Abstract
In this work, we investigate the controlled fabrication of Sn-doped TiO2 nanorods (Sn/TiO2 NRs) for photoelectrochemical water splitting. Sn is incorporated into the rutile TiO2 nanorods with Sn/Ti molar ratios ranging from 0% to 3% by a simple solvothermal synthesis method. The obtained Sn/TiO2 NRs are single crystalline with a rutile structure. The concentration of Sn in the final nanorods can be well controlled by adjusting the molar ratio of the precursors. Photoelectrochemical experiments are conducted to explore the photocatalytic activity of Sn/TiO2 NRs with different doping levels. Under the illumination of solar simulator with the light intensity of 100 mW/cm2, our measurements reveal that the photocurrent increases with increasing doping level and reaches the maximum value of 1.01 mA/cm2 at −0.4 V versus Ag/AgCl, which corresponds to up to about 50% enhancement compared with the pristine TiO2 NRs. The Mott-Schottky plots indicate that incorporation of Sn into TiO2 nanorod can significantly increase the charge carrier density, leading to enhanced conductivity of the nanorod. Furthermore, we demonstrate that Sn/TiO2 NRs can be a promising candidate for photoanode in photoelectrochemical water splitting because of their excellent chemical stability.
Avoid common mistakes on your manuscript.
Background
Growing global energy demand and increasing concern for climate change have aroused the interest in new technologies to harness energy from renewable sources while decreasing dependence on fossil fuels [1, 2]. One of the most attractive approaches is to produce hydrogen by solar water splitting, because of the high energy density of hydrogen and zero harmful byproduct after combustion as a fuel [3, 4]. Since the first report of the photoelectrochemical water splitting using n-type TiO2 in 1972 [5], TiO2 has drawn more and more attentions in this field and is regarded as one of the most promising materials as photoanode for solar water splitting, considering its high chemical stability, low cost, and nontoxicity [6, 7].
Early efforts in using TiO2 material for solar water splitting were mainly focused on the nanoparticle-based thin films for their large surface area-to-volume ratios. However, the high charge carrier recombination and low electron mobility at the grain boundary limit the performance of the films [8, 9]. Recently, researches shifted to the one-dimensional nanostructure including nanorods [10–12], nanotubes [13–15], and nanowires [16, 17]. Various fabrication processes were developed for the synthesis of TiO2 nanorods, nanowires, or nanotubes, such as catalyst-assisted vapor–liquid-solid (VLS) [16], hydrothermal process [10], electrochemical anodization [18, 19], etc. However, TiO2 is a wide band gap semiconductor, only absorbing UV-light, which suppresses its further applications. Considerable efforts have been devoted to improve the photon absorption and photocatalytic activity of TiO2 nanostructures, including synthesizing branched structures [20], exposing its active surface [21], hydrogen annealing process [22, 23], and sensitizing with other small band gap semiconductor materials such as PbS [14], CdSe [24], and CuInS [25].
Doping with other elements to tune the band gap of TiO2 is another efficient method to improve the photocatalytic activity. N, Ta, Nb, W, and C have been successfully incorporated into TiO2 photoanode and been demonstrated with enhanced photoconversion efficiency [26–29]. Besides, the SnO2/TiO2 composite fibers have also emerged and showed well photocatalytic property [30, 31]. Based on these researches, we expect that the incorporation of Sn into TiO2 would be an attractive approach since the small lattice mismatch between TiO2 and SnO2 is beneficial for the structural compatibility and stability. Meanwhile, the doping would significantly increase the density of charge carriers and lead to a substantial enhancement of photocatalytic activity. In this work, we successfully realized the controlled incorporation of Sn into TiO2 nanorods by a simple solvothermal synthesis method and investigated the role of Sn doping for enhanced photocatalytic activity in photoelectrochemical water splitting.
Methods
In our experiments, a transparent conductive fluorine-doped tin oxide (FTO) glass was ultrasonically cleaned in acetone and ethanol for 10 min, respectively, and then rinsed with deionized (DI) water. Twenty-five milliliters DI water was mixed with 25 mL concentrated hydrochloric acid (37%) in a Teflon-lined stainless steel autoclave. The mixture was stirred for several minutes before adding of 0.8 mL tetrabutyl titanate (TBOT). Then, 0–80 μL of Tin tetrachloride (SnCl4) solution was added for the synthesis of Sn-doped TiO2 nanorods (Sn/TiO2 NRs), followed by another several minutes stirring. Subsequently, the clean FTO substrate was placed into the Teflon-liner. The synthesis process was conducted in an electric oven, and the reaction temperature and time were 180°C and 6 h, respectively, for most of the experiments. After that, the autoclave was cooled, and the FTO substrate was taken out and rinsed with DI water. Finally, the sample was annealed at 450°C in quartz tube furnace (Thermo Scientific, Waltham, MA, USA) for 2 h in the air to remove the organic reactant and enhance the crystallization of the nanorods. For the synthesis of pristine TiO2 nanorods, the process was all the same, except for the elimination of the Sn precursor. The white nanorods film was detached from the FTO substrate with a blade and then added into ethanol followed by sonication for about 20 min. After that, two drops of the ultrasonically dispersed solution were dropped onto the copper grid and dried by heating in the ambient air for examination. To distinguish the samples with different doping levels, the Sn/TiO2 NRs were marked in the form of Sn/TiO2-a%, where a% is the molar ratio of SnCl4/TBOT.
The morphology and lattice structure of the nanorods were examined by the field-emission scanning electron microscopy (FESEM, JSM-7600 F, JEOL, Akishimashi, Tokyo, Japan) and field-emission transmission electron microscopy (FTEM, Tecnai G2 F30, FEI, Hillsboro, OR, USA). The energy-dispersive X-ray spectroscopy (EDX) combined with FSEM and FTEM was employed to detect the element composition of Sn/TiO2 NRs. To further determine the crystal structure and possible phase changes after introducing Sn doping, the crystal structure was examined with X-ray diffraction (XRD, PW3040/60, PANalytical, Almelo, The Netherlands). Moreover, X-ray photoelectron spectroscopy (XPS, VG Multilab 2000 X, Thermo Electron Corp., Waltham, MA, USA) was employed to determine the chemical composition and states of the nanorods. The binding energy of the C 1 s (284.6 eV) was used for the energy calibration, as estimated for an ordinary surface contamination of samples handled under ambient conditions.
To measure the performance of photoelectrochemical (PEC) water splitting, the exposed FTO was covered with a layer of silver paste and connected to Cu wires with solder. The silver paste, solder, edge and some part of the film were sealed with polydimethylsiloxane (PDMS) or epoxy, in which only a well-defined area about 1 cm2 of the white film was exposed to the electrolyte. A glass vessel filled with 400 mL 1 M KOH was used as the PEC cell, and a class AAA solar simulator (Oriel 94043A, Newport Corporation, Irvine, CA, USA) with the light intensity of 100 mW/cm2 was used as light source. The photocurrent and electrochemical impedance spectra were collected by electrochemical station (AUTOLAB PGSTAT302N, Metrohm Autolab, Utrecht, The Netherlands). Line sweep voltammograms were obtained at the scan rate of 20 mV/S. A Pt slice acting as the counter electrode and a standard Ag/AgCl reference electrode (containing saturated KCl solution) were used for the PEC measurements. The water splitting process in PEC cell was schematically illustrated in (Additional file 1: Figure S1).
Results and discussion
The morphology of the Sn/TiO2 nanorods synthesized under different conditions was depicted in Figure 1. Here, Figure 1a,d shows the top view and side view of the nanorods that were synthesized at 150°C for 18 h, Figure 1b,e shows the nanorods synthesized at 180°C for 6 h, and Figure 1c,f shows the nanorods synthesized at 180°C for 4 h, respectively. It reveals that the diameters of the nanorods are about 200, 100, and 80 nm, accordingly, each nanorod consisting of a bundle of thinner nanorods with rectangular top facets. The side view confirms that all the nanorods were grown almost perpendicularly to the FTO substrates, and the average length of the nanorods is 2.1, 2.1, and 1.5 μm, respectively. In order to optimize the surface area-to-volume ratio for PEC water splitting, and enhance the comparability between the nanorods with and without Sn doping, the reaction conditions for median Sn/TiO2 nanorods density (Figure 1b,e) were selected for all the remaining experiments in this paper. A wide range of precursor molar ratios (SnCl4/TBOT = 0% to 3%) in the initial reactant mixture were used for Sn doping, and almost no noticeable morphology change was observed, except that when the molar ratio reached to 8% the difference turned out to be obvious, as shown in (Additional file 1: Figure S2).
Figure 2 displays the TEM images and SAED pattern of a typical Sn/TiO2 NR. Although the nanorods detached from the FTO substrate have cracked as shown in the inset of Figure 2a, we can clearly find out that the diameter is about 100 nm, consistent with that measured by SEM in Figure 1b. The image of the nanorod tip confirms that each individual nanorod indeed consists of a bundle of thinner nanorods, with the diameters about 10 to 20 nm. The high-resolution transmission electron microscopy (HRTEM) image collected from the edge of the nanorods reveals that the typical Sn/TiO2 NR has a single crystalline structure with the interplanar spacings of 0.32 nm and 0.29 nm, in accordance with the d-spacings of (110) and (001) planes of rutile TiO2, respectively. These results indicate that the Sn/TiO2 NR grows along the <001 > direction. The sharp SAED pattern as shown in the inset of Figure 2b further confirms that the Sn/TiO2 NR is a single crystalline rutile structure.
Figure 3 illustrates the element composition of a representative Sn/TiO2-0.5% NR obtained by EDX. Figure 3a shows the high-angle annular dark-field (HAADF) scanning TEM image of the nanorod, while Figure 3b,c,d are elemental mappings of Ti, O, and Sn, respectively, collected from the nanorod within the rectangular region marked in Figure 3a. Although this percentage of Sn/Ti has approached to the detection limit of EDX and some background noise have kicked in, we can find that Sn atoms have been incorporated over the entire TiO2 nanorod obviously in Figure 3d. Besides, the Sn/Ti ratios of all the detected samples are close to the SnCl4/TBOT molar ratios as shown in (Additional file 1: Figure S3).
To further determine the crystal structure and possible phase changes after Sn doping, we collected the XRD spectra from pristine TiO2 NRs and Sn/TiO2 NRs synthesized with different precursor molar ratio, as shown in Figure 4, in which the typical diffraction peaks of the patterns have been marked. It confirms that the Sn/TiO2 NRs have a tetragonal rutile TiO2 crystal structure (JCPDS No. 21–1276), which is the same as the pristine TiO2 NRs. Even for the highly doped sample (Sn/TiO2-3%), there is no obvious change in diffraction peaks. We infer that the Sn atoms just replace Ti atoms in some spots without destroy the rutile TiO2 crystal structure as schematically illustrated in (Additional file 1: Figure S4). Noteworthy is that the relative intensity of (002) peaks seems to decrease as the doping level exceed 2%. This change may result from the fact that the perpendicularity of the nanorods to the substrate has reduced, as demonstrated in (Additional file 1: Figure S2).
To investigate the changes of the surface composition and chemical states of TiO2 NRs after introducing Sn doping, the XPS spectra collected from the pristine TiO2 NRs and two representative Sn/TiO2 NRs samples with initial SnCl4/TBOT molar ratio of 1% and 3% are compared in Figure 5a. The XPS peaks of the TiO2 NRs (with or without Sn doping) at about 458.1 and 463.9 eV correspond to Ti 2p3/2 and Ti 2p1/2 (Figure 5b), and the XPS peak at about 529.4 eV corresponds to O 1 s state (Figure 5c), respectively. In Figure 5d, the two peaks of the spectra collected from Sn/TiO2-3% NRs at about 486.2 and 494.8 eV correspond to Sn 3d5/2 and Sn 3d3/2, which confirms that the main dopant is Sn4+. Compared to the pristine TiO2 NRs, the Ti and O peaks of Sn/TiO2 NRs show a small positive shift (as shown in Figure 5b,c), which suggests a certain electron drain from the Ti4+ in the oxide matrix due to the presence of Sn4+, considering their difference in electronegativity (Sn = 1.96 vs. Ti = 1.54) [32]. This further confirms that the Sn dopant is indeed mixed into TiO2 NRs at the atomic level, agreeing well with the XRD results as shown in Figure 4. Besides, quantitative analysis of the spectra reveals that the Sn/Ti molar ratio is about 1.2% for Sn/TiO2-1% NRs and 3.2% for Sn/TiO2-3% NRs, respectively.
Next, the photocatalytic activities of the Sn/TiO2 NRs with different Sn doping levels for PEC water splitting are discussed. Figure 6a displays the line sweep voltammograms measured from pristine TiO2 NRs (black), Sn/TiO2-0.5% NRs (red), and Sn/TiO2-1% NRs (green), and the current of the pristine TiO2 NRs in dark is plotted in black dotted line for comparison. The photocurrent density of pristine TiO2 is 0.71 and 0.77 mA/cm2 at the potential of −0.4 and 0 V versus Ag/AgCl, while the value increases to 0.85 and 0.93 mA/cm2 for the Sn/TiO2-0.5% NRs and reaches 1.01 and 1.08 mA/cm2 for the Sn/TiO2-1% NRs. To further explore the effect of Sn doping on the photocatalytic activity, the photocurrent measurements were conducted for a series of samples synthesized with the precursor molar ratio from 0% to 3%. The photocurrent density ratios between Sn/TiO2 NRs and pristine TiO2 NRs photoanodes measured at −0.4 V versus Ag/AgCl are depicted in Figure 6b, where the inset is the optical image of the packaged Sn/TiO2 NR photoanodes. The results reveal that the photocurrent first increases as the doping level rises and reaches the max value of 142 ± 10% at precursor molar ratio of 1%, which corresponds to up to about 50% enhancement compared to pristine TiO2 NRs sample, and then decreases gradually and drops to a value even lower than that of a pristine nanorods.
To analyze the efficiency of Sn/TiO2 NRs for PEC water splitting quantitatively, the photoconversion efficiency is calculated as follow [33]:
where J is the photocurrent density at the measured potential, V is the applied voltage versus reversible hydrogen electrode (RHE), and P is the power intensity of 100 mW/cm2 (AM 1.5G). The RHE potential can be converted from the Ag/AgCl reference electrode [23]
As shown in Figure 6c, the pristine TiO2 NRs achieve the efficiency of 0.48%, while the Sn/TiO2-0.5% NRs and Sn/TiO2-1% NRs achieve the efficiencies of 0.59% and 0.69% at about −0.53 V versus Ag/AgCl, about 23% and 44% enhancement, respectively. The photocatalytic properties of TiO2 and Sn/TiO2-1% nanorods with different morphology were depicted in (Additional file 1: Figure S5), which further supports our choice of the reaction conditions for median nanorods density. These results suggest that appropriate incorporation of Sn atoms can significantly enhance the photocatalytic activity of TiO2 NRs and lead to substantial increase of the photocurrent density and photoconversion efficiency.
The time-dependent measurements also have been carried out on the three samples, as shown in Figure 6d. With repeated on/off cycles of illumination from the solar simulator, the three samples display highly stable photocurrent densities of 0.71, 0.86 and 1.01 mA/cm2 at −0.4 V versus Ag/AgCl, respectively. These measurements have been repeated in several months, and there is no noticeable change happened. This indicates that the Sn/TiO2 NRs possess highly chemical and structural stability for PEC water splitting, which is another critical factor to evaluate their potentials as the photoanode material.
To investigate the role of Sn doping on the enhanced photocatalytic activity, especially for its influence on the electronic properties of TiO2 NRs, we have conducted electrochemical impedance measurement on the pristine TiO2 and Sn/TiO2 NRs with different doping levels at the frequency of 5 kHz in dark as shown in Figure 7. All the samples measured show a positive slope in the Mott-Schottky plots, as expected for TiO2 which is a well-known n-type semiconductor. Importantly, the Sn-doped TiO2 NRs samples show substantially smaller slopes than that of the pristine TiO2 NRs, suggesting a significantly increase of charge carrier densities. Furthermore, the slope decreased gradually as the precursor molar ratio increased from 0.5% to 3%, which confirms the role of Sn doping on increasing the charge carrier density. The carrier densities of these nanorods can be calculated from the slopes of Mott-Schottky plots using the equation [23]
where N d is the charge carrier density, e0 is the electron charge, ϵ is the dielectric constant of TiO2 (ϵ = 170) [23], and ϵ0 is the permittivity of vacuum. The calculated charge carrier densities of the pristine TiO2, Sn/TiO2-1% and Sn/TiO2-3% NRs are 5.5 × 1017, 7.85 × 1018, and 1.25 × 1019 carries/cm3, respectively. We note that the Mott-Schottky method is derived based on a flat electrode model and may have errors in determining the accurate value of charge carrier density of the Sn/TiO2 NRs, since we use the planar area instead of the effective surface area for calculation [34]. Nevertheless, the qualitative comparison of the carrier density of these samples is valid, given that there is almost no difference between the morphology of pristine TiO2 and Sn/TiO2 NRs.
As oxygen vacancy serving as electron donor has been accepted generally as the main cause for the n-type conductivity of TiO2[35], we expect that the incorporation of Sn atoms may lead to the increase of oxygen vacancy which is responsible for the enhanced photocatalytic activity. Besides, other reported effects may also be at work. For instance, the formation of mixed-cation composition (Sn x Ti1−xO2) at the interface and associated modulation of electronic properties may facilitate the exciton generation and separation [30]. The potential difference of TiO2 and SnO2 may promote the photoelectron migration from TiO2 to SnO2 conducting band with decreasing combination, allowing both of the photogenerated electrons and holes to participate in the overall photocatalytic reaction [31]. However, the photocurrent of Sn/TiO2-3% NRs is lower to the pristine TiO2. This may be rationalized as the overly high Sn doping level upshifting the TiO2 band gap and creating much more interfaces, which substantially reduces the light absorption efficiency and impedes the photogenerated charge separation.
Conclusions
In summary, we have successfully realized the controlled incorporation of Sn into TiO2 NRs to enhance the photocatalytic activity for PEC water splitting. Sn concentration is well controlled by adjusting the precursor molar ratio. We studied the crystal structure of the obtained Sn/TiO2 NRs, which is the same as the pristine TiO2 NRs. The PEC measurements reveal that the photocurrent reaches the maximum value of 1.01 mA/cm2 at −0.4 V versus Ag/AgCl with a Sn/Ti molar ratio of about 1%, which corresponds to up to about 50% enhancement compared to the pristine TiO2 NRs. The Mott-Schottky plots indicate that the incorporation of Sn into TiO2 NRs can significantly increase the charge carrier density, hence improving the conductivity of TiO2 NRs and leading to the increase of photocurrent. Besides, the Sn/TiO2 NRs exhibit excellent chemical stability which further promotes them to be a promising candidate for photoanode in photoelectrochemical water splitting devices. With the enhanced conductivity, we believe the Sn/TiO2 NRs can also serves as substitution for pure TiO2 structures in other optoelectronic applications including photocatalysis, photodetectors, solar cells, etc.
References
Chen YW, Prange JD, Dühnen S, Park Y, Gunji M, Chidsey CED, McIntyre PC: Atomic layer-deposited tunnel oxide stabilizes silicon photoanodes for water oxidation. Nat Mater 2011, 10: 539–544. 10.1038/nmat3047
Davis SJ, Caldeira K, Matthews HD: Future CO2 emissions and climate change from existing energy infrastructure. Science 2010, 329: 1330–1333. 10.1126/science.1188566
Murdoch M, Waterhouse GIN, Nadeem MA, Metson JB, Keane MA, Howe RF, Llorca J, Idriss H: The effect of gold loading and particle size on photocatalytic hydrogen production from ethanol over Au-TiO2 nanoparticles. Nat Chem 2011, 3: 489–492.
Bai HW, Liu ZY, Sun DD: The design of a hierarchical photocatalyst inspired by natural forest and its usage on hydrogen generation. Int J Hydrogen Energy 2012, 37: 13998–14008. 10.1016/j.ijhydene.2012.07.041
Fujishima A, Honda K: Electrochemical photolysis of water at a semiconductor electrode. Nature 1972, 238: 37–38.
Roy P, Berger S, Schmuki P: TiO2 nanotubes synthesis and applications. Angew Chem Int Ed 2011, 50: 2904–2939. 10.1002/anie.201001374
Szymanski P, El-Sayed MA: Some recent developments in photoelectrochemical water splitting using nanostructured TiO2: a short review. Theor Chem Acc 2012, 131: 1202.
Hendry E, Koeberg M, O’Regan B, Bonn M: Local field effects on electron transport in nanostructured TiO2 revealed by terahertz spectroscopy. Nano Lett 2006, 6: 755–759. 10.1021/nl0600225
Fravventura MC, Deligiannis D, Schins JM, Siebbeles LDA, Savenije TJ: What limits photoconductance in anatase TiO2 nanostructures? A real and imaginary microwave conductance study. J Phys Chem C 2013, 117: 8032–8040. 10.1021/jp400222t
Liu B, Aydil ES: Growth of oriented single-crystalline rutile TiO2 nanorods on transparent conducting substrates for dye-sensitized solar cells. J Am Chem Soc 2009, 131: 3985–3990. 10.1021/ja8078972
Feng XJ, Shankar K, Varghese OK, Paulose M, Latempa TJ, Grimes CA: Vertically aligned single crystal TiO2 nanowire arrays grown directly on transparent conducting oxide coated glass: synthesis details and applications. Nano Lett 2008, 8: 3781–3786. 10.1021/nl802096a
Oh JK, Lee JK, Kim HS, Han SB, Park KW: TiO2 branched nanostructure electrodes synthesized by seeding method for dye-sensitized solar cells. Chem Mater 2010, 22: 1114–1118. 10.1021/cm902272q
Zhang ZH, Hossain MF, Takahashi T: Photoelectrochemical water splitting on highly smooth and ordered TiO2 nanotube arrays for hydrogen generation. Int J Hydrogen Energy 2010, 35: 8528–8535. 10.1016/j.ijhydene.2010.03.032
Ratanatawanate C, Xiong CR, Balkus KJ Jr: Fabrication of PbS quantum dot doped TiO2 nanotubes. ACS Nano 2008, 2: 682–1688.
Hou Y, Li XY, Zhao QD, Quana X, Chen GH: TiO2 nanotube/Ag–AgBr three-component nanojunction for efficient photoconversion. J Mater Chem 2011, 21: 18067–18076. 10.1039/c1jm12788h
Park YS, Lee JS: Morphology control of single crystalline rutile TiO2 nanowires. Bull Korean Chem Soc 2011, 32: 3571–3574. 10.5012/bkcs.2011.32.10.3571
Chen JZ, Ko WY, Yen YC, Chen PH, Lin KJ: Hydrothermally processed TiO2 nanowire electrodes with antireflective and electrochromic properties. ACS Nano 2012, 6: 6633–6639. 10.1021/nn300787r
Albu SP, Ghicov A, Macak JM, Schmuki P: 250 μm long anodic TiO2 nanotubes with hexagonal self-ordering. Phys Status Solidi (RRL) 2007, 1: R65-R67. 10.1002/pssr.200600069
Paramasivam I, Macak JM, Selvam T, Schmuki P: Electrochemical synthesis of self-organized TiO2 nanotubular structures using anionic liquid (BMIM-BF4). Electrochim Acta 2008, 54: 643–648. 10.1016/j.electacta.2008.07.031
Cho IS, Chen ZB, Forman AJ, Kim DR, Rao PM, Jaramillo TF, Zheng XL: Branched TiO2 nanorods for photoelectrochemical hydrogen production. Nano Lett 2011, 11: 4978–4984. 10.1021/nl2029392
Liu XL, Zhang HM, Yao XD, An TC, Liu PR, Wang Y, Peng F, Carroll AR, Zhao HJ: Visible light active pure rutile TiO2 photoanodes with 100% exposed pyramid-shaped (111) surfaces. Nano Res 2012, 5: 762. 10.1007/s12274-012-0259-5
Chen X, Liu L, Yu PY, Mao SS: Increasing solar absorption for photocatalysis with black hydrogenated titanium dioxide nanocrystals. Science 2011, 331: 746–750. 10.1126/science.1200448
Wang GM, Wang HY, Ling YC, Tang YC, Yang XY, Fitzmorris RC, Wang CC, Zhang JZ, Li Y: Hydrogen-treated TiO2 nanowire arrays for photoelectrochemical water splitting. Nano Lett 2011, 11: 3026–3033. 10.1021/nl201766h
Bang JH, Kamat PV: Solar cells by design: photoelectrochemistry of TiO2 nanorod arrays decorated with CdSe. Adv Funct Mater 2010, 20: 1970–1976. 10.1002/adfm.200902234
Zhou ZJ, Yuan SJ, Fan JQ, Hou ZL, Zhou WH, Du ZL, Wu SX: CuInS2 quantum dot-sensitized TiO2 nanorod array photoelectrodes: synthesis and performance optimization. Nanoscale Res Lett 2012, 7: 652. 10.1186/1556-276X-7-652
Hoang S, Guo SW, Hahn NT, Bard AJ, Mullins CB: Visible light driven photoelectrochemical water oxidation on nitrogen-modified TiO2 nanowires. Nano Lett 2012, 12: 26–32. 10.1021/nl2028188
Hoang S, Guo S, Buddie MC: Coincorporation of N and Ta into TiO2 nanowires for visible light driven photoelectrochemical water oxidation. J Phys Chem C 2012, 116: 23283–23290. 10.1021/jp309743u
Das C, Roy P, Yang M, Jha H, Schmuki P: Nb doped TiO2 nanotubes for enhanced photoelectrochemical water-splitting. Nanoscale 2011, 3: 3094–3096. 10.1039/c1nr10539f
Cho IS, Lee CH, Feng Y, Logar M, Rao PM, Cai L, Kim DR, Sinclair R, Zheng XL: Codoping titanium dioxide nanowires with tungsten and carbon for enhanced photoelectrochemical performance. Nat Comm 2013, 4: 1723.
Pan J, M Hühne S, Shen H, Xiao LS, Born P, Mader W, Mathur SJ: SnO2-TiO2Core-shell nanowire structures: investigations on solid state reactivity and photocatalytic behavior . Phys Chem C 2011, 115: 17265–17269. 10.1021/jp201901b
Liu Z, Sun DD, Guo P, Leckie JO: An efficient bicomponent TiO2/SnO2 nanofiber photocatalyst fabricated by electrospinning with a side-by-side dual spinneret method. Nano Lett 2007, 7: 1081–1085. 10.1021/nl061898e
Li J, Zeng HC: Hollowing Sn-doped TiO2 nanospheres via Ostwald ripening. J Am Chem Soc 2007, 129: 15839–15847. 10.1021/ja073521w
Walter MG, Warren EL, McKone JR, Boettcher SW, Mi Q, Santori A, Lewis NS: Solar water splitting cells. Chem Rev 2010, 110: 6446–6473. 10.1021/cr1002326
Lin YJ, Zhou S, Sheehan SW, Wang DW: Nanonet-based hematite heteronanostructures for efficient solar water splitting. J Am Chem Soc 2011, 133: 2398–2401. 10.1021/ja110741z
Janotti A, Varley JB, Rinke P, Umezawa N, Kresse G, Van de Walle CG: Hybrid functional studies of the oxygen vacancy in TiO2. Phys Rev B 2010, 81: 085212.
Acknowledgements
The authors are grateful for the financial supports by the National Natural Science Foundation of China (grant nos. 51175210 and 51222508).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
BS carried out experimental work, analyzed the data, and prepared the manuscript. TLS participated in the studies and supervised the research work. ZCP improved the manuscript. WJS and TJ participated in the experimental work. GLL participated in the studies, improved the manuscript, and supervised the research work. All authors read and approved the final manuscript.
Electronic supplementary material
11671_2013_1708_MOESM1_ESM.pdf
Additional file 1: Figure S1: Schematic illustration of the water splitting process in PEC cell. Figure S2. SEM images of the Sn/TiO2 NRs with different doping levels, (a) Sn/TiO2-0.5% NRs, (b) Sn/TiO2-8% NRs. Figure S3. EDX spectra measured from a series of Sn/TiO2 NRs, with initial SnCl4/TBOT ratio range from 0.5% to 8%, (a) 0.5%, (b) 1%, (c) 1.5%, (d) 2%, (e) 3%, (f) 8%, the marked values in the spectra are detected Sn/Ti ratio. Figure S4. A supercell for modeling the crystal structure of the Sn/TiO2 NRs. Figure S5. The photocatalytic properties of TiO2 and Sn/TiO2 nanorods with different morphology, (a) photoconversion density, (b) photoconversion efficiency. (PDF 550 KB)
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Sun, B., Shi, T., Peng, Z. et al. Controlled fabrication of Sn/TiO2 nanorods for photoelectrochemical water splitting. Nanoscale Res Lett 8, 462 (2013). https://doi.org/10.1186/1556-276X-8-462
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-8-462