Abstract
The stoichiometry of ozone and hypochlorous acid reactions with lignin and hexenuronic acid (HexA) was measured in bleaching experiments of Eucalyptus sp. kraft pulp. The progress of the reactions was followed by UV Resonance Raman spectroscopy that can quantify lignin and HexA based on the Raman scattering intensities of the carbon–carbon double bond in HexA and the aromatic ring in lignin. Here, one mol of ozone converted 0.16 mol of lignin (C9 monomer units) and 0.28 mol of HexA, whereas 1 mol of hypochlorous acid converted 0.09 mol of lignin and 0.23 mol of HexA. The use of a tertiary amine catalyst with the hypochlorous acid treatments did not affect these stoichiometries. The stoichiometric ratios showed that ozone was more efficient in oxidizing lignin than hypochlorous acid, while both electrophiles reacted with HexA to a similar extent. HexA reaction by hypochlorous acid was concluded to involve initial electrophilic chlorination of the carbon–carbon double bond, contributing to significant organochlorine (OX) formation in the pulp. Evidence on this was the linear correlation between the initial HexA content and OX (0.59 mol OX per mol HexA) and the high OX content in the xylan extracted from the bleached pulp. The 2D NMR HSQC and TOCSY spectra of the isolated xylans showed the disappearance of HexA signals after the treatment with hypochlorous acid and the appearance of a new spin system, yet to be fully identified.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Ozone (\({\rm{O}}_{3})\) and hypochlorous acid (\({\rm{HOCl}})\) are well known electrophilic agents that are widely used in water treatment and disinfection applications because they efficiently oxidize a wide range of organic substrates (Jyoti and Pandit 2004; Gombas et al. 2017; Ye et al. 2019). \({\rm{O}}_{3}\) is also utilized in the wood pulp industry, more specifically in pulp bleaching, where it is a well-established bleaching chemical, whereas \({\rm{HOCl}}\) has never been used directly for this application. However, recent laboratory studies on bleaching with \({\rm{HOCl}}\) have shown that, even at low dosages, \({\rm{HOCl}}\) can be an extremely efficient oxidant (Isaza Ferro et al. 2021), generating the question of how different the efficiencies of these two bleaching chemicals are.
\({\rm{O}}_{3}\) is the main oxidant for totally chlorine free pulp bleaching technologies. It degrades lignin, hexenuronic acid (HexA) and chromophores, but it can also depolymerize cellulose (Table 1) (Alen et al. 2011). More specifically, \({\rm{O}}_{3}\) reacts two times faster with HexA than lignin, and a 1000 times faster with lignin than with cellulose (Eriksson 1985; Wennerström 2005; Ventorim et al. 2008). Ozone’s reaction with HexA generates oxalic acid and hydroxyl radicals (Vuorinen et al. 1997; Pouyet et al. 2014). With lignin, it reacts by 1,3-dipolar cycloaddition across a double bond forming a primary ozonide, which leads to hydrogen peroxide, muconic acid analogues and structures with carbonyl groups (Gierer 1982, 1997)\(.\)Direct cellulose depolymerization by \({\rm{O}}_{3}\) only occurs when HexA and lignin amounts are low, by attacking cellulose anomeric carbon atoms or by reacting with the glycosidic oxygen atom (Pan et al. 1981). Additionally, the hydrogen peroxide and hydroxyl radicals (formed in situ) contribute to carbohydrate degradation in Z stage (Chirat and Lachenal 1997; Magara et al. 1998; Pouyet et al. 2013). The stoichiometry of lignin degradation with \({\rm{O}}_{3}\) has been studied in bleaching experiments with straw and model compounds, where it was identified that 0.2–0.3 mmol lignin were degraded per mmol \({\rm{O}}_{3}\) (Ben’ko et al. 2003, 2020). Whereas, for the reaction of \({\rm{O}}_{3}\) with HexA there are no stoichiometric ratios available in literature.
On the other hand, as stated earlier, \({\rm{HOCl}}\) has not been used directly in industrial pulp bleaching. It is an unstable compound that raises environmental concerns regarding the formation of organochlorinated compounds (Suess 2010). Instead, \({\rm{HOCl}}\) is an intermediate in chlorine dioxide (\({{\rm{ClO}}}_{2}\)) bleaching, the most common wood pulp bleaching technology. \({\rm{HOCl}}\) is produced when \({{\rm{ClO}}}_{2}\) reacts with lignin (Kolar et al. 1983). Once produced, it plays a crucial role in chlorine dioxide regeneration reaction, increasing the overall delignification of the bleaching stage (Tarvo et al. 2009; Lehtimaa 2010). The reactions of \({\rm{HOCl}}\) with lignin and HexA, have not been studied in detail but as a part of other bleaching treatments. However, as an electrophile, \({\rm{HOCl}}\) could react with lignin leading to muconic acid, quinones, lignin depolymerization and chlorination (Table 1) (Gierer 1982; Alen et al. 2011). In contrast, with HexA, \({\rm{HOCl}}\) is expected to react via chlorination, contributing to the OX of bleached pulps and AOX of bleaching filtrates (Ventorim et al. 2005).
Only recently, the direct application of \({\rm{HOCl}}\) in wood pulp bleaching has gained attention from scholars. Short laboratory bleaching sequences, which include a first stage with low amounts of \({\rm{HOCl}}\), produced fully bleached pulps in nearly 1 h (Afsahi et al. 2015). The stages with \({\rm{HOCl}}\) may be, uncatalyzed (Hmild) or catalyzed (Hcat). Hmild is a 10 min bleaching stage that uses \({\rm{HOCl}}\) (1% active chlorine (Act. Cl) on dry mass of pulp), pH 5 and 60 °C (Isaza Ferro et al. 2021). Hcat is similar to Hmild, but it is a faster stage due to the addition of a tertiary amine catalyst, and the consequential formation of a highly active chloroammonium cation (Afsahi et al. 2015).
Previous studies have shown the efficiency of Hcat and Hmild compared to D stage (Isaza Ferro et al. 2021). Hcat and Hmild stages were more efficient and selective towards delignification, even with smaller Act. Cl dosages, than D stage (Isaza Ferro et al. 2021). The pulp-bound organochlorinated compounds (OX) in Hcat/Hmild pulps were degraded in posterior Z and P bleaching stages, producing fully brightened pulps with low OX values (Isaza Ferro et al. 2021). The Adsorbable Organic Halides (AOX) produced in Hcat/Hmild stages were treated with aerobic bacteria and degraded to similar extend than the AOX formed in a D stage, reaching values accepted by the industry for AOX emissions (Isaza Ferro et al. 2021). Seeing that Hcat and Hmild stages delivered pulps and effluents with similar characteristics, it was proposed that the reaction routes and stoichiometries were similar in both bleaching stages (Isaza Ferro et al. 2021). However, more direct evidence is required to prove this hypothesis.
Nowadays, there is no clear comparison between efficiencies of \({\rm{HOCl}}\) and \({\rm{O}}_{3}\) for the degradation of lignin and HexA in wood pulp. Hence, this article intends to identify the stoichiometry of \({\rm{HOCl}}\) and \({\rm{O}}_{3}\) reactions with lignin and HexA, in bleaching experiments. These values will provide a more objective perspective on the efficiencies of these chemicals for pulp bleaching, which is interesting considering that both chemicals react fast even at low temperatures. This data will also show if Hcat and Hmild have the same stoichiometric ratios for the degradation of lignin and HexA. In this article degradation or conversion refers to changes in the molecular structure of lignin and HexA, not only to the breaking of the molecules into smaller ones. More specifically, the term is used to express the change on lignin’s aromatic character and the breaking of C=C or C=O bonds of HexA, measured with Ultraviolet Resonance Raman (UVRR) spectroscopy. Finally, a new hypothesis is proposed, stating that \({\rm{HOCl}}\) chlorinates HexA without releasing it from the xylan chain in pulp, and assessed by OX measurements and Nuclear Magnetic Resonance (NMR) of the extracted xylans.
Materials and methods
Materials
An oxygen-delignified Eucalyptus sp. kraft pulp with kappa number (KN) 11.9, 50.9% ISO brightness and 1100 ml/g viscosity, provided by a Brazilian pulp and paper mill, was used in the bleaching experiments.
Commercial 10% sodium hypochlorite (\({\rm{NaOCl}}\)) solution, sodium thiosulfate, potassium iodide, 1 M sulfuric acid and citrate pH 5 buffer were purchased from VWR.
Dimethyl sulfoxide (DMSO), ≥ 97.5 sulfuric acid and sugar monomers > 99% (D-(+)-xylose, D-(+)-galactose, D-(+)-glucose and L-rhamnose monohydrated) were obtained from Sigma Aldrich. D-(+)-mannose > 99% was acquired from Fluka. Copper Ethylenediamine (CED) solution (SCAN 16:62) was obtained from OY FF-Chemicals Ab. NMR solvents, deuterated dimethylsulfoxide (DMSO-d6) 99.8% and deuterium oxide were bought from Merck. 1-Ethyl-3-methylimiddazolium acetate (EMIM OAc) ≥ 95% was acquired from Proionic.
Ozone (\({\rm{O}}_{3}\)) was produced via oxygen electrolysis in a Wedeco GSO 30 reactor at a rate of 0.117 ± 0.01 g \({\rm{O}}_{3}\)/min. The tertiary amine catalyst, CEM-DABCO (1-carboethoxymethyl-1-azonia-4-aza-bicyclo[2.2.2]octane chloride) was synthetized according to Isaza Ferro et al. (2020). 1H NMR (400 MHz,\({\rm{D}}_{2}{\rm{O}}\)): δH 1.20 (3H, t, 3JHH = 7.2, \({\rm{COOCH}}_{2}{{\rm{CH}}}_{3}\)); 3.16 (6H, t, 3JHH = 7.6, (\({\rm{CH}}_{2})_{3}{{\rm{N}}}^{+}\)); 3.59, (6H, t, 3JHH = 7.6, (\({\rm{CH}}_{2})_{3}{\rm{N}}\)); 4.17 (2H, s,\({{\rm{N}}^{+}{\rm{CH}}}_{2}{\rm{COOEt}}\)); 4.21 (2H, q, 3JHH = 7.2, \({\rm{COOCH}}_{2}{\rm{CH}}_{3}\)). 13C NMR (400 MHz, \({\rm{D}}_{2}{\rm{O}}\)): 13.10, 43.97, 52.79, 61.67, 63.42, 164.70.
Bleaching experiments and pulp characterization
The molar ratio method was used to identify the stoichiometry of the reactions of \({\rm{O}}_{3}\) and \({\rm{HOCl}}\) with lignin and HexA. Hence, the eucalyptus pulp (42 mmol HexA and 44 mmol lignin C9 monomeric units per kg pulp) was bleached with varying oxidant dosages. The residual lignin and HexA contents were plotted against the oxidant dosage, with the maximum slope or slope in the first part of the plot corresponding to the stoichiometric ratio of the reaction.
Lignin and HexA quantities were measured using Ultraviolet Resonance Raman (UVRR) spectroscopy according to (Montet 2021). This method quantifies lignin and HexA by using the normalized (relative to cellulose) intensity of lignin’s aryl band (symmetric aryl ring stretch) at 1605 cm−1, and of HexA’s C=C and C=O bonds at 1655 cm−1 (Montet 2021). Montet’s quantitative method is an improved procedure based on Jääskeläinen et al. (2005). In comparison with the original method, Montet’s method is more accurate because it removes the effect of the mutual overlapping of lignin and HexA signals by deconvolution of the UVRR spectra. The method provides HexA in µmol/g pulp, and lignin in % (mg/g pulp). Hence, the equivalent moles of lignin were calculated by using molar mass of 230 g/mol for hardwood lignin C9 units \(({{\text{C}}_{9}{\text{H}}_{10.52}}{{\text{O}}_{3.36}}{(\text{OCH}_{3})_{1.20}})\) (Jahan et al. 2012).
Pulp bleaching experiments with \({\rm{HOCl}}\) (expressed as Act. Cl or Cl2), included: a bleaching stage at mild conditions (Hmild) and a catalytic pulp bleaching stage (Hcat), with 0.1% addition of a tertiary amine catalyst (CEM-DABCO) on pulp. Hmild and Hcat stages were made in plastic bags at pH 5–5.5, 60 °C and 10% weight pulp consistency, with \({\rm{NaOCl}}\) dosages from 0.2 to 2.5% Act. Cl on pulp. The plastic bags, containing the pulp and reagents, were placed inside a water bath at 60 °C and mixed manually for 10 to 30 min, until all the \({\rm{HOCl}}\) was consumed. Bleaching with \({\rm{O}}_{3}\) (Z stage) was carried out in a glass balloon flask at 30% consistency, 20 °C and constant agitation. The \({\rm{O}}_{3}\) dosages varied from 0.5 to 1.5% \({\rm{O}}_{3}\) on pulp, and the initial pH was 2.9. \({\rm{NaOCl}}\) and \({\rm{O}}_{3}\) were titrated daily before the experiments according to SCAN-C 29:72. The \({\rm{HOCl}}\) and \({\rm{O}}_{3}\) amounts presented in this article correspond to the amounts dosed into the system.
Pulps with different initial HexA content were produced by exposing the eucalyptus pulp to hot acid treatments (A stage) in plastic bags, at 90 ºC, 10% pulp consistency and pH 2.9. The pH was controlled by the addition of sulfuric acid, and the duration of the stage varied from 2 to 10 h. These pulps were used to identify possible correlation between initial HexA content and pulp-bound organochlorinated compounds (OX) production by \({\rm{HOCl}}\).
The OX content was determined according to ISO 11480 using a Trace Elemental Instruments Xplorer with duplicates. The standard error was ± 30 mg OX/kg.
The bleached pulps were washed with deionized water, centrifuged, homogenized, and stored in the fridge. Hand-sheets were made according to the standard method SCAN-CM 11:95 and used in ISO brightness and UVRR measurements. Viscosity was measured according to SCAN-CM 15:99. Structural carbohydrates were quantified following the NREL/TP-510-42618 laboratory analytical procedure, using a Thermo Scientific Dionex ICS 5000+ DC detector coupled with a Dionex ICS-500+ single pump and a Dionex ASP-AP autosampler.
Extraction of hemicelluloses
Hemicellulose samples from eucalyptus oxygen delignified and \({\rm{HOCl}}\) treated (Hmild 2% Act. Cl) pulps were extracted with the ionic liquid EMIM OAc. The extraction was done in a closed stainless-steel reactor using a EMIM OAc to distilled water ratio of 85:15, 5% weight pulp consistency, 30 rpm, 60 °C for 3 h. The pulp was filter pressed, using a 5 µm pore size metallic mesh, and the dissolved hemicelluloses in EMIM OAc were recovered. The pulp was washed again with a mix of EMIM OAc and distilled water (85:15) and filtered to collect the remaining solubilized hemicelluloses. The collected solutions were combined, and hemicelluloses were precipitated by distilled water addition and centrifugation. Thereafter, the samples were collected and freeze dried according to Roselli et al. (2014).
Hemicellulose characterization
The hemicellulose samples were characterized with FT-IR (Fourier transform infrared), UVRR (Ultraviolet Resonance Raman), 2D NMR (Nuclear Magnetic Resonance) spectroscopy as well as OX measurements.
The FT-IR spectra were measured with a PerkinElmer FT-IR instrument (Spectrum Two model). The UVRR spectra were measured as described earlier (Montet 2021). The NMR spectra of the extracted hemicelluloses were measured in DMSO-d6 at 298 K using a Bruker Avance NEO 600 spectrometer equipped with a 5 mm He-cooled TCI cryoprobe operating at 600.13 and 150.90 MHz for 1H and 13C, respectively. Chemical shifts were referenced to DMSO at 2.5 ppm (1H) and 39.52 ppm (13C). 1H spectra were acquired using a 1 s relaxation delay, 64 transients, a spectral width of 16 ppm, and 64 K data points. 13C spectra were recorded using 2 s relaxation delay, a spectral width of 235 ppm, 5 K transients, and 64 K data points. Phase-sensitive 2D 1H,13C HSQC spectra were acquired with spectral widths of 11 ppm for 1H and 215 ppm for 13C using 2 s relaxation delay, 1 K data points, 256 t1 increments, and 36 transients. An adiabatic version of the HSQC experiment was used (pulse program: hsqcetgpsisp.2). Phase-sensitive 2D 1H,1H TOCSY spectra were acquired with spectral width of 13 ppm in both dimensions using 2 s relaxation delay, 2 K data points, 256 t1 increments, and 16 transients. All TOCSY data were obtained with a mixing time of 80 ms using the DIPSI-2 spin-lock sequence (pulse program: dipsi2gpphzs).
Results and discussion
Stoichiometry of hexenuronic acid degradation by ozone and hypochlorous acid
The stoichiometric ratios of HexA degradation by ozone (\({\rm{O}}_{3}\)) and hypochlorous acid (\({\rm{HOCl}}\)) were calculated from the slopes of Fig. 1a–c. Here, oxygen delignified eucalyptus pulp with an initial HexA content of 42 mmol HexA/kg pulp was treated with variable amounts of \({\rm{O}}_{3}\) (in Z stage) or \({\rm{HOCl}}\) (during Hmild and Hcat stage). The change of HexA content as a function of added oxidant dosage revealed the stoichiometric ratios of the reactions. One mmol of \({\rm{O}}_{3}\) degraded 0.28 mmol HexA (Fig. 1a). Whereas one mmol of \({\rm{HOCl}}\) degraded 0.22 and 0.23 mmol HexA, in the catalyzed and uncatalyzed reactions, respectively (Fig. 1b, c). Hence, \({\rm{O}}_{3}\) was only 20% more efficient for HexA degradation, breaking of its C=C and C=O bonds, than \({\rm{HOCl}}\).
HexA’s degradation continued linearly until most of it was consumed. Additionally, the R2 for all the linear regressions, used to identify the slopes or stoichiometric ratios, were > 0.99 suggesting a high accuracy of the measurements (Fig. 1a–c).
The residual, ‘unreactive’ HexA content was 3–5 mmol/kg depending on the treatment (Fig. 1). This low residual and unreactive HexA relates to previous studies, which proposed that it is not HexA and it actually corresponds to other structures with UVRR shifts similar to HexA’s (Pouyet et al. 2012; Montet 2021).
Stoichiometry of lignin degradation with ozone and hypochlorous acid
The stoichiometry of the reactions of \({\rm{O}}_{3}\) and \({\rm{HOCl}}\) with lignin were identified in a similar manner than for HexA. Eucalyptus pulp, with initial C9 lignin content of 44 mmol /kg of pulp, was treated with variable dosages of oxidants (Fig. 2). The stoichiometric ratios of lignin degradation by \({\rm{O}}_{3}\) and \({\rm{HOCl}}\) were identified from the slopes in Fig. 2a–c. One mmol of \({\rm{O}}_{3}\) degraded 0.16 mmol lignin units (C9), while 1 mmol of \({\rm{HOCl}}\) degraded 0.09 mmol lignin units, in both Hmild and Hcat treatments. The stoichiometric ratios of 0.16 mmol lignin/mmol \({\rm{O}}_{3}\) and 0.09 mmol lignin/mmol \({\rm{HOCl}}\), suggest that \({\rm{O}}_{3}\) is a 70% more efficient than \({\rm{HOCl}}\) for lignin degradation (or disappearance of lignins aryl group) (Fig. 2). The measured stoichiometric ratio of lignin degradation by \({\rm{O}}_{3}\) of 0.16:1 is lower than the stoichiometric ratio of 0.2–0.3:1 reported by Ben’ko et al. (2003, 2020). This apparent lower stoichiometric ratio of lignin degradation by \({\rm{O}}_{3}\) is due to the presence of HexA in the sample, which also consumed \({\rm{O}}_{3}\).
\({\rm{O}}_{3}\) degraded lignin to a higher extent than \({\rm{HOCl}}\) did, probably due to the presence of hydroxyl radicals formed in Z stage (Ek et al. 1989; Pouyet et al. 2013). However, the residual lignin amounts remained constant even at large oxidant dosages for both oxidants. The residual lignin content for Z pulps was 16 mmol/kg pulp, whereas for \({\rm{HOCl}}\) treated pulp it was 23 mmol/kg pulp. These plateaus are well known in pulp bleaching, and they are one of the main reasons to have bleaching sequences with alternating oxidizing and alkaline stages, which solubilize the oxidized lignin.
Overall, it is evident that the catalyst used in the \({\rm{HOCl}}\) treatments did not affect the stoichiometry of the reactions with HexA and lignin (Figs. 1, 2). This confirms the observation from previous studies, that the catalyst only increases the speed of reaction of the \({\rm{HOCl}}\) with the substrates (Isaza Ferro et al. 2021). Therefore, only the data from Hmild will be taken into consideration from this point onwards.
Reactions taking place in Z and Hmild stage, including lignin degradation, are complex and vary widely depending on the oxidant used. \({\rm{O}}_{3}\) can react further with the muconic acid like structures initially formed (Gierer 1982). Whereas \({\rm{HOCl}}\), may chlorinate lignin, decreasing its reactivity for further oxidation (Dence et al. 1996; Tarvo et al. 2010; Alen et al. 2011). But overall is evident that both electrophiles were more selective towards HexA than lignin degradation.
Additionally, identifying possible cellulose degradation, especially at low oxidant dosages, where the stoichiometric ratios were calculated (0–150 mmol oxidant/kg pulp), is important because it could affect the stoichiometric values presented above. This was assessed by measuring the intrinsic viscosity of the samples (Fig. 3). To avoid underestimating the intrinsic viscosity of pulps with CO groups (Z and possibly Hcat and Hmild), the pulps were treated with an alkaline (E) stage before the viscosity measurement with CED (Pouyet et al. 2014). CO groups cause carbohydrate chains scissions in the CED measurements via β-elimination (Lewin et al. 1997).
The viscosity of the pulp decreased rapidly even with low \({\rm{O}}_{3}\) dosages (Fig. 3a), which can be mostly attributed to the reaction of the formed hydroxyl radicals with cellulose, just like proposed by Pouyet et al. (2013). The oxygen-delignified unbleached pulp (KN 11.9) contained abundantly HexA and lignin, which reacted with \({\rm{O}}_{3}\) producing hydroxyl radicals that lead to a sharp viscosity loss. A direct cellulose depolymerization by \({\rm{O}}_{3}\) is possible but unlikely at this low \({\rm{O}}_{3}\) dosages, due to the faster reaction of \({\rm{O}}_{3}\) with HexA and lignin than with cellulose (Eriksson 1985; Wennerström 2005). Increasing the ozone dosage from 200 to 300 mmol/kg didn’t lower the pulp viscosity further which confirms that \({\rm{O}}_{3}\) did not directly react with cellulose (Fig. 3a).
The viscosity loss in Hcat and Hmild experiments was very minor (Fig. 3b–c), and there was no change in viscosity at low \({\rm{HOCl}}\) dosages (at < 200 mmol \({\rm{HOCl}}\)/kg pulp). Also, there was no difference between the viscosity of the Hmild and Hcat treated samples and the pulps with posterior E stage, suggesting that the formation of CO groups was minimal in these treatments.
Overall, from the decrease in viscosity of the Z, Hmild and Hcat samples, at low oxidant dosages, it can be assumed that cellulose degradation did not consume significant amounts of \({\rm{O}}_{3}\) or \({\rm{HOCl}}\) directly, and hence, the lignin and HexA degradation stoichiometric ratios were not substantially affected.
On the other hand, \({\rm{HOCl}}\) is known to chlorinate HexA, during chlorine dioxide bleaching, and to form soluble organochlorinated compounds (AOX) in the bleaching filtrate (Ventorim et al. 2005). Nearly 80% of the AOX from D stage can be traced to soluble chlorinated HexA compounds. For example in a traditional D stage, 53 out of 60 mg AOX/kg pulp could be attributed to HexA (Freire et al. 2003). Instead, this article proposes that a significant part of the chlorinated HexA may initially remain in the pulp as OX, which has not been proved before. Hence, the next sections aim to finding enough evidence to prove this chlorination hypothesis and attempting to characterize the chlorinated compound.
Chlorination of HexA
The hypothesis that \({\rm{HOCl}}\) converts HexA, while forming OX, was studied by exposing oxygen delignified eucalyptus pulps with different initial HexA contents to a constant dosage of \({\rm{HOCl}}\) (1% Act. Cl). Through plotting the OX content of the treated pulps against their initial HexA content (Fig. 4), a linear correlation was found. The slope of the linear fitting indicates that the molar ratio between HexA content and OX formation was 0.59, indicating that OX formation was a major reaction in Hmild treatment. From the linear equation presented in Fig. 4, it is evident that only a minor part of OX was not related with HexA content, indicating the smaller role of lignin chlorination in the initial OX formation.
Characterization of Hmild extracted hemicelluloses
To identify the mechanism of OX formation from HexA, hemicelluloses from the unbleached eucalyptus oxygen delignified and Hmild (2% Act. Cl) pulps were extracted using EMIM OAc as solvent. Sugar analysis of the pulps before and after the extraction was done to identify the efficacy of the extraction process.
According to the sugar analysis, the Hmild and oxygen delignified pulps consisted mainly of cellulose (glucose) and xylan (xylose). The EMIM OAc treatment extracted most (> 70%) of the hemicelluloses from the pulps. However, only ~ 24% of the extracted hemicelluloses was precipitated and prepared for further analyses. Hence, the overall yield of the recovered hemicelluloses was 3.3% of the pulp.
OX of extracted hemicelluloses and pulps before and after the extraction
Because HexA is bound in xylan, the extracted hemicelluloses should have a higher OX content than the original pulp. Hence, the OX of the extracted hemicelluloses and pulps before and after the extraction were measured (Table 2). The extraction treatment of the Hmild treated pulp decreased its OX content by 77%, from 958 mg/kg to only 218 mg/kg, which relates nicely to the 70% hemicellulose extraction mentioned above. The OX content of the isolated hemicelluloses from the Hmild treated pulp was 7 times higher or 1749 mg/kg. Unfortunately, it was not possible to close the mass balance of OX because the applied conditions degraded part of OX during the extraction and purification steps, and as explained earlier, a large part of the hemicelluloses originally in Hmild pulp were lost in the precipitation process.
The high OX content (958 mg/kg pulp) in Hmild pulp before the extraction is due to the large \({\rm{HOCl}}\) dosage used in the bleaching treatment (2% Act. Cl). This large \({\rm{HOCl}}\) dosage was used to guarantee the abundance of the chlorinated HexA. Consequently, this OX content is much higher than the reported OX from traditional D stages (125 mg/kg pulp) and from Hmild (1% Act. Cl) ZP bleaching sequence (with final OX of 148 mg/kg pulp) (Isaza Ferro et al. 2021).
FT-IR and UVRR spectroscopy
FT-IR and UVRR spectroscopy were used to characterize the extracted hemicelluloses and to detect possible changes in them caused by the Hmild treatment.
The FT-IR spectra of the extracted hemicelluloses from oxygen delignified and Hmild pulps presented similar bands at 895, 984, 1040, 1164, 1241, 2886, 2913, and 2270 cm−1 (Fig. 5). These bands are characteristic of xylan structures (Table 3) and confirmed that the extracted hemicelluloses from both pulps were mainly xylans. The only difference the FT-IR spectra of the pulps, is the presence of a band of very low intensity at 734 cm−1. This can represent the C–Cl bond (Feng et al. 2016), suggesting some chlorination of xylan during the Hmild treatment.
The wide UVRR band region of 1250–1500 cm−1, present in the spectra of the extracted hemicelluloses, is non-specific and may have contributions from lignin, HexA and carbohydrates in general (Loureiro et al. 2013). In contrast, the band at 1606 cm−1 is characteristic of aromatic structures (Jääskeläinen et al. 2005), suggesting that the extracted hemicelluloses contained some lignin. Additionally the sample from the oxygen delignified pulp showed the characteristic HexA band at 1655 cm−1 (Jääskeläinen et al. 2005). The lack of the HexA band in the spectrum of Hmild treated sample can relate to the breaking of the C=C and C=O of HexA by \({\rm{HOCl}}\). Hence, the extractions were successful, and the samples were used to identify the possible chlorination of HexA.
2D HSQC and TOCSY NMR spectra
The 2D NMR HSQC spectra of the extracted hemicelluloses (Fig. 6) confirmed that they consisted mainly of xylans. The characteristic signals for xylan (X-I 1 to 5) (Fu et al. 2018) remained unchanged during the Hmild treatment, which confirms that xylan backbone was not modified during the treatment. The xylan 1H and 13C shifts were: 4.3/101.8 (X-I1), 3.9/63.3 (X-I5e); 3.2/63.3 (X-I5a); 3.5/75.5 (X-I4); 3.3/74.0 (X-I3) and 3.0/72.7 (X-I2) 1H/13C ppm which coincide with previous literature (Fundador et al. 2012).
On the other hand, the HSQC spectra of HexA was present only in hemicelluloses extracted from the oxygen delignified pulp. The following HexA signals were identified: 4.89/99.8 (HexA-I1), 3.47/71.0 (HexA-I2), 3.9/66.4 (HexA-I3) and 5.36/105.37 (HexA-I4) 1H/13C ppm. The signals were upfield shifted compared to the reported HexA shifts (Teleman et al. 1996b, a), probably due to the use of DMSO-d6 instead of D2O as NMR solvent. Zooming the HSQC spectra of the hemicelluloses from Hmild treatment revealed some possible new signals, and hence, TOCSY was used to identify possible new spin systems.
The TOCSY spectra of both hemicelluloses presented strong xylan signals, with all the protons being visible, including the hydroxyl protons C2–OH and C3–OH (Fig. 7). The HexA spin system was easily recognized only in the spectrum of hemicelluloses from oxygen delignified pulp, confirming the previously identified signals at: 4.89 (H1), 3.47 (H2), 3.9 (H3) and 5.36 (H4) 1H ppm (Fig. 7a–b). In the TOCSY spectrum of hemicelluloses from the Hmild treated pulp an unidentified spin system of four (4) protons was present (Fig. 7c–d). Two of the signals were close to HexA’s H2 (3.47 ppm) and H3 (3.9 ppm) shifts. The two other signals were downfield relative to HexA’s H1 and H4 shifts, at 5.03 and 5.58 ppm. Hence, the four new signals most likely relate to the structure formed after HexA was chlorinated. The de-shielding effect of chlorine atom in proton chemical shifts of organic compounds was reported by Sprengel et al. (2019).
The four new signals from the TOCSY spectrum were searched in the HSQC spectrum of the hemicelluloses from Hmild pulp. Three (3) of them were identified at 3.47/72.11 3.9/67.15 and 5.03/97.21 1H/13C ppm. The signal at 5.58 1H ppm was not located, and it would correspond to the chlorinated carbon. Unfortunately, it remains unclear why this signal cannot be seen in the HSQC spectrum.
Proposed HexA chlorination mechanism
The electrophilic addition of chlorine on C4 of HexA yields C5 carbonium ion, which is stabilized by the vicinity xylan ring oxygen atom (Fig. 8). Addition of water to the carbonium ion forms a hemiacetal that would ultimately liberate from the xylan chain yielding HexA derived AOX as proposed by earlier studies (Chenna et al. 2016). The formation of stable OX structures requires the nucleophile adding on the carbonium ion to be an alcohol group in xylan. Nevertheless such reaction has not been observed in previous studies with methyl 4-deoxy-ß-L-threo-hex-4-enopyranosiduronic acid (Chenna et al. 2016), and hence, the nucleophile is likely the O3 atom of the xylose unit on which HexA is attached with 1,2-glycosidic bond. The formed structure is an acetal that is relatively stable under mildly acidic and alkaline conditions.
This proposed structure is partly consistent with the observed new NMR spin system. However, we cannot confirm its assignment fully due to the low signal intensity deriving from the ca. 150:1 molar ratio between xylose units and OX in the extracted hemicellulose.
Conclusions
The stoichiometric ratios of lignin and HexA degradation, in eucalyptus wood pulp, with ozone (\({\rm{O}}_{3}\)) and hypochlorous acid (\({\rm{HOCl}}\)) were identified. \({\rm{O}}_{3}\) oxidized 70% more lignin compared to an equimolar amount of \({\rm{HOCl}}\). Surprisingly, both electrophiles had quite a similar efficiency for HexA conversion, which is reported for the first time. \({\rm{O}}_{3}\) degraded 0.16 and 0.28 equivalents of lignin (C9 units) and HexA, respectively. For \({\rm{HOCl}}\) the corresponding stoichiometric values were 0.09 and 0.23 equivalents. Also, both electrophiles were more selective towards HexA than lignin conversion.
The HexA conversion by \({\rm{HOCl}}\) was accompanied with chlorination (during Hmild stage), with the chlorinated structure staying mostly attached to the pulp. Evidence on this HexA related pulp chlorination includes a linear correlation between initial HexA content and the formed OX content (0.59 mmol OX/mmol HexA) and a eightfold OX content in the extracted xylan in comparison with the extracted \({\rm{HOCl}}\) treated pulp. Hence, this article showed that chlorinated HexA is a main component of OX in pulps treated with \({\rm{HOCl}}\). Unfortunately, the proposed chlorinated structure could not be fully identified, and it requires further studies.
Additionally, this study brings a new way of looking at the chemical reactions taking place in chlorine dioxide bleaching stage, where \({\rm{HOCl}}\) is present and plays an important role in the delignification and HexA degradation. The proposed chlorinated OX structure is certainly formed in D stage, contributing to OX of the bleached pulp.
Change history
13 November 2022
Country name France is replaced by Finland in the first affiliation.
References
Afsahi G, Chenna NK, Vuorinen T (2015) Intensified and short catalytic bleaching of eucalyptus kraft pulp. Ind Eng Chem Res 54:8417–8421. https://doi.org/10.1021/acs.iecr.5b01725
Alen R, Andersson R, Annergreen G, et al (2011) Chemical pulping, part 1, fibre chemistry and technology, 2nd edn. Paperi ja Puu Oy, Porvoo
Benko EM, Bokova MN, Pryakhin AN, Lunin VV (2003) The kinetic patterns of ozonolysis of model lignin compounds in aqueous solutions. Russ J Phys Chem 77:586–589
Benko EM, Chukhchin DG, Mamleeva NA et al (2020) Ozonolytic delignification of wheat straw. Russ J Phys Chem A 94:1535–1542. https://doi.org/10.1134/S0036024420080038
Chaikumpollert O, Methacanon P, Suchiva K (2004) Structural elucidation of hemicelluloses from Vetiver grass. Carbohydr Polym 57:191–196. https://doi.org/10.1016/j.carbpol.2004.04.011
Chenna NK, Piovano P, Järnefelt C, Vuorinen T (2016) Organochlorine formation in tertiary amine catalyzed pulp bleaching. J Wood Chem Technol 36:318–328. https://doi.org/10.1080/02773813.2016.1148166
Chirat C, Lachenal D (1997) Effect of hydroxyl radicals on cellulose and pulp and their occurrence during ozone bleaching. Holzforschung 51:147–154. https://doi.org/10.1515/hfsg.1997.51.2.147
Corradini FAS, Baldez TO, Milessi TSS et al (2018) Eucalyptus xylan: an in-house-produced substrate for xylanase evaluation to substitute birchwood xylan. Carbohydr Polym 197:167–173. https://doi.org/10.1016/j.carbpol.2018.05.088
Dence CW, Reeve DW, Histted JA et al (1996) Pulp bleaching principles and practice. In: Dence CW, Reeve DW (eds) 1st edn. TAPPI Press, Atlanta, pp 127–132, 241–260, 379–410, 408–409
Ek M, Gierer J, Jansbo K, Reitberger T (1989) Study on the selectivity of bleaching with oxygen-containing species. Holzforschung 43:391–396. https://doi.org/10.1515/hfsg.1989.43.6.391
Eriksson T (1985) Relative rate of ozonation of lignin model compounds. In: Third international symposium on wood and pulping chemistry, Vancouver, Canada
Feng S, Ma F, Liu R et al (2016) Highly efficient removal of trace level dieldrin from water resources utilizing a cerasomal strategy. J Mater Chem A 4:10263–10273. https://doi.org/10.1039/c6ta00969g
Freire CSR, Silvestre AJD, Neto CP et al (2003) Easily degradable chlorinated compounds derived from glucuronoxylan in filtrates from chlorine dioxide bleaching of Eucalyptus globulus kraft pulp. Holzforschung 57:81–87. https://doi.org/10.1515/HF.2003.013
Fu G, Yue P, Hu Y et al (2018) Fractionation of DMSO-extracted and NaOH-extracted hemicelluloses by gradient ethanol precipitation from neosinocalamus affinis. Int J Polym Sci. https://doi.org/10.1155/2018/9587042
Fundador NGV, Enomoto-Rogers Y, Takemura A, Iwata T (2012) Acetylation and characterization of xylan from hardwood kraft pulp. Carbohydr Polym 87:170–176. https://doi.org/10.1016/j.carbpol.2011.07.034
Gao C, Ren J, Kong W et al (2015) Comparative study on temperature/pH sensitive xylan-based hydrogels: their properties and drug controlled release. RSC Adv 5:90671–90681. https://doi.org/10.1039/c5ra16703e
Gierer J (1982) The chemistry of delignification—a general concept-part II. Holzforschung 36:55–64. https://doi.org/10.1515/hfsg.1982.36.2.55
Gierer J (1997) Formation and involvement of superoxide (O2-/HO2·) and hydroxyl (OH·) radicals in TCF bleaching processes: a review. Holzforschung 51:34–46. https://doi.org/10.1515/hfsg.1997.51.1.34
Gombas D, Luo Y, Brennan J et al (2017) Guidelines to validate control of cross-contamination during washing of fresh-cut leafy vegetables. J Food Prot 80:312–330. https://doi.org/10.4315/0362-028X.JFP-16-258
Isaza Ferro E, Perrin J, Dawson OGJ, Vuorinen T (2020) Tertiary amine-catalyzed generation of chlorine dioxide from hypochlorous acid and chlorite ions. Wood Sci Technol 55:67–81. https://doi.org/10.1007/s00226-020-01247-5
Isaza Ferro E, Ruuttunen K, Perrin J, Vuorinen T (2021) Sustainable bleaching of Eucalyptus sp. kraft pulp with hypochlorous acid, ozone and hydrogen peroxide. Ind Crops Prod. https://doi.org/10.1016/j.indcrop.2021.114004
Jääskeläinen AS, Saariaho AM, Vuorinen T (2005) Quantification of lignin and hexenuronic acid in bleached hardwood kraft pulps: a new calibration method for UVRR spectroscopy and evaluation of the conventional methods. J Wood Chem Technol 25:51–65. https://doi.org/10.1081/WCT-200058239
Jahan MS, Liu Z, Wang H et al (2012) Isolation and characterization of lignin from prehydrolysis liquor of kraft-based dissolving pulp production. Cellul Chem Technol 46:261–267
Jyoti KK, Pandit AB (2004) Ozone and cavitation for water disinfection. Biochem Eng J 18:9–19. https://doi.org/10.1016/S1369-703X(03)00116-5
Kacurakova M, Belton PS, Wilson RH, Ebringerova A (1998) Hydration properties of xylan-type structures: an FTIR study of xylooligosaccharides. J Sci Food Agric 77:38–44
Kolar JJ, Lindgren BO, Pettersson B (1983) Chemical reactions in chlorine dioxide stages of pulp bleaching. Wood Sci Technol 17:117–128. https://doi.org/10.1007/BF00369129
Lehtimaa T (2010) Reactions of chlorine (III) and their kinetics in the chlorine dioxide bleaching of kraft pulps. Doctoral dissertation, Aalto University
Lewin M, Herman F, Science A (1997) Macromol. Symposium, vol 118, 715–724, 724:715–724
Loureiro PEG, Sousa JIT, Carvalho MGVS, Evtuguin DV (2013) Contribution of xylan to the brightness development and stability in the final ECF bleaching of eucalypt (Eucalyptus globulus Labill.) kraft pulp. Holzforschung 67:497–503. https://doi.org/10.1515/hf-2012-0185
Magara K, Ikeda T, Tomimura Y, Hosoya S (1998) Accelerated degradation of cellulose in the presence of lignin during ozone bleaching. J Pulp Pap Sci 24:264–268
Montet E (2021) Investigation of the consequences of the use of ozone in the bleaching of cellulosic fibres. Doctoral dissertation, University Grenoble Alpes
Pan G, Chen C, Chang HM, Gratzl JS (1981) Model experiments on the splitting of glycosidic bonds by ozone. In: International symposium on wood and pulping chemistry, pp 132–144
Pouyet F, Lachenal D, Das S, Chirat C (2012) Minimizing viscosity loss during totally chlorine-free bleaching of hardwood kraft pulp. BioResources 8:238–249. https://doi.org/10.15376/biores.8.1.238-249
Pouyet F, Chirat C, Lachenal D (2013) On the origin of cellulose depolymerization during ozone treatment of hardwood kraft pulp. BioResources 8:5289–5298
Pouyet F, Chirat C, Potthast A, Lachenal D (2014) Formation of carbonyl groups on cellulose during ozone treatment of pulp: consequences for pulp bleaching. Carbohydr Polym 109:85–91. https://doi.org/10.1016/j.carbpol.2014.02.082
Roselli A, Hummel M, Monshizadeh A et al (2014) Ionic liquid extraction method for upgrading eucalyptus kraft pulp to high purity dissolving pulp. Cellulose 21:3655–3666. https://doi.org/10.1007/s10570-014-0344-x
Sprengel J, Wiedmaier-Czerny N, Vetter W (2019) Characterization of single chain length chlorinated paraffin mixtures with nuclear magnetic resonance spectroscopy (NMR). Chemosphere 228:762–768. https://doi.org/10.1016/j.chemosphere.2019.04.094
Suess HU (2010) Bleaching of chemical pulp. In: Pulp bleaching today. Walter de Gruyter GmbH & Co., pp 45–198
Tarvo V, Lehtimaa T, Kuitunen S et al (2009) The kinetics and stoichiometry of the reaction between hypochlorous acid and chlorous acid in mildly acidic solutions. Ind Eng Chem Res 48:6280–6286. https://doi.org/10.1021/ie801798m
Tarvo V, Lehtimaa T, Kuitunen S et al (2010) A model for chlorine dioxide delignification of chemical pulp. J Wood Chem Technol 30:230–268. https://doi.org/10.1080/02773810903461476
Teleman A, Hausalo T, Tenkanen M, Vuorinen T (1996a) Identification of the acidic degradation products of hexenuronic acid by NMR spectroscopy. Carbohydr Res 280:197–208
Teleman A, Siika-Aho M, Sorsa H et al (1996b) 4-O-methyl-β-L-idopyranosyluronic acid linked to xylan from kraft pulp: isolation procedure and characterisation by NMR spectroscopy. Carbohydr Res 293:1–13. https://doi.org/10.1016/0008-6215(96)00170-X
Ventorim G, Colodette JL, Eiras KMM (2005) The fate of chlorine species during high temperature chlorine dioxide bleaching. Nord Pulp Pap Res J 20:7–11. https://doi.org/10.3183/npprj-2005-20-01-p007-011
Ventorim G, Colodette JL, de Fatima GA, da Silva LH (2008) Reaction rates of lignin and hexenuronic acids with chlorine dioxide, ozone, and a sulfuric acid. Wood Fiber Sci 40:190–201
Vuorinen T, Fagerström P, Räsänen E, Vikkula A (1997) Selective hydrolysis of hexenuronic acid groups opens new possibilities for development of bleaching processes. In: International symposium on wood and pulping chemistry Montréal
Wennerström M (2005) Decreasing brightness reversion with powerful ozone bleaching. Pulp Pap Can 106:41–44
Ye B, Cang Y, Li J, Zhang X (2019) Advantages of a ClO2/NaClO combination process for controlling the disinfection by-products (DBPs) for high algae-laden water. Environ Geochem Health 41:1545–1557. https://doi.org/10.1007/s10653-018-0231-8
Acknowledgments
The authors thank Markus Kyllönen for his help in running some of the bleaching experiments, and to Yibo Ma for his guidance on the hemicellulose extraction procedure with EMIM OAc.
Funding
Open Access funding provided by Aalto University. This work was cofunded by Andritz Oy, Kemira Oyj, Metsä Group Oy, Stora Enso Oyj, UPM Kymmene Oyj, Suzano Pulp and Paper and Aalto University School of Chemical Engineering.
Author information
Authors and Affiliations
Contributions
EI and JP collected the experimental data, except for the NMR spectra which was collected by JK. EI wrote the manuscript under the supervision of TV and KR. JP and TV conceptualized the article. All authors revised the article.
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ferro, E.I., Ruuttunen, K., Koivisto, J.J. et al. Stoichiometry of reactions of ozone and hypochlorous acid with lignin and hexenuronic acid and its chlorination. Cellulose 30, 169–182 (2023). https://doi.org/10.1007/s10570-022-04913-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10570-022-04913-y