Abstract
The microstructure and mechanical properties of rheo-diecasting Al-6Zn-2Mg-2Cu alloys microalloyed with Ti, Sc and Sc+Zr were studied by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), hardness testing, and tensile testing. The swirled equilibrium enthalpy device (SEED) process was introduced to prepare the semisolid slurry. Results show that the addition of Ti, Sc, and Sc+Zr refines the grain size and improves the uniformity of the semisolid slurry and then suppresses the growth of the α-Al grain during solution heat treatment. The microstructure of the four alloys in as-cast state mainly consists of spherical α-Al and the Mg(Al, Cu, Zn)2 (η) eutectic phase. Moreover, primary Al3Sc, Al3(Sc, Zr) and Al3Zr are also found in the micro-alloying alloys. After solution and aging heat treatment, most of the Mg(Al, Cu, Zn)2 phases dissolve into the α-Al matrix, while part of Mg(Al, Cu, Zn)2 phases transform to Al2CuMg (S) phases. However, the coarse primary Al3Sc and Al3(Sc, Zr) still remain in the matrix, and promote crack initiation and propagation. With the tensile strength of 553 MPa, yield strength of 463 MPa and elongation of 13.4% at T6 state, trace Ti addition generates more attractive mechanical properties than the other three alloys.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Williams J C, Starke Jr. Progress in structural materials for aerospace systems. Acta Materialia, 2003, 51(19): 5775–5799.
Huda Z, Edi P. Materials selection in design of structures and engines of supersonic aircrafts: A review. Materials & Design, 2013, 46: 552–560.
Thanabumrungkul S, Janudom S, Burapa R, et al. Industrial development of gas induced semisolid process. Transactions of Nonferrous Metals Society of China, 2010, 20: 1016–1021.
Kim S, Kim D, Kim W, et al. The study on characteristics of heat treatment of the direct squeeze cast 7075 wrought Al alloy. Materials Science and Engineering: A, 2001, 304: 721–726.
Spencer D, Mehrabian R, Flemings M C, et al. Rheological behavior of Sn-15 pct Pb in the crystallization range. Metallurgical and Materials Transactions B, 1972, 3(7): 1925–1932.
Atkinson H V. Modelling the semisolid processing of metallic alloys. Progress in Materials Science, 2005, 50(3): 341–412.
Gladman T. Precipitation hardening in metals. Materials Science and Technology, 1999, 15(1): 30–36.
Toropova L S, Eskin D G, Kharakterova M L, et al. Advanced aluminum alloys containing scandium: Structure and properties. Gondon and Breach Science, 1998, 115.
Kendig K L, Miracle D B. Strengthening mechanisms of an Al-Mg-Sc-Zr alloy. Acta Materialia, 2002, 50(16): 4165–4175.
Marquis E A, Seidman D N. Nanoscale structural evolution of Al3Sc precipitates in Al(Sc) alloys. Acta Materialia, 2001, 49(11): 1909–1919.
Marquis E A, Seidman D N, Dunand D C. Effect of Mg addition on the creep and yield behavior of an Al-Sc alloy. Acta Materialia, 2003, 51(16): 4751–4760.
Fuller C B, Seidman D N, Dunand D C. Mechanical properties of Al(Sc, Zr) alloys at ambient and elevated temperatures. Acta Materialia, 2003, 51(16): 4803–4814.
Davydov V, Rostova T, Zakharov V, et al. Scientific principles of making an alloying addition of scandium to aluminium alloys. Materials Science and Engineering: A, 2000, 280(1): 30–36.
Robson J D. A new model for prediction of dispersoid precipitation in aluminium alloys containing zirconium and scandium. Acta Materialia, 2004, 52(6): 1409–1421.
Knipling K E, Seidman D N, Dunand D C. Ambient- and high-temperature mechanical properties of isochronally aged Al-0.06Sc, Al-0.06Zr and Al-0.06Sc-0.06Zr (at.%) alloys. Acta Materialia, 2011, 59(3): 943–954.
Zhao J W, Guo A, Li H, et al. Semisolid slurry of 7A04 aluminum alloy prepared by electromagnetic stirring and Sc, Zr additions. China Foundry, 2017, 14(3): 188–193.
Zhao J, Xu C, Dai G, et al. Microstructure and properties of rheo-diecasting wrought aluminum alloy with Sc additions. Materials Letters, 2016, 173: 22–25.
Cook R, Cooper P, Kearns M. Benefits of master alloy melt treatments in the aluminum foundry industry. Minerals, Metals and Materials Society, Warrendale, PA (United States), 1996.
Apelian D, Sigworth G K, Whaler K R. Assessment of grain refinement and modification of Al-Si foundry alloys by thermal analysis. AFS Trans., 1984, 92(2): 297–307.
Mollard F R, Flemings M C, Niyama E F. Aluminum fluidity in casting. JOM, 1987, 39: 34–37.
Dahle A, Tøndel P, Paradies C, et al. Effect of grain refinement on the fluidity of two commercial Al-Si foundry alloys. Metallurgical and Materials Transactions A, 1996, 27(8): 2305–2313.
Ditta A, Wei L, Xu Y, et al. Effect of hot extrusion and optimal solution treatment on microstructure and properties of spray-formed Al-11.3Zn-2.65Mg-1Cu alloy. Journal of Alloys and Compounds, 2019, 797: 558–565.
Ghosh A, Ghosh M, Kalsar R. Influence of homogenisation time on evolution of eutectic phases, dispersoid behaviour and crystallographic texture for Al-Zn-Mg-Cu-Ag alloy. Journal of Alloys and Compounds, 2019, 802: 276–289.
Norman A F, Prangnell P B, McEwen R S. The solidification behaviour of dilute aluminium-scandium alloys. Acta Materialia, 1998, 46(16): 5715–5732.
Mousavi M G, Cross C E, Grong Ø. Effect of scandium and titanium-boron on grain refinement and hot cracking of aluminium alloy 7108. Science and Technology of Welding and Joining, 1999, 4(6): 381–388.
Okamoto H. Al-Zr (aluminum-zirconium). Journal of Phase Equilibria and Diffusion, 2002, 23(5): 455.
Li J H, Wiessner M, Albu M, et al. Correlative characterization of primary Al3(Sc, Zr) phase in an Al-Zn-Mg based alloy. Materials Characterization, 2015, 102: 62–70.
Knipling K E, Dunand D C, Seidman D N. Criteria for developing castable, creep-resistant aluminum-based alloys — A review. International Journal of Materials Research, 2006, 97(3): 246–265.
Lohar A K, Mondal B N, Panigrahi S C. Influence of cooling rate on the microstructure and ageing behavior of as-cast Al-Sc-Zr alloy. Journal of Materials Processing Technology, 2010, 210(15): 2135–2141.
Dumont D, Deschamps A, Bréchet Y, et al. Characterisation of precipitation microstructures in aluminium alloys 7040 and 7050 and their relationship to mechanical behaviour. Materials Science and Technology, 2004, 20(5): 567–576.
Fan X G, Jiang D M, Meng Q C, et al. Characterization of precipitation microstructure and properties of 7150 aluminium alloy. Materials Science and Engineering: A, 2006, 427(1–2): 130–135.
Zhang M, Liu T, He C N, et al. Evolution of microstructure and properties of Al-Zn-Mg-Cu-Sc-Zr alloy during aging treatment. Journal of Alloys and Compounds, 2016, 658: 946–951.
Yu H H, Xin Y C, Wang M Y, et al. Hall-Petch relationship in Mg alloys: A review. Journal of Materials Science & Technology, 2018, 34(2): 248–256.
Shanmugasundaram T, Heilmaier M, Murty B S, et al. On the Hall-Petch relationship in a nanostructured Al-Cu alloy. Materials Science and Engineering: A, 2010, 527(29–30): 7821–7825.
Acknowledgement
The authors would like to express gratitude for the financial support from the National Key R&D Program of China (No. 2016YFB0301003).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors declare that they have no conflict of interest.
Additional information
Jian Feng Ph. D, Engineer. His research interests focus on materials design for high performance casting aluminum alloys, including high strength and toughness aluminum alloy, high thermal conductivity aluminum alloy, non-heat treatment aluminum alloy, and heat resistant aluminum alloy.
Rights and permissions
About this article
Cite this article
Hou, Sh., Feng, J., Chen, S. et al. Effect of Ti, Sc and Zr additions on microstructure and mechanical properties of rheo-diecasting Al-6Zn-2Mg-2Cu alloys. China Foundry 20, 125–133 (2023). https://doi.org/10.1007/s41230-022-2028-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41230-022-2028-8