Abstract
The dielectric and energy storage properties of lead lanthanum strontium zirconate stannate titanate [(Pb0.92La0.04Sr0.02)((Zr0.70Sn0.30)1−x Ti x )O3] ceramics were investigated as a function of x (0.07 ≤ x ≤ 0.13). With increasing titanium content, the tolerance factor increased, resulting in decreased stability of antiferroelectric phase in the ceramics. As the titanium content was increased, the maximum dielectric constant increased and the temperature of the dielectric maximum shifted to lower values. According to the polarization–electric field hysteresis loops, both the charged and discharged energy densities increased consistently with the increase of titanium content. The unreleased energy densities also showed a systematic trend. From charge–discharge measurements based on the resistance load circuit, the released energy densities and power densities as a function of discharge time were determined over the investigated composition range.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
J.F. Wang, T.Q. Yang, S.C. Chen, and G. Li, Mater. Res. Bull. 48, 3847 (2013).
K. Yao, IEEE Trans. Ultrason. Ferroelectr. 58, 1968 (2011).
Q.F. Zhang, T.Q. Yang, Y.Y. Zhang, J.F. Wang, and X. Yao, Appl. Phys. Lett. 102, 222904 (2013).
L. Shebanov, M. Kusnetsov, and A. Sternberg, J. Appl. Phys. 76, 4301 (1994).
S.E. Park, K. Markowski, S. Yoshikawa, and L.E. Cross, J. Am. Ceram. Soc. 80, 407 (1997).
K. Markowski, S.E. Park, S. Yoshikawa, and L.E. Cross, J. Am. Ceram. Soc. 79, 3294 (1996).
L. Wang, Q. Li, L.H. Xue, and Y.L. Zhang, J. Phys. Chem. Solids 68, 2008 (2007).
Q. Zhang, X.L. Liu, Y. Zhang, X.Z. Song, J. Zhu, I. Baturin, and J.F. Chen, Ceram. Int. 41, 3030 (2015).
M.J. Pan, S.E. Park, K.A. Markowski, W.S. Hackenberger, S. Yoshikawa, and L.E. Cross, Ferroelectrics 215, 153 (1998)
R.D. Shannon, Acta Cryst. A32, 751 (1976).
S. Švarcová, K. Wiik, J. Tolchard, H.J.M. Bouwmeester, and T. Grande, Solid State Ion. 178, 1787 (2008).
X.H. Hao and J.W. Zhai, J. Phys. D 40, 7447 (2007).
I. Burn and D.M. Smyth, J. Mater. Sci. 7, 339 (1972).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Song, X., Zhang, Y., Chen, Y. et al. Effect of Titanium Content on Dielectric and Energy Storage Properties of (Pb,La,Sr)(Zr,Sn,Ti)O3 Ceramics. J. Electron. Mater. 44, 4819–4824 (2015). https://doi.org/10.1007/s11664-015-4038-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-015-4038-4