Abstract
Nanoscale zero-valent iron particles were investigated as an antibacterial agent against two Gram-positive bacteria; Staphylococcus aureus NRRL B-313 (S. aureus), Bacillus subtilus NRC (B. subtilus), and two Gram-negative bacteria; Escherichia coli NRC B-3703 (E. coli), Pseudomonas aeruginosa NRC B-32 (Ps. aeruginosa). The characterization of synthesized nZVI particles was obtained by XRD, SEM, EDX, and TG analyses. The results demonstrated that the nZVI particles have a spherical shape, mean crystalline size of 44.43 nm, and exhibited a good chemical and thermal stability performance under different physical conditions. The bacterial suspensions were subjected to the treatment using nZVI particle suspensions with a concentration of 10 mg/mL. The minimum inhibitory concentration of nZVI particles was determined using the well diffusion assay method and found to be 15, 10, 10, and 5 mg for the following four strains; S. aureus, B. subtilus, E. coli, and Ps. aeruginosa, respectively. The biological treatment results of municipal wastewater using nZVI particles revealed that the counts of total bacteria, total coliform, fecal coliform, S. aureus, fecal Streptococcus, and E. coli were decreased to 44.29%, 51.76%, 90.95%, 46.67%, 33.33%, and 93.89%, respectively, while the Ps. aeruginosa not detected in the wastewater sample. The enhanced inactivation performance of nZVI nanoparticles was mainly attributed to the reactive oxygen species (ROS) production, releasing of iron corrosion products like Fe2+/Fe3+ ions, and direct friction of nZVI particles with bacterial cells membranes. In addition, the nZVI particles presented a striking disinfection behavior in comparison with other widespread disinfection technologies such as chlorination. Accordingly, the obtained results introduce the nZVI particles as a promising disinfection technology.
Graphical abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Various forms of metal and metal oxide nanoparticles have been investigated as antimicrobial agents (Cheeseman et al. 2020; Alt et al. 2004). These compounds have possessed a wide range of applications as disinfectants in the water treatment (Chou et al. 2005), in the biomedical fields (Alt et al. 2004; Furno et al. 2004), the textiles (Jeong et al. 2005; Hamdy et al. 2018), anti-biofilm agents (Sambhy et al. 2006), and as catalysts (Elawwad et al. 2020).
The presence of pathogenic microorganisms in the water sources represents various health risks, where many infectious disease microbes affecting individuals in a community can find their way into municipal sewage. Most of the organisms found in untreated wastewater are known as enteric organisms; they inhabit the intestinal tract where they can cause diseases, such as diarrhea (Al-Gheethi et al. 2018). Table 1 lists the infectious agents potentially present in raw domestic wastewater and the diseases associated with each organism. Montgomery and Elimelech (2007) have indicated that many people die annually from the diseases transmitted over contaminated water. Among these pollutants, those water-borne fungi, bacteria, and viruses showed great danger (Khezerlou et al. 2018; Pandey et al. 2014). Besides, it was found that during the wastewater treatment, the generated biosolids contained a variety of microorganisms (X-q et al. 2007; Paez-Rubio et al. 2007). When these bio-solids have been disposed to the waterways, those microbial species can transport over large distances, thus presenting serious health problems (Paez-Rubio et al. 2007). Whereas the adequate treatment of excreta and wastewater to protect the natural environment besides reducing water wastage and avoiding overexploitation fall among the direct goals of sustainable development according to UNESCO reports. Therefore, in the absence of proper drainage systems, sewage mixes with stormwater causing further pollution. It is estimated that up to 90% of all wastewater in developing countries is discharged untreated directly into rivers, lakes, or the oceans, causing major environmental and health risks (Connor 2015). Consequently, there was a great need for the biological pretreatment for the drinking- and wastewater, which helps in minimizing the associated biological health hazard for these streams.
The metal/metal oxides nanoparticles such as magnesium oxide (Stoimenov et al. 2002), magnetite (Hamdy 2021), copper (Hsiao et al. 2006), zinc oxide (Sánchez-López et al. 2020), and silver (Kaur et al. 2013; Sambhy et al. 2006; Morones et al. 2005) have exhibited remarkable antimicrobial properties. However, the antimicrobial activity mechanism of these compounds was still not clearly understood. Hence, a diversity of hypotheses had been proposed, including cell structures physical disruption (Stoimenov et al. 2002), permeability and respiration disturbance (Morones et al. 2005), and damage of the enzymatic proteins or the DNA by the metal ions that release from the nanoparticles (Gogoi et al. 2006). Among metal nanoparticles, the nZVI nanoparticles had been utilized in many fields such as the permeable reactive barriers for remediation of the groundwater contaminated with halogenated solvents (Farrell et al. 2000), and removal of heavy metals (Hamdy et al. 2021).
when Fe0 nanoparticles were used, the electron directly transferred from the metallic iron to the contaminants had been recognized as the main pathway of contaminant transformation in the subsurface (Hamdy et al. 2019a). The contaminants could also be oxidized in the presence of oxygen by hydroxyl radical and other oxidants generated during the corrosion process of Fe0 nanoparticles (Joo et al. 2005; Hamdy et al. 2019b). Accordingly, the nZVI nanoparticles had exhibited that it was a strong substitute for the granular Fe0 particles (Li et al. 2006). The nZVI nanoparticles have been distinguished from the granular Fe0 particles due to the improvement in their high mobility and reactivity, because of their higher surface area (Li et al. 2006; Hydutsky et al. 2007). Many studies were interested in the antimicrobial activity of metal nanoparticles and especially the widespread usage of nZVI nanoparticles for environmental remediation. Therefore, the nZVI nanoparticles were subjected to the investigation as an antimicrobial agent (Sun et al. 2019; Chen et al. 2013; Diao and Yao 2009). Furthermore, the previous investigators have mentioned the possibility of using the other kinds of iron-based compounds like microscale iron powder as bacteriophage inactivators (You et al. 2005), or iron oxide-coated sands (Ryan et al. 2002). However, the antimicrobial activity of these compounds demands relatively long treatment periods (for days or weeks), or high doses to be effective. Besides, it has an insignificant impact compared to nZVI particles.
Several previous studies report that the magnetic properties of nZVI resulted in significant bacterial removal, and the removal efficiency largely depends on the Fe0/Fe3O4 shell compositions, bacteria type, and bacteria concentrations. ROS generally includes superoxide (·\( {O}_2^{-} \)), hydrogen peroxide (H2O2) (oxidation potential 1.8 V), and hydroxyl radical (·OH) which are the most harmful radicals. Usually, the hydroxyl radicals form in the presence of transition metals such as iron during the redox cycle (Gold et al. 2018; Arakha et al. 2015). To defend against oxidative stress induced by reactive oxygen species (ROS), bacteria have developed their fighting mechanisms. In response to excess iron levels, bacteria not only regulate mineral balance through the use of metalloregulatory proteins, but also by releasing ROS scavengers such as peroxidases, catalase and, superoxide dismutase (SOD), or by complexing Fe2+ ions into an inoffensive form (Diao and Yao 2009; Miethke and Marahiel 2007). To regulate iron levels, the bacteria use a highly specific transport system for storage high levels of iron ions through secreting low molecular weight compounds and the siderophores, which bind to Fe3+ ions, and the ferric siderophores are then actively transported back into bacterial cells. Whilst, when the iron is in excess, the inactivation of bacteria occurs due to the formation and accumulation of hydroxyl radicals (Xu et al. 2019). Another study indicated that superoxide (produced by aerobic organisms) could accelerate DNA damage by raising levels of free iron in cells indicating that control of iron balance and responses to oxidative stress are actively coordinated by cells (Oprčkal et al. 2017).
In this study, we aimed to examine the synthesized nZVI nanoparticles as a bactericidal agent with various dosages versus the Gram (+) bacteria (S. aureus and B. subtilus) and the Gram (−) bacteria (E. coli and Ps. aeruginosa). Synthesis and precise characterization of nZVI nanoparticles using X-ray diffraction (XRD), scanning electron microscope (SEM), energy-dispersive X-ray (EDX), and thermogravimetric (TG) analyzers were reported as well as their chemical and thermal properties. The growth inhibition and the microbial inactivation mechanism of nZVI nanoparticles against different pathogen bacteria which including the release of Fe2+ and Fe3+ ions, ROS formation, and direct contact of nZVI particles with bacteria membranes were discussed in details. Furthermore, the sterilization effect and bioactivity of nZVI nanoparticles towards pathogenic sewage wastewater-bacteria, and their capability to dispose of these microorganisms from the real samples were studied besides comparing the antibacterial effect of nZVI particles with common wastewater treatment/disinfection technologies. In addition, from a microbiological standpoint, the results of antimicrobial activity of nZVI nanoparticles against water-contamination indicators (coliforms and E. coil) were scrutinized and were compared with limits of the international standards that regulate the reuse of reclaimed water in the different purposes for example; the agriculture and irrigation. Finally, the findings from this work provided further evidence that makes the nZVI nanoparticles are a promising antimicrobial agent for water disinfection.
Materials and methods
Synthesis of antimicrobial nZVI nanoparticles
An analytical grade of ferric chloride (FeCl3.6H2O, Loba Chemie, India), and sodium borohydride (NaBH4, Winlab Co., UK) were used without further purification for the synthesis process of nZVI nanoparticles. All reagents were prepared using double-deionized water (DDI) throughout this study. The nZVI nanoparticles were synthesized by the chemical reduction method via the reduction of ferric ions using the borohydride agent. 0.5 g of ferric chloride was dissolved in a 4/1 (v/v) ethanol/water mixture. About 0.33 mol/L of sodium borohydride solution was poured into a burette and then added dropwise to the Fe(III) solution with continuous stirring of the mixture. Once drops of the borohydride solution were added to the ferric ions solution, a black precipitate of nZVI nanoparticles appeared. When the borohydride solution was completely added, the prepared nZVI nanoparticles were left for 15 min with stirring. Subsequently, the formed nZVI nanoparticles have separated by vacuum filtration using a 0.45 μm Whatman filter paper. Then, the precipitate had been washed with 4/1 (v/v) ethanol/water mixture followed by washing three times with ethanol only. Finally, the synthesized nZVI nanoparticles were undergone dried in a thermal oven at 60 °C overnight. The redox reaction can be represented by eq. (1):
Figure 1 represents a flowchart for the synthesis process of nZVI nanoparticles.
Characterization apparatuses
X-ray diffraction instrument (X-Pert – PRO – PANalytical Netherland) was used to perform an XRD analysis of the nZVI particles at 30 mA and 45 kV. CuKα radiation and graphite monochromator were used to yield X-rays with a wavelength of 1.54 Å. The nZVI sample was scanned in the range of 4–80° with a rate of 0.5 s. The estimated value of the crystalline diameter was calculated using the Scherer equation:
where Dp is the crystalline diameter of particle (nm), λ is the CuKα radiation wavelength (Å), i.e., 0.154 nm, β is the full width at half maximum (FWHM) in radians, and θ is the Bragg angle obtained from 2θ corresponding to maximum peak intensity (°) (Soliman and Vshivkov 2019). For a spherical particle with a diameter of D, the specific surface area (SSA) can be calculated by the following equation:
where ρ is the density of the solid particle (7800 kg/m3 for iron) (Sun et al. 2006).
The morphology, size, and composition of the nZVI nanoparticles were investigated using a scanning electron microscope (FE-SEM, Quanta FEG 250, Philips, USA) equipped with EDX. The nZVI powder was stacked on gluey carbon tape which is supported on a metallic disk and then has been submitted to the SEM equipment. The elemental analysis of the nZVI sample was assayed using the EDX analyzer to determine the surface structure composition of the individual points or to map out the lateral distribution of the elements from the imaged area, and estimate their proportion at different positions, consequently giving an overall mapping of the sample.
Thermogravimetric analyzer – (TGA-50, Shimadzu, Japan) was used to perform thermal analysis on an nZVI sample weighed 8.678 mg under a nitrogen atmosphere and using a platinum pan in temperature ranges of 0–1100 °C with a heating rate of 10 °C/min compared with alumina (Al2O3) as a reference powder.
Stability of nZVI nanoparticles
The chemical and thermal stability of nZVI nanoparticles under different conditions of pH and temperatures were evaluated. Chemical stability was performed by equilibrating nZVI particles with a series of solutions that have pH values from 2 to 12 at 25 °C for 2 h. Several conical flasks contained 100 mL of distilled water adjusted to the selected pH values were shaken together with approximately 0.1 g of powdered nZVI for each flask. The corresponding number of filter papers were dried in an oven at 103 °C for 1–2 h, cooled in a desiccator, and then weighed. At the end of the shaken period, the nZVI nanoparticle residues were filtered using the filter papers that were previously dried and rinsed 3 times with distilled water to remove the excess of acids or alkalis. Finally, the nZVI nanoparticles residues along with filter papers were dried in the oven at 103 °C for 2 h, cooled in a desiccator, and then weighed. The thermal stability of nZVI nanoparticles was determined by weighed 0.1 g of nZVI powder in a beaker and exposed it to different temperatures from 45 to 100 °C for 2 h, cooled, and re-weighed. The weight loss (%) of nZVI was calculated as follows (Nigam Ahuja et al. 2020):
Bacterial strains and media
Four bacterial strains were used to test the germicidal activity of the nZVI nanoparticles. Two of the bacterial strains were Gram (+) Staphylococcus aureus NRRL B-313 and Bacillus subtilus NRC, while the others were Gram (−) Escherichia coli NRC B-3703 and Pseudomonas aeruginosa NRC B-32. Nutrient agar media was used for bacterial strain growth. The liquid medium was sterilized using autoclave at 121 °C for 15 min and then sub-cultured. Subsequently, the solid media were used for the agar well diffusion assay (Suganya et al. 2012).
Well diffusion assay method
Determination of the antibacterial activity of nZVI nanoparticles
About 20 mL from the nutrient agar medium was placed into 10 mL Petri dishes, and 0.1 mL of fresh cultures for the four strains; S. aureus, B. subtilus, E. coli, and Ps. aeruginosa were spread over the plates using a sterile swap spreader to get a uniform bacterial growth for all plates (Suganya et al. 2012). Thereafter, a well with a 9 mm diameter was created on each agar plate. The wells were filled with 100 μL of the nZVI nanoparticles substance (0.01 g from the nZVI nanoparticles has been dissolved in 1 mL of dimethyl sulfoxide (DMSO)). Then, the plates have left for 120 min in the refrigerator to allow the diffusion of the nZVI substance. After the previous period expiration, the plates of strains were incubated at 37 °C for 24 h. Finally, the inhibition zone was measured with a ruler.
Determination of minimal inhibitory concentration (MIC) of nZVI nanoparticles
MIC is defined as the lowest concentration of the antimicrobial agent that inhibits microbial growth after 24 h of incubation time. Determination of MIC for the S. aureus, B. subtilus, E. coli, and Ps. aeruginosa was carried out by the well-diffusion assay method. The nZVI nanoparticles have been tested for determining the MIC according to the method reported by Hammer et al. (1999). For this purpose, the culture medium was poured into the Petri dishes and maintained at 45 °C until the samples were added to the agar. The samples were added using a micropipette by the sequence of 2.25, 2.5, 5.0, 7.5, 10, 15, 20, and 22.5 mg/20 mL agar media for the S. aureus and E. coli, while 2.5, 5.0, 7.5, and 10 mg/20 mL agar media have been added for the B. subtilus and Ps. aeruginosa, accompanied with constant stirring to assure the uniform distribution. Afterward, exactly 50 μL of the different bacteria strains were layered using an automatic micropipette over the surface of the solidified medium containing the sample. After the bacteria were absorbed into the agar, the plates were incubated for 24 h at 37 °C. The MIC has been determined as the lowest concentration of the nZVI nanoparticles had caused the inhibition of visible growth of each bacteria on the agar plate.
Potential application of nZVI nanoparticles on sewage water
Real municipal wastewater was collected from the influent of Helwan sewage treatment plant in Arab Abu Said village at latitude 29°44′51''N and longitude 31°19′50''E. Subsequently, the sample was examined for physical and chemical properties according to the standards methods for the examination of water and wastewater 23rd edition for 2017 (Baird and Bridgewater 2017) before undergoes for treatment by nZVI nanoparticles. Table 2 shows the composition of the collected raw sewage sample in addition to the corresponded limitations of reclaimed water quality required to reuse the treated municipal wastewater in agriculture and irrigation according to the recommended concentrations by the different regulatory organizations.
The optical density assay was performed for four trials containing 5 mL of the sewage water mixed with different concentrations (2, 3, 4, and 5 mg/mL) of the nZVI nanoparticles substance (0.01 g from the nZVI nanoparticles in 1 mL DMSO) which compared with the control sample (sewage water without adding the nZVI substance). The tubes were incubated for 48 h at 37 °C, and then the growth inhibition was measured with a spectrophotometer at OD of 620 nm (Shahneh et al. 2013).
Membrane filter technique
To inspect the microbiological treatment of contaminated sewage water using nZVI nanoparticles, two grams from the nZVI nanoparticles were put into 1 L of the sewage water. After accomplishing the treatment process; the results were compared with the control sample (sewage water without adding the nZVI substance). The growth inhibition was measured by the membrane filter (MF) technique, which is fully accepted as the preferred technique for monitoring the drinking water quality in many countries. In this method, the water sample is filtered on a sterile filter with 0.45 μm pore size which retained the bacteria, then the filter was incubated on a selective medium. Ultimately, the colonies reserved on the filter have been enumerated. Many media and incubation conditions for the membrane filter method had been tested for achieving the optimal recovery of the coliforms from the water samples (Grabow and Du Preez 1979). Using this technique could be determined the total bacteria, total coliform, and fecal coliform. As well, gram (+) S. aureus and fecal streptococci. Further, gram (−) E. coli and Ps. aeruginosa in the sewage water samples.
Determination of total bacteria
The membrane filter method gives a direct estimation for the count of bacteria in the water-based on the growth of the colonies on the membrane filter modified surface (Dufour et al. 1981). A water sample was filtered through the membrane that retained the bacteria. After filtration, the membrane was placed on a differential and selective medium, mTEC, and then incubated at 35 °C and 22 °C ± 0.5 °C for 24 h. Following the incubation period, the filter was moved to a filter pad saturated with urea as a substrate. After 15 min, the yellow, yellow-green, or yellow-brown colonies were counted using a fluorescent lamp and a magnifying lens.
Determination of fecal coliform and total coliform
The membrane filter technique was used for the identification of fecal coliform (FC) and total coliform (TC) organisms in the two sewage water (before and after treatment) samples according to the APHA method (APHA 1995a). The samples were tested by covering the membrane filter unit with aluminum foil and sterile it subsequently. Then, the membrane was placed on the Membrane lauryl sulfate (MLS) media culture over the Petri dish which incubated at the temperature of 44 °C and 37 °C ± 0.5 °C for the fecal coliform and the total coliform, respectively. After 24 h, the colonies that had yellow colors were counted as a colony-forming unit (CFU) per 100 mL of the sample.
Determination of S. aureus
Isolation of the S. aureus has been performed according to the APHA method (APHA 1997), which includes the enrichment of one gram of the sample in 10 mL of cooked meat media plus 9% NaCl (w/v). Posteriorly, the inoculation process for 24 h for the enrichment culture has performed on Baird-Parker agar that containing potassium tellurite along with egg yolk agar, which had been confirmed via the coagulase test of the lipase-positive jet-black colonies.
Determination of fecal streptococci
The fecal streptococci characterize by grows on sodium azide medium at 37–44 °C. Where it is detected through reduction of the stain (generally a tetrazolium-containing compound) or the aesculin hydrolysis (APHA 1998).
Determination of E. coli
The E. coli was considered the most harmful due to its presence is directly related to fecal contamination and its implied enteric disease presence (Rice et al. 1991). Accordingly, to detect E. coli strain, tubes are containing gas-positive Lauryl Sulphate Broth (LSB) were undergone to analyzing by the EC broth. Afterward, the EC tubes were incubated for 24 h at 44.5 °C. In this case, the presence of E. coli is monitored in the positive tubes by detecting the production of indole with tryptone water. The tubes that give positive results confirm the presence of E. coli via indole and gas production (APHA 1995b).
Determination of Ps. aeruginosa
Ps. aeruginosa is recognized through the production of fluorescent pigment, which could be disclosed by UV irradiation. According to this method, the number of microbes is the Most Probable Number (MPN) which is a method used to estimate the concentration of viable microorganisms in a sample through replicate liquid broth growth ten-fold dilutions. Thus after each round, the reactor water is cultured on asparagine and set amid broth tubes. By the end of the incubation period that continued for 48 h at 37 °C, the number of cells is counted (APHA 2005).
Results
Structure of nZVI nanoparticles
Crystallinity and specific surface area
The XRD pattern for the nZVI nanoparticles was shown in Fig. 2a. The peak at 2θ of 44.8096° which represent 100% intensity indicates that the sample predominantly of the α-Fe0 nanoparticles. The peak at 2θ = 31.8197° revealed the existence of a thin layer of iron oxides (Fe2O3 or Fe3O4). The mean crystalline size of the Fe0 nanoparticle was found to be 44.43 nm, which was estimated by the Scherer equation. According to eq. 3; the theoretical SSA for 44.43 nm particles is therefore 17.31 m2/kg, so can be summarized the properties of as-prepared nZVI particles in the following Table 3.
SEM studies
The SEM image for the synthesized nZVI particles as was shown in Fig. 2b has elucidated that the iron particles appear spherical and have a particle size distribution within 20–100 nm, demonstrating the characteristic chain-like morphology. Agglomeration of the nZVI nanoparticles was mentioned to be caused by the magnetic dipole-dipole interactions, and the high surface area of the individual particles. Similar results were observed in previous studies (Peng et al. 2017; Mukherjee et al. 2016). Literature resources indicate that the nZVI nanoparticles possess a core-shell structure, in which the shell represents the oxidized part that surrounds the iron core and preserves it against further oxidation. Where Yan et al. mentioned that the analysis provides unambiguous evidence of the structure of the nZVI layers, which consist of a metallic iron core coated with a thin crust of amorphous oxide (Yan et al. 2010).
EDX studies
The data estimated from the EDX spectrum were summarized in the inset Table in Fig. 2c, which illustrated the surface atomic distribution and chemical elemental composition of nZVI particles. As the iron surface layer is so thin, thus the electron beam can penetrate it and arrive at the core of the nZVI particles, and provide detailed information about the composition of the particles. From the Table, it can be observed the presence of high contents of C, O represents 23.05% (w), and 46.51% (w), respectively. Which often adsorbed on the nZVI surface during the washing step using the alcohol through the preparation process, as well maybe resulted due to oxidation of nZVI particles surface within the measurement step on the SEM equipment (Ayob et al. 2016). Additionally, the appearance of sodium and chloride peaks in the spectrum may back to the presence of some residual by-products. Furthermore, the spectrum pattern showed that the energy levels for nZVI were found at 0.8 keV, 6.4 keV, and 7.1 keV, indicating that the main peak at 6.4 keV is the typical characteristic peak of the iron particles as reported in other studies (Prema et al. 2011). Moreover, the iron has represented a %weight of 18.48 in the sample.
TGA studies
Thermogravimetric analysis (TGA) is a method of thermal stability analysis for the samples in which the mass of a sample is measured as the temperature changes over time. This measurement provides information about physical phenomena, such as phase transitions, the absorption-desorption mechanisms; as well as chemical phenomena including chemisorption, thermal decomposition, and solid-gas reactions, e.g., oxidation or reduction (Prime et al. 2009). According to the thermal analysis results obtained from TGA analysis, the TGA curve of nZVI particles displayed two degradation steps as shown in Fig. 3. The first step was identified in the range of 15–263 °C with a mass loss of 1.064 mg (percent loss = 12.26%) due to possible evaporation of both the adsorbed water that exists as moisture content on the surface of nZVI particles and loss of adsorbed carbon which is originally due to the ethyl alcohol used in wash off the nZVI particles. The second decomposition step at a range of 691–1009 °C with a mass loss of 1.130 mg (percent loss = 13.02%) is mainly resulting due to the decomposition of some nZVI particles, although with the exclusion of the prospective of iron melting entirely at this point. Where the solid iron metal needs a temperature of 1538 °C to reach the melting point. Furthermore, the lately mentioned decay may back to the decomposition of oxide shell surrounds of nZVI particles, which potentially be consists of FeO, and/or FeOOH referring to the breaking of some chemical bonds between iron and oxygen atoms, i.e. reduction of iron oxides through oxygen elimination from the nZVI oxide shell. It is well known that iron may have several crystalline structures. Iron has a body-centered cubic (bcc) lattice known as α-Fe at room temperature. When the temperature is raised above 912 °C, the α-iron transformed into a face-centered cubic (fcc) lattice referred to as γ-Fe; and when the temperature rises above 1394 °C, the γ-iron transformed into a body-centered cubic lattice again, called δ-Fe, which it is the state that the iron remains in it until the melting point (1538 °C). Thus, the second thermal transition in the TGA curve of nZVI particles may be due to the transformation of the crystal lattice of nZVI from a crystalline phase to another phase (Song et al. 2014; Chaung et al. 2014). Generally, nZVI particles were lost almost a weight of 2.181 mg matching a loss percent equal to 25.13% from the original nZVI sample weight, which confirms the high purity of synthesized nZVI particles. Finally, from the previous results, we can conclude that the thermal stability curve exhibited the best thermal performance of nZVI particles at temperatures below 600 °C.
Properties of nZVI nanoparticles
Chemical stability of nZVI nanoparticles
The weight loss (%) of the nZVI sample was used to express the chemical stability of nZVI. Where the weight loss of nZVI samples was calculated for a series of solutions with different pH values as follows 2, 4, 6, 8, 10, and 12. Figure 4a showed that the nZVI particles exposed a considerable weight loss (%) as 90.87 and 88.82% at pH 2 and 12, respectively. This means at very low and high pH values, the nZVI particles were subjected to rapid corrosion and dissolution in the extremely acidic and basic mediums, as a result of the presence of high concentrations of H+ and −OH, leading to accelerating the redox reactions, and dissolution or precipitation of nZVI particles to Fe(II), Fe(III) and iron hydroxides. This means that the nZVI is unstable in very acidic and basic conditions. On the other hand, the weight loss (%) values of nZVI decreased in the range of pH values from 4 to 8. Where the nZVI exhibited the lowest value of weight loss (%) as 54.75% at pH 8. Thus, it can be concluded that the nZVI is remaining stable and is preferably used in neutral, slightly acidic, and slightly basic mediums.
Thermal stability of nZVI nanoparticles
The thermal stability of nZVI particles was examined under a different temperature range of 45, 60, 75, and 100 °C, and weight loss (%) of nZVI particles was evaluated. Figure 4b showed that the nZVI particles exhibited a negligible weight loss at temperatures till 60 °C, which may be attributed to the removal of moisture content from the nZVI surface. In the contrast, at high temperatures values of 75 and 100 °C, the surface thin layer of nZVI began to corrode and decompose. Where, the nZVI displayed slight values of weight loss (%) equivalent to 1.24 and 1.96%, respectively. Which is still a very low percentage. Consequently, this suggested that the nZVI particles are widely stable under the temperature range of 45–60 °C, and can be used safely at this range.
Discussion
Inactivation mechanisms of nZVI nanoparticles
The nZVI suspension has the iron in zero oxidation state (Fe0) which loss the electrons causing oxidization of iron metal to soluble ferrous and ferric ions:
The free-electron attacks the dissolved oxygen from the atmosphere, and water molecules to yield superoxide anion, and super hydroxides radicals, respectively:
The \( {HO}_2^{.} \)produces as a result of the reaction of the yielded superoxide anion with H+:
Interfering of \( {HO}_2^{.} \)with electrons leads to the generation of hydrogen peroxide anion subsequently reacts with H+ to give hydrogen peroxide molecule:
The released iron species oxidizes using dissolved oxygen in redox reactions into many forms of iron oxides:
Based on the previous reactions, there are many explanations concerning antimicrobial mechanisms of the nZVI nanoparticles, as follow:
ROS production
-
The antimicrobial mechanisms of nZVI included the production of many reactive oxygen species (ROS), such as hydroxyl radical, superoxide radical, active radical species, and hydrogen peroxide molecules. It is known that the generation of ROS inducts oxidative stress of the cellular proteins, cell membranes, and DNA of the bacteria consequently causes fatal damage to the membrane structure of the bacteria cells. Where, the outer bilayer membrane is consists of lipopolysaccharides, proteins, and phospholipids that are destroying by the action of ROS active species. Therefore, most of the hurtful effects on the bacterial cells exceedingly occur due to the high concentrations of ROS, which leads to consecutive Fenton reactions. Thence, the Fe-S groups for the bacterial coenzymes are destructed resulting in bacteria injury and death.
-
On the other hand, it can be suggested that the generation of H2O2 molecules may be causing the lipid peroxidation of the bacteria cells. Where the H2O2 can penetrate the cell membrane causing the degradation of membrane structure and then distorting the cells. Therefore, it can be concluded that increasing the ROS species and metal oxidation are related to the degree of nZVI toxicity.
-
The nano-domain size of nZVI particles is recognized by the high specific surface area. This means a high surface activity of nZVI particles which facilitates the entrance of nZVI particles into the bacteria cells. Consequently, causes cell wall decomposition, and then rupturing the cell membrane followed by leakage of cell content. Finally, bacterial cell death occurs.
Liberation of Fe2+, Fe3+ ions
-
Indeed, the resistance of microorganisms can be declined in front of the ability of nZVI particles on inserting the mechanism of poisoning by the free metal ions. Which this free metal ion concentrations arise as a result of decomposing the surface layers of the nanoparticles. Accordingly, the nZVI nanoparticles have high reactivity. Where the nZVI is localizing in zero-state which tends to oxidize vigorously into divalent and trivalent oxidation states by losing the electrons and releasing Fe2+, and Fe3+ ions. Thence promoted the toxicity of nZVI via the high solubility rate of these ions in the microbes-containing medium, and its high capability to penetrate the intracellular contents of the bacteria membranes.
-
Furthermore, the antibacterial efficacy of nZVI may be attributed to the strong electrostatic interaction of the liberated positively charged ferrous and ferric ions (Fe2+, Fe3+) with negatively charged bacteria. Therefore, cell death befalls as a result of the destructive attraction between the bacteria wall surface and nZVI particles. Over and above that, these ions could also bind to the outer cell membrane causing bacteria cell disorder.
-
Since the presence of atmospheric oxygen in contact with the nZVI particles, it might result in the formation of iron oxides, such as Fe3O4, Fe2O3, and FeO, which encourage the wide propagation of ROS species to modify the redox status, thus this implies an enhancement of the nZVI ability to killing the microbes.
Contact of nZVI nanoparticles with bacteria
-
Sometimes, it is not necessarily an occurrence of cell deterioration due to the diffusion of ions or metals inside the cells. Nevertheless, the direct contact of abrasive nZVI particles with the bacterial membranes may cause many micro-environmental changes encloses the contact areas such as; disorder of bacterial cell wall, likewise increasing of cell membrane permeability, and sequentially leading to a high consecutive cellular internalization of the nZVI particles throughout the cells.
-
Therefore, the distinctive capability of nZVI cytotoxicity towards discouragement of the survival of disease-causing microorganisms might be attributed to its ability to doing the changes in the structures of proteins, peptidoglycan, DNA, and lipids structure of the bacteria cell membrane because of the agglomeration of nZVI particles on the bacteria surface. Therefore, these modifications will be causes disruption of the bacterial electron transportation chain by prohibiting metabolic enzyme activities, suppress bacterial duplication, and accordingly prevent the activity of bacteria.
The previous possible mechanisms were represented in Fig. 5 (the figure was designed using Office PowerPoint v. 2016):
Bioactivity of nZVI nanoparticles
Often, the nZVI nanoparticles have shown a varying degree of toxicity against the four strains of the microorganisms namely; B. subtilus, S. aureus, Ps. aeruginosa, and E. coli as 14, 9, 18, and 21 mm, respectively. Whereas, the inhibition zone above a diameter of 10 mm has recorded a positive result as shown in Fig. 6. Generally, most of the tested microorganisms displayed a high sensitivity towards the nZVI nanoparticle substance, and these findings have agreed with that previously reported in the literature. Mahdy et al. indicated that the nZVI nanoparticles possess great potential to use as antimicrobials (Mahdy et al. 2012). Besides, they mentioned that the growth of E. coli and S. aureus was significantly inhibited compared with the control samples using the highest dose of iron oxide which was 30 μg/mL.
Based on the results, the Gram (−) bacteria showed higher sensitivity than Gram (+) bacteria towards the antibacterial activity of the nZVI agent. This may be attributed to the cell wall structure of the Gram (+) bacteria, which consist of a thick layer of lipopolysaccharide, lipid A, and peptidoglycan that have supported it against the nZVI devastating effect. While the cell walls of Gram (−) bacteria contain only a thin layer of peptidoglycan, which allowed the mobility and permeability of nZVI particles into the cells. Therefore, the nanoparticle/bacterial interactions improved due to lacking the ability of a thin peptidoglycan layer to repulsed of nZVI attack. Besides, Gram (−) bacteria have a negatively charged lipopolysaccharide layer, which contributed as a considerable incorporation factor for the positive ions (Fe2+/Fe3+) into the cells causing rapid intracellular damage, and destruction of bacterial DNA. Thus, it could be stated that maintenance of cell integrity, membrane functions, and efficiency of enzymes associated with the membrane depend foremost upon the structure of the cell surface.
The size of the inhibition zone for various group antimicrobial agents previously reported in the literature was compared with the observed zone of the nZVI agent as tabulated in Table 4. It could be concluded that the nZVI agent has achieved resemble results with most of the other antimicrobial materials, which reflects that the inhibition capacity of antimicrobial agents is a function of its particle size, and proportion directly with the concentration.
MIC of nZVI nanoparticles
In general, a higher concentration of the nZVI nanoparticles suspension was observed to have the highest inactivation efficiency versus Gram (+) and Gram (−) bacteria as listed in Table 5. Accordingly, the MIC values determined by the well diffusion assay for the four strains (S. aureus, B. subtilus, E. coli, and Ps. aeruginosa) were found to be 15, 10, 10, and 5 mg, respectively.
Table 6 shows the quantitative values of MIC that measured for the proposed nZVI agent and different antimicrobial agents mentioned in some studies to establishing whether the agents are microbistatic or microbicidal towards various pathogens. Proportionately, the relative anti-bacteriophage activity of nZVI suspension in terms of MIC was seemed to be equivalent to other bacteriocins’ suspensions. According to this comparison, it can well accommodate the role of agent concentration on the yielded value of MIC. This can be explained that based on the increase of nZVI agent concentrations will result in increasing the specific surface area to the volume and releasing a large number of killer species from the surface of the nanoparticles. Sequentially, this will lead to more inhibitory strength of nanoparticles toward the bacterial growth causing the cells to eventually die.
nZVI nanoparticles for municipal wastewater disinfection
nZVI particles have been examined as a disinfectant agent for municipal wastewater against the pathogen bacteria, and it is found that the nZVI substance had an effective effect on the microbial load in the sewage water. Where Fig. 7 indicated that the high concentration of nZVI nanoparticles suspension was observed to have a high inactivation rate against the microorganisms in the sewage water samples. However, the high concentrations of nZVI suspension might result in movement restriction and high aggregation of nanoparticle causes reducing the activity of their relative surface and inactivation efficiency. in this context, Nurmi et al. reported the difficulty to avoid such aggregations (Nurmi et al. 2005). Where nature of the active sites on particle surface was observed to be affected by the surrounding environment in addition to the particle size (Kuhn et al. 2002; Signorini et al. 2003). Generally, under normal environmental conditions, the nZVI particles are covered with passivation layers that form a shell of oxides and giving nZVI particles the properties of the core-shell structure (Nurmi et al. 2005; Mulvaney 2001). Both the Gram (+) and Gram (−) bacteria extremely exist in municipal wastewater. Thus, an investigation survey has been procced to examine the inactivation proficiency of nZVI particles for these bacteria. From Fig. 8, and Table 7, it could be concluded the antimicrobial effect of nZVI particles on the bacteria of the wastewater sample. Where the counts of total bacteria, total coliform, and fecal coliform had decreased to 44.29%, 51.76%, and 90.95% respectively. Likewise, the counts of Gram (+) S. aureus, and fecal Streptococcus had decreased to 46.67%, and 33.33%, respectively. Furthermore, the count of Gram (−) E. coli had decreased to 93.89%. While the Ps. aeruginosa was not detected in the wastewater sample. Nevertheless, many previous studies have reported similar results, for example; Diao and Yao (2009) mentioned that the nZVI nanoparticles had accomplished a complete inactivation for Gram (−) Ps. fluorescent, whilst the inactivation efficiency reached 95% and 80% for Gram (+) B. subtilis and Aspergillus Versicolor fungus, respectively. Also, Lee et al. (2008) indicated that the nZVI nanoparticles in the aqueous solution rapidly inactivate the E. coli. Besides, George et al. (2013) reported that the maximum inhibition percentages of the nZVI nanoparticles have been recorded against Ps. aeruginosa with a value of 92%, followed by E. coli with more than 91%, then pursued by the S. aureus with inhibition percentage reached 89%. While, Hsueh et al. (2017) demonstrated that the nZVI nanoparticles with a concentration of 1000 mg/L have high toxicity against the Gram (+) B. thuringiensis and B. subtilis, but didn’t affect the Gram (−) E. coli strains.
Generally, the treatment processes efficacies for microbial reduction differ among the microbial groups due to the inherently different properties of the microbes (e.g., size, nature of protective outer layers, physicochemical surface properties, etc.). However, the differences in treatment process efficiencies are smaller among the specific species, types, or strains of microbes. Table 8 provides a summary of treatment processes that are commonly used individually or integrally to achieve microbial reductions. The table presents conservative estimates of microbial reductions based on the more resistant or persistent pathogenic members of the microbial group. Besides, the different treatment processes were compared with the effect of nZVI particles against the total bacteria count in the sewage sample to demonstrate their efficiency as a disinfector agent.
Sun et al. (2019) reported that in the comparison of nZVI nanoparticles with chlorine, it was found that the nZVI particles are safer as a disinfector agent due to the absence of carcinogenic disinfection byproducts (DBPs) such as trihalomethanes (THMs), haloacetic acids (HAAs), chlorite, and bromate. Where the United States Environmental Protection Agency (USEPA), European Union, and World Health Organization (WHO) classify these compounds as major pollutants in drinking water. At the same time, disinfection using nZVI particles is advantageous over chlorination especially in the disinfection of wastewater where large amounts of pollutants are present. This advantage is due to the ability of nZVI particles to remove coexisting contaminants like organic pollutants and heavy metals simultaneously. In the case of chlorination, these pollutants must be removed because they might act as precursors of DBPs, and therefore increase the operation cost. The inactivation through magnetic separation along with accompanying physical removal of bacteria from water bodies using nZVI particles was remarkably beneficial for practical disinfection. Whereas this physical treatment process reducing the chemical oxygen demand (COD) by eliminating the risks of the potential spread of antibiotic resistance genes through horizontal gene transfer and regrowth of inactivated bacteria by removing the debris of inactivated microbes. Besides, the nZVI particles are more applicable for handling, transport, storage, and deployment than chlorine, which enables their uses in more valuable applications such as point-of-use water purification, and disinfection of the noncentral water supply.
Microbiological aspect for wastewater reuse
Wastewater treatment is the most effective way to reduce the health, environmental, and other risks associated with the use of reclaimed water. Choosing the most appropriate treatment technology for water reuse is a complex procedure that must take into consideration various criteria, including technical and regulatory requirements, as well as social, political, and economic considerations specific to the local conditions. It is important to stress that economic and financial constraints have to be taken into account in countries where reclaimed water is a vital water resource for sustainable development. Some developing countries advocate another strategy of controlling health risks by adopting a low technology/low-cost approach based on the WHO recommendations (Al-Gheethi et al. 2018; Division et al. 2004).
Efforts to rehabilitate urban water resources include the increasing use of wastewater for peri-urban agriculture and energy production. An increasing number of initiatives are now looking at opportunities to integrate water management with urban needs in energy, green spaces, and food security. It is a matter of distinguishing the right kind of treatment for the right kind of use. There are a growing number of examples of reclaimed wastewater being used in agriculture, for irrigating municipal parks and fields, in industrial cooling systems, and even in some cases, mixed in with drinking water (2030 WRG, 2013) (Jaramillo and Restrepo 2017; Connor 2015). The parameters recommended for the minimum monitoring of community supplies are those that best establish the hygienic state of the water and thus the risk of waterborne disease. The essential parameters of water quality and common indicator bacteria are E. coli and thermotolerant (fecal) coliforms which are accepted as suitable substitutes – and chlorine residual (if chlorination is practiced) (Water and Organization 2006).
The Guidelines suggest that, regardless of the type of reclaimed water use, some level of disinfection should be provided to avoid adverse health consequences from inadvertent contact or accidental or intentional misuse of a water reuse system. For nonpotable uses of reclaimed water, two levels of disinfection are recommended. Reclaimed water used for applications where no direct public or worker contact with the water is expected should be disinfected to achieve an average fecal coliform concentration not exceeding 200/100 mL (Division et al. 2004). Moreover, the health-based targets in WHO guidelines ( 2006) are: 1. determine the realistic human exposure scenarios and the number of pathogens that could be ingested under different irrigation regimes for different crop types; 2. calculate the required reduction of pathogen numbers that need to be achieved depending on the initial wastewater quality and the crop type (Mara and Kramer 2008). Table 9 presents suggested treatment processes, reclaimed water quality, and monitoring frequency for water reuses in various categories. These guidelines apply to domestic wastewater from municipal or other wastewater treatment facilities having a limited input of industrial waste. The suggested regulatory guidelines are based on microbiological quality represented by the coliforms that are reduced principally for water reclamation with highlighting the role of nZVI particles as an effective disinfectant against these indicators.
Comparison with other antimicrobial agents
The antibacterial behavior of the nZVI particles was compared with other antimicrobial agents in the literature based on the eligibility of these agents on hindering bacterial growth. As shown in Table 10, the nZVI exhibited a satisfactory growth inhibition effect towards the majority of tested bacteria, and its efficacy consistent with that for the other antimicrobial agents. Furthermore, the collected results from the literature survey provided evidence for the important considerations, which highlighted the effective factors for the microbiological treatment of municipal wastewater using various antimicrobial agents against numerous types of pathogenic bacteria. In addition to introducing the restriction mechanisms of its harmful existence in the treated water as a necessary step for the toxicity risk assessment of these pathogenic bacteria in the aquatic environment and its implications for the common health.
Conclusion
In this study, the nZVI nanoparticles were prepared via the reduction of ferric iron by a borohydride agent. The XRD analysis demonstrated that the mean crystalline dimension of the Fe0 nanoparticle was found to be 44.43 nm with an appearance of low-intensity peaks an indication of the formation of thin oxide layers on the nZVI surface. The SEM image showed that the nZVI particles have a spherical shape and were formed in chain-like aggregates, where tend to accumulate in larger conglomerates. Also, the EDX spectrum was confirmed the chemical structure of the nZVI particles. Moreover, the thermal properties of synthesized nZVI particles were studied using the TGA technique. The nZVI particles had been shown a synergistic enhancement of the antimicrobial activity towards both Gram (+) and Gram (−) bacteria. Where, the minimum inhibitory concentration of nZVI particles was estimated by the well diffusion assay method, and was found to equivalent to 15, 10, 10, and 5 mg for the following four bacteria strain S. aureus, B. subtilus, E. coli, and Ps. aeruginosa, respectively. In general, the use of nZVI nanoparticles as a pre-treatment and disinfection technique for the municipal wastewater were helped in minimizing the associated biological health hazard for both the Gram (+) and Gram (−) bacteria, which probably highly exist in the polluted water.
Data availability
All data generated or analyzed during this study are included in this manuscript.
Abbreviations
- B. subtilus:
-
Bacillus Subtilus
- CFU:
-
Colony Forming Units
- DDI:
-
Double-Deionized Water
- DMSO:
-
Dimethyl Sulfoxide
- DNA:
-
Deoxyribonucleic Acid
- E. coli :
-
Escherichia coli
- EC:
-
Escherichia coli
- EDX:
-
Energy-Dispersive X-ray Spectroscopy
- FAO:
-
Food and Agriculture Organization
- FE-SEM:
-
Field-Emission Scanning Electron Microscope
- FC:
-
Fecal Coliform
- Gram (+):
-
Gram-Positive Bacteria
- Gram (-):
-
Gram-Negative Bacteria
- ISO:
-
International Organization for Standardization
- LSB:
-
Lauryl Sulphate Broth
- MF:
-
Membrane Filter
- MIC:
-
Minimum Inhibitory Concentration
- MLS:
-
Membrane Lauryl Sulfate
- MPN:
-
Most Probable Number
- ND:
-
Not Detected
- NPs:
-
Nanoparticles
- nZVI:
-
Nanoscale Zero-Valent Iron
- OD:
-
Optical Density Assay
- Ps. aeruginosa:
-
Pseudomonas aeruginosa
- ROS:
-
Reactive Oxygen Species
- S. aureus :
-
Staphylococcus aureus
- TC:
-
Total Coliform
- TG:
-
Thermogravimetric
- USEPA:
-
U.S. Environmental Protection Agency
- WHO:
-
World Health Organization
- XRD:
-
X-ray Diffraction
- Dp :
-
Crystalline diameter of particle, nm
- λ :
-
CuKα radiation wavelength, Å
- β :
-
Full width at half maximum (FWHM), radians
- θ :
-
Bragg angle, degree
References
Al-Gheethi A, Efaq A, Bala J, Norli I, Abdel-Monem M, Kadir MA (2018) Removal of pathogenic bacteria from sewage-treated effluent and biosolids for agricultural purposes. Appl Water Sci 8:1–25. https://doi.org/10.1007/s13201-018-0698-6
Alt V, Bechert T, Steinrücke P, Wagener M, Seidel P, Dingeldein E, Domann E, Schnettler R (2004) An in vitro assessment of the antibacterial properties and cytotoxicity of nanoparticulate silver bone cement. Biomaterials 25:4383–4391. https://doi.org/10.1016/j.biomaterials.2003.10.078
American Public Health Association (APHA) (1995a) Manual standard methods for the examination of water and wastewater, 19th edn. AWWA
American Public Health Association (APHA) (1995b) Manual standard methods for the examination of water and wastewater, 19th edn. AWWA
American Public Health Association (APHA) (1997) In Compendium of methods for the microbiological examination, 4th edn. Washington, DC, District of Columbia USA. Pages 105–119, 325–367, 371–415, and 637–658
American Public Health Association (APHA) (1998) Standard methods for the examination of Water and wastewater, 20th edn. AWWA, AEF, Washington, DC
American Public Health Association (APHA) (2005) Standard methods for the examination of water and wastewater, 20th edn. AWWA, WEF, Washington, DC
Arakha M et al (2015) Antimicrobial activity of iron oxide nanoparticle upon modulation of nanoparticle-bacteria interface. Sci Rep 5:1–12. https://doi.org/10.1038/srep14813
Avanzato C, Follieri J, Banerjee I, Fath K (2009) Biomimetic synthesis and antibacterial characteristics of magnesium oxide-germanium dioxide nanocomposite powders. J Compos Mater 43:897–910. https://doi.org/10.1177/0021998308103158
Ayers RS, Westcot DW (1985) Water quality for agriculture vol 29. Food and Agriculture Organization of the United Nations Rome. ISBN 92-5-102263-1
Ayob A, Santiagoo R, Amneera WA, Ismail N, Abdullah AZ (2016) Ultrasonic-assisted synthesis of reactive carboxymethyl cellulose stabilized nano zero-valent iron and its application for removal of Cr6+ and Cu2+ ions. Environ Prot Eng 42:10.37190/160204
Azizi-Lalabadi M, Ehsani A, Divband B, Alizadeh-Sani M (2019) Antimicrobial activity of titanium dioxide and zinc oxide nanoparticles supported in 4A zeolite and evaluation the morphological characteristic. Sci Rep 9:1–10. https://doi.org/10.1038/s41598-019-54025-0
Baird R, Bridgewater L (2017) Standard methods for the examination of water and wastewater, 23rd edn. American Public Health Association, Washington DC
Bhavyasree P, Xavier T (2020) Green synthesis of copper oxide/carbon nanocomposites using the leaf extract of Adhatoda vasica Nees, their characterization and antimicrobial activity. Heliyon 6:e03323. https://doi.org/10.1016/j.heliyon.2020.e03323
Bhushan M, Kumar Y, Periyasamy L, Viswanath AK (2018) Antibacterial applications of α-Fe2O3/Co3O4 nanocomposites and study of their structural, optical, magnetic and cytotoxic characteristics. Appl Nanosci 8:137–153. https://doi.org/10.1007/s13204-018-0656-5
Blumenthal UJ, Mara DD, Peasey A, Ruiz-Palacios G, Stott R (2000) Guidelines for the microbiological quality of treated wastewater used in agriculture: recommendations for revising WHO guidelines. Bull World Health Organ 78:1104–1116. https://doi.org/10.1590/S0042-96862000000900006
Buszewski B, Railean-Plugaru V, Pomastowski P, Rafińska K, Szultka-Mlynska M, Golinska P, Wypij M, Laskowski D, Dahm H (2018) Antimicrobial activity of biosilver nanoparticles produced by a novel Streptacidiphilus durhamensis strain. J Microbiol Immunol Infect 51:45–54. https://doi.org/10.1016/j.jmii.2016.03.002
Chaung S-H, Wu P-F, Kao Y-L, Yan W, Lien H-L (2014, 2014) Nanoscale zero-valent iron for sulfide removal from digested piggery wastewater. J Nanomater. https://doi.org/10.1155/2014/518242
Cheeseman S et al (2020) Antimicrobial metal nanomaterials: from passive to stimuli-activated applications. Advanced Science 7:1902913. https://doi.org/10.1002/advs.201902913
Chen Q, Li J, Wu Y, Shen F, Yao M (2013) Biological responses of gram-positive and gram-negative bacteria to nZVI (Fe0), Fe2+ and Fe3+. RSC Adv 3:13835–13842. https://doi.org/10.1039/C3RA40570B
Chou WL, Yu DG, Yang MC (2005) The preparation and characterization of silver-loading cellulose acetate hollow fiber membrane for water treatment. Polym Adv Technol 16:600–607. https://doi.org/10.1002/pat.630
Connor R (2015) The United Nations world water development report 2015: water for a sustainable world vol 1. UNESCO publishing. ISBN:978-92-3-100080-5 (set), 978-92-3-100071-3, 978-92-3-100099-7 (ePub)
Diao M, Yao M (2009) Use of zero-valent iron nanoparticles in inactivating microbes. Water Res 43:5243–5251. https://doi.org/10.1016/j.watres.2009.08.051
Dimapilis EAS, Hsu C-S, Mendoza RMO, Lu M-C (2018) Zinc oxide nanoparticles for water disinfection. Sustainable Environment Research 28:47–56. https://doi.org/10.1016/j.serj.2017.10.001
Division USEPAOoWMMS, Transfer NRMRLT, Division S (2004) Guidelines for water reuse. US Environmental Protection Agency. EPA/625/R-04/108
Dufour AP, Strickland ER, Cabelli VJ (1981) Membrane filter method for enumerating Escherichia coli. Applied and environmental microbiology 41:1152-1158. 0099-2240/81/051152-07$02.00/0
Elawwad A, Ragab M, Hamdy A, Husein DZ (2020) Enhancing the performance of microbial desalination cells using δMnO2/graphene nanocomposite as a cathode catalyst. Journal of Water Reuse and Desalination 10:214–226. https://doi.org/10.2166/wrd.2020.011
Elmi F, Alinezhad H, Moulana Z, Salehian F, Mohseni Tavakkoli S, Asgharpour F, Fallah H, Elmi MM (2014) The use of antibacterial activity of ZnO nanoparticles in the treatment of municipal wastewater. Water Sci Technol 70:763–770. https://doi.org/10.2166/wst.2014.232
EPA (2012) 2012 guidelines for water reuse. US Agency for International Development Washington, DC. EPA/600/R-12/618
Farrell J, Kason M, Melitas N, Li T (2000) Investigation of the long-term performance of zero-valent iron for reductive dechlorination of trichloroethylene. Environ Sci Technol 34:514–521. https://doi.org/10.1021/es990716y
Furno F, Morley KS, Wong B, Sharp BL, Arnold PL, Howdle SM, Bayston R, Brown PD, Winship PD, Reid HJ (2004) Silver nanoparticles and polymeric medical devices: a new approach to prevention of infection? J Antimicrob Chemother 54:1019–1024. https://doi.org/10.1093/jac/dkh478
George A, Namasivayam S, Raju S (2013) Synthesis, characterization and anti bacterial activity of chitosan stabilized nano zero valant iron. BOPAMS 1:7–11
Gogoi SK, Gopinath P, Paul A, Ramesh A, Ghosh SS, Chattopadhyay A (2006) Green fluorescent protein-expressing escherichia coli as a model system for investigating the antimicrobial activities of silver nanoparticles. Langmuir 22:9322–9328. https://doi.org/10.1021/la060661v
Gold K, Slay B, Knackstedt M, Gaharwar AK (2018) Antimicrobial activity of metal and metal-oxide based nanoparticles. Advanced Therapeutics 1:1700033. https://doi.org/10.1002/adtp.201700033
Grabow W, Du Preez M (1979) Comparison of m-Endo LES, MacConkey, and Teepol media for membrane filtration counting of total coliform bacteria in water. Applied and environmental microbiology 38:351-358. 0099-2240/79/09-0351/08$02.00
Gunalan S, Sivaraj R, Rajendran V (2012) Green synthesized ZnO nanoparticles against bacterial and fungal pathogens. Progress in Natural Science: Materials International 22:693–700. https://doi.org/10.1016/j.pnsc.2012.11.015
Hamdy A (2021) Experimental study of the relationship between dissolved Iron, turbidity, and removal of cu(II) ion from aqueous solutions using zero-valent Iron nanoparticles. Arab J Sci Eng 46:5543–5565. https://doi.org/10.1007/s13369-020-05079-0
Hamdy A, Ismail SH, Ebnalwaled A, Mohamed GG (2021) Characterization of superparamagnetic/monodisperse PEG-coated magnetite nanoparticles Sonochemically prepared from the hematite ore for cd(II) removal from aqueous solutions. J Inorg Organomet Polym Mater 31:397–414. https://doi.org/10.1007/s13369-020-05079-0
Hamdy A, Mostafa M, Nasr M (2019a) Regression analysis and artificial intelligence for removal of methylene blue from aqueous solutions using nanoscale zero-valent iron. Int J Environ Sci Technol 16:357–372. https://doi.org/10.1007/s13762-018-1677-z
Hamdy A, Mostafa MK, Nasr M (2018) Zero-valent iron nanoparticles for methylene blue removal from aqueous solutions and textile wastewater treatment, with cost estimation. Water Sci Technol 78:367–378. https://doi.org/10.2166/wst.2018.306
Hamdy A, Mostafa MK, Nasr M (2019b) Techno-economic estimation of electroplating wastewater treatment using zero-valent iron nanoparticles: batch optimization, continuous feed, and scaling up studies. Environ Sci Pollut Res 26:25372–25385. https://doi.org/10.1007/s11356-019-05850-3
Hammer KA, Carson CF, Riley TV (1999) Antimicrobial activity of essential oils and other plant extracts. J Appl Microbiol 86:985–990. https://doi.org/10.1046/j.1365-2672.1999.00780.x
Hsiao M-T, Chen S-F, Shieh D-B, Yeh C-S (2006) One-pot synthesis of hollow Au3Cu1 spherical-like and biomineral botallackite Cu2(OH)3Cl flowerlike architectures exhibiting antimicrobial activity. J Phys Chem B 110:205–210. https://doi.org/10.1021/jp054827x
Hsueh Y-H, Tsai P-H, Lin K-S, Ke W-J, Chiang C-L (2017) Antimicrobial effects of zero-valent iron nanoparticles on gram-positive Bacillus strains and gram-negative Escherichia coli strains. Journal of nanobiotechnology 15:1–12. https://doi.org/10.1186/s12951-017-0314-1
Hussein-Al-Ali SH, El Zowalaty ME, Kura AU, Geilich B, Fakurazi S, Webster TJ, Hussein MZ (2014, 2014) Antimicrobial and controlled release studies of a novel nystatin conjugated iron oxide nanocomposite. Biomed Res Int. https://doi.org/10.1155/2014/651831
Hydutsky BW, Mack EJ, Beckerman BB, Skluzacek JM, Mallouk TE (2007) Optimization of nano-and microiron transport through sand columns using polyelectrolyte mixtures. Environ Sci Technol 41:6418–6424. https://doi.org/10.1021/es0704075
Jaramillo MF, Restrepo I (2017) Wastewater reuse in agriculture: a review about its limitations and benefits. Sustainability 9:1734. https://doi.org/10.3390/su9101734
Jeong SH, Yeo SY, Yi SC (2005) The effect of filler particle size on the antibacterial properties of compounded polymer/silver fibers. J Mater Sci 40:5407–5411. https://doi.org/10.1007/s10853-005-4339-8
Joo SH, Feitz AJ, Sedlak DL, Waite TD (2005) Quantification of the oxidizing capacity of nanoparticulate zero-valent iron. Environ Sci Technol 39:1263–1268. https://doi.org/10.1021/es048983d
Kaur H, Kaur S, Singh M (2013) Biosynthesis of silver nanoparticles by natural precursor from clove and their antimicrobial activity. Biologia 68:1048–1053. https://doi.org/10.2478/s11756-013-0276-1
Khezerlou A, Alizadeh-Sani M, Azizi-Lalabadi M, Ehsani A (2018) Nanoparticles and their antimicrobial properties against pathogens including bacteria, fungi, parasites and viruses. Microb Pathog 123:505–526. https://doi.org/10.1016/j.micpath.2018.08.008
Kuhn LT, Bojesen A, Timmermann L, Nielsen MM, Mørup S (2002) Structural and magnetic properties of core-shell iron-iron oxide nanoparticles. J Phys Condens Matter 14:13551. https://doi.org/10.1088/0953-8984/14/49/311
Lee C, Kim JY, Lee WI, Nelson KL, Yoon J, Sedlak DL (2008) Bactericidal effect of zero-valent iron nanoparticles on Escherichia coli. Environ Sci Technol 42:4927–4933. https://doi.org/10.1021/es800408u
Li L, Fan M, Brown RC, Van Leeuwen J, Wang J, Wang W, Song Y, Zhang P (2006) Synthesis, properties, and environmental applications of nanoscale iron-based materials: a review. Crit Rev Environ Sci Technol 36:405–431. https://doi.org/10.1080/10643380600620387
Mahdy SA, Raheed QJ, Kalaichelvan P (2012) Antimicrobial activity of zero-valent iron nanoparticles. International Journal of Modern Engineering Research 2:578–581
Mara DD, Kramer A (2008) The 2006 WHO guidelines for wastewater and greywater use in agriculture: a practical interpretation. In: Al Baz I, Otterpohl I, Wendland C (eds) Efficient Management of Wastewater : its treatment and reuse in Water scarce countries. Springer, pp 1–17. https://doi.org/10.1007/978-3-540-74492-4_1
Miethke M, Marahiel MA (2007) Siderophore-based iron acquisition and pathogen control. Microbiol Mol Biol Rev 71:413–451. https://doi.org/10.1128/MMBR.00012-07
Montgomery MA, Elimelech M (2007) Water and sanitation in developing countries: including health in the equation. ACS Publications 41:17–24. https://doi.org/10.1021/es072435t
Morones JR, Elechiguerra JL, Camacho A, Holt K, Kouri JB, Ramírez JT, Yacaman MJ (2005) The bactericidal effect of silver nanoparticles. Nanotechnology 16:2346. https://doi.org/10.1088/0957-4484/16/10/059
Moustafa MT (2017) Removal of pathogenic bacteria from wastewater using silver nanoparticles synthesized by two fungal species. Water Science 31:164–176. https://doi.org/10.1016/j.wsj.2017.11.001
Mukherjee R, Kumar R, Sinha A, Lama Y, Saha AK (2016) A review on synthesis, characterization, and applications of nano zero valent iron (nZVI) for environmental remediation. Crit Rev Environ Sci Technol 46:443–466. https://doi.org/10.1080/10643389.2015.1103832
Mulvaney P (2001) Metal nanoparticles: double layers, optical properties, and electrochemistry. Nanoscale Materials in Chemistry:121–167. https://doi.org/10.1002/0471220620.ch5
Narayanan P, Wilson WS, Abraham AT, Sevanan M (2012) Synthesis, characterization, and antimicrobial activity of zinc oxide nanoparticles against human pathogens. BioNanoScience 2:329–335. https://doi.org/10.1007/s12668-012-0061-6
Nigam Ahuja N, Ansari A A, Rajput R, Singh P (2020) Synthesis and characterization of zero valent Iron nanoparticles for textile wastewater treatment. Pollution 6:773-783. https://doi.org/10.22059/poll.2020.296735.740
Nurmi JT, Tratnyek PG, Sarathy V, Baer DR, Amonette JE, Pecher K, Wang C, Linehan JC, Matson DW, Penn RL (2005) Characterization and properties of metallic iron nanoparticles: spectroscopy, electrochemistry, and kinetics. Environ Sci Technol 39:1221–1230. https://doi.org/10.1021/es049190u
Oprčkal P, Mladenovič A, Vidmar J, Pranjić AM, Milačič R, Ščančar J (2017) Critical evaluation of the use of different nanoscale zero-valent iron particles for the treatment of effluent water from a small biological wastewater treatment plant. Chem Eng J 321:20–30. https://doi.org/10.1016/j.cej.2017.03.104
Organization WH (2004) Report on the WHO/AFESD regional consultation to review national priorities and action plans for wastewater reuse and management, Amman, Jordan, 20–22 October 2003. World Health Organization. Regional Office for the Eastern Mediterranean. https://apps.who.int/iris/handle/10665/255081
Organization WH (2006) A compendium of standards for wastewater reuse in the Eastern Mediterranean Region. https://apps.who.int/iris/handle/10665/116515
Paez-Rubio T, Ramarui A, Sommer J, Xin H, Anderson J, Peccia J (2007) Emission rates and characterization of aerosols produced during the spreading of dewatered class B biosolids. Environ Sci Technol 41:3537–3544. https://doi.org/10.1021/es061786p
Pandey PK, Kass PH, Soupir ML, Biswas S, Singh VP (2014) Contamination of water resources by pathogenic bacteria. AMB Express 4:51. https://doi.org/10.1186/s13568-014-0051-x
Pelletier DA, Suresh AK, Holton GA, McKeown CK, Wang W, Gu B, Mortensen NP, Allison DP, Joy DC, Allison MR (2010) Effects of engineered cerium oxide nanoparticles on bacterial growth and viability. Appl Environ Microbiol 76:7981–7989. https://doi.org/10.1128/aem.00650-10
Peng Z, Xiong C, Wang W, Tan F, Xu Y, Wang X, Qiao X (2017) Facile modification of nanoscale zero-valent iron with high stability for Cr(VI) remediation. Sci Total Environ 596:266–273. https://doi.org/10.1016/j.scitotenv.2017.04.121
Pescod MB (1992) The urban Water cycle, including wastewater use in agriculture. Outlook on Agriculture 21:263–270. https://doi.org/10.1177/003072709202100404
Prema P, Thangapandian S, Selvarani M, Subharanjani S, Amutha C (2011) Color removal efficiency of dyes using nanozerovalent iron treatment. Toxicol Environ Chem 93:1908–1917. https://doi.org/10.1080/02772248.2011.606613
Prime RB, Bair HE, Vyazovkin S, Gallagher PK, Riga A (2009) Thermogravimetric analysis (TGA). Thermal analysis of polymers: Fundamentals and applications:241–317. https://doi.org/10.1002/9780470423837.ch3
Punjabi K, Mehta S, Chavan R, Chitalia V, Deogharkar D, Deshpande S (2018) Efficiency of biosynthesized silver and zinc nanoparticles against multi-drug resistant pathogens. Front Microbiol 9:2207. https://doi.org/10.3389/fmicb.2018.02207
Rice EW, Allen M, Brenner D, Edberg S (1991) Assay for beta-glucuronidase in species of the genus Escherichia and its applications for drinking-water analysis. Appl Environ Microbiol 57:592–593. https://doi.org/10.1128/AEM.57.2.592-593.1991
Ryan JN, Harvey RW, Metge D, Elimelech M, Navigato T, Pieper AP (2002) Field and laboratory investigations of inactivation of viruses (PRD1 and MS2) attached to iron oxide-coated quartz sand. Environ Sci Technol 36:2403–2413. https://doi.org/10.1021/es011285y
Sambhy V, MacBride MM, Peterson BR, Sen A (2006) Silver bromide nanoparticle/polymer composites: dual action tunable antimicrobial materials. J Am Chem Soc 128:9798–9808. https://doi.org/10.1021/ja061442z
Sánchez-López E et al (2020) Metal-based nanoparticles as antimicrobial agents: an overview. Nanomaterials 10:292. https://doi.org/10.3390/nano10020292
Shahneh FZ, Valiyari S, Azadmehr A, Hajiaghaee R, Yaripour S, Bandehagh A, Baradaran B (2013) Inhibition of growth and induction of apoptosis in Fibrosarcoma cell lines by Echinophora platyloba DC: in vitro analysis. Advances in Pharmacological and Pharmaceutical Sciences 2013:1–7. https://doi.org/10.1155/2013/512931
Shoushtarian F, Negahban-Azar M (2020) Worldwide regulations and guidelines for agricultural water reuse: a critical review. Water 12:971. https://doi.org/10.3390/w12040971
Signorini L, Pasquini L, Savini L, Carboni R, Boscherini F, Bonetti E, Giglia A, Pedio M, Mahne N, Nannarone S (2003) Size-dependent oxidation in iron/iron oxide core-shell nanoparticles. Phys Rev B 68:195423. https://doi.org/10.1103/PhysRevB.68.195423
Soliman T, Vshivkov S (2019) Effect of Fe nanoparticles on the structure and optical properties of polyvinyl alcohol nanocomposite films. J Non-Cryst Solids 519:119452. https://doi.org/10.1016/j.jnoncrysol.2019.05.028
Song B, Dong S, Deng S, Liao H, Coddet C (2014) Microstructure and tensile properties of iron parts fabricated by selective laser melting. Opt Laser Technol 56:451–460. https://doi.org/10.1016/j.optlastec.2013.09.017
Stoimenov PK, Klinger RL, Marchin GL, Klabunde KJ (2002) Metal oxide nanoparticles as bactericidal agents. Langmuir 18:6679–6686. https://doi.org/10.1021/la0202374
Suganya S, Bharathidasan R, Senthilkumar G, Madhanraj P, Panneerselvam A (2012) Antibacterial activity of essential oil extracted from Coriandrum sativam (L.) and GC-MS analysis. J Chem Pharm Res 4:1846–1850
Sun H et al (2019) Rapid aerobic inactivation and facile removal of Escherichia coli with amorphous zero-valent iron microspheres: indispensable roles of reactive oxygen species and iron corrosion products. Environ Sci Technol 53:3707–3717. https://doi.org/10.1021/acs.est.8b06499
Sun Y-P, X-q L, Cao J, W-x Z, Wang HP (2006) Characterization of zero-valent iron nanoparticles. Adv Colloid Interf Sci 120:47–56. https://doi.org/10.1016/j.cis.2006.03.001
Tang Z-X, Lv B-F (2014) MgO nanoparticles as antibacterial agent: preparation and activity. Braz J Chem Eng 31:591–601. https://doi.org/10.1016/j.jconhyd.2010.09.003
Water S, Organization WH, Sanitation and Health Team (2006) Guidelines for drinking-water quality [electronic resource] : incorporating first addendum. Vol. 1, Recommendations, 3rd ed. World Health Organization. https://apps.who.int/iris/handle/10665/43428
X-q L, Brown DG, W-x Z (2007) Stabilization of biosolids with nanoscale zero-valent iron (nZVI). J Nanopart Res 9:233–243. https://doi.org/10.1007/s11051-006-9187-1
Xu C, Akakuru OU, Zheng J, Wu A (2019) Applications of iron oxide-based magnetic nanoparticles in the diagnosis and treatment of bacterial infections. Frontiers in bioengineering and biotechnology 7:141. https://doi.org/10.3389/fbioe.2019.00141
Yan W, Herzing AA, Kiely CJ, W-x Z (2010) Nanoscale zero-valent iron (nZVI): aspects of the core-shell structure and reactions with inorganic species in water. J Contam Hydrol 118:96–104. https://doi.org/10.1016/j.jconhyd.2010.09.003
You Y, Han J, Chiu PC, Jin Y (2005) Removal and inactivation of waterborne viruses using zerovalent iron. Environ Sci Technol 39:9263–9269. https://doi.org/10.1021/es050829j
Acknowledgments
The authors gratefully acknowledge the Housing & Building National Research Center (HBRC) www.hbrc.edu.eg/ and National Research Centre (NRC) www.nrc.sci.eg/ for providing facilities.
Code availability
Not applicable.
Author information
Authors and Affiliations
Contributions
Ahmed H. Sadek performed research, Conceptualization, Methodology, Software, and Writing-Original draft preparation. Mohsen S. Asker performed Data curation, Investigation, Resources, reviewed and edited the paper. Sayeda A. Abdelhamid performed analysis, Validation, Writing-Reviewing, and Editing.
Corresponding author
Ethics declarations
Ethics approval
Not applicable.
Consent to participate
All the authors listed have approved the manuscript.
Consent for publication
All the authors listed have approved the publication.
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher’s note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Sadek, A.H., Asker, M.S. & Abdelhamid, S.A. Bacteriostatic impact of nanoscale zero-valent iron against pathogenic bacteria in the municipal wastewater. Biologia 76, 2785–2809 (2021). https://doi.org/10.1007/s11756-021-00814-w
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11756-021-00814-w