Abstract
A new series of flexible nanocomposite-solid polymer electrolyte (SPEs) in the form of poly(vinyl alcohol) (PVA) impregnated by core-shells polyaniline (PANI)-La2CuO4 (20:2 wt%) of nanofillers, 10 wt% LiClO4 as electrolyte and various amount 2, 4, 6, and 8 wt% of propylene carbonate, PC as plasticizer via solvent intercalation method. The obtained plasticized PVA-SPEs films were evaluated for their microstructural and morphological behaviors via X-ray diffraction (XRD), scanning electron microscopy (SEM), and Fourier transform infrared (FTIR) spectroscopy, respectively. The surface morphology of plasticized PVA-SPEs films illustrated the finer dispersion of inclusion fillers in the PVA matrix with increasing the dosage of PC content. FTIR spectra showed a reduction in the characteristic peaks of PVA in composite films and that denoted the interaction between PVA-OH and fillers. Optical findings exhibited higher absorbance of PVA-SPE in the visible region compared with pure PVA; in addition, the band-gap energy was reduced to 2.68 eV for PVA-SPE containing 8 wt% PC. The current-voltage characteristics showed a slight deviation for all PVA-SPE films denoting to non-ohmic behavior. Besides, the maximum ac-conductivity was found at 40.3 × 10−5 S/cm for PVA-SPE film containing 8 wt% PC with enhanced their specific capacitance by two folds compared with pure PVA. Mechanical testing showed that elongation at break has been increased attributed to increasing flexibility of polymeric segments with the increase in PC content.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
S. Kim and S. J. Park, Solid State Ion, 178, 973 (2007).
N. Shukla and A. K. Thakur, Ionics, 15, 357 (2009).
X. H. Flora, M. Ulaganathan, K. Kesavan, and S. Rajendran, Zeits. Phys. Chem., 228, 673 (2014).
N. Rajeswari, S. Selvasekarapandian, M. Prabu, S. Karthikeyan, and C. Sanjeeviraja, Bull. Mater. Sci., 36, 333 (2013).
A. Arya, S. Sharma, A. L. Sharma, D. Kumar, and M. Sadiq, Asian J. Eng. Appl. Technol., 5, 4 (2016).
J. Niu, C. Xiaohua, H. Dengwen, C. Liangren, W. Yaping, C. Jianwen, and Z. Yutian, Chem. Eng. J., 424, 130418 (2021).
C. Jianwen, Z. Yutian, C. Xiaohua, P. Duo, S. Gang, G. Zhanhu, and N. Nithesh, Adv. Funct. Mater., 31, 2104686 (2021).
J. Chen, F. Wang, G. Zhu, C. Wang, X. Cui, M. Xi, X. Chang, and Y. Zhu, ACS Appl. Mater. Interfaces, 13, 51567 (2021).
S. W. Woo, K. Dokko, H. Nakano, and K. Kanamura, J. Power Sources, 190, 596 (2009).
B. C. Kim, J. S. Kwon, J. M. Ko, J. H. Park, C. O. Too, and G. G. Wallace, Synth. Met., 160, 94 (2010).
Y. Zhao, H. Wei, M. Arowo, X. Yan, W. Wu, J. Chen, Y. Wang, and Z. Guo, Phys. Chem. Chem. Phys., 17, 1498 (2015).
A. G. El-Shamy and H. S. Zayied, Synth. Met., 259, 116218 (2020).
H. M. Gayitri, M. Q. A. Al-Gunaid, F. H. AL-Ostoot, N. Al-Zaqri, A. Boshaala, and A. P. Gnanaprakash, Polym. Bull., DOI: https://doi.org/10.1007/s00289-021-04056-3 (2022).
C. L. Zhu, S. W. Chou, S. F. He, W. N. Liao, and C. C. Chen, Nanotechnology, 18, 275604 (2007).
A. Bekhoukh, M. Mekhloufi, R. Berenguer, A. Benyoucef, and E. Morallon, Colloid Polym. Sci., 294, 1877 (2016).
L. Zu, X. Cui, Y. Jiang, Z. Hu, H. Lian, Y. Liu, Y. Jin, Y. Li, and X. Wang, Materials (Basel), 8, 1369 (2015).
B. S. Shashikala, M. Q. A. Al-Gunaid, B. H. Anupama, S. J. Anasuya, and Siddaramaiah, Polym. Plast. Technol. Mater., 60, 1656 (2021).
B. H. Anupama, M. Q. A. Al-Gunaid, and Siddaramaiah, Polym. Bull., 78, 3023 (2021).
S. Sugai, Y. Takayanagi, N. Hayamizu, and T. Muroi, J. Phys. Chem. Solids, 69, 3058 (2008).
L. Zhang, Y. Zhang, H. Dai, J. Deng, L. Wei, and H. He, Catal. Today, 153, 143 (2010).
E. R. Macam, B. M. Blackburn, and E. D. Wachsman, Sens. Actuators B Chem., 158, 304 (2011).
D. K. Pradhan, B. K. Samantaray, R. N. P. Choudhary, and A. K. Thakur, J. Power Sources, 139, 384 (2005).
M. Z. Luisiana, L. Tomas, C. B. Felipe, A. M. Z. Minerva, E. A. S. M. Marisela, D. L. G. Patricia, M. C. Guillermo, R. G. Francisco, N. Guadalupe, and S. V. Saúl, Mater. Chem. Phys., 261, 124180 (2021).
M. Amid, N. Nabian, and M. Delavar, Sep. Purif. Technol., 251, 117332 (2020).
M. Q. A. Al-Gunaid, A. M. N. Saeed, and Siddaramaiah, J. Appl. Polym. Sci., 135, 45852 (2018).
A. M. N. Saeed, A. Hezam, M. Q. A. AL-Gunaid, T. E. Somesh, and Siddaramaiah, Polym. Plast. Technol. Mater., 60, 132 (2021).
M. Q. A. Al-Gunaid, A. M. N. Saeed, H. M. Gayitri, and Siddaramaiah, Polym. Plast. Technol. Mater., 59, 469 (2020).
H. Gao, T. Jaing, B. Han, Y. Wang, J. Du, Z. Liu, and J. Zhang, Polymer, 45, 3017 (2004).
T. E. Somesh, M. Q. A. Al-Gunaid, B. S. Madhukar, and Siddaramaiah, J. Mater. Sci. Mater. Electron., 30, 37 (2019).
B. S. Shashikala, M. Q. A. Al-Gunaid, T. E. Somesh, S. J. Anasuya, and Siddaramaiah, Polym. Bull., DOI: https://doi.org/10.1007/s00289-021-03754-2 (2021).
F. Chen and P. Liu, Macromole. Res., 19, 883 (2011).
T. M. Wu and Y. W. Lin, Polymer, 47, 3576 (2006).
V. Sami, A. Lambert, and C. Oliver, APL Mater., 9, 041107 (2021).
S. A. Chandrasekarn, S. Palaniappan, and F. Chandezon, Mater. Lett., 62, 882 (2008).
A. M. N. Saeed, M. Q. A. AL-Gunaid, and Siddaramaiah, Polym. Plast. Technol. Mater., 57, 1554 (2018).
S. Honmute, S. V. Ganachari, R. Bhat, H. M. P. Kumar, D. S. Huh, and A. Vankataraman, Int. J. Sci. Res., 1, 102 (2012).
M. D. Bedre, D. Raghunandan, S. Basavaraj, and A. Venkataraman, Am. J. Mater. Sci., 2, 39 (2012).
H. M. Gayitri, M. Q. A. AL-Gunaid, Siddaramaiah, and A. P. G. Prakash, Polym. Bull., 77, 5005 (2020).
J. M. Gohil, A. Bhattacharya, and P. Ray, J. Polym. Res., 13, 161 (2006).
M. Hasik, A. Drelinkiiewicz, E. Wenda, C. Paluszkiewicz, and S. Quillard, J. Mol. Struct., 596, 89 (2001).
M. D. Bedre, S. Basavaraja, B. D. Salwe, V. Shivakumar, L. Arunkumar, and A. Venkataraman, Polym. Compos., 30, 1668 (2009).
P. K. Khanna, N. Singh, S. Charan, and A. K. Visawanath, Mater. Chem. Phys., 92, 214 (2005).
J. Deng, C. L. He, Y. Peng, J. Wang, X. Long, P. Li, and A. S. Chan, Synth. Met., 139, 295 (2003).
A. Mostafaei and A. Zolriasatein, Prog. Nat. Sci. Mater. Int., 22, 273 (2012).
M. Q. A. Al-Gunaid, T. E. Somesh H. M. Gayitri, F. H. Al-Ostoot, and Siddaramaiah, Polym. Plast. Technol. Mater., 59, 215 (2020).
H. M. Gayitri, M. Q. A. AL-Gunaid, B. S. Madhukar, Siddaramaiah, and A. P. G. Prakash, Polym. Plast. Technol. Mater., 58, 1110 (2019).
S. El-Sayed, T. Abel-Baset, A. Abou-Elfadl, and A. Hassen, Physica B, 464, 17 (2015).
K. Gurunathan, D. P. Amalnerkar, and D. C. Trivedi, Mater. Lett., 57, 1642 (2003).
R. Gangopadhyay, D. Amitabha, and G. Ghosh, Synth. Met., 123, 21 (2001).
H. M. Gayitri, M. Q. A. AL-Gunaid, Siddaramaiah, and A. P. G. Prakash, Indian J. Eng. Mater. Sci., 27, 320 (2020).
S. Koul, R. Chandra, and S. K. Dhawan, Polymer, 41, 9305 (2000).
B. G. Soares and M. E. Leyva, Mater. Eng., 292, 354 (2007).
J. K. Rao, A. Raizada, D. Ganguly, M. M. Mankad, S. V. Satyanarayana, and G. M. Madhu, Polym. Bull., 72, 2033 (2015).
M. Schroers, A. Kokil, and C. Weder, J. Appl. Polym. Sci., 93, 2883 (2004).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Acknowledgment: The authors are thankful to late. Dr. Siddaramaiah, Prof and Head, the department of Polymer Science and Technology, JSS Science and Technology University, Mysuru, India, for the support and guidance throughout this work. The authors extend their appreciation to the Researchers Supporting Project number (RSP-2021/396), King Saud University, Riyadh, Saudi Arabia.
Rights and permissions
About this article
Cite this article
Al-Gunaid, M.Q.A., Shashikala, B.S., Gayitri, H.M. et al. Characterization of Opto-Electrical, Electrochemical and Mechanical Behaviors of Flexible PVA/(PANI+La2CuO4)/LiClO4-PC Polymer Blend Electrolyte Films. Macromol. Res. 30, 650–658 (2022). https://doi.org/10.1007/s13233-022-0070-4
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13233-022-0070-4