Abstract
Due to an increased use of gold nanoparticles (AuNPs) in various consumer products we aimed to investigate the cytotoxic impact of AuNPs found in a commercial dietary supplement drink (SD-AuNPs). The cytotoxic impact of SD-AuNPs was determined in mouse connective tissue fibroblasts (L929). The cells were treated with different concentrations of SD-AuNPs (0.2, 0.5, 10, 20, 30, 40, and 50 µg/mL). The results indicated that the toxicological effect of SD-AuNPs on L929 cells occurred in a dose-dependent manner. Significant reduction of cell viability was found in L929 cells treated with 10, 20, 30, 40, and 50 µg/mL SD-AuNPs for 24 h. L929 cells treated with 40 and 50 µg/mL SD-AuNPs produced significant intracellular reactive oxygen species and TNF-α. High levels of intracellular uptake of these compounds were also observed in L929 cells treated with 50 µg/mL SD-AuNPs.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Gold nanoparticles (AuNPs) have been of interest in biomedical applications [1,2,3,4]. Furthermore, they have been included in consumer food and drink products [4]. Accordingly, direct exposure of humans to AuNPs through ingestion, inhalation, and skin contact has increased. Although many reports have shown that AuNPs have less toxicity than other types of metal-based nanoparticles, their prevalent use makes it still of importance to evaluate the effect of AuNPs contained in consumer products. The intensive use of AuNPs in daily life can lead to more chances of exposure of the human body to these nanoparticles. Several investigations on the toxic effects of synthesized AuNPs, both from academic research laboratories and commercial sources, have been reported [5,6,7]. Recently, there have been many commercial dietary supplement drinks on the market that contain AuNPs (SD-AuNPs). These companies claim that addition of AuNPs into dietary supplement drinks provides health benefits, including acting as an anti-inflammatory agent, and can lead to mood enhancement, and improvements in cognitive function [8]. Therefore, these products can be officially labeled as dietary supplement drinks. However, the addition of AuNPs into these dietary supplement drinks increases the direct exposure of the human body to AuNPs. Most products that contain nanoparticles do not provide detailed information on the prepared nanoparticles used in the products. This issue has led to a growing concern for human health because any risk posed by those nanoparticles is unknown. Especially based on our available knowledge, the information of cytotoxic investigation of AuNPs contained in dietary supplement drinks is very rare. Due to this reason, we were interested in testing whether SD-AuNPs could have an impact on cellular activities. To perform these studies, we used connective tissue fibroblast cells (L929) as test cells in our study. The reason that we focused on this type of fibroblast cells is because they are the predominantly common cells in connective tissue, which is the most abundant tissue in the body. Fibroblast cells play a major role in building to the extracellular matrix to support and maintain tissue structures including oral cavity and intestine. When nanomaterials containing in the drink are consumed, both oral and intestinal absorption of nanomaterials by fibroblasts can occur. Furthermore, L929 cells have been widely used in a standardized nanotoxicity test [9,10,11,12]. Thus, we used L929 cells to explore the toxicity of SD-AuNPs. It should be emphasized that we separated SD-AuNPs out from a dietary supplement drinks through centrifugation, characterized their properties, and then used them for cytotoxicity assessment. A commercial dietary supplement drink with a claim of containing AuNPs was used in this work. We investigated how SD-AuNPs impact the cell viability, reactive oxygen species (ROS) generation, and the inflammatory responses of L929 fibroblasts. Cellular uptake of SD-AuNPs was also investigated to provide more information on the relationship between the amount of AuNPs taken up by fibroblasts and cytotoxicity. A study of cellular response to SD-AuNPs was also included.
2 Materials and methods
2.1 Characterization of SD-AuNPs from a representative dietary supplement drink
The size of SD-AuNPs contained in a representative dietary supplement drink was characterized by using transmission electron microscopy (TEM; TECNAI 20 TWIN, USA). To separate SD-AuNPs from the drink, 1 mL of drink was centrifuged at 9,391 g for 15 min to pellet SD-AuNPs. The SD-GNP pellet was then dispersed in Milli-Q water and the suspension was applied to a copper grid coated with formvar film and dried for TEM analysis. Light absorption of SD-AuNPs was also measured using UV-vis spectroscopy (Shimadzu UV-2550, Japan). The zeta potential and hydrodynamic diameter of the SD-AuNPs were measured by using dynamic light scattering (DLS, Zetasizer, Malvern, UK). The SD-AuNPs were dispersed in Milli-Q water or in cell culture media to check whether the cell culture media has any impact on light absorption, zeta potential, and hydrodynamic size of SD-AuNPs. The SD-AuNPs used in this work is a commercial product purchased from Japan. Based on product information, the surface of SD-AuNPs in the test drink was stabilized with carboxymethyl cellulose (CMC). Other ingredients are water and minerals (sodium, potassium, calcium, and magnesium).
2.2 Cell culture
L929 cells (Riken Cell Bank) were cultured in RPM 1640 medium supplemented with 10% FBS plus 1% penicillin–streptomycin. Cells were maintained in a 5% CO2 humidified incubator at 37 °C.
2.3 Measurement of SD-AuNPs gold concentration by inductively coupled plasma mass spectrometry (ICP-MS)
The gold concentration in the SD-AuNPs was investigated using ICP-MS (Agilent Technologies, USA). A 4.5 mL of SD-AuNPs diluted in Milli-Q water (100 ×) was mixed with a 250 µL of 65% HNO3 and a 250 µL of 37% HCl. The mixed solution was heated using a block heater at 100 °C for 5 h, and ICP-MS measurements were performed. A solution of Au(III) at concentrations of 0, 5, 10, 20, 50, 100, and 200 ppb was prepared for making a linear calibration curve. Optimization of rf power, nebulizer gas flow, auxiliary gas flow, and plasma gas flow was performed before the measurement.
2.4 Cell viability assay
A cell viability measurement was performed by seeding L929 cells at a density of 1 × 104 cells/well into a 96-well plate and culturing in RPMI 1640 supplemented with 10% FBS and 1% antibiotic solution for 24 h at 37 °C. After culturing, various concentrations of SD-AuNPs (0.2, 0.5, 10, 20, 30, 40, and 50 µg/mL) in fresh cell culture media were applied to the cells for 24 h. L929 cells in media were used as control. L929 cells exposed to 1 µg/mL of lipopolysaccharide (LPS from Escherichia coli; O111:B4, Sigma) were under the same conditions as the positive control. After treatment, cells were washed twice with a serum-free medium, and the viability was measured using a CellTiter-Glo assay (Promega) following the protocol provided by the manufacturer. Luminescence signals were collected using a microplate reader (SpectraMax® M3, USA). The relative cell viability was calculated by comparing the luminescent signal of the treated cells with those of the untreated cells.
2.5 ROS generation detection
L929 cells (1 × 104 cells/well) were seeded into a 96-well plate. After incubation for 24 h the cells were exposed to various concentrations of SD-AuNPs (from 0.2 to 50 µg/mL) for 3 h at 37 °C. Cells treated with H2O2 were also prepared as a positive control. The treated condition was performed in RPMI 1640 supplemented with 10% FBS and 1% antibiotic solution. The cells were washed twice with a serum-free medium and treated with 10 µM dichloro-dihydro-fluorescein diacetate (DCFH-DA, Sigma) for 30 min. After treatment, the DCFH-DA was removed and the cells were washed twice with cold PBS before lysing with 20% Tween-20 (in PBS w/o Ca2+ and Mg2+). During the lysing process, cells were shaken for 30 min. The fluorescence signals were measured at 492 nm and 595 nm using a microplate reader.
2.6 Pro-inflammatory cytokine measurement
L929 cells (1 × 104 cells/well) were exposed to SD-AuNPs at concentrations of 0.2, 0.5, 10, 20, 30, 40, and 50 µg/mL for 24 h. After exposure, the cell culture media were collected and centrifuged at 9,391 g for 15 min to remove SD-AuNPs remaining in the cell culture media (RPMI 1640 supplemented with 10% FBS and 1% antibiotic solution). Thereafter, the supernatant of each treatment was stored at − 80 °C and used for determining inflammatory cytokine production (Interleukin-1beta (IL-1β); Interleukin-6 (IL-6); and Tumor necrosis factor (TNF-α)) using an enzyme-linked immunosorbent assay (ELISA) kit (Biolegend). This assay was performed by following the instructions from the manufacturer.
2.7 Cellular uptake of SD-AuNPs and localization of SD-AuNPs in L929 cells
The cellular uptake of SD-AuNPs by L929 cells was investigated using ICP-MS (PerkinElmer, USA). The measurement was done by following the protocol published by Kim et al. [13]. L929 cells were seeded onto a 24-well plate at a density of 2 × 104 cells/well and incubated for 24 h at 37° C in a 5% CO2 incubator. Cells were then cultured with RPMI-1640 medium plus 10% FBS containing SD-AuNPs at 0.2 and 50 µg/mL for 24 h. After the incubation, cells were washed three times with PBS and then lysed by addition of 20% Tween-20 in PBS and sonicated for 30 min. The cell lysate was digested overnight by addition of 250 µL of digestion buffer (3 mL of HNO3 and 1 mL of H2O2). Next, a 3 mL of aqua regia (HCl: HNO3 = 3:1) was added into the samples and incubated for 2 h. After incubation, the samples were diluted, and the final samples contained 5% aqua regia. A gold standard solution (Au(III)) at concentrations of 0, 0.2, 0.5, 1.0, 2.0, 5.0, 10, and 20 ppb was prepared to make a calibration curve used for determining the amount of gold taken up by the cells. The operating conditions of the ICP-MS were also set before measuring the gold content.
The localization of SD-AuNPs inside cells was investigated by using TEM. L929 cells at a density of 1 × 105 cells/mL were cultured in a cell culture dish containing a glass cover slip for 24 h. Following incubation, cells were treated with 0.2 and 50 µg/mL SD-AuNPs for 24 h. Cells were then washed with 0.1 M sodium cacodylate buffer (SCB). After washing, cells were pre-fixed with 2.5% glutaraldehyde dissolved in 0.1 M SCB. The pre-fixed cell samples were stored at 4 °C overnight. Next, cells were washed with 0.1 M SCB three times and then the cells were post-fixed with 1% osmium tetroxide (OsO4) dissolved in 0.2 M SCB at 4 °C for 1 h. Cells were washed again after fixing by using the same washing process mentioned previously. Following this, cells were dehydrated by performing a sequential treatment with serial dilutions of ethanol at different concentrations (30%, 50%, 70%, 80%, 90%, and 95%) for 15 min (at each concentration) at 4 °C. 100% ethanol was added to the cells and soaked for 15 min at 4 °C. This was repeated 4 times in total. Following this soaking step, the embedding process was done. With this process, a mixture of propylene oxide and 100% ethanol at a ratio of 1:1 was added to cells, incubated for 15 min at room temperature, and then decanted. Mixtures of propylene oxide and araldite resin at ratios of 3:1, 1:1, and 1:3 were then prepared at room temperature. A 3:1 propylene oxide/araldite resin mixture was added to the cells and incubated for 1 h and then the mixture was decanted. The process was repeated using a 1:1 propylene oxide/araldite resin mixture. Finally, the 3:1 propylene oxide/araldite resin mixture was added to the cells and the sample was polymerized in a hot air oven at 45 °C for 2 days, and then at 60 °C for another 2 days. The embedding process was prepared by transferring the sample into a mold and pure araldite resin was added. The embedded sample was further incubated in a hot air oven at 60 °C for 2 days. Finally, ultrathin sections were cut from the cell samples at a thickness of 60–90 nm and observed by TEM (268 Morgagni, Thermofisher, The Netherlands) at 80 kV.
2.8 Statistical analysis
All experimental data are expressed as a mean ± standard error (SE). The data were analyzed by using one-way analysis of variance (ANOVA) and Tukey’s multiple comparison test in GraphPad Prism® version 6. The significance of statistical data was calculated at p ˂ 0.01.
3 Results and discussion
3.1 Characterization of SD-AuNPs
TEM characterization of the morphology and core size of SD-AuNPs revealed that their morphology was spherical shape (Fig. 1a) and their sizes were not uniform, varying from ~ 8 to 58 nm. The majority of the particles (~ 53.7%) had a diameter of ~ 14.2 ± 0.1 nm. Approximately 30.1% of the SD-AuNPs had a diameter of ~ 8.0 ± 0.1 nm, and 10.2% of the population had a diameter of ~ 24.0 ± 0.1 nm. Large particles ~ 33.6 nm (5.2%), 41.4 nm (0.7%), and 58.1 nm (0.1%) were also detected. The hydrodynamic diameters of SD-AuNPs were ~ 73 nm (both in original dietary supplement drink and dispersed in Milli-Q water) and ~ 64.5 nm (in cell culture media; Fig. S1 in Supporting Information). Only one plasmon resonance peak was detected, and it had a maximum light absorption peak at ~ 523 nm (Fig. 1b). When SD-AuNPs were dispersed in cell culture media, a very small redshift (~ 1 nm) of a maximum light absorption was detected. The zeta potentials of SD-AuNPs were also investigated. The zeta potential of the SD-AuNPs was ~ − 24.1 mV. According to the label information on the dietary supplement drink, the mass concentration of gold contained in the drink is 10 µg/mL. To confirm the amount of gold in this dietary supplement drink, we analyzed the gold content using ICP-MS and found that the content of gold was 9.2 ± 0.6 µg/mL. This mass concentration was in agreement with the gold amount indicated on the label of the representative dietary supplement drink. When the original dietary supplement drink was diluted with Milli-Q water to a mass, concentration of 0.2 µg/mL SD-AuNPs, we found that the zeta potential was ~ − 25.1 mV. This indicates that Milli-Q water had no impact on changing the zeta potential of SD-AuNPs. However, when SD-AuNPs at the same concentration were dispersed in cell culture media, the zeta potential of AuNPs showed a less negative value (~ − 6.0 mV). This change is in accordance with many reports [14, 15]. The reason for the change of zeta potential could be because of the strong ionic strength of the media, which contains organic salts, amino acids, proteins, and vitamins [16, 17].
3.2 Cell viability and cellular uptake of SD-AuNPs
Following characterization, the viability of L929 cells treated with SD-AuNPs was investigated. L929 cells were incubated with different concentrations (0.2–50 µg/mL) of SD-AuNPs for 24 h. The viability of L929 cells treated with 0.2 and 0.5 µg/mL was ~ 91.5% and 92.9%, respectively. At higher concentrations, in the range of 10–50 µg/mL, the viability significantly decreased in a dose-dependent manner to ~ 80.8% (10 µg/mL), 81.5% (20 µg/mL), 81.4% (30 µg/mL), 73.5% (40 µg/mL), and 63% (50 µg/mL) as compared to untreated cells (Fig. 2a). Cells treated with LPS (1 µg/mL) had the lowest cell viability (60.5%). Greater concentrations of SD-AuNPs likely lead to a higher degree of interaction between the AuNPs and cells which could cause more cellular internalization of SD-AuNPs. To test this hypothesis, the cellular uptake or cellular interaction of AuNPs at a low concentration (0.2 µg/mL) and high concentration (50 µg/mL) was investigated. The results from ICP-MS showed that L929 cells treated with 0.2 µg/mL SD-AuNPs for 24 h had a gold concentration of ~ 3.4 ± 0.3 µg/L. A much higher gold content (14.5 ± 0.9 µg/L) was detected in L929 cells treated with 50 µg/mL SD-AuNPs as shown in Fig. 2b. This implies that association and cellular uptake of SD-AuNPs was dependent on the concentration of AuNPs. It was reported that high concentrations of AuNPs in a solution could increase the chance of AuNPs rapidly interacting with cellular receptors, resulting in greater cellular uptake activity than cells treated with low concentration AuNPs [18].
ICP-MS can only provide information on the amount of SD-AuNPs associated with the cells, and does not distinguish between surface bound AuNPs and internalized AuNPs. TEM analysis was performed to see whether SD-AuNPs can translocate into cells, and examine the intracellular distribution of the AuNPs. As expected, no SD-AuNPs were detected in control cells (untreated; Fig. 3a). In the case of L929 cells treated with 0.2 µg/mL SD-AuNPs, internalized SD-AuNPs were detected (Fig. 3b). The clusters of SD-AuNPs detected in this treatment were not many. However, L929 cells treated with 50 µg/mL showed many large clusters of internalized SD-AuNPs (Fig. 3c). These results, from ICP-MS and TEM imaging confirm that the concentration of SD-AuNPs directly impacted cellular uptake. As shown in Fig. 3c, a high number of SD-AuNPs accumulated inside the cells and formed a large group of SD-AuNPs. This cluster formation by the SD-AuNPs could be involved in the observed reduction of cell viability. It was reported by Wang et al. [19] that higher doses of AuNPs could result in a higher density and higher propensity towards aggregation of AuNPs inside cells. This could lead to a greater reduction of cell viability. Other studies have also reported a similar impact of the dose of AuNPs on their cluster forming ability and its correlation with the induction of cytotoxicity [20, 21].
3.3 Reactive oxygen species (ROS) generation
Although it is commonly believed that gold is chemically inert, many studies have shown that the surface properties of AuNPs could impact ROS induction [22,23,24,25]. However, this induction might be dependent on the concentration of the AuNPs. For this reason, it was important to investigate whether different concentrations of SD-AuNPs could induce ROS production. We found that L929 cells treated with 40 and 50 µg/mL SD-AuNPs for 3 h significantly induced ROS production (Fig. 4). As expected, a significant induction of ROS was detected in L929 cells treated with 50 mM H2O2 (a positive control cell). A recent work published by Chaves et al. [26] also demonstrated that at a higher concentration, AuNPs could induce a higher concentration of ROS production at earlier time points. The enhancement of this ROS generation by AuNPs could lead to different pathological events involved in cell death. The size of the AuNPs also has an impact on the induction of ROS. It was reported that AuNPs of 30 nm could induce more ROS generation than the smaller AuNPs [27]. From TEM images, the sizes of the SD-AuNPs was non-uniform, which might lead to different degrees of interaction between the AuNPs and the cellular membrane of the L929 cells, resulting in different degrees of ROS generation that could impact cell death [28]. Although the current study only focused on the impact of SD-AuNPs on the induction of cytotoxicity, without extensive investigation of the surface properties of commercial SD-AuNPs, it is important to note that besides the size and concentration of AuNPs, the surface property of AuNPs plays a major role in ROS induction as reported by Iswarya et al. [29]. However, a significant induction of ROS was not detected when cells were treated with lower concentrations of SD-AuNPs (10, 20, and 30 µg/mL). This implies that the significant reduction of cell viability at these three concentrations is unlikely to be related to oxidative stress.
3.4 Inflammatory cytokine response
It is well known that inflammatory cytokines have an impact on cellular activities such as cell growth and differentiation, as well as on the stimulation of cellular functions [30]. TNF-α, IL-6, and IL-1β play a major role in immune dysfunction and in the inflammatory response [31,32,33]. Therefore, we examined the impact of SD-AuNPs on the induction of these three inflammatory cytokines in L929 cells. After cells were treated with different concentrations of SD-AuNPs for 24 h, we found that significant induction of TNF-α was only detected in cells treated with SD-AuNPs at concentrations of 40 and 50 µg/mL SD-AuNPs (p ˂0.01) (Fig. 5a). Our results show that significant induction of ROS and TNF- α occurred at the same concentrations. This suggests that there might be a related mechanism between the production of these molecules. It was reported that the ROS generated by nanoparticles could lead to induction of TNF-α [34]. According to our previous publication [35], an increase in TNF- α could be involved in stimulating cell death. It has also been reported that TNF-α could lead to the death of fibroblasts [36]. Furthermore, the study by Cheng et al. [37] revealed that TNF-α could induce apoptotic and autophagic cell death in L929 cells. Therefore, it is very important that consumer’s attention should be drawn to the concentration of SD-AuNPs. Insignificant increases of IL− 6 from ~ 3.8 pg/mL (non-treated cells) to ~ 50 pg/mL in L929 cells treated with 30, 45, and 50 µg/mL SD-AuNPs were detected (Fig. 5b). The small amounts of secreted IL-6 by cells treated with 0.2, 0.5, 10, and 20 µg/mL SD-AuNPs were ~ 3.0, 8.9, 15.4, and 20.1 pg/mL respectively. IL-6 also plays an important role in host defense due to its ability to activate acute inflammation [38]. Although there was no significant induction of IL-6, the trend of an increased level of IL-6 when the concentration of SD-AuNPs was elevated, should be of concern. The amounts of IL-1β in L929 cells treated with different concentrations of SD-AuNPs and non-treated cells were similar (Fig. 5c). This implies that SD-AuNPs at the tested concentrations here had no effect on IL-1β induction in L929 cells. As expected, the positive control, L929 cells treated with LPS had high level of all three inflammatory cytokines.
4 Conclusion
We have demonstrated the impact of SD-AuNPs in a commercial supplement drink on L929 cells. The cytotoxic impact of SD-AuNPs on L929 cells is highly dependent on concentration. Although AuNPs have been applied in many biological applications, it is important to be aware of their toxicity. Our results provide information that although the product is sold in the form of a supplement drink, consumers still need to pay strong attention to the consumption dose (the suggested dose of this SD-AuNPs is ~ 0.2 µg/mL) to avoid any adverse effects that may occur with ingestion.
References
Dykman L, Khelbstov N (2012) Gold nanoparticles in biomedical applications: recent advances and perspectives. Chem Soc Rev 41:2256–2282
Pissuwan D, Niidome T, Cortie MB (2011) The forthcoming applications of gold nanoparticles in drug and gene delivery systems. J Control Release 149:65–71
Pissuwan D, Valenzuela SM, Cortie MB (2006) Therapeutic possibilities of plasmonically heated gold nanoparticles. Trends Biotechnol 24:62–67
Frohlich E, Roblegg E (2012) Models for oral uptake of nanoparticles in consumer products. Toxicology 291:10–17
Coradeghini R, Gioria S, Garcia CP, Nativo P, Franchini F, Gilliland D, Ponti J, Rossi F (2013) Size-dependent toxicity and cell interaction mechanisms of gold nanoparticles on mouse fibroblasts. Toxicol Lett 217:205–216
Jo MR, Bae SH, Go MR, Kim HJ, Hwang YG, Choi SJ (2015) Toxicity and biokinetics of colloidal gold nanoparticles. Nanomaterials 5:835–850
Sung JH, Ji JH, Park JD, Song MY, Song KS, Ryu HR, Yoon JU, Jeon KS, Jeong J, Han BH, Chung YH, Chang HK, Lee JH, Kim DW, Kelman BJ, Yu IJ (2011) Subchronic inhalation toxicity of gold nanoparticles. Part Fibre Toxicol 8:16
Ravensthorpe M (2013) Colloidal gold: the great rejuvenator of mind and body. IOP Publishihing Natural News Web. https://thezeitgeistindia.blogspot.com/2013/12/new-post-three-beneficial-colloids-and.html. Accessed 19 Dec 2013
Chaves CA, Vergani CE, Thomas D, Young A, Costa CA, Salih VM, Machado AL (2014) Biological effects of soft denture reline materials on L929 cells in vitro. J Tissue Eng 5:1–8
Hashimoto M, Yamaguchi S, Sasaki J, Kawai K, Kawakami H, Iwasaki Y, Imazato S (2016) Inhibition of matrix metalloproteinases and toxicity of gold and platinum nanoparticles in L929 fibroblast cells. Eur J Oral Sci 124:68–74
Liu X, Tang M, Zhang T, Hu Y, Zhang S, Kong L, Xue Y (2013) Determination of a threshold dose to reduce or eliminate CdTe-induced toxicity in L929 cells by controlling the exposure dose. PLoS ONE 8:59359
Miranda RB, Fidel SR, Boller MA (2009) L929 cell response to root perforation repair cements: an in vitro cytotoxicity assay. Braz Dent J 20:22–26
Kim C, Agasti SS, Zhu Z, Isaacs L, Rotello VM (2010) Recognition-mediated activation of therapeutic gold nanoparticles inside living cells. Nat Chem 2(11):962–966
Foo YY, Periasamy V, Kiew LV, Kumar GG, Malek SNA (2017) Curcuma mangga-mediated synthesis of gold nanoparticles: characterization, stability, cytotoxicity, and blood compatibility. Nanomaterials 7:1
Sabuncu AC, Grubbs J, Qian S, Abdel-Fattah TM, Stacey MW, Beskok A (2012) Probing nanoparticle interactions in cell culture media. Colloids Surf B Biointerfaces 95:96–102
Moore TL, Rodriguez-Lorenzo L, Hirsch V, Balog S, Urban D, Jud C, Rothen-Rutishauser B, Lattuada M, Petri-Fink A (2015) Nanoparticle colloidal stability in cell culture media and impact on cellular interactions. Chem Soc Rev 44:6287–6305
Yallapu MM, Chauhan N, Othman SF, Khalilzad-Sharghi V, Ebeling MC, Khan S, Jaggi M, Chauhan SC (2015) Implications of protein corona on physico-chemical and biological properties of magnetic nanoparticles. Biomaterials 46:1–12
Trono JD, Mizuno K, Yusa N, Matsukawa T, Yokoyama K, Uesaka M (2011) Size, concentration and incubation time dependence of gold nanoparticle uptake into pancreas cancer cells and its future application to x-ray drug delivery system. J Radiat Res Appl Sci 52:103–109
Wang SH, Lee CW, Shen KC, Tseng FG, Wei PK (2015) Dose dependent distribution and aggregation of gold nanoparticles within human lung adeno-carcinoma cells. RSC Adv 5:98309–98317
Rayavarapu RG, Petersen W, Hartsuiker L, Chin P, Janssen H, Van Leeuwen FW, Otto C, Manohar S, Van Leeuwen TG (2010) In vitro toxicity studies of polymer-coated gold nanorods. Nanotechnology 21:145101
Yao C, Zhang L, Wang J, He Y, Xin J, Wang S, Xu H, Zhang Z (2016) Gold nanoparticle mediated phototherapy for cancer. J Nanomater 2016:1–26
Chompoosor A, Saha K, Ghosh PS, Macarthy DJ, Miranda OR, Zhu ZJ, Arcaro KF, Rotello VM (2010) The role of surface functionality on acute cytotoxicity, ROS generation and DNA damage by cationic gold nanoparticles. Small 6:2246–2249
Mateo D, Morales P, Avalos A, Haza AI (2014) Oxidative stress contributes to gold nanoparticle-induced cytotoxicity in human tumor cells. Toxicol Mech Methods 24:161–172
Rosa S, Connolly C, Schettino G, Butterworth KT, Prise KM (2017) Biological mechanisms of gold nanoparticle radiosensitization. Cancer Nanotechnol 8(1):2
Wahab R, Dwivedi S, Khan F, Mishra YK, Hwang IH, Shin HS, Musarrat J, Al-Khedhairy AA (2014) Statistical analysis of gold nanoparticle-induced oxidative stress and apoptosis in myoblast (C2C12) cells. Colloids Surf B Biointerfaces 123:664–672
Chaves LC, Alvaredo SJ, Bayon MM, Bettmer J, Llopis J, Gonzalez SC (2018) Gold nanoparticles: distribution, bioaccumulation and toxicity. In vitro and in vivo studies. Nanomedicine 14(1):1–12
Piryazev A, Azizova O, Aseichev A, Dudnik L, Sergienko V (2013) Effect of gold nanoparticles on production of reactive oxygen species by human peripheral blood leukocytes stimulated with opsonized zymosan. Bull Exp Biol Med 156:101–103
Wang P, Wang X, Wang L, Hou X, Liu W, Chen C (2015) Interaction of gold nanoparticles with proteins and cells. Sci Technol Adv Mater 16:034610
Iswarya V, Manivannan J, DeSubhabrata A, Roy P, Johnson JB, Kundu R, Chandrasekaran N, Mukherjee A (2016) Surface capping and size-dependent toxicity of gold nanoparticles on different trophic levels. Environ Sci Pollut Res Int 23:4844–4858
Zhang JM, An J (2007) Cytokines, inflammation, and pain. Int Anesthesiol Clin 45(2):27–37
Wojdasiewicz P, Poniatowski LA, Szukiewicz D (2014) The role of inflammatory and anti-inflammatory cytokines in the pathogenesis of osteoarthritis. Mediators Inflamm. https://doi.org/10.1155/2014/561459
Tackey E, Lipsky P, Illei GG (2004) Rationale for interleukin-6 blockade in systemic lupus erythematosus. Lupus 13(5):339–343
Umare V, Pradhan V, Nadkar M, Rajadhyaksha A, Patwardhan M, Ghosh KK, Nadkarni AH (2014) Effect of proinflammatory cytokines (IL-6, TNF-alpha, and IL-1beta) on clinical manifestations in Indian SLE patients. Mediators Inflamm 2014:385297
Matthias R, Cordula H, Jean-Pierre K, Harald FK, Peter W (2013) Comparability of in vitro tests for bioactive nanoparticles: a common assay to detect reactive oxygen species as an example. Int J Mol Sci 14(12):24320–24337
Pissuwan D, Kumagai Y, Smith NI (2013) Effect of surface-modified gold nanorods on the inflammatory cytokine response in macrophage cells. Part Part Syst Charact 30:427–433
Pastorino JG, Simbula G, Yamamoto K, Glascott PA, Rothman RJ, Farber JL (1996) The cytotoxicity of tumor necrosis factor depends on induction of the mitochondrial permeability transition. J Biol Chem 271:29792
Cheng Y, Qiu F, Tashiro SI, Onodera S, Ikejima T (2008) ERK and JNK mediate TNFα-induced p53 activation in apoptotic and autophagic L929 cell death. Biochem Biophys Res Commun 376:483–488
Simson RJ, Hammacher A, Smith DK, Matthews JM, Ward LD (1997) Interleukin-6: structure-function relationships. Protein Sci 6:929–955
Acknowledgements
This work received major funding support from the Capability Building Unit for Nanoscience and Nanotechnology, Faculty of Science, Mahidol University. The authors thank the Center of Excellence on Environmental Health and Toxicology (EHT), Toxicology and Materials Science and Engineering Programs, Center of Nanoimaging (CNI), and Prof. Piyarat Govitrapong at Faculty of Science, Mahidol University for supporting some facilities used in this work. The authors also thank minor funding support from the Development and Promotion for Science and Technology talents project (DPST). Furthermore, the authors are thankful for the extra funding from the Faculty of Science to support this work. Finally, the authors thank Dr. Sujin Jiracheewanun and Mr. Preecha Sowanthip for their technical support.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Chaicherd, S., Killingsworth, M.C. & Pissuwan, D. Toxicity of gold nanoparticles in a commercial dietary supplement drink on connective tissue fibroblast cells. SN Appl. Sci. 1, 336 (2019). https://doi.org/10.1007/s42452-019-0354-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s42452-019-0354-2