Abstract
A series of Gd-substituted Ba-Co-based (M-type) hexaferrites having the chemical compositions of Ba0.5Co0.5Gd x Fe12−x O19 (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) were prepared by co-precipitation method. The pellets formed by co-precipitated powder were calcined at a temperature of 1200°C for 20 h. Final sintering was done at 1320°C for 4 h. From the x-ray diffraction analysis, it was revealed that all the samples showed M-type hexagonal structure as a major phase. The scanning electron microscope was used to examine the morphology of the sintered ferrites. The average grain size estimated by the line intercept method was found to be in the range of 2.8–1.0 μm. The room temperature DC resistivity increases with increasing Gd-contents to make these ferrites useful for high frequency applications and microwave devices. Lower values of coercivity (H c) and higher saturation magnetization (M s) may be suitable to enhance the permeability of these ferrites, which is favorable for impedance matching in microwave absorption. In addition, reflection coefficients for a sample was also measured from a frequency of 1 MHz to 3 GHz and a reflection peak was observed at about 2.2 GHz.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
H. Yamamoto, M. Nagakura, and H. Terada, IEEE Trans. Magn. 26, 1144 (1990).
G. Li, G.G. Hu, H.D. Zhou, X.J. Fan, and X.G. Li, Mater. Chem. Phys. 75, 101 (2002).
F. Kools, A. Morel, R. Grossinger, J.M. Le Breton, and P. Tenaud, J. Magn. Magn. Mater. 1270, 242 (2002).
H. Pfeiffer, R.W. Chantrell, P. Gornert, W. Schuppel, E. Sinn, and M. Rosler, J. Magn. Magn. Mater. 125, 373 (1993).
A. Ghasemi and A. Morisako, J. Alloys Compd. 456, 485 (2008).
X. Tang, Y. Yang, and K. Hu, J. Alloys Compd. 477, 322 (2009).
M.V. Rane, D. Bahadur, S.D. Kulkarni, and S.K. Date, J. Magn. Magn. Mater. 195, L256 (1999).
S. Ounnunkada and P. Winotai, J. Magn. Magn. Mater. 301, 292 (2006).
B. Kaur, M. Bhat, F. Licci, R. Kumar, K.K. Bamzai, and P.N. Kotru, Mater. Chem. Phys. 103, 255 (2007).
S. Ounnunkad, Solid State Commun. 138, 472 (2006).
J.F. Wang, C.B. Ponton, and I.R. Harris, J. Magn. Magn. Mater. 298, 122 (2006).
X. Liu, W. Zhong, S. Yang, Z. Yu, B. Gu, and Y. Du, J. Magn. Magn. Mater. 238, 207 (2002).
L. Lechevallier, J.M. Le Breton, J.F. Wang, and I.R. Harris, J. Magn. Magn. Mater. 269, 192 (2004).
N. Rezlescu, C. Doroftei, E. Rezlescu, and P.D. Popa, J. Alloys Compd. 451, 492 (2008).
M. Ahmad, F. Aen, M.U. Islam, S.B. Niazi, and M.U. Rana, Ceram. Int. 37, 3691 (2011).
B.D. Cullity, Elements of X-ray Diffraction, Vol. 338 (Upper Saddle River: Prentice Hall, 1977), p. 102.
G. Listsardakis, I. Manolakis, and K. Efthimiadis, J. Alloys Compd. 427, 194 (2007).
Y. Ogata, Y. Kubota, T. Takami, M. Tokunaga, and T. Shinohara, IEEE Trans. Magn. 35, 3334 (1999).
F. Kools, A. Morel, P. Tenaud, M. Reossignol, O. Isnard, R. Grossinger, J.M. Le Breton, and J. Teillet, Proceeding of the International Conference on ferrites ICF8 (Kyoto Japan, 2000), p. 437.
A. Goldman, Modern Ferrite Technology, 2nd ed. (New York: Springer, 2006), p. 83.
M. Ahmad, R. Grössinger, M. Kriegisch, F. Kubel, and M.U. Rana, Curr. App. Phys. 12, 1413 (2012).
H. Taguchi, J. Phys. IV Fr. 7, c1-299 (1997).
C. Kittel, Introduction to Solid State Physics, 5th ed. (New York: John Wiley & Sons Inc., 1956), p. 24.
J. Smit and H.P. Wijin, Ferrites (London: Cleaver-Hume Press, 1959), p. 185.
S.A. Safaan and A.M. Abo, J. Magn. Magn. Mater. 302, 362 (2006).
T.G.W. Stijintjes, A. Broese Vas Groenou, R.F. Pearson, J.E. Knowles, and P. Rankin, Proceedings of the International Conference (1970).
M. Ajmal and A. Maqsood, Mater. Sci. Eng. B 139, 164 (2007).
M.J. Iqbal and R.A. Khan, J. Alloys Compd. 478, 847 (2009).
A.A. Sattar, H.M. El-sayed, K.M. El-shokrofy, and M.M. El-Tabey, J. Appl. Sci. 5, 162 (2005).
M. Ahmad, R. Grössinger, M. Kriegisch, F. Kubel, and M.U. Rana, J. Magn. Magn. Mater. 332, 137 (2013).
A. Globus, J. Phys. (Paris) Colloq., 1, C1 (1977).
I. Ali, M.U. Islam, M.S. Awan, M. Ahmad, M.N. Ashiq, and S. Naseem, J. Alloys Compd. 550, 564 (2013).
X.-H. Wang, T.-L. Ren, L.-Y. Li, and L.-S. Zhang, J. Magn. Magn. Mater. 184, 95 (1998).
L.Z. Wu, J. Ding, H.B. Jiang, L.F. Chen, and C.K. Ong, J. Magn. Magn. Mater. 285, 33 (2005).
M.B. Reddy and P.V. Reddy, Appl. Phys. 24, 975 (1991).
S.C. Watawe, B.D. Sarwede, S.S. Bellad, B.D. Sutar, and B.K. Chougule, J. Magn. Magn. Mater. 214, 55 (2000).
G. Mu, N. Chen, X. Pan, H. Shen, and M. Gu, Mater. Lett. 62, 840 (2008).
Acknowledgement
The authors gratefully acknowledge Prof. Dr. Shehzad Naseem, CSSP, University of the Punjab, Lahore for providing the necessary experimental facilities.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ahmad, I., Ahmad, M., Ali, I. et al. Effects of Gd-Substitutions on the Microstructure, Electrical and Electromagnetic Behavior of M-Type Hexagonal Ferrites. J. Electron. Mater. 44, 2221–2229 (2015). https://doi.org/10.1007/s11664-015-3671-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-015-3671-2