Abstract
The recycling of steel plant side streams through cold-bonded briquettes has become quite common. However, Portland cement is mainly used as a binder in the briquettes, contributing significantly to the energy consumption, costs, and carbon footprint associated with the production of cold-bonded briquettes. This paper reports on a more sustainable method for side stream recycling that involves replacing cement with an ettringite-based binder. Ettringite binders develop early high strength and mainly consist of ladle slag, another side stream of the industry. Here, the ettringite-based binder is assessed in terms of its mechanical and thermal properties against a reference briquette made using the conventional technique. Three different briquette types are produced using several side stream materials and varying ettringite-based binder content. Briquettes produced using 15% and higher ettringite-based binder content exhibited excellent mechanical properties within a shorter curing period compared to conventional used binder. Moreover, the ettringite-based binder briquettes exhibited a better swelling behavior to conventional cement briquettes under conditions simulating a blast furnace.
Graphical Abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
During steel production, several side streams are generated. Conventionally, such side streams are landfilled or recycled through sintering plants; however, many of these side streams are rich in iron and carbon, which make them suitable for recycling into different steelmaking processes, such as the blast furnace, electric arc furnace, and basic oxygen furnace. Therefore, due to growing environmental restrictions, as well as the shutdown of several sintering plants, especially in Europe and North America [1], several beneficiation techniques have been innovated to allow for better utilization of such streams in order to reintroduce them to the ironmaking process. These methods range from agglomeration techniques (such as pelletizing and briquetting) to hydrometallurgical, thermal, and physical techniques [2].
Cold-bonded agglomeration has emerged as an alternative to the sintering process as one of the more common beneficiation techniques [3]. A briquette is an agglomerate produced and shaped by pressure while utilizing a binder usually under ambient temperatures [4]. The briquetting process has several benefits including energy savings and reducing environmental load and costs resulting from landfilling [2, 5, 6]. Briquettes must maintain certain chemical and mechanical properties to be suitable for recycling in different steelmaking processes [7]. Moreover, the binders used in briquettes must meet certain physical and chemical properties to ensure the success of the briquetting process [8]. The use of briquettes in blast furnaces (BFs) leads to increased contact between the carbonaceous material and ore bed, which ultimately results in improved CO gas utilization and a lowered temperature of the thermal reserve zone [9].
Several plants in Sweden, Finland, and the USA have successfully adopted cement-bonded briquetting with the aim of recycling side streams [10,11,12]. Although the raw materials for ordinary Portland cement (OPC) have a relatively low cost, their production is energy-intensive and associated with high carbon dioxide emissions (up to 913 kg CO2/t) [13]. Following their production, briquettes may require curing for 24 h under high humidity conditions at a temperature of around 20 °C [14]. Moreover, disadvantages involved in the use of cement-bonded briquettes also include briquette disintegration at low temperatures, increased temperature imbalance in the furnace, and higher energy requirements associated with additional slag formation [15]. The use of briquettes with low strength in BFs, for example, may result in fine generation, which would lower the permeability in the furnace shaft, leading to lower furnace efficiency [6].
Many attempts—with varying degrees of success—have been made to replace the cement in cold-bonded briquettes with different organic and inorganic binders. Binder limitations stem from the presence of impurities, high production costs, and insufficient green strength [7, 16,17,18,19]. For example, using bentonite as a binder results in contamination of product with silica, which may ultimately lead to an increase in energy consumption during production [7]. The use of plastics as a binder is challenging due to the fact that dissociation temperature of plastics is lower than that of iron oxide reduction [16]. Lime and finely dispersed slag may not ensure the required green strength of briquettes when used as binders [19]. Petroleum-based binders used in briquetting may result in the release of volatile substances upon charging [19]. This study is focused on producing cement-free briquettes using ettringite-based binders from ladle slag. Ladle slags are produced either through BOF or EAF steelmaking routes, and they usually contain less than 3% FeO. However, in certain melt shops, this content may rise up to 10% [5]. Ladle slag may be crushed and recycled back to the ladle in order to assist in the formation of the same slags [5]. Ladle slag has a CaO/SiO2 ratio of around 2 and contains calcium aluminates and calcium silicate as its main mineral phases [20, 21]. It also has a relatively high Al2O3 content compared to other steel slags. However, basicity and Al2O3 content may considerably vary depending on the refining process in ladle slag with some sources reporting CaO/SiO2 ratio up to 8 and Al2O3 content as low as 1.3% [22,23,24,25,26]. Calcium aluminates and calcium silicate are both favorable for use in binders, with the former exhibiting a very fast reaction time and the latter increasing the molar ratio of calcium, resulting in enhanced hydraulic properties [20]. Moreover, slowly cooled ladle slag has a very high content of fine powder due to the conversion of β-C2S to γ-C2S [21]. Previous researchers have suggested the use of ladle slag alone or in combination with granulated ground blast furnace slag (GGBFS) in briquettes made for recycling purposes [22, 27]. However, GGBFS is a product that can be used to replace ordinary Portland cement (OPC), and therefore replacing it with lower-value side streams would incur further benefits.
Here, in this study, the thermal and mechanical properties of the produced briquettes using ettringite-based binder are compared against conventional briquettes produced using rapid Portland cement and GGBFS cement. The aim is to produce briquettes with enhanced characteristics to minimize fine particle generation and sustain adequate levels of furnace permeability during furnace operation. The study also aims to increase the use of in-plant fines by attempting to minimize the binder share in the briquette and to analyze the mechanical and thermal behavior of briquettes produced using ettringite-based binders.
Materials and Methods
Materials
Side Streams
Several side stream materials used in this work were obtained from the SSAB plant in Raahe, Finland. These materials were evaluated for their physical and chemical properties. Representative samples were taken using a standard conning and quartering method [28]. Samples were dried, and their moisture content was determined by the heating samples in a lab oven at 105 °C until a constant mass was achieved. The apparent density of each material was determined based on the average of three measurements according to the ISO standard [29] using the following equation:
A gas pycnometer, AccuPyc II 1340, was used to determine the skeleton density (\({\rho }_{S})\) for each of the side stream materials. True density is defined as the mass of a substance divided by its volume, excluding open and closed pores. The pycnometer uses helium as the displacement gas and had a 10 cm3 sample chamber. Determination of skeletal density does not exclude the closed pores volumes since helium may not be able to penetrate through the closed pores. True density could only be equal to the skeletal density if no internal/closed pores exist in the material. The skeletal density of each material was determined based on the average of three consecutive measurements.
To obtain the particle size distribution (PSD) of each material, an adequate representative sample of each material was sieved using the commercially available Analysette 3 Pro Vibratory Sieve Shaker from Fritsch, Germany to separate the coarser fraction. The PSD of the finer fraction (less than 2 mm) was then determined using Beckman Coulter LS 13 320 Universal Liquid Module Laser Diffraction Particle Size Analyzer.
A calibrated Panalytical Axios Max wavelength-dispersive spectrometer equipped with a rhodium anode tube was used for the X-ray fluorescence (XRF) analyses. The carbon content of the samples was determined using LECO CS-200 and calibrated against a sample with predetermined carbon and sulfur content (AR 309). The mineralogical composition of the samples was determined using Rigaku SmartLab 9 kW with a 2θ angle ranging from 4 to 90º and a step of 0.02˚. The samples were scanned at 40 kV and 135 mA. Phases were identified from the diffraction pattern using PDXL 2.6, Rigaku integrated X-ray powder diffraction software.
Ettringite-Based Binder from Ladle Slag and Gypsum
The ettringite-based binder (LSG) was formed from the hydration between the ladle slag (LS—a by-product of the steelmaking process from the ladle furnace) and synthetic gypsum (G). The LS was provided by SSAB Europe Oy (Raahe, Finland), and the commercial gypsum was supplied by VWR Finland (product code: 22,451.360). The former was ground by a ball mill to reach a d50 value of approximately 10 µm, which is similar to previous work [30], while the latter was used as received, with the d50 being roughly 12 µm. In addition, citric acid (product code: C1949, supplied by Tokyo Chemical Industry Co., Ltd., Japan) was used as a set retarder to control the workability of the LSG. This acid has been effectively used in ettringite-based binders [20, 31] via the reduction in the dissolution rate of calcium in the cement grains [32].
As reported in [30, 33], ettringite is the dominant crystalline phase in the structure of LSG and, hence, the strength-giving phase at an early age for the material. Furthermore, details on the material mineralogy, characterization, and analysis of LSG were well detailed in our previous work [30, 33, 34]. Ettringite was formed in the binder within minutes after exposure to the precursors with water, and the main hydrates were ettringite, monosulfate, amorphous aluminum hydroxide, and a C–(A–)S–H gel. Therefore, LSG exhibits potential to be used as a high early-age strength cementitious binder to produce briquettes.
Binder Preparation and Briquette Making
Two types of binders were used: The first binder consisted of rapid cement and ground granulated blast furnace slag cement with a ratio of 50:50, while the second binder used was a LSG binder. Briquettes produced using the first binder were used as reference briquettes to assess their performance against the LSG binder. The first type of briquette is referred to as reference briquettes. The reference briquette contained a 12.6% binder on a dry mass basis, while three LSG briquettes types were produced with a binder content of 10%, 15%, and 20%. Details about the proportion between binder and side streams in reference briquette are covered by industrial confidentiality. All briquettes consisted of a mixture of side stream materials, binder, and water. The mixture of side stream materials in all produced briquettes consisted of components listed in Table 1. Desulfurization scrap is obtained from post-processing of slag from primary and secondary desulfurization process. The post-processing involves magnetic separation of the metallic portion of the slag. Similarly, steel scrap was obtained from post-processing of BOF slag.
To prepare the reference briquettes, side stream materials and binders were dry mixed together using a lab bowl mixer until a homogenous mixture was obtained. Water was added gradually afterward, and mixing continued for another five minutes to produce the wet paste. To produce LSG briquettes, the binder was first prepared by dry mixing gypsum and ladle slag powder. This was followed by adding the required recipe water with dissolved citric acid to the mix. All binder components were thoroughly mixed. The side stream materials were dry mixed separately and were then wet mixed with the binder. The mixing was also continued for another five minutes until a homogenous mixture was achieved.
Briquettes were made using a lab press and die briquetting machine. Moisture content and briquetting force play a crucial role in determining the produced briquette strength [35, 36]. To optimize the reference briquette properties, four different sets (three briquettes in each set) were produced using a moisture content of 8.5% and 9.5% and a briquetting pressure of 100 bar and 200 bar. It was found that briquettes produced using a moisture content of 9.5% and a briquetting pressure of 100 bar yielded the best compression strength. Therefore, these two factors were kept constant in all produced briquettes. The produced briquettes had a diameter and height of 55.5 and 51.0 mm, respectively. The briquettes produced using rapid cement and GGBFS were labeled “Ref,” while those produced using 10%, 15%, and 20% of the new LSG binder were labeled LSG10, LSG15, and LSG20, respectively.
Curing of the reference briquettes took place under high humidity conditions during the first two days and then under ambient conditions until the 28th day. Curing of the LSG briquettes took place for the same durations with the difference that curing was done under ambient laboratory conditions, which may offer a more cost-efficient option compared to high humidity, elevated temperature chambers that are conventionally used for the curing of cement briquettes.
Briquette Particle Packing
Filling the voids between coarse particles when making briquettes results in a significant strength increase. Some researchers have suggested this could be achieved by increasing the finer fraction in briquettes up to 30%, while others have concluded that 80% of the material feed in briquette production should be finer than 200–250 µm in order to obtain optimum strength [35, 37, 38].
To produce the reference briquette, the particle packing of the briquette was first checked using EMMA (Elkem Materials Mixture Analyzer) software. EMMA software [39] predicts optimum packing, utilizing either an Andreassen model or modified Andreassen model. The software then displays the optimum packing line (target line) against the resultant packing line (recipe line) based on the PSD and density of the recipe mixture components provided by the user. Better recipe packing is achieved with the recipe line approaching the target line. Unlike the Andreassen model, the modified Andreassen model considers a minimum particle size value, which makes it more suitable for practical applications. Moreover, it was found that a 100% packing density could be obtained using a distribution coefficient of 0.37 or less [40, 41]. The modified Andreassen equation is as follows:
where CPFT is the “Cumulative Percent Finer Than,” D is the particle size (diameter), DL is the maximum particle size, DS is the minimum particle size, and q is the distribution coefficient.
Briquette Testing and Characterization
Compressive Test
The compression test was conducted according to BS ISO 4700:2007 utilizing the 100 kN Zwick/Z100 testing machine. Briquettes were compressed at a constant speed of 10 mm/min between two parallel flat platens. The test was considered completed either when the load fell to less than 50% of the maximum load recorded or when the gap between the platens became less than 50% of the initial diameter of the test specimen [42].
Drop Test
In the drop test, each sample was dropped from a height of 1 m into a box made of steel, and its mass was recorded after each drop. The procedure was repeated until either the briquette lost 50% of its original mass or when it survived 50 drops without dropping below 50% of its original mass. The number of drops was then recorded as an indication of the drop damage resistance. A similar drop test approach was adopted in recent research [17]. Fines generated after each briquette drop were collected, and their mass was determined.
Phase Characterization
Two sets of briquettes were examined using a Zeiss ULTRA plus field-emission scanning electron microscope (FESEM) attached to an energy-dispersive X-ray spectroscopy (EDS) detector in order to study their structure, morphology, and chemical composition. The briquette pieces of the first set were mounted in epoxy resin using a JEE-420 Vacuum Evaporator to avoid air bubble formation. The surface of the samples was polished afterward using Struers LaboPol-6 with different grinding and polishing discs. The final polishing steps were taken using a 0.25 µm abrasive cloth and EtOH as a lubricant at a force of 10 N/specimen and 150 rpm for two minutes. Finally, the specimen was carbon coated.
The briquette pieces from a second set of briquettes were examined without prior polishing. This set was used to study the morphology of the briquettes, and it was not polished in order to avoid information loss regarding smaller particles found on the surface of bigger particles that would otherwise be lost due to polishing [43]. The composition of certain areas of interest was determined using EDS. Moreover, EDS was used to generate element maps of certain polished sections.
Similar to raw product characterization, the mineralogical composition of the samples was determined by X-ray diffraction (XRD) using Rigaku SmartLab 9 kW in the range 2θ of 5 to 120º with a step of 0.02˚. The samples were scanned under 40 kV and 135 mA conditions. Phase analysis of the diffraction pattern was performed using Rigaku integrated X-ray powder diffraction software PDXL 2.6.
TGA–MS Analysis
TGA–MS measurements were carried out using Netzsch STA 449F3 coupled with Quadrupole Mass Spectrometer (QMS) 403 Aëolos Quadro. Analysis was done using Netzsch Proteus 6.1 software. The sample used was a piece of the briquette weighing around 4 g. Then, the sample was heated from 30 to 1600 °C in an Ar atmosphere at a flow rate of 40 ml/min and a uniform heating rate of 30 °C/min.
Blast Furnace Simulator High-Temperature Behavior
To assess the behavior of the produced briquettes under high-temperature resembling conditions in a BF, a modified blast furnace simulator (BFS) was used. The schematic diagram of the BFS, which was used in our previous work to study pellet reduction [44], is shown in Fig. 1.
The BFS consists of a tube furnace with a sample basket connected to a scale to continuously measure the sample weight. The furnace has an inner diameter of 95 mm; it employs a predetermined heating program, with a temperature and gas mixture set for each heating stage. The furnace can reach a temperature of 1100 °C, and several gases are available in the BFS, including N2 and CO, which were used in this study. The pre-set program used in this study with its temperature and gas profiles is shown in Table 2.
The reduction program in this study consisted of two main stages: The first stage lasted two hours, during which, N2 was introduced to the furnace at a flow rate of 15 l/min (NTP). The sample was heated until a temperature of 950° C was reached. The set temperature was maintained at 950 °C for another 15 min to ensure a stabilized and homogenous temperature profile inside the furnace. In the second stage, a reducing gas mixture of N2 and CO was used. The reducing atmosphere was maintained for 240 min, with the furnace temperature being 950 °C. After the second stage was completed, the N2 flow was introduced to the furnace at a flow rate of 10 l/min (NTP) to cool the sample while avoiding sample re-oxidation. The sample was observed during the test using a video camera and a mirror fixed at the top of the apparatus, adjusted to reflect the image of the sample inside BFS. The video camera recording was used to assess the swelling and cracking behavior of the briquette sample during the different stages of the program.
The briquette was assumed to be a perfect circular cylinder, and the final swelling was calculated based on the initial and final volume of the briquette using the following equation:
where \({A}_{f}\) is the final top surface area of the briquette after reduction, \({h}_{f}\) is the final briquette height after reduction, \({A}_{i}\) is the initial top surface area of the briquette before reduction, and \({h}_{i}\) is the initial briquette height before reduction.
Similarly, swelling during reduction was estimated based on information on the initial and final briquette dimensions along with briquette top surface area measurements from the video recording (i.e., as the top surface area increased to achieve the final surface area, the height of the briquette was assumed to increase proportionally to achieve the final briquette height). Finally, the briquettes were characterized for phase changes after reduction in the BFS using the same testing parameters employed in the XRD scanning of the briquettes pre-reduction.
Results and Discussions
Side Stream Characterization
Moisture content, apparent density, true density, and voids of side stream materials are listed in Table 3. It appears that most of side streams used have an average voidage of about 50%, except for coke, which has a much higher porosity of about 81.70%.
Figure 2 shows the particle size distribution of the side stream materials as well as the used rapid cement and GGBFS cement. Particle size distribution and side streams densities are used to determine the particle packing of the briquettes using EMMA software. The reference briquette particle packing determined using the modified Andreassen model with two distribution coefficients of 0.28 and 0.30 is shown in Figs. 3 and 4, respectively. The lines’ proximity to one another shows that the briquette exhibits relatively good particle packing.
The chemical composition of each sample is presented in Table 4. It appears that harmful elements, especially Zn and P, are in relatively low concentrations in the side stream materials. The highest sulfur content is found in the desulfurization scrap and alkalis in the rapid cement. When replacing rapid and GGBFS cement with an LSG binder, the alkalis in the binder would be reduced at the expense of higher sulfur coming from the gypsum in the LSG binder. This may require special operational precautions depending on the process through which the briquettes are recycled because limited amount of sulfur should not be exceeded in binders intended to be used in steel mills [4]. Increased sulfur content coming from binders in briquettes used in processes like the BOF may result in increased costs related to further hot metal treatment and additional flux charge [5]. In blast furnace, more than half of the sulfur is transferred to the slag through reaction with calcium oxide to form calcium sulfide [8]. This also implies that increased sulfur input requires higher slag volume. This may eventually result in increased costs. Therefore, cost savings from side streams recycling should be carefully considered against resulting costs from binder use.
Detected phases of the samples are shown in Table 5. It appears that iron oxides are the dominating phases in the side stream material. Other phases present are calcite and quartz.
Briquette Properties and Characterization
Compressive Strength
Figure 5 shows the arithmetic mean value of two to three cold compression strength tests for each briquette recipe. The results show that the reference briquette exhibited an increase of strength over the 28-day curing period, which was expected due to the formation of C–S–H. In the hydration of the Portland cement, around 70% of C3S reacts during the first 28 days and the rest reacts over the course of a year. Moreover, β-C2S behaves similarly, with 90% reacting over the course of the first year [45]. Therefore, the resulting strength of binding matrix is expected to increase further as more C–S–H are formed. The force load at which the 28-day-cured briquettes failed was similar to results obtained by other researchers [38].
For the briquette with the new LSG binder, it appears that the strength increased as the binder content increased in the initial 2nd and 7th days of tests. High early strength development is attributed to the formation of ettringite (\({\text{C}}_{3}\text{A}\cdot 3\text{C}\overline{\text{S} }\cdot 32\text{H}\)), a crystalline hydration product of the LSG binder [30], at a very early age (early hydration stage). Another hydration product that leads to an increase in strength is amorphous gibbsite (AH3), which fills the voids between other phases, improving pore structure and increasing rigidity [46]. It is worth noting that LSG15 briquettes achieved comparable strength to the reference briquette on 2 and 7 days of test, while LSG20 binder developed significantly higher strength on 2 and 7 days of testing compared to the reference briquette.
However, after 28 days of curing, the strength of the LSG briquettes appeared to remain almost constant compared to the LSG briquettes cured for seven days. One exception was the 20% LSG binder briquettes, which exhibited a slight decrease in strength on the 28th day of test compared to the 7th day of compression test. One reason that could explain this behavior is the transformation of part of the ettringite into a monosulfate (AFm) [30]. In addition, a reduction in the water-to-binder ratio seems to be another factor that led to this reduction. In all briquette mixtures, a constant water content of 9.5% was used. Hence, with an increase in percentage of the binder being used (i.e., up to 20% binder), the water-to-binder ratio decreased, which might lead to a lower degree of hydration due to an insufficient amount of water available for hydration, as the water-to-binder ratio has a significant influence on the long-term strength development resulting from ladle slag hydration [47].
Drop Test
A drop test was performed to assess the drop damage resistance of the briquette. Figure 6 shows that, in the two-day drop test, the reference briquette had a drop damage resistance of around 39 on average. The LSG10 briquettes had a drop damage resistance of 5. On the other hand, all LSG15 and LSG20 briquettes showed better performance and were able to survive 50 drops without breaking. On the 7th day of drop test, the drop damage resistance of the LSG10 briquettes increased to 10.5 and remained almost constant through the 28th day of drop test. Ref, LSG15, and LSG20 briquettes were all able to survive 50 drops—in both the 7th and 28th days of tests.
To further assess the LSG binder performance, the mass loss of the briquettes was compared against the reference briquette. It could be seen that the LSG15 and LSG20 briquettes were superior when compared to the reference briquettes during the two and seven days of drop tests, while the reference briquette exhibited less mass loss compared to the LSG briquettes on the 28th day of the drop test.
Similar to the compression strength test, the superior performance of the LSG briquettes in the two and seven days of drop tests can be attributed to the early strength development as a result of ettringite phase formation that contributed to the high early strength. This could be particularly useful when aiming to avoid briquette breaking during moving as well as extended curing periods, especially when considering that some plants have cement-bonded briquettes cured in high humidity chambers for the first 24 h following briquette production [14]. The briquettes are taken outside of the plant afterward to be stored and continue their curing. Therefore, the fast strength development of the briquettes would be highly appreciated from this point of view as it would save costs and energy associated with high humidity chamber-curing. Overall, the LSG briquettes utilizing 15 and 20% binder showed comparable or even better mechanical performance than the reference briquette.
XRD
Figure 7 shows the XRD patterns for the produced briquette shell and core. The phase characterization for the reference briquette, which utilizes a mixture of rapid and GGBFS cement as a binder, shows the formation of portlandite (calcium hydroxide, Ca(OH)2), an expected hydration phase [48], along with iron oxides phases previously detected in the raw material. The hydration of Portland cement results in the formation of nearly amorphous C–S–H.
Gibbsite (AH3) is an anticipated hydration product. It cannot be clearly detected through XRD because it does not have a well-defined crystal structure below 40 °C. The weak peaks around 21° may be attributed to its presence [46, 49].
From diffraction peaks, gypsum can be clearly identified. The reason for the presence of the unreacted gypsum might be due to the formation of AH3, which envelops other particles, preventing them from further hydration [45, 46]. Another reason might be that not enough water was available for the reaction with mayenite (C12A7) to produce AH3 according to Eq. 4. Similar diffraction peaks can be observed for the core and shell of the briquettes utilizing the LSG binder. However, the intensity of the characteristic peaks varies, decreasing as the LSG binder percentage increases.
Since the hydration took place at a temperature of around 20 °C, the hydration and conversion reactions are considered as the following [50]:
The conversion reaction from metastable C2AH8 to C3AH6 was expected to lead to a significant loss in strength as metastable hexagonal calcium aluminate hydrate was converted into stable cubic C3AH6, which has a considerably higher density. This conversion reaction leads to a volume change, causing a loss of strength due to an increase in the porosity of the binder [47, 51]. Some literature has reported the conversion reaction starting after 48 h when curing at 20 °C. The conversion reaction is accompanied by the release of water, which may further assist in the hydration of C12A7 [50]. Previous research reported a decrease in strength on the 28th day of test as much as 50% of this strength developed on 3rd day [47]. One reason why there was no sharp decline in the briquette strength on the 7th and 28th days of test is the presence of gypsum, which prevented the formation of C3AH6, with ettringite being formed instead [34] through the following reaction:
Similar to gibbsite (AH3), monosulfate (\({\text{C}}_{4}{\text{A}}\overline{\text{SH}}_{12}\), AFm) was likely not detected by XRD due to its poor crystallinity [49]. Although it is possible to detect AFm within a few days from the beginning of hydration, it could take months before AFm peaks are visible [45].
FESEM
The FESEM reference briquette polished section with an elemental detection map using EDS is shown in Fig. 8. The Fe distribution indicates the presence of iron oxide, which is likely to be hematite, as it was the dominating phase in the side stream materials, as determined by XRD. The Ca and Si distributions indicate the C–S–H formation of a binding matrix that envelops smaller particles while connecting the by-product particles.
EDS mapping for the LSG20 briquette is shown in Fig. 9. The EDS maps clearly show the borders of the iron oxides from the side streams. Ca is well distributed around the iron oxide particles. Its presence with Al and S indicates that ettringite and monosulfate widely exist in the binding matrix. In certain parts of the map, especially the middle, Al exists with Ca but without a corresponding S in the same position, indicating the presence of mayenite (C12A7) and possibly AH3 in small amounts, as AH3 contains Ca from nanosized tricalcium aluminate hexahydrate [49].
A FESEM image of briquettes utilizing a 10% LSG binder is shown in Fig. 10. Circular ettringite crystals were detected with their needle-like structure, identical to that identified in the previous research [52, 53]. AH3 can be found in the shape of villous spherical particles that are 1–10 μm, which mainly contains Al and O along with a small amount of Ca [49]. They cannot be particularly detected in the FESEM images, possibly because they are incorporated into the ettringite matrix [46]. It is clear from the image how ettringite is forming a binding matrix around the spherical iron oxide particle.
TGA–MS
The influence of replacing rapid Portland cement and GGBFS cement with the LSG binder on the mass loss during heating was determined using thermogravimetric analysis (TGA). TGA and derivative thermogravimetry (DTG) curves for the reference briquette and LSG binder are given in Fig. 11. The thermogravimetric analysis/mass spectrometry (TGA–MS) curves for the reference briquette and LSG20 briquette are shown in Fig. 12. Due to the small size of the sample, reactions taking place during heating are assumed to be homogenous throughout the sample volume [54].
From the TGA–DTG curves, it appears that only a minor mass loss took place due to dehydration for both briquettes. For the LSG20 briquette, an obvious peak is observed at a temperature of around 150 °C, which corresponds to the decomposition of ettringite [30, 55, 56]. Dehydration of gypsum also occurs at around 150 °C [46]. For the reference briquette, a small peak is observed around 450 °C, which may correspond to the decomposition of Ca(OH)2 [57]. Additionally, a small peak observed around 380 °C can be attributed to the dehydration of Mg(OH)2 [58]. AH3 is expected to be detected at a temperature of around 270 °C; however, it was not detected, as it might have converted into ettringite, via the reaction shown in Eq. 7 [46] or, a more likely possibility is that AH3 might have formed in a small fraction in the binder due to the need for an abundant amount of water for the reaction to take place, which was not the case with the briquettes made. The latter possibility is more likely.
For both the reference briquette and LSG20 briquette, a peak can be observed around 550 °C and 750 °C, which corresponds to the decomposition of CaCO3, which mainly comes from side streams in the case of the LSG binder [56, 57]. At 750 °C, the peak may also correspond to a reduction in higher iron oxides [54].
It is likely that, in a composite containing carbon-bearing material, the reduction of iron oxides to metallic iron is initiated by a solid–solid reaction between carbon and iron oxide, and then reduction proceeds with the aid of the evolving CO gas from carbon gasification according to the following reactions [59, 60],
Between temperatures of 490 °C and 770 °C, slow and steady mass loss can be noted, which likely corresponds to a reduction in hematite according to Eq. 10 [61]:
Moreover, the CO2 gas evolving from the dissociation of CaCO3 likely contributes to the gasification of carbon from the coke dust. At 800 °C, a significant mass loss began to take place, which indicates the start of coke carbon gasification and the indirect reduction of iron oxides.
Almost full reduction of iron oxides to metallic iron has likely taken place with the reduction of wüstite to metallic iron starting around 750 °C. However, the stepwise reduction from hematite and magnetite to wüstite and finally to metallic iron was not clearly observed in the TG curve because the heating rate was high and rapidly reached a high temperature required for the reduction of wüstite to metallic iron. A similar trend in TG reduction curves has been observed under equivalent conditions [59].
The first H2O peak in the range of 20 °C to 380 °C likely corresponds to the dehydration of the AFm and AFt phases and the release of physically bound water [57]. A second peak is detected around 450–500 °C, which obviously corresponds to the dehydration of Ca(OH)2 according to Eq. 11 [62]:
CO2 gas evolution started from temperature of 500 °C up to 770 °C, which corresponds with the decomposition of CaCO3 and the reduction of a higher amount of oxides according to Eq. 12 [62]:
When studying the behavior of self-reducing mixtures, coke gasification was found to take place at a temperature of 848–860 °C [59, 61]. In this study, the gasification appears to start around 800 °C, which might be due to the presence of metallic iron, which acts as a catalysis for the gasification process [59, 63].
Briquette Reduction and Swelling in BFS
In this series of experiments, three briquettes were heated up to 950 °C in a N2 atmosphere, and the temperature was kept constant. After 135 min from the beginning of heating, reducing CO gas was introduced along with N2, and the reduction stage continued for another 240 min. Fig. 13 shows the mass loss and swelling of the samples during the heating program. It can be seen from the figure that, 120 min after the program was initiated (when the temperature reached 950 °C in the inert atmosphere), the briquettes lost a significant amount of their mass. The reference briquette lost the least amount of mass (5.60% of its initial mass), while the LSG20 briquette was the briquette that exhibited the greatest mass loss (8.56% of its initial mass). Beside the loss of moisture, the steep mass loss of the LSG15 and LSG20 briquettes during the early stages of heating (below 250 °C) can be attributed to ettringite disintegration and was only temperature-dependent, as it took place before a possible reduction could have taken place. Further mass loss in the briquettes during the heating stage can be attributed to the decomposition of CaCO3 and Ca(OH)2. After the reducing gas was introduced, a similar trend in mass loss was observed for all briquettes, mainly corresponding to the reduction of iron oxide in the briquette.
In terms of swelling, Fig. 13 shows contradicting behavior between the LSG briquettes and reference briquettes during the heating stage in N2. However, similar swelling trends among the briquettes were observed following the introduction of the reducing gas. The BFS reduction program resembles conditions at which the briquettes are more likely to exhibit catastrophic swelling, with the heating taking place non-isothermally in the first stage, reaching a maximum temperature of 950 °C, and using CO as the reducing gas [64].
During the heating stage in N2, the LSG briquettes exhibited a slight contraction, with the volume of the LSG20 and LSG15 briquette decreasing 5.7% and 0.6%, respectively. On the other hand, the reference briquette volume exhibited a 16.3% increase of its initial volume. Such observation indicates that the ettringite binder decomposition is accompanied by slight briquette volume shrinkage. On the other hand, increased swelling was observed in the LSG briquettes as well as the reference briquette after the introduction of the reducing atmosphere. This can be mainly attributed to the reduction of iron oxides present in all three tested briquettes (hematite to magnetite to wüstite and, finally, to metallic iron).
When heating the reference briquette in N2 up to 950 °C, the C–S–H gel is converted to C2S and CaO, which supposedly reacts with the iron oxides to form calcium ferrite (CF) and calcium silicoferrite (C3SF3) [64]. When introducing CO reducing gas, metastable Fe3C forms and later oxidizes to Fe. Evolving gases may contribute to further swelling. The reactions can be written as [64]
Images of the briquettes post reduction in the BFS are shown in Fig. 14. It appears that the reference briquette exhibited more swelling and developed more cracks compared to the LSG briquettes.
To examine the briquette structure post reduction, FESEM-EDS was used. Pieces from the fracture surface of the briquette were placed on a carbon tape and platinum-coated. Figure 15 shows the formation of fibrous metallic iron in the reference briquette post reduction. The metallic fibrous iron contributes to the swelling by exerting an internal stress on the briquette structure, pushing against its surrounding. On the other hand, no fibrous iron was formed in the LSG20 briquette. Iron takes the form of closely packed thick and irregular tubes with a coarse outer texture. Differences between reference and LSG20 briquettes with respect to the structure of formed iron might have contributed to the lower swelling in the LSG briquettes.
A compression strength test was carried out for the briquettes post reduction in the BFS. All tested briquettes virtually lost all their strength after reduction. The force at which the briquettes exhibited failure was 329.8, 215.5, and 57.6 N for the reference, LSG20, and LSG15 briquette, respectively. The briquettes exhibited significant strength loss when heated in the nitrogen atmosphere due to the destruction of the bonding matrix. Strength loss became even more drastic when heating took place in the reducing atmosphere, since the destruction of the binding matrix is coupled with the transformation of the aggregate [38]. The results also show that binder content plays a major role in retaining briquettes strength after heating as LSG20 had significantly higher strength compared to LSG15.
XRD for the briquettes post reduction was carried out for the reference, LSG15, and LSG20 briquettes. The detected phases are shown in Fig. 16. It appears that most iron oxides reduced to metallic iron; however, some wüstite remains unreduced. Mayenite could be detected in the LSG briquettes, indicating that part of mayenite did not completely hydrate and remained throughout the curing as well as after reduction. It also appears that C–S–H converted into Ca2SiO4 and partly reacted with iron, forming CaFe2O4.
Conclusions
The performance of cold-bonded briquettes utilizing ettringite-based binders was evaluated in terms of their mechanical and thermal characteristics. Cold-bonded briquettes produced using 10, 15, and 20% of ettringite-based binder (LSG) were compared against a reference briquette produced using ground granulated blast furnace slag and rapid cement. Briquettes produced using 15 and 20% LSG binder exhibited rapid early strength development after being cured in ambient conditions. They were superior to the reference briquettes in terms of strength and drop damage resistance after the 2nd and 7th days of curing and had comparable performance after the 28th day of curing.
The high-temperature thermal behavior of the briquettes was assessed using TGA–DTG–MS for a small sample size in an Ar atmosphere. Full-size briquettes of each type were also tested in a reducing atmosphere in a blast furnace simulator. The TG–MS results showed that the ettringite phase in the LSG briquettes dissociated at around 150 °C. Meanwhile, CaCO3 dissociated above 770 °C and produced CO2 gas, which contributed to the gasification of carbon in coke and, subsequently, the reduction of the iron oxides. In terms of swelling, the reference briquette exhibited significant swelling when heated in the N2 atmosphere up to 950 °C compared to the briquettes with 15 and 20% LSG binder, which exhibited slight shrinkage instead. Upon the introduction of the reducing gas at 950 °C, both briquette types exhibited major swelling. However, the briquette with 20% LSG binder exhibited less swelling compared to the reference briquette. The main reason for the relatively increased swelling in the reference briquette is the formation of fibrous metallic iron, which pushes against its surrounding, as confirmed by the FESEM images.
Overall, the LSG binder is a potentially good alternative to conventional cement in briquette making due to its early strength development and reduced swelling. Moreover, the LSG binder offers a chance to reduce CO2 emissions, since the LSG binder mostly consists of ladle slag, another side stream from the iron and steelmaking industry. However, sulfur content originating from gypsum and potential low-temperature disintegration due to the dissociation of ettringite may limit the use of briquettes in some industrial applications, such as the BF.
References
Wang H, Zhao W, Chu M et al (2017) Current status and development trends of innovative blast furnace ironmaking technologies aimed to environmental harmony and operation intellectualization. J Iron Steel Res Int 24:751–769. https://doi.org/10.1016/S1006-706X(17)30115-2
Das B, Prakash S, Reddy PSR, Misra VN (2007) An overview of utilization of slag and sludge from steel industries. Resour Conserv Recycl 50:40–57. https://doi.org/10.1016/j.resconrec.2006.05.008
Singh M, Björkman B (2004) Effect of processing parameters on the swelling behaviour of cement-bonded briquettes. ISIJ Int 44:59–68. https://doi.org/10.2355/isijinternational.44.59
Pietsch W (2002) Agglomeration processes: phenomena, technologies, equipment. Wiley-VCH, Weinheim
Koros PJ (2003) Dusts, scale, slags, sludges... not wastes, but sources of profits. Metall Mater Trans B 34:769–779
Singh AKP, Raju MT, Jha U (2011) Recycling of Basic Oxygen Furnace (BOF) sludge in iron and steel works. Int J Environ Technol Manag 14:19. https://doi.org/10.1504/IJETM.2011.039255
Qiu G, Jiang T, Li H, Wang D (2003) Functions and molecular structure of organic binders for iron ore pelletization. Colloids Surf Physicochem Eng Asp 224:11–22. https://doi.org/10.1016/S0927-7757(03)00264-4
Geerdes M, Chaigneau R, Kurunov I et al (2015) Modern blast furnace ironmaking: an introduction. IOS Press, Amsterdam
Kasai A, Matsui Y (2004) Lowering of thermal reserve zone temperature in blast furnace by adjoining carbonaceous material and iron ore. ISIJ Int 44:2073–2078. https://doi.org/10.2355/isijinternational.44.2073
Robinson R, Ökvist LS (2003) Recycling of by-product pellets as burden in the blast furnace process: a lab and pilot scale investigation. In: METEC Congress 2003. Düsseldorf, pp 370–375
Landow MP, Martinez M, Barnett T (1997) The recycling of waste oxides at Great Lakes Division. National Steel Corporation, Iron and Steel Society, Warrendale, PA (United States), United States
Kemppainen A, Iljana M, Heikkinen E-P et al (2014) Reduction behavior of cold-bonded briquettes under simulated blast furnace conditions. ISIJ Int 54:1539–1545. https://doi.org/10.2355/isijinternational.54.1539
De Belie N, Soutsos M, Gruyaert E (2018) Properties of fresh and hardened concrete containing supplementary cementitious materials: state-of-the-art report of the RILEM Technical Committee 238-SCM, Working Group 4. Springer, Cham
Sundqvist Ökvist L, Jonsson K, Lampinen H, Eriksson L (1999) Recycling of in-plant fines as cold-bonded agglomerates. Belgium, Brussels
Singh M, Björkman B (1999) Cold bond agglomerates of iron and steel plant byproducts as burden material for blast furnaces. In: Proceedings of the REWAS’99: global symposium on recycling, waste treatment and clean technology, pp 1539–1548
Drobíková K, Plachá D, Motyka O et al (2016) Recycling of blast furnace sludge by briquetting with starch binder: waste gas from thermal treatment utilizable as a fuel. Waste Manag 48:471–477. https://doi.org/10.1016/j.wasman.2015.11.047
Mousa EA, Ahmed HM, Wang C (2017) Novel approach towards biomass lignin utilization in ironmaking blast furnace. ISIJ Int 57:1788–1796. https://doi.org/10.2355/isijinternational.ISIJINT-2017-127
Echterhof T, Willms T, Preiss S et al (2019) Fabrication of agglomerates from secondary raw materials reinforced with paper fibres by stamp pressing process. Appl Sci 9:3946. https://doi.org/10.3390/app9193946
Babanin VI, Eremin AY, Bezdezhskii GN (2007) Development and introduction of a new technology for briquetting finely divided materials with sodium silicate. Metallurgist 51:6
Choi S, Kim J-M, Han D, Kim J-H (2016) Hydration properties of ladle furnace slag powder rapidly cooled by air. Constr Build Mater 113:682–690. https://doi.org/10.1016/j.conbuildmat.2016.03.089
Shi C (2002) Characteristics and cementitious properties of ladle slag fines from steel production. Cem Concr Res 32:459–462. https://doi.org/10.1016/S0008-8846(01)00707-4
Adolfsson D, Robinson R, Engström F, Björkman B (2011) Influence of mineralogy on the hydraulic properties of ladle slag. Cem Concr Res 41:865–871. https://doi.org/10.1016/j.cemconres.2011.04.003
Adesanya E, Ohenoja K, Kinnunen P, Illikainen M (2017) Properties and durability of alkali-activated ladle slag. Mater Struct 50:255. https://doi.org/10.1617/s11527-017-1125-4
Shi C, Hu S (2003) Cementitious properties of ladle slag fines under autoclave curing conditions. Cem Concr Res 33:1851–1856. https://doi.org/10.1016/S0008-8846(03)00211-4
Papayianni I, Anastasiou E (2012) Effect of granulometry on cementitious properties of ladle furnace slag. Cem Concr Compos 34:400–407. https://doi.org/10.1016/j.cemconcomp.2011.11.015
Rađenović A, Malina J, Sofilić T (2013) Characterization of ladle furnace slag from carbon steel production as a potential adsorbent. Adv Mater Sci Eng 2013:1–6. https://doi.org/10.1155/2013/198240
Adolfsson D, Engström F, Robinson R, Björkman B (2011) Cementitious phases in ladle slag. Steel Res Int 82:398–403. https://doi.org/10.1002/srin.201000176
British Standards Institution (1986) Methods for determination of particle size distribution. Part 1: Guide to powder sampling (BS 3406–1:1986). British Standards Institution (BSI), London
British Standards Institution (1998) Tests for mechanical and physical properties of aggregates. Part 3: Determination of loose bulk density and voids (BS EN 1097 :1998). British Standards Institution (BSI), London
Nguyen H, Adesanya E, Ohenoja K et al (2019) Byproduct-based ettringite binder: a synergy between ladle slag and gypsum. Constr Build Mater 197:143–151. https://doi.org/10.1016/j.conbuildmat.2018.11.165
Pelletier L, Winnefeld F, Lothenbach B (2010) The ternary system Portland cement–calcium sulphoaluminate clinker–anhydrite: hydration mechanism and mortar properties. Cem Concr Compos 32:497–507. https://doi.org/10.1016/j.cemconcomp.2010.03.010
Möschner G, Lothenbach B, Figi R, Kretzschmar R (2009) Influence of citric acid on the hydration of Portland cement. Cem Concr Res 39:275–282. https://doi.org/10.1016/j.cemconres.2009.01.005
Nguyen H, Kinnunen P, Carvelli V et al (2019) Strain hardening polypropylene fiber reinforced composite from hydrated ladle slag and gypsum. Compos Part B Eng 158:328–338. https://doi.org/10.1016/j.compositesb.2018.09.056
Nguyen H, Staudacher M, Kinnunen P et al (2019) Multi-fiber reinforced ettringite-based composites from industrial side streams. J Clean Prod 211:1065–1077. https://doi.org/10.1016/j.jclepro.2018.11.241
Kumar DS, Sah R, Sekhar VR, Vishwanath SC (2017) Development and use of mill scale briquettes in BOF. Ironmak Steelmak 44:134–139. https://doi.org/10.1080/03019233.2016.1165499
El-Hussiny NA, Shalabi MEH (2011) A self-reduced intermediate product from iron and steel plants waste materials using a briquetting process. Powder Technol 205:217–223
Singh M (2001) Studies on the cold bonded briquettes of iron and steel plant by-products as burden material for blast furnaces. DIVA
Singh M, Bjorkman B (2006) Strength of cement-bonded briquettes. Miner Metall Process 23:203–213
Elkem Elkem Materials Mixture Analyser software
Myhre B, Hundere AM (1996) The use of particle size distribution in development of refractory castables
Sarkar R (2016) Particle size distribution for refractory castables: a review. Interceram Int Ceram Rev 65:82–86. https://doi.org/10.1007/BF03401156
British Standards Institution (2015) Iron ore pellets for blast furnace and direct reduction feedstocks — Determination of the crushing strength (BS ISO 4700:2015). British Standards Institution (BSI), London
Andersson A, Ahmed H, Rosenkranz J et al (2017) Characterization and upgrading of a low zinc-containing and fine blast furnace sludge: a multi-objective analysis. ISIJ Int 57:262–271. https://doi.org/10.2355/isijinternational.ISIJINT-2016-512
Abdelrahim A, Iljana M, Omran M et al (2020) Influence of H2–H2O content on the reduction of acid iron ore pellets in a CO–CO2–N2 reducing atmosphere. ISIJ Int. https://doi.org/10.2355/isijinternational.ISIJINT-2019-734
Taylor HFW (1997) Cement chemistry, 2nd edn. T. Telford, London
Chang J, Zhang Y, Shang X et al (2017) Effects of amorphous AH 3 phase on mechanical properties and hydration process of C 4 A 3 S ¯ -C S ¯ H 2 -CH-H 2 O system. Constr Build Mater 133:314–322. https://doi.org/10.1016/j.conbuildmat.2016.11.111
Adesanya E, Sreenivasan H, Kantola AM et al (2018) Ladle slag cement: characterization of hydration and conversion. Constr Build Mater 193:128–134. https://doi.org/10.1016/j.conbuildmat.2018.10.179
Liu S, Han W, Li Q (2017) Hydration properties of ground granulated blast-furnace slag (GGBS) under different hydration environments. Mater Sci 23:70–77. https://doi.org/10.5755/j01.ms.23.1.14934
Song F, Yu Z, Yang F et al (2015) Microstructure of amorphous aluminum hydroxide in belite-calcium sulfoaluminate cement. Cem Concr Res 71:1–6. https://doi.org/10.1016/j.cemconres.2015.01.013
Edmonds RN, Majumdar AJ (1988) The hydration of 12CaO.7AI2O3, at different temperatures. Cem Concr Res 18:6
Majumbar A, Singh B, Edmonds R (1989) Hydration of mixtures of C12A7 and granulated blastfurnace slag. Cem Concr Res 19:9
Aye T, Oguchi CT, Takaya Y (2010) Evaluation of sulfate resistance of Portland and high alumina cement mortars using hardness test. Constr Build Mater 24:1020–1026. https://doi.org/10.1016/j.conbuildmat.2009.11.016
Franus W, Panek R, Wdowin M (2015) SEM investigation of microstructures in hydration products of Portland cement. In: Polychroniadis EK, Oral AY, Ozer M (eds) 2nd international multidisciplinary microscopy and microanalysis congress. Springer International Publishing, Cham, pp 105–112
Bagatini MC, Zymla V, Osório E, Vilela ACF (2017) Scale recycling through self-reducing briquettes to use in EAF. ISIJ Int 57:2081–2090. https://doi.org/10.2355/isijinternational.ISIJINT-2017-242
Sha W, Pereira GB (2001) Differential scanning calorimetry study of hydrated ground granulated blast-furnace slag. Cem Concr Res 31:327–329. https://doi.org/10.1016/S0008-8846(00)00472-5
El-Didamony H (1980) Application of differential thermogravimetry to the hydration of expansive cement pastes. Thermochim Acta 35:201–209. https://doi.org/10.1016/0040-6031(80)87194-2
Morandeau A, Thiéry M, Dangla P (2014) Investigation of the carbonation mechanism of CH and C-S-H in terms of kinetics, microstructure changes and moisture properties. Cem Concr Res 56:153–170. https://doi.org/10.1016/j.cemconres.2013.11.015
Fang Y, Chang J (2015) Microstructure changes of waste hydrated cement paste induced by accelerated carbonation. Constr Build Mater 76:360–365. https://doi.org/10.1016/j.conbuildmat.2014.12.017
Ahmed HM, Viswanathan NN, Björkman B (2017) Isothermal reduction kinetics of self-reducing mixtures. Ironmak Steelmak 44:66–75. https://doi.org/10.1080/03019233.2016.1165497
Sharma T (1993) Non-coking coal quality and composite pre-reduced pellets. Int J Miner Process 39:299–311. https://doi.org/10.1016/0301-7516(93)90022-3
Zuo H, Hu Z, Zhang J et al (2013) Direct reduction of iron ore by biomass char. Int J Miner Metall Mater 20:514–521. https://doi.org/10.1007/s12613-013-0759-7
Mikhail SA, Turcotte A-M (1998) Thermal reduction of steel-making secondary materials I. Basic-oxygen-furnace dust. Thermochim Acta 7:9
Lotfian S, Ahmed H, El-Geassy A-HA, Samuelsson C (2017) Alternative reducing agents in metallurgical processes: gasification of shredder residue material. J Sustain Metall 3:336–349. https://doi.org/10.1007/s40831-016-0096-y
Singh M, Björkman B (2004) Swelling behaviour of cement-bonded Briquettes-proposed Model. ISIJ Int 44:482–491. https://doi.org/10.2355/isijinternational.44.482
Acknowledgements
The authors would like to acknowledge Mr. Tommi Kokkonen from the Process Metallurgy research unit at the University of Oulu for his technical support. They would also like to acknowledge the Centre for Material Analysis (CMA) at the University of Oulu for their assistance in the chemical and mineralogical characterization. This work was supported by Business Finland through SYMMET Project (4236/31/2018), Kvantum institute (University of Oulu), and Academy of Finland [Grant Nos. 322085, 329477 and 326291]. The Finnish Cultural Foundation (Grant No.: 60212342/2021), Walter Ahlström Foundation, and Olvi Foundation are acknowledged for their financial support.
Funding
Open Access funding provided by University of Oulu including Oulu University Hospital.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Additional information
The contributing editor for this article was Adam Clayton Powell.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Abdelrahim, A., Nguyen, H., Omran, M. et al. Development of Cold-Bonded Briquettes Using By-Product-Based Ettringite Binder from Ladle Slag. J. Sustain. Metall. 8, 468–487 (2022). https://doi.org/10.1007/s40831-022-00511-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40831-022-00511-1