Abstract
In the present paper, we have studied a new approach to the description ofcorrelation between the optical and structural properties of ZnO thin films withdoping levels of Al, Co, and In. The doped zinc oxide thin films were depositedusing ultrasonic spray technique on a glass substrate at 350°C. Thecorrelation between structural and optical properties with doping level suggeststhat the crystallite size of the films is predominantly estimated by the bandgapenergy and the concentration of Al, Co, and In. Also, the gap energy of dopedfilms was estimated by the crystallite size and doping level. The measurement inthe crystallite size and optical gap energy of doped films with correlation isequal to the experimental data. The minimum error value was estimated in dopedZnO thin films with indium and cobalt. Thus, results indicate that such Co-dopedZnO thin films are chemically purer and have many fewer defects and lessdisorder, owing to an almost complete chemical decomposition.
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Findings
Background
Zinc oxide has a wurtzite structure, which is a hexagonal crystal structure(lattice parameter: a = 0.325 nm,c = 0.521 nm), belonging to the space group P63mc, and ischaracterized by two interconnecting sublattices of Zn2+ andO2-, such that each Zn ion is surrounded by a tetrahedra of Oions and vice versa [1]. ZnO which is one of the most important binary II-VI semiconductorcompounds is a natural n-type electrical conductor with a direct energy widebandgap of 3.37 eV at room temperature and a large exciton binding energy(approximately 60 meV) [2–5].
ZnO thin films can be doped with a variety of semiconductors to meet the demandsof several application fields. Stoichiometric ZnO films are highly resistive.Conducting films can be made either by creating oxygen vacancies, which act asdonors, or by doping with various dopants such as Ga3+,Mn4+, Al3+, In3+, Co2+, andV3+[6–11]. Many attempts were reported about doped ZnO films, but most of themare related with Al doping. There are several works that use dopants such as Co,In, or Al in ZnO to enhance the optical and electrical conductivity. The dopedfilms can be used for various applications such as transparent electronics,piezoelectronic devices, gas sensors, and the transparent electrode window layerof thin-film solar cells [8–13]. The films (ZnO:Al) are considered to be utmost important materialsdue to their high conductivity, good transparency, and lower cost.
The aim of this paper is to study the possibility of the correlation between theoptical and structural properties of ZnO thin films with doping level. Ramana etal. [14] found that the grain size of V2O5 thin filmsproduced by pulsed laser ablation strongly influences their opticalcharacteristics. Bensouyad et al. [15] describe the relation between structural and optical properties ofTiO2:ZnO thin films in a considerate experimental study andcontrolled the variation of crystallite size by modifying the annealingtemperature, film thickness, and doping. Therefore, Cuong Ton-That et al. [16] estimated the direct correlation between the bandgap and crystalstructure and suggest that the band edge optical properties of Mn-doped ZnO arepredominantly influenced by the amount of Mn atoms substituting Zn on thelattice sites. However, similar works have investigated the dependence ofphysical properties of a ZnO thin film as a function of parameter conditionssuch a temperature, thickness, oxidizing conditions, nitrogen addition, anddoping for characterizing the thin films [17–25].
The aim of our paper is to present a new approach to calculate the crystallitesize by the optical gap energy and doping level of a doped ZnO thin film. Also,we have estimated the relationships between the optical gap energy and thecrystallite size with doping level of doped ZnO thin films. Detailedcalculations are developed from doped ZnO thin films with Al, Co, and In.
Methods and model
The ZnO, ZnO:Al, ZnO:Co, and ZnO:In samples were deposited on glass substratesusing ultrasonic spray technique at a temperature of 350°C with 2 min ofdeposition time. The optical gap energy and crystallite size of the films weremeasured with doping level. In our papers, we have studied the effect of variousparameters such as doping level, growth times, substrate temperature, andannealing temperature of the ZnO thin films [26–31] (see Table 1).
The correlation between the structural and optical properties of doped ZnO thinfilms was investigated in two parts. First, we studied the optical gap energyand doping level. Second, we estimated a correlation with crystallite size andthe doping level for the optical gap energy, wherein ZnO was doped by variouselements such Al, Co, and In and the element concentration was changed to get adoping limitation.
The correlation parameters for the crystallite size (G), bandgap energy(E g ), and doping level X 0 of doped ZnO thin films resulted from the following equation:
where G(e), Eg(e), and X0(e) are the experimental data; G(e)Max, Eg(e)Max, and X0(e)Max are maximal experimental values; and G(*), Eg(*), and X0(*) are the first values that have been calculated in thecorrelation relationships.
Results
Correlation with crystallite size
The doped ZnO thin films were deposited for the precursor molarity equal to 0.1M. In this point, the doping level is equal to zero for undoped ZnO thin films.Therefore, we have estimated the relationships between the crystallite size andthe bandgap energy with doping level as the following empiricalrelationships:
where a, b, and c are empirical constants and dependon the dopant. These parameters are collected in Table 2 and estimated as a function of dopant element. Table 3 present the correlate values.
Correlation with optical gap energy
In this part, we have studied the correlation between the optical gap energy andthe crystallite size with doping level. The formula studied in the correlationwith crystallite size is based on a nonlinear correlation; however, we havechosen the complex equation to correlate the optical gap energy as the followingempirical relationships:
where a′, b′, and c′ are empiricalconstants and depend on the dopant. These parameters are collected inTable 2 and estimated as a function of dopantelement.
Discussion
In this study, we will show the evolution of the doping level on the crystallite sizeand optical gap energy. We tried to establish correlations for each model proposed.In our calculations, the crystallite size and optical gap energy of doped ZnO thinfilms were estimated from Equations 2 and 3; the ZnO films exhibiting singlecrystals are n-type semiconductors with a high crystallinity.
As shown in Figures 1, 2, and 3, significant correlation was found between the crystallitesize and the optical gap values of the doped ZnO thin films as a function of Al, Co,and In concentration, respectively. The increase of the crystallite size has beenindicated by the enhancement of the crystallinity and c axis orientation ofZnO thin films by Zhu et al. [25]. The measurement in the crystallite size of doped films byEquation 2 is equal to the experimental data; thus, the error of thiscorrelation is smaller than 13% and can be calculated from the relationship|(GExp - GCorr)/GExp| × 100. The minimum error value was estimated in thecobalt- and indium-doped ZnO thin films (see Figure 4).
The maximum enhancement of the crystallite size was found to be of minimum errorafter doping at 3 wt.% (see Figure 4). The amount of Al,Co, and In doping contents achieved in doped ZnO film is 3 wt.%. Based on theexperimental and correlation values for the crystallite size that were developed,good agreement was found between the calculated and experimental values.
The variation of optical gap energy with doping level calculated by Equation 3is shown in Figures 5, 6, and 7 and shows that the optical gap energy can be estimated usingcrystallite size data by varying the doping level in all films. The finalcorrelation data show that the errors calculated from Equation 3 are smallerthan those from Equation 2, as shown in Figure 8. Ascan be seen, the minimal error is achieved in Co-doped ZnO thin films and limited to0% in all concentrations.
We know that such ZnO:Co and ZnO:In thin films are chemically purer and have manyfewer defects and less disorder, owing to an almost complete chemical decomposition,and contain higher optical bandgap energy; thus, we have obtained a minimum errorwith crystallite size from Equation 2.
We have estimated the crystallite size and optical bandgap of doped films usingvarious elements such as Al, Co, and In. The element concentration was changed toget a doping limitation. As can be noted, the ZnO thin film considers a highertransition tail width between the conduction band and valence band. FromEquation 3, it can be concluded that the optical gap is affected by thecrystallite size of undoped and doped ZnO thin films. Thus, the correlation betweenthe crystallite size and the bandgap with the doping level was investigated.
Conclusion
In this paper, we have presented a new approach to the description of correlationbetween crystallite size and optical gap energy with doping levels of Al, Co, andIn. The following conclusions can be drawn from the results presented:
-
The correlation between the crystallite size and the bandgap withdoping levels of Al, Co, and In was investigated.
-
The crystallite size of the films is predominantly estimated by thebandgap energy and the concentration of Al, Co, and In. Also, the gap energy ofdoped films was estimated by the crystallite size and doping level.
-
The measurement in the crystallite size and optical gap energy ofdoped films with correlation is equal to the experimental values.
-
The error of correlation of the crystallite size is smaller than14%; the minimum error achieved for ZnO:Co and ZnO:In is limited to 0%. However, forthe correlation of the optical gap energy, the error found is smaller than 2%.Co-doped ZnO films have a minimal error limited to 0%.
References
Ohtsu M: Progress in Nano-Electro Optics VII. Tokyo; 2002:73–108.
Zhang Y, Wu C, Zheng Y, Guo T: Synthesis and efficient field emission characteristics of patterned ZnOnanowires. J. Semicond. 2012, 33: 023001–1. 10.1088/1674-4926/33/2/023001
Zhang H, Liu H, Lei C, Zhou A, Yuan C: Low-temperature deposition of transparent conducting Mn–W co-doped ZnOthin films. J. Semicond. 2010, 31: 083005–1. 10.1088/1674-4926/31/8/083005
Benramache S, Benhaoua B, Khechai N, Chabane F: Elaboration and characterization of ZnO thin films. Matériaux Tech. 2012, 100: 573–580. 10.1051/mattech/2012052
Ma L, Ai X, Huang X, Ma S: Effects of the substrate and oxygen partial pressure on the microstructuresand optical properties of Ti-doped ZnO thin films. Superlattice. Microst. 2011, 50: 703–712. 10.1016/j.spmi.2011.09.012
Wang SK, Lin TC, Jian SR, Juang JY, Jang JSC, Tseng JY: Effects of post-annealing on the structural and nanomechanical properties ofGa-doped ZnO thin films deposited on glass substrate by rf-magnetronsputtering. Appl. Surf. Sci. 2011, 258: 1261–1266. 10.1016/j.apsusc.2011.09.088
Mazhdi M, Saydi J, Karimi M, Seidi J, Mazhdi F: A study on optical, photoluminescence and thermoluminescence properties ofZnO and Mn doped-ZnO nanocrystalline particles. Optik 2011, 124: 4128–4133.
Hafdallah A, Yanineb F, Aida MS, Attaf N: In doped ZnO thin films. J. Alloys. Compd. 2011, 509: 7267–7270. 10.1016/j.jallcom.2011.04.058
Rahmane S, Djouadi MA, Aida MS, Barreau N, Abdallah B, Hadj Zoubir N: Power and pressure effects upon magnetron sputtered aluminum doped ZnO filmsproperties. Thin Solid Films 2010, 519: 5–10. 10.1016/j.tsf.2010.06.063
Van LH, Hong MH, Ding J: Structural and magnetic property of Co-doped ZnO thin films prepared bypulsed laser deposition. J. Alloys. Compd. 2008, 449: 207–209. 10.1016/j.jallcom.2006.02.114
Mhamdi A, Boukhachem A, Madani M, Lachheb H, Boubaker K, Amlouk A, Amlouk M: Study of vanadium doping effects on structural, opto-thermal and opticalproperties of sprayed ZnO semiconductor layers. Optik 2013, 124: 3764–3770. 10.1016/j.ijleo.2012.11.074
Rozati SM, Akesteh S: Characterization of ZnO:Al thin films obtained by spray pyrolysistechnique. Mater. Charact. 2007, 58: 319–323. 10.1016/j.matchar.2006.05.012
Ma QB, Ye ZZ, He HP, Wang JR, Zhu LP, Zhao BH: Preparation and characterization of transparent conductive ZnO:Ga films by DCreactive magnetron sputtering. Mater. Charact. 2008, 59: 124–129. 10.1016/j.matchar.2006.11.020
Ramana CV, Smith RJ, Hussain OM: Grain size effects on the optical characteristics of pulsed-laser depositedvanadium oxide thin films. Phys. Stat. Sol. A 2003, 199: R4-R6. 10.1002/pssa.200309009
Bensouyad H, Adnane D, Dehdouh H, Toubal B, Brahimi M, Sedrati H, Bensaha R: Correlation between structural and optical propertiesof TiO2:ZnO thin filmsprepared by sol–gel method. J. Sol–gel Sci. Technol. 2011, 59: 546–552.
Ton-That C, Foley M, Phillips MR, Tsuzuki T, Smith Z: Correlation between the structural and optical properties of Mn-doped ZnOnanoparticles. J. Alloys. Compd. 2012, 522: 114–117.
Joshi B, Ghosh S, Srivastava P, Kumar P, Kanjilal D: Correlation between electrical transport, microstructure and room temperatureferromagnetism in 200 keV Ni2+ ion implanted zinc oxide (ZnO)thin films. Appl. Physica. 2012, 107: 393–400.
Wang SD, Miyadera T, Minari T, Aoyagi Y, Tsukagoshi K: Correlation between grain size and device parameters in pentacene thin filmtransistors. Appl. Phys. Lett. 2008, 93: 043311–1. 10.1063/1.2967193
Minami T, Nanto H, Takata S: Correlation between film quality and photoluminescence in sputtered ZnO thinfilms. J. Mater. Sci. 1982, 17: 1364–1368. 10.1007/BF00752247
Zhu JJ, Vines L, Aaltonen T, Kuznetsov AY: Correlation between nitrogen and carbon incorporation into MOVPE ZnO atvarious oxidizing conditions. Microelectronics J. 2009, 40: 232–235. 10.1016/j.mejo.2008.07.042
Deng R, Zou Y, Tang H: Correlation between electrical, optical properties and Ag2+centers of ZnO:Ag thin films. Physica. B. 2008, 403: 2004–2007. 10.1016/j.physb.2007.11.007
Ajimsha RS, Das AK, Singh BN, Misra P, Kukreja LM: Correlation between electrical and optical properties of Cr:ZnO thin filmsgrown by pulsed laser deposition. Physica. B. 2011, 406: 4578–4583. 10.1016/j.physb.2011.09.024
Gredig T, Silverstein EA, Byrne MP: Height-height correlation function to determine grain size in ironphthalocyanine thin films. J. Phys. Conference Series 2013, 417: 012069–5.
Vollmann W, Berger W, Hamann C, Libera L: Relations between the morphology and conductivity of thin films oftetrathiofulvalinium-tetracyanoquinodimethane. Thin Solid Films 1984, 111: 7–16. 10.1016/0040-6090(84)90344-4
Asadov A, Gao W, Li Z, Lee J, Hodgson M: Correlation between structural and electrical properties of ZnO thinfilms. Thin Solid Films 2005, 476: 201–205. 10.1016/j.tsf.2004.09.038
Benramache S, Chabane F, Benhaoua B, Lemmadi F: Influence of growth time on crystalline structure, conductivity and opticalproperties of ZnO thin films. J. Semicond. 2013, 34: 023001–1. 10.1088/1674-4926/34/2/023001
Gahtar A, Benramache S, Benhaoua B, Chabane F: Preparation of transparent conducting ZnO:Al films on glass substrates byultrasonic spray technique. J. Semicond. 2013, 34: 073001–1. 10.1088/1674-4926/34/7/073001
Benramache S, Benhaoua B, Bentrah H: Preparation of transparent conducting of ZnO:Co and ZnO:In thin films byultrasonic spray method. J. Nanostruct. Chemist. 2013, 3: 1–7.
Benramache S, Benhaoua B, Chabane F: Effect of substrate temperature on the stability of transparent conductingcobalt doped ZnO thin films. J. Semicond. 2012, 33: 093001–1. 10.1088/1674-4926/33/9/093001
Benramache S, Benhaoua B: Influence of substrate temperature and cobalt concentration on structural andoptical properties of ZnO thin films prepared by ultrasonic spraytechnique. Superlattice. Microst. 2012, 52: 807–815. 10.1016/j.spmi.2012.06.005
Benramache S, Benhaoua B: Influence of annealing temperature on structural and optical properties ofZnO:In thin films prepared by ultrasonic spray technique. Superlattice. Microst. 2012, 52: 1062–1070. 10.1016/j.spmi.2012.08.006
Zhu BL, Zhao XZ, Su FH, Li GH, Wu XG, Wu J, Wu R: Low temperature annealing effects on the structure and optical properties ofZnO films grown by pulsed laser deposition. Vacuum 2010, 84: 128–130.
Acknowledgments
We thanks Pr. M.S. Aida and Pr. A. Chari (Constantine University), Pr. Z.Boumerzoug, Pr. H. Ben Temam, Dr. S. Rahmane, Mr. B. Gasmi, Dr. C. Mahboub andDr. H. Bentrah (Biskra Universty) for helpful counseling.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
AA participated in the modeling section. OB and AG participated in the designsection. SB participated in the experimental data and performed the statisticalanalysis. SB, AA, OB, and AG carried out the manuscript preparation. All authorsread and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Benramache, S., Arif, A., Belahssen, O. et al. Study on the correlation between crystallite size and optical gap energy of doped ZnO thin film. J Nanostruct Chem 3, 80 (2013). https://doi.org/10.1186/2193-8865-3-80
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/2193-8865-3-80