Abstract
Extruded magnesium alloys with strong basal texture present tension and compression asymmetry. Dislocation slip dominates plastic deformation during tension along the extrusion direction (ED), whereas twinning is the main contributor to plastic strain when compressed along the ED. In this work, an extruded AZ31 Mg alloy was prestrained by tension along the ED to 5 and 10% of total strain, followed by compression, in order to investigate twin-slip interaction. The results show that the yield stress in compression only slightly increases with increasing prestrain. Notably, the hardening rate at the low stress stage during compression remains almost unchanged, compared to specimens without prestrain. Our results suggest that the contribution of twin-slip interaction to hardening is negligible in deformation of Mg alloys.
Access provided by CONRICYT-eBooks. Download conference paper PDF
Similar content being viewed by others
Keywords
Introduction
Deformation twinning and dislocation slip are two important modes during plastic deformation in hexagonal-close-packed (hcp) metals. Especially, the \( \left\{ {10\overline{1} 2} \right\}10\overline{1} \overline{1} \) twinning mode is the most prevalent twinning mode in hcp metals [1,2,3,4]. The favorable stress state for the \( \left\{ {10\overline{1} 2} \right\} \) extension twinning can be achieved by tension along c-axis or compression perpendicular to c-axis. In situ neutron diffraction [5,6,7,8], in situ X-ray diffraction [9] as well as acoustic emission [6, 10] studies on early stage of plastic deformation in Mg alloys reveal that \( \left\{ {10\overline{1} 2} \right\} \) extension twinning accounts for a major portion of the plastic deformation. Recent measurement of contribution of \( \left\{ {10\overline{1} 2} \right\} \) twinning to plastic strain in an extruded Mg alloy also indicated that ~90% of the plastic strain comes from \( \left\{ {10\overline{1} 2} \right\} \) twining during low stress stage deformation [11]. Extruded Mg alloys with strong basal texture exhibit tension-compression asymmetry. Yield stress and strain hardening behavior are largely dependent on the dominant mechanism of plastic deformation. During tension along the extrusion direction (ED), dislocation slip dominates plastic deformation. However, when compressed along the ED, \( \left\{ {10\overline{1} 2} \right\} \) twinning is the main contributor during early stage of plastic deformation in Mg alloys . Thus, the yield strength under ED compression is lower than that under ED tension. Also, the strain hardening rate is higher during ED tension compared with ED compression.
A number of researchers investigated the influence of prestrain on flow curve and work hardening behavior [12,13,14,15,16]. Slip-slip [17,18,19,20], twin-twin [21,22,23] and slip-twin interactions [24,25,26,27] during deformation were studied. The slip-slip interaction take place during plastic flow, especially when it is accomplished by dislocation glide on multiple slip systems. The interaction generally gives rise to a reduction in mobile dislocations, thus promoting work hardening [28]. The sub-grains resulted from twinning and twin-twin interaction also provide a strengthening mechanism, which is attributed to the dynamic Hall-Petch effect [29]. The twin-slip interaction is a more complex mechanism and still not well understood. Serra et al. [30] considered twin-dislocation interaction as an important hardening mechanism because twin boundaries hinder subsequent slip and twinning deformation. Proust et al. [31] proposed that during the preloading, <a> and <c+a> dislocations are introduced. These dislocations may act as barriers to twin nucleation or/and twin propagation. El Kadiri and Oppedal [32] developed dislocation transmutation theory, which hypothesizes that dislocations inside parent are incorporated and transmuted into immobile defects in twins, promoting latent hardening. Some researchers suggest when lattice dislocations meet with a twin boundary, dislocation dissociation will occur, which is also a mechanism for enlarging or shrinking the twin domain [33].
The current work aims to investigate twin-slip interaction by taking the advantage that slip and twinning dominated deformation can be activated separately by controlling the loading direction on extruded specimens. By pre-tension of extruded specimens to various levels of plastic strain, dislocations of different density are first introduced. Then the deformation is changed to compression such that twinning is activated. As such, twin-slip interaction and its contribution to strain hardening can be studied without ambiguity.
Experimental Method
An extruded, commercially obtained AZ31B Mg alloy was used for the current investigation. The circular extruded bar had a diameter of 38.1 mm. Dog-bone specimens were machined from the extruded bar with the gage section along the extrusion direction. The specimens had a gage length of 13.0 mm and gage diameter of 9.0 mm. An Instron load frame with a loading capacity of 25 kN was used to conduct the experiments. The specimens were carefully aligned to avoid triggering early buckling. Lubrication was applied between the moving surfaces. The extruded AZ31 Mg alloy was first prestrained by tension along the ED to 5 and 10% of total strain, respectively, followed by consecutive compression along the ED. The reason we did not pre-tensile the specimen to higher strain levels lies in that the fracture strain is approximately 12% for the material under tension. The mechanical experiments were conducted in strain-control mode at a strain rate of \( 8 \times 10^{ - 4} \) at ambient temperature.
For electron backscatter diffraction (EBSD) scans, cylindrical specimens with a thickness of 5 mm were sectioned in the middle of the gage section perpendicular to the ED. The specimens were ground mechanically down to 1200/4000 grit number on SiC sand papers, followed by electrochemical polishing with a solution of 5% nitric acid, 0.5% perchloric acid and 94.5% ethanol at 20 V for ~20 s. EBSD scans were conducted on a JEOL 7100F field emission scanning electron microscope (SEM) with an Oxford HKL Channel 5 instrument. An acceleration voltage of 20 kV and a working distance of 25 mm were used. For better statistics and analysis of the twinning behavior, at least three different regions were scanned by EBSD with a step size ranging from 0.5 to 1 µm for each companion specimen. All the EBSD scans were performed on a cross-section perpendicular to the ED or the loading axis.
Results and Discussion
The initial grain structure and the texture of the as-extruded specimens are shown in Fig. 1a, b, respectively. The as-received AZ31B presents a typical rod-texture in which the (0001) basal pole is nearly perpendicular to the ED, and the \( \left\{ {10\overline{1} 0} \right\} \) pole presents a strong intensity along the ED. Intensity peaks appear at ~4 and 10 o’clock positions in (0001) PF in Fig. 1b, which is likely due to the inhomogeneity in microstructure and the region for EBSD scan off the center of the extruded bar.
The stress-strain curves for 5% prestrain and 10% prestrain are displayed in Fig. 2. Firstly, we prestrained the specimens to 5% and 10% total strain in tension, then subjected the specimens to compression. The red dots denote strain levels at which the compression was interrupted and EBSD scans were performed on the specimens. The influence of prestrain on the compression behavior is shown in Fig. 3 which compares the stress-strain curves for 0% (i.e. monotonic compression), 5 and 10% prestrains.
Several important features can be noted in Fig. 3. First, the yield stresses in compression of the prestrained specimens are slightly higher than the specimen without prestrain . As the prestrain increases, the yield stress in compression slightly increases. In our most recent measurements of twin volume fraction at low stress stage compression of extruded AZ31 specimens [11], we observed that at plastic strain ~0.25%, deformation twinning has already been activated but with a low volume fraction. The main contributor to plastic strain is dislocation slip. But the twin volume fraction rapidly increases as the strain increases. During the low stress stage deformation, twinning accounts for 80–90% contribution to the plastic strain. Thus, the increase in yield stress in Fig. 3 can be attributed to the hardening effect of the pre-existing dislocations generated in prestraining.
Second and most interestingly, it can be observed that the hardening behavior during the low stress stage deformation remains almost identical. Figure 4 plots the hardening rate in the three scenarios. The difference between the zero-prestrain, 5% prestrain and 10% prestrain specimens is obvious. The prestrained specimens present slightly lower hardening rates if compared to the un-prestrained specimen. This raises a question as to what a role twin-slip interaction plays in the hardening. Twin-slip interaction has been considered as an important contributor to the increase in hardening rate during twinning and after twinning [13, 30, 34, 35]. Dynamic Hall-Petch effect [36,37,38] has been proposed as one of the mechanisms that contributes to strain hardening when twinning is activated along with dislocation slip. Twin boundaries act as new grain boundaries that reduce the effective grain size and the mean free path of dislocations. However, our experimental results indicate that the contribution of twin-slip interaction to the hardening is negligible.
The EBSD results in Fig. 5 show the evolution of extension twins of the specimens with and without prestrain . In the zero-prestrain specimen (Fig. 5a), which is under monotonic compression at low stress stage of plastic deformation in an extruded Mg alloy [11], \( \left\{ {10\overline{1} 2} \right\} \) twinning is activated at very early stage of plastic deformation, the density of twins increases rapidly with increasing strain. The specimen with 5% prestrain (Fig. 5b) presents a similar trend: as the plastic strain increases, the twin volume fraction increases. However, for the 10% prestrained specimen, substantial difference in twinning behavior upon subsequent tension was observed, that is, twin nucleation is retarded by the pre-introduced dislocations. It can be observed that at εp = 1.22% (Fig. 5c), twins with a very low density are activated. However, after nucleation, the twin volume fraction rapidly increases as does in the zero-prestrain and the 5% prestrain specimens. Mahajan [39] reported that prestraining of iron prior to shock-loading inhibits the formation of shock twins, there are a lot of mobile dislocations, fewer twins are required to accommodate plastic strain. Boucher and Christian [40] studied the influence of prestrain on deformation twinning in niobium single crystals, it is found that prestrain is effective in suppressing twinning at temperatures down to 77 K. These dislocations induced by prestrain may increase the energy barriers for twin nucleation. This would explain the increase of the stress corresponding to the onset of twinning with increasing prestrain . Since conventional EBSD is unable to resolve dislocation type and density, transmission electron microscopy (TEM) and computer simulations are needed to reveal how twinning interacts with slip in our future work.
Skrotzki [41] reported that in γ-TiAl, one part of the possible glide dislocations remains completely unaffected by the twin interface when these dislocations come across twin boundary. Zhu et al. [42] found that there is no energy change (barrier) when 90° partial pass the twin boundary by cross-slip in bcc metals. Hence, the twin boundary will not necessarily act barriers for dislocation slip. Recently, Li and Ma [43] showed that \( \left\{ {10\overline{1} 2} \right\} \) twinning in Mg alloy is actually mediated by atomic shuffling. A large deviation between the actual twin boundaries and the theoretical \( \left\{ {10\overline{1} 2} \right\} \) twinning plane was also observed [44]. More recently, Li and Zhang [45, 46] showed that the twinning shear of \( \left\{ {10\overline{1} 2} \right\}10\overline{1} \overline{1} \) mode can only be zero because the twinning plane is not an invariant plane and thus no shear deformation mediated by twinning dislocations can occur on the twinning plane. These new findings, along with our experimental observations, call for reconsideration of the nature of twin-slip interaction in Mg alloys and other HCP metals. Computer simulations may be needed to resolve the mechanisms.
Conclusion
By prestraining in tension of extruded AZ31B specimens, we investigated twin-slip interaction during plastic deformation. The results show that the yield stress in compression only slightly increases with increasing prestrain . However, the hardening rate at the low stress stage during compression remains almost unchanged, indicating that the contribution of twin-slip interaction to hardening is negligible in deformation of Mg alloys .
References
Christian JW, Mahajan S (1995) Deformation twinning. Prog Mater Sci 39:1–157.
Yoo MH, Lee JK (1991) Deformation twinning in hcp metals and alloys. Philos Mag A 63:987–1000.
Yoo MH (1981) Slip, twinning, and fracture in hexagonal close-packed metals. Metall Trans A 12:409–418.
Barnett MR (2007) Twinning and the ductility of magnesium alloys. Mater Sci Eng A 464:8–16. https://doi.org/10.1016/j.msea.2007.02.109.
Agnew SR, Brown DW, Tomé CN (2006) Validating a polycrystal model for the elastoplastic response of magnesium alloy AZ31 using in situ neutron diffraction. Acta Mater 54:4841–4852. https://doi.org/10.1016/j.actamat.2006.06.020.
Muránsky O, Barnett MR, Carr DG, et al (2010) Investigation of deformation twinning in a fine-grained and coarse-grained ZM20 Mg alloy: Combined in situ neutron diffraction and acoustic emission. Acta Mater 58:1503–1517. https://doi.org/10.1016/j.actamat.2009.10.057.
Muránsky O, Carr DG, Šittner P, Oliver EC (2009) In situ neutron diffraction investigation of deformation twinning and pseudoelastic-like behaviour of extruded AZ31 magnesium alloy. Int J Plast 25:1107–1127. https://doi.org/10.1016/j.ijplas.2008.08.002.
Agnew SR, Tomé CN, Brown DW, et al (2003) Study of slip mechanisms in a magnesium alloy by neutron diffraction and modeling. Scr Mater 48:1003–1008. https://doi.org/10.1016/S1359-6462(02)00591-2.
Lynch PA, Kunz M, Tamura N, Barnett MR (2014) Time and spatial resolution of slip and twinning in a grain embedded within a magnesium polycrystal. Acta Mater 78:203–212. https://doi.org/10.1016/j.actamat.2014.06.030.
Lou XY, Li M, Boger RK, et al (2007) Hardening evolution of AZ31B Mg sheet. Int J Plast 23:44–86. https://doi.org/10.1016/j.ijplas.2006.03.005.
Chen P, Li B, Culbertson D, Jiang Y, Contribution of extension twinning to plastic strain at low stress stage deformation of a Mg-3Al-1Zn alloy, Mater. Sci. Eng. A. 709 (2018) 40–45.
Zhao S, Guo E, Wang L, et al (2015) Effect of pre-compressive strain on microstructure and mechanical properties of Mg–2.7Nd–0.4Zn–0.5Zr alloy. Mater Sci Eng A 647:28–33. https://doi.org/10.1016/j.msea.2015.08.092.
Xin Y, Lv L, Chen H, et al (2016) Effect of dislocation-twin boundary interaction on deformation by twin boundary migration. Mater Sci Eng A 662:95–99. https://doi.org/10.1016/j.msea.2016.03.061.
Hama T, Nagao H, Kuchinomachi Y, Takuda H (2014) Effect of pre-strain on work-hardening behavior of magnesium alloy sheets upon cyclic loading. Mater Sci Eng A 591:69–77. https://doi.org/10.1016/j.msea.2013.10.083.
Hama T, Kariyazaki Y, Hosokawa N, et al (2012) Work-hardening behaviors of magnesium alloy sheet during in-plane cyclic loading. Mater Sci Eng A 551:209–217. https://doi.org/10.1016/j.msea.2012.05.009.
Zhang J, Xi G, Wan X, Fang C (2017) The dislocation-twin interaction and evolution of twin boundary in AZ31 Mg alloy. Acta Mater 133:208–216. https://doi.org/10.1016/j.actamat.2017.05.034.
Nogaret T, Curtin WA, Yasi JA, et al (2010) Atomistic study of edge and screw <c+a> dislocations in magnesium. Acta Mater 58:4332–4343. https://doi.org/10.1016/j.actamat.2010.04.022.
Li B, Zhang QW, Mathaudhu SN (2017) Basal-pyramidal dislocation lock in deformed magnesium. Scr Mater 134:37–41. https://doi.org/10.1016/j.scriptamat.2017.02.040.
Geng J, Chisholm MF, Mishra RK, Kumar KS (2014) The structure of <c+a> type dislocation loops in magnesium. Philos Mag Lett 94:377–386. https://doi.org/10.1080/09500839.2014.916423.
Lavrentev FF (1980) The type of dislocation interaction as the factor determining work hardening. Mater Sci Eng 46:191–208. https://doi.org/10.1016/0025-5416(80)90175-5.
Yu Q, Wang J, Jiang Y, et al (2014) Co-zone 1¯012 Twin Interaction in Magnesium Single Crystal. Mater Res Lett 2:82–88. https://doi.org/10.1080/21663831.2013.867291.
El Kadiri H, Kapil J, Oppedal AL, et al (2013) The effect of twin–twin interactions on the nucleation and propagation of {101¯2} twinning in magnesium. Acta Mater 61:3549–3563. https://doi.org/10.1016/j.actamat.2013.02.030.
Yu Q, Wang J, Jiang Y, et al (2014) Twin–twin interactions in magnesium. Acta Mater 77:28–42. https://doi.org/10.1016/j.actamat.2014.05.030.
Lv L, Xin Y, Yu H, et al (2015) The role of dislocations in strain hardening of an extension twinning predominant deformation. Mater Sci Eng A 636:389–395. https://doi.org/10.1016/j.msea.2015.04.007.
Zhou N, Zhang Z, Jin L, et al (2014) Ductility improvement by twinning and twin–slip interaction in a Mg-Y alloy. Mater Des 1980-2015 56:966–974. https://doi.org/10.1016/j.matdes.2013.12.014.
Cepeda-Jiménez CM, Molina-Aldareguia JM, Pérez-Prado MT (2015) Origin of the twinning to slip transition with grain size refinement, with decreasing strain rate and with increasing temperature in magnesium. Acta Mater 88:232–244. https://doi.org/10.1016/j.actamat.2015.01.032.
Ezaz T, Sangid MD, Sehitoglu H (2011) Energy barriers associated with slip–twin interactions. Philos Mag 91:1464–1488. https://doi.org/10.1080/14786435.2010.541166.
Madec R, Devincre B, Kubin L, et al (2003) The Role of Collinear Interaction in Dislocation-Induced Hardening. Science 301:1879–1882. https://doi.org/10.1126/science.1085477.
Kalidindi S r., Salem A a., Doherty R d. (2003) Role of Deformation Twinning on Strain Hardening in Cubic and Hexagonal Polycrystalline Metals. Adv Eng Mater 5:229–232. https://doi.org/10.1002/adem.200300320.
Serra A, Bacon DJ, Pond RC (2002) Twins as barriers to basal slip in hexagonal-close-packed metals. Metall Mater Trans A 33:809–812. https://doi.org/10.1007/s11661-002-0149-7.
Proust G, Tomé CN, Jain A, Agnew SR (2009) Modeling the effect of twinning and detwinning during strain-path changes of magnesium alloy AZ31. Int J Plast 25:861–880. https://doi.org/10.1016/j.ijplas.2008.05.005.
El Kadiri H, Oppedal AL (2010) A crystal plasticity theory for latent hardening by glide twinning through dislocation transmutation and twin accommodation effects. J Mech Phys Solids 58:613–624. https://doi.org/10.1016/j.jmps.2009.12.004.
El Kadiri H, Barrett CD, Wang J, Tomé CN (2015) Why are twins profuse in magnesium? Acta Mater 85:354–361. https://doi.org/10.1016/j.actamat.2014.11.033.
Wang F, Agnew SR (2016) Dislocation transmutation by tension twinning in magnesium alloy AZ31. Int J Plast 81:63–86. https://doi.org/10.1016/j.ijplas.2016.01.012.
Xu J, Guan B, Yu H, et al (2016) Effect of Twin Boundary–Dislocation–Solute Interaction on Detwinning in a Mg–3Al–1Zn Alloy. J Mater Sci Technol 32:1239–1244. https://doi.org/10.1016/j.jmst.2016.08.023.
Park SH, Hong S-G, Lee JH, Lee CS (2012) Multiple twinning modes in rolled Mg–3Al–1Zn alloy and their selection mechanism. Mater Sci Eng A 532:401–406. https://doi.org/10.1016/j.msea.2011.11.003.
Oppedal AL, El Kadiri H, Tomé CN, et al (2012) Effect of dislocation transmutation on modeling hardening mechanisms by twinning in magnesium. Int J Plast 30:41–61. https://doi.org/10.1016/j.ijplas.2011.09.002.
Ma Q, El Kadiri H, Oppedal AL, et al (2012) Twinning effects in a rod-textured AM30 Magnesium alloy. Int J Plast 29:60–76. https://doi.org/10.1016/j.ijplas.2011.08.001.
Mahajan S (1970) Effects of existing substructure on shock-twinning behaviour of iron. Phys Status Solidi A 2:217–223. https://doi.org/10.1002/pssa.19700020205.
Boucher NA, Christian JW (1972) The influence of pre-strain on deformation twinning in niobium single crystals. Acta Metall 20:581–591. https://doi.org/10.1016/0001-6160(72)90013-2.
Skrotzki B (2000) Crystallographic aspects of deformation twinning and consequences for plastic deformation processes in γ-TiAl. Acta Mater 48:851–862. https://doi.org/10.1016/S1359-6454(99)00385-7.
Zhu YT, Wu XL, Liao XZ, et al (2011) Dislocation–twin interactions in nanocrystalline fcc metals. Acta Mater 59:812–821. https://doi.org/10.1016/j.actamat.2010.10.028.
Li B, Ma E (2009) Atomic Shuffling Dominated Mechanism for Deformation Twinning in Magnesium. Phys Rev Lett 103:035503. https://doi.org/10.1103/PhysRevLett.103.035503.
Zhang XY, Li B, Wu XL, et al (2012) Twin boundaries showing very large deviations from the twinning plane. Scr Mater 67:862–865. https://doi.org/10.1016/j.scriptamat.2012.08.012.
Li B, Zhang XY (2014) Global strain generated by shuffling-dominated {101-2}<10-1-1>twinning. Scr Mater 71:45–48. https://doi.org/10.1016/j.scriptamat.2013.10.002.
Li B, Zhang XY (2016) Twinning with zero twinning shear. Scr Mater 125:73–79. https://doi.org/10.1016/j.scriptamat.2016.07.004.
Acknowledgements
Bin Li gratefully thanks support from the U.S. National Science Foundation (NSF) (CMMI-1635088). Yanyao Jiang acknowledges support from the NSF (CMMI-1462885).
Author information
Authors and Affiliations
Corresponding author
Editor information
Editors and Affiliations
Rights and permissions
Copyright information
© 2018 The Minerals, Metals & Materials Society
About this paper
Cite this paper
Chen, P., Li, B., Culbertson, D., Jiang, Y. (2018). Twin-Slip Interaction at Low Stress Stage Deformation in an AZ31 Mg Alloy. In: Orlov, D., Joshi, V., Solanki, K., Neelameggham, N. (eds) Magnesium Technology 2018. TMS 2018. The Minerals, Metals & Materials Series. Springer, Cham. https://doi.org/10.1007/978-3-319-72332-7_30
Download citation
DOI: https://doi.org/10.1007/978-3-319-72332-7_30
Published:
Publisher Name: Springer, Cham
Print ISBN: 978-3-319-72331-0
Online ISBN: 978-3-319-72332-7
eBook Packages: Chemistry and Materials ScienceChemistry and Material Science (R0)