Abstract
For the first time, the ability of dyeing the montmorillonite (Mt) mineral with reactive dye aiming to prepare a new nanopigment was investigated and the optimum conditions were determined. The prepared nanopigment was characterized by Fourier-transform infrared spectra (FTIR), transmission electron microscope (TEM), Brunauer-Emmett-Teller (BET), reflectance spectrophotometer (RS) and colorimetry analyses. The results showed that the dye molecules were attached to the hydroxyl groups of Mt plates through a covalent linkage. Also, the BET surface area values slightly increased after the dyeing process due to the separation of Mt plates and the reduction of particle size because of penetration of dye molecules among the plates. Colorimetry analysis revealed that the intercalation of dye molecules was depended on dye concentration and number of reactive sites on the Mt surface. The prepared nanopigment was used for dyeing the polyester fabric in high pressure and temperature conditions. The SEM, colorimetry, electromagnetic reflectance, flammability, and TGA tests were performed to investigate the properties of fabrics. Results indicated that intercalation of Mt nanopigment in the polyester fiber enhances the flame retardant, electromagnetic reflection and breathability of fabrics. Also, the optimum amount of nanopigment in the dyeing process was reported. It can be suggested that the prepared fabric can be a good candidate for utilizing in military and electronic aspects.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
References
W. Ali, P. Sultana, M. Joshi, and S. Rajendran, Adv. Mater. Res.-Switz., 64, 399 (2016).
A. Walawska, B. Filipowska, and E. Rybicki, Fibres Text. East. Eur., 11, 41 (2003).
K. Kunttou, S. Hongyo, and S. Maeda, Text. Res. J., 75, 149 (2005).
O. Glenz, W. Beckmanann, and D. W. Wunde, J. Soc. Dyers and Colourists, 76, 141 (1959).
F. J. Carrion Fite, Text. Res. J., 65, 362 (1995).
A. K. Choudhury, “Textile Preparation and Dyeing”, Science Publishers, USA, 2006.
M. Montazer, J. Taheri, and T. Harifi, J. Appl. Polym. Sci., 124, 342 (2012).
M. Parvinzadeh Gashti, I. Ebrahimi, and M. Pousti, Curr. Appl. Phys., 15, 1075 (2015).
S. Adeel, F.-U. Rehman, R. Hanif, M. Zuber, E.-U. Haq, and M. Munir, Asian J. Chem., 26, 830 (2014).
M. Parvinzadeh Gashti, R. Rashidian, A. Almasian, and A. Badakhshan Zohouri, Pigm. Resin. Technol., 42/3, 175 (2013).
E. Ruiz-Hitzky, P. Aranda, and J. M. Serratosa in “Handbook of Layered Materials” (S. M. Auerbach, K. A. Carrado, and P. K. Dutta Eds.), pp. 91–154, Marcel Dekker, New York, 2004.
S. Pavlidou and C. D. Papaspyrides, Prog. Polym. Sci., 33, 1119 (2008).
H. Xu, X. Shi, Y. Lv, and Z. Mao, Text. Res. J., 83, 321 (2013).
D. Wang, Y. Li, G. L. Pum, C. Wang, P. Wang, W. Zhang, and Q. Wang, Appl. Catal., B, 168–169, 25 (2015).
F. Akhavan and M. Montazer, Ultrason. Sonochem., 21, 681 (2013).
A. Behzadnia, M. Montazer, A. Rashidi, and M. Mahmoudi Rad, Ultrason. Sonochem., 21, 1815 (2014).
I. Perelshtein, G. Applerot, N. Perkas, G. Guibert, S. Mikkhailov, and A. Gedanken, Nanotechnology, 19, 245705 (2008).
V. Allahyarzadeh, M. Montazer, N. H. Nejad, and N. Samadi, Polym. Biomed. Appl., 129, 892 (2013).
L. Peng, R. Guo, J. Lan, S. Jiang, and S. Lin, Appl. Surface Sci., 386, 151 (2016).
T. Harifi and M. Montazer, Dyes Pigment., 97, 440 (2013).
M. I. Beltrán, V. Benavente, V. Marchante, H. Dema, and A. Marcilla, Appl. Clay Sci., 97–98, 43 (2014).
S. Raha, I. Ivanov, N. H. Quazi, and S. N. Bhattacharya, Appl. Clay Sci., 42, 661 (2009).
J. Sivathasan, Masters Thesis, RMIT University, Melbourne, 2007.
N. S. E. Ahmed, Dyes Pigment., 65, 221 (2005).
G. Monti, L. Catarinucci, and L. Tarricone, Microw Opt. Technol. Lett., 52, 1700 (2010).
H. Dave, L. Ledwani, and S. K. Nema, Plasma Chem. Plasma Process, 36, 599 (2016).
S. R. K. Velho, L. F. W. Brum, C. O. Petter, J. Henrique Z. dos Santos, S. Simuni, and W. Helmut Kappa, Dyes Pigment., 136, 248 (2017).
N. M. Mahmoodi, J. Abdi, and F. Najafi, J. Colloid Interf. Sci., 400, 88 (2013).
A. Almasian, F. Najafi, M. Mirjalili, M. Parvinzadeh Gashti, and Gh. Chizari Fard, J. Taiwan Inst. Chem. E, 67, 306 (2016).
M. Parvinzadeh, S. Moradian, A. Rashidi, and M. E. Yazdanshenas, Appl. Surf. Sci., 256, 2792 (2010).
L. B. D. Paiva, A. R. Morales, and F. R. V. Diaz, Appl. Clay Sci., 42, 8 (2008).
M. Parvinzadeh Gashti, A. Almasian, M. Parvinzadeh Gashti, Sensor Actuat A-Phys., 187, 1 (2012).
E. M. A. Khalil, F. H. ElBatal, Y. M. Hamdy, H. M. Zidan, M. S. Aziz, and A. M. Abdelghany, Physica B, 405, 1294 (2010).
A. Almasian, M. E. Olya, and N. M. Mahmoodi, J. Taiwan Inst. Chem. E, 49, 119 (2015).
M. Parvinzadeh and Sh. Eslami, Res. Chem. Intermed., 37, 771 (2011).
C. A. Hacker, K. A. Anderson, L. J. Richter, and C. A. Richter, Langmuir, 21, 882 (2005).
A. Almasian, N. M. Mahmoodi, and M. E. Olya, J. Ind. Eng. Chem., 32, 85 (2015).
V. Singha, A. Kumar Sharma, and R. Sanghi, J. Hazard Mater., 166, 327 (2009).
C.-C. Wang, L.-C. Juang, T.-C. Hsu, C.-K. Lee, J.-F. Lee, and F.-C. Huang, J. Colloid Interf. Sci., 273, 80 (2004).
Z. Yi, F. Jihong, and C. Shuilin, Color. Technol., 121, 76 (2005).
J. D. Sudha, S. Sivakala, R. Prasanth, V. L. Reena, and P. Radhakrishnan Nair, Compos. Sci. Technol., 69, 358 (2009).
M. C. Golt, S. Yarlagadda, and J. W. Gillespie Jr., J. Thermoplast. Compos. Mater., 22, 569 (2009).
M. Parvinzadeh Gashti and A. Almasian, Compos. Part B-Eng., 43, 3374 (2012).
M. Parvinzadeh Gashti, M. Y. Navid, and M. H. Rahimi, J. Appl. Polym. Sci., 125, 143 (2012).
J. Njuguna, K. Pielichowski, and S. Desai, Polym. Adv. Technol., 19, 947 (2008).
D. W. Litchfield and D. G. Baird, Polymer, 49, 5027 (2008).
M. Parvinzadeh Gashti and A. Almasian, Compos. Part B-Eng., 52, 340 (2013).
M. Validi, S. Bazgir, A. Rashidi, and M. E. Yazdanshenas, Ceram-Silikaty, 56, 152 (2012).
J. B. Dahiya and K. Kumar, J. Sci. Ind. Res., 68, 548 (2009).
M. Parvinzadeh Gashti and A. Almasian, Compos. Part-B Eng., 45, 282 (2013).
A. Almasian, M. L. Jalali, Gh. Chizari Fard, and L. Maleknia, Chem. Eng. J., 326, 1232 (2017).
A. Almasian, M. E. Olya, and N. M. Mahmoodi, J. Taiwan Inst. Chem. Eng., 49, 119 (2015).
S. R. Shukla, A. M. Harad, and L. S. Jawale, Polym. Degrad. Stabil., 94, 604 (2009).
D. Patterson and R. P. Sheldon, Trans. Faraday Soc., 55, 1254 (1959).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Almasian, A., Mirjalili, M., Maleknia, L. et al. Preparation of Multi-Functional Polyester Fabrics with the Use of a New Organo-Clay Nanopigment in High Temperature/High Pressure Condition. Fibers Polym 20, 1387–1395 (2019). https://doi.org/10.1007/s12221-019-8524-9
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12221-019-8524-9