Abstract
In this work, transmission electron microscopy has been used to investigate HgCdSe/ZnTe/Si (211) heterostructures grown by molecular beam epitaxy and to study the effects of chemical etchants for measurements of defect density in the HgCdSe epilayers. Both ZnTe/Si and HgCdSe/ZnTe interfaces were decorated with {111}-type stacking faults inclined at angles of ∼ 19° or ∼ 90° with respect to the interface plane. Similar stacking faults were also present in the upper regions of the HgCdSe films. High-resolution imaging and Fourier image analysis revealed dislocations, mostly with \( \frac{a}{3}\left\langle\bar{1}11\right\rangle \) Burgers vector, at both ZnTe/Si and HgCdSe/ZnTe interfaces. Etching solutions based on different combinations of nitric acid, hydrochloric acid and lactic acid were tried in attempts to identify an etchant that provided one-to-one correspondence between etch pits and defects in the HgCdSe layer. Focused-ion-beam milling and transmission electron microscopy were used to prepare site-specific cross-section samples from across the etch pits. However, many defects in regions surrounding the etch pits were unaffected by the various different etchants.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
P. Wijewarnasuriya, Y. Chen, G. Brill, N. Dhar, D. Benson, L. Bubulac, and D. Edwall, J. Electron. Mater. 39, 1110 (2010).
M. Vaghayenegar, R.N. Jacobs, J.D. Benson, A.J. Stoltz, L.A. Almeida, and D.J. Smith, J. Electron. Mater. 46, 5007 (2017).
J. Chu and A. Sher, in Physics and Properties of Narrow Gap Semiconductors (Springer, 2008), Chapter 1, p. 7.
P. Capper, in Narrow-gap II–VI Compounds for Optoelectronic and Electromagnetic Applications (Chapman and Hall, London, 1997), Chapter 6, p. 204.
R.N. Andrews, F.R. Szofran, and S.L. Lehoczky, J. Cryst. Growth 92, 445 (1988).
C.R. Whitsett, J.G. Broerman, and C.J. Summers, in Semiconductors and Semimetals (1988), vol. 18, Chapter 2, p. 54.
G. Brill, Y. Chen, and P. Wijewarnasuriya, J. Electron. Mater. 8, 1679 (2011).
J.W. Garland and S. Sivananthan, in Springer Handbook of Crystal Growth, ed. by G. Dhanaraj, K. Byrappa, V. Prasad, and M. Dudley (Springer, Heidelberg, 2010), Chapter 32, p. 1076.
K. Doyle, C.H. Swartz, J.H. Dinan, T.H. Myers, G. Brill, Y. Chen, B.L. Vanmil, and P. Wijewarnasuriya, J. Vac. Sci. Technol. B 31, 03C124 (2013).
W.F. Zhao, G. Brill, Y. Chen, and D.J. Smith, J. Electron. Mater. 41, 2852 (2012).
K. Doyle, Development of Hg 1−x Cd x Se for 3rd Generation Focal Plane Arrays (Morgantown: West Virginia University, 2013).
S. Farrell, M.V. Rao, G. Brill, Y. Chen, P. Wijewarnasuriya, N. Dhar, J.D. Benson, and K. Harris, J. Electron. Mater. 42, 3097 (2013).
Y. Chen, S. Simingalam, G. Brill, P. Wijewarnasuriya, N. Dhar, J.J. Kim, and D.J. Smith, J. Electron. Mater. 41, 2917 (2012).
P. Walker and W.H. Tarn, CRC Handbook of Metal Etchants (Boca Raton: CRC Press LLC, 1991), pp. 221–809.
K. Doyle and S. Trivedi, Dislocation Etching Solutions for Mercury Cadmium Selenide ARL-CR-0744 (2014).
S.Y. Woo, G.A. Devenyi, S. Ghanad-Tavakoli, R.N. Kleiman, J.S. Preston, and G.A. Botton, Appl. Phys. Lett. 102, 132103 (2013).
X.J. Wang, Y. Chang, C.R. Becker, C.H. Grein, S. Sivananthan, and R. Kodama, J. Electron. Mater. 40, 1860 (2011).
D.J. Smith, S.C.Y. Tsen, D. Chandrasekhar, P.A. Crozier, S. Rujirawat, G. Brill, Y.P. Chen, R. Sporken, and S. Sivananthan, Mater. Sci. Eng. B 77, 93 (2000).
Y.A.R. Dasilva, R. Kozac, R. Erni, and M.D. Rossel, Ultramicroscopy 176, 11 (2017).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Vaghayenegar, M., Doyle, K.J., Trivedi, S. et al. Microstructural Characterization of Defects and Chemical Etching for HgCdSe/ZnTe/Si (211) Heterostructures. J. Electron. Mater. 48, 571–582 (2019). https://doi.org/10.1007/s11664-018-6737-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-018-6737-0