes having anions which are slightly specifically adsorbed: Part II. The (100) face. J. Electroanal. Chem. Interfacial Electrochem. 138, 37–54 (1982).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Kresse, G. & Hafner, J. Ab initio molecular-dynamics simulation of the liquid-metal—amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994).
Mathew, K., Sundararaman, R., Letchworth-Weaver, K., Arias, T. A. & Hennig, R. G. Implicit solvation model for density-functional study of nanocrystal surfaces and reaction pathways. J. Chem. Phys. 140, 084106 (2014).
Mathew, K., Chaitanya Kolluru, V. S., Mula, S., Steinmann, S. N. & Hennig, R. G. Implicit self-consistent electrolyte model in plane-wave density-functional theory. J. Chem. Phys. 151, 234101 (2019).
Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Sundararaman, R. et al. JDFTx: Software for joint density-functional theory. SoftwareX 6, 278–284 (2017).
Sheppard, D., Xiao, P., Chemelewski, W., Johnson, D. D. & Henkelman, G. A generalized solid-state nudged elastic band method. J. Chem. Phys. 136, 074103 (2012).
Henkelman, G., Uberuaga, B. P. & Jónsson, H. A climbing image nudged elastic band method for finding saddle points and minimum energy paths. J. Chem. Phys. 113, 9901–9904 (2000).
Favaro, M. et al. Subsurface oxide plays a critical role in CO2 activation by Cu(111) surfaces to form chemisorbed CO2, the first step in reduction of CO2. Proc. Natl Acad. Sci. USA 114, 6706 (2017).
Ye, Y. et al. Dramatic differences in carbon dioxide adsorption and initial steps of reduction between silver and copper. Nat. Commun. 10, 1875 (2019).
Acknowledgements
This project was supported by the Research Grant Council of Hong Kong SAR (Project numbers 16204818), NSFC-RGC Joint Research Scheme (N_HKUST607/17), the Innovation and Technology Commission (ITC-CNERC14SC01), the Guangzhou Science & Technology (Project 201704030134). This work was also supported by the Joint Center for Artificial Photosynthesis (JCAP), a DOE Energy Innovation Hub, supported through the Office of Science of the U.S. Department of Energy under Award No. DE-SC0004993. The calculations were performed on computer clusters at the materials and process simulation center (MSC) at Caltech, the high-performance computing (HPC) facility at Caltech, and the HKUST (funded by the School of Engineering).
Author information
Authors and Affiliations
Contributions
M.D.H., W.A.G., and Z.T.L. conceived the idea and designed the research. M.D.H. performed all the calculations. M.D.H., Y.H., and T.H.Y. participated in discussions analyzing the data obtained from the calculations. M.D.H., W.A.G., and Z.T.L. wrote the paper with helpful comments from Y.H. and T.H.Y.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Alexis Bell, and other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hossain, M.D., Huang, Y., Yu, T.H. et al. Reaction mechanism and kinetics for CO2 reduction on nickel single atom catalysts from quantum mechanics. Nat Commun 11, 2256 (2020). https://doi.org/10.1038/s41467-020-16119-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-16119-6
- Springer Nature Limited
This article is cited by
-
Identification of K+-determined reaction pathway for facilitated kinetics of CO2 electroreduction
Nature Communications (2024)
-
Disentangling heterogeneous thermocatalytic formic acid dehydrogenation from an electrochemical perspective
Nature Communications (2024)
-
Importance of broken geometric symmetry of single-atom Pt sites for efficient electrocatalysis
Nature Communications (2023)
-
How water molecules occupying the active site of a single-atom catalyst affect the electrochemical reduction of carbon dioxide
Nano Research (2023)
-
Recent advances in the rational design of single-atom catalysts for electrochemical CO2 reduction
Nano Research (2022)