Abstract
In this paper, silicon carbide (SiC) particles were successfully inserted into AA6061-T6 aluminium matrix using multi-pass friction stir processing (MPFSP). The effects of MPFSP and SiC particles on temperature distribution, microstructural evolution, and mechanical properties are being investigated in detail. Processing was carried out at a constant process parameter, i.e., tool rotational speed of 1100 rpm, tool traverse speed of 1.5 mm/sec, and tool tilt angle of 2° to modify the microstructure and mechanical properties of MPFSP. It has been observed that SiC particles are not homogeneously distributed after the first pass, and particles congregate in some places. On the other hand, fourth-pass FSP results in a uniform distribution of particles. Agglomeration of SiC particles decreases with an increase in the number of passes and is uniformly distributed in the fourth pass of FSP. It has been observed that peak temperature, particle size, grain size, and mechanical properties are all influenced by MPFSP. The microhardness has significantly improved with increasing the number of passes. After MPFSP, the peak temperatures of the first pass, second pass, third pass, and fourth pass were recorded as 339.67 °C, 330.64 °C, 320.20 °C, and 312.81 °C, respectively, on the advancing side (AS), and similarly, on the retreating side (RS), 334.03 °C, 322.11 °C, 312.30 °C, and 303.72 °C, respectively. The values of the maximum ultimate tensile strength (UTS) and 0.2% yield stress were observed as 231 MPa, 247 MPa, 296 MPa, 308 MPa, and 178 MPa, 188 MPa, 202 MPa, and 225 MPa with the first pass, second pass, third pass, and fourth pass, respectively. But at the same time, % elongation decreased with an increase the number of passes.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Data availability
The authors confirm that the data supporting the findings of this study are available within the article.
References
Pasha MA, Reddy PR, Laxminarayana P, Khan IA (2016) Mechanical behavior of silicon carbide reinforced friction stir welded joint of aluminium alloy 6061. Int J Eng Res 5(05)
Zuhailawati H, Anasyida AS (2019) Investigation of the microstructure, mechanical and wear properties of AA6061-T6 friction stir weldments with different particulate reinforcements addition. J Mater Res Technol 8(5):3917–3928
Rathee S, Maheshwari S, Siddiquee AN, Srivastava M (2018) A review of recent progress in solid state fabrication of composites and functionally graded systems via friction stir processing. Crit Rev Solid State Mater Sci 43(4):334–366
Sethi D, Acharya U, Kumar S, Shekhar S, Roy BS (2022) Effect of tool rotational speed on friction stir welded AA6061-T6 scarf joint configuration. Advanced Composites and Hybrid Materials, pp 1–16
Elangovan K, Balasubramanian V, Valliappan M (2008) Effect of tool pin profile and tool rotational speed on mechanical properties of friction stir welded AA6061 aluminium alloy. Mater Manuf Processes 23(3):251–260
Thomas WM, Nicholas ED, Needham JC, Murch MG, Templesmith P, Dawes CJ (1991) International Patent Application No. PCT/GB92/02203 and GB Patent Application No. 9125978.8
Selvakumar S, Dinaharan I, Palanivel R, Babu BG (2017) Development of stainless steel particulate reinforced AA6082 aluminum matrix composites with enhanced ductility using friction stir processing. Mater Sci Eng, A 685:317–326
Dinaharan I, Balakrishnan M, Selvam JDR, Akinlabi ET (2019) Microstructural characterization and tensile behavior of friction stir processed AA6061/Al2Cu cast aluminum matrix composites. J Alloys Compd 781:270–279
Dawes CJ (1995) Friction stir joining of aluminium alloys. Bulletin 6
Ceschini L, Boromei I, Minak G, Morri A, Tarterini F (2007) Effect of friction stir welding on microstructure, tensile and fatigue properties of the AA7005/10 vol.% Al2O3p composite. Compos Sci Technol 67(3–4):605–615
Sharifitabar M, Sarani A, Khorshahian S, Afarani MS (2011) Fabrication of 5052Al/Al2O3 nanoceramic particle reinforced composite via friction stir processing route. Mater Des 32(8–9):4164–4172
Sharma A, Sharma VM, Mewar S, Pal SK, Paul J (2018) Friction stir processing of Al6061-SiC-graphite hybrid surface composites. Mater Manuf Processes 33(7):795–804
Sharma DK, Patel V, Badheka V, Mehta K, Upadhyay G (2019) Fabrication of hybrid surface composites AA6061/(B4C+ MoS2) via friction stir processing. J Tribol 141(5)
Sharma V, Prakash U, Kumar BM (2015) Surface composites by friction stir processing: A review. J Mater Process Technol 224:117–134
Khademi AR, Afsari A (2017) Fabrications of surface nanocomposite by friction stir processing to improve mechanical and microstructural properties of low carbon steel. Trans Indian Inst Met 70(5):1193–1198
Alavi Nia A, Nourbakhsh SH (2016) Microstructure and mechanical properties of AZ31/SiC and AZ31/CNT composites produced by friction stir processing. Trans Indian Inst Met 69(7):1435–1442
Akramifard HR, Shamanian M, Sabbaghian M, Esmailzadeh M (2014) Microstructure and mechanical properties of Cu/SiC metal matrix composite fabricated via friction stir processing. Mater Des 1980–2015(54):838–844
Mishra RS, Ma ZY, Charit I (2003) Friction stir processing: a novel technique for fabrication of surface composite. Mater Sci Eng, A 341(1–2):307–310
Zahmatkesh B, Enayati MH (2010) A novel approach for development of surface nanocomposite by friction stir processing. Mater Sci Eng, A 527(24–25):6734–6740
Shafiei-Zarghani A, Kashani-Bozorg SF, Zarei-Hanzaki A (2009) Microstructures and mechanical properties of Al/Al2O3 surface nano-composite layer produced by friction stir processing. Mater Sci Eng, A 500(1–2):84–91
Sahraeinejad S, Izadi H, Haghshenas M, Gerlich AP (2015) Fabrication of metal matrix composites by friction stir processing with different particles and processing parameters. Mater Sci Eng, A 626:505–513
Kumar A, Mahapatra MM, Jha PK, Mandal NR, Devuri V (2014) Influence of tool geometries and process variables on friction stir butt welding of Al–4.5% Cu/TiC in situ metal matrix composites. Mater Des 59:406–414
Dinaharan I, Murugan N (2012) Effect of friction stir welding on microstructure, mechanical and wear properties of AA6061/ZrB2 in situ cast composites. Mater Sci Eng, A 543:257–266
Yuvanarasimman P, Malayalamurthi R (2018) Studies on fractures of friction stir welded Al matrix SiC-B4C reinforced metal composites. SILICON 10(4):1375–1383
Mishra RS, Ma ZY (2005) Friction stir welding and processing. Mater Sci Eng R Rep 50(1–2):1–78
Jamalian HM, Ramezani H, Ghobadi H, Ansari M, Yari S, Givi MKB (2016) Processing–structure–property correlation in nano-SiC-reinforced friction stir welded aluminum joints. J Manuf Process 21:180–189
Rathee S, Maheshwari S, Siddiquee AN (2018) Issues and strategies in composite fabrication via friction stir processing: a review. Mater Manuf Processes 33(3):239–261
Srivastava M, Rathee S (2021) A study on the effect of incorporation of SiC particles during friction stir welding of Al 5059 alloy. SILICON 13(7):2209–2219
Sethi D, Acharya U, Kumar S, Shekhar S, Roy BS (2021) Effect of reinforcement particles on friction stir welded joints with scarf configuration: an approach to achieve high strength joints. Silicon 1–14
Sun YF, Fujii H (2011) The effect of SiC particles on the microstructure and mechanical properties of friction stir welded pure copper joints. Mater Sci Eng, A 528(16–17):5470–5475
Dolatkhah A, Golbabaei P, Givi MB, Molaiekiya F (2012) Investigating effects of process parameters on microstructural and mechanical properties of Al5052/SiC metal matrix composite fabricated via friction stir processing. Mater Des 37:458–464
Kumar M, Kumar R, Kore SD (2020) Study of temperature distribution and material flow in friction stir welding of AA6061-T6.
Rathee S, Maheshwari S, Siddiquee AN, Srivastava M (2019) Investigating the effects of SiC particle sizes on microstructural and mechanical properties of AA5059/SiC surface composites during multi-pass FSP. SILICON 11(2):797–805
Mehdi H, Mishra RS (2021) Effect of multi-pass friction stir processing and SiC nanoparticles on microstructure and mechanical properties of AA6082-T6. Adv Ind Manuf Eng 3:100062
Jain R, Pal SK, Singh SB (2016) A study on the variation of forces and temperature in a friction stir welding process: a finite element approach. J Manuf Process 23:278–286
Kumar AV, Balasrinivasan M, Kumar RV, Balachandar K, Sivakumar C (2020) Temperature distribution study of friction stir welded aluminum alloy 7075–T6 joints reinforced with SiC powders. Materials Today: Proceedings 22:1333–1340
Mehdi H, Mishra RS (2020) Influence of friction stir processing on weld temperature distribution and mechanical properties of TIG-welded joint of AA6061 and AA7075. Trans Indian Inst Met 73(7):1773–1788
Rathee S, Maheshwari S, Siddiquee AN, Srivastava M (2017) Investigating effects of groove dimensions on microstructure and mechanical properties of AA6063/SiC surface composites produced by friction stir processing. Trans Indian Inst Met 70(3):809–816
Kumar N, Gautam G, Gautam RK, Mohan A, Mohan S (2016) Wear, friction and profilometer studies of insitu AA5052/ZrB2 composites. Tribol Int 97:313–326
Zapata-Solvas E, Jayaseelan DD, Lin HT, Brown P, Lee WE (2013) Mechanical properties of ZrB2-and HfB2-based ultra-high temperature ceramics fabricated by spark plasma sintering. J Eur Ceram Soc 33(7):1373–1386
Hashmi AW, Mehdi H, Mishra RS, Mohapatra P, Kant N, Kumar R (2022) Mechanical properties and microstructure evolution of AA6082/sic nanocomposite processed by multi-pass FSP. Trans Indian Inst Met 1–14
Chang CI, Lee CJ, Huang JC (2004) Relationship between grain size and Zener-Holloman parameter during friction stir processing in AZ31 Mg alloys. Scripta Mater 51(6):509–514
Azimzadegan T, Serajzadeh S (2010) An investigation into microstructures and mechanical properties of AA7075-T6 during friction stir welding at relatively high rotational speeds. J Mater Eng Perform 19(9):1256–1263
Fuller CB, Mahoney MW, Calabrese M, Micona L (2010) Evolution of microstructure and mechanical properties in naturally aged 7050 and 7075 Al friction stir welds. Mater Sci Eng, A 527(9):2233–2240
Sethi D, Acharya U, Shekhar S, Roy BS (2022) Applicability of unique scarf joint configuration in friction stir welding of AA6061-T6: analysis of torque, force, microstructure and mechanical properties. Defence Technology 18(4):567–582
Kumar S, Acharya U, Sethi D, Medhi T, Roy BS, Saha SC (2020) Effect of traverse speed on microstructure and mechanical properties of friction-stir-welded third-generation Al–Li alloy. J Braz Soc Mech Sci Eng 42(8):1–13
Pandey C, Mahapatra MM, Kumar P, Thakre JG, Saini N (2019) Role of evolving microstructure on the mechanical behaviour of P92 steel welded joint in as-welded and post weld heat treated state. J Mater Process Technol 263:241–255
Ceschini L, Boromei I, Minak G, Morri A, Tarterini F (2007) Microstructure, tensile and fatigue properties of AA6061/20 vol.% Al2O3p friction stir welded joints. Compos A: Appl Sci Manuf 38(4):1200–1210
Marzoli LM, Strombeck AV, Dos Santos JF, Gambaro C, Volpone LM (2006) Friction stir welding of an AA6061/Al2O3/20p reinforced alloy. Compos Sci Technol 66(2):363–371
Hamdollahzadeh A, Bahrami M, Nikoo MF, Yusefi A, Givi MB, Parvin N (2015) Microstructure evolutions and mechanical properties of nano-SiC-fortified AA7075 friction stir weldment: The role of second pass processing. J Manuf Process 20:367–373
Banik A, Roy BS, Barma JD, Saha SC (2018) An experimental investigation of torque and force generation for varying tool tilt angles and their effects on microstructure and mechanical properties: Friction stir welding of AA 6061–T6. J Manuf Process 31:395–404
Barmouz M, Asadi P, Givi MB, Taherishargh M (2011) Investigation of mechanical properties of Cu/SiC composite fabricated by FSP: Effect of SiC particles’ size and volume fraction. Mater Sci Eng, A 528(3):1740–1749
Mehdi H, Mishra RS (2022) Modification of microstructure and mechanical properties of AA6082/ZrB2 processed by multipass friction stir processing. J Mater Eng Perform 1–11
Maeda M, Liu H, Fujii H, Shibayanagi T (2005) Temperature field in the vicinity of FSW-tool during friction stir welding of aluminium alloys. Weld World 49(3):69–75
Acknowledgements
The first author wishes to thank the Ministry of Human Resource Development of India for giving funding in the form of a fellowship. The authors would like to thank the MSE department, ACMS at IIT Kanpur (specifically Mrs. Samata Samal, Anoop Kumar Raut for microscopic imaging analysis and tensile testing) for their cooperation and smooth testing.
Author information
Authors and Affiliations
Contributions
Setu Suman: Conceptualization, Writing—original draft, Investigation, Visualization, Durjyodhan Sethi: Formal analysis, Methodology, resources, Manish Bhargava: review & editing Barnik Saha Roy: review & editing.
Corresponding author
Ethics declarations
Ethics Approval
Not Applicable.
Consent for Publication
Consent was obtained from all the authors for the publication of this manuscript.
Consent to Participate
Not Applicable.
Conflict of Interest
The authors declare that they have no known competing financial interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Suman, S., Sethi, D., Bhargava, M. et al. Investigating the Effect of Multi-pass Friction Stir Processing of SiC Particles on Temperature Distribution, Microstructure and Mechanical Properties of AA6061-T6 Plate. Silicon 15, 1621–1633 (2023). https://doi.org/10.1007/s12633-022-02108-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12633-022-02108-5