Abstract
Electrospinning provides an effective method for generating nanofibers from solution of carboxymethyl chitosan/polyoxyethylene oxide (CMCS/PEO). The goal of this work is to explore the potential application of electrospun CMCS/PEO nanofiber membrane in fruit fresh-keeping. The microstructure, antibacterial activity, hydrophilia, and air permeability of the nanofiber membrane have been tested. For comparison, the fresh-keeping effects of commercial cling wrap and CMCS/PEO nanofiber membranes on strawberries’ rotting rate and weight loss rate have been studied. The results indicate that the electrospun CMCS/PEO membrane could effectively avoid water loss in strawberries and has a remarkable effect to prolong strawberries’ shelf life due to its breathability and antibacterial activity. In addition, the composite CMCS/PEO, nanofiber membrane is non-poisonous and edible, which can be used in food industry.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
The development of food protecting films and coatings were turned from physical or mechanical treatments to chemical protection. People focus on biological materials which most possess edibility such as proteins, lipids, and polysaccharide instead of traditional protective film like plastic, papers and paraffin [1, 2]. With the growing awareness of environmental protection, edible coatings and films can be extensively used in food especially for fruits and vegetables which need highly effective maintained freshness. Simple coating even a thin layer of membrane with some specific features may achieve better effects [3]. Chitosan is an excellent natural fit in food due to its biodegradability, biocompatibility, antimicrobial activity, non-toxicity, versatile chemical, and physical properties [4, 5], and with its unique antibacterial property, rot resistance, and film-forming property, it has been widely used in medicine, textile and food [6,7,8,9]. Particularly, chitosan can be derived from the raw materials of silkworm, shrimp, and crab shells, which are widely and abundantly distributed in nature [10].
Electrospinning, which continuously fabricates soft nanofibrous membranes [11, 12], can offer gentle protection to fruits. This may help to solve the storage and transportation problems of some fruits such as strawberry, cherry tomatoes, and kumquat. With a layer of soft nanofibers, the surface of the fruit can be protected from the outside invasion, like the introduction of bacteria and scratches. In several studies, concentrated acetic acid solution was used as a solvent for electrospinning chitosan nanofibers, and carboxymethyl chitosan (CMCS) electrospun nanofibers were prepared using deionized water as a solvent [13,14,15]. Water soluble polyoxyethylene oxide (PEO) also added into CMCS solution as an adjuvant to optimization the electrospinning process [16], which is recognized as a non-toxic polymer [17,18,19].
Recently, a strategy about fruit fresh-keeping based on chitosan was reported by painting chitosan solution onto the fruit surface to form a wet film, but there existed a few methods to assess fibrous membranes based on electrospinning [20,21,22]. However, the wet coating film provides contact between the fruit skin and moisture in the air, thus providing an opportunity for bacteria growth and moisture loss. In addition, this coating method requires drying throughout the whole process, which further causes potential damage to the fruit. In this work, we utilize a new type of hand-held electrospinning device for preparation of non-toxic and edible CMCS/PEO nanofiber film (Fig. 1) [5, 23]. The purpose of this research is to evaluate the potential application of chitosan nanofiber films in fruit fresh-keeping and to improve the quality of traditional coatings and extend the shelf life of strawberries.
Methods/Experimental
Materials
Organically grown table strawberries were harvested in Laoshan District (Qingdao, China) and took to laboratory as soon as possible; residuals were removed before coating. The strawberries selected are those without mechanical hazard scratches and with similar size, shape, and maturity. CMCS (Mw 80,000 ~ 250,000) with 95% N-deacetylation was purchased from Aoduofuni (Nanjing, China). PEO (Mw ~ 5,000,000) was purchased from Aladdin.
Preparation of Spinning Solution
Table 1 shows the details of different ratios of the mixed solutions containing CMCS, PEO, and deionized water. Briefly, 3.0 g of CMCS was mixed with 0.16 g, 0.20 g, and 0.25 g PEO, respectively. Then, they were put into 40.0 g deionized water in a bottle of 100 ml. A magnetic stirring was applied for about 4 h at room temperature until the solutions became transparent and homogeneous.
Preparation of Nanofiber Membranes
The composite fiber membranes were prepared as follows: 40% relative humidity, syringe needle-to-collector distance of 20 cm, and applied spinning voltage of 20 kV. In this work, a hand-held electrospinning device designed by Qingdao Junada Technology Co. Ltd. was used to prepare CMCS/PEO nanofiber membranes. Figure 1 shows the schematic diagram of the preparation technique and the process of electrospinning.
Characterization of e-spun Membranes
The morphologies and diameters of nanofibers were characterized by a scanning electron microscopy (SEM; Phenom Pro). The polymer intermolecular structure was determined by a Fourier transform infrared (FTIR) spectrometer (Nicolet iN10; Thermo Fisher Scientific, Waltham). The breathability was measured by a gas transmission rate tester (FX 3300; Zurich).
Preparation of Preservation Process
The strawberries were divided into four groups randomly. Every group had six strawberries in culture dish. The first group was completely exposed to the atmosphere as a blank control group. The second group was wrapped with ordinary household polyethylene plastic film. The third group was painted with the electrospinning solution (PEO: CMCS = 1:20) to form a protective layer with glaze surface outer. In this group, the sample was carefully dried to form a protective film. In addition, electrospun CMCS/PEO nanofiber membrane was used to cover the last group. Finally, these groups were placed at room temperature without sunlight, observed, and recorded at the same time each day. Figure 2 is a schematic diagram of strawberry preservation.
Results and Discussion
Morphological Analysis
Although pure CMCS solution has high viscosity which can reach up to 400–800 mPa ∙ s, it is still difficult to form fibers by electrostatic fields. The obstacle originates from the molecular structure and solubility of chitin and chitosan, especially for CMCS. For this reason, the fiber forming facilitating polyol binder such as PEO was added into CMCS solution. Under the applied voltage, clear Taylor cone was observed for the CMCS/PEO solutions in the concentration range of 2.5–7.5 wt% (Fig. 1). Figure 3 shows the SEM images and fiber diameter distribution of the composite CMCS/PEO fibers with different ratios. These composite fibers have a cylindrical morphology with fiber diameters about 130–400 nm.
When a smaller amount of PEO was mixed with CMCS, as presented in Fig. 3a (PEO: CMCS = 1:24), the fibers were thinner and inhomogeneous with diameter of 130–280 nm. For solution with PEO: CMCS = 1:18, the average fiber diameter was about 210 nm, and some conglutination between the relatively coarse fibers was observed in Fig. 3b. As the ratio of the PEO increased (PEO: CMCS = 1:12), fairly homogeneous fibers with an average diameter of 290 nm were obtained (Fig. 3c). The nanofiber membrane with ratio of 1:12 of PEO/CMCS was selected as the packaging film, because the solution of 1:12 of PEO/CMCS has a more suitable viscosity for electrospinning and it is easier to form a complete nanofibrous film to cover the fruit, and the electrospun film has a more even breathing intensity due to the uniform size micropores according with the SEM images.
Infrared Spectroscopy
Figure 4 shows the FTIR spectra of electrospun CMCS powder and CMCS/PEO composite nanofibers. The frequencies and assignments for the pristine CMCS are indicated as follows: the peaks at 1320 cm−1, 1137 cm−1, and 1050 cm− 1 were from C–H bending vibration, glycosidic bond C–O–C, and C–O stretching vibration of CMCS, respectively. In the spectra, new peaks at 1603 cm−1 characteristic of carboxylic acid salt (–COO– asymmetrical and symmetrical stretch) appeared, while a shoulder peak around 1650 cm−1 indicative of the amino group. Though some difference in the two figures were observed, both of them showed the basic characteristic peaks for CMCS at 3423 cm−1 (O–H stretch) and 2960–2970 cm−1 (C–H stretch). We can see that the FTIR spectra had no change by an addition of the PEO, which indicated that there was no obvious change of structure between CMCS powder and CMCS/PEO.
Air Permeability Test
Many studies have found that permeability is an important factor for preserving fruits. The microporous membrane can promote the exchange of gas inside and outside the package, regulate the concentration of O2 and CO2, and make the packaged fruits and vegetables have a good storage environment, thus ensuring its quality or being less affected [24]. The certain permeability of the plastic wrap can maintain the appropriate concentration CO2 in the confined space. The formation of storage atmosphere can inhibit the respiration of vegetables and extend the shelf life. Provided that breathability is too high, it is easy to make the package oxygen content too high, accelerating breathing of fruits, aging faster, browning, and fading serious [25]. Similarly, poor air permeability or poor air tightness can lead to fruit anaerobic production of alcohol, which ultimately exacerbates fruit rot. [26]. Obviously, the permeability of nanofiber membranes decreases with increasing film thickness. In this experiment, PEO/CMCS composite nanofiber membrane with the ratio of 1: 12 and plastic film were selected for the permeability test. The basic test principle of the device used here is as below (Fig. 5a). Difference in gas pressure at both ends of a circular tube is controlled, 200 Pa in this case. Then measure the air flow rate at the air outlet, so that the greater the air resistance, the lower the air velocity. In the same situation, the measuring result of plastic wrap was 0 mm s−1. According to the literature, we know that the air permeability of nylon and other fabrics is between 100 and 300 mm s−1 in average [27]. In the measurement of 200 Pa and 20 cm2, the measured value of PEO/CMCS composite nanofiber evenly distributed in the 40–50 mm s−1 (Fig. 5), indicating that the CMCS/PEO composite membrane had uniform air permeability. In this test, the average film thickness was 0.108 mm. Generally speaking, this breathability is suitable for using as a packaging material with preservation function.
Antibacterial Test
Presently, many studies have been focused on the antibacterial property of chitosan, but less on the antibacterial property of CMCS. Chitosan has a significant inhibitory effect on many bacteria and fungi, such as Escherichia coli and Staphylococcus aureus, both of which are the culprits of fruit spoilage [28]. According to investigation, although the antibacterial ability of CMCS is not in direct proportion with its concentration, CMCS showed the strongest ability of antibacterial at the appropriate concentration [29]. It is particularly pointed out that amino of CMCS could inhibit the bacteria after the CMCS was dissolved in the solution by combining the anion [30, 31]. From the viewpoint of bacteriostasis, electrospun CMCS nanofibers are suitable as antimicrobial food packaging material, even if their water solubility limited the application range. As shown in Fig. 6, we performed antibacterial experiments on filter paper and CMCS fiber membranes using Escherichia coli and Staphylococcus aureus, respectively. The results showed that CMCS/PEO nanofiber membrane had obvious inhibitory effect on these two kinds of bacteria and formed a broad antibacterial ring after 18 h of training. However, the two control groups did not have any bacteriostatic effect in (a) and (b). It is noted that the bacteriostatic rings were not uniform in Fig. 6c, d due to the water solubility and fluidity of CMCS.
Weight Loss Percentage
The weight-loss ratio could be calculated from the following formula:
Weight loss (%) \( =\frac{M_0-M}{M_0}\times 100\% \),
where M0 is the fresh weight of the strawberries (strawberries are stored for 0 day), and M is the weight of samples stored for different days.
Weights of different treatment groups were measured at different storage times. As shown in Fig. 7, the blank control group experienced an acceleration of weight loss, which can be attributed to an increase in the fruit’s metabolic activity. Compared with the blank control group, the fruit treated with wrapping by plastic film has quite low weight loss on account of the compactness the plastic film. Apparently, we focused on the group of the CMCS/PEO coating film that the weight loss is more severe. In this case, despite the forming of the CMCS/PEO layer, it leads to physical and direct contact between moisture and fruit surface. With contact of the both, moisture destroyed the outermost natural protection layer of fruits, which in turn resulted in the acceleration in the inside water loss rate. For the group covered by electrospun CMCS/PEO nanofiber film, it showed the fairly good water retention compared with the blank control group and it did not have many effects of the film that the raw materials are hydro soluble.
Fruit Fresh-Keeping Test
With regard to fruit fresh-keeping, sensory properties are clearly a significant characteristic as an evaluation criterion. The initial (day 0) sensory properties (color, odor and texture) of these four samples are presented as consistency to the same extent (Fig. 8a). As can be seen from the Fig. 8, throughout storage, colors were dimmed in various degrees in all treatments. The initial full and glossy appearance of the blank control group had largely disappeared, and 70% of the fruit had begun to rot, on account of strawberries that are thinly peeled and rich in juice, being extremely mechanical vulnerable, especially for water loss. The applied example shows that volume had been obviously shrunk to some extent, with quality decrease from 19.59 to 11.10 g for an average of control (Fig. 8b). PE wrapper had some implications in the management of prevention and control of dehydration. In Fig. 8c, strawberries had wilted for a few, with the color became darkened, and mildew appeared on the part of the individual. It is noted that the group of CMCS/PEO paint coatings is mainly darkening and browning (Fig. 8d). Browning is mainly due to the oxidative degradation of ascorbic acid. As mentioned above, the group of those decorated with paint coatings had destroyed skin and the covering layers of the fruits look in bad condition such as the skin was not smooth and severe shrinkage, but without any rot. The results showed that the electrospun CMCS/PEO nanofiber film was effective in preventing diseases and rot and improving the appearance of fruit in the storage in the Fig. 8e. Just like other groups, the strawberries in this group also had a little shrinkage and an aromatic flavor. The causes of off-flavor, in general, can be related to the microbial proliferation and sugar accumulation.
Conclusions
In summary, we developed a non-poisonous and edible CMCS/PEO nanofiber membrane that not only showed the excellent antimicrobial property but also had admirable air permeability by the hand-held electrospinning device. The CMCS/PEO nanofiber membrane exhibited antibacterial capability to both Escherichia coli and Staphylococcus aureus. The measured gas permeability was on a scale of 40–50 mm s−1 in the 200 Pa. These results indicate that the CMCS/PEO nanofiber membrane may be suitable as packing materials for fruit. Compared with typical conventional coatings, the nanofiber film may have potential applicability. This environmentally friendly technology may provide an alternative approach to the fruit in growing, transporting, and selling.
Abbreviations
- CMCS:
-
Carboxymethyl chitosan
- FTIR:
-
Fourier transform infrared
- PEO:
-
Polyoxyethylene oxide
- SEM:
-
Scanning electron microscopy
References
Diab T, Biliaderis CG, Gerasopoulos D (2001) Physicochemical properties and application of pullulan edible films and coatings in fruit preservation. J Sci Food Agric 81:988–1000
Muschiolik G (1995) Edible coatings and films to improve food quality. In: Herausgegeben von JM, Krochta EA, Baldwin und MO (eds) Molecular Nutrition and Food Research. Trends in Food Science & Technology, Lancester, pp 335–335
Mohammed FA, Balaji K, Girilal M (2009) Mycobased synthesis of silver nanoparticles and their incorporation into sodium alginate films for vegetable and fruit preservation. J Agric Food Chem 57:6246–6252
Dutta PK, Tripathi S, Mehrotra GK (2009) Perspectives for chitosan based antimicrobial films in food applications. Food Chem 114:1173–1182
Kumar MNVR (2000) A review of chitin and chitosan applications. React Funct Polym 46:1–27
Cabañas A, Poliakoff M (2001) The continuous hydrothermal synthesis of nano-particulate ferrites in near critical and supercritical water. J Mater Chem 11:1408–1416
Greiner A, Wendorff JH (2007) Electrospinning: a fascinating method for the preparation of ultrathin fibers. Cheminform 46:670–703
Han JH (2001) 4–Antimicrobial food packaging. Novel Food Packag Tech 2003:50–70
Hulteen JC, Martin CR (1997) A general template-based method for the preparation of nanomaterials. J Mater Chem 7:1075–1087
Rinaudo M (2007) Chitin and chitosan: properties and applications. Cheminform 38:603–632
Huang ZM, Zhang YZ, Kotaki M (2003) A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos Sci Technol 63:2223–2253
Li D, Xia Y (2010) Electrospinning of nanofibers: reinventing the wheel? Adv Mater 16:1151–1170
Duan B, Dong C, Yuan X (2004) Electrospinning of chitosan solutions in acetic acid with poly(ethylene oxide). J Biomater Sci Polym Ed 15:797–811
Elsabee MZ, Naguib HF, Morsi RE (2012) Chitosan based nanofibers, review. Mater Sci Eng C 32:1711–1726
Homayoni H, Ravandi SAH, Valizadeh M (2009) Electrospinning of chitosan nanofibers: processing optimization. Carbohydr Polym 77:656–661
Jin HJ, Fridrikh SV, Rutledge GC (2002) Electrospinning Bombyx mori silk with poly(ethylene oxide). Biomacromolecules 3:1233
Han J, Zhang J, Yin R (2011) Electrospinning of methoxy poly(ethylene glycol)-grafted chitosan and poly(ethylene oxide) blend aqueous solution. Carbohydr Polym 83:270–276
Ignatova M, Manolova N, Rashkov I (2007) Electrospinning of poly(vinyl pyrrolidone)–iodine complex and poly(ethylene oxide)/poly(vinyl pyrrolidone)–iodine complex – a prospective route to antimicrobial wound dressing materials. Eur Polym J 43:1609–1623
Lu JW, Zhu YL, Guo ZX (2009) Electrospinning of sodium alginate with poly(ethylene oxide). Polymer 47:8026–8031
Chien PJ, Sheu F, Lin HR (2007) Coating citrus (Murcott tangor) fruit with low molecular weight chitosan increases postharvest quality and shelf life. Food Chem 100:1160–1164
Sánchez-González L, Pastor C, Vargas M (2011) Effect of hydroxypropylmethylcellulose and chitosan coatings with and without bergamot essential oil on quality and safety of cold-stored grapes. Postharvest Biol Technol 60:57–63
Treviño-Garza MZ, García S, Arévalo-Niño K (2015) Edible active coatings based on pectin, pullulan, and chitosan increase quality and shelf life of strawberries (Fragaria ananassa). J Food Sci 80:M1823–M1830
Liu LS, Jin T, Liu CK (2008) A preliminary study on antimicrobial edible films from pectin and other food hydrocolloids by extrusion method. J Nat Fibers 5:366–382
Exama A, Arul J, Lencki RW (1993) Suitability of plastic films for modified atmosphere packaging of fruits and vegetables. J Food Sci 58:1365–1370
Beaudry RM (1999) Effect of O2, and CO2, partial pressure on selected phenomena affecting fruit and vegetable quality. Postharvest Biol Technol 15:293–303
Pesis E, Dvir O, Feygenberg O (2002) Production of acetaldehyde and ethanol during maturation and modified atmosphere storage of litchi fruit. Postharvest Biol Technol 26:157–165
Leroux F, Perwuelz A, Campagne C (2006) Atmospheric air-plasma treatments of polyester textile structures. J Adhes Sci Technol 20:939–957
Jeon YJ, Park PJ, Kim SK (2001) Antimicrobial effect of chitooligosaccharides produced by bioreactor. Carbohydr Polym 44:71–76
Hong KN, Na YP, Lee SH (2002) Antibacterial activity of chitosans and chitosan oligomers with different molecular weights. Int J Food Microbiol 74:65–72
Sabaa MW, Mohamed NA, Mohamed RR (2010) Synthesis, characterization and antimicrobial activity of poly (-vinyl imidazole) grafted carboxymethyl chitosan. Carbohydr Polym 79:998–1005
Sun L, Du Y, Fan L (2006) Preparation, characterization and antimicrobial activity of quaternized carboxymethyl chitosan and application as pulp-cap. Polymer 47:1796–1804
Funding
This work was supported by the National Natural Science Foundation of China (51673103), the Key Research and Development Plan of Shandong Province, China (2016GGX102011), and the Postdoctoral Scientific Research Foundation of Qingdao (2016014).
Availability of Data and Materials
The datasets generated during and/or analyzed during the current study are available from the corresponding authors on reasonable request.
Author information
Authors and Affiliations
Contributions
YZL developed the concept and designed the experiments. TTY, XL, and XXW performed the experiments. TTY, XY, XXW, MY, JWM, YZ, and SR contributed to data analysis and discussion. All authors wrote and revised the paper. All authors read and approved the final manuscript.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Yue, TT., Li, X., Wang, XX. et al. Electrospinning of Carboxymethyl Chitosan/Polyoxyethylene Oxide Nanofibers for Fruit Fresh-Keeping. Nanoscale Res Lett 13, 239 (2018). https://doi.org/10.1186/s11671-018-2642-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-018-2642-y