Abstract
A set of ceria, ceria-zirconia (Ce 80 at.%, Zr 20 at.%), ceria-praseodymia (Ce 80 at.%, Pr 20 at.%) and ceria-zirconia-praseodymia (Ce 80 at.%, Zr 10 at.% and Pr 10 at.%) catalysts has been prepared by the solution combustion synthesis (SCS). The effects of Zr and Pr as dopants on ceria have been studied in CO and soot oxidation reactions. All the prepared catalysts have been characterized by complementary techniques, including XRD, FESEM, N2 physisorption at −196 °C, H2-temperature-programmed reduction, and X-ray photoelectron spectroscopy to investigate the relationships between the structure and composition of materials and their catalytic performance. Better results for CO oxidation have been obtained with mixed oxides (performance scale, Ce80Zr10Pr10 > Ce80Zr20 > Ce80Pr20) rather than pure ceria, thus confirming the beneficial role of multicomponent catalysts for this prototypical reaction. Since CO oxidation occurs via a Mars-van Krevelen (MvK)-type mechanism over ceria-based catalysts, it appears that the presence of both Zr and Pr species into the ceria framework improves the oxidation activity, via collective properties, such as electrical conductivity and surface or bulk oxygen anion mobility. On the other hand, this positive effect becomes less prominent in soot oxidation, since the effect of catalyst morphology prevails.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Background
Ceria has extensively been investigated in many oxidation reactions, thanks to its unique redox properties that allow rapid oxygen intake-uptake [1–3]. Much research has proven the success of ceria in catalyzing soot and CO oxidations [4–10]. In soot oxidation, a ceria-based catalyst requires a good contact with carbon soot; this is normally attained by tuning ceria morphology at a nanoscale level [7, 8, 11–13]. Due to the complexity of solid-gas interaction in soot oxidation reaction, the ability of ceria-based catalysts to initiate active oxygen species is strictly necessary. In CO oxidation, on the other hand, the oxygen storage capacity (OSC), which is high in ceria, plays the crucial role since it has been well understood that CO oxidation over ceria conforms to the Mars-van Krevelen (MvK)-type mechanism [3–5, 14]. In this mechanism, oxygen vacancies are formed during the reaction with CO, followed by oxygen refilling from the bulk phase.
Deficiency of oxygen as the prerequisite of enhanced redox properties is created by introducing metallic dopants [3, 15, 16]. The insertion of dopants perturbs the crystal structure of the catalyst, creating defects that may take form as vacancies or interstitial defects. In general, this may result in more cerium anions in a reduced state (Ce3+), improving the OSC of the catalyst. However, different effects might arise depending on the type of the metal. Among the metallic elements frequently investigated as dopants for ceria, zirconium and praseodymium have become of particular interest [6, 11, 15]. Previous experiments with soot oxidation over ceria-zirconia catalysts have shown that the catalytic activity over ceria-zirconia significantly improves [15]. It has also been found that higher dopant content gives better thermal stability (less reducible). However, the cerium redox sites decrease as the dopant concentration increases. Conversely, different phenomena have been observed for praseodymium as dopant for ceria. Our previous work with well-defined nanostructured catalysts has demonstrated that inserting more praseodymium into a ceria lattice framework results in more cerium redox sites, thus increasing the oxygen vacancies. This eventually impacts the catalytic activity, which is the highest for equimolar ceria-praseodymia [11].
In this article, we analyze the effect of zirconium and praseodymium as dopants for ceria-based catalysts. We introduce herein two bi-metallic oxides (ceria-zirconia and ceria-praseodymia) and one tri-metallic oxide (ceria-zirconia-praseodymia) as our testing materials to observe possible synergistic effects among the active species. Therefore, we tested a set of ceria, ceria-zirconia (Ce 80 at.%, Zr 20 at.%), ceria-praseodymia (Ce 80 at.%, Pr 20 at.%), and ceria-zirconia-praseodymia (Ce 80 at.%, Zr 10 at.% and Pr 10 at.%) catalysts for the CO and soot oxidation reactions. Finally, complementary physico-chemical characterizations are provided to accompany the understanding of the catalysts’ properties.
Methods
Preparation of Samples
Pure ceria (denoted as Ce100), ceria-zirconia (denoted as Ce80Zr20; Zr atomic percentage = 20 %), ceria-praseodymia (denoted as Ce80Pr20; Pr atomic percentage = 20 %), and ceria-zirconia-praseodymia (denoted as Ce80Zr10Pr10; Pr, Zr atomic percentage = 10 %) were prepared via solution combustion synthesis (SCS) [17]. Therefore, in all ceria-doped catalysts, the total atomic amount of dopants is equal to 20 %. Ce(NO3)3·6H2O, ZrO(NO3)2·xH2O and Pr(NO3)3·6H2O were used as the precursors, all from Sigma-Aldrich. In a typical preparation of the tri-metallic oxide (Ce80Zr10Pr10), 1.5 g of cerium precursor, 0.1 g of zirconium precursor, and 0.2 g of praseodymium precursor were dissolved in 60 mL of water. 0.8 g of urea was then added into the stirring solution. The final clear solution was then transferred into a ceramic crucible which was successively heated in a furnace to 650 °C.
Characterizations of Samples
Powder X-ray diffractograms of the samples were recorded in an X’Pert Philips PW3040 diffractometer using Cu Kα radiation, 2θ range of 20°–70° (angle step size at 0.02°) and a time per step of 0.2 s. The International Centre of Diffraction Data (ICDD) was used as the reference for peak identification. Scherrer’s equation, D = 0.9λ/bcosθ, was applied to predict the crystallite size of the sample where λ is the wavelength of the Cu Kα radiation, b is the full width at half maximum in radians, 0.9 is the shape factor for spheres, and θ is the diffraction peak angle.
N2 physisorption of the samples at −196 °C was performed by a Micrometrics ASAP 2020 instrument to determine the specific surface areas and total pore volumes. Removal of water and contaminants from the samples was done prior to analyses by heating the samples at 200 °C for 2 h. The Brunauer-Emmett-Teller (BET) method was applied to calculate the specific surface area of the sample (S BET).
Field emission scanning electron microscope (FESEM Zeiss MERLIN, Gemini-II column) was used to analyze the morphology of the samples.
H2-temperature-programmed reduction (TPR) was performed to analyze the reducibility of the samples. Sample pretreatment was conducted prior to analyses by treating 50 mg of catalyst under air (40 mL min−1) at 150 °C for 1 h, followed by cooling with Ar to room temperature. The H2-TPR analysis was executed by increasing gradually the sample temperature to 800 °C with the rate of 5 °C min−1 under Ar (4.95 %-mol H2 in Ar). The instrument was equipped with thermal conductivity detector (TCD) to recognize the H2 signal.
X-ray photoelectron spectroscopy measurements were collected on XPS PHI 5000 VersaProbe apparatus using a band-pass energy of 187.85 eV, a 45° takeoff angle, and a 100.0-μm-diameter X-ray spot size. Curve fits were obtained by Multipack 9.0 software.
Catalytic Tests
CO oxidation tests were carried out in a fixed-bed Quartz reactor (4-mm inner diameter, U-tube) heated by a vertical tubular furnace. In a typical run, 0.1 g of powdered sample was inserted in the reactor. The temperature of the reactor bed was detected by a K-type thermocouple, placed as close as possible to the bed. The test started by continuously flowing 50 mL min−1 gas containing 1000 ppm of CO and 50 %-vol air in N2 into the reactor. Meanwhile, the furnace heated up at a rate of 5 °C min−1 until complete CO conversion was reached. Non-dispersive infrared analyzers were used to record COx concentrations at the reactor outlet.
Soot oxidation tests were conducted in the same fixed-bed Quartz reactor heated by a vertical tubular furnace. In a typical run, a reactor bed contained 5 mg of soot (Printex-U), 45 mg of powdered sample, and 150 mg of silica. The bed was prepared by ball-milling the solid mixture at 250 rpm for 10 min to get a “tight” contact between the soot and the catalyst. The test started by flowing 100 mL min−1 gas comprising of 50 %-vol of air and 50 %-vol of N2 to the reactor. The reaction temperature increased from 100 to 700 °C with a 5 °C min−1 heating rate. Non-dispersive infrared analyzers were used to record COx concentrations at the reactor outlet.
Results and Discussion
Physical Properties of the Samples
Figure 1 shows the X-ray diffractograms of the samples. Analyses with X-ray diffraction prove that all prepared samples refer to a cubic fluorite structure of CeO2, indicated typically by (111), (200), (220), (311), and (222) peaks [18, 19]. No additional peaks due to either zirconia (ZrO2) or praseodymia (PrO2) phases were found in the diffractograms, thus confirming the presence of a single phase for these catalysts.
Simple prediction with Scherrer’s equation using (111) peak as the reference demonstrates the decrease in crystallite size due to the addition of dopants, with the tri-metallic oxide sample having the lowest size (see Table 1). Lattice parameters are modified when dopants are introduced. Zirconia-containing samples experience lattice shrinkage since Zr ionic radii are far lower than those of Ce (ionic radii of Zr4+ and Ce4+/Ce3+ are 0.72 Å and 0.87/1.01 Å) [20]. On the other hand, lattice expansion is found in the ceria-praseodymia sample (Ce80Pr20) despite the similar ionic radii of Ce and Pr (ionic radii of Pr4+/Pr3+ are 0.85/0.99 Å) [20]. This implies that more 3+ metal ions exist in the sample when Pr is introduced; similar findings have been observed in our previous work [11].
The BET specific surface areas of the samples derived from N2 physisorption can be seen on Table 1. The addition of dopants generally increases the surface area; however, the increment depends much on the inserted metals. Introducing zirconia into ceria structure enlarges the surface area, while embedding only praseodymium into ceria does not modify significantly the overall structure. Again, this might be because both cerium and praseodymium ions are nearly identical in size. The trend for surface area increases as follows: Ce100 < Ce80Pr20 < Ce80Zr20 < Ce80Zr10Pr10.
Figure 2 shows the morphology of the samples observed through FESEM. Synthesis by solution combustion technique allows the formation of a spongy framework (three-dimensional structures) comprising of small nanoscale agglomerates, thanks to gaseous products rapidly emitted during the reaction. The effect of dopants seems nearly negligible on the overall structure of the samples.
Reducibility and Redox Properties of the Samples
Figure 3 shows the H2-TPR curves for all samples. Reduction profiles of all samples accord generally with the profile of high-surface ceria; the initial reduction occurs at a low temperature (400–600 °C) and the final reduction occurs at a high temperature (>800 °C) [7, 11]. The initial reduction infers the role of surface oxygen, which is weakly attached to the surface of the catalyst. The final reduction is eventually triggered by the slow release of lattice oxygen at an extremely high temperature. The Ce80Zr20 sample has a lower initial reduction peak temperature (505 °C) than the pure ceria sample (563 °C). The Ce80Pr20 sample, on the other hand, exhibits two peaks during the initial reduction: the small one at 501 °C which appears incomplete and then the large one which appears at 576 °C. Although the main peak temperature of ceria-praseodymia sample is higher than that of pure ceria, the reduction commences earlier at a much lower temperature. It is likely that doping with praseodymium favors the weakening of Ce–O bonds, as observed in our previous research [11]. The tri-metallic oxide sample (Ce80Zr10Pr10) is ultimately the most reducible catalyst in the series, having two reduction peaks due to the effect of praseodymium and lower peak temperatures compared to ceria-praseodymia, thanks to the presence of zirconium.
Figures 4, 5, and 6 show the XPS spectra in the O (1s), Ce, Zr, and Pr (3d) BE regions. The O 1s spectra (Fig. 4) display the peaks assigned to either chemisorbed oxygen (Oα species) or lattice oxygen (Oβ species). As a whole, the peak at 528.9–529.5 eV corresponds to Oβ (i.e. O2−), whereas the signals at 531.1–531.5 eV are usually due to surface oxygens (e.g. O2 2−, O−, OH−, CO3 2−) [7, 11, 15]. As reported in Table 2, different Oα/Oβ ratios appear for the prepared samples. Interestingly, the Ce80Zr10Pr10 sample exhibits the lowest Oα/Oβ ratio, although it has the highest surface area. This suggests that oxidation reactions over the Ce80Zr10Pr10 catalyst might be mediated mainly by the lattice oxygens [6].
The dissociative adsorption of molecular oxygen requires steps of electron transfers from the solid catalyst into the anti-bonding π-orbital of the molecule until cleavage of the O–O bond is reached [21–23]:
This electronic property is beneficial in oxidation catalysis, since the requirements for the MvK mechanism to take place comprise a good mobility of both electrons and lattice oxygen anions within the solid catalyst. Previous research have demonstrated that introducing dopants into the ceria framework facilitates the activation of adsorbed oxygen to form superoxo (O2 −) and peroxo species (O2 2−) [24, 25].
Table 3 reports the relative abundance of the Ce3+ and Ce4+ species for each sample which is estimated considering the deconvolution results of Ce 3d (Fig. 5). As summarized in Table 4, the relative amount of Ce3+ species ranges from 16 to 24 at.%. The highest Ce3+ content is reached for the Ce80Pr20 sample, thus suggesting the role of Pr4+ ions in maintaining a lower oxidation state of Ce species. On the other hand, Zr4+ species have an opposite effect on the oxidation state of Ce species [15]. As a result, an intermediate value of the Ce3+ abundance can be found for the Ce80Zr10Pr10 sample (namely, 21 at.%). Figure 6a shows the Zr (3d) spectra for the Ce80Zr20 and Ce80Zr10Pr10 samples. The peaks at 181.9–182.3 eV correspond to the Zr 3d 5/2 states, whereas the signals at 184.4 eV reflect the Zr 3d 3/2 levels. As a whole, no signal is due to the ZrO2 phase (expected at ca. 182.9 eV) [15, 26], further confirming its absence in these mixed oxides (no-extra framework ZrO2), in agreement with XRD results. This means that a good incorporation of the Zr species into the ceria framework has been obtained for both samples. The different peak intensities for the two samples is essentially due to the dissimilar Zr loading into the materials (namely, 10 or 20 at.% for the Ce80Zr20 and Ce80Zr10Pr10 samples, respectively). The ratios between the areas of the 3d 5/2 and 3d 3/2 peaks are slightly different for the two samples (see Table 5), reflecting a difference in terms of electronic state of Zr species. Figure 6b shows finally the Pr 3d core-level XPS spectra of the Ce80Pr20 and Ce80Zr10Pr10 samples. The peaks in the spectra reflect two different states: (i) Pr 3d 5/2 at lower binding energies (927–933 eV), in which two peaks, m and s, were designated, and (ii) Pr 3d 3/2 at higher binding energies (952–965 eV), in which four peaks appear (namely, m’, s’, t’, and f’). The denotation m,m’ and s,s’ refers to the “main” and “satellite” peaks, respectively, while t’ refers to extra-structure, existing only in 3d 3/2 form (Table 6) [27]. On the other hand, the peak f’, originated uniquely from the PrO2 phase as a marker of Pr4+ oxidation state [28, 29], does not occur. This means that in the ceria framework, both Pr3+ and Pr4+ oxidation states exist. However, the relative abundance of these two species remains a difficult task. In fact, the primary peaks (m,m’, s,s’, t’) appear equally in Pr2O3 and PrO2, and hence the ascription of peaks to a definite oxidation state is rather impossible. Nevertheless, a different distribution of the energetic states m,m’, s,s’, and t’ occurs for the two mixed oxides.
Catalytic Tests
Figure 7 summarizes the results of CO oxidation catalytic tests over four samples. The curves indicate the CO conversion to CO2 as a function of temperature. In general, our catalysts improve greatly the CO conversion, as only about 40 % of the initial CO converts naturally to CO2 at 500 °C. It is evident that the Ce80Zr10Pr10 sample outperforms the other oxides. The tri-metallic oxide sample is able to convert half of the CO reactant at the lowest temperature (T 50% = 249 °C). This high activity likely draws contributions from the high reducibility, better redox properties, and the average particle size of the catalyst (vide supra). Since the MvK-type mechanism governs the reaction of CO oxidation over ceria-based catalysts, the reducibility and redox behavior of the solid catalysts plays a pivotal role in obtaining a high activity. In fact, the more reducible the catalyst, the easier the release of surface oxygen species accessible to CO molecule; moreover, a high electrical conductivity and oxygen anion mobility are beneficial factors for the oxidative mechanism [30, 31]. On the other hand, the geometric factor seems to play a role on the catalytic performances: smaller particle size helps to improve the catalytic activity by providing more accessible active sites to CO molecules [32].
It appears that the activity trend for CO oxidation follows this order: Ce100 < Ce80Pr20 < Ce80Zr20 < Ce80Zr10Pr10 (see Table 7 for complete data). This means that the Ce80Pr20 sample is less active than Ce80Zr20 despite having better reducibility. However, a similar trend has also been encountered in the BET surface areas. This implies the dependence of CO oxidation reaction on surface area. The MvK-type mechanism suggests that the reaction between CO and oxygen specie takes place on the catalyst surface. A higher surface area grants more opportunity for reactions to occur. This reactivity order reflects fairly well the abundance of Oβ-species which is maximum for the Ce80Zr10Pr10 sample, as revealed by XPS data. Thus, a collective (electronic) behavior of the active (redox) sites for the tri-metallic oxide seems to have a beneficial effect on the catalytic reactivity.
On the other hand, all the prepared oxide catalysts performed similarly with soot oxidation (Fig. 8). The temperatures at which half of carbon soot converted for Ce100, Ce80Zr20, Ce80Pr20, and Ce80Zr10Pr10 are 451, 469, 457, and 444 °C, respectively. Full data of the conversion temperatures are summarized in Table 8. The catalytic activity trend does not conform to the one for CO oxidation, although the tri-metallic oxide sample is still the most performing catalyst in the series. It seems that adding single dopants like Zr and Pr species does not promote enhanced catalytic activities. This is in fair agreement with previous measurements of Zr [15] and Pr [11] doping of SCS ceria, with respect to pure SCS ceria, although not verified in their co-presence. In contrast to this result, our previous works have also demonstrated that zirconium as well as praseodymium contributes positively to soot oxidation reaction over well-defined nanostructured catalysts (e.g., nanocubes and nanorods). This reconfirms our previous implication that soot oxidation reaction is highly structure-dependent [7].
As previously seen through FESEM (see Fig. 2), our samples prepared via solution combustion technique possess similar structures irrespective of their metallic dopants. The primary particles constituting the overall structure are somewhat polycrystalline and lacking in low index planes such as (100) and (110) [4, 11, 33]. The presence of more uncoordinated atoms on these planes enhances the reactivity due to the instability of the atoms. Unlike CO, carbon soot is rather a passive reactant: it lacks mobility. Hence, the reaction strictly necessitates high surface reactivity of the catalyst as well as good catalyst-soot contact. This eventually justifies the aim of adjusting proper morphology of catalysts for soot oxidation [34].
Finally, Fig. 9 shows the profiles of COx concentrations. The presence of catalysts increases the reaction selectivity to CO2, as the intensity of CO peak falls off at below 200 ppm. The introduction of dopants modifies the reaction selectivity to CO2 to a little extent; hence, the one for pure ceria sample (Ce100) is 94.7 %, while the one for the tri-metallic oxide sample (Ce80Pr10Zr10) is about 93.7 %.
Conclusions
In this work, we present our tri-metallic oxide sample (Ce80Zr10Pr10) which has exhibited the highest catalytic activity of CO and soot oxidations among other oxides. Zr and Pr as dopants for ceria gives a significant impact on the catalytic activity of CO oxidation, as they enhance catalyst reducibility, redox behavior, and tune up catalyst physical properties (e.g., surface area and primary particle size). On the other hand, the effect of dopants is hardly observable in soot oxidation due to the morphological drawback resulted from solution combustion synthesis.
References
Terribile D, Llorca J, Boaro M, de Leitenburg C, Dolcetti G, Trovarelli A (1998) Fast oxygen uptake/release over a new CeOx phase. Chem Commun. 1897-1898
Aneggi E, Boaro M, de Leitenburg C, Dolcetti G, Trovarelli A (2006) Insight into the redox properties of ceria-based oxides and their implications in catalysis. J Alloys Compd 408–412:1096–1102
Trovarelli A, Fornasiero P (2013) Catalysis by ceria and related materials, 2nd edn. Imperial College Press, London
Aneggi E, Llorca J, Boaro M, Trovarelli A (2005) Surface-structure sensitivity of CO oxidation over polycrystalline ceria powders. J Catal 234:88–95
Wu Z, Li M, Overbury SH (2012) On the structure dependence of CO oxidation over CeO2 nanocrystals with well-defined surface planes. J Catal 285:61–73
Piumetti M, Bensaid S, Fino D, Russo N (2016) Ceria-zirconia nanocatalysts for CO oxidation: study on surface properties and reactivity. Appl Catal B. DOI:10.1016/j.apcatb.2016.02.023
Piumetti M, Bensaid S, Russo N, Fino D (2015) Nanostructured ceria-based catalysts for soot combustion: investigations on the surface sensitivity. Appl Catal B 165:742–751
Aneggi E, Wiater D, de Leitenburg C, Llorca J, Trovarelli A (2014) Shape-dependent activity of ceria in soot combustion. ACS Catal 4:172–181
Miceli P, Bensaid S, Russo N, Fino D (2014) CeO2-based catalysts with engineered morphologies for soot oxidation to enhance soot-catalyst contact. Nanoscale Res Lett 9:254
Bensaid S, Russo N, Fino D (2013) CeO2 catalysts with fibrous morphology for soot oxidation: the importance of the soot-catalyst contact conditions. Catal Today 216:57–63
Andana T, Piumetti M, Bensaid S, Russo N, Fino D, Pirone R (2016) Nanostructured ceria-praseodymia catalysts for diesel soot combustion. Appl Catal B. DOI: 10.1016/j.apcatb.2015.12.030
Yang Z, Zhou K, Liu X, Tian Q, Lu D, Yang S (2007) Single-crystalline ceria nanocubes: size-controlled synthesis, characterization and redox property. Nanotechnology 18:185606
Mai H-X, Sun L-D, Zhang Y-W, Si R, Feng W, Zhang H-P, Liu H-C, Yan C-H (2005) Shape-selective synthesis and oxygen storage behavior of ceria nanopolyhedra, nanorods, and nanocubes. J Phys Chem B 109:24380–24385
Royer S, Duprez D (2011) Catalytic oxidation of carbon monoxide over transition metal oxides. ChemCatChem 3:24–65
Piumetti M, Bensaid S, Russo N, Fino D (2016) Investigations into nanostructured ceria–zirconia catalysts for soot combustion. Appl Catal B 180:271–282
Bueno-López A (2014) Diesel soot combustion ceria catalysts. Appl Catal B 146:1–11
Bensaid S, Russo N (2011) Low temperature DPF regeneration by delfossite catalysys. Cat Tod 176:417–423
Thrimurthulu G, Rao KN, Devaiah D, Reddy BM (2012) Nanocrystalline ceria-praseodymia and ceria-zirconia solid solutions for soot oxidation. Res Chem Intermed 38:1847–1855
Reddy BM, Thrimurthulu G, Katta L, Yamada Y, Park S-E (2009) Structural characteristics and catalytic activity of nanocrystalline ceria-praseodymia solid solutions. J Phys Chem C 113:15882–15890
Shannon RD (1976) Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Cryst A32:751–767
Chen H-T, Chang J-G, Chen H-L, Ju S-P (2009) Identifying the O2 diffusion and reduction mechanisms on CeO2 electrolyte in solid oxide fuel cells: a DFT + U study. J Comput Chem 30:2433–2442
Choi YM, Abernathy H, Chen H-T, Lin MC, Liu M (2006) Characterization of O2-CeO2 interactions using in situ Raman spectroscopy and first-principle calculations. Chem Phys Chem 7:1957–1963
Zeng W, Liu T, Wang Z, Tsukimoto S, Saito M, Ikuhara Y (2010) Oxygen adsorption on anatase TiO2 (101) and (001) surfaces from first principles. Mater Trans 51:171–175
Cen W, Liu Y, Wu Z, Wang H, Weng X (2012) A theoretic insight into the catalytic activity promotion of CeO2 surfaces by Mn doping. Phys Chem Chem Phys 14:5769–5777
Wang H-F, Li H-Y, Gong X-Q, Guo Y-L, Lu G-Z, Hu P (2012) Oxygen vacancy formation in CeO2 and Ce1-xZrxO2 solid solutions: electron localization, electrostatic potential and structural relaxation. Phys Chem Chem Phys 14:16521–16535
Suhonen S, Valden M, Hietikko M, Laitinen R, Savimäki A, Härkönen M (2001) Effect of Ce-Zr mixed oxides on the chemical state of Rh in alumina supported exhaust catalysts studied by XPS and XRD. Appl Catal A 218:151–160
Gurgul J, Rinke MT, Schellenberg I, Pöttgen R (2013) The antimonide oxides REZnSbO and REMnSbO (RE = Ce, Pr)—an XPS study. Solid State Sci. 122-127
Bianconi A, Kotani A, Okada K, Giorgi R, Gargano A, Marcelli A, Miyahara T (1988) Many-body effects in praseodymium core-level spectroscopies of PrO2. Phys Rev B 38:3433–3437
Lütkehoff S, Neumann M, Ślebarski A (1995) 3d and 4d x-ray-photoelectron spectra of Pr under gradual oxidation. Phys Rev B 52:13808–13811
Vedrine JC (2014) Revisiting active sites in heterogeneous catalysis: their structure and their dynamic behaviour. Appl Catal A 474:40–50
Grasselli RK (2001) Genesis of site isolation and phase cooperation in selective oxidation catalysis. Top Catal 15:93–101
Freund HJ, Meijer G, Scheffler M, Schlögl R, Wolf M (2011) CO oxidation as a prototypical reaction for heterogeneous processes. Angew Chem Int Ed 50:10064–10094
Zhou K, Wang X, Sun X, Peng Q, Li Y (2005) Enhanced catalytic activity of ceria nanorods from well-defined reactive crystal planes. J Catal 229:206–212
Fino D, Bensaid S, Piumetti M, Russo N (2016) A review on the catalytic combustion of soot in Diesel particulate filters for automotive applications: from powder catalysts to structured reactors. Appl Catal A 509:75–96
Acknowledgements
The Ministero dell’Università e della Ricerca (MIUR) (grant number: RBFR12LS6M 001) is acknowledged for sponsoring this research activity (FIRB - Futuro in Ricerca 2012). This work was also co-funded through a SINCHEM Grant. SINCHEM is a Joint Doctorate program selected under the Erasmus Mundus Action 1 Programme (FPA 2013-0037).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing Interests
The authors declare that they have no competing interests.
Authors’ Contributions
TA prepared and tested the catalysts. MP and SB conceived the catalysts and directed the project. NR, DF, and RP supervised the results’ discussion and paper writing. All authors approved the final manuscript.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Andana, T., Piumetti, M., Bensaid, S. et al. CO and Soot Oxidation over Ce-Zr-Pr Oxide Catalysts. Nanoscale Res Lett 11, 278 (2016). https://doi.org/10.1186/s11671-016-1494-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1494-6