Abstract
Iodine-doped CdTe and Cd1−x Mg x Te layers were grown by molecular beam epitaxy. Secondary ion mass spectrometry characterization was used to measure dopant concentration, while Hall measurement was used for determining carrier concentration. Photoluminescence intensity and time-resolved photoluminescence techniques were used for optical characterization. Maximum n-type carrier concentrations of 7.4 × 1018 cm−3 for CdTe and 3 × 1017 cm−3 for Cd0.65Mg0.35Te were achieved. Studies suggest that electrically active doping with iodine is limited with dopant concentration much above these values. Dopant activation of about 80% was observed in most of the CdTe samples. The estimated activation energy is about 6 meV for CdTe and the value for Cd0.65Mg0.35Te is about 58 meV. Iodine-doped samples exhibit long lifetimes with no evidence of photoluminescence degradation with doping as high as 2 × 1018 cm−3, while indium shows substantial non-radiative recombination at carrier concentrations above 5 × 1016 cm−3. Iodine was shown to be thermally stable in CdTe at temperatures up to 600°C. Results suggest iodine may be a preferred n-type dopant compared to indium in achieving heavily doped n-type CdTe.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
M.A. Green, K. Emery, Y. Hishikawa, W. Warta, and E.D. Dunlop, Prog. Photovolt. 24, 1 (2016).
H. Zhao, A. Farah, D. Morel, and C. Ferekides, Thin Solid Films 517, 2365 (2009).
Y. Zhao, M. Boccard, S. Liu, J. Becker, X.-H. Zhao, C.M. Campbell, E. Suarez, M.B. Lassise, Z. Holman, and Y.-H. Zhang, Nat. Energy 1, 16067 (2016).
J.J. Becker, C.M. Campbell, Y. Zhao, M. Boccard, D. Mohanty, E. Suarez, M. Lassise, I. Bhat, Y.-H. Zhang, in Proceedings of the 2016 IEEE 43rd Photovoltaic Specialists Conference (2016), p. 1421.
R. Scheer and H.W. Schock, Chalcogenide Photovoltaics: Physics, Technologies, and Thin Film Devices (Weinheim: Wiley, 2011), pp. 137–145.
X.-H. Zhao, S. Liu, Y. Zhao, C.M. Campbell, M.B. Lassise, Y.-S. Kuo, and Y.-H. Zhang, IEEE J. Photovolt. 6, 552 (2016).
A. Waag, T. Litz, F. Fischer, H. Heinke, S. Scholl, D. Hommel, G. Landwehr, and G. Bilger, J. Cryst. Growth 138, 437 (1994).
F. Bassani, S. Tatarenko, K. Kheng, P. Jouneau, K. Saminadayar, N. Magnea, and R. Cox, Appl. Phys. Lett. 63, 2106 (1993).
D. Brun-Le-Cunff, T. Baron, B. Daudin, S. Tatarenko, and B. Blanchard, Appl. Phys. Lett. 67, 965 (1995).
N.C. Giles, J. Lee, T.H. Myers, Z. Yu, B.K. Wagner, R.G. Benz, and C.J. Summers, J. Electron. Mater. 24, 691 (1995).
C.H. Swartz, K.N. Zaunbrecher, S. Sohal, E.G. LeBlanc, M. Edirisooriya, O.S. Ogedengbe, J.E. Petersen, P.A.R.D. Jayathilaka, T.H. Myers, M.W. Holtz, and T.M. Barnes, J. Appl. Phys. 120, 165305 (2016).
C.H. Swartz, M. Edirisooriya, E.G. LeBlanc, O.C. Noriega, P.A.R.D. Jayathilaka, O.S. Ogedengbe, B.L. Hancock, M. Holtz, T.H. Myers, and K.N. Zaunbrecher, Appl. Phys. Lett. 105, 222107 (2014).
D.C. Look, Electrical Characterization of GaAs Materials and Devices (New York: Wiley, 1989), p. 115.
S. Sohal, M. Edirisooriya, O. Ogedengbe, J. Petersen, C. Swartz, E. LeBlanc, T. Myers, J. Li, and M. Holtz, J. Phys. D Appl. Phys. 49, 505104 (2016).
R.N. Bicknell, N.C. Giles, and J.F. Schetzina, Appl. Phys. Lett. 49, 1095 (1986).
F. Fischer, A. Waag, G. Bilger, T. Litz, S. Scholl, M. Schmitt, and G. Landwehr, J. Cryst. Growth 141, 93 (1994).
W. Van Roosbroeck and W. Shockley, Phys. Rev. 94, 1558 (1954).
A. Rakhshani, J. Appl. Phys. 81, 7988 (1997).
X.-H. Zhao, M.J. DiNezza, S. Liu, C.M. Campbell, Y. Zhao, and Y.-H. Zhang, Appl. Phys. Lett. 105, 252101 (2014).
K.N. Zaunbrecher, D. Kuciauskas, C.H. Swartz, P. Dippo, M. Edirisooriya, O.S. Ogedengbe, S. Sohal, B.L. Hancock, E.G. LeBlanc, and P.A. Jayathilaka, Appl. Phys. Lett. 109, 091904 (2016).
J.M. Burst, J.N. Duenow, D.S. Albin, E. Colegrove, M.O. Reese, J.A. Aguiar, C.-S. Jiang, M. Patel, M.M. Al-Jassim, and D. Kuciauskas, Nat. Energy 1, 16015 (2016).
S. Murakami, T. Okamoto, K. Maruyama, and H. Takigawa, Appl. Phys. Lett. 63, 899 (1993).
C. Maxey, C. Jones, N. Metcalfe, R. Catchpole, M. Houlton, A. White, N. Gordon, and C. Elliott, J. Electron. Mater. 25, 1276 (1996).
C. Maxey, J. Camplin, I. Guilfoy, J. Gardner, R. Lockett, C. Jones, P. Capper, M. Houlton, and N. Gordon, J. Electron. Mater. 32, 656 (2003).
S. Kasap and P. Capper, Springer Handbook of Electronic and Photonic Materials (New York: Springer, 2007), p. 316.
Acknowledgements
Funding from the Alliance for Sustainable Energy, LLC, the manager and operator of the National Renewable Energy Laboratory for the US Department of Energy. Contract No. DEAC36-08GO28308 FPACE II: Approaching the S-Q Limit with Epitaxial CdTe, Subcontract No. ZEJ-4-42007-0.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ogedengbe, O.S., Swartz, C.H., Jayathilaka, P.A.R.D. et al. Iodine Doping of CdTe and CdMgTe for Photovoltaic Applications. J. Electron. Mater. 46, 5424–5429 (2017). https://doi.org/10.1007/s11664-017-5588-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-017-5588-4