Abstract
The present study is devoted to the problem of enhancing fracture toughness of ZrO2 ceramic materials through the formation of composite structure by addition of Al2O3 and NiO particles. In this paper, we analyzed the general and distinguished features of microstructure of both composite materials and its effect on fracture toughness of materials. In this paper, we used the XRD, SEM, and EDS methods for determination of granulometric, phase, and chemical composition of sintered materials. The peculiarities of dependence of fracture toughness values from dopant concentration and changing the Y3+ amount in zirconia grains allow us to assume that at least two mechanisms can affect the fracture toughness of ZrO2 ceramics. Crack bridging/deflection processes with the “transformation toughening” affect the K1C values depending on the dopant concentration. Crack deflection mechanism affects the K1C values when the dopant concentrations are low, and transformation toughening affects the K1C values when the dopant concentrations begin to have an impact on microstructure reorganization–redistribution of Y3+ ions and formation of Y3+-depleted grains with high ability to phase transformation.
Avoid common mistakes on your manuscript.
Background
Technical progress every year presents new and more stringent performance requirements for materials and devices. The lifetime and reliability of the devices should be increased, and the wear and fracture should be decreased significantly. This is especially true for durable ceramic products, operating in aggressive environments and at high temperatures, when the fracture of article can be initiated by small damage (pore, scratch, defects). This leads to formation of a new trend in material design—the production of materials tolerant to the defects. So, the structure of material, in our case ceramic material, must withstand external shocks. For example, these are self-healing materials [1, 2]. The corrosion resistance of silicon nitride ceramics can be increased by modifying its secondary phase. The formation of insoluble oxide layers will strongly reduce damage caused by subcritical crack growth. Creation of ceramic matrix composite (CMC) and metal matrix composite (MMC) materials also is the way of formation of the special microstructures in materials with enhanced properties. So, the development of new methods of formation of predetermined structure of ceramic material may improve the reliability of ceramic materials.
As it is known, the damage mechanisms depend on the structure and the type of the materials. Also, it is known that the hard materials tend to be brittle and materials with lower strength tend to be tougher. The damage process is associated with initiation and propagation of cracks in the material. As it was shown by Ritchie “the intrinsic damage processes that operate ahead of the tip of a crack to promote its propagation, and extrinsic crack-tip-shielding mechanisms that act mostly behind the crack tip to inhibit this propagation” [3]. Intrinsic toughening is the source of fracture resistance in ductile materials. This mechanism is effective against the initiation and propagation of cracks. Most metallic materials are toughened by this mechanism. Usually, brittle materials, such as ceramics, cannot be toughened by plastic deformation and have low values of fracture toughness. Typically, fracture toughness values for Al2O3, SiC, and Si3N4 are less than 3–4 MPa*m1/2. The extrinsic mechanisms, which are inherent to ceramic materials, are only effective in resisting crack propagation; they can have no effect on crack initiation. The basic variants of extrinsic toughening mechanisms are crack or fiber bridging and crack deflection.
Ceramic materials on the basis of zirconia are distinguished from other ceramic materials by the highest fracture toughness value because they demonstrate the well-known “transformation toughening effect,” which took part in the field of stresses caused by the propagation of cracks in sintered materials [4, 5]. The martensitic phase transformation (with increasing specific volume of transformed grains), which takes part in zirconia ceramic, is the manifestation of extrinsic toughening mechanism [6], but it happen ahead of the crack tip. So, zirconia-based materials have three variants of increasing the fracture toughness value—by transformation toughening, crack bridging, and crack deflection processes. Perhaps, the synergetic effects may be realized in the special composite structure.
There are many studies devoted to the formation of composite structures on the basis of zirconia. Zirconia–alumina (ZrO2–Al2O3) composites have been the subject of extensive research because they couple a high toughness with the desirable properties of alumina, i.e., good resistance to wear and chemical stability [7, 8]. Also, it has been reported that the addition of Al2O3 in a ZrO2 matrix can suppress the low-temperature degradation of mechanical properties of zirconia [9]. The addition of Al2O3, besides their low solubility in ZrO2, practically did not affect the phase stabilization, i.e., zirconia and alumina exist as separate phases [7, 10, 11]. But, our investigations [12] show that method of composite powder preparation has strong effect on fracture toughness value of material. It was shown that the increasing of K1C value of zirconia ceramics with a small amount of alumina, sintered from nanopowders and obtained using co-precipitation technique, can be conditioned through a series of processes for composite structure formation during precipitation, crystallization, and sintering of composite nanopowders.
A small number of studies have been devoted to the influence of Ni and NiO particles on the fracture toughness of monolithic 3Y-TZP ceramic materials [13, 14]. Another widely known system on the basis of zirconia is 8YZrO2-Ni(NiO) system for SOFC anode [15]. The triple junction between zirconia and Ni particles ensues the high level of catalytic properties of porous ZrO2-Ni(NiO) composite material. As engineering material, the composite Al2O3–Ni is more studied. In the studies [16, 17], it was shown that addition of nickel inclusions in alumina and zirconia matrix leads to increase in the fracture toughness of alumina or zirconia ceramic material. In this work, it has found two facts which addition of NiO during sintering promotes to (i) stabilization of a cubic phase of zirconia and (ii) destabilization of tetragonal phase and a formation of monoclinic phase. The formation of monoclinic phase even at small quantities of NiO (0.3–2 wt%) leads to sample destruction. In our previous study [18], it was found that the phase transformation from tetragonal to monoclinic phase in 3Y-TZP-NiO composite occurs only during sintering in air environment, and during sintering in argon environment, there are no traces of monoclinic phase, but the fracture toughness value increased by 40–50% [19]. The increasing amount of cubic phase of zirconia was also found. Probably in these two cases [12, 19], we can see the synergetic effect—increasing transformability of zirconia T-phase, and crack deflection/bridging caused by appearing of zone of tensile or compressive stresses near the inclusions. In turn, inclusions are realized during creation and decomposition of solid solutions under sintering process, but the physical properties (coefficient of thermal expansion, Young’s modulus, etc.) of chosen dopants (Al2O3 and NiO) are quite different. In this study, we try to separate the influence of residual stresses and transformability of tetragonal phase on fracture toughness of zirconia-based composites. These effects cannot be realized without changes in microstructure and chemical and phase composition of matrix phase.
In this work, we try to analyze and summarize the facts of influence of the Al2O3 and NiO additions on the structure formation of structure of zirconia ceramic materials and linked these structure peculiarities with the fracture mechanisms of zirconia ceramics.
Methods
Material Synthesis
The matrix ZrO2-3 mol% Y2O3 nanopowders (3Y-ZrO2) and composite ZrO2-3 mol% Y2O3-Al2O3 (3Y-ZrO2–Al2O3) nanopowders were synthesized by a co-precipitation technique using ZrOCl2·nH2O and AlCl3·6H2O salts. Based on previous investigations [12], the amount of Al2O3 was 2 wt%. For understanding the trends of the other composition, the amounts of 0.5 and 1 wt% have been used if needed. All chemicals used were of chemical purity (SiO2 <0.008 wt%, Fe2O3 <0.01 wt%, Na2O <0.01 wt%). At first, the appropriate amounts of Y2O3 were dissolved in nitric acid; then, the zirconium and yttrium salts (in case of matrix material) and zirconium, aluminum, and yttrium salts (in case of composite material) were mixed with a propeller stirrer for 30 min and were subsequently added to an aqueous solution of the precipitant (25% NH4OH) with constant stirring. Sediments were mixed for 1 h at room temperature at a pH of 9. Sediments were then repeatedly washed and filtered with distilled water. Washing was carried out until a negative test for C1− ions is obtained with the use of a silver nitrate solution. After washing and filtration, the hydrogel was dried in a microwave furnace with an output power of 700 W and at a frequency of 2.45 GHz. The calcination of dried zirconium hydroxides and composites was carried out in resistive furnaces at 700 °C with dwelling time 2 h. Because the nickel hydroxide is soluble in ammonia salts, the preparation of the nanocomposite ZrO2-3 mol% Y2O3-NiO (3Y-ZrO2-NiO) powders was conducted by mixing appropriate amounts of zirconia and nickel oxalate powders in distilled water using ultrasound at a frequency of 22 kHz. NiO in the composite nanopowders were obtained by the calcination of powders at 600 °C [fedor]. Based on the previous investigations [19], the amount of nickel oxide was 10 wt%, but for understanding the trends of the other composition, the amounts from 1 to 7.5 wt% have been used if needed.
Cylindrical (20-mm diameter and 3 mm in height) and rectangular (45 × 4 × 4 mm) specimens were prepared firstly by uniaxial cold pressing, then by isostatic pressing at 200 MPa, and finally by pressureless sintering at 1500 °C for 1 h in air atmosphere in case of ZrO2-3 mol% Y2O3 and ZrO2-3 mol% Y2O3 + Al2O3 and in argon atmosphere in case of ZrO2-3 mol% Y2O3-NiO. The sintering of ZrO2-3 mol% Y2O3-NiO composites was performed in argon atmosphere because the total sample destruction took place in case of sintering in air. The specimens used for mechanical testing were ground with a 180-grit diamond wheel and were subsequently polished with diamond slurries to minimize machining flaws.
Material Characterization
The powders and sintered specimens were characterized by XRD (Dron-3) with Cu-Kα radiation for crystallite sizes and quantitative phase analyses by a proven method [20]. For identifying of the monoclinic (M), tetragonal (T), and cubic (C) phases of zirconia, as well as Ni, NiO, and Al2O3, the angular regions of 25°–45° and 71°–77° were used. Particle sizes of different calcined powders were estimated by transmission electron microscopy (TEM) (JEM 200, Jeol, Japan). Reliable data were obtained by analyzing data from 30 TEM fields.
The flexural strength was measured using a four-point bending test on polished samples with a cross-head speed of 0.5 mm/min (Tinius Olsen H50kT, USA). The inner and outer spans were 20 and 40 mm, respectively. The hardness and fracture toughness of the materials was measured at room temperature by the Vickers indentation technique (Vickers tester TP-7p-1) on mirror-polished surfaces with a 98- and 196-N load, respectively. At 196-N loads, the Palmquist type cracks were propagated in 3Y-TZP and composited with alumina. The fracture toughness values were calculated by Niihara equation for Palmquist type cracks [21]. The density was measured using the Archimedes method. The microstructures of the ceramics were studied by scanning electron microscopy (JSM 6490LV Jeol) of thermally etched surfaces at 1450 °C polished surfaces as well as fractured surfaces.
Results and Discussion
Powder Characterization
According to the electron microscopy and XRD data, the average particle size of matrix 3Y-TZP nanopowders was 17.5 nm. The mean particle size of ZrO2-3 mol% Y2O3-Al2O3 nanopowders, obtained by co-precipitation, decreased from 17.5 to 14.4 nm with increasing concentrations of Al2O3 from 0 to 2 wt%. After the calcination of the ZrO2-3 mol% Y2O3 + NiC2O4 nanopowder mix at 600 °C, nickel oxide was formed with an average particle size of 40 nm. All powders are represented in Fig. 1. Zirconia in powders was represented by the tetragonal phase (P4m2), and NiO was represented by the cubic phase (Fm3m). The absence of (101) Al2O3 peak at 43.36° in synthesized nanopowders and its appearance in the sintered material was discussed early [12].
In the case of ZrO2-3 mol% Y2O3-Al2O3 nanopowder, incorporation of Al3+ cations into the ZrO2 particles limited its crystallization [22] and consequently decreased the particle size of zirconia-alumina composite powders during calcination. According to ultrasonic mixing technology, the NiO NPs in zirconia matrix nanopowder can be distinguished by TEM (Fig. 1c) but not Al2O3 NPs (Fig. 1b).
Characterization of Structure of Sintered Ceramic Materials
After sintering at 1500 °C in air environment, the phase composition of zirconia in 3Y-ZrO2 matrix material and in 3Y-ZrO2-Al2O3 composites did not change according to XRD results. The phase composition was 9–11% in the cubic phase, with the remaining composition in the tetragonal phase. These structure parameters are typical for such chemical composition and sintering conditions. The SEM analysis of fracture surfaces of the samples has no differences in grain size of 3Y-ZrO2 matrix material and 3Y-ZrO2-Al2O3 composites, besides the character of fracture. In the case of 3Y-ZrO2 matrix material, the intercrystalline type of fracture was observed and in the case of 3Y-ZrO2-Al2O3 composites the transcrystalline one (Fig. 2). These peculiarities were studied in our previous work [12] and will be not discussed here.
The average grain sizes with tetragonal and cubic phases in 3Y-ZrO2 matrix material by SEM data were 0.2–0.4 and 1–2 μm, respectively. In the case of 3Y-ZrO2-Al2O3 composite, the average grain sizes with tetragonal and cubic phases were 0.2–0.4 and 1– μm, respectively. But, the SEM analysis of thermally etched surfaces shows the macroscopic difference in the structure of zirconia grains between matrix material and composite (Fig. 3). Shown in Fig. 3b is the increasing number of “big” grains, which traditionally corresponds to the cubic phase of zirconia. The EDS analysis shows the increasing amount of Y3+ ions in the big grains, up to 8–10 wt% (4.5–5.5 mol%). This value is approaching the concentration of Y3+ ions, which corresponds to the chemical composition of cubic phase of ZrO2 (7–8 mol%), but it is not clear cubic phase. These data are coinciding with the data of Matsui [23], where it was showed that Al3+ ions segregated at grain boundaries directly enhance T → C phase transformation and grain growth at sintering temperatures above 1500 °C. The concentration of Y3+ ions in the matrix “small” grains of tetragonal phase decreased down to 2–2.5 mol% instead of 3 mol%, which corresponds to chemical composition of tetragonal phase of ZrO2. So, it was found that addition of Al2O3 to 3Y-ZrO2 ceramics leads to enrichment of some ZrO2 grains of tetragonal phase by Y3+ ions and depletion of the rest ZrO2 grains by Y3+ ions. Alumina in the sintered composites was represented by α-Al2O3 (black grains on Fig. 3b). The α-Al2O3 grains in 3Y-ZrO2-Al2O3 composites were presented as typical intercrystalline inclusions.
After sintering at 1500 °C in argon atmosphere, the phase composition of zirconia in 3Y-ZrO2 matrix material and 3Y-ZrO2-NiO composites changes according to XRD results. The amount of cubic phase in 3Y-ZrO2-NiO composite increased up to 20% in comparison with 3Y-ZrO2 (11%). SEM analysis of thermally etched surfaces also shows the macroscopic difference in the structure of zirconia grains. The amount of big grains, which traditionally corresponds to cubic phase of zirconia, and their size increased (Fig. 3c) in comparison with matrix 3Y-ZrO2. The average grain sizes with tetragonal and cubic phases in 3Y-ZrO2-NiO material by SEM data were 0.2–0.4 and 2–4 μm, respectively. The EDS analysis shows the increasing amount of Y3+ ions in the big grains up to 9–11 wt% (5–6 mol%). This value is approaching the concentration of Y3+ ions, which corresponds to chemical composition of cubic phase of ZrO2 (7–8 mol%). The concentration of Y3+ ions in the matrix small grains of tetragonal phase decreased to 1.6–2.5 mol% instead of 3 mol%, which corresponds to chemical composition of tetragonal phase of ZrO2. So, it was found that addition of NiO to 3Y-ZrO2 ceramics leads to depletion of ZrO2 grains of tetragonal phase by Y3+ ions, even more than addition of Al2O3.
Mechanical Properties of Sintered Ceramic Materials
All samples were sintered to greater than 99% of theoretical density. The four-point bending strength values for 3Y-ZrO2-Al2O3 and 3Y-ZrO2-NiO composites decreased by less than 10% in comparison with 3Y-ZrO2 matrix material (from 850 ± 60 to 760 ± 70 and 820 ± 78 MPa, respectively). Hardness values for 3Y-ZrO2-Al2O3 composite increased slightly from 12.0 ± 0.2 to 12.45 ± 0.3 GPa and for 3Y-ZrO2-NiO composite from 12.0 ± 0.2 to 12.1 ± 0.3 GPa. We know that the absolute fracture toughness values obtained by the indentation method could be overestimated, but this technique has been approved by many authors to provide the estimation of the fracture toughness values for samples with high-density levels, where the porosity cannot have effect on crack propagation [11, 24–28].
Analysis of crack propagation after Vickers indentation showed that the crack length in matrix 3Y-ZrO2 material was 387 μm (Fig. 4a), in 3Y-ZrO2-2 wt%Al2O3 composite material was 208 μm, and in 3Y-ZrO2-10 wt%NiO composite was 237 μm (Fig. 4b, c). Decreasing the dopant concentration leads to increasing in the crack length and consequently to decreasing the fracture toughness value (Fig. 5)
Thus, it was found that increasing in fracture toughness value of zirconia-based ceramic composites by 40–50% in comparison with 3Y-ZrO2 is caused by addition of different types of dopants—Al2O3 and NiO. These materials strongly differ by crystal lattice (Al2O3—trigonal, NiO—cubic), density (Al2O3—3.96 g/cm3, NiO—7.45 g/cm3), CTE (Al2O3—8.86 × 10−6K−1, NiO—12.8 × 10−6K−1), and Young’s modulus (Al2O3—400 GPa, NiO—95 GPa). The analogical parameters for ZrO2 are 5.95–6.1 g/cm3 (density), 10.8–11.5 × 10−6 K−1 (CTE), and 195–205 GPa (Young’s modulus). So, besides the direct influence on crack propagation as inclusions of alien material, these inclusions affect the structure and phase composition of matrix zirconia, the distribution of residual stresses, and other physical and chemical properties. Let us consider the impact of these dopants on the fracture toughness of zirconia ceramics and try to find the general and distinguish features.
Analysis of the possible toughened mechanisms in 3Y-TZP-based ceramic composites shows that the basic toughening mechanisms are phase transition in zirconia, crack bridging, and deflection by inclusion grains. Let us start with the crack deflection and crack bridging processes which take place for different types of materials [3, 6, 11]. According to the equation from [11], the crack bridging by NiO grains can lead to increasing in K1C value only by 0.1–0.3 MPa m1/2 and crack deflection by NiO grains on 0.6–1.0 MPa m1/2 in comparison with the matrix material ZrO2–3 mol%Y2O3. In the case of 3Y-ZrO2-Al2O3 composite, the increasing of K1C value is even less, because the amount of Al2O3 is several times less than NiO. These calculations were performed in our previous works [12, 19]. For these calculations, the Young modulus for NiO was near 100 GPa [29] and for Al2O3 380–400 GPa [30, 31]. The calculated fracture toughness increments explained the increasing of fracture toughness values due to the increasing number of filler grains (NiO or Al2O3) in composites (Fig. 5). The residual stresses around the inclusions have a great effect on the crack deflection. These stresses are conditioned with CTE mismatch between matrix material and inclusions. The calculation of the level of residual stresses (q) and its influence on fracture toughness values was done with the equation from Li [11] or Kern [28] studies,
where q is the thermal residual stress in the matrix and λ is the average interparticle spacing, which can be related to the average diameter d and the volume fraction f of particles as follows:
and q can be calculated with the following equations [11]:
where β and A are the composition from the Young and Poisson modules of ZrO2 and Al2O3 or NiO [11].
The values of residual stresses around the second-phase particle are proportional to the differences in the thermal expansion coefficients between the matrix and the second-phase particle (Δα). Based on Timoshenko and Gudier theory and data from Awaji’s [32] work, we know that the stress state in the zirconia matrix with the Al2O3 second-phase inclusion is expressed as σ r < 0 and σ θ > 0 and matrix material near the boundary between matrix and inclusion is under radial compressive (σ r ) and tensile tangential (σ θ ) stresses. It is because the difference in CTE (Δα = α(ZrO2) − α(Al2O3)) between ZrO2 and Al2O3 is large enough (11.8 × 10−6–8.86 × 10−6 K−1). In the case of NiO inclusions, the difference in CTE values between ZrO2 and NiO decreases (11.8 × 10−6–12.86 × 10−6 K−1) but has an opposite (negative) sign. So, the stress state in the matrix material near the boundary between matrix and inclusion with the NiO second-phase inclusion is σ r > 0 and σ θ < 0; matrix material near NiO particles is under radial tensile stress and under compressive tangential stress. The computer simulation of the residual thermal stresses in these structures by ABAQUS software confirms these results (Fig. 6). This analysis shows that the residual stresses in the Al2O3 and NiO inclusions and around them are quite different and the crack tip behavior in these different conditions near the inclusion should be different too. For example, the crack may turn towards to the zone with high tensile stresses and it is the possibility of tensile fracture in brittle particles. Or, when the boundary between the matrix and the inclusion undergoes a highly compressive stress, this system is desirable for fabrication of dislocations around the dispersed particle, as it was shown in [32]. But, as mentioned above, the crack deflection and crack bridging processes that caused by intercrystalline type of NiO and Al2O3 inclusions cannot explain the high experimentally observed values of K1C. It is extremely pronounced in the case of Al2O3 inclusions, where the increasing of K1C in 25% observed at 0.5 wt% of dopant. Also, it should be remembered that the enlarged amount of cubic phase in both types of composites may be a cause of slightly decreasing of fracture toughness value of samples, because the cubic phase has a lower indentation fracture toughness value in comparison with tetragonal phase.
The sharp increasing of fracture toughness may be conditioned only if we assume that the addition of NiO and Al2O3 affects the transformability of the tetragonal phase in 3Y-TZP. In our previous study [12], we investigate the crack propagation in 3Y-ZrO2-Al2O3 composite material and made a conclusion that formation of multi-level system of Al2O3 inclusions in combination with the enrichment of zirconia grain boundaries allows to increase fracture toughness of zirconia ceramics. But, detailed studies of SEM and EDS data from thermally etched surfaces of 3Y-ZrO2-Al2O3 composite material and comparison of these results with analogical data for 3Y-TZP-NiO (Fig. 3) allow us to suggest that the addition of Al2O3 and NiO promotes the increasing of Y3+ concentration in big zirconia grains in composites and leads to increasing metastability of rest Y3+-depleted ZrO2 grains. This correlation is shown in Table 1.
As it is known [33], this process took part in zirconia ceramic during sintering–cooling process. When the sintering temperature increases, the amount of segregated Y3+ ions on grain boundaries also increases because the diffusion process and ion segregation are enhanced, and a part of the tetragonal phase in Y-TZP transform into the cubic phase which is thermodynamically stable. During cooling, the grains, which were depleted by Y3+, become thermodynamically unstable and can be easily transformed into monoclinic phase in the stress field of propagated crack and stopped it. This is the transformation toughening effect [34]. In this case, the conception of critical grain size d c is introduced. The grains with size smaller than d c are stable, and grains with size greater than d c are unstable and easily transformed into monoclinic phase. The d c depends from dopant type and concentration and varied in a wide range from 150 to 1000 nm [34–36]. The most common value for tetragonal 3Y-ZrO2 is 300–400 nm. Increasing the dopant concentration leads to increase the critical grain size and, respectively, decreasing the dopant concentration leads to decreasing d c . The average grain size, which formed during sintering, depends on sintering conditions, initial powder characteristics, etc. For standard sintering conditions (1500 °C), which were used in this study, the average grain size is near 400 nm. So, decreasing the Y3+ ion concentration in zirconia grains in this study leads to decreasing the d c to the value less then experimentally observed values of average grain size of ZrO2 in T-phase.
As you can see from Table 1, the concentration Y3+ ions in small grains in both types of composites decreased faster in comparison with matrix 3Y-ZrO2 material. As mentioned above, the number and size of big zirconia grains with a high yttrium concentration in both composites are increased. In case of 3Y-ZrO2-NiO composite, these changes can be fixed by XRD. Because the experimental observed average size of zirconia grains in tetragonal phase in matrix 3Y-ZrO2 material and in both composites practically did not change but concentration of Y3+ in zirconia grains in T-phase in composites are decreased (Table 1), we can make a conclusion that the value of critical grain size of tetragonal phase in both composites are decreased (Fig. 7). The greater the influence of dopant ion on the phase stability, the faster the changes on the critical grain size is. Hence, the T-M phase transformation in Y3+-depleted grains can be realized more easily and transformation toughening effect may have more influence on fracture toughness value in both composites. The increasing of K1C value with increasing dopant concentration and its stabilization after attaining the certain value of dopant concentration allows us to assume that at least two mechanisms can affect the fracture toughness of ZrO2 ceramics. First, mechanism is the crack bridging and deflection processes, which affects the K1C value in a region where dopant concentration is low. In this region, K1C values increases with increasing dopant concentration. Second, mechanism is the transformation toughening effect. It affects the K1C values when the dopant concentrations increased to the critical values and can impact microstructure reorganization (formation of big grains with a higher Y3+ content). At low dopant concentration, this mechanism has low influence on K1C value, but its influence increased with increasing dopant concentration. Dopants initiated the Y3+ ion diffusion in zirconia lattice and formation of Y3+ ion enrichment and depleted zirconia grains (formation big grains with higher Y3+ concentration). In this structure, the transformation toughening effect affects on fracture toughness value. The supersaturation of zirconia by Al2O3 and NiO dopants may reduce the K1C values for the formation of zirconia grains with low stability (spontaneous transformation from tetragonal to monoclinic phase and damage of the samples due to cracking). By the way, we found in our previous studies a decrease of the K1C value after the excess of the dopant concentration limits (5 wt% for Al2O3 and 20 wt% for NiO) [12, 19]. The interaction of these two mechanisms (alien grains in structure and phase destabilization in the matrix grains) can ensure the nonmonotonic dependence of K1C value from dopant concentration. The differences in the “critical” concentration values (changing K1C from increasing to stabilization) for Al2O3 and NiO may be explained as effect of dopant type and difference in the methods of powder synthesis (co-precipitation and mixing).
The key condition is that the dopant should enhance the diffusion of Y3+ ions in zirconia lattice and should not form the unwanted chemical compounds. By changing the type of dopant and its concentration, the formation of a ceramic material with enhanced level of fracture toughness and predetermined strength value can be created. So, the combination of structure peculiarities–multilevel inclusion structure and phase metastability can enhance the toughening mechanisms in zirconia-based composites.
Conclusions
The effect of Al2O3 and NiO on microstructure peculiarities, mechanical properties, and fracture toughness behavior of 3Y-ZrO2 ceramics was investigated. The following conclusions could be drawn:
-
By SEM data, it was shown that Al2O3 and NiO additions lead to acceleration of bimodal grain structure formation, when the Y3+ ion enrichment and depleted zirconia grains are formed.
-
Analysis of influence of Al2O3 and NiO additions on indentation fracture toughness values of 3Y-ZrO2 ceramics shows the increasing of fracture toughness values with increasing dopant concentration and its stabilization on certain value.
-
The combination of such behavior of K1C dependences and structure peculiarities allows us to assume that at least two mechanisms can influence on fracture ZrO2 ceramics: (i) first mechanism is the crack bridging and deflection process, which affects in a region when K1C grows with increasing dopant concentration; (ii) second mechanism is the transformation toughening effect, which exerts one’s influence with increasing dopant concentration to the highest level.
-
The combination of multilevel inclusion structure and phase metastability can enhance the toughening mechanisms in zirconia-based composites.
Abbreviations
- 3Y-ZrO2 :
-
3 mol% yttria-stabilized tetragonal zirconia polycrystal
- EDS:
-
Energy-dispersive analysis
- K1C :
-
Critical coefficient of stress intension (K1)
- SEM:
-
Scanning electron microscopy
- TEM:
-
Transmission electron microscopy
- XRD:
-
X-ray diffraction
References
Herrmann M (2013) Corrosion of silicon nitride materials in aqueous solutions. J Am Ceram Soc 96:3009–22
Herrmann M, Höhn S, Bales A (2012) Kinetics of rare earth incorporation and its role in densification and microstructure formation of –SiAlON. J Eur Ceram Soc 32:1313–19
Ritchie RO (2011) The conflicts between strength and toughness. Nat Mater 10:817–22
Hannik R, Kelly P, Muddle B (2000) Transformation toughening in zirconia-containing ceramics. J Am Ceram Soc 83:461–87
Garvie RC, Hannink RH, Pascoe RT (1975) Ceramic steel? Nature 258:703–4
Ritchie RO (1999) Mechanisms of fatigue-crack propagation in ductile and brittle solids. Int J Fracture 100:55–83
Szutkowska M (2004) Fracture resistance behavior of alumina–zirconia composites. J Mater Proc Techn 153–154:868–74
Casellas D, Rafols I, Llanes L, Anglada M. Fracture toughness of zirconia–alumina composites. Int J Refract Met Hard Mater. 1999;17:11–20.
Lughi V, Sergo V (2010) Low temperature degradation—aging of zirconia: a critical review of the relevant aspects in dentistry. Dent Mater 26:807–20
Kageyama K, Harada Y, Kato H (2003) Preparation and mechanical properties of alumina–zirconia composites with agglomerated structures using pre-sintered powder. Mater Trans 44:1571–76
Li J, Watanabe R (1995) Fracture toughness of Al2O3-particle-dispersed Y2O3 partially stabilized zirconia. J Am Ceram Soc 78:1079–82
Danilenko I, Konstantinova T, Volkova G, Burkhovetski V, Glazunova V (2015) The role of powder preparation method in enhancing fracture toughness of zirconia ceramics with low alumina amount. J Ceram Sci Tech 6:191–200
Lopez-Esteban S, Rodriguez-Suarez T, Esteban-Betego F, Pecharroma C, Moya J (2006) Mechanical properties and interfaces of zirconia/nickel in micro-and nanocomposites. J Mater Sci 41:5194–9
Delaforce PM, Yeomans JA, Filkin NC, Wright GJ, Thomson RC (2007) Effect of NiO on the phase stability and microstructure of yttria-stabilized zirconia. J Am Ceram Soc 90:918–24
Fonseca FC, de Florio DZ, Esposito V, Traversa E, Muccillo E, Muccillo R (2006) Mixed ionic–electronic YSZ/Ni composite for SOFC anodes with high electrical conductivity. J Electrochem Soc 153:A354–60
Chen R, Chiu Y, Tuan W (2000) Toughening alumina with both nickel and zirconia inclusions. J Eur Ceram Soc 20:1901–6
Sun X, Yeomans J (1996) Microstructure and fracture toughness of nickel particle toughened alumina matrix composites. J Mater Sci 31:875–80
Danilenko I, Glazunov F, Konstantinova T, Volkova G, Burkhovetski V (2013) Effect of oxide nanofillers on fabrication, structure, and properties of zirconia-based composites. J Eur Ceram Soc 33:2321–5
Danilenko I, Glazunov F, Konstantinova T, Yashchyshyn I, Burkhovetski V, Volkova G (2014) Effect of Ni/NiO particles on structure and crack propagation in zirconia based composites. Adv Mat Lett 5:465–71
Garvie RC, Nicholson PS (1972) Phase analysis in zirconia systems. J Am Ceram Soc 55:303–5
Niihara K (1983) A fracture mechanics analysis of indentation-induced Palmqvist crack in ceramics. J Mater Sci Lett 2:221–3
Navarro LM, Recio P, Duran P (1995) Preparation and properties evaluation of zirconia-based/Al2O3 composites as electrolytes for solid oxide fuel cell systems. J Mater Sci 30:193l–8
Matsui K, Ohmichi N, Ogai M, Yoshida H, Ikuhara Y (2006) Effect of alumina-doping on grain boundary segregation-induced phase transformation in yttria-stabilized tetragonal zirconia polycrystal. J Mater Res 21:2278–89
Vasylkiv O, Sakka Y, Skorokhod V (2003) Low-temperature processing and mechanical properties of zirconia and zirconia–alumina nanoceramics. J Am Ceram Soc 86:299–304
Nevarez-Rascon A, Aguilar-Elguezabal A, Orrantia E, Bocanegra-Bernal MH (2011) Compressive strength, hardness and fracture toughness of Al2O3 whiskers reinforced ZTA and ATZ nanocomposites: Weibull analysis. Int J Refract Met Hard Mater 29:333–40
Santos C, Teixeira L, Daguano J, Rogero S, Strecker K, Elias C (2009) Mechanical properties and cytotoxicity of 3Y-TZP bioceramics reinforced with Al2O3 particles. Ceram Int 35:709–18
Li S, Izui H, Okano M, Zhang W, Watanabe T (2012) Microstructure and mechanical properties of ZrO2 (Y2O3)–Al2O3 nanocomposites prepared by spark plasma sintering. Particuology 10:345–51
Kern F, Palmero P (2013) Microstructure and mechanical properties of alumina 5vol% zirconia nanocomposites prepared by powder coating and powder mixing routes. Ceram Int 39:673–82
Notis M, Spriggs R, Hahn JW (1971) Elastic moduli of pressure-sintered nickel oxide. J Geophys Res 76:7052–61
Asmani M, Kermel C, Leriche A, Ourak M. Influence of porosity on Young's modulus and Poisson's ratio in alumina ceramics. J Eur Ceram Soc. 2001;21:1081–86.
Tuan WH, Chen RZ, Wang CH, Cheng PS, Kuo PS (2002) Mechanical properties of Al2O3/ZrO2composites. J Eur Ceram Soc 22:2827–33
Awaji H, Choi S, Yagi E (2002) Mechanisms of toughening and strengthening in ceramic-based nanocomposites. Mech Mater 34:411–22
Matsui K, Horikoshi H, Ohmichi N, Ohgai M, Yoshida H, Ikuhara Y (2003) Cubic-formation and grain-growth mechanisms in tetragonal zirconia polycrystal. J Am Ceram Soc 86:1401–8
Lange F (1982) Transformation toughening. J Mater Sci 17:225–63
Trunec M (2008) Effect of grain size on mechanical properties of 3Y-TZP ceramics. Ceramics–Silikáty 52:165–71
Basu B, Vleugels J, Van Der Biest O (2004) Transformation behaviour of tetragonal zirconia: role of dopant content and distribution. Mater Sci Eng A366:338–47
Acknowledgements
This work was supported by the grant AZ 90355 of the VW foundation program “Trilateral Partnerships.” Authors are grateful to the KIPT (Kharkov) for SEM investigation.
Authors’ Contributions
ID produced the main idea for writing this manuscript, analyzed the data, designed the experiments, and wrote the manuscript. GL performed the calculation of residual stresses in composites. IB performed the synthesis of nanopowders. VB performed the analysis of composite structure by SEM and EDS. LA performed the sample compaction, sintering, and preparation for mechanical testing. All authors read and approved the final manuscript.
Competing Interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Danilenko, I., Lasko, G., Brykhanova, I. et al. The Peculiarities of Structure Formation and Properties of Zirconia-Based Nanocomposites with Addition of Al2O3 and NiO. Nanoscale Res Lett 12, 125 (2017). https://doi.org/10.1186/s11671-017-1901-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-017-1901-7