Abstract
Microstructural, electrical, and optical properties of undoped and Nd3+-doped SiO x /SiN y multilayers fabricated by reactive radio frequency magnetron co-sputtering have been investigated with regard to thermal treatment. This letter demonstrates the advantages of using SiN y as the alternating sublayer instead of SiO2. A high density of silicon nanoclusters of the order 1019 nc/cm3 is achieved in the SiO x sublayers. Enhanced conductivity, emission, and absorption are attained at low thermal budget, which are promising for photovoltaic applications. Furthermore, the enhancement of Nd3+ emission in these multilayers in comparison with the SiO x /SiO2 counterparts offers promising future photonic applications.
PACS: 88.40.fh (Advanced materials development), 81.15.cd (Deposition by sputtering), 78.67.bf (Nanocrystals, nanoparticles, and nanoclusters).
Avoid common mistakes on your manuscript.
Introduction
Silicon nanoclusters [Si-ncs] with engineered band gap [1] have attracted the photonic and the photovoltaic industries as potential light sources, optical interconnectors, and efficient light absorbers [2–5]. Multilayers [MLs] of silicon-rich silicon oxide [SiO x ] alternated with SiO2 became increasingly popular due to the precise control on the density and size distribution of Si-ncs [6, 7]. Moreover, the efficiency of light emission from SiO x -based MLs exceeds that of the single SiO x layers with equivalent thickness due to the narrower Si-nc size distribution. The ML approach is also a powerful tool to investigate and control the emission of rare-earth [RE] dopants, for example, Er-doped SiO x /SiO2 MLs [8]. It also allows us to control the excitation mechanism of the RE ions by adjusting the optimal interaction distance between the Si-ncs and the RE ions. However, achieving electroluminescence and hence extending its usage for photovoltaic applications are problematic due to the high resistivity caused by SiO2 barrier layers [9]. Hence, replacement of the SiO2 sublayer by alternative dielectrics becomes interesting. Due to the lower potential barrier and better electrical transport properties of silicon nitride [Si3N4] in comparison to SiO2, multilayers like SiO x /Si3N4 [10], Si-rich Si3N4 (SiN y )/Si3N4 [11], and Si-rich Si3N4/SiO2 [12] were proposed and investigated [13] for their optical and electrical properties.
In this letter, we investigate SiO x /SiN y MLs and compare them with the SiO x /SiO2 counterparts reported earlier [9, 14]. We demonstrate that an enhancement in the conductive and light-emitting properties of SiO x /SiN y MLs can be achieved with a reduced thermal budget. We also report a pioneering study on Nd-doped SiO x /SiN y MLs. A comparison between the properties of Nd3+-doped SiO x /SiO2 and SiO x /SiN y MLs are presented, and we show the benefits of using SiN y sublayers to achieve enhanced emission from Nd3+ ions.
Experimental details
Undoped and Nd-doped 3.5-nm SiO x /5-nm SiN y (50 periods) MLs were deposited at 500°C on a 2-inch p-Si substrate by radio frequency [RF] magnetron co-sputtering of Si and SiO2 targets in hydrogen-rich plasma for the SiO x sublayers and a pure Si target in nitrogen-rich plasma for the SiN y sublayers. An additional Nd2O3 target was used to dope the SiO x and SiN y sublayers by Nd3+ ions. More details on the growth process can be found elsewhere [15]. The excess Si content in the corresponding SiO x and SiN y single layers obtained from RBS studies are calculated to be 25 and 11 at.%, respectively (i.e., SiOx = 1and SiNy = 1.03). Conventional furnace annealing under nitrogen atmosphere at different temperatures, TA = 400 to 1,100°C, and times, tA = 1 to 60 min, was performed on the MLs. X-ray diffraction analysis was performed using a Phillips XPERT HPD Pro device (PANalytical, Almelo, The Netherlands) with CuKα radiation (λ = 0.1514 nm) at a fixed grazing angle incidence of 0.5°. Asymmetric grazing geometry was chosen to increase the volume of material interacting with the X-ray beam and to eliminate the contribution of the Si substrate. Photoluminescence [PL] spectra were recorded in the 550- to 1,150-nm spectral range using the Triax 180 Jobin Yvon monochromator (HORIBA Jobin Yvon SAS, Longjumeau, Paris, France) with an R5108 Hamamatsu PM tube (Hamamatsu, Shizuoka, Japan). The 488-nm Ar+ laser line served as the excitation source. All the PL spectra were corrected by the spectral response of the experimental setup. Top and rear-side gold contacts were deposited on the MLs by sputtering for electrical characterization. Current-voltage measurements were carried out using a SUSS Microtec EP4 two-probe apparatus (SUSS Microtec, Germany) equipped with Keithley devices (Keithly, Cleveland, OH, USA). Energy-filtered transmission electron microscopy [EFTEM] was carried out on a cross-sectional specimen using a TEM-FEG microscope Tecnai F20ST (FEI, Eindhoven, The Netherlands) equipped with an energy filter TRIDIEM from Gatan (Gatan, München, Germany). The EFTEM images were obtained by inserting an energy-selecting slit in the energy-dispersive plane of the filter at the Si (17 eV) and at the SiO2 (23 eV) plasmon energy, with a width of ± 2 eV.
Results and discussions
Effect of annealing on the PL
Since an annealing at TA = 1,100°C and tA = 60 min is the most suitable to achieve an efficient PL from Si-ncs either in sputtered SiO x single layers [7] or in SiO x /SiO2 MLs [16], such treatment was first employed on SiO x /SiN y MLs. The X-ray diffraction [XRD] broad peak centered around 2θ = 28° is the signature of the Si nanoclusters' formation in the SiO x /SiO2 (Figure 1, curve 1) and SiO x /SiN y MLs (Figure 1, curve 2) as already observed by means of atomic scale studies on similar multilayers [17]. However, contrary to the PL emission obtained from the SiO x /SiO2 MLs, no PL emission was observed in the SiO x /SiN y MLs after such annealing (Figure 2a). This stimulated a deeper investigation of the post-fabrication processing to achieve efficient light emission from the SiO x /SiN y MLs.
It was observed that the PL signals from the MLs annealed during tA = 60 min are significant only at lower temperatures (TA = 400°C to 700°C), and high intensities are obtained when the samples are annealed at high temperatures for a short time (TA = 900°C to 1,000°C, tA = 1 min). It is interesting to note that an interplay between TA and tA can yield similar PL efficiencies, as can be seen for TA = 900°C and tA = 1 min, and TA = 700°C and tA = 15 min (Figure 2a).
The highest PL intensity in SiO x /SiN y MLs was obtained with TA = 1,000°C and tA = 1 min (Figure 2b,c), whereas the SiO x /SiO2 MLs showed no emission after such short-time annealing treatment (Figure 2a). Corresponding XRD pattern of this short-time annealed [STA] (STA = 1 min, 1,000°C) SiO x /SiNy showed a broad peak in the range 2θ = 20° to 30° which is absent in STA SiO x /SiO2 MLs (Figure 1, curves 3 and 4). This suggests the presence of small Si clusters in the SiO x /SiN y MLs, with lower sizes (broader peak) by comparison with higher annealing temperature (1,100°C; Figure 1, curves 1 and 2). However, we cannot distinguish which of the sublayer is at the origin of the PL emission. Consequently, the recorded PL may be a combined contribution of the Si-ncs in the SiO x sublayers and the localized bandtail defect states in the SiN y sublayers.
Absorption and electrical studies
The absorption studies show similar absorption coefficients for as-grown and STA MLs, whereas annealing at TA = 1,100°C and tA = 60 min results in an absorption enhancement (Figure 3a). One can say that, at such temperature, an increase in density and size of the Si-ncs occurs due to phase separation of the SiO x sublayers into Si and SiO2 phases. The formation of Si nanocrystals is complete at TA = 1,100°C and tA = 60 min and leads to this enhancement. This reasoning is supported by the results obtained from the PL and the XRD analysis of the samples annealed at such temperature. The PL in the SiO x /SiN y MLs is quenched after an increase in the time and temperatures of annealing (Figure 2a), and this can be attributed to the increase in the size leading to the loss of quantum confinement effect. The formation of Si nanoclusters can be witnessed from the appearance of the XRD peak at 2θ = 28° (Figure 1, curve 2), which is not seen in the short-time annealed sample (Figure 1, curve 3).
Considering a balance between light emission and absorption for photovoltaic applications, we chose to study STA SiO x /SiN y MLs with a total thickness of 850 nm for electrical measurements. Figure 3b compares the dark current curves of 3.5-nm SiO x /5-nm SiN y with our earlier reported 3.5-nm SiO x /3.5-nm SiO2 (140 nm) MLs [14]. The resistivity was calculated at 7.5 V to be 2.15 and 214 MΩ·cm in the SiO x /SiNy and SiO x /SiO2 MLs, respectively. Since the thickness of the SiO x sublayer is the same in both cases (3.5 nm), this decrease in the resistivity of the SiO x /SiNy MLs can be ascribed to the substitution of 3.5-nm SiO2 by 5-nm SiN y sublayers. This hundred-times enhanced conductivity at low voltage paves way for further improvement of the SiO x /SiN y MLs' conductivity, for example, by decreasing the thickness of this SiN y sublayer.
Microstructural studies
The high-resolution transmission electron microscope [HRTEM] and EFTEM observations on STA SiO x /SiN y show Si-ncs in the SiO x sublayers with an average diameter of 3.4 nm. Only a couple of Si nanocrystals were observed in the HRTEM (Figure 4a), whereas a high density of Si-nanoclusters of about 1019 nc/cm3 can be witnessed from the EFTEM images taken at the Si plasmon energy (Figure 4c) implying that they are predominantly amorphous. Interestingly, this density of the Si-ncs in the SiO x /SiN y MLs is an order of magnitude higher than the Si-ncs formed in the SiO x /SiO2 MLs fabricated under similar conditions. The brighter SiO x sublayers are distinguished from the darker SiN y sublayers by filtering the SiO2 plasmon energy (Figure 4b). No evidence of Si-ncs within the SiN x sublayers was obtained. The STA could favor the formation of Si-ncs only in SiO x and not in SiN y sublayers. This could be attributed to the different mechanism of Si-ncs formation in SiO x and SiN y in MLs as opposed to that in single layers [18] and/or the low Si-excess content in SiN y .
Effect of Nd3+-doping
Understanding the microstructure of MLs and considering the enhancement of absorption and emission properties in SiO x /SiN y MLs compared to the SiO x /SiO2 MLs, we investigate the effect of using SiN y sublayer on the PL emission from Nd3+ ions. For this purpose, the SiO x -Nd/SiN y -Nd and SiO x -Nd/SiO2-Nd MLs were fabricated, and their PL properties were compared. No PL emission was detected from the Nd3+-doped SiN y single layers at the different annealing treatments investigated here. Figure 5 shows the PL spectra of the Nd3+-doped as-grown MLs under non-resonant excitation with peaks corresponding to the 4F3/2→4I9/2 and 4F3/2→4I11/2 transitions at 1.37 and 1.17 eV, respectively. The comparison between the PL properties of undoped (Figure 2c) and Nd3+-doped MLs (Figure 5, inset) clearly shows the quenching of visible PL emission and the appearance of two Nd3+-related PL peaks in the Nd-doped MLs. Moreover, the intensity of Nd3+ PL from the doped SiO x /SiN y MLs exceeds that of the SiO x /SiO2 MLs (Figure 5, inset). Thus, we deal with the efficient energy transfer towards Nd3+ ions not only in SiO x but also in SiN y sublayers. Since this emission is observed for as-grown MLs, when no Si-ncs were formed in these MLS, it is obvious that the emission from the Nd3+ ions in the SiN x -Nd sublayers is due to an efficient energy transfer from SiN y -localized defect states towards the Nd3+ ions [19, 20]. PL observed from the doped MLs after STA was not intense, and it was quenched with increasing annealing time. The same behavior was observed for the 900°C annealing. This could be due to the decrease in the number of defect-related sensitizers in SiN y and the formation of Nd2O3 clusters in the SiO x sublayers [21]. On the other hand, annealing at TA = 400°C to 700°C, discussed above for the undoped SiO x /SiNy MLs, enhance Nd3+ PL emission when applied to the doped counterparts (Figure 3). Thus, we attain intense PL at a low thermal budget with TA (400°C to 700°C) and tA (1 min). To optimize Nd3+ emission, the effect of the thickness of each sublayer in SiO x /SiN y MLs is under consideration now.
Conclusion
In conclusion, we show that SiO x /SiN y MLs fabricated by RF magnetron sputtering can be engineered as structures for photovoltaic and photonic applications. The as-grown and STA SiO x /SiN y MLs show enhanced optical and electrical properties than the SiO x /SiO2 counterparts. Besides achieving a high density of Si-ncs at a reduced thermal budget, we show that high emission and absorption efficiencies can be achieved even from amorphous Si-ncs. The Nd-doped MLs, as-grown and those annealed at lower thermal budgets, demonstrate efficient emission from rare-earth ions. We also show that our STA SiO x /SiN y MLs have about a hundred times higher conductivity compared to the SiO x /SiO2 MLs. These results show the advantages of SiO x /SiN y MLs as materials for photovoltaic and photonic applications and open up perspectives for a detailed study.
Abbreviations
- MLs:
-
multilayers
- PL:
-
photoluminescence
- Si-nc:
-
silicon nanoclusters
- SiN y :
-
silicon-rich silicon nitride
- SiO x :
-
silicon-rich silicon oxide
- STA:
-
short time annealing at 1,000°C for 1 min.
References
Canham LT: Silicon quantum wire array fabrication by electrochemical and chemical dissolution of wafers. Appl Phys Lett 1990, 57: 1046. 10.1063/1.103561
Pavesi L, Dal Negro L, Mazzoleni C, Franzo G, Priolo F: Optical gain in silicon nanocrystals. Nature 2000, 408: 440. 10.1038/35044012
Irrera A, Franzo G, Iacona F, Canino A, Di Stefano G, Sanfilippo D, Piana A, Fallica PG, Priolo F: Light emitting devices based on silicon nanostructures. Physica E 2007, 38: 181. 10.1016/j.physe.2006.12.019
Garrido B, Lopez M, Pérez Rodriguez A, Garcia C, Pellegrino P, Ferré R, Moreno JA, Morante JR, Bonafas C, Carrada M, Claverie A, De La Torre J, Souifi A: Optical and electrical properties of silicon nanocrystals ion-beam synthesized in SiO2. Nucl Inst Meth Phys B 2004, 216: 231.
Conibeer G, Green MA, Corkish R, Cho Y, Cho EC, Jiang CW, Fangsuwannarak T, Pink E, Huang Y, Puzzer T, Trupke T, Richards B, Shalav A, Lin KL: Silicon nanostructures for third generation photovoltaic solar cells. Thin Solid Films 2006, 511: 654.
Zacharias M, Heitmann J, Scholz R, Kahler U, Schimdt M, Blasing J: Size controlled highly luminescent silicon nanocrystals: a SiO/SiO2superlattice approach. Appl Phys Lett 2002, 80: 661. 10.1063/1.1433906
Gourbilleau F, Portier X, Ternon C, Voivenel V, Madelon R, Rizk R: Si-rich/SiO2nanostructured multilayers by reactive magnetron sputtering. Appl Phys Lett 2001, 78: 3058. 10.1063/1.1371794
Gourbilleau F, Dufour C, Madelon R, Rizk R: Effects of Si nanocluster size and carrier Er interaction distance on the efficiency of energy transfer. J Lumin 2007, 126: 581. 10.1016/j.jlumin.2006.10.008
Maestre D, Palais O, Barakel D, Pasquinelli M, Alfonso C, Gourbilleau F, De Laurentis M, Irace A: Structural and optoelectronical characterization of Si-SiO2/SiO2multilayers with applications in all Si tandem solar cells. J Appl Phys 2010, 107: 064321. 10.1063/1.3309761
Di D, Perez-Wurfl I, Conibeer G, Green MA: Formation and photoluminescence of Si quantum dots in SiO2/Si3N4hybrid matrix for all-Si tandem solar cells. Solar Energy Materials & Solar Cells 2010, 94: 2238. 10.1016/j.solmat.2010.07.018
So YH, Huang S, Conibeer G, Green MA: Formation and photoluminescence of Si nanocrystals in controlled multilayer structure comprising of Si-rich nitride and ultrathin silicon nitride barrier layers. Thin Solid Films 2011, 519: 5408. 10.1016/j.tsf.2011.02.060
Delachat F, Carrada M, Ferblantier G, Grob JJ, Slaoui A, Rinnert H: The structural and optical properties of SiO2/Si rich SiN x multilayers containing Si-ncs. Nanotechnology 2009, 20: 275608. 10.1088/0957-4484/20/27/275608
Conibeer G, Green MA, Perez- Wurfl I, Huang S, Hao X, Di D, Shi L, Shrestha S, Puthen-Veetil B, So Y, Zhang B, Wan Z: Silicon quantum dot based solar cells: addressing the issues of doping, voltage and current transport. In Prog Photovolt: Res Appl. Paper presented at the 25th EU PVSEC WCPEC-5, Spain; 2010.
Pratibha Nalini R, Dufour C, Cardin J, Gourbilleau F: New Si-based multilayers for solar cell applications. Nanoscale Res Lett 2011, 6: 156. 10.1186/1556-276X-6-156
Ternon C, Gourbilleau F, Portier X, Voivenel P, Dufour C: An original approach for the fabrication of Si/SiO2multilayers using reactive magnetron sputtering. Thin Solid Films 2002, 419: 5. 10.1016/S0040-6090(02)00294-8
Gourbilleau F, Ternon C, Maestre D, Palais O, Dufour C: Silicon-rich SiO2/SiO2multilayers: a promising material for the third generation of solar cell. J Appl Phys 2009, 106: 013501. 10.1063/1.3156730
Talbot E, Lardé M, Gourbilleau F, Dufour C, Pareige P: Si nanoparticles in SiO2: an atomic scale observation for optimization of optical devices. EPL 2009, 87: 26004. 10.1209/0295-5075/87/26004
Dal Negro L, Yi JH, Michel J, Kimerling MC, Chang TWF, Sukhovatkin V, Sargent EH: Light emission efficiency and dynamics in silicon-rich silicon nitride films. Appl Phys Lett 2006, 88: 233109. 10.1063/1.2208378
Biggemann D, Tessler LR: Near infra-red photoluminescence of Nd3+in hydrogenated amorphous silicon sub-nitrides a-SiN x :H <Nd>. Mat Sci Eng B 2003, 105: 188. 10.1016/j.mseb.2003.08.043
Lin R, Yerci S, Kucheyev SO, Van Buuren T, Dal Negro L: Energy transfer and stimulated emission dynamics at 1.1 μm in Nd-doped SiNx. Optics Express 2011, 19: 5379. 10.1364/OE.19.005379
Debieu O, Bréard D, Podhorodecki A, Zatryb G, Misiewicz J, Labbé C, Cardin J, Gourbilleau F: Effect of annealing and Nd concentration on the photoluminescence of Nd3+ions coupled with silicon nanoparticles. J Appl Phys 2010, 108: 113114. 10.1063/1.3510521
Acknowledgements
This study is supported by the DGA (Defense Procurement Agency) through the research program no. 2008.34.0031. The authors acknowledge J. Pierriére for the RBS measurements done with the SAFIR accelerator (INSP, UPMC) and X. Portier (CIMAP) for the TEM image.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
RPN fabricated the undoped multilayers under investigation and carried out the characterization studies. LK and OD fabricated the Nd-doped layers and studied the effect of Nd doping on the MLs. JC and CD made contributions to the optical studies. MC performed the EFTEM measurements. FG conceived of the study and participated in the coordination of the manuscript. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Nalini, R.P., Khomenkova, L., Debieu, O. et al. SiO x /SiN y multilayers for photovoltaic and photonic applications. Nanoscale Res Lett 7, 124 (2012). https://doi.org/10.1186/1556-276X-7-124
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-7-124