Abstract
To achieve a better material for thermoelectric power generation device, filled skutterudite Yb0.3Co4Sb12 samples were fabricated by melting–quenching–annealing–spark plasma sintering (SPS) method. Two sets of samples, before and after SPS, were investigated. In both the two sets of samples, the average grain size of the samples increases monotonously with the increase of annealing time, while Yb filling fraction firstly increases and then decreases. Yb not filling into the skutterudite remains at the grain boundaries in the form of Yb2O3 after SPS, which could be quantified by the spatially difference method of energy dispersive spectra. Step distribution of Yb filling fraction was observed in the samples annealed for 1 h, which was caused by the microstructural evolution from the peritectic phases to the skutterudite phase. The sample annealed for 3 days and SPS sintered possesses the maximum value of Yb filling fraction 0.249 and the maximum ZT value of 1.24 at 850 K. These results are helpful to better understand the microstructural evolution and Yb filling behavior in skutterudite materials.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Sales BC, Mandrus D, Williams RK. Filled skutterudite antimonides: A new class of thermoelectric materials. Science 1996, 272: 1325–1328.
Shi X, Kong H, Li C-P, et al. Low thermal conductivity and high thermoelectric figure of merit in n-type BaxYbyCo4Sb12 double-filled skutterudites. Appl Phys Lett 2008, 92: 182101.
Leithe-Jasper A, Kaczorowski D, Rogl P, et al. Synthesis, crystal-structure determination and physical properties of YbFe4Sb12. Solid State Commun 1999, 109: 395–400.
Nolas GS, Kaeser M, Littleton RT, et al. High figure of merit in partially filled ytterbium skutterudite materials. Appl Phys Lett 2000, 77: 1855–1857.
Dilley NR, Bauer ED, Maple MB, et al. Thermoelectric properties of chemically substituted skutterudites YbyCo4SnxSb12−x. J Appl Phys 2000, 88: 1948–1951.
Park Y-S, Thompson T, Kim Y, et al. Protective enamel coating for n-and p-type skutterudite thermoelectric materials. J Mater Sci 2015, 50: 1500–1512.
Zhu T, Liu Y, Fu C, et al. Compromise and synergy in high-efficiency thermoelectric materials. Adv Mater 2017, 29: 1605884
Sales BC, Mandrus D, Chakoumakos BC, et al. Filled skutterudite antimonides: Electron crystals and phonon glasses. Phys Rev B 1997, 56: 15081–15089.
Mandrus D, Sales BC, Keppens V, et al. Filled skutterudite antimonides: Validation of the electron-crystal phonon-glass approach to new thermoelectric materials. MRS Proceedings 1997, 478: 199.
Sheet G, Rosner H, Wirth S, et al. High spin polarization in the ferromagnetic filled skutterudites KFe4Sb12 and NaFe4Sb12. Phys Rev B 2005, 72: 180407.
Pei YZ, Chen LD, Zhang W, et al. Synthesis and thermoelectric properties of KyCo4Sb12. Appl Phys Lett 2006, 89: 221107.
Zhao XY, Shi X, Chen LD, et al. Synthesis and thermoelectric properties of Sr-filled skutterudite SryCo4Sb12. J Appl Phys 2006, 99: 053711.
Chen LD, Kawahara T, Tang XF, et al. Anomalous barium filling fraction and n-type thermoelectric performance of BayCo4Sb12. J Appl Phys 2001, 90: 1864–1868.
Kang Y, Yu F, Chen C, et al. High pressure synthesis and thermoelectric properties of Ba-filled CoSb3 skutterudites. J Mater Sci: Mater Electron 2017, 28: 8771–8776.
Koza MM, Johnson MR, Viennois R, et al. Breakdown of phonon glass paradigm in La-and Ce-filled Fe4Sb12 skutterudites. Nat Mater 2008, 7: 805–810.
Feldman JL, Singh DJ, Kendziora C, et al. Lattice dynamics of filled skutterudites: La(Fe, Co)4Sb12. Phys Rev B 2003, 68: 094301.
Alboni PN, Ji X, He J, et al. Thermoelectric properties of La0.9CoFe3Sb12–CoSb3 skutterudite nanocomposites. J Appl Phys 2008, 103: 113707.
Tang XF, Chen LD, Goto T, et al. Synthesis and thermoelectric properties of filled skutterudite compounds CeyFexCo4−xSb12 by solid state reaction. J Mater Sci 2001, 36: 5435–5439.
Pei YZ, Bai SQ, Zhao XY, et al. Thermoelectric properties of EuyCo4Sb12 filled skutterudites. Solid State Sci 2008, 10: 1422–1428.
Lamberton Jr. GA, Bhattacharya S, Littleton IV RT, et al. High figure of merit in Eu-filled CoSb3-based skutterudites. Appl Phys Lett 2002, 80: 598–600.
Zhang Q, Chen C, Kang Y, et al. Structural and thermoelectric characterizations of samarium filled CoSb3 skutterudites. Mater Lett 2015, 143: 41–43.
Artini C, Zanicchi G, Costa GA, et al. Correlations between structural and electronic properties in the filled skutterudite Smy(FexNi1–x)4Sb12. Inorg Chem 2016, 55: 2574–2583.
Rogl G, Grytsiv A, Bauer E, et al. Thermoelectric properties of novel skutterudites with didymium: DDy(Fe1−xCox)4Sb12 and DDy(Fe1−xNix)4Sb12. Intermetallics 2010, 18: 57–64.
Sayles TA, Baumbach RE, Yuhasz WM, et al. Superconductivity and crystalline electric field effects in the filled skutterudite PrRu4As12. Phys Rev B 2010, 82: 104513.
Shi X, Yang J, Chen LD, et al. Materials genome approach to accelerate thermoelectric material performance optimization. Sci Technol Rev 2015, 33: 60–63.
Shi X, Zhang W, Chen LD, et al. Filling fraction limit for intrinsic voids in crystals: Doping in skutterudites. Phys Rev Lett 2005, 95: 185503.
Zhao XY, Shi X, Chen LD, et al. Synthesis of YbyCo4Sb12/Yb2O3 composites and their thermoelectric properties. Appl Phys Lett 2006, 89: 092121.
Salvador JR, Yang J, Shi X, et al. Transport and mechanical properties of Yb-filled skutterudites. Philos Mag 2009, 89: 1517–1534.
Wang Y, Mao J, Jie Q, et al. Filling fraction of Yb in CoSb3 skutterudite studied by electron microscopy. Appl Phys Lett 2017, 110: 163901.
Lee J-K, Choi S-M, Seo W-S, et al. Thermoelectric properties of spark plasma sintered InxYbyLa0.3–x–yCo4Sb12 skutterudite system. Renew Energ 2012, 42: 36–40.
Dahal T, Jie Q, Joshi G, et al. Thermoelectric property enhancement in Yb-doped n-type skutterudites YbxCo4Sb12. Acta Mater 2014, 75: 316–321.
Ballikaya S, Uher C. Enhanced thermoelectric performance of optimized Ba, Yb filled and Fe substituted skutterudite compounds. J Alloys Compd 2014, 585: 168–172.
Son G, Lee KH, Choi S-M. Enhanced thermoelectric properties of melt-spun p-type Yb0.9Fe3CoSb12. J Electron Mater 2017, 46: 2839–2843.
Nolas GS, Fowler G, Yang J. Assessing the role of filler atoms on the thermal conductivity of filled skutterudites. J Appl Phys 2006, 100: 043705.
Rowe DM. Thermoelectrics Handbook: Macro to Nano. CRC Press, 2005.
Artini C, Carlini R. Influence of composition and thermal treatments on microhardness of the filled skutterudite Smy(FexNi1−x)4Sb12. J Nanosci Nanotechno 2017, 17: 1634–1639.
Yao Z, Li XY, Tang YS, et al. Genomic effects of the quenching process on the microstructure and thermoelectric properties of Yb0.3Co4Sb12. J Electron Mater 2015, 44: 1890–1895.
Xing J, Gu H, Gloter A, et al. Bismuth nanoprecipitation at grain boundaries during microstructural evolution in (Sr, Ba)TiO3 ceramics. Acta Mater 2007, 55: 5323–5332.
Gu H, Nagano T, Zhan G-D, et al. Dynamic evolution of grain-boundary films in liquid-phase-sintered ultrafine silicon carbide material. J Am Ceram Soc 2003, 86: 1753–1760.
Yao Z, Qiu P-F, Li X-Y, et al. Investigation on quick fabrication of n-type filled skutterudites. J Inorg Mater 2016, 31: 1375–1382.
Ding J, Gu H, Qiu P, et al. Creation of Yb2O3 nanoprecipitates through an oxidation process in bulk Yb-filled skutterudites. J Electron Mater 2013, 42: 382–388.
Zebarja di M, Esfarjani K, Dresselhaus MS, et al. Perspectives on thermoelectrics: From fundamentals to device alications. Energy Environ Sci 2012, 5: 5147–5162.
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China under Grant Nos. 51532006 and 11704238, Shanghai Municipal Science and Technology Commission of Shanghai Municipality under Grant No. 16DZ2260601, and State Administration of Foreign Experts Affairs of China 111 Project under Grant No. D16002.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mei, J., Yao, Z., Zhu, S. et al. Step distribution of Yb filling fraction during microstructural evolution in skutterudites. J Adv Ceram 8, 62–71 (2019). https://doi.org/10.1007/s40145-018-0291-3
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40145-018-0291-3