Abstract
Rolling contact fatigue is the main failure mechanism of tapered roller bearings. This study investigated the fatigue mechanism of rollers in a tapered roller bearing that failed in a run-to-failure test. Roller microstructure and crack morphology were investigated through scanning electron microscopy. A microhardness test was performed to investigate the strain hardening of the roller material induced by rolling contact fatigue. Results showed that microcavities and holes are important influential factors of crack initiation and propagation. Crack propagation angle affects crack morphology and propagation mode. Material strain hardening accelerates crack growth. Furthermore, roller misalignment causes uneven hardenability and severe damage to roller ends.
Article PDF
Similar content being viewed by others
Avoid common mistakes on your manuscript.
References
Jiang L L, Liu Y L, Li X J, et al. Degradation assessment and fault diagnosis for roller bearing based on AR model and fuzzy cluster analysis. Shock Vib, 2011, 18: 127–137
Lei Y G, Lin J, He Z J, et al. Application of an improved kurtogram method for fault diagnosis of rolling element bearings. Mech Syst Signal Pr, 2011, 25: 1738–1749
Wang W, Lee H. An energy kurtosis demodulation technique for signal denoising and bearing fault detection. Meas Sci Technol, 2013, 24: 025601
Harris T A, Kotzalas M N. Essential Concepts of Bearing Technology. 5th ed. Boca Raton: CRC Press, 2006
Vieillard C, Kadin Y, Morales-Espejel G E, et al. An experimental and theoretical study of surface rolling contact fatigue damage progression in hybrid bearings with artificial dents. Wear, 2016, 364-365: 211–223
Sciammarella C A, Chen R J S, Gallo P, et al. Experimental evaluation of rolling contact fatigue in railroad wheels. Int J Fatigue, 2016, 91: 158–170
He C G, Guo J, Liu Q Y, et al. Experimental investigation on the effect of operating speeds on wear and rolling contact fatigue damage of wheel materials. Wear, 2016, 364-365: 257–269
He C G, Huang Y B, Ma L, et al. Experimental investigation on the effect of tangential force on wear and rolling contact fatigue behaviors of wheel material. Tribol Int, 2015, 92: 307–316
Gui X L, Wang K K, Gao G H, et al. Rolling contact fatigue of bainitic rail steels: The significance of microstructure. Mater Sci Eng-A, 2016, 657: 82–85
Benoît D, Salima B, Marion R. Multiscale characterization of head check initiation on rails under rolling contact fatigue: Mechanical and microstructure analysis. Wear, 2016, 366-367: 383–391
Ma L, He C G, Zhao X J, et al. Study on wear and rolling contact fatigue behaviors of wheel/rail materials under different slip ratio conditions. Wear, 2016, 366-367: 13–26
Tokaji K, Horie T, Enomoto Y. Roles of microstructure and carbides in fatigue crack propagation in high V-Cr-Ni cast irons. J Mater Process Tech, 2007, 190: 81–88
Garnham J E, Ding R G, Davis C L. Ductile inclusions in rail, subject to compressive rolling-sliding contact. Wear, 2010, 269: 733–746
Donzella G, Faccoli M, Mazzù A, et al. Influence of inclusion content on rolling contact fatigue in a gear steel: Experimental analysis and predictive modelling. Eng Fract Mech, 2011, 78: 2761–2774
Makino T, Neishi Y, Shiozawa D, et al. Effect of defect shape on rolling contact fatigue crack initiation and propagation in high strength steel. Int J Fatigue, 2016, 92: 507–516
Shen Y, Moghadam S M, Sadeghi F, et al. Effect of retained austenite–Compressive residual stresses on rolling contact fatigue life of carburized AISI 8620 steel. Int J Fatigue, 2015, 75: 135–144
Zhou Y, Peng J F, Wang W J, et al. Slippage effect on rolling contact wear and damage behavior of pearlitic steels. Wear, 2016, 362-363: 78–86
Zheng C, Lv B, Zhang F, et al. A novel microstructure of carbide-free bainitic medium carbon steel observed during rolling contact fatigue. Scripta Mater, 2016, 114: 13–16
Li Y, Kang G, Wang C, et al. Vertical short-crack behavior and its application in rolling contact fatigue. Int J Fatigue, 2006, 28: 804–811
Tokaji K, Horie T, Enomoto Y. Effects of microstructure and carbide spheroidization on fatigue behaviour in high V-Cr-Ni cast irons. Int J Fatigue, 2006, 28: 281–288
Shen Z J, He Z J, Chen X F, et al. A monotonic degradation assessment index of rolling bearings using fuzzy support vector data description and running time. Sensors, 2012, 12: 10109–10135
Bower A F. The influence of crack face friction and trapped fluid on surface initiated rolling contact fatigue cracks. J Tribol, 1988, 110: 704–711
Wolf E. Fatigue crack closure under cyclic tension. Eng Fract Mech, 1970, 2: 37–45
Suresh S, Zamiski G F, Ritchie D R O. Oxide-induced crack closure: An explanation for near-threshold corrosion fatigue crack growth behavior. Metall Mater Trans A, 1981, 12: 1435–1443
Solanki K, Daniewicz S R, Newman Jr. J C. Finite element analysis of plasticity-induced fatigue crack closure: An overview. Eng Fract Mech, 2005, 71: 149–171
Hou C Y. Three-dimensional finite element analysis of fatigue crack closure behavior in surface flaws. Int J Fatigue, 2004, 26: 1225–1239
Paris P, Erdogan F. A critical analysis of crack propagation laws. J Basic Eng, 1963, 85: 528
Tanaka K. Fatigue crack propagation from a crack inclined to the cyclic tensile axis. Eng Fract Mech, 1974, 6: 493–507
Erdogan F, Sih G C. On the crack extension in plates under plane loading and transverse shear. J Basic Eng, 1963, 85: 519
Shiozawa K, Lu L, Ishihara S. S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel. Fat Frac Eng Mat Struct, 2001, 24: 781–790
Qin X F, Sun D L, Xie L Y, et al. Hardening mechanism of Cr5 backup roll material induced by rolling contact fatigue. Mater Sci Eng-A, 2014, 600: 195–199
Wasiluk B, Hoshide T. The fracture process in elastic-plastic materials under biaxial cyclic loading. Int J Fatigue, 2003, 25: 221–229
Daily J S, Klingbeil N W. Plastic dissipation in mixed-mode fatigue crack growth along plastically mismatched interfaces. Int J Fatigue, 2006, 28: 1725–1738
Irwin G R. Plastic zone near a crack and fracture toughness. In: Proceedings of 7th Sagamore Ordnance Materials Conference. Syracuse: Syracuse University Press, 1960. 63–78
Zhao J S, Liu W, Zhang Y, et al. Effects of gyroscopic moment on the damage of a tapered roller bearing. Mechanism Machine Theor, 2013, 69: 185–199
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Guo, W., Cao, H., Zi, Y. et al. Material analysis of the fatigue mechanism of rollers in tapered roller bearings. Sci. China Technol. Sci. 61, 1003–1011 (2018). https://doi.org/10.1007/s11431-017-9249-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11431-017-9249-2