Abstract
Applications for smart medical implants require hermetic and mechanically strong seals between functional and biocompatible materials. Hermetic seals between titanium Ti6Al4V and silica-based glass can be produced using a novel bonding method based on glass pressing at temperatures around the softening point. This paper presents investigation results for the tensile bond strength and the gas leak rate depending on the manufacturing process parameters. Notably, when using blasted surfaces, the tensile bond strengths reached 12 MPa and good adherence with very low leakage due to the removed oxide layer and surface structure. The interface is analyzed and characterized by applying SEM methods related to the different adhesion mechanisms.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
Glass-to-metal seals are required in numerous technological fields such as aerospace engineering [1], battery technology [2], and medical engineering [3]. Mechanical strength and sealing quality are the significant properties that determine the performance of glass-to-metal bondings. The glass material and the metal alloy must be biocompatible for applications in medical engineering.
Implantable electronic devices such as pacemakers are encapsulated in order to protect the human body from potentially harmful substances. Titanium alloys combine mechanical strength with biocompatibility, making them the material of choice for most medical implants containing electronic systems. Figure 1 illustrates an implantable electronic system with a titanium housing. This implant contains an optical window for optical data communication with a control system located outside the body, as described in [4]. Other potential applications for optical windows are optical diagnosis systems. Silica-based glasses match the requirements for mechanical strength, biocompatibility, and optical transmission. Moreover, the hermetic sealing between the titanium housing and the glass window is a crucial part of the encapsulation system (Fig. 1).
Bonding of glass and metal is an old technology that can even be traced back to ancient Egypt, where decorative glass coatings were manufactured on metal surfaces. The technology applied for these coatings is based on glass melting and wetting of the metal surface, which was later referred to as enameling. Most industrial applications such as light bulbs or enameled cookware are produced by this common type of manufacturing process using high temperatures to melt the glass, allowing it to wet the metal surface [5]. Bonding of glass and titanium for medical and other applications is challenging and has been studied extensively [6,7,8].
Compared to the conventional glass melting approach, other bonding methods with low process temperatures have been introduced [9]. In the anodic bonding process [10], the glass remains in its solid state, and static electric fields create the glass-to-metal interface. This technology is used for microfluidic applications [11].
This paper investigates an alternative glass-to-metal bonding technology, first introduced in [12], with process temperatures between conventional melting technologies and low-temperature bonding technologies. The interface created at medium temperatures allows glass to be formed by compressive forces. The investigations’ objective comprises determining the influence of the relevant process parameters on the quality of the glass-to-metal seal.
2 Setup and procedure to test bonding properties
2.1 Sample design
The investigation of the alternative bonding method uses a combination of a titanium alloy and a silica-based glass. Titanium grade 5 (Ti6Al4V) is the most common material used for medical implants and combines high mechanical strength with biocompatibility. The glass type B270 by Schott is an optical crown glass and was selected as its thermal expansion coefficient (10.3 × 10−6 K−1) is similar to that of Ti6Al4V (9.5 × 10−6 K−1). The major glass components comprise SiO2 (69%), B2O3 (11%), Na2O (10%), K2O (6%), and BaO (3%).
Two different sample geometries were designed in order to fulfill the requirements for measuring both the mechanical strength of the glass-to-metal interface and its hermetic sealing quality (leak tightness). Figure 2a shows the cross-section of the axially symmetric bonding device used for the determination of the bond’s tensile strength and consists of two titanium punches enveloping a cylindrical glass element of 3 mm thickness and a diameter of 15 mm. This design allows the direct measurement of the tensile strength (Fig. 2b) without requiring any glue. The second sample design in Fig. 3a consists of a titanium ring surrounding a glass cylinder of the same geometry, allowing the leak rate measurement through the glass-to-metal peripheral interface.
All titanium samples were produced by precision milling. The blasted surfaces in contact with the glass were roughened by blasting with glass powder (type 09-0010, Baltrusch & Mütsch) in a microblasting tool. A tactile roughness instrument was applied for measuring the surface roughness, which resulted in Ra = 0.3 µm for the milled surface, and Ra = 1.7 µm for the blasted one.
2.2 Bonding process: glass pressing
The glass samples are placed in a pressing die with a Ti sample on both the bottom and the upper punch in a vacuum chamber mounted in a universal testing machine. The samples are heated to the process temperature Tp in an argon atmosphere at a pressure of 5 mbar. Compared to a vacuum, the low-pressure atmosphere of inert gas allows for better heat conductivity from the heated die into the glass sample. In addition, the partial pressure of oxygen is further reduced, which prevents the growth of an oxide layer.
Applying compressive forces on the die provides bonding of the Ti and glass samples. The two parts of the die are equipped with a heater allowing for homogeneous temperature distribution. In the first sample geometry, the die touches the upper titanium sample, and the glass is pressed between the two titanium samples (Fig. 2a). In the second sample geometry, the upper punch directly touches the glass, which bonds to the ring-shaped titanium sample (Fig. 3a). These components are coated with a boron nitride layer to prevent the glass from bonding with the upper punch or the sample holder.
During pressing, the maximum process force Fp is maintained for 15 s. The applied bonding procedure and process parameters are identical for the two sample geometries. Therefore, the measurement results regarding tensile strength and gas leak rates are comparable to samples produced with the same process parameters. Winkler et al. [13] describe the layout of the glass-pressing tool and the individual process steps in detail.
The tested process temperatures of TP = 705 °C, 745 °C, and 785 °C cover a range of 1.5 orders of magnitude in viscosity around the softening point of the glass material B270 at 724 °C. The selected process forces FP = 200 N, 500 N, and 1200 N correspond to compressive stress values between 1 and 7 MPa, which is typical in glass pressing.
2.3 Measurement of tensile strength and leak rate
The adherence of a glass coating on a metal surface can be measured indirectly, e.g. by the Vickers indentation method [14], or directly with a pull-off test [15], in which the sample has to be glued to the testing machine. The tested device and the mechanical interlocking of the two titanium elements (Fig. 2b) are connected to the universal testing machine to avoid the difficulties of detecting the failure point associated with using glue. The tensile force increases in a linear rate of 20 N/s up to 1000 N and 200 N/s above this threshold. The maximum force before the breakage is registered, and the bond tensile strength RH is calculated using the sample area of 177 mm2 (Ø 15 mm).
The leak rate QL is a measured parameter for hermetic sealing quality and is usually specified by the unit mbar∙l/s. The size of the bonded area amounts to 141 mm2 in the experimental setup. At first, all samples are measured with a pressure gain test (Fig. 3c) as specified in DIN EN 1779. The vacuum chamber on the bottom side of the sample is evacuated, and then the vacuum pump is disconnected. The leak rate QL can be calculated based on recording the rising pressure over time due to leakage through the glass-to-metal interface. The helium leak test is applied as a second measurement method [16] for samples with leak rates lower than 10−4 mbar l/s. Figure 3b illustrates the experimental setup. The Ti sample’s upper side is filled with helium under atmospheric pressure of 1 bar, while the bottom side is evacuated and connected to a mass spectrometer designed for the helium leak test. The test procedure is capable of measuring leak rates down to 10−12 mbar l/s.
3 Results and discussion
3.1 Tensile bond strength and leak rate
Figures 4 and 5 present the results of the tensile strength RH and the leak rate QL for the indicated parameter combinations. For most of the experiments, the tensile strength ranges from 7 MPa to 12 MPa. Only three parameter combinations resulted in very low values for RH, which implies no adhesion. The leak rate results (Fig. 5) are similar to those of the tensile strength and are divided into two groups. The first group comprises leak rates of 1∙10−6 mbar∙l/s and below, which is considered technically hermetic, while the second group of leak rates amounts to more than 0.01 mbar∙l/s, which is considered non-hermetic.
In addition to measuring their tensile strength and leak rates, the samples were analyzed by scanning electron microscopy (SEM). Four of the leak-rate-samples with selected parameter combinations were cut perpendicular to the glass titanium interface, ground, polished, and cleaned before being analyzed by SEM. Figure 6 shows the SEM images together with the corresponding process parameters.
3.2 Bonding mechanism
Bonding can be defined as adhesion, which describes the connection between two dissimilar materials at their contact surface. Even today, numerous aspects of adhesion are still subject to research. Various adhesion models with mechanical, electrostatic, chemical, or thermodynamic approaches are available for describing the effects of adhesion. Adhesion can roughly be subdivided into mechanical adhesion and specific adhesion [17]. Mechanical adhesion is based on interlocking, where the first material fills voids, pores, or undercuts of the second material. Specific adhesion is based on electrostatic and molecular forces such as chemical forces or van der Waals forces. It describes adhesion between flat surfaces.
Oxide layers, such as TiO2, can prevent glass-to-metal bonding. The samples were cleaned as described by Donald [1] and bonded directly after machining and blasting to avoid the negative influence of titanium oxide layers. In the SEM images in Fig. 6c, d, the blasted titanium surface appears rough compared to the milled surface in Fig. 6a, b. However, undercuts can be excluded since tensile tests checked the adhesion using a test force perpendicular to the interface. Thus, mechanical adhesion can be neglected. However, specific adhesion does not require a roughened surface but can be increased by roughening the surface as it increases the surface area of the interface between the two materials.
In general, higher process temperatures, higher process forces, and a rough titanium surface lead to better results for both tensile strength and seal quality defined by leak rate. All samples with blasted surfaces are hermetic with leak rates lower than 1∙10−6 mbar∙l/s and show high tensile strength values, with one exception (TP = 705 °C, FP = 200 N). The increased surface area can explain this effect due to the roughened metal surface.
In the SEM images in Fig. 6a, c, d, the materials are in close contact, and no visible gap can be detected. The observed seal quality is verified by the high tensile strength and low leak rate measured in samples produced with the same process parameters. In contrast, Fig. 6b shows a gap of approx. 5 µm between glass and titanium. Accordingly, the measured leak rate is high. However, the parameter combination resulted in a relatively high tensile strength of more than 10 MPa. As two different sample designs were used, it is possible that in this case, the resulting glass-to-titanium interfaces significantly deviate in the two designs, even though they were produced with the same process parameters.
The SEM images in Fig. 6 show an accumulation of circular shapes in the glass material close to the interface. The shapes only appear at high process temperatures of TP = 785 °C and appear to have no influence on the seal quality. Further analyses showed that the shapes are spherical cavities in the glass sample that were exposed during the preparation of the SEM samples. Since the cavities do not appear in all samples, they must originate from the bonding process. These cavities may be explained by gases, which are produced in chemical reactions during the bonding process at higher temperatures. However, no literature references were found indicating such effects. Another explanation for the cavities is the inclusion of argon gas, which fills the process chamber during the bonding process at low pressure. Edelmann [18] reported this effect for a similar hot embossing process.
3.3 Conclusion
The basic applicability of the novel bonding method has already been demonstrated by Winkler et al. [13]. However, other boundary conditions from relevant applications restrict the parameter field of the process. For example, optical functional surfaces such as lenses are typically molded below the softening point due to tool adhesion. Moreover, the design does not allow the application of high process forces in narrow electrical feedthroughs. Therefore, an optimum combination of process parameters has to be chosen depending on the application.
Results with low tensile strength and high leak rates occur at low process temperatures and low process forces. Due to the high viscosity of glass, more time is required for the glass to form a uniform interface to the metal. As all experiments were performed with the same process time of 15 s, the glass could not cover the metal surface entirely at low temperatures and low process forces, which strongly reduced the seal quality. If it becomes necessary to realize the connection at temperatures below the softening point, the surface must be roughened, and high pressing loads have to be applied (see Figs. 4, 5). Longer process times are rarely possible due to poor demolding. Good mechanical adhesion was achieved at the high process force applied for the parameter combination in Fig. 6b. However, this good mechanical adhesion was not evenly distributed over the entire bond surface, so that no hermetic seal quality was achieved.
In all other applications, bonding should take place above the softening point. In this case, the clean and smooth surface shows no functional disadvantages regarding strength and hermetic seal quality if the process force is sufficient. However, too high process temperatures lead to bubble formation at the interface. Ideally, the process window’s central area is derived at a bonding temperature just above the softening point and at pressing loads above 2.5 MPa, independent of the surface roughness.
4 Summary and outlook
An alternative process was tested and verified for bonding glass and titanium at medium temperatures by glass pressing. The most relevant process parameters were investigated, and the tensile strength and the leak rate were measured. Leak rates below 1∙10−6 mbar∙l/s and tensile strengths of more than 7 MPa were verified for most parameter combinations. The material interface was analyzed using SEM for selected parameter combinations.
Tensile strength and leak rate can be improved by higher process temperatures, and, to a smaller degree, by higher process forces. The blasted surface provides better bonding quality. Applying low process temperatures in combination with low process forces results in a mechanically weak interface that is not hermetic. In the SEM analysis, a large gap between the materials was observed for these samples. Using high temperatures led to cavities in the glass at the material interface, which did not negatively affect the seal quality.
It would be necessary to understand the adhesion mechanisms to obtain a deeper understanding of the process parameters’ influence. While mechanical adhesion can be neglected, the type of forces affecting adhesion cannot be determined using the methods described in these investigations. Spectroscopic analysis such as auger electron spectroscopy [19] could be used to analyze the nature of the adhesion mechanism.
References
Donald I (2009) Glas-to-metal seals. Society of Glass Technology
Song S (2010) New glass-ceramic sealants for Na/S battery. J Solid State Electrochem 14(9):S1735–S1740
Gomez-Vega J et al (2001) Bioactive glass-mesoporous silica coatings on Ti6Al4V through enameling and triblock-copolymer-templated sol-gel processing. J Biomed Mater Res A 56:382–389
Winkler S, Edelmann J, Welsch C, Ruff R (2017) Different encapsulation strategies for implanted electronics. Curr Dir Biomed Eng 3(2):725–728
Donald I, Mallinson P, Metcalfe B, Gerrard L, Fernie J (2011) Recent developments in the preparation, characterization and applications of glass-and glass-ceramic-to-metal seals and coatings. J Mater Sci 46:1975–2000
Pazo A, Saiz E, Tomsia A (1998) Silicate glass coatings on Ti-based implants. Acta Mater 46:2551–2558
Goldstein JI et al (1995) Solid-state reactions and phase relations in the Ti-Si-O system at 1373 K. J Am Ceram Soc 78:313–322
Passerone AP, Valbusa G, Biagini E (1977) The titanium-molten glass system: interactions and wetting. J Mater Sci 12:2465–2474
Kuckert H, Born C, Wagner G, Eifler D (2001) Helium-tight sealing of glass with metal by ultrasonic welding. Adv Eng Mater 3:903–905
Briand D, Weber P, De Rooij NF (2004) Bonding properties of metals anodically bonded to glass. Sens Actuators A Phys 114:543–549
Khandan O, Stark D, Chang A, Rao MP (2014) Wafer-scale titanium anodic bonding for microfluidic applications. Sens Actuators B Chem 205:244–248
Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. (2017) Patent: Housing Component, and Method for Manufacturing Same. 2017-05-11. WO 2017/194685 A1
Winkler S, Edelmann J, Günther D, Wieland S, Selbmann F, Baum M, Schubert A (2019) Sealing of glass with titanium by glass pressing at the softening point. SN Appl Sci 1(6):562
Lopez-Esteban S, Saiz E, Fujino S, Oku T, Suganuma K, Tomsia AP (2003) Bioactive glass coatings for orthopedic metallic implants. J Eur Ceram Soc 23:2921–2930
Goller G (2004) The effect of bond coat on mechanical properties of plasma sprayed bioglass-titanium coatings. Ceram Int 30:351–355
Kutzke K (1998) Dichtheitsprüfungen und Lecksuche mit dem Helium-Leckdetektor: ein Leitfaden zum praktischen Einsatz bei der Qualitätssicherung und Wartung. Expert Verlag, Renningen
Bischof C, Possart W (1983) Adhäsion: theoretische und experimentelle Grundlagen. Akademie-Verlag, Berlin
Edelmann J (2012) Mikrostrukturierung von Flachglas durch Heißprägen. Diss. Technische Universität Chemnitz
Takahashi K, Ishii H, Takahashi Y, Nishiguchi K (1992) Valence auger analysis of the annealing effect on atomic interaction at titanium–sapphire, titanium–silica and silver–silica interfaces. Thin Solid Films 221:98–103
Acknowledgements
The work was developed as part of the Fraunhofer pilot project Theranostic Implants—Approval-relevant development of key technologies for medicine to the authors thank the Fraunhofer-Gesellschaft for its support.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Winkler, S., Edelmann, J. & Schubert, A. Characterization of a bonding method for titanium-glass sealing. SN Appl. Sci. 2, 2028 (2020). https://doi.org/10.1007/s42452-020-03871-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s42452-020-03871-z