Abstract
Damage to components made of brittle material due to thermal shock represents a high safety risk. Predicting the degree of damage is therefore very important to avoid catastrophic failure. An energy-based linear elastic fracture mechanics bifurcation analysis using a three-dimensional finite element model is presented here, which allows the determination of crack length and crack spacing for a defined thermal load in a free plate. It is assumed that a hierarchical crack pattern is formed due to cooling penetration. The constant growth of the ideal regular pattern of hexagons can change into a pattern with a different symmetry by slightly changing the cooling conditions. This bifurcation point is determined by the second derivative of the mechanical potential with respect to the geometry of the crack front. The very high computational effort for the second derivative is reduced by describing the three-dimensional crack front with a limited number of Fourier coefficients. A one-dimensional transient temperature field at a sufficient distance from the plate edge is assumed. For alumina, the crack length and crack spacing curves are computed for different quenching temperatures and heat transfer coefficients. The corresponding final crack lengths are also calculated as a measure of damage. Comparison with a two-dimensional model confirms the expected 1/2 difference in crack spacing. Data from thermal shock experiments are also presented. However, due to the cracks caused by the strong cooling at the edge, these correspond to the results of the two-dimensional model.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
The study of thermal shocks in brittle materials and the accompanying damage in form of cracks employed by scientists for decades. Fascinating complex crack pattern formations arise during thermal shock. Beside this it is also important to know the residual strength after a thermal shock case to avoid catastrophic failure in technical systems such as gas turbines. Engineering ceramics are widely used as thermal barriers, as they can withstand very high temperatures. This application is always critical due to the relatively low fracture toughness of ceramics. It was analyzed in Kingery (1955) and Hasselman (1963, 1969) which material properties affect thermal shock damage. This was investigated experimentally by quenching alumina rods in water (Hasselman 1970). An overview of various failure phenomena and related thermal stress resistance parameters is given in Hasselman (1985).
The first investigations of 2D hierarchical parallel crack patterns and the associated analysis with a bifurcation instability criterion were carried out in Nemat-Nasser et al. (1978) and Bažant et al. (1979). Based on this criterion, the 2D crack patterns that occur when glass quartz plates are quenched in water (Bahr et al. 1986) were qualitatively investigated in Bahr et al. (1988) using the Boundary Element Method (BEM). It was found that after thermal shock the final crack length has a significant influence on the strength degradation. Nemat-Nasser et al. (1980) then published another bifurcation instability criterion which was also used in later publications (Bahr et al. 1996, 2010; Hofmann et al. 2011). In Bahr et al. (1992) another bifurcation criterion based on the mechanical potential and an eigenvalue analysis was shown. This criterion is equivalent to that of Nemat-Nasser et al. (1980). Furthermore, in Bahr et al. (1992) the correctness of the assumption of the hierarchical crack pattern, that one crack stops and another one grows, and the influence of a disturbance on it was shown. Many publications investigated crack patterns by experiments and by various simulation methods, e.g. Shao et al. (2011), Jiang et al. (2012), and Xu et al. (2016a). However, they all focus on 2D crack patterns.
In Bourdin et al. (2014), a scalar damage variable within a non-local damage model was used to simulate the growth of 3D columnar joints in thermal shocked ceramics. It was shown that this can explain the formation of imperfect polygonal patterns and their selective coarsening during propagation, but an analysis of the 3D crack pattern geometry is still missing. 3D crack patterns of basalt columns were investigated with the Finite Element Method (FEM) in Bahr et al. (2009) by a fracture mechanic bifurcation analysis based on the local energy release rate. This research is similar to the investigated 2D cases in Bahr et al. (1988, 2009, 2010). In order to determine the 3D crack contour, an elaborate gradient method was used for the bifurcation analysis. To avoid this cumbersome iteration of the crack front, a new effective calculation method was developed based on the global energy release rate G and on a Fourier series expansion of the 3D crack front in order to simplify the bifurcation analysis. The application of this method has been demonstrated in Anderssohn et al. (2018). To enable a comparison with Bahr et al. (2009), the growth of 3D crack patterns of basalt columns was also investigated with a steady-state temperature field. The method of Anderssohn et al. (2018) can now be used to investigate the growth of other crack patterns, e.g., generated by drying or, as here, by a transient thermal shock load case for a finite length.
In the present work, we use the ideal hexagonal three column pattern from Bahr et al. (2009) and the Fourier series expansion of the 3D crack front contour from Anderssohn et al. (2018). An FE model for an infinite free plate of thickness 2b is built, which allows for calculating the resulting normalized crack spacing L/b and crack length \({a_{0}}/{b}\) due to thermal shock. Finally, the goal of the present study is to predict the normalized final crack length \({a_{end}}/{b}\) which is crucial for the residual strength of ceramic components that were damaged by thermal shocks.
This paper is organised as follows: Sect. 2 presents the analytical temperature field and the basic thermo-mechanical equations. In addition, the underlying model of the periodic contiuable ideal hexagonal three column pattern is described. The presentation of the theory of eigenanalysis of the global mechanical potential together with the development of the crack front geometry as a Fourier series, which was used to find the bifurcation points, concludes the section. In Sect. 3, the numerical parameters of the FE model and the central Finite Difference Method (FDM) used to determine the derivatives of the mechanical potential are explained. A convergence analysis and the effects of different numbers of Fourier series coefficients on the result are shown. Successful calculations for different temperature differences \(\varDelta T\) and heat transfer coefficients h were performed in Sect. 4. The influence of \(\varDelta T\) and h on the crack length \(a_0/b\) and the crack spacing L/b is discussed. For the validation of the 3D model, thermoshock experiments and calculations for an already existing 2D model were performed, evaluated and compared with the data of the 3D model in Sect. 5. Furthermore, a novel evaluation method based on Computed Tomography (CT) was applied to the thermo-shocked specimens in this work. Note: Similar experiments have already been performed, for example, in Shao et al. (2010) and Xu et al. (2016b). Unfortunately, no material data are given in these publications and thus cannot be used for validation. Finally, in Sect. 6, several conclusions are drawn and an outlook on possible future applications of the model presented in this paper is given.
2 Theoretical considerations
2.1 Temperature profile
First, a plate is heated to the temperature \(T_0\) and then quenched in cooling liquid of temperature \(T_1\). The area under consideration is the center of the plate far away from the edges. In the center the temperature field can be described by a simple 1D analytical solution, while at the edges a more complex temperature field is expected. It is assumed that the cracking process has no influence on the temperature field. This assumption is confirmed by two points: firstly, the cracks are orthogonal to the isotherms that means that they do not interfere with the heat flux. Secondly the crack opening is very small so heat transport through the air filled cracks is very small compared to the heat transport through the solid. Due to the short duration of the thermal shock process, this is a common hypothesis (Bahr et al. 1988; Li et al. 2013). Therefore, the transient temperature profile is used for an infinite plate with a thickness of 2b and with symmetrical boundary conditions (Tautz 1971)
where \(\delta =\sqrt{4Dt,}\) \(\mu _n ={hb}/{\kappa } \ \cot (\mu _n)\) and \(\varDelta T=T_0-T_1\). Here, \(\mu _n, n=1...\infty \) are the positive eigenvalues, \(\kappa \) the thermal conductivity, h heat transfer coefficient and D the thermal diffusivity. In Tautz (1971), the origin of the z coordinate is in the centre of the plate, whereas in the present study it is at the surface. This shift of the coordinate system is implemented in Eq. (1) by the \(-\mu _n\) term in the second cosine function (see also Bahr et al. 1987, 1988).
For short times \(\delta ^2 /4b^2 \ll 1\), (it should be noted that in the literature often \(\tau \) for \(\delta ^2 /4b^2\) is used) the number of the used eigenvalues \(\mu _n\) must be high enough. Otherwise Eq. (1) is not valid (Bahr et al. 1987; Martin et al. 2019). 50 and 100 eigenvalues were calculated with the mathematic program MATLAB. For \(\delta /b=0.01\), the maximal difference of the summation term in Eq. (1) was approx \(3.6\cdot 10^{-4}\). In the simulations the smallest time is \(\delta /b=0.1\), therefore 100 eigenvalues are more than enough.
In Fig. 1 the temperature function Eq. (1) is plotted for different \(hb/\kappa \) and \(\delta /b\). The greater \({hb}/{\kappa }\) is, the better is the heat transport between the heated plate and the cooling liquid. An increase of \({hb}/{\kappa }\) leads to an increase of the temperature gradient and therefore the thermal stresses also increase. Because of that, the value of the heat transfer coefficient h is very important for the determination of the damage by the thermal shock. It should be noted that the experimental determination of h is very difficult. In Singh et al. (1981), Zhou et al. (2012), and Jiang et al. (2012) different methods were used to determine h in the case of a thermal shock of alumina in water. The results for the heat transfer coefficient h range from \(10^3 \ \text {W} {\text {m}^{-2} \text {K}^{-1}}\) to \(10^5 \ \text {W} {\text {m}^{-2} \text {K}^{-1}}\).
2.2 Fundamental thermoelastic equations
Due to the thermal shock, the ceramic plate experiences shrinkage leading to mechanical stresses. In Takeuti and Furukawa (1981) it is shown that the ratio of \(V=v_p b /D\) decides if acceleration terms have to be considered for the penetration of a temperature field. Thereby is \(v_p=\sqrt{(1-\nu )E/((1+ \nu )(1-2 \nu )\rho )}\). The thermal diffusivity can be calculated with \(D=\kappa /\rho C_p\). However, for the materials used in this work, neither D nor the specific heat capacity \(C_p\) is given, see Table 1. From Zhou et al. (2012), \(D=5.4\cdot 10^{-6} \text {m}^2 \text {s}^{-1}\) for alumina with similar purity (99.5\(\%\)) and density (\(\rho =3.98 \cdot 10^{3} \text {kg m}^{-3}\)) can be taken. For the \(\hbox {Al}_2\) \(\hbox {O}_3\) material with 99.7\(\%\) purity used in the experiments, with a plate thickness of \(b=3.5\cdot 10^{-3}\) m, \(V=v_p b /D=6.9 \cdot 10^6\) is obtained. For such large values of V, according to Takeuti and Furukawa (1981), p. 118, the ratio of dynamic and quasi-static stresses is equal to one. Thus the acceleration terms can be neglected. Volume forces are not present and the local mechanical equilibrium conditions read
where \(\sigma _{ij}\) are the mechanical stresses. Eq. (2) must be fulfilled in every point of the structure. We assume an isotopic linear thermo-elastic material with linarised kinematics for which the strain \(\varepsilon _{ij}\) can separated into an elastic and a thermal part:
Here, \(u_i\) denotes the displacement, E is the Young’s modulus, \(\nu \) the Poisson’s ratio and \(\delta _{ij}\) the Kronecker symbol in the elastic strain \(\varepsilon _{ij}^{el}\). The third term describes the thermal strain \(\varepsilon _{ij}^{th}\). Here, \(\alpha \) is the thermal expansion coefficient and \(T(z,\delta )-T_0\) the temperature difference according to Eq. (1). \(T_0\) is the reference temperature at which no thermal stresses are present.
For a plate having a 3D crack pattern, to which an instationary temperature field like Eq. (1) is applied, unfortunately no analytical solution of Eq. (2) is available. Therefore, the solution must be obtained numerically. In the present research, this is done by the FEM through the program Ansys. Please note that an analytical solution of the stress field which fulfills Eq. (2) for a plate without cracks is given in Timoshenko and Goodier (2017) and Parkus (1968).
2.3 Model development and boundary conditions
In experimental investigations on dried starch-water suspensions, it was found that a regular hexagonal cracking pattern causes three columns to merge into a larger one, see Fig. 2a. A similar type of column could be observed in basalt columns, which were formed by thermal contraction of solidified lava. In both cases, the tensile stress caused by drying or cooling is the reason for the appearance of the cracks (see also Goehring et al. 2006; Goehring 2008). The process of merging three columns into one is periodically repeatable in the depth (z-direction) and also in the width of the material. This was used to form the model described below. Fig. 2b shows the idealised model with three regions. In region (I) there are three hexagonal columns of equal size with column diameter L. These columns are caused by the steady propagation of the crack front and are referred to as fundamental solution. The model then assumes that the crack stops growing at the (bp) point in the middle of the three columns. So there is another solution besides the fundamental solution. The point (bp) is hence a bifurcation point in the mathematical sense.
In region (II), the crack front between \(s/{\tilde{p}}=0\) and \(s/{\tilde{p}}=1\) in Fig. 3a stops growing. With this termination, the high symmetry of the hexagons is lost and mixed mode crack propagation with curved crack faces occurs. The three columns merge in region (III) to form a larger column with a new column diameter of \(\sqrt{3}L\). It should be noted that region (II) after the bifurcation point is called the post-critical solution.
As in Anderssohn et al. (2018) and Bahr et al. (2009), we use symmetry and periodicity to reduce the computational costs. The representative volume element, used for the calculation in the case of a bifurcation, is one half of a hexagonal column (gray area in Fig. 3b). This is sufficient due to the periodic repetition. In Fig. 3b this is shown by the three points 0 in which the crack stops in the other two surrounding three hexagonal column configurations. This leads to a point symmetry with respect to point 2 with the following coupling of the displacements in the ligament surfaces E and F of the representative volume element in Fig 3b:
Here, the index n stands for the normal direction of the ligament surfaces and s is the coordinate of the crack front. Furthermore, the stresses must be consistent at the surfaces E and F. The plate is not subjected to external kinematic constraints, so that the two surfaces G and the ligament surface at D are unloaded in the normal direction, i.e.
This condition was implemented by the Ansys command CE with the requirement that all FE nodes have the same displacement in the surface normal direction. The surface of the plate \(z=0\) and the crack surface are unloaded, i.e. \(\sigma _{ij} n_j=0\). The lower face, at \(z=b\), is the symmetry area at which the boundary condition \(u_i n_i =0\) and \(\sigma _{ij}n_j=0 \ (i \ne j)\) applies.
In the case of uniform column growth, a twelfth of the column is sufficient for the calculation since a higher symmetry is present than in the case of column merging. The ligament face B, shown in Fig. 4, is force-free in the normal direction according to Eq. (5). The faces A, C, and lower face, at \(z=b\), are symmetry areas for which the boundary conditions \(u_j n_j =0\) and \(\sigma _{ij}n_j=0 \ (i \ne j)\) hold. The top surface and the crack surface are free of forces \(\sigma _{ij} n_j =0\) as in the half column model.
2.4 Fracture mechanics and bifurcation
Following Anderssohn et al. (2018), we use the Fourier series
for the parameterization of the crack front. Here, \(a_0\) is the crack length, j the number of cosine elements, \(C_i\) the time-invariant coefficients, \({\tilde{p}}=L/ \sqrt{3}\) the column side width shown in Fig. 3b, and s the crack front curve variable. To ensure that the Fourier series can be used as the crack front geometry for the fundamental and also for the bifurcation solution, the product \(2{\tilde{p}}\) is included. The function a(s) is the crack length measured from the surface of the plate, as shown in Fig. 4.
For steady growth, the crack front geometries of the three-column configuration must match the opposite column. Due to the symmetry and periodicity of this configuration, \(i=4, 8, \ldots \) are the only coefficients in Eq. (6) that are nonzero. Due to the huge increase in computation time by increasing the number of coefficients and the low effect on the result (see Fig. 9), the highest Fourier coefficient \(C_4\) is selected.
We introduce here for the case of quasi-static crack growth, the change in the global mechanical potential (see for example Kuna (2013, pp. 42–44))
where the elastic strain energy reads
and the fracture energy
\(W_a\) is the external work. In Eq. (7), the dot above the symbols represents the change between two states. These states can be two different times or, as in this study, the first state is before the crack extension and the second state is after the crack extension \(\partial A\). As there are no external forces or supports acting on the free plate,
Furthermore, the kinetic energy equals zero. The thermal energy has no influence on the crack growth and thus the change in the thermal energy is negligible. Consequently, Eq. (7) has the character of a potential.
The integral over the crack front a(s) in \(W_{fr}\) is equal to the full crack area. \(G_C\) is the critical energy release rate of the material. Integration over the full volume of the strain energy density \(\frac{1}{2} \sigma _{kl} \varepsilon ^{el}_{ij}\) leads to the elastic strain energy \(U_{el}\). The elastic strain energy \(U_{el}\) is implicitly dependent on a(s). Using the Fourier series (Eq. (6)), the mechanical potential \(\varPi (a(s))\), which is a functional, is thus converted into the function \(\varPi (a_0,C_i)\).
As in Anderssohn et al. (2018), Hofmann et al. (2011), Bahr et al. (2009), and Bahr et al. (2010), we use characteristic lengths to scale our model and produce values with the dimension in m. Our model contains six characteristic lengths. Geometric lengths are the crack space L, half the plate thickness b, and the crack length \(a_{0}\) measured from the plate surface, see Fig. 4. Furthermore, \(\delta =\sqrt{4Dt}\) is the penetration depth and \(\kappa /{h}\) is the cooling length of the temperature field according to Eq. (1). From the fracture mechanics side
is the length in the 3D case. The fracture mechanics length \(l_0\) is a value that contrasts the fracture energy per crack area \(G=G_c\), necessary for crack propagation and the stored elastic energy per volume. According to Irwin (1958, p. 560), the mode I energy release rate for the 3D case can be calculated by
\(l_0\) and \(\kappa /{h}\) are given by the mechanical and thermal material properties. The geometrical length b is given by half of the plate thickness. We consider the problem quasi-statically for a time \(\delta =\sqrt{4Dt}\). For this time, \(a_{0}\) and L can be calculated using the two equations for stationary crack propagation \(G=G_c\) and the bifurcation criterion, which will be discussed below.
In the following we give a short overview of the bifurcation analysis considerations according to Anderssohn et al. (2018).
For stationary crack propagation, it is necessary that
is fulfilled.
The system tends to a minimum. This can be calculated by setting the first partial variation of the mechanical potential Eq. (7) to zero, i.e.
Due to the mechanical potential \(\varPi (a_0,C_i)\), Eq. (14) can be rewritten as
which is the fundamental solution of the problem. This solution leads to \(j+1\) equations. \(G_c\) and \(l_0\) are both known in Eq. (11) and if we assume that L is also given, we can use Eq. (15) to determine \(a_0\) and \(C_i\) at a time \(\delta \). Note that changes in the pattern perpendicular to the crack growth direction are excluded in the case of the fundamental solution. This is ensured by the fact that mode I is the only stress intensity factor acting on the entire crack front.
The phenomenon of the merging of the three hexagonal columns, as described in Sect. 2.3, can be understood as a mathematical bifurcation problem. This means that there exists a second solution in addition to the fundamental one. Our goal is to find this bifurcation solution for a set of critical characteristic lengths. Starting from Eq. (15), we formed the second derivative, which leads to the Hessian matrix
where \(C_0=a_0\). The eigenvalue problem
has a nontrivial solution when the coefficient determinant is zero
This leads to \(j+1\) eigenvalues \(\lambda _i\). All eigenvalues have real values because of the symmetry of the Hessian matrix, which results in \(j+1\) real eigenvectors \({\textbf{v}}_i\) computed by \(({\textbf{H}}-\lambda _i {\textbf{I}}){\textbf{v}}_i={\textbf{0}}\).
If Eq. (18) results in positive eigenvalues, then the minimum of the mechanical potential \(\varPi \) (Eq. (7)) is found and the system is stable. This is the case for the fundamental solution, see Sect. 2.3. When one or more of the eigenvalues become negative, the system is unstable and bifurcation occurs. This leads to the merging of the three columns into one. The behavior after the bifurcation can be determined from the eigenvector \({\textbf{v}}\) in conjunction with the fundamental solution a(s) (Nguyen 1987). A set of characteristic lengths is found where the smallest eigenvalue becomes zero, i.e.
Then, the bifurcation point is reached.
The crack grows stationary as long as Eq. (13) is true. It stops growing when the condition (see also Bahr et al. 1988)
is fulfilled. This condition states that for a fixed crack length \(a_0\) the energy release rate G does not increase even though the temperature field (the cooling) continues to penetrate. If the condition
is fulfilled also with the still further penetrating temperature field, it does not come again to the crack growth. Thus, the fixed crack length \(a_0\) in Eq. (20) is the final crack length \(a_{end}\).
3 Finite element model
In this section we will first describe the general procedure how to determine \(a_0/b\) and L/b from the FE analysis. In the following we will give more details about the used numerical methods and the influence of the number of Fourier series coefficients.
As described in Sect. 2.4 we have six characteristic lengths of which four are given. The remaining two can be determined with the condition for stationary crack growth Eq. (13) and with the condition for the occurrence of a bifurcation point Eq. (19).
For a fixed \(hb/\kappa \) and \(\delta /b\), for different crack lengths \(a_0/b\) and crack spacings L/b, the energy release rate \(G_{c FEM}\) is calculated according to the Eq. (15)\(_1\) and the smallest eigenvalue \(\lambda _{min}\) is determined according to the Eqs. (16)–(18) by FE analysis. Due to the restriction to linear elastic material and small deformations, normalized material values \(E=1\), \(\alpha =1\) and a normalized temperature difference \(\varDelta T=1\) can be used in the FE calculations. The dependence of \(\nu \) will be discussed below. Now, by using \(G_{c FEM}\) and the normalized \(E, \alpha , \varDelta T\) and a given \(\nu \), the fracture mechanical length \(l_{0 FEM}\), according to Eq. (11), can be obtained. In a further step, the searched \(a_0/b\) and L/b are now determined. For this purpose, linear interpolation is performed between the values of \(\lambda _{min}\) so that Eq. (19) is fulfilled. Furthermore, \(l_{0 Mat}\) is calculated from a given material, e.g. in Table 1. The fracture mechanical length \(l_{0 FEM}\) is then linearly interpolated so that it matches \(l_{0 Mat}\). This corresponds to the condition for the steady-state crack growth, Eq. (13). Thus, the crack length \(a_0/b\) and crack spacing L/b were determined for a given \(\delta /b\) and a given \(hb/\kappa \). This process was then repeated for further \(\delta /b\) and \(hb/\kappa \).
Note that \(\partial G/\partial \delta \) is always determined with the FE analysis. During the evaluation it can be checked whether the condition for crack stop, Eq. (20), is true. Furthermore, Eq. (11) depends on the Poission’s ratio \(\nu \). In Fig. 5 the normalised fracture mechanical length \(l_0/b\) is plotted against \(\nu \). It can be seen that \(\nu \) has a non-negligible influence. The dependence of \(\nu \) is also given in the analytical solution of the temperature-loaded free plate in Timoshenko and Goodier (2017). Therefore, the Poisson’s ratio \(\nu \) of the material must be taken into account in the FE analysis.
Geometric limits result from the variation of the crack space \(L/b=0.05 \ldots 1\). The change of L causes a change of the model size and due to the meshing, the crack length is thus limited in the range of \(a_{0}/b=0.1 \ldots 0.9\). For some combinations of \(a_{0}/b\) and L/b, crack closures occur when \(\delta /b<0.5\). A more detailed investigation for the values \(a_0/b<0.1\), \(L/b>1\) and \(\delta /b<0.5\) is possible by adapting the FE mesh.
The determination of the derivatives in the fundamental solution Eq. (15), the bifurcation solution Eq. (19), and the change of the energy release rate over \(\delta /b\) Eq. (20) was performed with the FDM analogous to Anderssohn et al. (2018). The central difference quotient with step size \(h_{a}\) for crack length and \(h_\delta \) for time was used for this purpose.
Isoparametric hexahedral elements with quadratic shape functions were chosen for the FE mesh. To guarantee the independence of the step size \(h_a\) in the FDM for the first and second derivatives, small step sizes are required compared to the crack spacing. This means that the strain energies must be determined as accurately as possible. Especially at the crack front, increased stresses and strains occur due to the singularity. Therefore, the crack tip was meshed with singular elements (Barsoum 1976) and a much finer discretisation was carried out in the vicinity of the crack tip (see Fig. 1). It was checked by a convergence analysis that the FE mesh is fine enough and the step sizes \(h_a/b\) and \(h_{\delta }/b\) are sufficiently small for the FDM. Fig. 6 shows the results for the fundamental solution Eq. (15)\(_1\) using the twelfth hexagonal model and Fig. 7a shows the results for \(\lambda _{min}\) (Eqs. (16)–(18)) using the half hexagonal model. Differences in the computation of \(l_0/b\) and \(\lambda _{min}\) are not recognized for the presented range of \(a_0/b\) with increasingly finer FE meshes and shorter step sizes. For the calculation of \(\lambda _{min}\), the second derivative of the strain energy is needed according to Eq. (16). Thus, \(\lambda _{min}\) is more sensitive to numerical inaccuracies compared to \(l_0/b\). Therefore, for \(\lambda _{min}\) the range in which the abscissa is cut (in which then also the bifurcation point occurs according to Eq. (19)), was shown detailed in Fig. 7b. Because of the many possible configurations for L/b, \(\delta /b\), and \(hb/\kappa \), the following settings were chosen for the further analyses for certainty: 65000 nodes for the twelfth hexagonal model, 380000 nodes for the half hexagonal model and \(h_a/b=5\cdot 10^{-4}\) for the step size of the crack length. For the choice of \(h_{\delta }/b\), a similar consideration was made for \(\partial G/\partial \delta \) as for \(\lambda _{min}\) shown in Fig. 8. Again, the differences due to various step sizes \(h_{\delta }/b\) are negligible. Based on Fig. 8b, the step size \(h_{\delta }/b=5\cdot 10^{-4}\) was chosen for the further calculations.
The Hessian matrix Eq. (16) was passed to the mathematical program Matlab, where the eigenvalues \(\lambda _i\) were calculated.
The 1D temperature field Eq. (1) was loaded into the nodes of the 3D FE mesh using a special routine.
To determine \(C_4/b\) (according to Eq. (15)\(_2\)), five FEM calculations were performed with given crack length \(a_0/b\) and given crack spacing L/b using the twelfth column model (fundamental solution). From these calculations with different given values for \(C_4/b\), five values for the elastic strain energy Eq. (8) are obtained. According to the principle of minimum potential energy, the correct value for \(C_4/b\) is the minimum of the least squares interpolation function. As an example, the calculated minimum and maximum values of \(C_4/b\) with the corresponding settings are given in Table 2.
The influence of the number of coefficients j in the Fourier series Eq. (6) is shown in Fig. 9. The calculations were performed for the \(\hbox {Al}_2\) \(\hbox {O}_3\) 99.8% plate (Table 1) with \(h=10^4 {\text {W}}/{\text {m}^2 \text {K}}\) resulting in \({hb}/{\kappa }=1.0833\) and \(\varDelta T=800 K\). The crack spacing L/b versus the crack length \(a_0/b\) is presented in Fig. 9a. In Fig. 9b, the time variation of the energy release rate \(\partial G /\partial \delta \) versus the crack length \(a_0/b\) is shown. As can be seen, the difference in the results is low. This is in good agreement with the results by Anderssohn et al. (2018). For example, in Fig. 9b, where the curves cross the abscissa, the final crack length \(a_{end} /b\) is readable. The relative difference between \(j=1\) (\(a_{end,C1}/b=0.4839\)) and \(j=4\) (\(a_{end,C4}/b=0.4936\)) is about 2%. To save computational time, \(j=1 \ (a_{0}\) and \( C_1)\) was chosen for further calculations.
4 Crack pattern in thermo-shocked free alumina plate
It is assumed that an alumina plate is heated to a temperature \(T_0\). Then the plate is quenched in a cooling liquid of constant temperature \(T_1\). At a sufficient distance from the interface, the temperature field (Eq. (1)) holds in the plate.
Table 1 shows the material, thermal and geometrical properties of alumina plates.
Extensive simulations were performed for the \(\hbox {Al}_2\) \(\hbox {O}_3\) 99.7% plate (Table 1). The results are illustrated in Figs. 10 and 11.
If \({a_{end}}/{b}\) or \({L_{end}}/{b}\) or better both are known from experiments and all parameters listed in Table 1 are also known, it is generally possible to determine the heat transfer coefficient h from diagrams like Fig. 10 between any brittle material and the cooling medium.
Here, the value \({hb}/{\kappa }=1\) represents a kind of transition point. For \({hb}/{\kappa }<1\), small changes of \({hb}/{\kappa }\) have a very strong influence on the temperature gradient and thus on the stress. The final crack length achieved (Fig. 10a) and the final crack spacing (Fig. 10b) are very different. For \({hb}/{\kappa }>1\), only large changes in \({hb}/{\kappa }\) have a noticeable effect on \({a_{end}}/{b}\) and \({L_{end}}/{b}\). If \({hb}/{\kappa }>2\) the values of \({a_{end}}/{b}\) and \({L_{end}}/{b}\) very quickly approach the values of the asymptote at \({hb}/{\kappa }=\infty \). This means for the alumina plate 99.7% (Table 1) that the dependence in the final results is small for values of the heat transfer coefficient in the range \(h=16{,}000 \text {W} {\text {m}^{-2} \text {K}^{-1}}\) to \(h=\infty \ \text {W} {\text {m}^{-2} \text {K}^{-1}}\). This could explain why in the literature, e.g. Hasselman (1970), Jiang et al. (2012), Li et al. (2013), and Xu et al. (2016a), the heat transfer coefficient h between water and ceramics was determined to vary over a large range.
The progression of L/b over \({a_{0}}/{b}\) for \({hb}/{\kappa }=1.0833\) and \({hb}/{\kappa }=\infty \) as significant examples is shown in Fig. 11. As can be seen, L/b decreases with increasing \(\varDelta T\). This could also be observed in the experiments, see Figs. 12, 13, and 14, and by Bahr et al. (1986, Fig. 2) and Xu et al. (2016b, Fig. 2) on the outside of the quenched plates. Furthermore, in Fig. 11a it can be seen that the value of the crack spacing L/b hardly changes with the growth of the crack \({a_{0}}/{b}\). This indicates that there is no merging of three columns as described in Sect. 2.3 and that the columns therefore grow in a steady course (fundamental solution). The calculated bifurcation points are not valid because the fixed point 0 in the model (Fig. 3) wants to catch up again. A postcritical analysis could show this (see Bahr et al. 2009, p. 4). However, for \({hb}/{\kappa }=\infty \) in Fig. 11b the crack space L/b is almost tripled for \(\varDelta T=400\) K as well as for \(\varDelta T=450\) K. For the other \(\varDelta T\), L/b changes also significantly with increasing crack length. If the perturbation of the crack pattern is small enough, this will show the same trend as in Fig. 3 and the new diameter should be close to \(\sqrt{3}L\). With the increase of \(\varDelta T\) the tensile stress increases according to Eq. (3). This leads to more cracks and thus to a decrease in the crack spacing L/b. This was also found out in 2D by thermal shock experiments with \(50\times 10 \times 1\, \textrm{mm}^3\) thin ceramic specimens in Jiang et al. (2012, Table 1). Consequently, the competition between short cracks increases. Short cracks have a smaller crack spacing while long cracks have a larger one.
5 Comparison with 2D model and experiments
To validate the developed model, analyses were also performed with a comparable 2D FE model. Furthermore, alumina plates were thermally quenched for different \(\varDelta T\) and evaluated. In Fig. 12 the results from the thermal shock experiment, the 2D and the 3D FEM bifurcation analysis are plotted. First, a brief explanation of the experiments and their evaluation is given. This is followed by a description of the 2D model with a comparison to the data from the 3D model and the experiments. At the end of this section, possible reasons why the 2D model fits the experimental data better than the 3D model are discussed.
The plates for the experiments were made of DOCERAM A-132 \(\hbox {Al}_\text {2}\,\hbox {O}_\text {3}\) 99.7% with the properties given in Table 1 with dimensions of \(40\,\times \, 40\, \textrm{mm}^{2}\). The plates were heated to \(T=550\,^\circ \text {C}\), \(750\,^\circ \text {C}\), \(950\,^\circ \text {C}\) and quenched in boiled water of \(T=100\,^\circ \text {C}\). The quenched temperatures were thus \(\varDelta T=450\,^\circ \text {C}\), \( 650\,^\circ \text {C}\), \( 850\,^\circ \text {C}\). Then the plates were treated with a contrast agent (Schilling et al. 2005) to achieve a better separation of ceramic and crack for the evaluation. Next, the plates were scanned with CT in High Aspect Ratio Tomography mode.
Through the CT scan and the contrast agent, it is possible to produce images of the surface of the sample, but also of the deep interior of the sample with the cracks highlighted, see Figs. 13 and 14.
The crack length \(a_0/b\) and the crack spacing L/b of the thermal shock experiment were measured from Fig. 14. The procedure is exemplified by Fig. 14 (e). The sectional view was loaded into the programme Engauge Digitizer version 10.10. Based on the scale line, the thickness of the sample was determined (2b = 6.97 mm). Then horizontal lines were inserted from the top to the middle. These lines start and end at the outer cracks. The intersections of the lines with the cracks were counted. The crack widths are given by \(L=\)(width of the line)/(number of intersections -1). The associated crack length \(a_0\) is the z-position of the line. Then the ratios L/b and \(a_0/b\) can be determined with the measured b. All information is collected in Table 3.
The 2D FE model is described in Bahr et al. (1988). For the analysis the bifurcation criterion from Nemat-Nasser et al. (1980) and Bahr et al. (1992) was used. In order to compare the results with the 3D model, the same material, thermal and geometrical settings (see Table 1\(\hbox {Al}_2\) \(\hbox {O}_3\) 99.7%) were used in the 2D model as in the 3D model. For the 2D model, the same temperature field as in Eq. (1) was applied.
The results for the final crack length \(a_{end}/b\) with the corresponding final penetration depth of the temperature field \(\delta _{end}/b\) and the final crack space \(L_{end}/b\) in the case of ideal cooling (\(hb/\kappa =\infty \)) are presented in Fig. 15 for the 2D and 3D FE model. The values of \(\delta _{end}/b\) match quite well. The achieved values for \(a_{end}/b\) are slightly larger in the 2D FE model than in the 3D FE model. The difference for \(L_{end}/b\) is slightly larger. A factor of 2 or less between the results of the 2D FE model and those of the 3D FE model agrees well with the findings in Bahr et al. (2009). This kind of difference in \(a_{end}/b\) and \(L_{end}/b\) was also found out in the experiments by Shao et al. (2010). In our investigations, similar results were obtained for other values of \(hb/\kappa \), as shown in Fig. 12.
As shown in Fig. 12, the results of the 2D analysis between \(hb/\kappa =0.5416\) and \(hb/\kappa =1.0833\) agree well with the measured values of the samples. Thus, a heat transfer coefficient between \(h=4.3 \cdot 10^{3} \ \text {W} {\text {m}^{-2} \text {K}^{-1}}\) and \(h=8.7 \cdot 10^{3} \ \text {W} {\text {m}^{-2} \text {K}^{-1}}\) can be determined. This is slightly lower than the measured h in Zhou et al. (2012). This is due to the fact that nucleate boiling occurs at low sample temperatures due to the lower water temperature in Zhou et al. (2012) of 20 \(^\circ \hbox {C}\), thus increasing the heat transfer coefficient. Quenching in boiling water favours the formation of a vapour film, which decreases the heat transfer coefficient (Singh et al. 1981).
It is the question of why the 2D bifurcation analysis seems to predict the crack width L/b better than the 3D one. Here are two possible explanations.
First, due to the fine grain of the material, the cracks can close again after unloading. Thus, it is possible that the contrast agent does not reach every crack and thus the cracks or their lengths are partially poorly detectable. For more details see Zielke et al. (2021).
Second, the 2D and 3D models do not predict cracks going through the entire body, see Fig. 14. In Fig. 13, especially in Fig. 13b, e, h, it can be seen that the cracks start from the edge and go into the whole body. It can be assumed that there is a surplus of energy at the edge due to the high temperature gradient. This causes the cracks to grow unstably into the body. The fact that the cracks also branch out is an indication of this (Kanninen and Popelar 1985, pp. 205–207). These cracks relieve the body and convert the 3D stress state in a 2D stress state.
Thus, there is no longer a closed plate when the cooling penetrates further from the surface. The penetrating cracks have cut the plate into many small slices. As has been shown by Shao et al. (2010, Figs. 3e and f), when comparing a whole plate and stacked individual plates at high temperature differences \(\varDelta T\), the crack pattern on the cooled surface looks similar. So, even for the stacked individual plates, the crack pattern is not invariant in the x- or y-direction (see also Bahr et al. 1986). However, between the interior surfaces of the stacked single plates and the cut surfaces at the whole plates, the patterns differ. Thus, more cracks are found in the whole plates, and thus a shorter crack spacing L/b, than in the interior surfaces of the stacked individual plates. This is not addressed in Shao et al. (2010). Only the fact that crack branching occurs in the stacked single plates and not in the whole plate is explained by a different stress field caused by edge effects in the stacked single plates.
One reason or a combination of both reasons may explain why the 2D bifurcation analysis fits well with the measured data from the experiments.
Nevertheless, in the following aspect the data from the 3D model, as well as the 2D model, match the experiments. Both models predict that the crack spacing will change only slightly. This means that the cracks grow stable and do not recede. This agrees well with the measured data shown in Fig. 12, although it should be noted that the increase in experimental data in L/b is due to the cracks penetrating from the edge.
6 Conclusion and future work
The model developed by Bahr et al. (2009) was applied and adapted to predict the complex growth of the hierarchical 3D crack pattern of a brittle plate under thermal shock conditions without external constraints. This model is based on the assumption that the cracks form ideal hexagonal columns and that in this idealised crack pattern, the merging of three columns into a larger column is the mechanism for increasing the crack spacing. For cooling penetration, it was assumed that a 1D stationary temperature field (Eq. (1)) exists far enough away from the edges. Based on these assumptions, a 3D FEM bifurcation analysis with the Fourier expansion of the crack front (Anderssohn et al. 2018) was performed. Besides the different type of temperature field, the following differences and extensions are present in the model used in this work compared to Bahr et al. (2009) and Anderssohn et al. (2018).
The model no longer has infinite dimensions in the z-direction but the finite thickness b. The temporal penetration of the symmetrical temperature field Eq. (1), the associated reduction of the temperature gradient and thus the reduction of the mechanical stress, leads to crack arrest and thus to a final crack length \(a_{end}\). The final crack length was determined by evaluating the change in the energy release rate as a function of time (Eq. (20)). \(a_{end}\) is the measure of the damage to the structure and can be used later for a residual strength analysis. Because the plate can contract without hindrance, freedom from forces in the lateral direction of the model is required.
Through a convergence study, which includes the optimisation of the FE mesh and the influence of the FDM step size, the computational effort could be reduced. Furthermore, it was shown that the results converge rapidly for an increasing number of Fourier coefficients. To reduce the computational effort even further, the different calculations were carried out with only one Fourier coefficient (\(j =1\)).
Due to the linear nature of the problem and the use of the characteristic lengths, describing the material and the thermal load, it was effectively possible to determine the evolution of the crack spacing L/b over the crack length \(a_0/b\) by a parametric analysis.
The 3D model was verified by a comparison with an existing 2D model by Bahr et al. (1988). As in Bahr et al. (2009), the expected difference between 2D and 3D FE model in L/b was smaller than a factor of 2. Due to the intense cooling at the edge of the specimens and the associated formation of cracks through the whole specimen, a validation of the 3D model by experimental data was unfortunately not possible. In further research, additional experimental investigations are planned in which the specimen will be isolated at the edge. It should be noted that due to the evaluation by CT scan, the dimensions of the specimens are limited and specimens with larger dimensions cannot be simply used.
Further investigations with the presented 3D model are possible. For example, by modifying the FE mesh towards very short cracks, the critical temperature difference \(\varDelta T_c\) for thermal shock could be analysed at which no crack growth occurs. It should be noted that a good knowledge of the mechanical and thermal material data is important for an accurate analysis. Conversely, it is possible to determine the critical stress intensity factor \(K_{IC}\) and the heat transfer coefficient h using 3D FEM bifurcation analysis. Both values are difficult to determine using other methods. For this, the curves of \(a_{0}/b\) and L/b must be known from thermal shock experiments.
Abbreviations
- a(s):
-
Contour of crack front
- \(a_{0}\) :
-
Crack length, distance between crack front and plate surface (characteristic length)
- \(a_{end}\) :
-
Final crack length
- b :
-
Half of the plate thickness (characteristic length)
- \(C_i\) :
-
Fourier coefficients
- \(C_p\) :
-
Specific heat capacity
- D :
-
Thermal diffusivity
- E :
-
Young’s modulus
- G :
-
Global energy release rate
- \(G_c\) :
-
Critical energy release rate
- \(G_{c FEM}\) :
-
Energy release rate from FE analysis
- \(\textbf{H}\) :
-
Hessian matrix
- h :
-
Heat transfer coefficient
- \(h_a\) :
-
Step size of the crack length for FDM
- \(h_\delta \) :
-
Step size of the penetration length for FDM
- \(\textbf{I}\) :
-
Identity matrix
- \(K_I\) :
-
Mode I stress intensity factor
- \(K_{IC}\) :
-
Critical mode I stress intensity factor
- L :
-
Crack spacing (characteristic length)
- \(l_0\) :
-
Fracture mechanical length (characteristic length)
- \(l_{0 FEM}\) :
-
Fracture mechanical length from FE analysis
- \(l_{0 Mat}\) :
-
Fracture mechanical length from given material properties
- \(n_i\) :
-
Normal vector
- \(\tilde{p}\) :
-
Column side width
- s :
-
Projected path variable along hexagonal crack front
- \(T_0\) :
-
Temperature of the heated plate before quenching
- \(T_1\) :
-
Temperature of the cooling liquid
- \(T(z,\delta ), T\) :
-
Temperature field depending on location z and penetration length \(\delta (t)\)
- t :
-
Time
- \(U_{el}\) :
-
Elastic strain energy
- \(u_i\) :
-
Displacement, displacement vector
- \(\textbf{v}\) :
-
Eigenvector
- \(W_{fr}\) :
-
Fracture energy
- \(\alpha \) :
-
Thermal expansion coefficient
- \(\delta \) :
-
Time dependent penetration length of the temperature field
- \(\delta _{ij}\) :
-
Kronecker symbol
- \(\varepsilon _{ij}^{el}, \varepsilon _{ij}^{th}\) :
-
Strain tensor, el-elastic, th-thermal
- \(\kappa \) :
-
Thermal conductivity
- \(\lambda \) :
-
Eigenvalue
- \(\nu \) :
-
Poisson’s ratio
- \(\varPi \) :
-
Global mechanical potential
- \(\rho \) :
-
Material density
- \(\sigma _{ij}\) :
-
Stress tensor
- 1D, 2D, 3D:
-
One-, two-, three-dimensional
- BEM:
-
Boundary element method
- CT:
-
Computed tomography
- FDM:
-
Central finite difference method
- FE(M):
-
Finite element (method)
References
Anderssohn R, Hofmann M, Bahr HA (2018) FEM-bifurcation analysis for 3D crack patterns. Eng Fract Mech 202:363–374. https://doi.org/10.1016/j.engfracmech.2018.07.040
Bahr HA, Fischer G, Weiss HJ (1986) Thermal-shock crack patterns explained by single and multiple crack propagation. J Mater Sci 21:2716–2720. https://doi.org/10.1007/BF00551478
Bahr HA, Balke H, Kuna M, Liesk H (1987) Fracture analysis of a single edge cracked strip under thermal shock. Theor Appl Fract Mech 8:33–39. https://doi.org/10.1016/0167-8442(87)90016-4
Bahr HA, Weiss HJ, Maschke HG, Meissner F (1988) Multiple crack-propagation in a strip caused by thermal-shock. Theor Appl Fract Mech 10:219–226. https://doi.org/10.1016/0167-8442(88)90014-6
Bahr HA, Bahr U, Petzold A (1992) 1-d deterministic crack pattern formation as a growth process with restrictions. Europhys Lett 19:485–490. https://doi.org/10.1209/0295-5075/19/6/008
Bahr HA, Bahr U, Gerbatsch A, Pflugbeil I, Vojta A, Weiss HJ (1996) Fracture mechanical analysis of morphological transitions in thermal shock cracking. In: Fracture mechanics of ceramics, vol. 11 : R-Curve behavior, toughness determination, and thermal shock
Bahr HA, Hofmann M, Weiss HJ, Bahr U, Fischer G, Balke H (2009) Diameter of basalt columns derived from fracture mechanics bifurcation analysis. Phys Rev E. https://doi.org/10.1103/PhysRevE.79.056103
Bahr HA, Weiss HJ, Bahr U, Hofmann M, Fischer G, Lampenscherf S, Balke H (2010) Scaling behavior of thermal shock crack patterns and tunneling cracks driven by cooling or drying. J Mech Phys Solids 58:1411–1421. https://doi.org/10.1016/j.jmps.2010.05.005
Barsoum RS (1976) On the use of isoparametric finite elements in linear fracture mechanics. Int J Numer Methods Eng 10:25–37
Bažant Z, Ohtsubo H, Aoh K (1979) Stability and post-critical growth of a system of cooling or shrinkage cracks. Int J Fract 15:443–456. https://doi.org/10.1007/BF00023331
Bourdin B, Marigo JJ, Maurini C, Sicsic P (2014) Morphogenesis and propagation of complex cracks induced by thermal shocks. Phys Rev Lett. https://doi.org/10.1103/PhysRevLett.112.014301
CeramTec GmbH (2015) https://www.ceramtec-group.com/fileadmin/user_upload/Corporate/11_Downloads/3880_Prosp_Keram_Werkstoffe_DE-EN_Montage_web.pdf
DOCERAM GmbH (2014) https://www.moeschter-group.com/de/werkstoffe/aluminiumoxid
Goehring LAZ (2008) On the scaling and ordering of columnar joints. University of Toronto
Goehring L, Morris SW, Lin Z (2006) Experimental investigation of the scaling of columnar joints. Phys Rev E. https://doi.org/10.1103/PhysRevE.74.036115
Hasselman DPH (1963) Elastic energy at fracture and surface energy as design criteria for thermal shock. J Am Ceram Soc 46:535–540. https://doi.org/10.1111/j.1151-2916.1963.tb14605.x
Hasselman DPH (1969) Unified theory of thermal shock fracture initiation and crack propagation in brittle ceramics. J Am Ceram Soc 52:600–604. https://doi.org/10.1111/j.1151-2916.1969.tb15848.x
Hasselman DPH (1970) Strength behavior of polycrystalline alumina subjected to thermal shock. J Am Ceram Soc 53:490–495. https://doi.org/10.1111/j.1151-2916.1970.tb15997.x
Hasselman DPH (1985) Thermal stress resistance of engineering ceramics. Mater Sci Eng 71:251–264. https://doi.org/10.1016/0025-5416(85)90235-6
Hofmann M, Bahr HA, Weiss HJ, Bahr U, Balke H (2011) Spacing of crack patterns driven by steady-state cooling or drying and influenced by a solidification boundary. Phys Rev E. https://doi.org/10.1103/PhysRevE.83.036104
Irwin GR (1958) Flügge, S.: Handbuch der Physik. Band 6, Springer Verlag, Berlin,, chap Fracture, pp 551–590
Jiang C, Wu X, Li J, Song F, Shao Y, Xu X, Yan P (2012) A study of the mechanism of formation and numerical simulations of crack patterns in ceramics subjected to thermal shock. Acta Mater 60:4540–4550. https://doi.org/10.1016/j.actamat.2012.05.020
Kanninen MF, Popelar CH (1985) Advanced fracture mechanics. Oxford University Press, New York/Clarendon, Oxford
Kingery WD (1955) Factors affecting thermal stress resistance of ceramic materials. J Am Ceram Soc 38:3–15. https://doi.org/10.1111/j.1151-2916.1955.tb14545.x
Kuna M (2013) Finite elements in fracture mechanics, theory—numerics—applications, 1st edn. Springer, Dordrecht. https://doi.org/10.1007/978-94-007-6680-8
Li J, Song F, Jiang C (2013) Direct numerical simulations on crack formation in ceramic materials under thermal shock by using a non-local fracture model. J Eur Ceram Soc 33:2677–2687. https://doi.org/10.1016/j.jeurceramsoc.2013.04.012
Martin H, Wetzel T, Dietrich B (2019) VDI-Wärmeatlas Fachlicher Träger VDI-Gesellschaft Verfahrenstechnik und Chemieingenieurwesen, 12th edn, Springer Vieweg, Berlin, chap E2 Wärmeleitung - instationär, pp 729–755
Nemat-Nasser S, Keer LM, Patihar KS (1978) Unstable growth of thermally induced interacting cracks in brittle solids. Int J Solids Struct 14:409–430. https://doi.org/10.1016/0020-7683(78)90007-0
Nemat-Nasser S, Sumi Y, Keer LM (1980) Unstable growth of tension cracks in brittle solids: stable and unstable bifurcations, snap-through, and imperfection sensitivity. Int J Solids Struct 16:1017–1035. https://doi.org/10.1016/0020-7683(80)90102-X
Nguyen Q (1987) Bifurcation and post-bifurcation analysis in plasticity and brittle fracture. J Mech Phys Solids 35:303–324. https://doi.org/10.1016/0022-5096(87)90010-X
Parkus H (1968) Thermoelasticity. Blaisdell Publishing Company, Waltham, Massachusetts
Schilling PJ, Karedla B, Tatiparthi AK, Verges MA, Herrington PD (2005) X-ray computed microtomography of internal damage in fiber reinforced polymer matrix composites. Compos Sci Technol 65:2071–2078. https://doi.org/10.1016/j.compscitech.2005.05.014
Shao Y, Xu X, Meng S, Bai G, Jiang C, Song F (2010) Crack patterns in ceramic plates after quenching. J Am Ceram Soc 93:3006–3008
Shao Y, Zhang Y, Xu X, Zhou Z, Li W, Liu B (2011) Effect of crack pattern on the residual strength of ceramics after quenching. J Am Ceram Soc 94:2804–2807. https://doi.org/10.1111/j.1551-2916.2011.04728.x
Singh JP, Tree Y, Hasselman DPH (1981) Effect of bath and specimen temperature on the thermal stress resistance of brittle ceramics subjected to thermal quenching. J Mater Sci 16:2109–2118. https://doi.org/10.1007/BF00542371
Takeuti Y, Furukawa T (1981) Some considerations on thermal shock problems in a plate. J Appl Mech 48:113–118. https://doi.org/10.1115/1.3157552
Tautz H (1971) Wärmeleitung und Temperaturausgleich. Akademie-Verlag, Berlin, Die mathematische Behandlung instationärer Wärmeleitungsprobleme mit Hilfe von Laplace-Transformationen
Timoshenko SP, Goodier JN (2017) Theory of elasticity, 3rd edn. McGraw-Hill, New York
Xu XH, Sheng SL, Tian C, Yuan WJ (2016) A comparative analysis of reticular crack on ceramic plate driven by thermal shock. Sci China Phys Chem. https://doi.org/10.1007/s11433-016-0098-2
Xu X, Lin Z, Sheng S, Yuan W (2016) Evolution mechanisms of thermal shock cracks in ceramic sheet. J Appl Mech-T ASME 10(1115/1):4033175
Zhou ZL, Song F, Shao YF, Meng SH, Jiang CP, Li J (2012) Characteristics of the surface heat transfer coefficient for Al2O3 ceramic in water quench. J Eur Ceram Soc 32:3029–3034. https://doi.org/10.1016/j.jeurceramsoc.2012.04.027
Zielke R, Tillmann W, Fischoeder M, Ambaum M (2021) Einsatz von röntgenografischen Verfahren zur hochauflösenden Analyse von Rissmustern. https://www.ndt.net/search/docs.php3?id=26260
Acknowledgements
The authors would like to acknowledge the financial support of the Deutsche Forschungsgemeinschaft (DFG) under Grant No. HO 4791/1-2. The authors are grateful to the Center for Information Services and High Performance Computing [Zentrum für Informationsdienste und Hochleistungsrechnen (ZIH)] at TU Dresden for providing its facilities for high throughput calculations.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jesch-Weigel, N., Zielke, R., Hofmann, M. et al. Analysis of 3D crack patterns in a free plate caused by thermal shock using FEM-bifurcation. Int J Fract 241, 53–72 (2023). https://doi.org/10.1007/s10704-022-00688-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10704-022-00688-2