Abstract
Corrosion resistance of Fe-based bulk metallic glass with sulfide inclusion was investigated in HCl, H2SO4, NaCl and NaOH solutions at different ambient temperature. The results indicate that Fe-based amorphous alloy generally exhibits more excellent corrosion resistance in alkaline solutions than that in acidic solutions, and presents high spontaneous passivated ability and evident passivation region in all solutions. Electrochemical impedance spectroscopy results display that all of the Nyquist curves are composed of just a single capacitive loop, and the electrode reaction is mainly controlled by the electrode potential. The mass loss exceeds 0.67 mg/cm2 in 0.5 M H2SO4 solution, and rapider than that in another solutions. With increase of ambient temperature, the corrosion resistance decreases in all solutions. No pitting corrosion occurs in acidic solutions, though the inclusion particle is dissolved firstly. Seemly, some pit can be formed in NaCl solution, when ambient temperature exceeds 60 °C.
Access provided by CONRICYT-eBooks. Download conference paper PDF
Similar content being viewed by others
Keywords
Introduction
Due to excellent corrosion resistance and high microhardness, Fe-based amorphous alloys present an extensive potential application as anti-corrosive or anti-wearing materials, such as nuclear power, thermal power, ship, automobile, sports equipment, and so on. So many Fe-base amorphous alloy systems as Fe–Co–B–Si–Nb–Cr [1], Fe–Co–Cr–Mo–C–B–Y [2], Fe–Cr–Mo–C–B [3], Fe–Si–B–Nb–Cu [4], have been developed in the last decades. Since the high brittleness, Farmaer et al. [5] has attempted the applications of Fe-based amorphous coatings on the containers for the transportation, aging and disposal of spent nuclear fuel. The neutron absorption cross section in transmission for thermal neutrons of Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 (SAM2X5) with high boron content is four times greater than that of borated stainless steel, and twice as good as nickel-based alloy (C-4) with additions of Gd. The Fe-based amorphous coating with the composition of Fe54.2Cr18.3Mo13.7Mn2W6B3.3C1.1Si1.4(wt%) on the marine pump impellers exhibits 2–3 times erosion rate than that of SUS304, believed to enhance effectively the lifetime of pump impellers in sand-containing seawater [6]. The corrosion rate of Fe-based amorphous coating of Fe48Cr16Mo16C14B2Mn2Y2 is 1/1000 of that of 20G steel in the artificial simulation environment of power plant Boiler [7]. However, for all Fe-based amorphous alloys above mentioned, the produce cost is very high since high pure elements, which limits the extensive application in industries.
In our group, the Fe–C–Si–B–P–Cr–(Mo, Al, Co) amorphous alloy was developed using cast iron, industrial ferroalloys and commercial grade elements [8, 9]. Effects of elements, pH, ambient temperature on corrosion resistance were investigated in the published literatures [10, 11]. Since the impurity elements of oxygen and sulphur in raw materials, some oxide and sulphide can be detected in some bulk amorphous alloy. The effect of sulphur on the glass forming ability and corrosion resistance was investigated [12, 13]. However, effect of sulphide on corrosion behaviors of Fe-based amorphous alloy is unknown. In this paper, the corrosion resistance of Fe-based bulk amorphous alloy with sulphide inclusion will be discussed in difference solutions.
Experimental
The Fe-based amorphous alloy rods with the nominal composition of Fe66.6C7.1Si3.3B5.5P8.7Cr2.3Mo2.5Al2.0Co1.0S1.0 (at.%) were fabricated by the water cooling copper mold suction-casting, and the detailed processing and the composition of raw materials were shown in the literature [9]. Prior to immersion tests and electrochemical measurements, the specimens were degreased in acetone, washed in distilled water and dried in air. Corrosion rates were estimated from the weight loss after immersed in 0.5 M HCl, H2SO4, NaCl and NaOH solutions, respectively, open to air at room temperature for 30 days. The electrochemical measurements were conducted by a potentiostat (CHI 660E PARSTAT) and a three-electrode cell. The counter electrode was platinum and the reference electrode was a saturated calomel electrode (SCE). The potentiodynamic polarizations were measured in 1 M HCl, H2SO4, NaCl and NaOH solutions with 60 mV/min sweep rate at 20, 40 and 60 °C, respectively. The potentiostatic polarization were conducted by applying a potential of 0.5 V in acidic solutions or 0 V (SCE) in alkaline solutions for 2 h at different ambient temperatures. The electrochemical impedance was measured from 0.01 Hz to 100 kHz with the AC mode after the specimens were immersed for 20 min to obtain a stable open circuit potential. After immersion, the surface morphologies were observed by scanning electron microscope (SEM).
Results and Discussions
Figure 1 shows the potentiodynamic polarization curves in 1 M HCl, H2SO4, NaCl and NaOH solutions at different ambient temperature. In HCl solution, the specimen exhibits spontaneous passivation when scanning voltage exceeds 0.3 V, and presents transpassivation as scanning voltage is larger than 1.2 V in different ambient temperature. As the ambient temperature increases, corrosion current density and passive current density also increases, while corrosion potential and passive potential region seem no variation. The all related electrochemical results are shown in Table 1. Compared with HCl solution, a similar tendency can been attained in 1 M H2SO4, NaCl and NaOH solutions.
The current density versus passivation time during the potentiostatic polarization in four solutions is shown in Fig. 2. The applied potential of 0.5 V was selected from the potentiodynamic polarization curves. In HCl solution, the current densities decrease continuously with time and finally reach a steady state current density at 20 °C. While as ambient temperature exceeds 40 °C, the potentiostatic polarization curves are different. Corrosion current density decreases to near 30 μA/cm2 during first 200 s, and then increases sharply, finally reaches a steady state current density of 700 μA/cm2 in the 40 °C. As ambient temperature reaches 60 °C, corrosion current density decreases during first 500 s, the lowest current density is near 200 μA/cm2. And then it increases sharply, finally reaches a steady state current density of 950 μA/cm2. Only when ambient temperature exceeds 60 °C, the corrosion current density decreases firstly, and then increases, finally reaches a steady state in H2SO4 solution. While in NaCl solution, the current density can’t reach a steady state, and increase gradually as increase of time at 60 °C. Moreover, many peak of corrosion current density increasing can be observed during scanning time at 60 °C, which means pitting corrosion. Though ambient temperature exceeds 60 °C, the current densities decrease continuously with time and finally reach a steady state current density in NaOH solution.
Figure 3 shows Nyquist polts obtained from electrochemical impedance spectroscopy measurements in different solutions. The experimental data in the figure are presented as symbols and the solid lines are attained by curve fitting using non-linear-least-square fit analysis [10]. The charge transfer resistance decreases continuously with increase of ambient temperature in all solution. The opposite behavior is observed for the capacitance, as shown in Table 1.
Figure 4 presents the mass loss with the immersion time. It can be observed mass loss increases during the first stage, and then reaches a steady state in four solutions. The highest mass loss rate exceeds 0.67 mg/cm2 in H2SO4 solution, the lowest mass loss rate is near to 0.04 mg/cm2 in NaCl solution. During immersion test, as no passive film is formed on the surface, the mass loss increases with time at first stage. The mass loss is stable gradually, since the formation of passive film and the precipitation of corrosion products on the surface with immersion time increase.
The surface morphologies immersed in four solutions are shown in Figs. 5, 6, 7 and 8. The ‘dried riverbed’ cracked morphologies are clearly observed on the surface immersed in acidic solutions, as shown in Fig. 5 (HCl solution) and Fig. 6 (H2SO4 solution). While no crack, just smoothing surfaces are remained in NaCl (Fig. 7) and NaOH (Fig. 8) solutions. In acidic solutions, firstly, the groove is observed near the inclusion particle in Fig. 5b, and then some cracks originate from the inclusion particles, even pass through them, as shown in Figs. 5c and 6b. Finally, more and more cracks are formed and propagated along all direction on the surface, thus the ‘dried riverbed’ cracked morphologies are formed, as shown in Figs. 5d and 6d. According to the variety of corrosion morphology characteristics, it may be deduced that the inclusion particles are dissolved firstly, and some corrosion products are formed on the position of inclusion particles. With acceleration of corrosion products on the surface, the microstructure in the position of inclusion particles becomes more loosing, compared to other. Therefore, the cracks will initiate and propagate with the great internal stress in the cast specimen.
In alkaline solutions, it is well know that Fe2O3 is main corrosion product and it is stable. So a greater amount of Fe2O3 will precipitated on the surface and this was indentified in the literature [10]. The acicular shape Fe2O3 layer is porosity and loosing, which is benefit to the release of internal stress in cast specimen. Therefore, no crack is formed on the surface.
It is well known that the reaction rate is accelerated generally since the intensifying activity of ions or elements with increase of ambient temperature. Though Fe48.7Cr18Mn1.9Mo7.4W1.6V15.2C3.8Si2.4 amorphous alloy coating is spontaneously passivated with a low passive current density in different ambient temperatures, the passive current density progressively increases and the pitting potential decreases as temperature increases [14]. While the erosion rates of FeBSiNb amorphous coating decrease with increase of test temperature, since the formation of a thick oxide, and surface characteristic modification during erosion testing [15]. Liu [16] found that the Fe-based amorphous composite exhibits an excellent hot corrosion resistance and excellent thermal stability in molten Na2SO4 + K2SO4 salt at 923 K, due to the formation of a continuous and protective Cr2O3 oxide which acts as an effective barrier to the inward diffusion of corrosive species during the hot corrosion process.
In general, the CPE is related to the layer capacitance of the electrode. The thicker the corrosion product is, the higher the CPE is. With increase of ambient temperature, the corrosion reaction is also accelerating, thus the corrosion product is accumulating. The Rct is charge transfer resistance. The increase of Rct indicates an increase in the insulating character of the oxide film [17].
Conclusions
-
(1)
With increase of ambient temperature, the corrosion rate of Fe-based amorphous alloy will accelerate in all solutions.
-
(2)
No pitting corrosion occurs in acidic solutions, though the inclusion particle is dissolved firstly. Seemly, some pit can be formed in NaCl solution, when ambient temperature exceeds 60 °C.
-
(3)
Fe-based amorphous alloy generally exhibits more excellent corrosion resistance in alkaline solutions than that in acidic solutions.
References
Z.L. Long, Y. Shao, A. Inoue, Cr effects on magnetic and corrosion properties of Fe–Co–Si–B–Nb–Cr bulk glassy alloys with high glass-forming ability. Intermetallics 15, 1453–1458 (2007)
H.B. Fan, W. Zhang, J. Shen, Corrosion behavior of Fe41Co7Cr15Mo14C15B6Y2 bulk metallic glass in sulfuric acid solutions. Metallur. Mater. Trans. A 42, 1524–1533 (2011)
S.J. Pang, T. Zhang, A. Inoue, Bulk glassy Fe–Cr–Mo–C–B alloys with high corrosion resistance. Corr. Sci. 44, 1847–1856 (2002)
A. Pardo, E. Otero, M.C. Merino, Influence of Cr addition on the corrosion resistance and magnetic properties of amorphous Fe73.5Si13.5B9Nb3Cu1 in simulated industrial environments. J. Non-Cryst. Solids 287, 421–427 (2001)
J.C. Farmer, J. Haslam, S. Day, The corrosion resistance of Fe-based amorphous metals: Fe49.7Cr17.7Mn1.9Mo7.4W1.6B15.2C3.8Si2.4 and other compositions. Mater. Sci. Tech. 318–392 (2007)
Y. Wang, Y.G. Zheng, Z.M. Yao, Investigation of HVOF-sprayed Fe-based amorphous metallic coatings with high erosion resistance and corrosion resistance, in The 6th China Corrosion Conference, pp. 1030–1036 (2011)
J. Lu, C. Liu, Y. Han, Analysis of utilizing anti-corrosion Fe-based amorphous coating material with the flue gas waste heat in the power plant boiler. Electr. Power Sci. Eng. 30, 13–18 (2014)
H.X. Li, J.E. Gao, S.L. Wang, Formation, crystallization behavior, and soft magnetic properties of FeCSiBP bulk metallic glass fabricated using industrial raw materials. Metall. Mater. Trans. A 43A, 2615–2619 (2012)
S.L. Wang, H.X. Li, S. Yi, Effects of Cr contents in Fe-based bulk metallic glasses on the glass forming ability and the corrosion resistance. Mater. Chem. Phys. 113, 878–883 (2009)
S.L. Wang, H.X. Li, S. Yi, Effects of electrolyte pH on the electrochemical behavior of Fe-based bulk metallic glass. Met. Mater. Inter. 18, 791–797 (2012)
S.L. Wang, S. Yi, The corrosion behaviors of Fe-based bulk metallic glasses in a sulfuric solution at 70 & #xB0;C. Intermetallics 18, 1950–1953 (2010)
S.L. Wang, J.C. Cheng, S. Yi, Precipitation of sulfide particle in situ formed in Fe-based bulk metallic glass. Foundy 62, 491–495 (2013)
S.L. Wang, S.B. Chen, S. Yi, Effects of sulphide on pit corrosion in metallic glass steel. Mater. Res. Innov. 18, 638–641 (2014)
R.Q. Guo, C. Zhang, L. Liu, Corrosion and wear resistance of a Fe-based amorphous coating in underground environment. Intermetallics 30, 94–99 (2011)
J.B. Cheng, X.B. Liang, Y.X. Chen, High-temperature erosion resistance of FeBSiNb amorphous coatings deposited by arc spraying for boiler applications. J. Therm. Spray. Techn. 820–827 (2013)
W.Y. Liu, Y. Hou, C. Liu, Hot corrosion behavior of a centimeter Fe-based amorphous composite coating prepared by laser cladding in molten Na2SO4 + K2SO4 salts. Surf. Coat. Techn. 270, 33–38 (2015)
F. Rosalbino, S. Delsante, G. Borzone, Influence of rare earth metals on the characteristics of anodic oxide films on aluminium and their dissolution behaviour in NaOH solution. Corr. Sci. 52, 322–328 (2010)
Acknowledgements
The work was supported by the National Natural Science Foundation of China (No. 51461031), Department of Education Fund of Jiangxi Province (GJJ150733), Natural Science Foundation of Jiangxi Province (20161BBH80031) and Power Construction Corporation of China (DJ-ZDXM-2014-34).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 Springer Nature Singapore Pte Ltd.
About this paper
Cite this paper
Zuo, Y., Wang, S.L., Huang, Y., Wang, S.X. (2018). Corrosion Resistance of Fe-Based Bulk Amorphous Alloy with Sulfide Inclusion. In: Han, Y. (eds) Advanced Functional Materials. CMC 2017. Springer, Singapore. https://doi.org/10.1007/978-981-13-0110-0_35
Download citation
DOI: https://doi.org/10.1007/978-981-13-0110-0_35
Published:
Publisher Name: Springer, Singapore
Print ISBN: 978-981-13-0109-4
Online ISBN: 978-981-13-0110-0
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)